JP3485643B2 - Coated zinc oxide powder and composition containing coated zinc oxide powder - Google Patents

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to zinc oxide powder used as an ultraviolet absorbing pigment and the like. More specifically, the surface of the zinc oxide powder is coated with a coupling agent to absorb, sterilize, and disinfect the zinc oxide itself. While maintaining the effects of mildew proofing, deodorization, etc., the photocatalytic activity of zinc oxide itself is suppressed, and resin compositions (paints, coatings, films, resin moldings, fibers, etc.) and oil and fat compositions Coated zinc oxide powder that has improved dispersibility in (cosmetics, etc.) and, as a result, effectively prevents their photodegradation when blended in a resin composition or an oil / fat composition and improves storage stability. Regarding

[0002]

2. Description of the Related Art Organic resin compositions and oil and fat compositions cause decomposition, deterioration, discoloration and the like due to ultraviolet rays contained in sunlight. UV absorbers are one of the additives that are aimed at preventing their decomposition, deterioration, discoloration, etc.These are roughly classified into organic UV absorbers such as benzophenone and benzotriazole, and zinc oxide powder and oxides. It is classified into an inorganic ultraviolet absorber represented by titanium powder.

Organic ultraviolet absorbers are disadvantageous in that they are organic substances and therefore deteriorate when they are exposed to ultraviolet light, and with the passage of time, so-called so-called "embosses" appear on the surface of a coating film or a molded article. It is well known that it has the drawback of causing blooming and being gradually washed away by rainwater or the like. Not only in terms of UV absorption effect, but also from the viewpoint of global environmental protection that has been increasing in recent years, it is chemically stable and does not cause blooming, and not only its excellent UV absorption effect from old times, but also sterilization, Inorganic UV absorbers such as zinc oxide and titanium oxide, which have been confirmed to have antibacterial, antifungal, and deodorizing effects, are being revisited.

[0004] However, zinc oxide and titanium oxide exhibit an excellent ultraviolet ray absorbing action, and therefore, when incorporated into a resin composition or an oil and fat composition, their deterioration due to ultraviolet ray irradiation can be prevented, while they are excited by ultraviolet ray irradiation. It has a high photocatalytic activity and also has the drawback of accelerating the decomposition, deterioration, discoloration, etc. of resin compositions and fats and oils compositions, and is well known to cause so-called chalking, which causes the surface of coating films and resin molded products to become chalky. ing. In other words, to use zinc oxide or titanium oxide as a UV absorber,
It has been a technical subject how to suppress the photocatalytic activity which is the defect.

As a means for solving this problem, titanium oxide is subjected to a surface coating treatment with Al ₂ O ₃ , SiO ₂ , ZnO, TiO ₂ or the like, which is already commercially available. For surface treatment of zinc oxide, see Table 4-5
Japanese Patent No. 06674 discloses a UV-absorbing, chemically inactive pigment zinc oxide coated with a water-insoluble metal soap of a monocarboxylic acid, but does not show deterioration of the resin during kneading or molding. Judging from the contents of description of the effects in Examples 6 to 10, the chemically inert pigment zinc oxide referred to in the invention described in JP-A-4-506674 is against the thermal deterioration during melt kneading or hot press molding. It means a pigment zinc oxide having improved stability, and attempts to suppress the deterioration of the resin composition or the oil and fat composition by suppressing the photocatalytic activity of zinc oxide excited by ultraviolet irradiation referred to in the present invention. Is something else. Also, as in the case of titanium oxide, the surface of zinc oxide particles is Al, Si, Z.
A technique for coating an oxide or hydroxide of r or Sn is disclosed in JP-A-3-183620.

[0006]

However, in order to meet the recent market demands for transparency and chromaticity of resin compositions and oil and fat compositions containing an ultraviolet absorber, zinc oxide powder is further made into fine particles, The powder specific surface area tends to increase. Since the increase of the specific surface area leads to the increase of the required coating amount, the surface coating treatment with the oxide or hydroxide of Al, Si, Zr or Sn based on the conventional technique requires the coating amount required to suppress the photocatalytic activity. It has started to be feared that the UV absorption rate of the liver and kidney may be adversely affected. In other words, the development of surface treatment technology that can suppress photocatalytic activity with a smaller coating amount, that is, without relatively reducing the content of zinc oxide as much as possible, is accompanied by the demand of the ultraviolet absorber market that requires fine particle formation. It has become an urgent task.

