JP3636292B2 - Method for producing ferrite sintered body - Google Patents

Method for producing ferrite sintered body Download PDF

Info

Publication number
JP3636292B2
JP3636292B2 JP2000187365A JP2000187365A JP3636292B2 JP 3636292 B2 JP3636292 B2 JP 3636292B2 JP 2000187365 A JP2000187365 A JP 2000187365A JP 2000187365 A JP2000187365 A JP 2000187365A JP 3636292 B2 JP3636292 B2 JP 3636292B2
Authority
JP
Japan
Prior art keywords
weight
ferrite
polyethylene glycol
parts
aqueous solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2000187365A
Other languages
Japanese (ja)
Other versions
JP2002012476A (en
Inventor
浩 原田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TDK Corp
Original Assignee
TDK Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TDK Corp filed Critical TDK Corp
Priority to JP2000187365A priority Critical patent/JP3636292B2/en
Priority to TW089116986A priority patent/TW479003B/en
Priority to KR1020000048812A priority patent/KR100588853B1/en
Priority to CNB00131677XA priority patent/CN1309512C/en
Priority to US09/644,217 priority patent/US6416681B1/en
Publication of JP2002012476A publication Critical patent/JP2002012476A/en
Application granted granted Critical
Publication of JP3636292B2 publication Critical patent/JP3636292B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【0001】
【発明の属する技術分野】
本発明は、フェライト成形用顆粒を用いて成形、焼結することにより得られるフェライト焼結体の製造方法に係り、特に磁心損失が低減されたフェライト焼結体の製造方法に関する。
【0002】
【従来の技術】
フェライトは電子部品に幅広く用いられる。そのフェライトはフェライト材料を用いて成形され、その成形体を焼成することにより得られる。従来、フェライト成形体を製造する方法としては、種々の方法が採用されているが、なかでも乾式の加圧成形法が一般的に広く行われている。たとえばフェライト原料粉末とバインダーと水とにより水性スラリーを調整し、これをスプレードライヤーで噴霧乾燥して作製した顆粒、またはフェライト原料粉末とバインダー溶液とを攪拌混合し、乾燥とオシレーティング押出し造粒を繰り返して作製した顆粒を加圧成形することにより、フェライト成形体が製造される。そしてその成形体を焼成することにより焼結体が得られる。なお、オシレーティング押出し造粒法とは、例えば数mm程度の粒径に造粒された粒子を網上で押し潰して細かくした粒子を落下させるという作業を、網目を順次細かくした数段の工程で行うことにより、所定の粒径以下の粒子を得る方法である。
【0003】
前述のような焼結前の成形体を得る際の加圧成形方法においては、フェライト成形用顆粒として、流動性が良好で、金型への充填性(流動性)が良く、しかも小さい圧力で潰れやすいものを使用することが、得られるフェライト焼結体の品質を良くし、かつ生産性を高めるという見地から重要である。
【0004】
ところで、流動性が良く、小さい圧力で潰れやすい顆粒を製造する方法としては、特開平5−159918号公報や特公平7−17460号公報に、分散剤を用いてスラリーを調整してこれを造粒する方法が開示されている。また、特公平3−31660号公報や特開平10−59776号公報には、バインダーの偏析を抑制して造粒する方法が開示されている。
【0005】
【発明が解決しようとする課題】
しかしながら、前記公報に記載の方法は、一般にスプレードライヤーを用いた噴霧乾燥造粒法に適用される技術であって、オシレーティング押出し造粒法に適用しても、所定の効果を発揮することはできず、用途が狭い。
【0006】
また、前記公報に記載の方法は、顆粒の流動性や潰れ易さは改善されるものの、得られる成形体の強度や、焼結体の電磁気特性、特に磁心損失については満足しうる効果が得られない。
