JP5541857B2 - Bifunctional (meth) acrylate with fluorene skeleton - Google Patents

Description

  The present invention relates to a novel bifunctional (meth) acrylate having a fluorene skeleton (specifically, a 9,9-bisphenylfluorene skeleton).

  For optical materials such as optical overcoat agent, hard coat agent, antireflection film, spectacle lens, optical fiber, optical waveguide, hologram, etc., polyfunctionality such as diacrylate of bisphenols (bisphenol A etc.) or its ethylene oxide adducts Acrylates are used. Such polyfunctional acrylates are required to have improved properties such as moisture resistance, heat resistance, and high refractive index.

  On the other hand, a compound having a 9,9-bisphenylfluorene skeleton such as bisphenolfluorene (BPF) is known to have an excellent function in heat resistance and the like, and such a compound is used as a polyfunctional acrylate raw material. It is also known.

  For example, Japanese Patent Laid-Open No. 4-325508 (Patent Document 1) discloses a copolymer of a composition capable of radical polymerization, the main component of which is a compound represented by the following formula (1), having a refractive index of 1. More than 60 plastic lens materials are disclosed.

(Wherein R ₁ and R ₂ are hydrogen or a methyl group, m and n are integers of 0 to 5)
In this document, as a compound represented by the formula (1), a compound obtained by reacting 9,9-bis (4-hydroxyphenyl) fluorene with (meth) acrylic acid chloride, or 9,9-bis (4- It describes compounds in which (meth) acrylic acid is reacted after addition of ethylene oxide or propylene oxide to (hydroxyphenyl) fluorene.

  JP-A-2005-162785 (Patent Document 2) discloses a resin composition composed of a compound having a fluorene skeleton and a thermoplastic resin. , 9-bis (4- (meth) acryloyloxyphenyl) fluorene, 9,9-bis (3-methyl-4- (meth) acryloyloxyphenyl) fluorene, 9,9-bis (3-methyl-4- ( It is described that bifunctional (meth) acrylates such as 2- (meth) acryloyloxyethoxy) phenyl) fluorene can be used.

Since the (meth) acrylates described in these documents have a 9,9-bisphenylfluorene skeleton, compared to conventional (meth) acrylates such as di (meth) acrylates of bisphenols or ethylene oxide adducts thereof. Various properties can be improved, such as a higher refractive index. However, some of the (meth) acrylates described in these documents are not sufficient in terms of handling properties, such as viscosity is too high, and further development of (meth) acrylates with excellent practicality is expected. .
JP-A-4-325508 (Claim 1, paragraph number [0011]) JP 2005-162785 A (Claim 1, paragraph numbers [0047], [0048])

  Accordingly, an object of the present invention is to provide a novel fluorene skeleton-containing bifunctional (meth) acrylate and a resin composition thereof excellent in handling properties even if they have a fluorene skeleton (9,9-bisphenylfluorene skeleton). It is to provide.

  Another object of the present invention is to provide a cured product formed of a novel bifunctional (meth) acrylate having low viscosity and excellent handling properties and having excellent properties such as high refractive index and high hardness. .

  As a result of intensive studies to achieve the above-mentioned problems, the present inventors have a novel fluorene skeleton containing a combination of a 9,9-bis (monoalkylphenyl) fluorene skeleton and a branched oxyalkylene group (such as an oxypropylene group). Although the bifunctional (meth) acrylate has a 9,9-bisphenylfluorene skeleton, it has been found that it has excellent handling properties, and the present invention has been completed.

  That is, the compound of the present invention is a compound represented by the following formula (1).

(Wherein R ¹ represents a cyano group, a halogen atom or an alkyl group, R ² represents a branched alkylene group, R ³ represents a hydrogen atom or a methyl group, R ⁴ represents an alkyl group, and k represents 0 to 0) An integer of 4 and m is an integer of 1 or more.)
In the formula (1), R ² may be, for example, a branched C _3-4 alkylene group (eg, propylene group), and m may be about 1 to 4. In the formula (1), R ⁴ may be a C _1-4 alkyl group (for example, a methyl group). In particular, in the formula (1), R ² may be a propylene group, m may be 1 to 2, and R ⁴ may be a methyl group.

  Typical compounds represented by the formula (1) include compounds represented by the following formula (1A).

(Wherein R ¹ , R ² , R ³ , R ⁴ , k and m are the same as above).
In particular, the compound represented by the formula (1) is 9,9-bis [4- (2- (meth) acryloyloxypropoxy) -3-C _1-4 alkylphenyl] fluorene {for example, 9,9- Bis [4- (2- (meth) acryloyloxypropoxy) -3-methylphenyl] fluorene etc.} may be used.

  The present invention also includes a mixed compound (mixture) of the compound and a compound represented by the following formula (3).

(In the formula, R ¹ , R ² , R ³ , R ⁴ , k, and m are the same as described above.)
The present invention also includes a resin composition containing the compound (including the mixed compound) (for example, a resin composition containing the compound and a polymerization initiator, the compound, other polyfunctional (meth) acrylates, and polymerization). Also included are resin compositions containing initiators.

  Furthermore, the hardened | cured material of the said compound (or the said resin composition) is also contained in this invention.

  In the present specification, the “class” such as a compound name includes a case of “having no substituent” and a case of “having a substituent”, and “may have a substituent”. May mean.

  The novel fluorene skeleton-containing bifunctional (meth) acrylate and the resin composition thereof of the present invention are excellent in handling properties even if they have a fluorene skeleton (9,9-bisphenylfluorene skeleton). Therefore, the cured product of (meth) acrylate (or resin composition thereof) of the present invention is formed of a novel bifunctional (meth) acrylate having low viscosity and excellent handling properties, and has high heat resistance, high refractive index, It has excellent properties such as high hardness and high practical value.

  The compound of the present invention (sometimes referred to as fluorene skeleton-containing bifunctional (meth) acrylate, di (meth) acrylate, (meth) acrylate, etc.)) is a compound represented by the following formula (1).

(Wherein R ¹ represents a substituent, R ² represents a branched alkylene group, R ³ represents a hydrogen atom or a methyl group, R ⁴ represents an alkyl group, k represents an integer of 0 to 4, and m represents (It is an integer of 1 or more.)
In the above formula (1), examples of the substituent represented by the group R ¹ include a cyano group, a halogen atom (a fluorine atom, a chlorine atom, a bromine atom, etc.), a hydrocarbon group [for example, an alkyl group, an aryl group ( Non-reactive substituents such as a C _6-10 aryl group such as a phenyl group], and the like, and particularly a halogen atom, a cyano group or an alkyl group (particularly an alkyl group). Examples of the alkyl group include C _1-6 alkyl groups such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, and a t-butyl group (for example, a C _1-4 alkyl group, particularly a methyl group). . In addition, when k is plural (two or more), the groups R ¹ may be different from each other or the same. Further, the groups R ¹ substituted on the two benzene rings constituting the fluorene (or fluorene skeleton) may be the same or different. Further, the bonding position (substitution position) of the group R ¹ with respect to the benzene ring constituting the fluorene is not particularly limited. The preferred substitution number k is 0 to 1, in particular 0. In the two benzene rings constituting fluorene, the number of substitutions k may be the same or different from each other.