Another problem of the prior art is to improve the dispersibility of zinc oxide powder in a resin composition or a fat composition. The ultraviolet absorber is used as an additive dispersed in a resin composition or an oil and fat composition. That is, it is well known that the ultraviolet ray absorbing effect when it becomes a resin composition or an oil and fat composition is important, and even in titanium oxide and the like, the worse the dispersibility and the stronger the aggregation, the faster the deterioration of the resin. There is. The surface coating treatment with an inorganic substance such as Al, Si, Zr, or Sn oxide or hydroxide based on the conventional technique leaves a problem in dispersibility with the resin composition or the oil / fat composition. Even if you suppress the photocatalytic activity,
Due to poor dispersibility, it is feared that the effect of absorbing ultraviolet rays when it becomes a resin composition or oil / fat composition of the liver and kidney is poor, and it is not possible to exert sufficient effect for preventing photodegradation of the resin composition or oil / fat composition. .

The object of the present invention is to use the zinc oxide powder itself as a UV absorber with a small amount of surface coating which does not adversely affect the UV absorption, sterilization, antibacterial, antifungal and deodorizing effects and effects of the zinc oxide powder itself. The amount of surface coating that sufficiently suppresses the photocatalytic activity that deteriorates the resin composition and the oil and fat composition, which are the disadvantages of zinc oxide when it is present, and at the same time improves the dispersibility of the zinc oxide in the resin composition and the oil and fat composition. Is covered with
When used as a resin composition (coating film, film, resin molded product, fiber, etc.) or oil / fat composition (cosmetics, etc.), it works as a suitable UV absorber, bactericidal, antibacterial, antifungal, deodorant, etc. To provide a coated zinc oxide powder which suppresses photodegradation of a resin composition or an oil and fat composition, an additive containing the coated zinc oxide powder as an active ingredient, and a composition comprising the coated zinc oxide powder. is there.

[0009]

Means for Solving the Problems The inventors of the present invention have conducted extensive studies in order to achieve the above-mentioned object, and as a result, by coating a small amount of a coupling agent on the surface of zinc oxide powder particles, The inventors have found that the problems can be solved and completed the present invention. That is, the coated zinc oxide powder of the present invention,
The surface of the zinc oxide particles has been coated with a coupling agent .
The coating amount of the coupling agent was 0.
It is characterized by being 2 to 10% by weight .

Further, the additive of the present invention contains the above-mentioned coated zinc oxide powder as an active ingredient and has ultraviolet absorption, sterilization, antibacterial, antifungal and deodorizing effects, but the photocatalytic activity is suppressed. Furthermore, the resin composition and the oil / fat composition of the present invention are characterized by containing the above-mentioned coated zinc oxide powder.

The present invention will be described in detail below. The zinc oxide powder to be coated to obtain the coated zinc oxide powder of the present invention may be obtained by a so-called wet synthesis method or may be obtained by a so-called dry synthesis method. As a method for coating the surface of the zinc oxide powder particles with the coupling agent, a so-called wet method in which the coupling agent is added while stirring a slurry of zinc oxide powder in water or in a non-aqueous solvent may be used, and high-speed rotation is also possible. A so-called dry method in which the coupling agent is sprayed or dropped while stirring the zinc oxide powder at high speed with a Henschel mixer or high-speed mixer is also possible, and it is also possible to carry in a reaction vessel containing the zinc oxide powder with an inert gas such as nitrogen. Introduced coupling agent,
A so-called vapor-phase method for coating may be used.

However, regarding the coating amount, it is necessary to consider the specific surface area of the zinc oxide powder to be coated. For example, in Example 2 described in detail later, the zinc oxide powder used has a specific surface area of 20 m ² / g according to the BET method,
By coating 1% by weight of a silane coupling agent on this, the photocatalytic activity of zinc oxide could be suppressed almost completely, but for the same purpose coating of finer zinc oxide powder with a larger specific surface area was possible. In the case of treatment, it is easily inferred that the photocatalytic activity cannot be sufficiently suppressed unless the coating amount is increased with the coverage as a guide.

That is, when coating zinc oxide powder having a remarkably large specific surface area (for example, 400 m ² / g), a coating amount of about 20% is required, and conversely, the specific surface area is several m ² / g. When coating zinc oxide powder having a relatively large particle size of about g, a sufficient effect can be expected even with a coating amount of about 0.1%. Therefore, the usual range of the coating amount is 0.1 to 20% by weight, and considering the dispersibility, it is preferably 0.1.
2 to 15% by weight, preferably 0.1 considering the cost.
1 to 10% by weight, preferably 0.2 to 10% by weight in total.

