JP5957807B2 - Packaging bag - Google Patents

Description

  The present invention relates to a multilayer film and a packaging bag suitable for filling a viscous content, and more particularly to a multilayer film and a packaging bag that are thermally contracted after the content is filled to suppress the movement of the content.

  Conventionally, packaging bags for foods such as flour paste, jam, rice cake, and the like, which are viscous foods, which are conventionally used for large-capacity packaging for business use, have a three-side seal system (horizontal seal 510, 520, vertical seal 530), and sealed with a large capacity of 1 kg to 10 kg.

  In such a business packaging bag, it is desired that the packaging bag be easily opened so that the contents can be easily taken out. For example, in Patent Document 1, the laminated film is formed in a substantially parallel shape with a cylindrical shape curved so that both side edges overlap, and a strip-like non-seal portion is left on the tip side of the outer side edge. Further, a technology of a filling and packaging bag is disclosed in which a three-sided seal bag having a plurality of vertical seal portions and a horizontal seal portion formed so as to intersect with both longitudinal ends of the vertical seal portions is filled with an object to be filled. Yes.

  The laminated film in Patent Document 1 is formed by using a base layer that provides film strength to the intermediate layer, with the inner and outer layers being made of a low-density polyethylene seal layer, and the longitudinal seal portion and the lateral seal portion are easily opened. Since the packaging bag is formed as a seal (easy peel), it can be opened simply by picking and pulling the strip-shaped non-seal portion with a finger.

  In addition, when a large vibration occurs during the storage operation or distribution of the packaging bag, there has been a problem that the easy peel portion is peeled off due to the content being vibrated and stressed. Furthermore, it has been recognized that the composition network of the contents collapses due to external pressure such as vibration, and moisture and the like aggregate on the surface of the packaging bag from the inside, thereby deteriorating the quality and appearance.

  For such problems, as shown in FIG. 5, a packaging bag is formed by using a biaxially stretched plastic film as a raw material of the packaging bag, and the contents are suppressed from shrinking by heat shrinking after filling the contents. Shrink packaging bags are used.

  As shown in FIG. 6, the conventional shrink wrapping bag has a heat-shrinkable plastic film 60 laminated cross section, and a biaxially stretched polyamide base material 630 that can be heat-sealed is arranged on the outermost layer, and heat-sealing is possible on the inner layer. A linear low density polyethylene (LLDPE) 650 having a suitable sealant and at least one selected from the group consisting of polyolefin, polyester, and polyamide are laminated, and a base material 630 made of shrink and a sealant 650 are laminated. The non-stretched polyethylene 640 is used to buffer the peeling of the film, and the innermost layers are heat-sealed as shown in FIG. 7, and the heat-shrinkable plastic film 60 is continuously formed into a cylindrical shape. A seal portion 530 (FIG. 5) is formed.

  As a technique for improving the openability of such a shrink wrapping bag, for example, in Patent Document 2, by providing a vertical notch in the horizontal seal portion, it is possible to use an opening device such as a knife, a cutter, and a bag. A technique relating to a packaging bag that secures an opening is disclosed.

International Publication No. 2006/038700 Japanese Patent No. 38459797

  However, in the shrink wrapping bag having easy-openability disclosed in Patent Document 2, the contents are taken out by tearing only in one longitudinal direction with reference to the notch, and there is still a problem that the ease of taking out is not sufficient. is there.

  Therefore, the present invention has been made in view of the above-mentioned conventional problems, and in a packaging bag in which the contents are sealed by heat sealing after filling the contents and heat-shrinked, the opening is easy and the contents are taken out. It aims at providing the packaging bag which improved ease.