【0007】
本発明は、上記問題点に鑑み、磁心損失が低減されたフェライト焼結体の製造方法を提供することを目的とする。
【0008】
【課題を解決するための手段】
請求項1のフェライト焼結体の製造方法は、フェライト原料粉末と、
バインダーとしてのポリビニルアルコールに可塑剤として分子量が1000以上6000以下のポリエチレングリコールを加えた水溶液とを混合してフェライト成形用顆粒を造粒し、
該顆粒を型により成形し、
該成形体を焼結して吸水率が0.2重量%以下の焼結体を得る
ことを特徴とする。
【0009】
請求項2のフェライト焼結体の製造方法は、請求項1のフェライト焼結体の製造方法において、
造粒用バインダーとしてのポリビニルアルコール100重量部に対し、可塑剤としてのポリエチレングリコールを5重量部以上50重量部以下添加する
ことを特徴とする。
【0010】
本発明のフェライト成形用顆粒の原料粉末は、特に限定されるものではないが、例えば、Fe、MgO、MnO、NiO、CuO、ZnOを主成分とし、必要に応じて、さらに、副成分ないし不可逆的不純物として、Co、W、Bi、Si、B、Zr等の金属酸化物が含まれてもよい。
【0011】
また、フェライト原料粉末の好ましい平均粒径は、0.01〜5μmであり、より好ましくは0.1〜1.5μmである。好ましい平均粒径にするためには、ボールミル、攪拌ミル、アトライター等のような粉砕方式によっても良く、また、湿式粉砕、乾式粉砕のいずれでも良い。
【0012】
第一の必須成分であるポリビニルアルコールは、一次粒子の結合剤、すなわち原料粉末と原料粉末の結合材として機能するものであり、公知のものの中から、鹸化度や重合度を適宜選択して用いることができる。このポリビニルアルコールの添加量は、原料粉末100重量部に対して、通常0.2〜10重量部、より好ましくは0.5〜3重量部である。ポリビニルアルコールの添加量が0.2重量部未満であると、フェライト粒子を造粒できなくなるので好ましくない。逆に10重量部を超えると、フェライト顆粒が硬くなりすぎ、潰れが悪くなることにより、顆粒粒界を多く残し成形不良を発生させる。また、容量欠陥が増加するので好ましくない。
【0013】
第二の必須成分であるポリエチレングリコールは、フェライト成形体顆粒において、可塑剤として機能し、低圧潰れ性と圧力伝達性を改善し、顆粒粒界を低減するものである。ポリエチレングリコールの分子量は1000〜6000の範囲のものが好ましく、より好ましくは2000〜4000である。分子量が1000未満のものでは、低圧潰れ性は改善するが、吸湿性が大きいため、顆粒の流動性が低下し、金型への均一充填ができない。また、6000を超える分子量のものでは、添加による低圧潰れ性の改善効果が少なく、かつ成形体強度の低下によるクラックが発生し易くなる。
【0014】
本発明によるフェライト成形用顆粒は、従来より公知の方法である例えばスプレードライヤーによる噴霧造粒法や、オシレーティング押出し造粒法等により、フェライト粉末を造粒することにより得られる。このようにして得られたフェライト顆粒の平均粒径は、通常50〜500μm、好ましくは70〜300μm、より好ましくは80〜150μmである。平均粒径が50μm未満であると、流動性および金型への充填が悪くなることにより、成形体の寸法および単重量のばらつきが大きくなるので好ましくない。また、金型への微粉付着(スティッキング)が発生し易くなるので、好ましくない。逆に500μmを超えると、顆粒粒界を多く残し成形不良を発生させる。また、成形体の寸法および単重量のばらつきも大きくなる。
【0015】
本発明による高密度フェライト成形体を製造するには、フェライト成形用顆粒を金型を用いて乾式加圧成形を行う。この際、プレス圧力は、通常、40〜500MPa、好ましくは80〜400MPaの範囲で選ばれる。
【0016】
本発明の焼結体製造に用いる成形用顆粒において、ポリエチレングリコールの添加量が50重量部を越えると、成形体強度の低下によるクラックが発生し易くなる。また、5重量部未満では、添加による低圧潰れ性の改善効果が不十分である。ポリビニルアルコールに対するポリエチレングリコールの添加量は、より好ましくは、20〜40重量部である。
【0017】
【発明の実施の形態】
〔造粒材料の調整〕
表1、表2に示すように、フェライト焼結体を作製するに当たり、造粒は、オシレーティング押出し造粒法と、スプレー噴霧造粒法を用いた。また、このような造粒を行うための材料として、フェライト粉末と、ポリビニルアルコール(PVA)とポリエチレングリコールの水溶液またはポリビニルアルコール単独の水溶液とを混合し、造粒のための材料とした。
【0018】
ここで、PVA水溶液No.5〜7はスプレー噴霧造粒によるもので、それ以外のものはオシレーティング押出し造粒による。オシレーティング押出し造粒によるもの(No.5〜7以外のもの)については、Mn−Mg−Zn系フェライト粉末100重量部に、ポリエチレングリコール添加または不添加の種々のポリビニルアルコール水溶液を17重量部添加し、攪拌造粒機TMミキサー(三井鉱山社製)で混合攪拌造粒を行い、造粒粉を調整した。
【0019】