In the formula (1), examples of the branched alkylene group represented by the group R ² include branched C _3-6 alkylene groups such as a propylene group (or 1,2-propanediyl group) and 1,2-butanediyl group. A branched C _3-4 alkylene group is preferable, and a propylene group is more preferable. In addition, when m is 2 or more, the branched alkylene group may be composed of different branched alkylene groups, and may be generally composed of the same branched alkylene group. In the two benzene rings, the groups R ² may be the same or different, and may usually be the same.

The number (number of added moles) m of the oxyalkylene group (OR ² ) can be selected from the range of about 1 to 15 (eg, 1 to 12), for example, 1 to 8, preferably 1 to 6, and more preferably 1 -4 (e.g. 1-3), especially 1-2. The number of substitutions m may be the same or different in different benzene rings. Moreover, in two benzene rings, the total (mx2) of oxyalkylene groups can be selected from the range of about 2 to 30 (for example, 2 to 24), for example, 2 to 16 (for example, 2 to 14), Preferably it may be 2 to 12 (eg 2 to 10), more preferably 2 to 8 (eg 2 to 6), especially 2 to 4 (eg 2 to 3).

In the formula (1), examples of the alkyl group represented by the group R ⁴ include C, such as methyl group, ethyl group, propyl group, isopropyl group, butyl group, s-butyl group, and t-butyl group. _1-20 alkyl group (for example, C _1-10 alkyl group), preferably C _1-8 alkyl group (for example, C _1-6 alkyl group), more preferably C _1-4 alkyl group (for example, C _{1- 1 3} alkyl groups), in particular methyl groups. The groups R ⁴ substituted on different benzene rings may be the same or different from each other, and may usually be the same.

  Typical compounds represented by the formula (1) include 9,9-bis ((meth) acryloyloxy-branched alkoxy-monoalkylphenyl) fluorenes (a compound in which m is 1 in the formula (1)). ), 9,9-bis ((meth) acryloyloxy-poly branched alkoxy-monoalkylphenyl) fluorenes (compounds in which m is 2 or more in the formula (1)).

9,9-bis ((meth) acryloyloxy-branched alkoxy-monoalkylphenyl) fluorenes include, for example, 9,9-bis ((meth) acryloyloxy-branched C _3-4 alkoxy-monoalkylphenyl) fluorene. {E.g., 9,9-bis [4- (2- (meth) acryloyloxypropoxy) -3-methylphenyl] fluorene, 9,9-bis [4- (2- (meth) acryloyloxypropoxy) -3 9,9-bis ((meth) acryloyloxy-branched C _3-4 such as -ethylphenyl] fluorene, 9,9-bis [4- (2- (meth) acryloyloxypropoxy) -2-methylphenyl] fluorene alkoxy - mono _{C 1-4} alkyl phenyl) fluorene, preferably 9,9-bis (2- (meth) acryloyl Kishipuropokishi - and the like mono _{C 1-4} alkylphenyl) fluorene}.

9,9-bis ((meth) acryloyloxy-poly branched alkoxy-monoalkylphenyl) fluorenes correspond to the 9,9-bis ((meth) acryloyloxy-branched alkoxy-monoalkylphenyl) fluorenes. , M is 2 or more, for example, 9,9-bis ((meth) acryloyloxy-dibranched C _3-4 alkoxy-monoalkylphenyl) fluorenes {eg, 9,9-bis {4- [2 9,9-bis ((meth) acryloyloxy-dibranched C _3-4 alkoxy-mono C _1-4 alkylphenyl) such as-(2- (meth) acryloyloxypropoxy) propoxy] -3-methylphenyl} fluorene Fluorene, preferably 9,9-bis [2- (2- (meth) acryloyloxypropoxy) propoxy- Bruno _{C 1-4} and the like alkyl phenyl] fluorene}.

Among these, preferable compounds represented by the formula (1) include compounds in which the substitution position of R ⁴ is the 3-position in the formula (1), that is, compounds represented by the following formula (1A). .

(Wherein R ¹ , R ² , R ³ , R ⁴ , k and m are the same as above).
Particularly preferable compounds represented by the formula (1) include compounds in which R ² is a propylene group among the compounds represented by the formula (1A), such as 9,9-bis [4- (2- (Meth) acryloyloxypropoxy) -3-alkylphenyl] fluorenes {eg, 9,9-bis [4- (2- (meth) acryloyloxypropoxy) -3-C _1-4 alkylphenyl] fluorene}, 9,9-bis {4- [2- (2- (meth) acryloyloxypropoxy) propoxy] -3-alkylphenyl} fluorenes {for example, 9,9-bis {4- [2- (2- (meta ) Acryloyloxypropoxy) propoxy] -3-C _1-4 alkylphenyl} fluorene} and the like.

(Method for producing compound represented by formula (1))
The compound represented by the formula (1) is not particularly limited, but can be produced by reacting a compound represented by the following formula (2) with (meth) acrylic acid or a derivative thereof.

(Wherein R ¹ , R ² , R ⁴ , k, m are the same as above)
Examples of the compound represented by the formula (2) include compounds corresponding to the compound represented by the formula (1), for example, 9,9-bis (hydroxy-branched alkoxy-monoalkylphenyl) fluorenes {for example, 9,9-bis (hydroxy-branched C _3-4 alkoxy-mono C _1-4 alkylphenyl) fluorene such as 9,9-bis [4- (2-hydroxypropoxy) -3-methylphenyl] fluorene, preferably 9,9-bis (hydroxy-branched C _3-4 alkoxy-monoalkylphenyl) fluorenes such as 9,9-bis (2-hydroxypropoxy-monoC _1-4 alkylphenyl) fluorene}, 9,9-bis (Hydroxy-poly-branched alkoxy-monoalkylphenyl) fluorenes {eg, 9,9-bis [4- {2- (2-hydro 9,9-bis (hydroxy-dibranched C _3-4 alkoxy-mono C _1-4 alkylphenyl) fluorene such as xypropoxy) propoxy} -3-methylphenyl] fluorene, preferably 9,9-bis [2- 9,9-bis (hydroxy-dibranched C _3-4 alkoxy-monoalkylphenyl) fluorenes such as (2-hydroxypropoxy) propoxy-mono C _1-4 alkylphenyl] fluorene} and the like.

Alkylene wherein the compound represented by formula (2) is not particularly limited, for example, corresponding to (1) a compound represented by the following formula (2A), an alkylene oxide or a radical R ² corresponds to the radical R ² It can be obtained by a method of reacting with carbonate, (2) a method of reacting a compound represented by the following formula (2B) with a compound represented by the following formula (2C), or the like.