In Examples 1 to 3 described later, silane coupling agents KBM-403 (γ-glycidoxypropyltrimethoxysilane) manufactured by Shin-Etsu Chemical Co., Ltd. and KBM-5 were used.
03 (γ-methacryloxypropyltrimethoxysilane) was used as a coating treatment agent, but the main reason for the reaction with the surface of the inorganic oxide particles such as zinc oxide is that the hydrolyzable group of the coupling agent is hydrolyzed. It is well known that a silanol group generated by decomposition and an organic functional group such as an epoxy group or a methacryl group mainly reacts with various resins to be bonded. For the purpose of suppressing the photocatalytic activity, even if other silane coupling agents, that is, silane coupling agents having a vinyl group, a mercapto group, an amino group, etc. are used, titanium-based compounds other than silane coupling agents are also used. Other coupling agents such as aluminum-based, zirconium-based, zirco-aluminate-based, or silane may be used.

Incidentally, it is not clear why the photocatalytic activity of zinc oxide can be suppressed in a small amount when a coupling agent is used as the surface coating agent as compared with the case of using an inorganic material of the prior art, but zinc oxide particles The reactivity between the active site controlling the surface photocatalytic activity and the coupling agent is much higher than the reactivity between the active site controlling the photocatalytic activity on the zinc oxide particle surface and the inorganic surface treatment agent. Therefore, it seems that the coupling agent may kill the active sites controlling the photocatalytic activity on the surface of the zinc oxide particles without waste even with a small coating amount.

In the coated zinc oxide powder of the present invention, the photocatalytic activity can be suppressed with a smaller coating amount, that is, without reducing the relative content of zinc oxide as much as possible, so that the ultraviolet absorbing action of zinc oxide itself is maintained. Although the photocatalytic activity is further suppressed, the bactericidal, antibacterial, antifungal and deodorizing effects are maintained as they are. The reason for this is not clear, but one hypothesis is that the active sites that control photocatalytic activity are different from the active sites that control sterilization, antibacterial, antifungal, deodorizing, etc. The necessary and minimum amount that can kill the active sites that control the photocatalytic activity, that is, the necessary and minimum amount that can suppress the photocatalytic activity, sterilization, antibacterial, antifungal, deodorant active sites that remain, such as sterilization, The effects of antibacterial, mildew-proof, and deodorizing are maintained as they are.

In order to further improve the dispersibility in the resin, it is necessary to select the coupling agent in consideration of the compatibility between the resin used and the organic functional group of the coupling agent. This is a point of improving the dispersibility which could not be achieved by the surface coating treatment with the inorganic material such as Al, Si, Zr or Sn oxide or hydroxide based on the prior art, and for example, Examples 4 to 6 described later. In this case, since polyethylene resin is used, zinc oxide powder surface-coated with KBM-503 was used.

The coated zinc oxide powder of the present invention has ultraviolet absorption, bactericidal, antibacterial, antifungal, and deodorizing effects, but is used as an additive whose photocatalytic activity is suppressed. For example, it is used in resin compositions and oil and fat compositions. By adding and using it, UV absorption, sterilization, antibacterial, antifungal, deodorizing and other effects are achieved.
Moreover, since the photocatalytic activity is suppressed, the resin composition and the oil and fat composition are not decomposed, deteriorated, or discolored. When used as an additive in the present invention, the coated zinc oxide powder may be used alone or as a mixture with other components.

When the additive of the present invention is added to the paint, it may be added directly to the paint or may be prepared as a paint after being mixed with one component of the paint. When the paint prepared in this way is applied to walls, floors, ceilings, etc., it is possible to prevent the coating film from discoloring or deteriorating due to the ultraviolet rays contained in the sunlight or the like inserted through the window, and to deodorize. , Can prevent the development of mold.

Kneading the additive of the present invention into a resin composition,
For example, when it is formed into a film and used as a packaging material for foods, etc., it prevents discoloration of foods due to ultraviolet rays, and at the same time, sterilization, antibacterial, prevention of decay due to mildew-proofing and deodorization during opening. It can prevent an unpleasant odor. Also, when the film-like material is used as wallpaper or the like, it is possible to prevent the wallpaper from being discolored or deteriorated by ultraviolet rays contained in the sunlight or the like that is inserted through the window, and it is possible to prevent deodorization and the occurrence of mold. .