また、表1において、PVA水溶液No.5、6のもの(スプレー噴霧造粒)については、Mn−Mg−Zn系フェライト粉末69重量部、水25重量部、固形分濃度12重量%のポリエチレングリコール添加ポリビニルアルコール水溶液を6重量部および分散剤としてポリカルボン酸アンモニウム塩0.25重量部を湿式混合して、フェライトスラリーを調整した。PVA水溶液No.7のもの(スプレー噴霧造粒)は、ポリエチレングリコールを添加しないこと以外はPVA水溶液No.5、6と同様に調整した。
【0020】
ここで、表1に示すように、ポリビニルアルコールは、鹸化度が98.5で重合度が2400のもの(PVA水溶液No.1〜4、8〜13、17〜20)と、鹸化度が88.0で重合度が500のもの(PVA水溶液No.5〜7)と、鹸化度が88.0で重合度が1700のもの(PVA水溶液No.14〜16、21〜23)とを使用した。
【0021】
また、ポリエチレングリコールは、分子量が600のもの(PVA水溶液No.3、20、22)と、分子量が1000のもの(PVA水溶液No.12〜14、23)と、分子量が2000のもの(PVA水溶液No.1、6、8、15〜18、21)と、分子量が4000のもの(PVA水溶液No.2、5、9、19)と、分子量が6000のもの(PVA水溶液No.10)、分子量が10000のもの(PVA水溶液No.11)とを使用し、ポリビニルアルコール100重量部に対するポリエチレングリコールの添加量を表1の右欄に示すように種々に変化させた。
【0022】
【表1】

Figure 0003636292
【0023】
〔造粒〕
PVA水溶液No.1〜4、8〜23のものについては、表2に示すように、前記造粒粉をベルト乾燥機で乾燥処理し、オシレーティング造粒解砕機で押出し造粒を行い、シフターにて整粒し、平均粒径250μmの顆粒を得た。また、PVA水溶液No.5〜7のものにおいては、スプレー噴霧造粒機で造粒し、平均粒径125μmの球形顆粒を得た。
【0024】
〔流動度の測定〕
得られた顆粒の流動度をJIS Z2502に規定されている漏斗よりフェライト顆粒50gを流下させる時間(秒/50g)を測定した。
【0025】
〔顆粒の成形〕
次いで、得られた顆粒をそれぞれ98MPaの圧力で乾式加圧成形し、長さ55mm、幅12mm、高さ5mmの直方体状のブロック成形体を得た。このブロック成形体の抗折強度を、荷重試験機(アイコーエンジニアリング社製)を用いてJIS R1601に規定されている方法に従い測定した。
【0026】
〔成形体の焼結〕
さらに、得られた顆粒をそれぞれ98MPaの圧力で乾式加圧成形し、外径21mm、内径12mm、厚さ7mmのリング状成形体を作製した。ついで、これらを1300℃の温度において2時間焼結し、リング状コアを作製した。
【0027】
〔磁心損失の測定〕
次に、これらのリング状コアの磁心損失Pcvを、64kHz、50mT、100℃の条件下で、B−H アナライザー(岩崎通信機社製 SY−8216)により測定した。
【0028】
〔吸水率の測定〕
また、このコアの吸水率を、JIS C2141に準じた方法で測定した。すなわち、試験片となるコアを105℃〜120℃で乾燥後、デシケーター中で室温に戻し、乾燥質量W1を測定し、その後、コアを水中で沈め、煮沸して冷却した後、表面の水分をガーゼにより拭き取って飽水試験片を得てその重量W2を測定し、吸水率(%)を次式から求めた。
【0029】
吸水率=100×(W2−W1)/W1
得られた磁心損失Pcvと吸水率の測定結果を表2に示す。
【0030】
【表2】
Figure 0003636292
【0031】
〔成形圧力と成形体密度との関係〕
次に、PVA水溶液No.6、7で作製した顆粒1.5gを直径6mmの金型に充填し、成形圧力49〜294MPaの間で変化させ、乾式加圧成形することにより、直径6mm、長さ16〜19mmの円柱状のフェライト成形体を作製し、このサンプルについて、成形圧力と成形体密度との関係を求めた。その結果を図1に示す。
【0032】
〔側面の写真〕
また、成形圧力196MPaで作製した成形体のコア側面の潰れ状態をSEM写真で撮影した結果を図2に示す。図2(a)、(b)、(c)は、PVA水溶液No.6で作製した顆粒を成形した成形体の上部、中間部、下部の各側面を示す。また、図2(d)、(e)、(f)は、PVA水溶液No.7で作製した顆粒を成形した成形体の上部、中間部、下部の各側面を示す。
【0033】
〔評価〕
(ポリエチレングリコールの添加の有無)
上述のように、可塑性剤としてポリエチレングリコールをポリビニルアルコールに加えて顆粒を得、その顆粒によりフェライト成形体を製造することにより、顆粒粒界が少ない高密度のフェライト成形体が得られる。この成形体を焼結することにより、緻密で空隙の少ない、すなわち吸湿性が少ない焼結体が得られる。
そのため、焼結体内の欠陥の減少により、磁心損失Pcvが大幅に改善されたフェライト焼結体が得られた。
【0034】
(ポリエチレングリコールの分子量について)
PVA水溶液No.12、14、すなわちポリエチレングリコールの分子量が1000の場合、磁心損失Pcvが70と低く、流動度がそれぞれ25、26であって、好ましい流動度である28以下であり、抗折強度も1.7、1.7と、好ましい抗折強度である1.2以上であり、両者とも良好な範囲である。
【0035】