In order to solve the above-mentioned problems, the packaging bag according to the present invention is a packaging bag that heat-seals the contents after filling, seals the contents, and thermally shrinks, and can form an easy peel on the inner layer and the outer layer. A thermoplastic resin that shrinks when heat is applied to the intermediate layer, a multilayer film in which polyethylene is laminated between the inner layer and the outer layer and the intermediate layer, and the inner layer and the outer layer are made of linear low-density polyethylene. The thermoplastic resin of the intermediate layer is made of biaxially stretched polyamide, the polyethylene laminated between the inner and outer layers and the intermediate layer is made of low density polyethylene, and the packaging bag is made of the multilayer film. A tip of one side edge portion that has an overlapping portion that is curved in a cylindrical shape and that is overlapped at both ends thereof and that is on the outer surface side of the overlapping portion Having a vertical seal portion in a state where a finger insertion portion which is a strip-shaped non-seal portion having a width (10-20 mm) enough to be picked by a finger is left, and crosses both longitudinal ends of the vertical seal portion. It has a formed horizontal seal portion, the vertical seal portion is an easy peel with a heat seal strength of less than 10 N / 15 mm width according to JIS K6854, and the vertical seal portion is made of a cohesive peel easy-open seal The horizontal seal part has a heat seal strength of 10 N / 15 mm width or more according to JIS K6854, and the non-seal part has an easy opening means for tearing in the short direction.

  According to the present invention, in a packaging bag in which the contents are sealed by heat-sealing after the contents are filled and heat-shrinked, it is easy to open and the ease of taking out the contents can be improved.

It is a top view of the packaging bag in the embodiment of the present invention. It is a figure which shows the laminated structure of the multilayer film in embodiment of this invention. It is AA sectional drawing of FIG. 1 of the packaging bag in embodiment of this invention. It is a top view of the packaging bag in other embodiments of the present invention. It is a top view of the conventional packaging bag. It is a figure which shows the layer structure of the conventional multilayer film. It is BB sectional drawing of FIG. 5 of the conventional packaging bag.

  Next, embodiments for carrying out the present invention will be described in detail with reference to the drawings. In addition, in each figure, the same code | symbol is attached | subjected to the part which is the same or it corresponds, The duplication description is simplified thru | or abbreviate | omitted suitably.

  The packaging bag using the said multilayer film in embodiment of this invention is demonstrated. FIG. 1 is a plan view of a packaging bag according to an embodiment of the present invention, and FIG. 3 is a cross-sectional view taken along line AA of FIG. 1 of the packaging bag according to an embodiment of the present invention.

  In FIG. 1, the packaging bag 20 is manufactured with the pillow packaging machine using the multilayer film 10 described in FIG. The packaging bag 20 includes horizontal seal portions 210 and 220 and a vertical seal portion 230. These seal portions in this embodiment are all easy peels having a heat seal strength of less than 10 N / 15 mm width according to JIS K6854.

  The packaging bag 20 forms an overlapping portion 300 (see FIG. 3) formed by curving the multilayer film 10 into a cylindrical shape and overlapping both ends thereof, and is on the outer surface side of the overlapping portion 300. The vertical seal portion 230 (see FIG. 1) with the finger insertion portion 310, which is a strip-shaped non-seal portion having a width (10 to 20 mm) that can be picked by a finger, on the front end 320 side of one side edge portion. Is formed into a cylindrical body. The overlapping portion 300 is formed by joining the outer layer 110 and the inner layer 150 in the multilayer film 10. In the present embodiment, it goes without saying that the vertical seal portion 230 may be formed by only one thick line or a plurality of thin lines.

  The cylindrical body 20 is filled with a predetermined amount of an object to be filled, and both lateral seals 210 and 220 are formed so as to intersect with the vertical seal 230 and sealed. Here, the vertical seal portion 230 and the horizontal seal portions 210 and 220 are not peeled off before being opened in order to take out the filling material from the packaging bag 20. When opening, it is easy to agglomerate and peel with sufficient strength that the vertical seal portion 230 and the horizontal seal portions 210 and 220 are peeled off simply by picking and pulling the finger insertion portion 310 which is a belt-like non-seal portion with a finger. It consists of an openable seal (so-called easy peel).

  It should be noted that the seal width of the vertical seal portion 230 is preferably less than 15 mm in order to facilitate opening when the finger holder 310, which is a strip-shaped non-seal portion, is picked and opened with a finger. By the way, the cohesive peel easy-open seal is such that the seal layer itself is broken and peeled off, and no stringing occurs at the time of peeling. Therefore, there is no possibility of mixing in the filling material. In addition, the seal strength is stable with a smooth peeling feeling, and the temperature dependency is very small. Furthermore, a pure white peeling mark is generated on the peeling surface. Since this white peeling trace can be visually confirmed by peeling whether or not the seal is properly formed, it can also be used for checking the sealing state in the packaging process. As a result, the reliability of the filling object is maintained.