Kneading the additive of the present invention into a resin composition,
When it is used as a resin molded product, or when the additive of the present invention is kneaded into a resin composition and then pulverized once to obtain a resin powder, and a resin molded product prepared by coating a substrate with the powder For example, in the case of kitchen utensils, sterilization,
Antibacterial and antifungal effects prevent spoilage and deodorize.

When the additive of the present invention is used in fibers,
By kneading the additives in the spinning step, or by post-processing by spinning after spinning, discoloration of the textile product due to ultraviolet rays is prevented, and at the same time, effects such as sterilization, antibacterial activity, mildew proofing, and deodorization are achieved. When the additive of the present invention is added to cosmetics, the additive of the present invention may be added as it is, or a powder resin or the like supported on the surface may be added.
The cosmetic thus prepared has not only an ultraviolet absorbing effect but also an effect of deodorizing sweat odor and the like.

[0023]

【Example】

Example 1 While stirring an aqueous slurry of zinc oxide powder having a BET specific surface area of 20 m ² / g, a predetermined amount of silane coupling agent KBM-503 was added dropwise so that the coating amount was 0.5% by weight. Stirring was continued for a while, and then the slurry was filtered, washed, and further dried by heating in a dryer to obtain a dry powder of coated zinc oxide powder.

The photocatalytic activity of the zinc oxide powder obtained as described above was examined in order to investigate the effect of suppressing the photocatalytic activity by coating the surface of the particles of the zinc oxide powder. As a measure of the effect of suppressing photocatalytic activity, put the acetaldehyde gas and a certain amount of the above zinc oxide powder in a transparent sealed container, irradiate with ultraviolet light, and measure the decomposition rate of acetaldehyde due to autoxidation, measured after a certain period of time. Using. The measurement results are shown in Table 1 together with the surface coating and the coating amount.

Example 2 A dry powder of coated zinc oxide powder was obtained in the same manner as in Example 1 except that a predetermined amount of the silane coupling agent KBM-503 was used so that the coating amount was 1%. Example 1
The effect of suppressing the photocatalytic activity was examined in the same manner as in. The measurement results are shown in Table 1 together with the surface coating and the coating amount. Furthermore,
The deodorizing activity of the coated zinc oxide powder obtained in this example was investigated. As a measure of the deodorizing effect, hydrogen sulfide and coated zinc oxide powder were put in a transparent sealed container, and the change with time of the residual hydrogen sulfide concentration in the transparent sealed container was measured. The measurement result is shown in FIG.

Example 3 A dry powder of coated zinc oxide powder was obtained in the same manner as in Example 1 except that KBM-403 was used as the silane coupling agent. Further, the effect of suppressing the photocatalytic activity was examined in the same manner as in Example 1. The measurement results are shown in Table 1 together with the surface coating and the coating amount.

Comparative Examples 1 to 3 In accordance with the method described in JP-A-3-183620, S
A predetermined amount of zinc oxide powder having a BET specific surface area of 20 m ² / g was added to an aqueous solution of sodium silicate so that the coverage of io ₂ was 3%, 7% and 18%, respectively, and the pH of the solution was carefully monitored. A hydrochloric acid diluted solution was gradually added to the aqueous solution. Then, when the pH reached about 7, the addition was stopped and the mixture was allowed to stand for a while. Next, these suspensions were filtered, washed, and further dried by heating at 105 ° C. in a dryer to obtain dry powders of coated zinc oxide powder. Further, the effect of suppressing the photocatalytic activity was examined in the same manner as in Example 1. The measurement results are shown in Table 1 together with the surface coating and the coating amount.

Comparative Example 4 The uncoated zinc oxide powder itself having a BET specific surface area of 20 m ² / g before the surface coating treatment used in Examples 1 to 3 and Comparative Examples 1 to 3 was used as a comparative control. Further, the effect of suppressing the photocatalytic activity was examined in the same manner as in Example 1. The measurement results are shown in Table 1. Further, the deodorizing effect was examined in the same manner as in Example 2. The measurement result is shown in FIG.