一方、ポリエチレングリコールの分子量が600であるPVA水溶液No.3、20、22については、磁心損失Pcvはそれぞれ62、63、64と低く、良好であるが、流動度がそれぞれ30、29、31と悪く、抗折強度もそれぞれ0.9、0.9、1.0と低いという結果が得られた。そしてこの流動性の悪化により、金型への顆粒の充填性が悪く、不安定なものとなるため、寸法・単重量のばらつきにつながるため、好ましくない。また、抗折強度の低下もクラックの発生につながるため、好ましくない。従って、ポリエチレングリコールの分子量は1000以上であることが好ましい。
【0036】
一方、ポリエチレングリコールの分子量が6000であるPVA水溶液No.10の場合、磁心損失Pcvが72と低く、流動度が26、抗折強度が1.7と両者とも良好な範囲である。しかしポリエチレングリコールの分子量が10000であるPVA水溶液No.11の場合、磁心損失Pcvが85と高く、抗折強度も1.1と低い結果となった。このことから、ポリエチレングリコールの分子量は6000以下であることが好ましい。
【0037】
また、ポリエチレングリコールの分子量が2000または4000であって、ポリエチレングリコールの添加量が所定の範囲内(ポリビニルアルコール100重量部に対してポリエチレングリコール5〜50重量部)であるPVA水溶液No.1、2、5、6、8、10、12、15、21においては、吸水率がいずれも0.2%以下であり、また、磁心損失Pcvが72以下でいずれも低く、流動度も26以下、抗折強度も1.4以上と良好な範囲であるため、分子量は2000〜4000の範囲にあることが好ましい。
【0038】
(ポリエチレングリコールの添加量について)
ポリエチレングリコールの分子量が2000でポリビニルアルコールに対する添加量が5重量部であるPVA水溶液No.8の場合、磁心損失Pcvが74と低く、流動度は25、抗折強度は1.8といずれも良好な範囲である。しかし、ポリエチレングリコールの分子量が4000でポリビニルアルコールに対する添加量が3重量部であるPVA水溶液No.9の場合、ポリエチレングリコールの分子量が1000でポリビニルアルコールに対する添加量が2重量部であるPVA水溶液No.13の場合、ポリエチレングリコールの分子量が2000でポリビニルアルコールに対する添加量が3重量部であるPVA水溶液No.16の場合、いずれも磁心損失Pcvが80以上と高い値を示す。従ってポリエチレングリコールの添加量は5重量部以上であることが好ましい。
【0039】
一方、ポリエチレングリコールの添加量が50重量部であるPVA水溶液No.18やNo.23の場合、磁心損失Pcvがそれぞれ62、65と低く、良好である。また、抗折強度は低下するものの、許容範囲(1.2以上)である。
【0040】
しかし、ポリエチレングリコールの添加量が60重量部であるPVA水溶液No.17やNo.19の場合、磁心損失Pcvが60、62と低く、良好であるが、抗折強度が0.7と低く、クラックが発生し易い結果となった。このようなことから、ポリエチレングリコールの添加量は50重量部以下であることが好ましい。
【0041】
また、ポリエチレングリコールの分子量が2000、4000の場合、ポリエチレングリコールのポリビニルアルコールに対する添加量が20〜40重量部の範囲内にあるPVA水溶液No.1、2、5、6の場合、いずれも、吸水率が0.07以下と低く、また磁心損失Pcvが69以下と低く、流動度は26以下で、抗折強度も1.4以上と良好な範囲であるため、ポリエチレングリコールより好ましい添加量は20〜40重量部である。
【0042】
(吸水率と磁心損失Pcvとの関係について)
図3に表2の吸水率と磁心損失Pcvとの関係を散布図として示す。吸水率が0.2%以下であれば、この例の組成のフェライトにおいて、80kW/m以下の低い磁心損失Pcvのコアが得られることが判る。さらに、70kW/m以下のより低い磁心損失Pcvのコアを得るためには、吸水率が0.1%以下であることが好ましい。
【0043】
【発明の効果】
請求項1によれば、フェライト原料粉末と、バインダーとしてのポリビニルアルコールと、可塑剤として添加され、分子量が1000以上6000以下のポリエチレングリコールとを混合し造粒し、これを成形し、焼結することによりフェライト焼結体を得ているので、成形時の低圧潰れ性が改善され、フェライト成形体の顆粒粒界が低減され、その焼結体の内部欠陥の低減により磁心損失が低いフェライト焼結体が得られる。
【0044】
請求項2によれば、請求項1において、ポリビニルアルコール100重量部に対し、ポリエチレングリコールを5重量部以上50重量部以下添加してなるので、請求項1、の効果がよりよく達成される。
【図面の簡単な説明】
【図1】本発明の実施例および比較例における成形体の成形圧力と成形体密度との関係を示すグラフである。
【図2】本発明の実施例および比較例における成形体の状態を示す写真図である。
【図3】本発明におけるフェライト焼結体の吸水率と磁心損失との関係図である。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a method for manufacturing a ferrite sintered body obtained by molding and sintering using ferrite forming granules, and more particularly to a method for manufacturing a ferrite sintered body with reduced core loss.
