JP3315394B2 - Animal waste treatment material containing plastic waste material and method for producing the same - Google Patents

Animal waste treatment material containing plastic waste material and method for producing the same

Info

Publication number
JP3315394B2
JP3315394B2 JP2000099701A JP2000099701A JP3315394B2 JP 3315394 B2 JP3315394 B2 JP 3315394B2 JP 2000099701 A JP2000099701 A JP 2000099701A JP 2000099701 A JP2000099701 A JP 2000099701A JP 3315394 B2 JP3315394 B2 JP 3315394B2
Authority
JP
Japan
Prior art keywords
powder
waste
coating layer
water
granular core
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP2000099701A
Other languages
Japanese (ja)
Other versions
JP2000295933A (en
Inventor
伊藤  博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Daiki Co Ltd
Original Assignee
Daiki Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Daiki Co Ltd filed Critical Daiki Co Ltd
Priority to JP2000099701A priority Critical patent/JP3315394B2/en
Publication of JP2000295933A publication Critical patent/JP2000295933A/en
Application granted granted Critical
Publication of JP3315394B2 publication Critical patent/JP3315394B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、プラスチック廃
材、特にポリエチレンテレフタレート廃材、ポリエチレ
ン廃材、ポリプロピレン廃材、及びポリスチレン廃材等
のプラスチック廃材を原料とする動物用排泄物処理材に
関し、特にポリエチレンテレフタレート廃材を原料とす
る保水機能を有する動物用排泄物処理材に関する。また
本発明は、ポリエチレンテレフタレート等のプラスチッ
ク廃材を原料とし、排泄時に使用して、動物、特に愛玩
用の家畜の体に付着する害虫を動物の体から駆除した
り、動物用の体に付着しないようにする防虫機能を有す
る動物用泄物処理材に関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an animal excrement disposal material made from plastic waste, particularly polyethylene terephthalate waste, polyethylene waste, polypropylene waste, and polystyrene waste, and more particularly to polyethylene terephthalate waste. The present invention relates to an animal excrement disposal material having a water retention function. Further, the present invention uses a plastic waste material such as polyethylene terephthalate as a raw material and uses it at the time of excretion to exterminate pests that adhere to animals, especially pets, and do not adhere to animal bodies. The present invention relates to an animal excrement disposal material having an insect repellent function.

【0002】[0002]

【従来技術】例えば、ペツトボトルは、ポリエチレンテ
レフタレート製の軽くて割れ難い透明な容器で、醤油や
清涼飲料水の壜として広く使用されている。また、例え
ば、紙おむつ製造工程から発生する規格外の紙おむつ
は、粉砕され、風簸により分級されて、ポリエチレン、
ポリプロピレン及びゴム等の粉砕混合物からなるプラス
チック廃材粉と、吸水性樹脂及び紙粉とに分けられてい
る。この分離過程で生ずる吸水性樹脂及び紙粉は、紙お
むつの原料として利用されるか、又は別の用途に利用さ
れている。
2. Description of the Related Art For example, a pet bottle is a light and hard-to-break transparent container made of polyethylene terephthalate, which is widely used as a soy sauce or soft drink bottle. Further, for example, non-standard disposable diapers generated from the disposable diaper manufacturing process are pulverized, classified by elutriation, polyethylene,
It is divided into plastic waste material powder composed of a crushed mixture of polypropylene and rubber, and water-absorbent resin and paper powder. The water-absorbent resin and paper powder generated in this separation process are used as raw materials for disposable diapers or used for other purposes.

【0003】[0003]

【発明が解決しようとする課題】しかし、この分離過程
で生ずるポリエチレン、ポリプロピレン及びゴム等のプ
ラスチック廃材は、処理される紙おむつ廃材の約1/4
以上に及び大量に発生する。これらのプラスチック廃材
は、他の産業廃棄物として大量に発生するブラスチック
廃材と同様に、再利用できる用途が無く、しかも、発熱
量が5,500キロカロリー/kg以上と高いので、そ
の侭焼却すると炉を痛めるために、一般のごみと区別さ
れており、焼却処理をするとしても不燃性のごみと一緒
に焼却しなければならず、多くの手間を要して間題であ
る。そこでプラスチック廃材は、その侭、埋め立てに使
用されるが、自然環境上問題であり、プラスチック廃材
について、一般ごみと同様に焼却できるプラスチック廃
材のについての有効活用が望まれている。本発明は、こ
れらプラスチック廃材の高発熱量のための焼却処理に係
る問題点を解決することを目的としている。
However, plastic waste such as polyethylene, polypropylene and rubber generated in this separation process is about one-fourth of waste diaper to be treated.
Above and in large quantities. These plastic wastes, like the plastic wastes generated in large quantities as other industrial wastes, have no reusable uses and have a high calorific value of 5,500 kcal / kg or more. In order to damage the furnace, it is distinguished from general waste, and even if it is incinerated, it must be incinerated together with non-combustible waste. Therefore, plastic waste is used for landfill as it is, but it is a problem in the natural environment, and effective utilization of plastic waste that can be incinerated in the same manner as general waste is desired. An object of the present invention is to solve the problems related to the incineration treatment for high calorific value of these plastic waste materials.

【0004】[0004]

【課題を解決するための手段】本発明者は、ポリエチレ
ンテレフタレート、ポリエチレン、ポリプロピレン及び
合成ゴム等のプラスチック廃材を、5mm以下、好まし
くは2mm以下の粒径に粉砕すると、これらの粉砕され
た粉体、即ち粉砕された粒子の集合体は、粉砕される前
と比較して、吸水性及び保水性が顕著に向上することを
発見した。また本発明者は、以上のように、例えば5m
m以下に粉砕されたポリエチレンテレフタレート等の高
発熱量のプラスチック廃材粉に不燃性の無機質配合材料
を配合し、さらに吸水性樹脂を配合して、粒状に形成す
ることにより、プラスチック廃材を、焼却可能の動物用
排泄物処理材の原料として使用できることを発見した。
The inventor of the present invention crushed plastic waste such as polyethylene terephthalate, polyethylene, polypropylene and synthetic rubber to a particle size of 5 mm or less, preferably 2 mm or less. That is, it has been found that the aggregate of the crushed particles has remarkably improved water absorption and water retention as compared to before the crushing. In addition, the present inventor, for example,
Plastic waste material can be incinerated by mixing non-flammable inorganic compounding materials with high calorific value plastic waste material powder such as polyethylene terephthalate ground to less than m, and further compounding a water-absorbing resin to form granules. It can be used as a raw material for animal excrement disposal materials.

【0005】また本発明者は、以上のように、例えば5
mm以下に粉砕されたポリエチレンテレフタレート等の
高発熱量のプラスチック廃材粉に不燃性の無機質配合材
料を配合し、さらに吸水性樹脂を配合して、吸水時の発
熱量が1000〜2500キロカロリー/kgの発熱量
の可燃物とすることにより、プラスチック廃材粉の吸水
性を活用して、焼却処理が可能となることを発見して、
動物用排泄物処理材に、プラスチック廃材粉を原料とし
て使用できることを発見して本発明に至った。さらに本
発明者は、以上のように粉砕されたポリエチレンテレフ
タレート、ポリエチレン、ポリプロピレン及び合成ゴム
等のプラスチック廃材粉は、高い発熱量を有するが、動
物用排泄物処理材に原料として使用すると、吸水性樹脂
に保有される多量の水分により、発熱量が1000〜2
500キロカロリー/kgに低下でき、焼却処理が可能
となることを発見した。そこで本発明者は、プラスチッ
ク廃材粉を、吸水性樹脂を原料として使用する動物用排
泄物処理材に配合することにより、プラスチック廃材粉
の吸水性が活用でき、且つ焼却処理が可能となることを
発見して、本発明に至った。
[0005] Further, as described above, the present inventor has proposed that
mm, a non-flammable inorganic compounding material is mixed with a high calorific value plastic waste material powder such as polyethylene terephthalate, and a water-absorbing resin is further mixed. By making it a combustible material with a calorific value, we discovered that it is possible to incinerate using the water absorption of plastic waste material powder,
The present inventors have found that a plastic waste material powder can be used as a raw material in animal excrement disposal materials, leading to the present invention. Furthermore, the present inventor has reported that plastic waste material powders such as polyethylene terephthalate, polyethylene, polypropylene and synthetic rubber which have been pulverized as described above have a high calorific value. Due to the large amount of water retained in the resin, the calorific value is 1000-2
It has been found that it can be reduced to 500 kcal / kg, and incineration can be performed. Therefore, the present inventor has found that by blending plastic waste material powder with animal excrement disposal materials using a water-absorbent resin as a raw material, the water absorption of plastic waste material powder can be utilized and incineration can be performed. The discovery has led to the present invention.