[0029]

[Table 1]

As shown in Table 1, the uncoated zinc oxide powder before the surface coating treatment of Comparative Example 4 has a very high decomposition rate of acetaldehyde of 86.0%, indicating that the photocatalytic activity is extremely high. . In the coated zinc oxide powder of Example 2 based on the present invention (coating amount of KBM-503: 1%), the decomposition rate of acetaldehyde was 0.9%, which is a drawback of zinc oxide as an ultraviolet absorber. It was confirmed that the photocatalytic activity was almost completely suppressed.

On the other hand, in the coated zinc oxide powders of Comparative Examples 1 to 3 based on the prior art, when the coating amount was 3%, the decomposition rate was 77.4% and there was almost no effect, and as the coating amount increased. Although the effect of suppressing photocatalytic activity is gradually increasing,
Even if the coating amount reaches 18%, the decomposition rate is about 12.6%,
When the coating amount of the coated zinc oxide powder of Example 2 is 1% and the decomposition rate is 0.9%, the effect of suppressing the photocatalytic activity is far short.

As described above, the coated zinc oxide powder of the present invention obtained by coating the coupling agent has an overwhelmingly small amount of zinc oxide powder as compared with the prior art in which the surface of the inorganic material is coated. It was confirmed that the photocatalytic activity can be suppressed. Further, in the graph of FIG. 1 showing the deodorizing effect, it means that the larger the slope of the straight line is, the larger the deodorizing effect of the coated zinc oxide is, and the coated zinc oxide powder prepared in Example 2 is the same as that of Comparative Example 4. It shows almost the same slope as the zinc oxide powder itself, that is, almost the same deodorizing effect. This deodorizing activity test was carried out without irradiation with ultraviolet light, but the result was almost the same when irradiation with ultraviolet light was carried out. In the measurement of photocatalytic activity, considering that it showed photocatalytic activity only when it was irradiated with ultraviolet light, in terms of phenomena, the active point controlling photocatalytic activity and the active point controlling sterilization, antibacterial, antifungal, deodorizing, etc. Are considered to be different. That is, it can be said that the coated zinc oxide of the present invention suppresses the photocatalytic activity, but the effects inherent to the zinc oxide such as the ultraviolet absorbing effect, sterilization, antibacterial, antifungal, deodorizing, etc. are hardly impaired.

Example 4 3 parts by weight of the coated zinc oxide powder obtained in Example 1 and 100 parts by weight of a polyethylene resin were melt-kneaded to a thickness of 50 μm.
Was formed into a film and the dispersibility of the coated zinc oxide powder in polyethylene resin was examined. Example 5 Dispersibility was examined in the same manner as in Example 4 except that the coated zinc oxide powder obtained in Example 2 was used. Further, in order to investigate the ultraviolet absorption efficiency when the zinc oxide powder became a resin composition, the spectral transmission spectrum of the obtained film was measured. The result is shown in FIG.

Example 6 The dispersibility was examined in the same manner as in Example 4 except that the coated zinc oxide powder obtained in Example 3 was used. Comparative Example 5 The dispersibility was examined in the same manner as in Example 4 except that the coated zinc oxide powder obtained in Comparative Example 1 was used. Further, in order to investigate the ultraviolet absorption efficiency when the zinc oxide powder became a resin composition, the spectral transmission spectrum of the obtained film was measured. The result is shown in FIG.

Comparative Example 6 Dispersibility was examined in the same manner as in Example 4 except that the coated zinc oxide powder obtained in Comparative Example 2 was used. Comparative Example 7 The dispersibility was examined in the same manner as in Example 4 except that the coated zinc oxide powder obtained in Comparative Example 3 was used. Further, in order to investigate the ultraviolet absorption efficiency when the zinc oxide powder became a resin composition, the spectral transmission spectrum of the obtained film was measured. The result is shown in FIG.

Comparative Example 8 The dispersibility was examined in the same manner as in Example 4 except that the zinc oxide powder of Comparative Example 4 was used. In addition, in order to investigate the ultraviolet absorption efficiency when the zinc oxide powder becomes a resin composition,
The spectral transmission spectrum of the obtained film was measured. The result is shown in FIG.

COMPARATIVE EXAMPLE 9 A film was formed in the same manner as in Example 4 except that the zinc oxide powder was not added, and the ultraviolet absorption efficiency when the zinc oxide powder became a resin composition was examined. The spectral transmission spectrum of the obtained film was measured. The result is shown in FIG.