[0002]
[Prior art]
Ferrite is widely used in electronic parts. The ferrite is formed by using a ferrite material, and is obtained by firing the formed body. Conventionally, various methods have been adopted as a method for producing a ferrite molded body, and among them, a dry pressure molding method is generally widely used. For example, an aqueous slurry is prepared with a ferrite raw material powder, a binder, and water, and the granule produced by spray drying this with a spray dryer, or the ferrite raw material powder and a binder solution are stirred and mixed, followed by drying and oscillating extrusion granulation. A ferrite molded body is manufactured by pressure-molding the granules produced repeatedly. And the sintered compact is obtained by baking the molded object. In addition, the oscillating extrusion granulation method is, for example, a process of smashing particles that have been granulated to a particle size of about several millimeters on a net and dropping the fine particles into several steps in which the mesh is successively fined This is a method for obtaining particles having a predetermined particle size or less.
[0003]
In the pressure molding method for obtaining a molded body before sintering as described above, the ferrite molding granules have good fluidity, good mold filling properties (fluidity), and low pressure. It is important from the viewpoint of improving the quality of the ferrite sintered body to be obtained and increasing the productivity to use a material that is easily crushed.
[0004]
By the way, as a method for producing granules having good fluidity and easy to be crushed with a small pressure, JP-A-5-159918 and JP-B-7-17460 prepare a slurry by adjusting a slurry using a dispersant. A method of granulating is disclosed. Japanese Patent Publication No. 3-31660 and Japanese Patent Laid-Open No. 10-59776 disclose a method of granulating while suppressing segregation of the binder.
[0005]
[Problems to be solved by the invention]
However, the method described in the above publication is a technique generally applied to the spray-drying granulation method using a spray dryer, and even when applied to the oscillating extrusion granulation method, it does not exhibit a predetermined effect. Can not be used, narrow application.
[0006]
Further, although the method described in the above publication improves the fluidity and friability of the granule, the method has a satisfactory effect on the strength of the obtained molded body and the electromagnetic characteristics of the sintered body, particularly the core loss. I can't.
[0007]
An object of this invention is to provide the manufacturing method of the ferrite sintered compact by which the magnetic core loss was reduced in view of the said problem.
[0008]
[Means for Solving the Problems]
The method for producing a ferrite sintered body according to claim 1 comprises a ferrite raw material powder,
A mixture of polyvinyl alcohol as a binder and an aqueous solution in which polyethylene glycol having a molecular weight of 1000 or more and 6000 or less is added as a plasticizer to granulate ferrite molding granules,
Forming the granules by a mold;
The molded body is sintered to obtain a sintered body having a water absorption of 0.2% by weight or less.
[0009]
The method for producing a ferrite sintered body according to claim 2 is the method for producing a ferrite sintered body according to claim 1 ,
5 parts by weight or more and 50 parts by weight or less of polyethylene glycol as a plasticizer is added to 100 parts by weight of polyvinyl alcohol as a granulating binder.
[0010]
The raw material powder of the granule for ferrite molding of the present invention is not particularly limited, but, for example, Fe 2 O 3 , MgO, MnO, NiO, CuO, ZnO is a main component, and if necessary, a sub- As components or irreversible impurities, metal oxides such as Co, W, Bi, Si, B, and Zr may be contained.
[0011]
Moreover, the preferable average particle diameter of ferrite raw material powder is 0.01-5 micrometers, More preferably, it is 0.1-1.5 micrometers. In order to obtain a preferable average particle size, a pulverization method such as a ball mill, a stirring mill, or an attritor may be used, and either wet pulverization or dry pulverization may be used.
[0012]
Polyvinyl alcohol, which is the first essential component, functions as a binder for primary particles, that is, a binder for raw material powder and raw material powder, and is used by appropriately selecting a degree of saponification and a degree of polymerization from known materials. be able to. The addition amount of this polyvinyl alcohol is 0.2-10 weight part normally with respect to 100 weight part of raw material powder, More preferably, it is 0.5-3 weight part. If the amount of polyvinyl alcohol added is less than 0.2 parts by weight, ferrite particles cannot be granulated. On the other hand, if it exceeds 10 parts by weight, the ferrite granules become too hard and the crushing becomes worse, leaving many grain boundaries and causing defective molding. Further, it is not preferable because capacity defects increase.
[0013]
Polyethylene glycol, which is the second essential component, functions as a plasticizer in the ferrite molded body granules, improves the low-pressure crushing property and pressure transmission property, and reduces the grain boundary. The molecular weight of polyethylene glycol is preferably in the range of 1000 to 6000, more preferably 2000 to 4000. When the molecular weight is less than 1000, the low-pressure crushing property is improved, but the hygroscopic property is large, so that the fluidity of the granules is lowered and the mold cannot be uniformly filled. In addition, when the molecular weight exceeds 6000, the effect of improving the low-pressure crushing property by addition is small, and cracks due to a decrease in the strength of the molded body are likely to occur.
[0014]
The ferrite molding granule according to the present invention can be obtained by granulating ferrite powder by a conventionally known method such as spray granulation using a spray dryer or oscillating extrusion granulation. The average particle size of the ferrite granules thus obtained is usually 50 to 500 μm, preferably 70 to 300 μm, more preferably 80 to 150 μm. If the average particle size is less than 50 μm, the fluidity and filling of the mold are deteriorated, resulting in a large variation in the size and single weight of the molded body, which is not preferable. Moreover, it is not preferable because fine powder adhesion (sticking) easily occurs on the mold. On the other hand, if it exceeds 500 μm, many granule boundaries are left and defective molding occurs. In addition, variations in dimensions and single weight of the molded body also increase.