(Wherein R ¹ , R ² , R ⁴ , k, m are the same as above)
(Method (1))
In the method (1), examples of the compound represented by the formula (2A) include compounds corresponding to the compound represented by the formula (2), for example, 9,9-bis (hydroxy-monoalkylphenyl) fluorenes. [For example, 9,9-bis (hydroxy-mono C _1-4 alkylphenyl) fluorene such as 9,9-bis (4-hydroxy-3-methylphenyl) fluorene] and the like.

  The compound represented by the formula (2A) may be a commercially available product. For example, an acid (for example, an inorganic acid such as hydrochloric acid or sulfuric acid, a solid acid) or a thiol (mercaptocarboxylic acid) may be used. Manufactured by a method of reacting the compound represented by the formula (2B) (fluorenones) and the corresponding phenols (for example, cresol such as o-cresol and p-cresol) in the presence of an acid, etc. You may use what you did.

  The purity of the compound represented by the formula (2A) used as a raw material is not particularly limited, but is usually 95% by weight or more, and preferably 99% by weight or more.

In method (1), the alkylene oxide corresponding to the group R ² may be a branched C _3-6 alkylene oxide such as propylene oxide or butylene oxide (1,2-epoxybutane), preferably a branched C _3-4 alkylene. And oxides. Examples of the alkylene carbonate corresponding to the group R ² include branched C _3-6 alkylene carbonates such as propylene carbonate and butylene carbonate, preferably branched C _3-4 alkylene carbonates. When alkylene oxide or alkylene carbonate is reacted, a (poly) oxyalkylene unit can be introduced through the hydroxyl group of the compound represented by the formula (2A). When alkylene carbonate is used, oxyalkylene units (branched alkoxy units) are introduced by the decarboxylation reaction after addition of alkylene carbonate.

In the method (1), the amount of alkylene carbonate corresponding to the alkylene oxide or a radical R ² corresponds to the group R ² may be adjusted according to the number of alkylene oxide units to be added is represented by the formula (2A) For example, 2 to 50 mol (eg 2 to 40 mol), preferably 2 to 30 mol (eg 2 to 25 mol), more preferably 2 to 20 mol (eg 2 to 15 mol) per mol of the compound. Mol) degree.

  The reaction may be carried out in the absence of a catalyst, but can usually be carried out in the presence of a catalyst. Examples of the catalyst include a base catalyst and an acid catalyst, and usually a base catalyst can be used. Base catalysts include metal hydroxides (alkali metals such as sodium hydroxide or alkaline earth metal hydroxides), metal carbonates (alkali metals such as sodium carbonate or alkaline earth metal carbonates, sodium hydrogen carbonate, etc.) Inorganic bases such as alkali metals or alkaline earth metal hydrogen carbonates; amines [for example, tertiary amines (trialkylamines such as triethylamine, aromatic tertiary amines such as N, N-dimethylaniline) , Heterocyclic tertiary amines such as 1-methylimidazole, etc.], and organic bases such as carboxylic acid metal salts (such as alkali metal acetates or alkaline earth metal salts such as sodium acetate and calcium acetate). The catalyst (base catalyst) may be used alone or in combination of two or more.

  The usage-amount of a catalyst can be adjusted according to the kind of catalyst, for example, 0.001-1 weight part (for example, 0.003-0.3.0) with respect to 1 weight part of compounds represented by the said Formula (2A). 5 parts by weight), preferably 0.005 to 0.3 parts by weight, more preferably about 0.01 to 0.1 parts by weight.

The reaction may be performed in a solvent. The solvent is not particularly limited and can be selected according to the raw material to be used. For example, when using an alkylene oxide, an ether solvent (dialkyl ethers such as diethyl ether, cyclic ethers such as tetrahydrofuran and dioxane, Anisole, etc.), halogen solvents (halogenated hydrocarbons such as methylene chloride, chloroform, carbon tetrachloride), hydrocarbon solvents (aromatic hydrocarbons such as benzene, toluene, xylene, etc.). When alkylene carbonate is used, in addition to the solvents exemplified above, alcohols (C _1-4 alcohols such as methanol and ethanol, (poly) C ₂ such as ethylene glycol, propylene glycol, diethylene glycol and dipropylene glycol) are used. _-3 alkylene glycol, etc.) may be used. The solvents may be used alone or in combination of two or more. The amount of the solvent to be used is, for example, 1 to 30 parts by weight, preferably 1.5 to 20 parts by weight, more preferably about 2 to 10 parts by weight with respect to 1 part by weight of the compound represented by the formula (2A). It may be.

  The reaction is often performed at, for example, about 0 to 170 ° C., preferably 10 to 150 ° C., more preferably about 20 to 130 ° C., depending on the type of compound to be added (alkylene oxide, alkylene carbonate) and the like. In particular, when alkylene carbonate is used, in order to efficiently perform the decarboxylation reaction, for example, the reaction is often performed at 70 to 150 ° C, preferably about 80 to 120 ° C. The reaction time is, for example, 30 minutes to 48 hours, usually 1 to 24 hours, preferably about 2 to 10 hours.

  The reaction may be performed with stirring, may be performed in air or in an inert atmosphere (such as nitrogen or a rare gas), or may be performed under normal pressure or under pressure. Moreover, you may react, removing the gas (carbon dioxide etc.) which generate | occur | produces as needed.

  The target product (compound represented by formula (2)) may be purified from the reaction mixture after completion of the reaction using a conventional purification method (extraction, crystallization, etc.).

(Method (2))
In the method (2), examples of the compound represented by the formula (2B) include fluorenones such as 9-fluorenone. The purity of the compound represented by formula (2B) used in the reaction (fluorenones) is not particularly limited, but may be usually 95% by weight or more, preferably 99% by weight or more.

In the method (2), examples of the compound represented by the formula (2C) include branched alkylene glycol mono (monoalkylphenyl) ethers {for example, branched C _3-4 alkylene glycol monotolyl ether [2- Branched C _3-4 alkylene glycol mono (mono C _1-4 alkylphenyl) ether, etc.] such as (2-methylphenoxy) propanol etc.} Alcohols wherein m is 1 in the formula (2C); Glycol mono (monoalkylphenyl) ethers {e.g., di-branched C _3-4 alkylene glycol monotolyl ethers (such as dipropylene glycol monotolyl ether) and the like di-branched C _3-4 alkylene glycol mono (mono C _1-4 alkyl Phenyl) ether, etc.} m is and alcohols is 2 or more at 2C).

  The purity of the compound (alcohol) represented by the formula (2C) is not particularly limited, but is usually 95% by weight or more, preferably 97% by weight or more, more preferably 99% by weight or more. Good.