【0006】即ち、本発明は、3mm以下の粒度のポリ
エチレンテレフタレート廃材粉、ポリエチレン廃材粉、
ポリプロピレン廃材粉、ポリアクリロニトリル廃材粉、
ナイロン廃材粉若しくはポリエステル廃材粉又はこれら
廃材粉の二種以上からなるプラスチック廃材粉と、前記
プラスチック廃材粉より少量の吸水性樹脂とを含有して
粒状に形成されていることを特徴とする動物用排泄物処
理材にあり、また、本発明は、3mm以下の粒度のポリ
エチレンテレフタレート廃材粉、ポリエチレン廃材粉、
ポリプロピレン廃材粉、ポリアクリロニトリル廃材粉、
ナイロン廃材粉若しくはポリエステル廃材粉又はこれら
廃材粉の二種以上からなるプラスチック廃材粉と、前記
プラスチック廃材粉より少量の吸水性樹脂と、小麦粉、
澱粉、コーンスターチ、カルボキシメチルセルロース、
プルラン若しくはゼラチン又はこれら二以上の潤滑、接
着及び保水機能を有する配合物質とを含有して粒状に形
成されていることを特徴とする動物用排泄物処理材にあ
り、さらに本発明は、3mm以下の粒度のポリエチレン
テレフタレート廃材粉、ポリエチレン廃材粉、ポリプロ
ピレン廃材粉、ポリアクリロニトリル廃材粉、ナイロン
廃材粉若しくはポリエステル廃材粉又はこれら廃材粉の
二種以上からなるプラスチック廃材粉と、前記プラスチ
ック廃材粉より少量の吸水性樹脂とを含有して粒状に形
成されている粒状芯部を有すると共に、紙粉及び吸水性
樹脂を含有して粒状芯部の表面上に形成されている被覆
層部を有し、前記粒状芯部と被覆層部とにより粒状に形
成されていることを特徴とする動物用排泄物処理材にあ
り、さらにまた、本発明は、3mm以下の粒度のポリエ
チレンテレフタレート廃材粉、ポリエチレン廃材粉、ポ
リプロピレン廃材粉、ポリアクリロニトリル廃材粉、ナ
イロン廃材粉若しくはポリエステル廃材粉又はこれら廃
材粉の二種以上からなるプラスチック廃材粉と、前記プ
ラスチック廃材粉より少量の吸水性樹脂と、小麦粉、澱
粉、コーンスターチ、カルボキシメチルセルロース、プ
ルラン若しくはゼラチン又はこれら二以上の潤滑、接着
及び保水機能を有する配合物質とを含有して粒状に形成
されている粒状芯部を有すると共に、紙粉及び吸水性樹
脂を含有して粒状芯部の表面上に形成されている被覆層
部を有し、前記粒状芯部と被覆層部とにより粒状に形成
されていることを特徴とする動物用排泄物処理材にあ
り、さらに加えて、本発明は、3mm以下の粒度のポリ
エチレンテレフタレート廃材粉、ポリエチレン廃材粉、
ポリプロピレン廃材粉、ポリアクリロニトリル廃材粉、
ナイロン廃材粉若しくはポリエステル廃材粉又はこれら
廃材粉の二種以上からなるプラスチック廃材粉と、前記
プラスチック廃材粉より少量の吸水性樹脂とを含有して
粒状に形成されている粒状芯部を有すると共に、紙粉及
び吸水性樹脂を含有して粒状芯部の表面上に形成されて
いる被覆層部を有し、前記粒状芯部と被覆層部とにより
粒状に形成されており、前記粒状芯部若しくは前記被覆
層部又は前記粒状芯部及び前記被覆層部に防黴剤が含有
されていることを特徴とする動物用排泄物処理材にあ
り、さらにまた、本発明は、3mm以下の粒度のポリエ
チレンテレフタレート廃材粉、ポリエチレン廃材粉、ポ
リプロピレン廃材粉、ポリアクリロニトリル廃材粉、ナ
イロン廃材粉若しくはポリエステル廃材粉又はこれら廃
材粉の二種以上からなるプラスチック廃材粉と、前記プ
ラスチック廃材粉より少量の吸水性樹脂と、小麦粉、澱
粉、コーンスターチ、カルボキシメチルセルロース、プ
ルラン若しくはゼラチン又はこれら二以上の潤滑、接着
及び保水機能を有する配合物質とを含有して粒状に形成
されている粒状芯部を有すると共に、紙粉及び吸水性樹
脂を含有して粒状芯部の表面上に形成されている被覆層
部を有し、前記粒状芯部と被覆層部とにより粒状に形成
されており、前記粒状芯部若しくは前記被覆層部又は前
記粒状芯部及び前記被覆層部に防黴剤が含有されている
ことを特徴とする動物用排泄物処理材にある。そしてま
た、本発明は、3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂とを含有して粒状に形成され
ている粒状芯部を有すると共に、紙粉及び吸水性樹脂を
含有して粒状芯部の表面上に形成されている被覆層部を
有し、前記粒状芯部と被覆層部とにより粒状に形成され
ており、前記粒状芯部若しくは前記被覆層部又は前記粒
状芯部及び前記被覆層部に蒸散性ピレスロイド系防虫剤
が含有されていることを特徴とする動物用排泄物処理材
にあり、さらに、本発明は、3mm以下の粒度のポリエ
チレンテレフタレート廃材粉、ポリエチレン廃材粉、ポ
リプロピレン廃材粉、ポリアクリロニトリル廃材粉、ナ
イロン廃材粉若しくはポリエステル廃材粉又はこれら廃
材粉の二種以上からなるプラスチック廃材粉と、前記プ
ラスチック廃材粉より少量の吸水性樹脂と、小麦粉、澱
粉、コーンスターチ、カルボキシメチルセルロース、プ
ルラン若しくはゼラチン又はこれら二以上の潤滑、接着
及び保水機能を有する配合物質とを含有して粒状に形成
されている粒状芯部を有すると共に、紙粉及び吸水性樹
脂を含有して粒状芯部の表面上に形成されている被覆層
部を有し、前記粒状芯部と被覆層部とにより粒状に形成
されており、前記粒状芯部若しくは前記被覆層部又は前
記粒状芯部及び前記被覆層部に蒸散性ピレスロイド系防
虫剤が含有されていることを特徴とする動物用排泄物処
理材にあり、さらにまた、本発明は、3mm以下の粒度
のポリエチレンテレフタレート廃材粉、ポリエチレン廃
材粉、ポリプロピレン廃材粉、ポリアクリロニトリル廃
材粉、ナイロン廃材粉若しくはポリエステル廃材粉又は
これら廃材粉の二種以上からなるプラスチック廃材粉
と、前記プラスチック廃材粉より少量の吸水性樹脂とを
含有して粒状に形成されている粒状芯部を有すると共
に、紙粉及び吸水性樹脂を含有して粒状芯部の表面上に
形成されている被覆層部を有し、前記粒状芯部と被覆層
部とにより粒状に形成されており、前記粒状芯部若しく
は前記被覆層部又は前記粒状芯部及び前記被覆層部に防
黴剤が含有されており、さらに前記粒状芯部若しくは前
記被覆層部又は前記粒状芯部及び前記被覆層部には、蒸
散性ピレスロイド系防虫剤が含有されていることを特徴
とする動物用排泄物処理材にあり、さらに加えて、本発
明は、3mm以下の粒度のポリエチレンテレフタレート
廃材粉、ポリエチレン廃材粉、ポリプロピレン廃材粉、
ポリアクリロニトリル廃材粉、ナイロン廃材粉若しくは
ポリエステル廃材粉又はこれら廃材粉の二種以上からな
るプラスチック廃材粉と、前記プラスチック廃材粉より
少量の吸水性樹脂と、小麦粉、澱粉、コーンスターチ、
カルボキシメチルセルロース、プルラン若しくはゼラチ
ン又はこれら二以上の配合物質とを含有して粒状に形成
されている粒状芯部を有すると共に、紙粉及び吸水性樹
脂を含有して粒状芯部の表面上に形成されている被覆層
部を有し、前記粒状芯部と被覆層部とにより粒状に形成
されており、前記粒状芯部若しくは前記被覆層部又は前
記粒状芯部及び前記被覆層部に防黴剤が含有されてお
り、さらに前記粒状芯部若しくは前記被覆層部又は前記
粒状芯部及び前記被覆層部には、蒸散性ピレスロイド系
防虫剤が含有されていることを特徴とする動物用排泄物
処理材にある。
That is, the present invention provides a polyethylene terephthalate waste powder, a polyethylene waste powder having a particle size of 3 mm or less,
Polypropylene waste powder, polyacrylonitrile waste powder,
An animal animal characterized by being formed into a granular form containing nylon waste material powder, polyester waste material powder, or a plastic waste material powder composed of two or more of these waste material powders, and a smaller amount of a water-absorbent resin than the plastic waste material powder. In the excrement disposal material, and the present invention, polyethylene terephthalate waste material powder having a particle size of 3 mm or less, polyethylene waste material powder,
Polypropylene waste powder, polyacrylonitrile waste powder,
Nylon waste material powder or polyester waste material powder or plastic waste material powder consisting of two or more of these waste material powders, a small amount of a water-absorbent resin than the plastic waste material powder, wheat flour,
Starch, corn starch, carboxymethyl cellulose,
An animal excrement disposal material characterized by being formed in a granular form containing pullulan or gelatin or a compound substance having two or more of these lubricating, adhesive and water retaining functions. Polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder having a particle size of, and plastic waste powder composed of two or more of these waste powders, and a smaller amount than the plastic waste powder A water-absorbent resin and containing a granular core formed in a granular form, and having a coating layer portion formed on the surface of the granular core containing paper powder and a water-absorbent resin, An animal excrement disposal material characterized by being formed in a granular form by a granular core portion and a coating layer portion. The present invention provides a plastic waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polypropylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder or a polyester waste material powder, or a plastic waste material powder composed of two or more of these waste material powders; A granular core formed into a granular form containing a smaller amount of a water-absorbent resin than waste material powder and wheat flour, starch, corn starch, carboxymethylcellulose, pullulan or gelatin or a compounded substance having two or more of these lubricating, adhesive and water retaining functions. Having a coating layer portion formed on the surface of the granular core portion containing paper powder and a water-absorbent resin, and having a granular shape formed by the granular core portion and the coating layer portion. The animal excrement disposal material is characterized in that, in addition to the The particle size of polyethylene terephthalate waste powder in the lower, polyethylene waste powder,
Polypropylene waste powder, polyacrylonitrile waste powder,
Nylon waste material powder or polyester waste material or plastic waste material powder consisting of two or more of these waste material powders, and having a granular core portion formed in a granular form containing a small amount of a water-absorbent resin than the plastic waste material powder, It has a coating layer portion formed on the surface of the granular core portion containing paper powder and a water-absorbent resin, and is formed in a granular shape by the granular core portion and the coating layer portion, and the granular core portion or An animal excrement disposal material characterized in that the coating layer portion or the granular core portion and the coating layer portion contain a fungicide, and the present invention further provides polyethylene having a particle size of 3 mm or less. From terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder, polyester waste powder or two or more of these waste powders Waste plastic powder, a water-absorbent resin in a smaller amount than the plastic waste powder, and wheat flour, starch, corn starch, carboxymethyl cellulose, pullulan or gelatin, or a combination of two or more of these substances having lubricating, adhesive and water retaining functions. It has a granular core portion formed in a granular form, and has a coating layer portion formed on the surface of the granular core portion containing paper powder and a water-absorbent resin, and the granular core portion and the coating layer portion The granular core portion or the coating layer portion or the granular core portion and the coating layer portion contain a fungicide in the animal excrement disposal material. Further, the present invention provides a plastic waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polypropylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder, a polyester waste material powder, or two or more kinds of these waste material powders. And having a granular core formed in a granular form containing a smaller amount of a water-absorbent resin than the plastic waste material powder, and being formed on the surface of the granular core containing a paper powder and a water-absorbent resin. The granular core and the coating layer are formed in a granular form, and the particulate core or the coating layer or the granular core and the coating layer have a transpirable pyrethroid-based insect repellent. And an animal excrement disposal material characterized by containing an agent. Phthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder or plastic waste powder consisting of two or more of these waste powders, and a small amount of a water-absorbent resin than the plastic waste powder , Wheat flour, starch, corn starch, carboxymethylcellulose, pullulan or gelatin or a combination of two or more of them having a lubricating, adhesive and water-retaining function. A coating layer portion formed on the surface of the granular core portion containing a conductive resin, wherein the granular core portion and the coating layer portion are formed in a granular form, and the granular core portion or the coating layer portion Or that the particulate core and the coating layer contain a transpirable pyrethroid-based insect repellent In the animal excrement disposal material characterized by the present invention, furthermore, the present invention provides a polyethylene terephthalate waste material powder, a polyethylene waste material powder, a polypropylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder or a polyester waste material powder having a particle size of 3 mm or less. A plastic waste material powder composed of two or more of these waste material powders, and having a granular core formed in a granular form containing a smaller amount of a water-absorbent resin than the plastic waste material powder, and containing paper powder and a water-absorbent resin. And a coating layer portion formed on the surface of the granular core portion, wherein the granular core portion and the coating layer portion are formed in a granular form, and the granular core portion or the coating layer portion or the granular core portion is formed in a granular form. Part and the coating layer portion contain a fungicide, and the granular core portion or the coating layer portion or the granular core portion and the coating layer portion An animal excrement disposal material characterized by containing a transpirable pyrethroid-based insect repellent, and in addition, the present invention provides a polyethylene terephthalate waste powder, a polyethylene waste powder, and a polypropylene waste material having a particle size of 3 mm or less. powder,
Polyacrylonitrile waste powder, nylon waste powder or polyester waste powder or plastic waste powder consisting of two or more of these waste powders, and a water-absorbent resin in a smaller amount than the plastic waste powder, wheat flour, starch, corn starch,
Having a granular core formed in a granular form containing carboxymethylcellulose, pullulan or gelatin or two or more of these compounded substances, and containing paper powder and a water-absorbent resin, formed on the surface of the granular core. Having a coating layer portion, wherein the granular core portion and the coating layer portion are formed in a granular form, and a fungicide is added to the granular core portion or the coating layer portion or the granular core portion and the coating layer portion. Animal excrement disposal material, wherein the particulate core or the coating layer or the particulate core and the coating layer further contain a transpirable pyrethroid-based insect repellent. It is in.