[0015]
In order to manufacture the high-density ferrite molded body according to the present invention, the ferrite molding granules are dry-pressed using a mold. At this time, the pressing pressure is usually selected in the range of 40 to 500 MPa, preferably 80 to 400 MPa.
[0016]
In the molding granule used for manufacturing the sintered body of the present invention, if the amount of polyethylene glycol added exceeds 50 parts by weight, cracks are likely to occur due to a decrease in the strength of the molded body. Moreover, if it is less than 5 weight part, the improvement effect of the low-pressure crushing property by addition is inadequate. The amount of polyethylene glycol added to polyvinyl alcohol is more preferably 20 to 40 parts by weight.
[0017]
DETAILED DESCRIPTION OF THE INVENTION
[Adjustment of granulation material]
As shown in Tables 1 and 2, in producing the ferrite sintered body, the oscillating extrusion granulation method and the spray spray granulation method were used for granulation. Moreover, as a material for performing such granulation, a ferrite powder and an aqueous solution of polyvinyl alcohol (PVA) and polyethylene glycol or an aqueous solution of polyvinyl alcohol alone were mixed to obtain a material for granulation.
[0018]
Here, PVA aqueous solution No. 5-7 are by spray atomization granulation, and others are by oscillating extrusion granulation. For oscillating extrusion granulation (other than Nos. 5-7), 17 parts by weight of various polyvinyl alcohol aqueous solutions with or without polyethylene glycol added to 100 parts by weight of Mn—Mg—Zn ferrite powder Then, the mixture was stirred and granulated with a stirring granulator TM mixer (Mitsui Mining Co., Ltd.) to prepare the granulated powder.
[0019]
In Table 1, PVA aqueous solution No. For 5 and 6 (spray spray granulation), 69 parts by weight of Mn—Mg—Zn ferrite powder, 25 parts by weight of water, and 6 parts by weight of a polyethylene glycol-added aqueous solution of polyvinyl alcohol having a solid content of 12% by weight are dispersed. A ferrite slurry was prepared by wet mixing 0.25 parts by weight of polycarboxylic acid ammonium salt as an agent. PVA aqueous solution No. No. 7 (spray spray granulation) is PVA aqueous solution No. except that polyethylene glycol is not added. Adjustments were made in the same manner as in 5 and 6.
[0020]
Here, as shown in Table 1, polyvinyl alcohol has a saponification degree of 98.5 and a polymerization degree of 2400 (PVA aqueous solution Nos. 1-4, 8-13, 17-20) and a saponification degree of 88. 0.0 and a polymerization degree of 500 (PVA aqueous solution No. 5-7) and a saponification degree of 88.0 and a polymerization degree of 1700 (PVA aqueous solution No. 14-16, 21-23) were used. .
[0021]
In addition, polyethylene glycol has a molecular weight of 600 (PVA aqueous solution No. 3, 20, 22), a molecular weight of 1000 (PVA aqueous solution No. 12-14, 23), and a molecular weight of 2000 (PVA aqueous solution). No. 1, 6, 8, 15-18, 21), a molecular weight of 4000 (PVA aqueous solution No. 2, 5, 9, 19), a molecular weight of 6000 (PVA aqueous solution No. 10), molecular weight 10000 (PVA aqueous solution No. 11) was used, and the amount of polyethylene glycol added to 100 parts by weight of polyvinyl alcohol was varied as shown in the right column of Table 1.
[0022]
[Table 1]
Figure 0003636292
[0023]
[Granulation]
PVA aqueous solution No. As for Tables 1 to 4 and 8 to 23, as shown in Table 2, the granulated powder is dried with a belt dryer, extruded and granulated with an oscillating granulator, and sized with a shifter. As a result, granules having an average particle size of 250 μm were obtained. Also, PVA aqueous solution No. In the case of 5-7, it granulated with the spray spray granulator, and obtained the spherical granule with an average particle diameter of 125 micrometers.
[0024]
[Measurement of fluidity]
The flow rate of the obtained granules was measured for the time (seconds / 50 g) during which 50 g of ferrite granules were allowed to flow down from the funnel defined in JIS Z2502.
[0025]
[Molding of granules]
Next, the obtained granules were each subjected to dry pressure molding at a pressure of 98 MPa to obtain a rectangular parallelepiped block molded body having a length of 55 mm, a width of 12 mm, and a height of 5 mm. The bending strength of the block molded body was measured using a load tester (manufactured by Aiko Engineering Co., Ltd.) according to the method defined in JIS R1601.
[0026]
[Sintering of compacts]
Further, each of the obtained granules was dry-pressure molded at a pressure of 98 MPa to produce a ring-shaped molded body having an outer diameter of 21 mm, an inner diameter of 12 mm, and a thickness of 7 mm. Subsequently, these were sintered at a temperature of 1300 ° C. for 2 hours to produce a ring-shaped core.