  The packaging bag 20 formed in this way undergoes a heat shrinking process in which it is left in 92 ° C. hot water for 1 minute, but the hot water temperature and time at this time are lower than this, and if it is short, it will not shrink sufficiently. It does not perform its original function. Further, when exposed to a high temperature atmosphere for a long time, the linear low density polyethylene layers 110 and 150 are peeled off. As a result, the film strength and the seal strength are lowered, and the seal portion is hardened and the stress for the opening operation is more than necessary. It will take. The heat shrinking step is not limited to the above numbers depending on the contents volume and temperature as long as it satisfies the original shrinkage and does not require seal strength and excessive tear stress. Furthermore, the heat shrinking step is not limited to hot water, and may be performed using a heater or the like.

  FIG. 2 is a diagram showing a laminated configuration of the multilayer film in the embodiment of the present invention. In FIG. 2, the multilayer film 10 in the present invention includes an outer layer 110, a sand layer 120, a shrink layer 130, a sand layer 140, and an inner layer 150.

  The outer layer 110 and the inner layer 150 are made of a thermoplastic resin capable of forming an easy peel that causes cohesive failure. For example, a composition of linear low density polyethylene (LLDPE) and polypropylene (PP), a composition of LLDPE and polybutene, a low density The composition of polyethylene (LDPE) and PP, the composition of ethylene-vinyl acetate copolymer (EVA) and PP, etc. are mentioned. In the present invention, the resin capable of forming an easy peel is not limited to these. It can be appropriately selected and used.

  The sand layers 120 and 140 are layers made of polyethylene provided between the shrink layer 130 and the outer layer 110 and the inner layer 150. For example, LLDPE or LDPE can be used. The shrinkable layer 130 can be bonded using a known adhesive. By having this sand layer, peeling from the outer layer 110 and the inner layer 150 when the shrink layer 130 is thermally contracted can be buffered.

  The shrink layer 130 is made of a thermoplastic resin that shrinks when heated, and a known biaxially stretched resin can be used, but polyamide is preferably used in order to satisfy various mechanical properties such as strength. Examples of polyamides include aliphatic nylons such as nylon 6, nylon 66, nylon 12, and nylon 46, aliphatic nylons containing aromatics such as MX_nylon, aromatic nylons, and their copolymer nylons, and resins thereof. Of the mixture.

  The biaxially stretched polyamide 130 is produced by a generally used infusion method or cast method, and is stretched by simultaneous biaxial stretching and sequential biaxial stretching. A biaxially stretched film may be prepared by a tubular method. The draw ratio of biaxial stretching is 2 to 6 times, preferably 3 to 5 times for each axis method. If the stretching ratio is 2 times or less, the heat shrinkability and break resistance, which are the effects of stretching, are not sufficiently exhibited. Moreover, if it exceeds 6 times, the film may be broken during stretching, and it is said that the film strength is remarkably lowered.

  Furthermore, the film laminating method in this embodiment can be produced by laminating each layer by a commonly used dry lamination method, extrusion lamination method, hot lamination method, or the like, or a combination thereof. As the adhesive, known ones that are generally used can be used.

  According to this embodiment, the heat-shrinkable biaxially stretched polyamide is sandwiched with the linear low density polyethylene forming the seal portion, and the low density polyethylene is further provided between the polyamide and the linear low density polyethylene. Thus, delamination during heat shrinkage can be prevented, and linear low density polyethylene disposed in the inner and outer layers can be heat-sealed to form an easy peel.

  Next, another embodiment of the present invention will be described. In the above-described embodiment, the lateral seal portion is used as an easy peel to improve the openability in the short direction. However, in this embodiment, an easy-opening means different from the lateral seal is provided. FIG. 4 is a plan view of a packaging bag according to another embodiment of the present invention. The packaging bag 40 is a strong seal in which the horizontal seals 410 and 420 are formed with a heat seal strength of 10 N / 15 mm width or more according to JIS K6854. The vertical seal 430 is configured with an easy peel in the same manner as the vertical seal 230 in the embodiment of FIG. The horizontal seals 410 and 420 can be formed by sealing at a higher temperature, pressure, and time than the horizontal seals 210 and 220 in the embodiment of FIG. This makes it possible to more completely prevent the contents from being exposed due to peeling of the horizontal seal, for example, at the same time as filling the contents in a vertical bag.