  The reaction may be performed in the presence of a catalyst. Usually, an acid catalyst can be used as the catalyst. Examples of the acid catalyst include inorganic acids [sulfuric acid, hydrogen chloride, hydrochloric acid (5 to 36% by weight, preferably about 20 to 36% by weight aqueous hydrogen chloride solution), phosphoric acid and the like], organic acids [sulfonic acid (methanesulfone). And alkane sulfonic acids such as acids). The sulfuric acid includes dilute sulfuric acid (for example, about 30 to 90% by weight sulfuric acid), concentrated sulfuric acid (for example, sulfuric acid having a concentration of 90% by weight or more), fuming sulfuric acid, and the like, and can be converted into sulfuric acid in the reaction system. For example, sulfur trioxide may be used as the sulfuric acid precursor. A solid acid (such as a cation exchange resin) may be used. The acid catalysts may be used alone or in combination of two or more.

In addition to the acid catalyst, thiols as a co-catalyst may be used in combination. Examples of thiols include conventional thiols that function as promoters, such as mercaptocarboxylic acids (mercaptoacetic acid, β-mercaptopropionic acid, α-mercaptopropionic acid, thioglycolic acid, mercaptosuccinic acid, mercaptobenzoic acid, etc.) Thiocarboxylic acid (thioacetic acid, thiooxalic acid, etc.), alkyl mercaptan (methyl mercaptan, ethyl mercaptan, propyl mercaptan, isopropyl mercaptan, n-butyl mercaptan, dodecyl mercaptan, etc., C _1-16 alkyl mercaptan (especially C _1-4 alkyl mercaptan) Etc.), aralkyl mercaptan (such as benzyl mercaptan) or a salt thereof. Examples of the salt include alkali metal salts (sodium salt and the like). Among these thiols, mercapto C _2-6 carboxylic acid (for example, β-mercaptopropionic acid) is preferable. Thiols can be used alone or in combination of two or more.

  The reaction (liquid phase reaction) is carried out using a reaction solvent such as an aromatic solvent (aromatic hydrocarbons such as benzene, toluene and xylene, anisole, etc.), an ether solvent (dialkyl ethers such as diethyl ether, tetrahydrofuran, etc. , Cyclic ethers such as dioxane, etc.), halogen solvents (halogenated hydrocarbons such as methylene chloride, chloroform, carbon tetrachloride, etc.) and the like.

  Although reaction temperature is not specifically limited, For example, 20-200 degreeC, Preferably it is 40-180 degreeC, More preferably, about 50-150 degreeC may be sufficient. Moreover, reaction time can be adjusted according to the kind of raw material, reaction temperature, the density | concentration in a solvent, etc., for example, 30 minutes-48 hours, Usually 1 to 24 hours, Preferably it may be about 1 to 10 hours. Good.

  The reaction may be performed with stirring, may be performed in air or in an inert atmosphere (nitrogen, rare gas, etc.), or may be performed at normal pressure or under pressure. The reaction may be performed while dehydrating.

  The target product (compound represented by formula (2)) may be purified from the reaction mixture after completion of the reaction using a conventional purification method (extraction, crystallization, etc.).

  As described above, the compound represented by the formula (2) is obtained. The compound represented by the formula (2) obtained by the reaction (or the compound used for the reaction with (meth) acrylic acid or a derivative thereof) may be a single compound, but the formula (2 It may be a mixture containing a plurality of compounds represented by For example, the compound represented by the formula (2) is a mixture of a compound in which m is 1 in the formula (2) and a compound in which m is 2 or more (for example, 2) in the formula (2). There may be. In such a mixture, the proportion of the single compound is, for example, 70% by weight or more (for example, 75 to 99.9% by weight), preferably 80% by weight or more (for example, 85 to 99.7% by weight), Preferably, it may be about 90% by weight or more (for example, 95 to 99.5% by weight).

In the (meth) acrylic acid or derivative thereof used for the reaction with the compound represented by the formula (2), examples of the (meth) acrylic acid derivative include (meth) acrylic acid lower alkyl ester (for example, (meth) ) Methyl acrylate, ethyl (meth) acrylate, C _1-4 alkyl (meth) acrylate such as butyl (meth) acrylate), (meth) acrylic acid halide (for example, (meth) acrylic acid chloride, etc.), Examples include (meth) acrylic anhydride.

  The ratio of (meth) acrylic acid or a derivative thereof is, for example, 2 to 20 mol, preferably 2.2 to 10 mol, more preferably 2.5 to 1 mol of the compound represented by the following formula (2). About 5 mol may be sufficient.

In the reaction, a catalyst (such as an acid catalyst or a base catalyst) may be used as appropriate. The acid catalyst is not particularly limited as long as it is an esterification acid catalyst. For example, inorganic acid (sulfuric acid, hydrochloric acid, phosphoric acid, etc.), organic acid [sulfonic acid (methanesulfonic acid, ethanesulfonic acid, trifluoromethanesulfonic acid, etc.) And alkanesulfonic acid, and arenesulfonic acid such as p-toluenesulfonic acid), etc.], and solidified acid [supporting acid (inorganic acid such as sulfuric acid, phosphoric acid, heteropoly acid, organic acid) on a carrier] Solid acid (such as solid phosphoric acid)], cation exchange resin, metal oxide (such as ZnO), metal halide (such as CuCl ₂ ), metal salt catalyst [metal sulfate (such as NiSO ₄ ), metal phosphorus Acid salts (such as phosphates of transition metals such as Zr and Ti), metal nitrates (such as Zn (NO ₃ ) ₂ · 6H ₂ O), etc.], natural minerals (acid clay, bentonite, kao, etc.) Also included are solid acid catalysts such as phosphorus and montmorillonite). The acid catalysts may be used alone or in combination of two or more.

  Examples of the base include metal carbonate (alkali metal or alkaline earth metal carbonate such as sodium carbonate, alkali metal or alkaline earth metal hydrogen carbonate such as sodium hydrogen carbonate), carboxylate metal salt (sodium acetate, Inorganic bases such as alkali metal acetates or alkaline earth metal salts such as calcium acetate), metal hydroxides (alkali metal hydroxides such as sodium hydroxide, alkaline earth metal hydroxides such as calcium hydroxide) Amines [for example, tertiary amines (trialkylamines such as triethylamine, triisopropylamine, tributylamine, aromatic tertiary amines such as N, N-dimethylaniline, and heterocyclic tertiary amines such as pyridine; And an organic base such as amine). The bases may be used alone or in combination of two or more.

  The amount of the catalyst (acid catalyst, base) used depends on the type of the catalyst, but is, for example, 0.01 to 10 mol, preferably 0 with respect to 1 mol of the compound represented by the formula (2). It may be about 0.05 to 5 mol, more preferably about 0.1 to 3 mol.

  Moreover, you may perform reaction in presence of a polymerization inhibitor (thermal polymerization inhibitor) as needed. Polymerization inhibitors include hydroquinones (eg, hydroquinone; hydroquinone monoalkyl ethers such as hydroquinone monomethyl ether (methoquinone)), catechols (eg, alkyl catechols such as t-butylcatechol), amines (eg, diphenylamine) Etc.), 2,2-diphenyl-1-picrylhydrazyl, 4-hydroxy-2,2,6,6-tetramethylpiperazine-1-oxyl and the like. The polymerization inhibitors may be used alone or in combination of two or more.

