JP7435966B1 - 道路補修用接着防水組成物 - Google Patents
道路補修用接着防水組成物 Download PDFInfo
- Publication number
- JP7435966B1 JP7435966B1 JP2022150168A JP2022150168A JP7435966B1 JP 7435966 B1 JP7435966 B1 JP 7435966B1 JP 2022150168 A JP2022150168 A JP 2022150168A JP 2022150168 A JP2022150168 A JP 2022150168A JP 7435966 B1 JP7435966 B1 JP 7435966B1
- Authority
- JP
- Japan
- Prior art keywords
- mass
- waterproofing
- road repair
- test
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
本発明の道路補修用接着防水組成物は、主剤と硬化剤とからなり、両者を混合して用いるものである。本発明の道路補修用接着防水組成物は、コンクリート床版の補修部分のコンクリートに塗布され、加熱アスファルト混合物の熱により硬化して防水効果を発揮するものである。
発明の道路補修用接着防水組成物の主剤は、ジエポキシ化合物にシリカ微粉末と希釈剤を添加したものである。ジエポキシ化合物の最も代表的なものとしては、ビスフェノールAとエピクロルヒドリンの縮合物であるジグリシジルエーテルを挙げることができる。この他、ビスフェノールF、フェノール、あるいはクレゾールノボラック樹脂等のジグリシジルエーテル、ダイマー酸等のジカルボン酸から得られたジグリシジルエーテル、ウレタンまたはCTBN変性されたビスフェノールA系ジグリシジルエーテルで、これらのジグリシジルエーテル化合物を1種又は2種以上混合したものであってもよい。
硬化剤は、主体となるモノアミン化合物に、液状ブタジエンゴムあるいはその誘導体と、ポリアミドアミンとを添加したものである。モノアミン化合物としては、炭素数C12以上の直鎖アルキル基を有するものが用いられる。このような炭素数C12以上の直鎖アルキル基を有するモノアミン化合物とは、ラウリルアミン、ミリスチルアミン、オレインアミン、ステアリルアミン等であり、アルキル基が飽和又は不飽和結合を1個以上有する直鎖または分岐のモノアミンである。アスファルトの相溶性若しくは製品の取り扱い性から、炭素数12-18の液状モノアミン化合物が望ましい。
このように、硬化剤成分として炭素数C12以上の長鎖アルキルモノアミン化合物50~70質量%を主体とすることで、初期の段階では反応は直鎖状に進み、熱硬化性と熱可塑性の両方の性質を具備させることができる。従来の道路補修剤に用いられていたエポキシは、2個以上のアミノ基と3個以上の活性水素を持つため硬化が網目構造となり、アスファルト混合物と一体となった密着性が得られなかった。これに対して本発明では、伸縮性のある直鎖状を主体とした架橋構造が得られるため、高粘度であっても-10℃の低温下でもしなやかさを確保することができ、アスファルト混合物と一体となった密着性を得ることができる。
ジエポキシ化合物のJER828を92%と希釈剤2エチルヘキシルグリシジルエーテル8%からなる主剤50部と、C18長鎖アルキルモノアミン(ファーミンOV 花王製)60%、アミノ基末端ブタジエンアクリロニトリル共重合体(Hypro ATBN1300×16 ハンツマン・ジャパン製)30%、(4ヒドロキシフェニル)プロパン10%からなる硬化剤50部とを混合して比較例1の樹脂組成物を得た。
ジエポキシ化合物のJER828を90%と希釈剤2エチルグリシジルエーテル10%からなる主剤60部と、C18長鎖アルキルモノアミン(ファーミンOV 花王製)25%、イソフォロンジアミンの変性物(ハードナーPH-875蝶理GLEX)47%、アミノ基末端ブタジエンアクリロニトリル共重合体(Hypro ATBN1300×16 ハンツマン・ジャパン製)20%、