【0007】そして本発明は、3mm以下の粒度のポリ
エチレンテレフタレート廃材粉、ポリエチレン廃材粉、
ポリプロピレン廃材粉、ポリアクリロニトリル廃材粉、
ナイロン廃材粉若しくはポリエステル廃材粉又はこれら
廃材粉の二種以上からなるプラスチック廃材粉と、無機
質配合材料粉と、前記プラスチック廃材粉より少量の吸
水性樹脂とを含有して粒状に形成されていることを特徴
とする動物用排泄物処理材にあり、また、本発明は、3
mm以下の粒度のポリエチレンテレフタレート廃材粉、
ポリエチレン廃材粉、ポリプロピレン廃材粉、ポリアク
リロニトリル廃材粉、ナイロン廃材粉若しくはポリエス
テル廃材粉又はこれら廃材粉の二種以上からなるプラス
チック廃材粉と、無機質配合材料粉と、前記プラスチッ
ク廃材粉より少量の吸水性樹脂と、小麦粉、澱粉、コー
ンスターチ、カルボキシメチルセルロース、プルラン若
しくはゼラチン又はこれら二以上の潤滑、接着及び保水
機能を有する配合物質とを含有して粒状に形成されてい
ることを特徴とする動物用排泄物処理材にあり、さら
に、本発明は、3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂とを
含有して粒状に形成されている粒状芯部を有すると共
に、紙粉及び吸水性樹脂を含有して粒状芯部の表面上に
形成されている被覆層部を有し、前記粒状芯部と被覆層
部とにより粒状に形成されていることを特徴とする動物
用排泄物処理材にあり、さらにまた、本発明は、3mm
以下の粒度のポリエチレンテレフタレート廃材粉、ポリ
エチレン廃材粉、ポリプロピレン廃材粉、ポリアクリロ
ニトリル廃材粉、ナイロン廃材粉若しくはポリエステル
廃材粉又はこれら廃材粉の二種以上からなるプラスチッ
ク廃材粉と、無機質配合材料粉と、前記プラスチック廃
材粉より少量の吸水性樹脂と、小麦粉、澱粉、コーンス
ターチ、カルボキシメチルセルロース、プルラン若しく
はゼラチン又はこれら二以上の潤滑、接着及び保水機能
を有する配合物質とを含有して粒状に形成されている粒
状芯部を有すると共に、紙粉及び吸水性樹脂を含有して
粒状芯部の表面上に形成されている被覆層部を有し、前
記粒状芯部と被覆層部とにより粒状に形成されているこ
とを特徴とする動物用排泄物処理材にあり、さらに加え
て、本発明は、3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂とを
含有して粒状に形成されている粒状芯部を有すると共
に、紙粉及び吸水性樹脂を含有して粒状芯部の表面上に
形成されている被覆層部を有し、前記粒状芯部と被覆層
部とにより粒状に形成されており、前記粒状芯部若しく
は前記被覆層部又は前記粒状芯部及び前記被覆層部に防
黴剤が含有されていることを特徴とする動物用排泄物処
理材にあり、そしてまた、本発明は、3mm以下の粒度
のポリエチレンテレフタレート廃材粉、ポリエチレン廃
材粉、ポリプロピレン廃材粉、ポリアクリロニトリル廃
材粉、ナイロン廃材粉若しくはポリエステル廃材粉又は
これら廃材粉の二種以上からなるプラスチック廃材粉
と、無機質配合材料粉と、前記プラスチック廃材粉より
少量の吸水性樹脂と、小麦粉、澱粉、コーンスターチ、
カルボキシメチルセルロース、プルラン若しくはゼラチ
ン又はこれら二以上の潤滑、接着及び保水機能を有する
配合物質とを含有して粒状に形成されている粒状芯部を
有すると共に、紙粉及び吸水性樹脂を含有して粒状芯部
の表面上に形成されている被覆層部を有し、前記粒状芯
部と被覆層部とにより粒状に形成されており、前記粒状
芯部若しくは前記被覆層部又は前記粒状芯部及び前記被
覆層部に防黴剤が含有されていることを特徴とする動物
用排泄物処理材にあり、さらに、本発明は、3mm以下
の粒度のポリエチレンテレフタレート廃材粉、ポリエチ
レン廃材粉、ポリプロピレン廃材粉、ポリアクリロニト
リル廃材粉、ナイロン廃材粉若しくはポリエステル廃材
粉又はこれら廃材粉の二種以上からなるプラスチック廃
材粉と、無機質配合材料粉と、前記プラスチック廃材粉
より少量の吸水性樹脂とを含有して粒状に形成されてい
る粒状芯部を有すると共に、紙粉及び吸水性樹脂を含有
して粒状芯部の表面上に形成されている被覆層部を有
し、前記粒状芯部と被覆層部とにより粒状に形成されて
おり、前記粒状芯部若しくは前記被覆層部又は前記粒状
芯部及び前記被覆層部に蒸散性ピレスロイド系防虫剤が
含有されていることを特徴とする動物用排泄物処理材に
あり、さらにまた、本発明は、3mm以下の粒度のポリ
エチレンテレフタレート廃材粉、ポリエチレン廃材粉、
ポリプロピレン廃材粉、ポリアクリロニトリル廃材粉、
ナイロン廃材粉若しくはポリエステル廃材粉又はこれら
廃材粉の二種以上からなるプラスチック廃材粉と、無機
質配合材料粉と、前記プラスチック廃材粉より少量の吸
水性樹脂と、小麦粉、澱粉、コーンスターチ、カルボキ
シメチルセルロース、プルラン若しくはゼラチン又はこ
れら二以上の潤滑、接着及び保水機能を有する配合物質
とを含有して粒状に形成されている粒状芯部を有すると
共に、紙粉及び吸水性樹脂を含有して粒状芯部の表面上
に形成されている被覆層部を有し、前記粒状芯部と被覆
層部とにより粒状に形成されており、前記粒状芯部若し
くは前記被覆層部又は前記粒状芯部及び前記被覆層部に
蒸散性ピレスロイド系防虫剤が含有されていることを特
徴とする動物用排泄物処理材にあり、さらに加えて、本
発明は、3mm以下の粒度のポリエチレンテレフタレー
ト廃材粉、ポリエチレン廃材粉、ポリプロピレン廃材
粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉若し
くはポリエステル廃材粉又はこれら廃材粉の二種以上か
らなるプラスチック廃材粉と、無機質配合材料粉と、前
記プラスチック廃材粉より少量の吸水性樹脂とを含有し
て粒状に形成されている粒状芯部を有すると共に、紙粉
及び吸水性樹脂を含有して粒状芯部の表面上に形成され
ている被覆層部を有し、前記粒状芯部と被覆層部とによ
り粒状に形成されており、前記粒状芯部若しくは前記被
覆層部又は前記粒状芯部及び前記被覆層部に防黴剤が含
有されており、さらに前記粒状芯部若しくは前記被覆層
部又は前記粒状芯部及び前記被覆層部には、蒸散性ピレ
スロイド系防虫剤が含有されていることを特徴とする動
物用排泄物処理材にある。そしてさらに,本発明は、3
mm以下の粒度のポリエチレンテレフタレート廃材粉、
ポリエチレン廃材粉、ポリプロピレン廃材粉、ポリアク
リロニトリル廃材粉、ナイロン廃材粉若しくはポリエス
テル廃材粉又はこれら廃材粉の二種以上からなるプラス
チック廃材粉と、無機質配合材料粉と、前記プラスチッ
ク廃材粉より少量の吸水性樹脂と、小麦粉、澱粉、コー
ンスターチ、カルボキシメチルセルロース、プルラン若
しくはゼラチン又はこれら二以上の潤滑、接着及び保水
機能を有する配合物質とを含有して粒状に形成されてい
る粒状芯部を有すると共に、紙粉及び吸水性樹脂を含有
して粒状芯部の表面上に形成されている被覆層部を有
し、前記粒状芯部と被覆層部とにより粒状に形成されて
おり、前記粒状芯部若しくは前記被覆層部又は前記粒状
芯部及び前記被覆層部に防黴剤が含有されており、さら
に前記粒状芯部若しくは前記被覆層部又は前記粒状芯部
及び前記被覆層部には、蒸散性ピレスロイド系防虫剤が
含有されていることを特徴とする動物用排泄物処理材に
ある。
The present invention provides a polyethylene terephthalate waste powder having a particle size of 3 mm or less, a polyethylene waste powder,
Polypropylene waste powder, polyacrylonitrile waste powder,
Nylon waste material powder or polyester waste material powder or a plastic waste material powder composed of two or more of these waste material powders, an inorganic compounding material powder, and a smaller amount of a water-absorbent resin than the plastic waste material powder are formed in a granular form. An animal excrement disposal material characterized by the following features:
mm or less particle size polyethylene terephthalate waste material powder,
Polyethylene waste material powder, polypropylene waste material powder, polyacrylonitrile waste material powder, nylon waste material powder or polyester waste material powder or plastic waste material powder composed of two or more of these waste material powders, inorganic compounded material powder, and a smaller amount of water absorption than the plastic waste material powder Animal excrement characterized by being formed into granules containing a resin and wheat flour, starch, corn starch, carboxymethylcellulose, pullulan or gelatin or a compounded substance having two or more lubricating, adhesive and water retaining functions. In the treated material, the present invention further comprises a polyethylene terephthalate waste powder, a polyethylene waste powder, a polypropylene waste powder, a polyacrylonitrile waste powder, a nylon waste powder or a polyester waste powder having a particle size of 3 mm or less, or two or more kinds of these waste powders. Naru Plasti Waste powder, inorganic blended material powder, and a granular core containing a smaller amount of water-absorbent resin than the plastic waste powder, and a granular core containing paper powder and water-absorbent resin. An animal excrement disposal material having a coating layer portion formed on the surface of the core portion, wherein the material is formed in a granular shape by the granular core portion and the coating layer portion. The present invention is 3 mm
Polyethylene terephthalate waste powder of the following particle size, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder or plastic waste powder composed of two or more of these waste powders, and inorganic compounding material powder, A water-absorbent resin in a smaller amount than the above-mentioned plastic waste material powder, and flour, starch, cornstarch, carboxymethylcellulose, pullulan or gelatin or a mixture of two or more of these compounds having lubricating, adhesive and water-retaining functions are formed into granules. Having a granular core, having a coating layer portion formed on the surface of the granular core portion containing paper powder and a water-absorbing resin, and being formed in a granular shape by the granular core portion and the coating layer portion. Animal excrement disposal material characterized by the fact that m or less, polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder or plastic waste powder comprising at least two of these waste powders, and inorganic compounding material powder. A plastic core having a granular core containing a smaller amount of a water-absorbent resin than the plastic waste material powder, and having a paper core and a water-absorbent resin formed on the surface of the granular core. It has a coating layer portion, and is formed in a granular shape by the granular core portion and the coating layer portion, and the fungicide is contained in the granular core portion or the coating layer portion or the granular core portion and the coating layer portion. The present invention also relates to an animal excrement disposal material, and the present invention provides a polyethylene terephthalate waste powder having a particle size of 3 mm or less, Polyethylene waste material powder, polypropylene waste material powder, polyacrylonitrile waste material powder, nylon waste material powder or polyester waste material powder or plastic waste material powder composed of two or more of these waste material powders, inorganic compounded material powder, and a smaller amount of water absorption than the plastic waste material powder Resin, flour, starch, corn starch,
A granular core containing carboxymethylcellulose, pullulan or gelatin or a compound substance having two or more of these features of lubrication, adhesion and water retention, and having a granular core containing paper powder and a water-absorbent resin. It has a coating layer portion formed on the surface of the core portion, is formed in a granular shape by the granular core portion and the coating layer portion, and the granular core portion or the coating layer portion or the granular core portion and the An animal excrement disposal material characterized in that the coating layer portion contains an antifungal agent, and the present invention further provides a polyethylene terephthalate waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polypropylene waste material powder, Polyacrylonitrile waste powder, nylon waste powder, polyester waste powder, or plastic waste powder composed of two or more of these waste powders, and mineral distribution It has a granular core which is formed in a granular form containing a material powder and a smaller amount of a water-absorbent resin than the plastic waste material powder, and is formed on the surface of the granular core which contains a paper powder and a water-absorbent resin. Having a coating layer portion that is formed, and is formed in a granular shape by the granular core portion and the coating layer portion, and the transpirable pyrethroid is formed on the granular core portion or the coating layer portion or the granular core portion and the coating layer portion. Animal excrement disposal material characterized by containing a systemic insect repellent, furthermore, the present invention provides a polyethylene terephthalate waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder,
Polypropylene waste powder, polyacrylonitrile waste powder,
Nylon waste material powder or polyester waste material powder or plastic waste material powder composed of two or more of these waste material powders, inorganic compounding material powder, water-absorbent resin in a smaller amount than the plastic waste material powder, wheat flour, starch, corn starch, carboxymethyl cellulose, pullulan Or, having a granular core formed in a granular form containing gelatin or a compounded substance having two or more of these lubricating, adhesive and water retaining functions, and a surface of the granular core containing paper powder and a water-absorbing resin. It has a coating layer portion formed thereon, and is formed in a granular shape by the granular core portion and the coating layer portion, and the granular core portion or the coating layer portion or the granular core portion and the coating layer portion An animal excrement disposal material characterized by containing a transpirable pyrethroid-based insect repellent. Polyethylene terephthalate waste material powder, polyethylene waste material powder, polypropylene waste material powder, polyacrylonitrile waste material powder, nylon waste material powder or polyester waste material powder having a particle size of, or a plastic waste material powder comprising two or more kinds of these waste material powders, and an inorganic compounding material powder, A coating layer having a granular core formed in a granular form containing a smaller amount of water-absorbent resin than plastic waste material powder, and being formed on the surface of the granular core containing paper dust and the water-absorbent resin Portion, the granular core and the coating layer are formed in a granular form, the granular core or the coating layer or the granular core and the coating layer contains a fungicide. Further, the granular core or the coating layer or the granular core and the coating layer may contain a transpirable pyrethroid-based insect repellent. In mammalian excrement treating article characterized by. And furthermore, the present invention
mm or less particle size polyethylene terephthalate waste material powder,
Polyethylene waste material powder, polypropylene waste material powder, polyacrylonitrile waste material powder, nylon waste material powder or polyester waste material powder or plastic waste material powder composed of two or more of these waste material powders, inorganic compounded material powder, and a smaller amount of water absorption than the plastic waste material powder A paper core having a granular core containing a resin, wheat flour, starch, corn starch, carboxymethyl cellulose, pullulan or gelatin or a combination of two or more of these having lubricating, adhesive and water-retaining functions; And a coating layer portion formed on the surface of the granular core portion containing a water-absorbent resin, wherein the granular core portion and the coating layer portion are formed in a granular shape by the granular core portion and the coating layer portion. A layer portion or the granular core portion and the coating layer portion contain a fungicide, and the granular core portion It is the covering layer section, or the granular core section and the covering layer section is in the animal excrement treatment material, wherein the vaporizable pyrethroid insecticide is contained.

【0008】[0008]

【発明の実施の形態】本発明は、高発熱量のプラスチッ
ク廃材粉を、動物用排泄物処理材の原料として活用する
ことにより、焼却可能にするものである。本発明におい
て、動物用排泄物処理材は、3mm以下の粒度、好まし
くは1mm以下の粒度のプラスチック廃材粉、有機質配
合材料、前記プラスチック廃材粉より少量の吸水性樹脂
を、配合して造粒された粒状芯部のみ又は該粒状芯部及
び該粒状芯部を被覆する被覆層部からなる粒状物に形成
され、プラスチック廃材と無機材料とを混合して造粒す
ることにより形成することができる。
DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention makes it possible to incinerate plastic waste material powder having a high calorific value as a raw material for animal excrement disposal materials. In the present invention, the animal excrement disposal material is granulated by blending a plastic waste material powder having a particle size of 3 mm or less, preferably a particle size of 1 mm or less, an organic compounding material, and a smaller amount of a water absorbent resin than the plastic waste material powder. It can be formed into a granular material composed of only the granular core portion or the granular core portion and a coating layer covering the granular core portion, and can be formed by mixing a plastic waste material and an inorganic material and granulating.

【0009】本発明において、プラスチック廃材は、一
種又は二種以上のプラスチック廃材を使用することがで
きる。このようなプラスチック廃材としては、ポリエチ
レンテレフタレート廃材(例えば、乾燥時発熱量:約
5,500キロカロリー/kg)、ポリエチレン廃材
(例えば、乾燥時発熱量:約9,950乃至10,72
0キロカロリー/kg)、ポリブロピレン廃材(例え
ば、乾燥時発熱量:約10,030乃至10,810キ
ロカロリー/kg)、ポリアクリロニトリル廃材、ナイ
ロン廃材及びポリエステル廃材等の5,500キロカロ
リー/kg以上の発熱量のプラスチック廃材がある。こ
のように発熱量の高いプラスチック廃材を、動物用排泄
物処理材の原料とすることにより、濡れた状態で1,0
00乃至2,500キロカロリー/kgの焼却可能の発
熱量を達成することができる。
In the present invention, one or more kinds of plastic waste can be used as the plastic waste. Examples of such plastic waste materials include polyethylene terephthalate waste material (for example, calorific value when dried: about 5,500 kcal / kg) and polyethylene waste material (for example, calorific value when dried: about 9,950 to 10,72).
0 kcal / kg), 5,500 kcal / kg or more of waste polypropylene (eg, calorific value when dried: about 10,030 to 10,810 kcal / kg), polyacrylonitrile waste, nylon waste, polyester waste, etc. Plastic waste. By using plastic waste having a high calorific value as a raw material for animal excrement disposal materials, 1,0
An incineration calorific value of 00 to 2,500 kcal / kg can be achieved.