  The amount of the polymerization inhibitor used is, for example, 0.1 to 10 parts by weight, preferably 0.3 to 8 parts by weight, more preferably 0.5 to 100 parts by weight with respect to 100 parts by weight of (meth) acrylic acid or its derivative. It may be about 5 parts by weight.

  The reaction may be performed in the absence of a solvent or in a solvent. Solvents (organic solvents) include hydrocarbons (aliphatic hydrocarbons such as hexane, heptane, and octane, aromatic hydrocarbons such as benzene, toluene, and xylene), halogenated hydrocarbons (methylene chloride, chloroform, etc.) And carbon tetrachloride), ether solvents (dialkyl ethers such as diethyl ether, cyclic ethers such as tetrahydrofuran and dioxane, anisole and the like), ketones (dialkyl ketones such as acetone and methyl ethyl ketone), and the like. The solvents may be used alone or in combination of two or more. In addition, when the said catalyst is a liquid, you may use the said catalyst as a solvent.

  The reaction temperature and reaction time can be appropriately selected according to the type of (meth) acrylic acid or its derivative used. The reaction time is, for example, 30 minutes to 48 hours, usually 1 to 36 hours, preferably about 2 to 24 hours.

  The reaction may be performed while refluxing, or may be performed while removing by-product water and alcohols. The reaction may be performed with stirring, may be performed in air or in an inert atmosphere (such as nitrogen or a rare gas), and may be performed under normal pressure, increased pressure, or reduced pressure. In particular, when the reaction is performed under reduced pressure, coloring can be reduced and the reaction time can be shortened.

  In addition, the produced | generated compound (compound represented by said Formula (1)) combined separation means, such as filtration, concentration, extraction, crystallization, recrystallization, column chromatography, etc., and these by the usual method. Separation and purification may be performed by separation means.

  In addition, the compound obtained by reaction may be a single compound of the compound represented by the formula (1) or a mixture containing a plurality of compounds represented by the formula (1). For example, the compound represented by the formula (1) is a mixture of a compound in which m is 1 in the formula (1) and a compound in which m is 2 or more (for example, 2) in the formula (1). There may be. In such a mixture, the ratio of the single compound among the compounds represented by the formula (1) is, for example, 50% by weight or more (for example, 55 to 99.9% by weight), preferably in terms of solid content. May be 60% by weight or more (for example, 65 to 99.5% by weight), more preferably 70% by weight or more (for example, 75 to 99% by weight).

  In addition, the compound produced by the reaction may be a compound that does not belong to the category of the compound represented by the formula (1) [for example, 2 in the formula (1), as long as the properties as a product are not impaired. A compound in which one m is 0; in the formula (1), one m is 0 and the other m is 1 or more; 1 mol per 1 mol of the compound represented by the formula (2) (Meth) acrylic acid or a derivative thereof added (reacted) (referred to as compound A) and the like]. Compound A is represented by the following formula (3).

(In the formula, R ¹ , R ² , R ³ , R ⁴ , k, and m are the same as described above.)
In such a mixture, the ratio of the compound represented by the formula (1) to the whole mixture is, for example, 50% by weight or more (for example, 53 to 99.9% by weight), preferably 55% in terms of solid content. % Or more (for example, 57 to 99.5% by weight), more preferably about 60% by weight or more (for example, 62 to 99% by weight).

In the mixture, the ratio between the compound represented by the formula (1) and the compound A is, for example, the former / the latter (molar ratio) = 97/3 to 40/60, preferably 95/5 to 45. / 55, more preferably 90/10 to 50/50, particularly about 88/12 to 55/45 (for example, 85/15 to 60/40). The compound represented by the formula (1) alone has a low viscosity and excellent handling properties compared to a compound in which R ² is a linear alkylene group (such as an ethylene group) in the formula (1). However, handling property can be further improved by constituting the mixture with Compound A. Therefore, the present invention also includes a mixture containing the compound represented by the formula (1) (in particular, a mixed compound of the compound represented by the formula (1) and the compound A).

Such a mixture (mixed compound) may be a mixture of the compound represented by the formula (1) and the compound A, but usually, as described above, the compound represented by the formula (2) , (Meth) acrylic acid or a derivative thereof can be produced. Incidentally, Compound A, the above formula (1) as compared with the case where R ² to produce a like compound is a straight-chain alkylene group (such as ethylene group) in, appears likely to be formed.

[Use of compound represented by formula (1)]
The compound of the present invention (the compound represented by the formula (1) or the compound obtained by the method) (including the mixture (or mixed compound), the same applies hereinafter) has a fluorene skeleton (specifically 9,9-bis). (Monoalkylaryl) fluorene skeleton) and has characteristics specific to the fluorene skeleton such as high heat resistance and high refractive index. Moreover, despite having such a fluorene skeleton, it has excellent handling properties.

  The viscosity of the compound of the present invention is, for example, 80000 mPa · s or less (eg, 3000 to 70000 mPa · s), preferably 60000 mPa · s or less (eg, 5000 to 55000 mPa · s), more preferably 50000 mPa · s at 25 ° C. Or less (for example, 10000 to 45000 mPa · s), particularly 40000 mPa · s or less (for example, 15000 to 35000 mPa · s), and usually about 10000 to 50000 mPa · s (for example, 20000 to 45000 mPa · s). Also good. The viscosity can be measured using, for example, a TV-22 viscometer (cone plate type), for example, as in the method described in the examples described later.

  As described above, the compound of the present invention has characteristics such as high heat resistance, is excellent in handling properties, and can be suitably used as a heat or photocurable (meth) acrylic resin. The heat or photocurable resin may usually constitute a resin composition containing a polymerization initiator and the like. The present invention also includes a resin composition containing such a compound.

The heat or photocurable (meth) acrylic resin (heat or photocurable (meth) acrylic resin component) may be composed of only the above compound, or may be combined with other polyfunctional (meth) acrylates. Good. When the heat or photocurable (meth) acrylic resin is composed of the compound of the present invention alone, the fluorene skeleton can be introduced into the cured product at a high concentration. Other polyfunctional (meth) acrylates include, for example, bifunctional (meth) acrylate {alkylene glycol di (meth) acrylate [ethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, 1,4- C _2-10 alkylene glycol di (meth) acrylate such as butanediol di (meth) acrylate], polyalkylene glycol di (meth) acrylate [di to tetraethylene glycol di (meth) acrylate, polyethylene glycol di (meth) acrylate , di or tetrapropylene glycol di (meth) acrylate, poly C _2-4 alkylene glycol di (meth) acrylates such as polytetramethylene glycol di (meth) acrylate, etc.], bisphenol a (or Di C _2-3 alkylene oxide adduct) of (meth) acrylates}, trifunctional or higher polyfunctional (meth) acrylate [e.g., glycerol tri (meth) acrylate, trimethylolpropane tri (meth) acrylate, tris ( Tri- or tetraol tri- or tetra- (meth) acrylates such as hydroxyethyl) isocyanurate tri (meth) acrylate, pentaerythritol tri- or tetra (meth) acrylate; ditrimethylolpropane tetra (meth) acrylate; dipentaerythritol tetra-hexa (Meth) acrylate, etc.], urethane (meth) acrylate, epoxy (meth) acrylate, polyester (meth) acrylate, poly having a fluorene skeleton that does not belong to the category of the compound represented by the formula (1) 9,9- such as functional (meth) acrylate {9,9-bis (4- (meth) acryloyloxyphenyl) fluorene, 9,9-bis (4- (meth) acryloyloxy-3-methylphenyl) fluorene Bis ((meth) acryloyloxyphenyl) fluorenes; 9,9-bis [(meth) acryloyloxy such as 9,9-bis [4- (2- (meth) acryloyloxyethoxy) -3-methylphenyl] fluorene (Poly) ethoxyphenyl] fluorenes, etc.}. These other polyfunctional (meth) acrylates may be used alone or in combination of two or more.