In Comparative Examples 5 to 7 in which the zinc oxide powder coated with SiO ₂ was used, undispersed agglomerates were visually observed, and comparison was made using uncoated zinc oxide powder. The dispersibility was worse than in the case of Example 8. Examples 4 to 6 using zinc oxide powder coated with a coupling agent
Comparing the case of No. 2 and the cases of Comparative Examples 5 to 8, the difference in dispersibility was visually apparent, but SEM photographs (composition image photographs) and EPMA photographs of the respective films were taken, and the agglomerates were zinc oxide. I checked if there was one. FIG. 3 is a SEM photograph (40 times) of the film obtained in Example 5, FIG.
Is a SEM photograph of the film obtained in Example 5 (1000
5) is an EPMA photograph (1000 times) of the film obtained in Example 5. FIG. 6 is a SEM photograph (40 times) of the film obtained in Comparative Example 5, FIG. 7 is a SEM photograph (1000 times) of the film obtained in Comparative Example 5, and FIG. 8 is a photograph of the film obtained in Comparative Example 5. EPMA photograph (1000 times)
Is. As is clear from the photographs of FIGS. 3 to 5, when the coated zinc oxide powder of the present invention was used, it was uniformly dispersed without aggregates. On the other hand, as is clear from the photographs of FIGS. 6 to 8, in the case of Comparative Example 5, there were large aggregates, some of which had a diameter of several hundreds of μm, and the dispersibility was obviously poor. It became clear.

In the case of Comparative Example 8 (using uncoated zinc oxide powder), so-called burning and discoloration were observed during kneading and molding. On the other hand, in the case of Examples 4 to 6, no burning or discoloration was observed, so that the zinc oxide surface-coated according to the present invention not only suppresses the photocatalytic activity, but also during kneading and molding. It was confirmed that the photocatalytic activity of zinc oxide with respect to the thermal deterioration of the is also suppressed. It should be noted that in Comparative Examples 5 to 7, slight burning and discoloration were observed, and it was confirmed that the present invention is superior to the prior art even with respect to thermal deterioration.

In Examples 4 to 6 and Comparative Examples 5 to 8, the dispersibility with the resin was examined by kneading with the resin for the sake of convenience. Produces similar results. In addition, basically the same result can be obtained even when dispersed in oil and fat. As is clear from the graph of FIG. 2, the film of Example 5 according to the present invention absorbs almost no ultraviolet rays (about 400 nm or less) and does not transmit it. The film of Example 5 contains zinc oxide powder prepared in Example 2 which almost completely suppresses the photocatalytic activity which is a drawback of zinc oxide as an ultraviolet absorber with a coating amount of the coupling agent of 1%. Has been done. That is, a small coating amount that does not affect the ultraviolet absorption efficiency of the zinc oxide powder aimed at by the present invention sufficiently suppresses the photocatalytic activity, which is a drawback of zinc oxide as an ultraviolet absorber, and at the same time makes it a resin of zinc oxide. It was confirmed that a coated zinc oxide powder having improved dispersibility and exhibiting a suitable action as an ultraviolet absorber when it became a resin composition was developed.

On the other hand, the films of Comparative Examples 5 and 7 based on the prior art have lower ultraviolet absorption ability than the film of Comparative Example 8 (using uncoated zinc oxide powder). The reason for this is considered to be that the dispersibility was lowered by the SiO ₂ surface coating treatment as described above. That is, the drawback of the prior art is that when the coating amount is increased in order to suppress the photocatalytic activity, the dispersibility of the resin composition decreases, and as shown by the spectra of Comparative Examples 5 and 7 in FIG. That is, the ultraviolet absorption efficiency is deteriorated. In a word, the present invention can be said to have solved this problem, which the conventional technique had, at once by using a coupling agent.

Example 7 While stirring an n-hexane slurry of zinc oxide powder (Comparative Example 4), a predetermined amount of titanium coupling agent KR TTS (manufactured by Ajinomoto Co., Inc.) was dropped so that the coating amount was 1% by weight. did. Stirring was continued for a while, then the slurry was filtered, washed and air dried overnight to give a dry powder of coated zinc oxide powder. With respect to the coated zinc oxide powder thus obtained, the effect of suppressing the photocatalytic activity was examined in the same manner as in Example 1.
Also, a film was formed in the same manner as in Example 4, and the dispersibility of the coated zinc oxide powder in the polyethylene resin was examined. Further, the ultraviolet absorption efficiency was examined in the same manner as in Example 5. The measurement results are shown in Table 2 together with the surface coating and the coating amount.