【0010】本発明において、このようなプラスチック
廃材は、粉砕して、直径3mm以下のプラスチック廃材
粉とすることにより、吸水及び保水能力が著しく向上す
ることが分かった。したがって、本発明においては、プ
ラスチック廃材は3mm以下の粉体に形成される。プラ
スチック廃材が軟質プラスチックの場合は、細かく粉砕
し難いので、3mm以下の粒度に粉砕されるが、吸水及
び保水能力を高める上では、2mm以下の粒度、さらに
好ましくは、1mm以下の粒度とするのが好ましい。プ
ラスチック廃材が硬質ブラスチックである場合には、粉
砕し易いところから、3mm以下の粒度に粉砕される
が、吸水及び保水能力を高める上では、1mm以下の粒
度に粉砕するのが好ましい。
In the present invention, it has been found that such a plastic waste material is pulverized into a plastic waste material powder having a diameter of 3 mm or less, thereby significantly improving the water absorption and water retention capabilities. Therefore, in the present invention, the plastic waste material is formed into a powder having a size of 3 mm or less. If the plastic waste material is a soft plastic, it is difficult to pulverize finely, so it is pulverized to a particle size of 3 mm or less.However, in order to enhance water absorption and water retention capacity, a particle size of 2 mm or less, more preferably a particle size of 1 mm or less. Is preferred. When the plastic waste material is a hard plastic, it is pulverized to a particle size of 3 mm or less because it is easily pulverized. However, it is preferable to pulverize the plastic waste material to a particle size of 1 mm or less from the viewpoint of increasing water absorption and water retention capacity.

【0011】本発明において、プラスチック廃材の発熱
量を低下させると共に、製品の猫砂に吸着性能及び吸収
性能を持たせるために、有機質配合材料が混合される。
このような有機質配合材料としては、高い発熱量のプラ
スチック廃材を使用するところから、プラスチック廃材
よりも、低い発熱量を有する有機質廃材が使用される。
このような有機質廃材としては、3,000乃至6,0
00キロカロリー/kgの範囲内の有機質廃材が好まし
い。このような有機質廃材としては、例えば、茶殻(例
えば、乾燥時の発熱量、約5,290キロカロリー/k
g)、コーヒー液抽出残渣(例えば、乾燥時の発熱量、
約5,600キロカロリー/kg)、紙粉(例えば、乾
燥時発熱量:約3,500乃至4,000キロカロリー
/kg)、木粉(例えば、乾燥時発熱量、約3,000
キロカロリー/kg)、α澱粉(4,200キロカロリ
ー/kg)又は製紙スラッジ(2,000キロカロリー
/kg)或いはこれら二種以上の混合物がある。
In the present invention, an organic compounding material is mixed in order to reduce the calorific value of the plastic waste material and to make the cat sand of the product have an adsorption performance and an absorption performance.
As such an organic compounding material, an organic waste material having a lower calorific value than a plastic waste material is used because a plastic waste material having a high calorific value is used.
Such organic waste materials include 3,000 to 6,0
Organic waste within the range of 00 kcal / kg is preferred. Such organic waste materials include, for example, tea leaves (for example, calorific value when dried, about 5,290 kcal / k)
g), coffee liquid extraction residue (for example, calorific value during drying,
About 5,600 kcal / kg), paper powder (eg, calorific value when dry: about 3,500 to 4,000 kcal / kg), wood flour (eg, calorific value when dry, about 3,000)
Kcal / kg), alpha starch (4,200 kcal / kg) or papermaking sludge (2,000 kcal / kg) or a mixture of two or more thereof.

【0012】本発明において使用される紙粉は、紙管の
廃材の粉砕物、製紙工場の廃棄パルプの粉砕物、パンチ
屑の粉砕物、古紙の粉砕物及びパルプ製の不織布の粉砕
物、並びに綿廃材、羊毛廃材及び麻廃材の粉砕物であ
る。紙粉は3mm以下の粒度で使用することができる
が、1mm以上の粒度で使用すると、均一な混合が容易
となり、また紙粉の吸水及び保水性を更に増加させるこ
とができるので好ましい。本発明において、プラスチッ
ク廃材粉に製材場から排出される木屑の粉体即ち木粉を
配合することができる。木粉は3mm以下の粒度で使用
することができるが、1mm以下の粒度で使用すると、
均一な混合が容易となり、また木粉の吸水及び保水性を
更に増加させることができるので好ましい。また、本発
明において、木粉として、ヒバ材の木屑及び/又は桧材
の木屑の粉体を使用すと、ヒバ材及び/又は桧材は、虫
の忌避作用を有するので、虫を忌避することができて好
ましい。この場合、木粉の量は、粒状芯部の3重量%以
上であり、虫の忌避材としての作用を強めるためには、
5重量%以上であるのが好ましい。ヒバ材の木屑及び/
又は桧材の木屑の使用は、動物用排泄物処理材に、消臭
機能、防虫機能、防黴機能及び香料機能を持たせること
ができる点からも好ましい。
The paper powder used in the present invention is a crushed material of paper tube waste material, a crushed material of waste pulp from a paper mill, a crushed material of punch waste, a crushed material of waste paper and a crushed material of pulp nonwoven fabric, and It is a crushed product of cotton waste material, wool waste material and hemp waste material. The paper powder can be used in a particle size of 3 mm or less, but it is preferable to use the paper powder in a particle size of 1 mm or more because uniform mixing becomes easy and the water absorption and water retention of the paper powder can be further increased. In the present invention, wood waste powder, that is, wood flour, discharged from a sawmill can be mixed with the plastic waste material powder. Wood flour can be used with a particle size of 3 mm or less, but when used with a particle size of 1 mm or less,
This is preferable because uniform mixing becomes easy and the water absorption and water retention of the wood flour can be further increased. Further, in the present invention, when powder of hiba wood chips and / or hinoki wood chips is used as the wood powder, the hiba wood and / or the hinoki wood have an insect repelling action, and thus repel insects. Is preferred. In this case, the amount of wood flour is 3% by weight or more of the granular core, and in order to strengthen the action as an insect repellent,
It is preferably at least 5% by weight. Hiba wood chips and / or
Alternatively, the use of wood chips of hinoki wood is preferable from the viewpoint that the animal excrement disposal material can be provided with a deodorizing function, an insect control function, a fungicide function and a fragrance function.

【0013】本発明において、使用するコーヒー液抽出
残渣としては、缶入り又はペットボトル入りコーヒー製
造時のコーヒー液抽出残渣、インスタントコーヒー製造
時のコーヒー液抽出残渣などの、焙煎コーヒー豆からの
コーヒー液抽出時に大量に生じる廃棄物のコーヒー液抽
出残渣がある。コーヒー液抽出残渣は粒度が3mm以下
の粒度で使用することができるが、1mm以下の粒度と
すると、均一な混合が容易となり、またコーヒー液抽出
残渣の吸水及び保水性を増加することができるので好ま
しい。本発明において、使用する茶殻としては、缶入り
又はペットボトル入り茶の製造時にお茶の葉からお茶製
造時に大量に生じる廃棄物の茶殻がある。茶殻は、粉砕
しないでその侭使用することができるが、3mm以下の
粒度又は好ましくは1mm以下の小さい粒度とすると、
均一な混合が容易となり、また茶殻の吸水及び保水性が
増加するので好ましい。
In the present invention, the coffee liquid extraction residue to be used includes coffee liquid extraction residues from canned or plastic bottled coffee production, coffee liquid extraction residue from instant coffee production, and the like from roasted coffee beans. There is a large amount of waste coffee liquid extraction residue generated during liquid extraction. The coffee liquid extraction residue can be used with a particle size of 3 mm or less, but a particle size of 1 mm or less facilitates uniform mixing and increases the water absorption and water retention of the coffee liquid extraction residue. preferable. In the present invention, examples of the tea husks used include waste tea husks generated in large quantities during the production of tea from tea leaves in the production of canned or PET bottled tea. Tea husks can be used as is without grinding, but with a particle size of 3 mm or less, or preferably a small particle size of 1 mm or less,
This is preferable because uniform mixing becomes easy and the water absorption and water retention of the tea husks increase.

【0014】本発明において、使用する無機質配合材料
としては、ベントナイト、ゼオライト、FJライト(商
品名)等のパルプスラッジの再燃焼焼却灰、汚泥や生ゴ
ミ等の再燃焼焼却灰、バーミキュライト、パーライト等
がある。本発明において、無機質配合材料の使用量は、
動物用排泄物処理材を使用後焼却して、発生する灰分量
が少なく、例えば40重量%以下となるように加えられ
るのが好ましい。この場合、無機質配合材料も3mm以
下の粒度で使用することができるが、無機質配合材料を
1mm以下の粒度で使用すると、造粒時の原料材料の混
合が容易となるので好ましい。本発明において、猫砂に
防虫機能を持たせるために、防虫機能を有する蒸散性の
ピレスロイド系防虫剤、例えばエンペンスリンを、プラ
スチック廃材に混合して使用することができる。
In the present invention, the inorganic compounding materials used include reburning incinerated ash of pulp sludge such as bentonite, zeolite, and FJ light (trade name), reburning incinerated ash of sludge and garbage, vermiculite, perlite and the like. There is. In the present invention, the amount of the inorganic compounding material used is
It is preferable that the animal excrement disposal material is incinerated after use and added so that the amount of generated ash is small, for example, 40% by weight or less. In this case, the inorganic compounding material can also be used in a particle size of 3 mm or less, but it is preferable to use the inorganic compounding material in a particle size of 1 mm or less because mixing of the raw materials during granulation becomes easy. In the present invention, a transpirable pyrethroid-based insect repellent having an insect repellent function, for example, empensrin, can be used by mixing it with plastic waste material in order to give the cat sand an insect repellent function.

【0015】本発明において使用される蒸散性のピレス
ロイド系防虫剤のエンペンスリンは、接触毒作用を有
し、殺虫成分であるが、温血動物に対しては比較的無害
であるので、防虫剤として使用されているものである。
エンペンスリンは、動物の体に接触して、ダニ及び蚤等
の害虫を動物の体から追い出すように作用し、その構造
式は、下式で示される。
The transpirable pyrethroid-based insect repellent empensulin used in the present invention has a contact toxic effect and is an insecticidal component, but is relatively harmless to warm-blooded animals. What is used.
Empensulin contacts the animal body and acts to expel pests such as mites and fleas from the animal body, and its structural formula is represented by the following formula.

【0016】[0016]

【化1】 Embedded image

【0017】本発明において、この粒状の動物用排泄物
処理材に防虫機能を持たせるために、蒸散性のピレスロ
イド系防虫剤は、粒状芯部及び/又は被覆層部とに含有
させることができる。蒸散性ピレスロイド防虫剤のエン
ペンスリンの含有量は、0.05重量%以上であり、好
ましくは0.4重量%以上である。しかし、蒸散性のピ
レスロイド防虫剤は比較的高価であり、その含有量は1
重量%以下とするのが好ましい。本発明において、防虫
機能を有する動物用排泄物処理材とするために、虫の忌
避成分として、蒸散性のピレスロイドのエンペンスリン
を配合させる場合には、エンペンスリンを、イソパラフ
ィン系溶剤、炭化水素溶剤、ハロゲン化炭化水素溶剤又
はエステル類の溶剤等の非アルコール系有機溶剤に分散
又は溶解させて、プラスチック廃材及び/又は無機質配
合材料に配合させることができる。このように動物用排
泄物処理材にエンペンスリンを配合することにより、排
泄時に、動物用排泄物処理材から防虫機能を有するエン
ペンスリンが蒸発して排泄時の動物の体に接触し、動物
の体に付着する該害虫を追い払うことができる。
In the present invention, a transpirable pyrethroid-based insect repellent can be contained in the particulate core and / or the coating layer in order to impart the insect repellent function to the granular animal excrement disposal material. . The content of empensulin in the transpirable pyrethroid insecticide is at least 0.05% by weight, preferably at least 0.4% by weight. However, transpirable pyrethroid insecticides are relatively expensive, and their content is 1%.
% By weight or less. In the present invention, in order to make an animal excrement disposal material having an insect repellent function, in the case of blending transpirable pyrethroid emempsulin as a repellent component of insects, when empensrin is used, isoparaffin-based solvent, hydrocarbon solvent, halogen It can be dispersed or dissolved in a non-alcoholic organic solvent such as a fluorinated hydrocarbon solvent or a solvent of esters, and blended with the plastic waste material and / or the inorganic compounding material. By blending empensin into the animal excrement disposal material in this way, at the time of excretion, empensulin having an insect repellent function evaporates from the animal excrement disposal material and comes into contact with the animal body at the time of excretion. The attached pests can be repelled.