  The ratio of the other polyfunctional (meth) acrylate is, for example, 1 to 100 parts by weight, preferably 2 to 60 parts by weight, more preferably 5 to 100 parts by weight of the compound represented by the formula (1). About 30 parts by weight may be used.

  In addition, the said resin composition may contain the polymerization initiator, the diluent, etc. as needed.

  The polymerization initiator includes a thermal polymerization initiator and a photopolymerization initiator. You may combine a thermal-polymerization initiator and a photoinitiator. Examples of thermal polymerization initiators include dialkyl peroxides (di-t-butyl peroxide, dicumyl peroxide, etc.), diacyl peroxides [dialkanoyl peroxide (such as lauroyl peroxide), and dialoyl peroxide (benzoyl peroxide). Organic peroxides such as peroxide esters (such as t-butyl peracetate), ketone peroxides, peroxycarbonates, peroxyketals; azonitrile compounds [2,2′-azobis ( Isobutyronitrile) and the like, and azo compounds such as azoamide compounds and azoamidine compounds. You may use a thermal-polymerization initiator individually or in combination of 2 or more types.

  Examples of the photopolymerization initiator include benzoins (benzoin alkyl ethers such as benzoin, benzoin methyl ether, benzoin ethyl ether, and benzoin isopropyl ether) and acetophenones (acetophenone, 2-hydroxy-2-methyl-1-phenyl). Propan-1-one), aminoacetophenones {2-methyl-1- [4- (methylthio) phenyl] -2-morpholinoaminopropanone-1}, anthraquinones (anthraquinone, 2-methylanthraquinone, etc.), Thioxanthones (2,4-dimethylthioxanthone, 2,4-diethylthioxanthone, 2-chlorothioxanthone, etc.), ketals (acetophenone dimethyl ketal, benzyldimethyl ketal, etc.), benzophenones Benzophenone), such as xanthones can be exemplified. These photopolymerization initiators may be used alone or in combination of two or more.

  Moreover, you may combine a photoinitiator with a photosensitizer. As photosensitizers, tertiary amines {eg, trialkylamines, trialkanolamines (such as triethanolamine), ethyl N, N-dimethylaminobenzoate [such as ethyl p- (dimethylamino) benzoate] , N, N-dimethylaminobenzoic acid amyl [p- (dimethylamino) benzoic acid amyl etc.] and other dialkylaminobenzoic acid alkyl esters, 4,4-bis (diethylamino) benzophenone (Michler's ketone) and other bis (dialkylamino) Conventional photosensitizers such as benzophenone, dialkylaminobenzophenone such as 4- (dimethylamino) benzophenone} and the like. The photosensitizers may be used alone or in combination of two or more.

  The amount of the polymerization initiator (and the total amount of the photosensitizer) is 0.1 to 30 parts by weight (for example, 1 to 30 parts by weight) with respect to 100 parts by weight of the heat or photocurable (meth) acrylic resin. 1 to 20 parts by weight (for example, 5 to 15 parts by weight), more preferably about 1.5 to 10 parts by weight. Moreover, the usage-amount of a photosensitizer is 5-200 weight part with respect to 100 weight part of polymerization initiators (photoinitiator), Preferably it is 10-150 weight part, More preferably, it is about 20-100 weight part. It may be.

Diluents include reactive diluents and non-reactive diluents (solvents). The reactive diluent is not particularly limited, and is a polymerizable monomer such as alkyl (meth) acrylate [methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, etc. C _1-20 alkyl (meth) acrylate, preferably C _1-10 alkyl (meth) acrylate], cycloalkyl methacrylate (meth) acrylic acid C _5-8 cycloalkyl such as cyclohexyl (meth) acrylate Etc.], aryl (meth) acrylate [phenyl (meth) acrylate, etc.], hydroxyalkyl (meth) acrylate [(2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-hydroxybutyl ( Hydroxy C _2-10 alkyl (meth) acrylate such as (meth) acrylate ), (Poly) oxyalkylene glycol mono (meth) acrylate (diethylene glycol mono (meth) acrylate, methoxytetraethylene glycol mono (meth) acrylate, polyethylene glycol mono (meth) acrylate and other (poly) oxy C _2-6 alkylene Glycol mono (meth) acrylate), alkoxyalkyl (meth) acrylate [2- (meth) acrylic acid 2-methoxyethyl, (meth) acrylic acid 3-methoxybutyl (meth) acrylic acid C _1-4 alkoxyalkyl, etc.], N-substituted (meth) acrylamide (N, N-diC _1-4 alkyl (meth) acrylamide such as N, N-dimethyl (meth) acrylamide, N-hydroxy C _1-4 such as N-methylol (meth) acrylamide Alkyl ( (Meth) acrylamide), aminoalkyl (meth) acrylate (N, N-dimethylaminoethyl acrylate, etc.), glycidyl (meth) acrylate, (meth) acrylic monomers such as tetrahydrofurfuryl (meth) acrylate, non- (meth) An acrylic monomer (for example, an aromatic vinyl monomer (such as styrene)) can be suitably used, and these compounds may be used alone or in combination of two or more.

  The ratio of the reactive diluent is, for example, 1 to 1000 parts by weight, preferably 5 to 500 parts by weight, and more preferably 10 to 200 parts by weight with respect to 100 parts by weight of the heat or photocurable (meth) acrylic resin. It may be a degree.

  Examples of the solvent include aliphatic hydrocarbons such as hexane, heptane, and octane; ketones such as ethyl methyl ketone and cyclohexanone; aromatic hydrocarbons such as toluene and xylene; cellosolve, methyl cellosolve, carbitol, and methylcarbide. Glycol ethers such as Tol, Propylene glycol monomethyl ether; Carboxylic acid esters (Acetic esters such as methyl acetate, ethyl acetate, butyl acetate, cellosolve acetate, butyl cellosolve acetate, carbitol acetate, butyl carbitol acetate, propylene glycol monomethyl ether acetate, etc. ), Esters such as carbonate esters (propylene carbonate, etc.); petroleum solvents such as petroleum ether, petroleum naphtha, and solvent naphtha. A solvent can be used individually or in combination of 2 or more types.