[0027]
[Measurement of magnetic core loss]
Next, the core loss Pcv of these ring-shaped cores was measured with a BH analyzer (SY-8216 manufactured by Iwasaki Tsushinki Co., Ltd.) under the conditions of 64 kHz, 50 mT, and 100 ° C.
[0028]
(Measurement of water absorption rate)
Moreover, the water absorption rate of this core was measured by the method according to JIS C2141. That is, after drying the core to be a test piece at 105 ° C. to 120 ° C., it is returned to room temperature in a desiccator, the dry mass W1 is measured, and then the core is submerged in water, boiled and cooled, and then the surface moisture is reduced. The saturated water test piece was obtained by wiping with gauze, its weight W2 was measured, and the water absorption rate (%) was determined from the following equation.
[0029]
Water absorption rate = 100 × (W2−W1) / W1
Table 2 shows the measurement results of the obtained magnetic core loss Pcv and water absorption.
[0030]
[Table 2]
Figure 0003636292
[0031]
[Relationship between molding pressure and compact density]
Next, PVA aqueous solution No. 6 and 7 are filled in a 6 mm diameter mold, changed between a molding pressure of 49 to 294 MPa, and dry pressure molded to form a cylindrical shape with a diameter of 6 mm and a length of 16 to 19 mm. A ferrite molded body was prepared, and the relationship between the molding pressure and the molded body density was determined for this sample. The result is shown in FIG.
[0032]
[Photo of the side]
Moreover, the result of having image | photographed the collapsed state of the core side surface of the molded object produced with the shaping | molding pressure 196MPa with the SEM photograph is shown in FIG. 2 (a), (b), and (c) show the PVA aqueous solution No. 6 shows the side surfaces of the upper part, the middle part, and the lower part of the molded body obtained by molding the granules produced in 6. 2 (d), (e), and (f) show the PVA aqueous solution No. 7 shows the side surfaces of the upper part, the middle part, and the lower part of the molded body obtained by molding the granules produced in 7.
[0033]
[Evaluation]
(With or without addition of polyethylene glycol)
As described above, polyethylene glycol is added as a plasticizer to polyvinyl alcohol to obtain granules, and a ferrite molded body is produced from the granules, thereby obtaining a high-density ferrite molded body with few grain boundaries. By sintering this molded body, a dense sintered body with less voids, that is, less hygroscopicity can be obtained.
Therefore, a ferrite sintered body in which the magnetic core loss Pcv is greatly improved due to the reduction of defects in the sintered body was obtained.
[0034]
(Molecular weight of polyethylene glycol)
PVA aqueous solution No. 12 and 14, that is, when the molecular weight of polyethylene glycol is 1000, the magnetic core loss Pcv is as low as 70, the fluidity is 25 and 26, respectively, the preferred fluidity is 28 or less, and the bending strength is 1.7. 1.7, which is a preferable bending strength of 1.2 or more, and both are good ranges.
[0035]
On the other hand, the PVA aqueous solution No. 4 having a molecular weight of polyethylene glycol of 600 is used. 3, 20, and 22, the magnetic core loss Pcv is as low as 62, 63, and 64, respectively, but is good, but the fluidity is as bad as 30, 29, and 31 respectively, and the bending strength is also 0.9, 0.9, respectively. , 1.0 was obtained. This deterioration in fluidity results in poor filling of the granules into the mold and becomes unstable, leading to variations in dimensions and unit weight, which is not preferable. Moreover, since the fall of bending strength also leads to generation | occurrence | production of a crack, it is unpreferable. Accordingly, the molecular weight of polyethylene glycol is preferably 1000 or more.
[0036]
On the other hand, a PVA aqueous solution No. 6000 having a polyethylene glycol molecular weight of 6000 was used. In the case of 10, the magnetic core loss Pcv is as low as 72, the fluidity is 26, and the bending strength is 1.7. However, PVA aqueous solution No. 1 whose molecular weight of polyethylene glycol is 10,000. In the case of 11, the magnetic core loss Pcv was as high as 85 and the bending strength was as low as 1.1. Therefore, the molecular weight of polyethylene glycol is preferably 6000 or less.
[0037]
Moreover, the molecular weight of polyethylene glycol is 2000 or 4000, and the addition amount of polyethylene glycol is within a predetermined range (5 to 50 parts by weight of polyethylene glycol with respect to 100 parts by weight of polyvinyl alcohol). In 1, 2, 5, 6, 8, 10, 12, 15, and 21, the water absorption is 0.2% or less, the core loss Pcv is 72 or less, and the fluidity is 26. Hereinafter, since the bending strength is in a favorable range of 1.4 or more, the molecular weight is preferably in the range of 2000 to 4000.