【0018】本発明において、蒸散性ピレスロイド系防
虫剤のエンペンスリンを単独で動物用排泄物処理材に配
合する場合には、粒状芯部については、プラスチック廃
材又は無機質配合材料或いはこれらの混合物に、エンペ
ンスリンの溶媒溶液を加えて、撹拌混合するか、又は造
粒過程で、エンペンスリンの溶媒溶液を、該混合物に散
布又は噴霧することにより配合し、被覆層部について
は、紙粉或いは紙粉と高吸水性樹脂の混合物に、エンペ
ンスリン溶媒溶液を、散布、噴霧等により含浸させるか
又は被覆処理前に、紙粉或いは紙粉と高吸水性樹脂の混
合物に、浸漬、散布又は噴霧等により含浸させることに
より、配合することができる。
In the present invention, when empenthrin, a transpirable pyrethroid-based insect repellent, is incorporated alone into an animal excrement disposal material, the particulate core is added to the plastic waste material or the inorganic compound material, or a mixture of these materials. Or agitating and mixing, or in the granulation process, a solvent solution of empensulin is mixed by spraying or spraying on the mixture, and the coating layer portion is paper powder or paper powder and high water absorption. The mixture of water-soluble resins is impregnated with an empensulin solvent solution by spraying, spraying or the like, or by impregnating paper powder or a mixture of paper powder and a superabsorbent resin with a dip, spray or spray, etc., before the coating treatment. , Can be blended.

【0019】本発明において、プラスチック廃材粉に製
材場から排出される木屑の粉体を配合する場合、ヒバ材
の木屑及び桧材の木屑は、虫の忌避作用を有するヒノキ
チオール及びヒバ油を含有するので、動物用排泄物処理
材に、蒸散性のピレスロイド系防虫剤のエンペンスリン
に加えて、ヒバ材の木屑及び桧材の木屑といった製材の
廃材の粉体を、プラスチック廃材粉に加えることによ
り、蒸散性のピレスロイド系防虫剤の虫の忌避作用に、
ヒバ油及び/又はヒノキチオールの虫の忌避作用を加え
ることとなり、動物用排泄物処理材の虫の忌避作用を増
すことになる。ヒバ材の木屑及び桧材の木屑を虫の忌避
成分として、エンペンスリンと共に使用する場合には、
ヒバ材の木屑及び桧材の木屑は、その侭、又は一定の粒
径、例えば被覆層の場合は、0.5mm以下、好ましく
は、0.3mm以下に粉砕して、排泄物処理材に配合さ
れ、押出し造粒による粒状芯部の場合は、粒子が押出し
過程で圧潰されるので、1mm以下の粒径とするのが好
ましい。
In the present invention, when wood dust discharged from a sawmill is mixed with the plastic waste powder, the wood dust of the hiba wood and the wood of the hinoki wood contain hinokitiol and hiba oil having an insect repellent action. Therefore, in addition to the transpirable pyrethroid-based insect repellent empensrin, the waste material powder of sawn timber and wood chips of cypress wood is added to the animal excrement disposal material to the plastic waste material powder. Repellent effect of insecticide pyrethroid insecticide,
The insect repellent action of Hiba oil and / or hinokitiol will be added, and the insect repellent action of the animal excrement disposal material will be increased. When using Hiba wood chips and Hinoki wood chips as an insect repellent component together with Empensulin,
Hiba wood chips and cypress wood chips are crushed as they are or at a fixed particle size, for example, 0.5 mm or less, preferably 0.3 mm or less in the case of a coating layer, and mixed with the excrement disposal material. In the case of a granular core formed by extrusion granulation, the particle size is preferably 1 mm or less because the particles are crushed during the extrusion process.

【0020】本発明においては、動物用排泄物処理材の
被覆層部には、保存時の黴の発生を避けるために、殺菌
作用を有する物質を添加することができる。このような
殺菌作用を有する物質としては、食塩、ソルビン酸又は
その塩、プロピオン酸カルシウム、次亜塩素酸ナトリウ
ム及び/又は安息香酸又はその塩などの殺菌剤、防腐剤
及び防黴剤がある。また本発明なおいて、動物用排泄物
処理材の被覆層部には、保存時の黴の発生を避けるため
に、ヒバ材の木屑及び/又は桧材の木屑を防黴剤として
使用することができる。本発明において、動物用排泄物
処理材は、水分含有率を15重量%以下となるように乾
燥することにより、保管時の黴の発生を防止することが
できる。本発明において、使用する無機質配合材料の
中、ベントナイト及びゼオライトについては、灰分で4
0重量%以下の量で配合して、脱臭剤としての機能を持
たせることができる。さらに本発明においては、保水機
能を増強するために、吸水剤として、高吸水性樹脂を配
合するのが好ましい。
In the present invention, a substance having a bactericidal action can be added to the covering layer of the animal excrement disposal material in order to avoid the generation of mold during storage. Substances having such a bactericidal action include bactericides, preservatives and fungicides such as salt, sorbic acid or salts thereof, calcium propionate, sodium hypochlorite and / or benzoic acid or salts thereof. Further, in the present invention, in order to avoid generation of mold during storage, wood chips of hiba wood and / or wood chips of hinoki wood may be used as a fungicide in the covering layer portion of the animal excrement disposal material. it can. In the present invention, the animal excrement disposal material is dried so that the water content becomes 15% by weight or less, whereby the generation of mold during storage can be prevented. In the present invention, among the inorganic compounding materials used, bentonite and zeolite are ash content of 4%.
It can be blended in an amount of 0% by weight or less to have a function as a deodorant. Furthermore, in the present invention, in order to enhance the water retention function, it is preferable to mix a super absorbent resin as a water absorbing agent.

【0021】本発明において、吸水性樹脂は、成形時の
潤滑をよくするために添加される。本発明において、吸
水性樹脂は、高吸水性樹脂以外の吸水性樹脂及び高吸水
性樹脂を意味する。したがって、吸水性樹脂としては、
高吸水性樹脂及び高吸水性樹脂として不良品の樹脂のい
ずれも使用することができる。高吸水性樹脂として不良
品の樹脂を使用すると製造費用が安くなるので好まし
い。吸水性樹脂は、動物用排泄物処理材の成形時におい
て、被成形混合物の保水機能を高めると共に、被成形混
合物の造粒時の潤滑材として機能するために、粒状芯部
のプラスチック廃材に加えられる。この場合、吸水性樹
脂は、造粒物の10乃至3重量%とされるが、5重量%
以下とするのが好ましい。本発明において、動物用排泄
物処理材の粒状芯部に、高吸水性樹脂を配合物質として
使用すると、高吸水性樹脂は、排泄時に粒状芯部の周囲
から吸水して、膨潤し、保水するように作用するので、
被覆部の湿度を調整することができ好ましい。
In the present invention, a water-absorbing resin is added to improve lubrication during molding. In the present invention, the water-absorbent resin means a water-absorbent resin other than the superabsorbent resin and a superabsorbent resin. Therefore, as a water absorbent resin,
Both the superabsorbent resin and the defective resin can be used as the superabsorbent resin. It is preferable to use a defective resin as the superabsorbent resin because the production cost is reduced. The water-absorbing resin enhances the water-retaining function of the mixture to be molded when the animal excrement disposal material is molded, and functions as a lubricant when the mixture to be molded is granulated. Can be In this case, the water-absorbent resin is 10 to 3% by weight of the granulated material, but 5% by weight.
It is preferable to set the following. In the present invention, when the superabsorbent resin is used as a compound substance in the granular core of the animal excrement disposal material, the superabsorbent resin absorbs water from around the granular core during excretion, swells, and retains water. So that
It is preferable because the humidity of the covering portion can be adjusted.

【0022】本発明においては、動物用排泄物処理材の
粒子表面で吸水し保水して、その周囲の動物用排泄物処
理材の粒子と付着することを容易にさせるために、吸水
性樹脂は、被覆部に13乃至7重量%の量で加えられ
る。一般に、粒子中の被覆部の量は25乃至15重量%
とすることができるが、10乃至20重量%とするのが
好ましい。本発明において、高吸水性樹脂は、自重の数
十倍から二百倍程度の水を吸収しても、形を保持できる
樹脂であり、例えば、ビニルエステルとエチレン系不飽
和カルボン酸又はその誘導体との共重合体鹸化物、澱粉
とアクリル酸のグラフト重合体、ポリアクリル酸の架橋
物、ビニルアルコールとアクリル酸の共重合体、ポリア
クリロニトリルの部分加水分解物、カルボキシメチルセ
ルロースの架橋物、ポリエチレングリコールの架橋物、
キトサンの塩又はプルランのゲルなどがあり、これら
は、プラスチック廃材に単独で又はこれら2種以上を混
合して配合物質として使用される。
In the present invention, in order to absorb and retain water on the surface of the particles of the animal excrement disposal material, the water-absorbing resin is used to facilitate the adhesion to the surrounding particles of the animal excrement disposal material. Is added to the coating in an amount of 13 to 7% by weight. Generally, the amount of coating in the particles is 25 to 15% by weight
However, the content is preferably 10 to 20% by weight. In the present invention, the superabsorbent resin is a resin that can retain its shape even when absorbing water of several tens to 200 times its own weight, for example, a vinyl ester and an ethylenically unsaturated carboxylic acid or a derivative thereof. Saponified copolymer with starch, graft polymer of starch and acrylic acid, cross-linked product of polyacrylic acid, copolymer of vinyl alcohol and acrylic acid, partially hydrolyzed product of polyacrylonitrile, cross-linked product of carboxymethyl cellulose, polyethylene glycol Crosslinked product,
There are chitosan salts and pullulan gels, which are used alone or as a mixture of two or more of these in plastic waste.

【0023】本発明においては、吸水倍率が200g/
g未満と吸水性能の乏しい吸水性樹脂を使用することが
できる。このような吸水性能の低いポリアクリル酸樹脂
には、粒径が、600μm以上のものと、20μm以下
と微細なものがあり、これら樹脂は、例えばおむつ廃材
から分級して得られるか、又はポリアクリル酸樹脂の規
格外の製品として入手することができる。粒径が600
μm以上のポリアクリル酸樹脂は、粒状芯部に使用する
のが好ましく、粒径が20μm以下の微細なポリアクリ
ル酸樹脂は被覆部に使用するのが好ましい。このよう
に、おむつの廃材中には、高吸水性樹脂が含有されてい
るので、プラスチック廃材粉におむつの廃材が配合され
るときには、高吸水性樹脂の添加量をその分減らすこと
ができる。本発明において、動物用耕泄物処理材に吸着
機能を持たせるために、プラスチック廃材に、可燃性の
吸着機能を有する材料、例えば、茶殻、コーヒー液抽出
残渣、木粉及びこれらの混合物を配合するのが好まし
い。
In the present invention, the water absorption capacity is 200 g /
When it is less than g, a water-absorbing resin having poor water-absorbing performance can be used. Such polyacrylic acid resins having a low water absorption performance include those having a particle size of 600 μm or more and those having a fine particle size of 20 μm or less. These resins are obtained, for example, by classification from waste diapers, or It is available as a nonstandard product of acrylic resin. Particle size 600
It is preferable to use a polyacrylic acid resin having a particle size of not less than μm in the granular core portion, and it is preferable to use a fine polyacrylic acid resin having a particle size of not more than 20 μm in the coating portion. As described above, since the waste material of the diaper contains the superabsorbent resin, when the waste material of the diaper is blended with the plastic waste material powder, the amount of the superabsorbent resin can be reduced accordingly. In the present invention, in order to impart an adsorption function to the animal cultivation treatment material, a plastic material having a flammable adsorption function, for example, a tea husk, a coffee liquid extraction residue, wood flour, and a mixture thereof are mixed with plastic waste. Is preferred.

【0024】本発明において、使用時の排泄物処理材の
粉化を避けるために、被覆層に、接着機能及び保水性を
有する物質を配合するのが好ましい。このような物質と
しては、水溶性又は水分散性のものとして、製紙工場の
廃材の粉砕加工した紙粉、パンチ屑の粉砕粉、ポリビニ
ルアルコール(PVA)、ポリエチレングリコール、ソ
ルビトール、ポリプロピレングリコールなどの希釈液、
α澱粉などがある。本発明において、使用時の排泄物処
理材の粉化を避けるために、粒状芯部には、潤滑機能、
接着機能及び保水機能を有する小麦粉、澱粉、コーンス
ターチ、カルボキシメチルセルロース(CMC)、プル
ラン又はゼラチンなどがあり、これらは、単独で使用さ
れるか、又はこれら2種以上を混合して配合物質として
使用することができる。
In the present invention, in order to avoid powdering of the excrement disposal material during use, it is preferable to incorporate a substance having an adhesive function and water retention into the coating layer. Examples of such substances include water-soluble or water-dispersible substances, such as crushed paper powder of paper mill waste, crushed punch dust, dilution of polyvinyl alcohol (PVA), polyethylene glycol, sorbitol, and polypropylene glycol. liquid,
α starch and the like. In the present invention, in order to avoid powdering of the excrement disposal material during use, the granular core has a lubricating function,
There are wheat flour, starch, corn starch, carboxymethylcellulose (CMC), pullulan or gelatin having an adhesive function and a water retaining function, and these are used alone or as a compounded substance by mixing two or more of these. be able to.