  The ratio of the solvent can be selected from the range of 1 to 500 parts by weight, for example, 10 to 400 parts by weight, preferably 20 to 300 parts by weight with respect to 100 parts by weight of the heat or photocurable (meth) acrylic resin. Part, more preferably about 30 to 200 parts by weight.

  The heat- or photo-curable (meth) acrylic resin composition may be prepared by using conventional additives such as colorants, stabilizers (thermal stabilizers, antioxidants, ultraviolet absorbers, etc.), fillers, antistatic agents. , A flame retardant, a flame retardant aid, a leveling agent, a silane coupling agent, a polymerization inhibitor (or a thermal polymerization inhibitor) and the like may be included. You may use an additive individually or in combination of 2 or more types.

  The present invention also includes a compound represented by the formula (1) (including the mixture, the same applies hereinafter) or a cured product of the resin composition. Such a cured product can be produced by curing the compound represented by the formula (1) or a resin composition thereof. For example, a film-like cured product is applied to the base material by applying the compound represented by the formula (1) or a resin composition thereof to form a coating film (or thin film) and then performing a curing treatment. You may manufacture by. In addition, the thickness of a film-form coating film (or thin film) can be selected according to a use, for example, 0.1-1000 micrometers, Preferably it is 1-500 micrometers, More preferably, about 5-300 micrometers may be sufficient. In addition, a cured product having a three-dimensional shape (for example, a lens shape) can be manufactured using cast molding or the like.

  In such a method, since the compound represented by the above formula (1) having excellent handling properties is used, dilution with a large amount of diluent (solvent, polymerizable diluent, etc.) and viscosity reduction A cured product can be produced without requiring heating at a high temperature. Therefore, it is easy to introduce a fluorene skeleton at a high concentration into the cured product, and a cured product having excellent characteristics (high refractive index, high heat resistance, etc.) can be easily produced.

  In addition, as a hardening process, a heat processing, a light irradiation process, etc. are mentioned. Heat treatment and light irradiation treatment may be combined. In the heat treatment, the heating temperature may be, for example, 50 to 250 ° C, preferably 60 to 200 ° C, and more preferably about 70 to 150 ° C.

Further, the light irradiation treatment (exposure), the light irradiation amount of energy applications varies depending on the film thickness of the coating film, usually, 0.1~10000mJ / cm ^2, preferably 1~8000mJ / cm ^2, further Preferably, it may be about 10 to 5000 mJ / cm ² .

  The compound of the present invention has excellent properties such as high heat resistance and a high refractive index, and is excellent in handling properties, and can be used for various heat or photocurable (meth) acrylic resin applications.

Specifically, the compound of the present invention (or a cured product obtained using the compound of the present invention) is an ink material, a light emitting material (for example, a light emitting material for organic EL), an organic semiconductor, a graphitization precursor, a gas. Separation membrane (for example, CO ₂ gas separation membrane), coating agent (for example, optical overcoat agent or hard coating agent for LED (light emitting diode) element coating agent), lens [pickup lens (for example, DVD (Digital versatile discs, etc.), micro lenses (eg, micro lenses for liquid crystal projectors), spectacle lenses, etc.], polarizing films (eg, polarizing films for liquid crystal displays), antireflection films (or reflections) Prevention film (for example, antireflection film for display device), film for touch panel, flexible Films for substrates, display films [for example, PDP (plasma display), LCD (liquid crystal display), VFD (vacuum fluorescent display), SED (surface conduction electron-emitting device display), FED (field emission display), NED (nano Emissive display), cathode ray tube, electronic paper display (particularly thin display) film (filter, protective film, etc.), fuel cell membrane, optical fiber, optical waveguide, hologram, etc. In particular, the compound of the present invention can be suitably used for optical material applications, and examples of the shape of such an optical material include films or sheets, plates, lenses, and tubes.

  Hereinafter, the present invention will be described in more detail based on examples, but the present invention is not limited to these examples.

  In the examples, various measurements were performed as follows.

(HPLC purity)
Using a reverse phase column (ODS-80TM) manufactured by Tosoh Corporation, water / acetonitrile (weight ratio) = 30/70 for 30 minutes at 254 nm, then water / acetonitrile (weight ratio) = 0/100 The purity was measured at 30 minutes.

(NMR)
¹ H-NMR spectra were recorded on a JEOL GTX-400 spectrometer using tetramethylsilane as internal standard and CDCl ₃ as solvent.

(Refractive index)
Using a multiwavelength Abbe refractometer (manufactured by Atago, DR-M2 <use of circulating water bath 60-C3>), the refractive index at 589 nm was measured while maintaining 25 degrees.

(viscosity)
Using a TV-22 type viscometer (cone plate type, manufactured by Toki Sangyo Co., Ltd., TVE-22L), with an optional rotor for high viscosity (07: 3 ° × R7.7) at 1.0 to 20 rpm, The viscosity at 25 ° C. was measured.

(HAZE)
Using a color difference turbidity measuring device (Nippon Denshoku Industries Co., Ltd., COH-300A), measurement was performed by putting acrylate into a test tube (manufactured by Maruemu, A-24 (24 × 200), straight port) or 10 × 10 mm quartz cell. .

(Hue)
Using a color difference turbidity measuring device (Nippon Denshoku Industries Co., Ltd., COH-300A), measurement was performed by putting acrylate into a test tube (manufactured by Maruemu, A-24 (24 × 200), straight port) or 10 × 10 mm quartz cell. .

(L *, a *, b *)
Using a color difference turbidity measuring device (Nippon Denshoku Industries Co., Ltd., COH-300A), measurement was performed by putting acrylate into a test tube (manufactured by Maruemu, A-24 (24 × 200), straight port) or 10 × 10 mm quartz cell. .

(Pencil hardness)
The cured film produced on the polyethylene terephthalate film was placed on a pencil hardness meter (HEIDON-14: manufactured by Shinto Kagaku Co., Ltd.), and various pencils were pressed at a 45 degree angle while applying a weight of 1 kg, and 25 mm / min. The pencil hardness was measured by moving the cured film at a speed and visually confirming the presence or absence of scratches on the cured film.

(Synthesis Example 1)
In a 10 L separable flask, 378 g (1.0 mol) of 9,9-bis (4-hydroxy-3-methylphenyl) fluorene (BCF, Osaka Gas Chemical Co., Ltd.), 1029 g (10 mol) of propylene carbonate, and solvent After adding 1500 g (17 mol) of diethylene glycol and adding 10 g of 1-methylimidazole (manufactured by Wako Pure Chemical Industries, Ltd.) as a catalyst, the mixture was heated to 100 ° C. and reacted for 5 hours. After completion of the reaction, 5000 ml of isopropyl alcohol was added and cooled to 10 ° C. to obtain 61 g of white powder. As a result of analyzing the obtained white powder, the target compound (compound represented by the following formula) in which 2 mol of oxypropylene group (propoxy group) was added to 1 mol of BCF used as a raw material with a purity of 98.9% by HPLC , BCF-PO).