  Moreover, the packaging bag 40 has an easy-opening means for improving the openability in the short direction in the non-sealing portion 440. As the easy-opening means, for example, as shown in FIG. 4, the notch 450 and 460 that are cuts are formed at both ends in the longitudinal direction of the non-seal portion 440, so that the ease of opening in the short direction can be improved. Further, the easy-opening means is not limited to such a notch, and may be any means such as providing a semi-penetrating cut or a fine flaw (hole) at the lateral edge of the non-seal portion 440. Of course.

  Furthermore, in order to further improve the openability, in addition to easy opening means such as a notch, an opening assisting means for assisting opening in the short direction may be provided in the vicinity of the lateral seals 410 and 420.

  Here, the opening assisting means is used to assist the incision cut by the easy opening means so as to be cut in a straight line (or a desired direction). For example, as shown in FIG. It can be formed by inserting some perforations 470, 480.

  As described above, according to the present invention, a multilayer film made of a heat-seal resin, a shrinkable resin, and a heat-seal resin is curved into a cylindrical shape, and both end portions thereof are overlapped. A vertical seal part is formed with the non-seal part left on the tip side of the part, a predetermined amount of filling material is filled inside the cylindrical body, and a horizontal seal is formed so as to intersect the vertical seal. By making the vertical seal and / or the horizontal seal easy peel, it is possible to easily open and take out the contents. In addition, by performing the shrink processing, the contents are compressed to an extent that they cannot move relative to each other, and the quality of the contents can be stabilized due to a change in the external environment where the packaging bag is placed.

  The present invention has been described above by the preferred embodiments of the present invention. While the invention has been described with reference to specific embodiments thereof, various modifications and changes can be made to these embodiments without departing from the broader spirit and scope of the invention as defined in the claims. is there.

DESCRIPTION OF SYMBOLS 10 Multilayer film 110 Outer layer 120,140 Sand layer 130 Shrink layer 150 Inner layer 20,40 Packaging bag 210,220 Side seal part (easy peel)
230, 430 Vertical seal (easy peel)
240, 440 Non-seal part 300 Superposition part 310 Finger insertion part 320 Tip 410, 420 Lateral seal (strong seal)
450, 460 Notch 470, 480 Perforation

Claims (2)

It is a packaging bag that heat-seals the contents after filling, seals the contents, and heat-shrinks,
A thermoplastic resin capable of forming an easy peel on the inner layer and the outer layer, a thermoplastic resin that shrinks by applying heat to the intermediate layer, and a multilayer film in which polyethylene is laminated between the inner layer and the outer layer and the intermediate layer,
The inner layer and the outer layer are made of linear low density polyethylene,
The thermoplastic resin of the intermediate layer is made of biaxially stretched polyamide,
The polyethylene laminated between the inner layer and outer layer and the intermediate layer is made of low density polyethylene,
The packaging bag has an overlapping portion in which the multilayer film is curved into a cylindrical shape and its both end portions are overlapped,
Vertically in a state where a finger insertion part which is a band-like non-seal part with a width (10-20 mm) that can be picked with a finger is left on the distal end side of one side edge part which is the outer surface side in the overlapping part. Having a seal part,
A transverse seal part formed to intersect with both longitudinal ends of the longitudinal seal part,
The vertical seal portion is an easy peel having a heat seal strength of less than 10 N / 15 mm width according to JIS K6854.
The vertical seal portion is a cohesive peel easy-open seal,
The horizontal seal portion has a heat seal strength of 10 N / 15 mm width or more according to JIS K6854,
The non-sealing portion, the packaging bag, characterized in Rukoto to have a easily openable means for tearing the lateral direction. The packaging bag according to claim 1, further comprising an opening assisting unit that assists in cutting the cut cut by the easy-opening unit in a desired direction.