【0025】本発明において、例えばポリエチレングリ
コールとソルビトールの混合希釈溶液を使用するとき
は、例えば0.08重量%のポリエチレングリコールと
0.03重量%のソルビトールの希釈溶液を使用するこ
とができる。この場合においては、例えば、動物用排泄
物処理材1kg当たり、ポリエチレングリコールとソル
ビトールの合計量が1gとなるように造粒物の被覆部上
に噴霧等により被覆することができる。本発明におい
て、動物用排泄物処理材は、プラスチック廃材粉に無機
質配合材料粉を配合して造粒して製造されるために、造
粒後の微細な粉塵の存在を極力避けるために、例えば3
mm以上の粒径の造粒物に造粒されるのが好ましいが、
7mm以上の粒径の粒子に造粒すると、例えばトイレ用
の箱から室内に散り難くなり、仮令散ったとしても、粒
子を拾い集めるのが容易であり、室内の衛生を保つ上で
好ましい。しかし、これらの場合、3mm以下の粒子の
存在や、7mm以下の粒子の存在を完全に排斥するもの
ではない。本発明において、造粒物は、球状、柱状、粒
状、顆粒状等各種形状に形成することができる。
In the present invention, for example, when a mixed diluted solution of polyethylene glycol and sorbitol is used, for example, a diluted solution of 0.08% by weight of polyethylene glycol and 0.03% by weight of sorbitol can be used. In this case, for example, the granulated material can be coated by spraying or the like such that the total amount of polyethylene glycol and sorbitol is 1 g per kg of the animal excrement disposal material. In the present invention, animal excrement disposal materials are manufactured by blending inorganic compounding material powder with plastic waste material powder and granulating, in order to minimize the presence of fine dust after granulation, for example, 3
It is preferable to granulate into granules having a particle size of at least mm,
When granulated into particles having a particle diameter of 7 mm or more, it is difficult to disperse the particles from the toilet box into the room, for example, and even if the particles are scattered, it is easy to collect and collect the particles, which is preferable in maintaining indoor hygiene. However, in these cases, the presence of particles of 3 mm or less or the presence of particles of 7 mm or less is not completely excluded. In the present invention, the granules can be formed into various shapes such as spherical, columnar, granular, and granular.

【0026】また、動物用排泄物処理材の表面に付着さ
せる被覆材料の紙粉等を、水溶性又はアルコール溶解性
の接着剤と共に付着させた場合には、動物の排泄時に、
造粒物に尿が付着するが、尿が付着した部分同士が簡単
にくっついて固まりとなるので好ましい。本発明におい
て、造粒に先立って配合される配合物質と、造粒物の表
面に付着させる配合物質は、同一のものとすることがで
き、また異なるものとすることができる。本発明におい
て、プラスチック廃材粉及び有機質配合材料の混合物、
プラスチック廃材、有機質配合材料及び高吸水性樹脂の
混合物、或いはプラスチック廃材、有機質配合材料、無
機質配合材料及び高吸水性樹脂の混合物は、混合装置に
おいて混合され、造粒装置により造粒される。造粒装置
としては、従来周知の、押出し造粒装置を使用すること
ができる。
When paper powder or the like as a coating material to be adhered to the surface of the animal excrement disposal material is adhered together with a water-soluble or alcohol-soluble adhesive, at the time of animal excretion,
Although the urine adheres to the granulated material, it is preferable because the urine-adhered portions easily adhere to each other to form a cake. In the present invention, the compounding substance to be compounded prior to granulation and the compounding substance to be adhered to the surface of the granulated material can be the same or different. In the present invention, a mixture of plastic waste powder and organic compounding material,
A mixture of plastic waste material, organic compound material and superabsorbent resin, or a mixture of plastic waste material, organic compound material, inorganic compound material and superabsorbent resin is mixed in a mixing device and granulated by a granulator. As the granulation device, a conventionally known extrusion granulation device can be used.

【0027】本発明において、造粒は、押出し造粒装置
以外に、パン型、ドラム型及び流動層型の各種造粒装置
を使用して行うことができる。前記プラスチック廃材等
の造粒物には、造粒後、接着能を有する配合物質、高吸
水性樹脂、殺菌作用を有する配合物質又はその他配合物
質をまぷすなどして、造粒物の表面に配合物質を付着さ
せ、その後乾燥することにより容易に剥落しないように
するのが好ましい。粒状芯部を被覆する場合には、被覆
層の保水性、外観性及び粘着性を向上させるために、例
えば、上質紙のパンチ屑などのように、比較的柔軟でな
く、吸水し難い紙粉の場合には、例えば0.5mm以下
の粒径にすることが必要であるが、吸水して柔軟性を発
揮する紙粉の場合には、例えば0.7mm以下と比較的
大きい粒径で散布し付着させることができる。
In the present invention, granulation can be carried out using various types of granulators, such as a pan type, a drum type and a fluidized bed type, in addition to the extrusion granulator. The granulated material such as the plastic waste material, after granulation, by mixing a compound having an adhesive ability, a highly water-absorbent resin, a compound having a bactericidal action or other compound, etc., on the surface of the granulated material. It is preferred that the compounding substance be deposited and then dried so that it does not easily fall off. When coating the granular core, in order to improve the water retention, appearance and adhesiveness of the coating layer, for example, paper powder that is relatively soft and hardly absorbs water, such as punch dust of high quality paper. In the case of, for example, it is necessary to make the particle size of 0.5 mm or less, but in the case of paper powder which exhibits flexibility by absorbing water, it is sprayed with a relatively large particle size of, for example, 0.7 mm or less. And can be attached.

【0028】本発明は、動物の排泄物処理材が、プラス
チック廃材及び無機質配合材料を主として含有し、3m
m以上、好ましくは7mm以上の粒径の造粒物に、水吸
収性の紙粉、高吸水性樹脂及び防虫剤の蒸散性のエンペ
ンスリン等の配合物質と共に成形されるので、動物の排
泄した尿の吸収が良く、また保水性が良く、さらに使用
する動物に対し防虫性が顕著に発揮でき良好である。し
かも、本発明の動物用排泄物処理材には、特に被覆部
に、紙粉及び高吸水性樹脂、並びにこれに加えて小麦
粉、ポバール、澱粉若しくはその他接着能を有する配合
物質、又は殺菌作用を有する物質或はこれら配合物質の
二以上のものが混合して配合することができるので、動
物の排泄物に付着して、排泄物を塊状に包み込むことと
なり、後始末が簡単かつ容易となる。また、この場合、
被覆部に脱臭剤及び/又は吸水剤が混合されているとき
には、動物用排泄物処理材として更に優れた脱臭性及び
吸水性を発揮することができ、さらにまた、殺菌作用を
有する物質が混合されているときには、動物用排泄物処
理材は、黴などの発生がなく長期間に亙って保存するこ
とができる。
According to the present invention, the animal excrement disposal material contains mainly plastic waste material and an inorganic compound material,
m or more, preferably 7 mm or more, is formed into a granulated material with water-absorbing paper powder, a superabsorbent resin, and a compound such as transpirant empensulin as an insect repellent. It has good absorption of water, good water retention and remarkable insect repellency to the animals used. In addition, the animal excrement disposal material of the present invention has, in particular, a paper powder and a superabsorbent resin, and in addition to this, wheat flour, poval, starch or other compounded substances having an adhesive ability, or a bactericidal action. Since these substances or two or more of these compounded substances can be mixed and compounded, they adhere to the excrement of the animal and wrap the excrement in a lump, so that the disposal is simple and easy. Also, in this case,
When a deodorant and / or a water-absorbing agent is mixed in the coating part, it can exhibit more excellent deodorizing and water-absorbing properties as an animal excrement disposal material, and further, a substance having a bactericidal action is mixed. In this case, the animal excrement disposal material can be stored for a long period of time without generating mold and the like.

【0029】以下、本発明の実施の態様の例を説明する
が、本発明は、以下の説明及び例示によって何等制限さ
れるものではない。図1は、本発明の一実施例の動物用
排泄物処理材を製造する工程を示す概略の流れ工程図で
ある。図2は、本発明の他の一実施例の動物用排泄物処
理材を製造する工程を示す概略の流れ工程図である。
Hereinafter, embodiments of the present invention will be described, but the present invention is not limited by the following description and illustrations. FIG. 1 is a schematic flow chart showing a process of manufacturing an animal excrement disposal material according to one embodiment of the present invention. FIG. 2 is a schematic flow chart showing a process of manufacturing an animal excrement disposal material according to another embodiment of the present invention.

【0030】[0030]

【実施例】本例の装置は以上のように構成されているの
で、所定量の紙おむつ廃材粉を計量ホッパー1に入れ、
また所定量のコーヒー液抽出残渣を計量ホッパー5に入
れる。そこで、紙おむつ廃材粉供給用のスクリューコン
ベヤ2、コーヒー液抽出残渣供給用のスクリューコンベ
ヤ6及びメインスクリューコンベヤ4を作動させて、混
合装置8に、夫々、所定量の紙おむつ廃材粉及びコーヒ
ー液抽出残渣を供給し、水供給管9から供給される水と
一様に混合一する。これら混合された紙おむつ廃材粉、
コーヒー液抽出残渣及び水の混合物は、作動している混
合物搬送用のスクリューコンベヤ11から、押出し造粒
装置12に送られる。本例において、押出し造粒装置1
2は、造粒される前記混合物をスクリュウの回転により
押して、ダイス14に設けられている孔に相当する断面
を有する。本例においては、ダイスは、5.5mmの孔
径を有し、厚さ30mmのものが使用された。
DESCRIPTION OF THE PREFERRED EMBODIMENTS Since the apparatus of this embodiment is constructed as described above, a predetermined amount of diaper waste material powder is put into a measuring hopper 1,
Also, a predetermined amount of coffee liquid extraction residue is put into the weighing hopper 5. Then, the screw conveyor 2 for supplying the paper diaper waste material powder, the screw conveyor 6 for supplying the coffee liquid extraction residue, and the main screw conveyor 4 are operated, and a predetermined amount of the paper diaper waste material powder and the coffee liquid extraction residue are respectively supplied to the mixing device 8. And uniformly mixed with the water supplied from the water supply pipe 9. These mixed disposable diaper waste powder,
The mixture of the coffee liquor extraction residue and water is sent from the operating screw conveyor 11 for conveying the mixture to the extrusion granulator 12. In this example, the extrusion granulation apparatus 1
2 has a cross section corresponding to a hole provided in the die 14 by pressing the mixture to be granulated by rotation of a screw. In this example, a die having a hole diameter of 5.5 mm and a thickness of 30 mm was used.

【0031】押出し造粒装置12のダイス14から押し
出された造粒物粒子は、例えば篩目の開きが8mmの上
段篩及び篩目の開きが4mmの下段篩を備える振動筋1
5に送られて篩分けされる。下段篩の篩下の、粒度が4
mmより小さい造粒物は、4mm篩の篩下出口18から
篩下粒子搬送用のコンベヤベルト19を経て、混合物搬
送用のスクリューコンベヤ11に戻され、造粒装置12
に送られて再度造粒される。粒度が8〜4mmの造粒
物、即ち4mm篩の篩上造粒物は、篩上造粒物搬送用出
口16から、回転円盤型の被覆装置17に送られる。そ
こで吸水性樹脂及び紙粉を所定量の配合比に配合されて
いる被覆材料がまぶされて被覆される。被覆装置17で
被覆された、被覆造粒物は、続く被覆装置24及び26
に送られ、そこで振動型円盤により転動されながら、夫
々、既に散布された吸水性樹脂及び紙粉の混合物の被覆
材料と接触して被覆される。
The granulated particles extruded from the die 14 of the extrusion granulator 12 are, for example, a vibrating streak 1 having an upper sieve having an opening of 8 mm and a lower sieve having an opening of 4 mm.
5 to be sieved. Particle size of 4 below the lower sieve
The granulated material smaller than 4 mm is returned to the screw conveyor 11 for conveying the mixture from the under-sieving outlet 18 of the 4 mm sieve, via the conveyor belt 19 for conveying the under-sieved particles,
And granulated again. The granulated material having a particle size of 8 to 4 mm, that is, a granulated material on a 4 mm sieve is sent to a rotating disk type coating device 17 from an outlet 16 for conveying the granulated material on the sieve. Then, a coating material in which the water-absorbent resin and the paper powder are mixed in a predetermined mixing ratio is dusted and coated. The coated granules coated with the coating device 17 are separated into the following coating devices 24 and 26.
And while being rolled by the vibrating disk there, each is contacted with the coating material of the mixture of the water-absorbent resin and the paper powder that has already been sprayed, and coated.

【0032】造粒物被覆装置17.24及び26で被覆
材料で被覆された造粒物粒子は、振動篩型整粒装置28
でほぐされて、粒度が10〜5mmの粒子は、振動篩型
整粒装置28の5mm篩の篩上出口31からコンベヤベ
ルト32.33及び34を経て第一乾燥装置35に送ら
れ乾燥される。一方、5mm未満の造粒物粒子は、5m
m篩の篩下粒子搬送用コンベヤベルト30によって、混
合物搬送用のスクリューコンベヤ11に送られ、造粒装
置12に戻され、再度造粒処理される。造粒物乾燥用の
第一乾燥装置35の温度は80℃以上の温度に保たれ
る。乾燥された造粒物は、被覆造粒物の表面の被覆材料
部の毛羽だち等を防止するために、ポリビニルアルコー
ル希釈液の噴霧装置39に送られる。噴霧装置39にお
いて、噴霧用ポリビニルアルコール希釈液タンク40か
ら、ポリビニルアルコール希釈液が噴霧される。ポリビ
ニルアルコール希釈液が噴霧された被覆造粒物は、被覆
造粒物搬送用コンベヤベルト41から、熱風乾燥機の被
覆造粒物乾燥用の第二乾燥装置42に送り出される。第
二乾燥装置は、第一乾燥装置に比して低い乾燥条件で、
被覆造粒物を乾燥する。乾燥された被覆造粒物は製品ホ
ッパー46に送られる。製品ホッパー46に入れられた
被覆造粒物は、整粒装置48で整粒されて、製品充填装
置51におくられ、袋詰めされて出荷される。
The granule particles coated with the coating material in the granule coating devices 17.24 and 26 are passed through a vibrating sieve type granulating device 28.
The particles having a particle size of 10 to 5 mm are sent to the first drying device 35 through the conveyor belts 32.33 and 34 through the 5 mm sieve outlet 31 of the vibrating sieve-type granulating device 28 and dried. . On the other hand, granulated material particles of less than 5 mm
The mixture is conveyed to the screw conveyor 11 for conveying the mixture by the conveyor belt 30 for conveying particles under the m-sieve, returned to the granulator 12, and subjected to granulation again. The temperature of the first drying device 35 for drying the granulated material is kept at a temperature of 80 ° C. or higher. The dried granules are sent to a spraying device 39 for diluting polyvinyl alcohol in order to prevent fluffing or the like of the coating material portion on the surface of the coated granules. In the spraying device 39, a polyvinyl alcohol diluent is sprayed from a polyvinyl alcohol diluent tank 40 for spraying. The coated granulated material sprayed with the polyvinyl alcohol diluent is sent from the coated granulated material conveyor belt 41 to a second drying device 42 for drying the coated granulated material of a hot air dryer. The second drying device has a lower drying condition than the first drying device,
Dry the coated granulation. The dried coated granules are sent to the product hopper 46. The coated granulated product put in the product hopper 46 is sized by a sizing device 48, placed in a product filling device 51, packed in a bag, and shipped.