¹ H-NMR (CDCl ₃ , δ) ppm: 1.2 ppm (d, 6H), 2.1 ppm (s, 6H), 3.6-4.2 ppm (m, 9H), 6.8 ppm (s, 2H) ), 7.0 ppm (t, 4H), 7.2-7.5 ppm (m, 6H), 7.8 (d, 2H).

Example 1
68.3 g (0.138 mol) of the compound obtained in Synthesis Example 1, 25.9 g (0.359 mol) of acrylic acid (manufactured by Tokyo Chemical Industry Co., Ltd.), p-toluenesulfonic acid (manufactured by Kishida Chemical Co., Ltd.) 3.28 g (0.017 mol), toluene 135 g (1.463 mol), and methoquinone (manufactured by Kishida Chemical Co., Ltd.) 0.3 g (0.002 mol) were charged, and the theoretical dehydration amount was refluxed at 100 ° C. to 115 ° C. The dehydration esterification reaction was performed until obtained. Thereafter, the reaction solution was neutralized with alkali and washed with 20% saline. After washing, toluene was removed to obtain a viscous product. Furthermore, as a result of ¹ H-NMR analysis of the resulting viscous product, it was confirmed that it was the target diacrylate (the following formula).

¹ H-NMR (400 MHz, CD ₂ Cl ₂ , δ):
2.1 ppm (s, 6H), 3.8-4.2 ppm (m, 4H), 5.8 ppm (d, 2H), 6.1 ppm (t, 2H), 6.3 ppm (d, 2H), 7 0.0-7.4 ppm (m, 12H) 7.8 ppm (d, 2H).

  The HPLC purity of the resulting viscous product was 32.2% for the compound (monoacrylate) in which one acrylic acid was added to BCF-PO, 62.4% for the target product (following formula) in which two were added, The multimer of impurities in which one or two acrylic acids were added to a plurality of molecules was 5.4%. The obtained viscous material has a refractive index of 1.599, a viscosity of 33010 mPa · s, a heating residue of 81.3%, a HAZE of 52.1, and a hue (APHA) of 230. Yes, L * was 100.4, a * was 1.2, and b * was 13.

(Example 2)
After 100 parts by weight of the viscous material obtained in Example 1 was heated to 120 ° C. to remove the solvent, the temperature was lowered to 80 ° C. and 3 parts by weight of a photopolymerization initiator (Irgacure 184, manufactured by Ciba Specialty Chemicals) ) And uniformly dissolved, then on a cellulose triacetate film (TAC100: manufactured by Fuji Film Co., Ltd.) or on a polyethylene terephthalate film (Tetron 100HL98W: manufactured by Fuji Film Co., Ltd.) (when measuring pencil hardness) It was applied and homogenized with a 250 μm applicator (manufactured by Dazai Equipment Co., Ltd.) (about 100 μm). In addition, although the viscous material obtained in Example 1 was heated and applied at 80 ° C. for comparison with Comparative Example 1 described later, the viscosity was low enough to be applied even after removal of the solvent. Thereafter, the film was irradiated with light at 500 mJ / cm ² using a UV irradiator (H015-L31: manufactured by Eye Graphics Co., Ltd.) to prepare a cured film.

  When various physical properties of the obtained cured film (cured film) were measured, the refractive index (25 ° C.) was 1.603, and the pencil hardness was 2H. Moreover, it was 158 degreeC when the hardened | cured material of the viscous material obtained in Example 1 was produced as follows and the glass transition temperature (Tg) was measured.

3 parts by weight of a photopolymerization initiator (Irgacure 184, manufactured by Ciba Specialty Chemicals) is added to 100 parts by weight of the viscous product obtained in Example 1, and heated to 80 ° C. to uniformly dissolve the photopolymerization initiator. After that, about 10 mg was weighed in an aluminum pan for DSC measurement, placed in an atmospheric dryer heated to 120 ° C., and left for 5 minutes to remove the solvent. Thereafter, using a UV irradiator (H015-L31: manufactured by Eye Graphics Co., Ltd.), light was irradiated at 2,000 mJ / cm ² to prepare a cured product. Then, DSC (DSC 6220: manufactured by SII) was heated at 10 ° C./min, and the glass transition temperature was measured in the range of 30 to 300 ° C.

(Comparative Example 1)
In Example 2, instead of the viscous material obtained in Example 1, BPEFA (Osaka Gas Chemical Co., Ltd., 9,9-bis [4- (2- (meth) acryloyloxyethoxy) phenyl] fluorene) A fluorene skeleton-containing (meth) acrylate having a high viscosity was used as a main component, and a cured film was produced in the same manner as in Example 2. BPEFA had a very high viscosity (100,000 mPa · s or more at 25 ° C.), but finally reached a viscosity that could be applied at 80 ° C., so it was applied at 80 ° C.

  When various physical properties of the obtained cured film were measured, the refractive index (25 ° C.) was 1.626, and the pencil hardness was 3H. Moreover, it was 211 degreeC when the glass transition temperature (Tg) was measured like Example 2. FIG.

  As is clear from these results, the compounds obtained in the examples have a relatively low viscosity and excellent handling properties, but their cured products are excellent as in the case of using BPEFA. It was found that the product has physical properties.

Claims (9)

A resin composition comprising a compound represented by the following formula (1) and a compound represented by the following formula (3) in a ratio of the former / the latter (molar ratio) = 95/5 to 45/55.

(Wherein R ¹ represents a cyano group, a halogen atom or an alkyl group, R ² represents a branched alkylene group, R ³ represents a hydrogen atom or a methyl group, R ⁴ represents an alkyl group, and k represents 0 to 0) An integer of 4 and m is an integer of 1 or more.)

(In the formula, R ¹ , R ² , R ³ , R ⁴ , k, and m are the same as described above.) ^2. The resin composition according to claim 1, wherein R ² is a propylene group and m is 1 to 4 in formula (1). The resin composition according to claim 1 or 2, wherein in formula (1), R ⁴ is a C _1-4 alkyl group. In formula (1), ^{R 2} is a propylene group, m is 1 to 2, the resin composition according to any one of claims 1 to 3 ^{R 4} is a methyl group. The resin composition according to any one of claims 1 to 4, wherein the compound represented by the formula (1) is a compound represented by the following formula (1A).

(Wherein R ¹ , R ² , R ³ , R ⁴ , k and m are the same as above). The resin according to any one of claims 1 to 5, wherein the compound represented by the formula (1) is 9,9-bis [4- (2- (meth) acryloyloxypropoxy) -3-methylphenyl] fluorene. Composition . The ratio of the compound represented by Formula (1) and the compound represented by Formula (3) is the ratio of the former / the latter (molar ratio) = 90 / 10-50 / 50. A resin composition according to claim 1 . A polymerizable resin composition comprising the resin composition according to claim 1 and a polymerization initiator. Hardened | cured material of the resin composition in any one of Claims 1-7.