(4ヒドロキシフェニル)プロパン8%からなる硬化剤40部を混合して比較例2の樹脂組成物を得た。
以上の結果を表1に示す。
(防水試験II)
300mm×300mm×60mmのコンクリート下地に本発明の接着防水材を1kg/m2塗布し、下記の舗装負荷Iおよび舗装負荷IIの条件で舗装した。室温で7日養生後、コアカッターで直径100mm×長さ100mmに採取し、道路橋防水便覧(日本道路協会)防水性試験II供試体作成方法に従って供試体をそれぞれ3個作成した後、23℃で加圧透水試験0.5MPa×24時間を実施した。その結果を表2に示す。
*舗装負荷I 供試体温度60℃ アスファルト混合物SMA(13) 180℃ アスファルト:改質II型
*舗装負荷II 供試体温度 室温 アスファルト混合物SMA(13) 140℃ アスファルト:ストレートアスファルト
300mm×300mm×60mmのコンクリート下地に本発明の接着防水材を1kg/m2塗布し、下記の舗装負荷IIおよび舗装負荷IIIの条件で舗装した。室温で7日養生後、道路橋防水便覧(日本道路協会)引張接着試験に従って、コアカッターで直径100mmの切り込みをそれぞれ3個入れた後、直径100mmの鋼製の治具を接着後、23℃で試験した。その結果を表3に示す。
*舗装負荷II 供試体温度 室温 アスファルト混合物SMA(13) 140℃ アスファルト:ストレートアスファルト
*舗装負荷III 供試体温度5℃ アスファルト混合物SMA(13) 110℃ アスファルト:改質II型
引張接着試験と同様に300mm×300mm×60mmのコンクリート下地に本発明の接着防水材を1kg/m3塗布し、舗装負荷IIおよび舗装負荷IIIの条件で舗装した。
室温で7日養生後、道路橋防水便覧(日本道路協会)せん断試験に従って、試験片をそれぞれ3個採取した後、23℃でせん断試験を行った。その結果を表4に示す。
300mm×300mm×60mmのコンクリート下地に本発明の接着防水材を1kg/m2塗布し、舗装負荷IIの条件で舗装した。室温で7日養生後、道路橋防水便覧(日本道路協会)水浸接着試験の供試体作成方法に従って直径100mmの切り込みを3個入れ、直径100mmの鋼製の治具を接着後、温度23±2℃の水槽に7日間浸漬させた。その後、水槽から取り出し、直ちに引張試験を行った。その結果を表5に示す。
床版防水便覧 日本道路協会のひび割れ防水性試験IIに規定する120mm×70mmのモルタル下地の6mm×40mmの部分に本発明の防水接着剤を施工したものを3個作成し、室温で7日養生した後-10℃±2℃の恒温槽に6時間以上放置した後、毎秒0.1N/mm2で鉛直方向に剤材料が破壊するまで載荷した。その結果を表6に示す。
150mm×70mmの鋼板下地に本発明の防水接着剤を施工したものを6枚作製し、床版防水便覧 日本道路協会の耐薬品性試験に従って、それぞれ2枚ずつ飽和水酸化カルシウム溶液、3%塩化ナトリウム溶液、3%塩化カルシウム溶液に15日間浸漬した。その結果を表7に示す。
なお、以上の説明はコンクリート床版の補修を中心としたが、本発明の道路補修用接着防水組成物は粘着性が高く、鋼床版の補修にも用いることができる。
2 塩化ビニルパイプ
3 シリコーンシーリング
4 離型紙
5 舗装
6 床版防水剤
7 コンクリート
8 2液硬化型エポキシ樹脂
9 ゴムパッキン
10 本体
11 空間
12 注水塔
13 圧力計
14 目盛り
15 圧力調整弁
Claims (2)
- 主剤と硬化剤とからなる道路補修用接着防水組成物であって、
主剤は、ジエポキシ化合物にシリカ微粉末と希釈剤を添加したものであり、硬化剤は、炭素数C 12 以上の直鎖アルキル基を有するモノアミン化合物:50-70質量%、両端末にアミノ基、水酸基、カルボキシル基の何れかを有する液状ブタジエンゴムあるいはその誘導体:20-35質量%、ポリアミドアミン3-5質量%、硬化促進剤:5-10質量%を含有することを特徴とする道路補修用接着防水組成物。 - 主剤は、ジエポキシ化合物:80-90質量%、モノエポキシ化合物の反応性希釈剤と非反応性希釈剤の合計:4-10質量%、シリカ微粉末:3-7質量%を含有することを特徴とする請求項1に記載の道路補修用接着防水組成物。