【0033】本例においては、蒸散性エンペンスリン、
殺菌剤等の示されていないが、第一乾燥後に蒸散性のエ
ンペンスリンの非アルコール系有機溶剤溶液や殺菌剤溶
液を、ポリビニルアルコールの希釈溶液と一緒に噴霧す
ることができる。この場合、ポリビニルアルコールのの
希釈液と、蒸散性のエンペンスリンや殺菌剤の溶剤溶液
を別個に形成して、夫々を、別個に又は混合して噴霧す
るようにしてもよい。また、本例においては、粒状芯部
には、防虫剤が配合されていないが、例えばエンペンス
リンの非アルコール有機溶剤溶液を吸水性樹脂に配合し
て水供給管17から配合して、造粒物に配合することが
できる。エンペンスリンを高吸水性樹脂に配合する場合
は、高吸水性樹脂の量を多くして行い、弱い乾燥条件で
乾燥するのが好ましい。
In the present example, transpirable empensulin,
Although a disinfectant or the like is not shown, a non-alcoholic organic solvent solution or a disinfectant solution of transpirable empensulin after the first drying can be sprayed together with a dilute solution of polyvinyl alcohol. In this case, a dilute solution of polyvinyl alcohol and a solvent solution of transpirable empensulin or a disinfectant may be separately formed, and each may be sprayed separately or mixed. Further, in this example, the insect repellent was not blended in the granular core, but for example, a non-alcoholic organic solvent solution of empensulin was blended into the water-absorbent resin and blended from the water supply pipe 17 to form the granulated product. Can be blended. When blending empensulin with the superabsorbent resin, it is preferable to increase the amount of the superabsorbent resin and to dry under weak drying conditions.

【0034】図2に示す実旋例は、図1とは異なる本発
明の一実旋例の動物用排泄物処理材を製造する工程を示
す概略の工程図である。図2において、紙おむつ廃材粉
の計量ホッパー52は、コンベヤ装置のコンベヤベルト
53の搬送路上に位置して、コンベヤベルト53に、紙
おむつ廃材粉を供給可能に設けられている。また、茶殻
ホッパー54は、コンベヤ装置のコンベヤベルト55の
搬送路上に位置して、コンベヤベルト55に茶殻を供給
可能に設けられている。コンベヤベルト53の出口側5
6及びコンベヤベルト55の出口側57は、紙おむつ廃
材粉と茶殻の混合物搬送用のコンベヤ装置のコンベヤベ
ルト58上に対向して設けられている。紙おむつ廃材粉
と茶殻の混合物搬送用のコンベヤベルト58の出口側5
9は、混合装置60上に位置している。本例において、
パルプスラッジ再燃焼灰製品粉用の計量ホッパー61
は、コンベヤ装置のコンベヤベルト62の搬送路上に位
置して、コンベヤ装置のコンベヤベルト62にパルプス
ラッジ再燃焼灰製品粉を供給可能に設けられている。パ
ルプスラッジ再燃焼灰製品粉供給用のコンベヤベルト6
2の出口側63は、混合装置60上に位置している。
The actual rotation example shown in FIG. 2 is a schematic process diagram showing a process of manufacturing an animal excrement disposal material according to one real rotation example of the present invention, which is different from FIG. In FIG. 2, a disposable diaper powder weighing hopper 52 is located on a conveying path of a conveyor belt 53 of a conveyor device, and is provided to the conveyor belt 53 so as to be able to supply the disposable diaper powder. Further, the tea hopper 54 is provided on the conveying path of the conveyor belt 55 of the conveyor device so as to be able to supply the tea husk to the conveyor belt 55. Exit side 5 of conveyor belt 53
The outlet side 57 of the conveyor belt 6 and the conveyor belt 55 are provided on a conveyor belt 58 of a conveyor device for conveying a mixture of waste paper diaper powder and tea leaves. Outlet side 5 of conveyor belt 58 for conveying a mixture of waste diaper powder and tea husk
9 is located on the mixing device 60. In this example,
Measuring hopper 61 for pulp sludge reburning ash product powder
Is located on the conveyance path of the conveyor belt 62 of the conveyor device, and is provided so that the pulp sludge reburning ash product powder can be supplied to the conveyor belt 62 of the conveyor device. Conveyor belt 6 for supplying pulp sludge reburning ash product powder
The second outlet side 63 is located on the mixing device 60.

【0035】混合装置60で混合された混合物を搬送す
るために、混合装置60の混合物出口64には、混合物
搬送用のコンベヤベルト65が設けられており、紙おむ
つ廃材粉、茶殻及びパルプスラッジ再燃焼灰製品粉は、
混合装置60で混合され、その混合物は、混合装置60
の出口64から、混合物搬送用のコンベヤ装置のコンベ
ヤベルト65に供給され、混合物搬送用コンベヤベルト
65から押出し造粒装置66の予備混合装置67に供給
される。予備混合装置67には、水が供給管68から供
給され、ここで、紙おむつ廃材粉、茶殻及びパルプスラ
ッジ再燃焼灰製品粉は一様に混合される。紙おむつ廃材
粉、茶殻及びパルプスラッジ再燃焼灰製品粉の混合物
は、押出し造粒装置66に導入されて、ダイス69側か
ら、柱状の造粒物として押し出される。押出し造粒装置
66のダイス69の下方には、押し出された造粒物を、
円形篩70に送るための造粒物搬送用のコンベヤ装置の
コンベヤベルト71が設けられている。
In order to transport the mixture mixed by the mixing device 60, a conveyor belt 65 for transporting the mixture is provided at the mixture outlet 64 of the mixing device 60, and the waste diaper powder, tea husk and pulp sludge are reburned. Ash product powder
The mixture is mixed in the mixing device 60, and the mixture is mixed in the mixing device 60.
Is supplied to a conveyor belt 65 of a conveyor device for transporting the mixture, and is supplied from the conveyor belt 65 for transporting the mixture to a pre-mixing device 67 of an extrusion granulation device 66. Water is supplied to the pre-mixing device 67 from a supply pipe 68, where the diaper waste material powder, the tea husk, and the pulp sludge reburned ash product powder are uniformly mixed. The mixture of the paper diaper waste material powder, the tea husk, and the pulp sludge reburned ash product powder is introduced into the extrusion granulator 66 and extruded from the die 69 side as a columnar granulated material. Below the die 69 of the extrusion granulator 66, the extruded granules are
A conveyor belt 71 of a conveyor device for conveying granulated materials to be sent to the circular sieve 70 is provided.

【0036】本例において、円形篩70の目の開きは4
mmであり、篩上粒子は、篩上出口72から出て、該篩
上出口72に接続する篩上粒子搬送用のコンベヤ装置の
コンベヤベルト73に供給される。篩上粒子搬送用コン
ベヤベルト73は、振動型整粒機74に接続している。
振動型整粒機74は、互いに付着する造粒物を、振動さ
せることによりほぐすものであり、使用時の粉化を極力
少なくするために設けられている。篩上粒子は、搬送用
コンベヤベルト73により、振動型整粒機74に供給さ
れる。一方、円形篩70の箭下粒子は、篩下出口75に
設けられている篩下粒子搬送用のコンベヤベルト76に
より、混合物搬送用のコンベヤベルト65を経て、押出
し造粒装置66に戻され、再度造粒される。振動型整粒
機74に送られた造粒物は、振動型整粒機74の振動に
より一粒宛ほぐされて送り出される。本例においては、
振動型整粒機74の出口側に、目の開きが4mmの篩7
7が設けられている。この篩77の篩下出口の下方に
は、混合物搬送用のコンベヤベルト65に接続する篩下
搬送用コンベヤベルト78が設けられており、篩77の
篩下粒子は、篩下搬送用コンベヤベルト78により、混
合物搬送用のコンベヤベルト65を経て、押出し造粒装
置66に戻され、再度造粒される。
In this example, the opening of the circular sieve 70 is 4
mm, and the particles on the sieve exit from the sieve outlet 72 and are supplied to the conveyor belt 73 of the conveyor device for conveying the sieve particles connected to the sieve outlet 72. The conveyor belt 73 for conveying particles on the sieve is connected to a vibration type particle sizer 74.
The vibration type granulator 74 is for loosening the granules adhering to each other by vibrating, and is provided to minimize powdering during use. The particles on the sieve are supplied to a vibration type granulator 74 by a conveyor belt 73 for conveyance. On the other hand, the particles under the circle of the circular sieve 70 are returned to the extrusion granulating device 66 via the conveyor belt 65 for transporting the mixture, by the conveyor belt 76 for transporting the undersize particles provided at the outlet 75 below the sieve, It is granulated again. The granulated product sent to the vibratory granulator 74 is loosened and sent out by the vibration of the vibratory granulator 74. In this example,
At the outlet side of the vibrating granulator 74, a sieve 7 having an opening of 4 mm
7 are provided. Below the undersize outlet of the sieve 77, there is provided an undersize transport conveyor belt 78 connected to the mixture transport conveyor belt 65, and the undersize particles of the sieve 77 are transferred to the undersize transport conveyor belt 78. Thus, the mixture is returned to the extrusion granulation device 66 through the conveyor belt 65 for conveying the mixture, and is granulated again.

【0037】振動型整粒機74において、4mm以上の
粒径の粒子は、篩上出口79に接続する筋上搬送用のコ
ンベヤ装置のコンベヤベルト80から搬出される。該篩
上搬送用のコンベヤベルト80の出口は第一の造粒物被
覆装置81に接続している。振動型整粒機74におい
て、4mm以上の粒径の粒子は、高吸水性樹脂及び紙粉
を表面に被覆するために、篩上出口79に接続する篩上
搬送用のコンベヤベルト80から搬出される。該篩上搬
送用のコンベヤベルト80に接続する第一の造粒物被覆
装置81の篩82に供給される。本例において、第一及
び第二の造粒物被覆装置81及び83は、共に振動型被
覆装置であり、直列に設けられている。第一の造粒物被
覆装置81の出口の篩分装置84は、出口を第二の造粒
物被覆装置83に接続している。第一の造粒物被覆装置
81の振動する被覆用搬送路上に出口を有する第一散布
用篩85が設けられ、第二の造粒物被覆装置83の振動
する被覆用搬送路上に噴霧ノズルを開口して第二散布用
噴霧装置86が設けられている。第一散布用筋85から
は、高吸水性樹脂及び紙粉の混合物が散布され、第二散
布用噴霧装置86からはポリビニルアルコール希釈液が
噴霧される。
In the vibration type granulator 74, particles having a particle diameter of 4 mm or more are carried out from a conveyor belt 80 of a conveyor device for conveying muscles connected to an outlet 79 on a sieve. The outlet of the conveyor belt 80 for conveying on the sieve is connected to a first granulated material coating device 81. In the vibration type granulator 74, the particles having a particle diameter of 4 mm or more are carried out from the on-sieving conveyor belt 80 connected to the on-sieving outlet 79 in order to coat the surface with the superabsorbent resin and the paper powder. You. It is supplied to the sieve 82 of the first granule coating device 81 connected to the conveyor belt 80 for conveying on the sieve. In this example, both the first and second granulated material coating devices 81 and 83 are vibration type coating devices and are provided in series. The sieving device 84 at the outlet of the first granule coating device 81 has an outlet connected to the second granule coating device 83. A first spraying sieve 85 having an outlet on the vibrating coating transport path of the first granule coating apparatus 81 is provided, and a spray nozzle is provided on the vibrating coating transport path of the second granule coating apparatus 83. An opening spraying device 86 is provided. A mixture of the superabsorbent resin and the paper powder is sprayed from the first spray streaks 85, and a polyvinyl alcohol dilution is sprayed from the second spraying device 86.