Example 8 A predetermined amount of a zircoaluminate coupling agent M (made by CAVEDON CHEMICAL CO. INC. Was added so that the coating amount was 1% by weight while stirring an aqueous slurry of zinc oxide powder (Comparative Example 4). )
Was dripped. Stirring was continued for a while, and then the slurry was filtered, washed, and further dried by heating in a dryer to obtain a dry powder of coated zinc oxide powder. With respect to the coated zinc oxide powder thus obtained, the effect of suppressing the photocatalytic activity was examined in the same manner as in Example 1. Also, a film was formed in the same manner as in Example 4, and the dispersibility of the coated zinc oxide powder in the polyethylene resin was examined. Further, the ultraviolet absorption efficiency was examined in the same manner as in Example 5. The measurement results are shown in Table 2 together with the surface coating and the coating amount.

Table 2 also shows the cases where the coated zinc oxide powder obtained in Example 2, the coated zinc oxide powder obtained in Comparative Examples 1 and 3 and the uncoated zinc oxide powder obtained in Comparative Example 4 were used. Show.

[0045]

[Table 2] The criteria for determining dispersibility in resin are as follows: 10 mm
In the number of aggregates of about 30 μm or more existing in the range of × 10 mm, ⊚: none, ∘: less than 10, Δ: 10 to 20
×: Over 20

As is clear from the data shown in Table 2,
It was confirmed that the coated zinc oxide powders obtained in Examples 2, 7 and 8 according to the present invention were far superior to the zinc oxide powders according to the prior art as UV absorbers.
The present invention relates to a coated zinc oxide powder obtained by coating a coupling agent, but titanium oxide also has a drawback that it has a stronger photocatalytic activity than zinc oxide as an ultraviolet absorber, and a cup Considering the reaction mechanism of the ring agent with the surface of the inorganic oxide, the same effect as that of the present invention can be obtained when titanium oxide is coated with the coupling agent.

[0047]

INDUSTRIAL APPLICABILITY The coated zinc oxide of the present invention has a small amount of surface coating which does not adversely affect the action and effects of ultraviolet absorption, sterilization, antibacterial, mildew, deodorization, etc. of the zinc oxide powder itself, and Sufficiently suppresses the photocatalytic activity that deteriorates the resin composition and the oil and fat composition, which are the drawbacks of zinc oxide when used as an ultraviolet absorber, and at the same time, disperses the zinc oxide in the resin composition and the oil and fat composition. It is coated with an improved surface coating amount, and it is suitable as a UV absorber, sterilizer, antibacterial when it becomes a resin composition (coating film, film, resin molded product, fiber, etc.) or fat composition (cosmetics, etc.). , Acts as an antifungal agent, a deodorant, etc., and suppresses the photodegradation of resin compositions and oil and fat compositions.

[Brief description of drawings]

FIG. 1 is a graph showing the deodorizing effect of a coated zinc oxide powder of Example 2 and an uncoated zinc oxide powder of Comparative Example 4.

2 is a spectral transmission spectrum of polyethylene films obtained in Example 5 and Comparative Examples 5, 7, 8 and 9. FIG.

FIG. 3 is a SEM photograph of the film obtained in Example 5 (4
0 times).

FIG. 4 is a SEM photograph of the film obtained in Example 5 (1
000 times).

5 is an EPMA photograph (1000 ×) of the film obtained in Example 5. FIG.

6 is a SEM photograph of the film obtained in Comparative Example 5 (4
0 times).

7 is a SEM photograph of the film obtained in Comparative Example 5 (1
000 times).

8 is an EPMA photograph (1000 times) of the film obtained in Comparative Example 5. FIG.

─────────────────────────────────────────────────── ─── Continuation of the front page (58) Fields surveyed (Int.Cl. ⁷ , DB name) A61K 7/00 C08L 1/00-101/16

Claims (5)

(57) [Claims] 1. A zinc oxide particle surface is coated with a coupling agent, and the coating amount of the coupling agent is zinc oxide.
0.2 to 10% by weight of the coated zinc oxide powder. 2. The coated zinc oxide powder according to claim 1, wherein the coupling agent is a silane coupling agent. 3. An additive having the coated zinc oxide powder according to claim 1 or 2 as an active ingredient, which has ultraviolet absorption, bactericidal, antibacterial, antifungal and deodorizing properties, but has suppressed photocatalytic activity. 4. A resin composition containing the additive according to claim 3. 5. An oil and fat composition comprising the additive according to claim 3.