[0038]
(About the amount of polyethylene glycol added)
PVA aqueous solution No. 2 in which the molecular weight of polyethylene glycol is 2000 and the amount added to polyvinyl alcohol is 5 parts by weight. In the case of 8, the core loss Pcv is as low as 74, the fluidity is 25, and the bending strength is 1.8. However, PVA aqueous solution No. 3 having a molecular weight of polyethylene glycol of 4000 and an addition amount to polyvinyl alcohol of 3 parts by weight. In the case of No. 9, PVA aqueous solution No. 1 in which the molecular weight of polyethylene glycol is 1000 and the amount added to polyvinyl alcohol is 2 parts by weight. In the case of No. 13, PVA aqueous solution No. 1 in which the molecular weight of polyethylene glycol is 2000 and the amount added to polyvinyl alcohol is 3 parts by weight. In the case of 16, the core loss Pcv is a high value of 80 or more. Therefore, the amount of polyethylene glycol added is preferably 5 parts by weight or more.
[0039]
On the other hand, PVA aqueous solution No. 5 in which the amount of polyethylene glycol added is 50 parts by weight. 18 or No. In the case of 23, the magnetic core loss Pcv is as low as 62 and 65, respectively. Moreover, although bending strength falls, it is an allowable range (1.2 or more).
[0040]
However, PVA aqueous solution No. in which the addition amount of polyethylene glycol is 60 parts by weight. 17 or No. In the case of 19, the magnetic core loss Pcv was as low as 60 and 62, which was good, but the bending strength was as low as 0.7, and cracks were likely to occur. For this reason, the amount of polyethylene glycol added is preferably 50 parts by weight or less.
[0041]
When the molecular weight of polyethylene glycol is 2000, 4000, the amount of polyethylene glycol added to polyvinyl alcohol is within the range of 20 to 40 parts by weight. In the case of 1, 2, 5, and 6, the water absorption is as low as 0.07 or less, the core loss Pcv is as low as 69 or less, the fluidity is 26 or less, and the bending strength is as good as 1.4 or more. Therefore, the addition amount is more preferably 20 to 40 parts by weight than polyethylene glycol.
[0042]
(Relationship between water absorption rate and magnetic core loss Pcv)
FIG. 3 is a scatter diagram showing the relationship between the water absorption rate and the magnetic core loss Pcv in Table 2. It can be seen that when the water absorption is 0.2% or less, a core with a low magnetic core loss Pcv of 80 kW / m 3 or less can be obtained in the ferrite having the composition of this example. Furthermore, in order to obtain a core with a lower core loss Pcv of 70 kW / m 3 or less, the water absorption is preferably 0.1% or less.
[0043]
【The invention's effect】
According to claim 1 , ferrite raw material powder, polyvinyl alcohol as a binder, and polyethylene glycol added as a plasticizer and having a molecular weight of 1000 or more and 6000 or less are mixed, granulated, molded, and sintered. Since the ferrite sintered body is obtained, the low-pressure crushability at the time of molding is improved, the grain boundary of the ferrite molded body is reduced, and the ferrite loss is reduced by reducing the internal defects of the sintered body. The body is obtained.
[0044]
According to claim 2, in claim 1, with respect to polyvinyl alcohol 100 parts by weight, since the addition below 50 parts by weight or more 5 parts by weight of polyethylene glycol, according to claim 1, the effect of being achieved better.
[Brief description of the drawings]
FIG. 1 is a graph showing the relationship between the molding pressure and the density of a molded body in Examples and Comparative Examples of the present invention.
FIG. 2 is a photograph showing the state of molded bodies in examples and comparative examples of the present invention.
FIG. 3 is a graph showing the relationship between the water absorption rate and magnetic core loss of a ferrite sintered body in the present invention.

Claims (2)

フェライト原料粉末と、
バインダーとしてのポリビニルアルコールに可塑剤として分子量が1000以上6000以下のポリエチレングリコールを加えた水溶液とを混合してフェライト成形用顆粒を造粒し、
該顆粒を型により成形し、
該成形体を焼結して吸水率が0.2重量%以下の焼結体を得る
ことを特徴とするフェライト焼結体の製造方法。
Ferrite raw material powder,
A mixture of polyvinyl alcohol as a binder and an aqueous solution in which polyethylene glycol having a molecular weight of 1000 or more and 6000 or less is added as a plasticizer to granulate ferrite molding granules,
Forming the granules by a mold;
A method for producing a ferrite sintered body, comprising sintering the molded body to obtain a sintered body having a water absorption of 0.2% by weight or less.
請求項1のフェライト焼結体の製造方法において、
造粒用バインダーとしてのポリビニルアルコール100重量部に対し、可塑剤としてのポリエチレングリコールを5重量部以上50重量部以下添加する
ことを特徴とするフェライト焼結体の製造方法。
In the manufacturing method of the ferrite sintered compact of Claim 1 ,
A method for producing a ferrite sintered body comprising adding 5 parts by weight or more and 50 parts by weight or less of polyethylene glycol as a plasticizer to 100 parts by weight of polyvinyl alcohol as a binder for granulation.
JP2000187365A 1999-08-24 2000-06-22 Method for producing ferrite sintered body Expired - Fee Related JP3636292B2 (en)