【0038】夫々の造粒物被覆装置において、振動する
造粒物上に被覆材料を散布して、造粒物の被覆を行う。
第一散布用篩85は、高吸水性樹脂及び紙粉の混合物を
入れる第一被覆材料散布用ホッパー87に接続してお
り、第二散布用噴霧装置86は、ポリビニルアルコール
希釈液を入れた被覆液タンク88に接続している。前記
散布用篩及び散布用噴霧装置は、散布用の被覆材料を、
造粒物に対し、常に一定の比率で散布することができる
ように形成されている。第二の造粒物被覆装置83に
は、被覆造粒物搬送用コンベヤ装置のコンベヤベルト8
9が接続して設けられており、第二の造粒物被覆装置8
3で被覆された造粒物は、被覆造粒物搬送用コンベヤベ
ルト89によつて、該被覆造粒物搬送用コンベヤベルト
89が接続する乾燥装置90に送られる。被覆された造
粒物は、乾燥装置90、例えば熱風乾燥機に導入され、
乾燥されて、乾燥物出口91に接続して設けられている
乾燥造粒物搬送用のコンベヤベルト92により、製品タ
ンク93に送られる。乾燥造粒物の製品は、製品タンク
93の下方の出口下方に設けられた製品搬出用のコンベ
ヤ装置のコンベヤベルト94により袋詰め領域95に取
り出され、袋詰めされて出荷される。
In each of the granule coating apparatuses, a coating material is sprayed on the vibrating granules to coat the granules.
The first spraying sieve 85 is connected to a first coating material spraying hopper 87 for containing a mixture of superabsorbent resin and paper powder, and a second spraying device 86 is used for coating a polyvinyl alcohol diluted liquid. Connected to liquid tank 88. The spraying sieve and the spraying device for spraying, a coating material for spraying,
It is formed so that it can always be sprayed at a fixed ratio to the granulated material. The second granulated material coating device 83 includes a conveyor belt 8 of a coated granulated material conveying conveyor device.
9 are connected and provided, and the second granulated material coating device 8 is provided.
The granulated material coated in 3 is sent to a drying device 90 to which the coated granulated material conveyor belt 89 is connected by a coated granulated material conveyor belt 89. The coated granules are introduced into a drying device 90, for example, a hot air dryer,
The dried granules are dried and sent to a product tank 93 by a conveyor belt 92 for conveying dried granules provided to be connected to a dried product outlet 91. The dried granulated product is taken out to a bagging area 95 by a conveyor belt 94 of a product carrying-out conveyor device provided below an outlet below a product tank 93, packed in a bag, and shipped.

【0039】本例の装置は以上のように構成されている
ので、所定量の紙為むつ廃材粉を計量ホッパー52に入
れ、また所定量の茶殻を計量ホッパー54に入れ、さら
に、所定量のパルプスラッジ再燃焼灰製品粉を計量ホッ
パー61に入れる。そこで、紙おむつ廃材粉供給用のコ
ンベヤベルト53、茶殻供給用のコンベヤベルト55、
コンベヤベルト58及びパルプスラッジ再燃焼灰製品粉
供給用のコンベヤベルト62を作動させて、混合装置6
0に、夫々、所定量の紙おむつ廃材粉、茶殻及びパルプ
スラッジ再燃焼灰製品粉を供給して混合する。これら混
合された紙おむつ廃材粉、茶殻及びパルプスラッジ再燃
焼灰製品粉の混合物は、作動している混合物搬送用のコ
ンベヤベルト65に送り出され、予備混合装置67に送
られる。予備混合装置67には、更に水が供給管68か
ら供給される。予備混合装置67において、紙おむつ廃
材粉、茶殻、パルブスラッジ再燃焼灰製品粉及び水は、
一様に混合され、この一様に混合された混合物は、押出
し造粒装置66に送られる
Since the apparatus of this embodiment is configured as described above, a predetermined amount of waste paper waste is put into the measuring hopper 52, a predetermined amount of tea leaves is put into the measuring hopper 54, and a predetermined amount of The pulp sludge reburned ash product powder is put into the weighing hopper 61. Therefore, a conveyor belt 53 for supplying waste paper powder for diapers, a conveyor belt 55 for supplying tea leaves,
By operating the conveyor belt 58 and the conveyor belt 62 for supplying the pulp sludge reburning ash product powder, the mixing device 6
At 0, a predetermined amount of disposable diaper waste powder, tea husk and pulp sludge reburned ash product powder are supplied and mixed. The mixed mixture of the waste paper diaper powder, the tea husk and the pulp sludge reburned ash product powder is sent to the operating conveyor belt 65 for conveying the mixture and sent to the pre-mixing device 67. Water is further supplied to the premixing device 67 from a supply pipe 68. In the pre-mixing device 67, the disposable diaper waste powder, the tea husk, the reburned ash product powder and the water,
Uniformly mixed, and the uniformly mixed mixture is sent to an extrusion granulator 66.

【0040】本例において、押出し造粒装置66は、造
粒される前記混合物をスクリュウの回転により押して、
ダイス69の穴に相当する断面を有している。本例にお
いては、6mmの直径で長さが10mmの円筒状の造粒
物が得られる。押出し造粒装置66のダイス69から押
し出される造粒物粒子は、造粒物搬送用のコンベヤベル
ト71より、例えば、4mmの篩目の開きの円形篩70
に送られて篩分けされる。篩下の粒径が4mm以下の粒
径の造粒物は、篩下粒子搬送用のコンベヤベルト76に
よつて、混合物搬送用のコンベヤベルト65に戻され、
造粒装置66に送られて再度造粒する。4mm以上の粒
径の篩上粒子は、篩上粒子搬送用のコンベヤベルト73
によって、振動型整粒機74に送られ、ほぐされて粒径
が4mm以上の粒子は、篩77の篩上搬送用のコンベヤ
ベルト80によつて、第一の造粒物被覆装置81に送ら
れ、そこで高吸水性樹脂及び紙粉を所定量の配合比に配
合されている被覆材料がまぶされて被覆される。他方、
振動型整粒機74でほぐされて4mm未満の粒径の粒子
は、篩77の篩下出口から篩下搬送用コンベヤベルト7
8によって、混合物搬送用のコンベヤベルト65に送ら
れ、造粒装置66に戻され、再度造粒処理される。
In this example, the extrusion granulating device 66 presses the mixture to be granulated by rotating a screw,
It has a cross section corresponding to the hole of the die 69. In this example, a cylindrical granulated material having a diameter of 6 mm and a length of 10 mm is obtained. The granulated particles extruded from the die 69 of the extrusion granulating device 66 are supplied from a conveyor belt 71 for conveying the granulated material, for example, a circular sieve 70 having an opening of 4 mm.
To be sieved. The granulated material having a particle size of 4 mm or less under the sieve is returned to the conveyor belt 65 for transporting the mixture by the conveyor belt 76 for transporting the undersize particles,
It is sent to the granulator 66 and granulated again. The on-screen particles having a particle size of 4 mm or more are conveyed by a conveyor belt 73 for conveying on-screen particles.
The particles having a particle diameter of 4 mm or more are sent to a vibrating granulator 74 and sent to a first granulated material coating device 81 by a conveyor belt 80 for conveying on a sieve of a sieve 77. Then, a coating material in which the superabsorbent resin and the paper powder are blended in a predetermined blending ratio is dusted and coated. On the other hand,
Particles having a particle size of less than 4 mm, which have been loosened by the vibration type particle sizer 74, are passed through the under-sieving outlet of the sieve 77 to the under-sieve conveyor belt 7.
By 8, the mixture is sent to the conveyor belt 65 for conveying the mixture, returned to the granulator 66, and subjected to the granulation processing again.

【0041】第一の造粒物被覆装置81で第一の被覆材
料で被覆された造粒物粒子は、第一の造粒物被覆装置8
1の出口の篩分装置84から第二の造粒物被覆装置83
に送られ、第二の被覆材料の被覆用希釈液が噴霧され
る。該被覆用希釈液が噴霧された造粒物粒子は、第二の
造粒物被覆装置83の出口コンベヤ89から乾燥機90
に送られて乾燥される。乾燥機90の温度は85℃以上
の温度に保たれる。乾燥された造粒物は、乾燥造粒物搬
送用のコンベヤベルト92により、製品タンク93に送
られ、出荷用の製品とされる。本例においては、乾燥
後、製品としているが、乾燥後に蒸散性のエンペンスリ
ンの非アルコール系有機溶剤溶液及びポリビニルアルコ
ールの希釈溶液を噴霧することができる。この場合、ポ
リビニルアルコールのの希釈液と、蒸散性のエンペンス
リンの非アルコール有機溶剤溶液を別個に形成して、夫
々を、噴霧するようにしてもよい。また、本例において
は、粒状芯部には、防虫剤が配合されていないが、例え
ばエンペンスリンの非アルコール有機溶剤を吸水性樹脂
に配合して水供給管68から配合して、造粒物に配合す
ることができる。エンペンスリンを高吸水性樹脂に配合
する場合は、高吸水性樹脂の量を多くして行い、弱い乾
燥条件で乾燥するのが好ましい。
The granulated particles coated with the first coating material in the first granulated material coating device 81 are mixed with the first granulated material coating device 8.
A second granulation material coating device 83 from the sieving device 84 at the first outlet
And a coating diluent for the second coating material is sprayed. The granulated particles sprayed with the coating diluent are passed through an outlet conveyor 89 of the second granulated material coating device 83 to a dryer 90.
And dried. The temperature of the dryer 90 is maintained at a temperature of 85 ° C. or higher. The dried granules are sent to a product tank 93 by a conveyor belt 92 for conveying the dried granules, and are made into products for shipping. In this example, the product is dried and then dried, but after drying, a non-alcoholic organic solvent solution of transpirable empensulin and a diluted solution of polyvinyl alcohol can be sprayed. In this case, a dilute solution of polyvinyl alcohol and a non-alcoholic organic solvent solution of transpirable empensine may be formed separately, and each may be sprayed. Further, in this example, the insect repellent is not blended in the granular core, but for example, a non-alcoholic organic solvent of empensulin is blended into the water-absorbent resin and blended from the water supply pipe 68 to form a granulated product. Can be blended. When blending empensulin with the superabsorbent resin, it is preferable to increase the amount of the superabsorbent resin and to dry under weak drying conditions.

【0042】例1.図1に示す装置を使用して猫砂を製
造した例である。本例において、1mm以下の粒度に粉
砕されたペットボトル粉砕粉86重量部、高吸水性樹脂
4重量部をリボンミキサーに入れ、水を加えて混合し、
含水率40重量%の混合物を得た。この混合物を押出し
造粒装置の押出部に入れて、直径5.5mmの開口及び
30mmのプレート厚さのダイスを通して押出し、チョ
ッパーで適宜裁断して造粒した。この造粒物を整粒装置
で整粒し、振動型円板の被覆装置に入れ、皿状円板を振
動させながら、0.4mm以下の粒度の紙粉65重量部
及び150μm以下の粒度の高吸水性樹脂35重量部の
混合物の被覆材料を、造粒物に対して10重量%の割合
で造粒物表面に散布することにより被覆した。被覆され
た造粒物を整粒機でほぐして、熱風乾燥機で、水分が1
3%になるまで乾燥した。得られた猫砂製品は、粒度1
0〜5mmの粒状物を得た。この粒状物は、乾燥時の発
熱量が5219キロカロリー/Kgであり、水分13%
時の発熱量は4,457キロカロリー/kgであった。
得られた猫砂10gに21gの吸尿時の、所謂使用時の
濡れた状態における発熱量は、1004キロカロリー/
kgであり、使用後の焼却処理が可能であることを示し
た。この粒状物を集めて、猫のトイレ用の砂とした。室
内において、この猫のトイレ用の砂20gに、水道水1
000ミリリツトルに食塩10g及びアンモニア水10
ミリリツトルを溶解した疑似尿を30ミリリツトルを加
え、疑似尿により固まった部分を取り出した。本例トイ
レ用の砂において、疑似尿により固まらないトイレ用の
砂の量は4.5gであった。したがつて、疑似尿により
固まり形成に必要とされた量は16.5gである。した
がつて、本例のトイレ用の砂における吸水性は、(30
/16.5)倍、即ち1.95倍であった。またこの猫
のトイレ用の砂を猫のトイレに厚さ3cmに敷いて使用
したが、猫は普段と同様にトイレとして使用しており、
使用の上で何等支障がなかった。猫が排泄に使用後、こ
の猫のトイレ用の砂の、猫が排泄した部分については、
容易に取り出すことができた。しかも、本例の猫のトイ
レ用の砂は、吸水性及び脱臭性を有し、屋内に不快な臭
い発生するのを避けることができた。
Example 1 This is an example of producing cat litter using the apparatus shown in FIG. In this example, 86 parts by weight of crushed plastic bottle powder crushed to a particle size of 1 mm or less and 4 parts by weight of a superabsorbent resin are put into a ribbon mixer, water is added and mixed,
A mixture having a water content of 40% by weight was obtained. This mixture was put into an extrusion section of an extrusion granulation apparatus, extruded through a die having an opening having a diameter of 5.5 mm and a plate having a thickness of 30 mm, and appropriately cut with a chopper to perform granulation. The granulated product is sized by a sizing device, placed in a vibrating disk coating device, and while vibrating the dish-shaped disk, 65 parts by weight of paper powder having a particle size of 0.4 mm or less and a particle size of 150 μm or less are crushed. The coating material of the mixture of 35 parts by weight of the superabsorbent resin was applied by spraying on the surface of the granules at a ratio of 10% by weight based on the granules. The coated granules are loosened with a sizing machine and dried with a hot air drier.
Dried to 3%. The resulting cat litter product has a particle size of 1
Granules of 0-5 mm were obtained. This particulate matter has a calorific value of 5219 kcal / Kg when dried, and a moisture content of 13%.
The calorific value at that time was 4,457 kcal / kg.
The calorific value in the wet state at the time of so-called use at the time of absorbing 21 g of urine in 10 g of the obtained cat litter is 1004 kcal /
kg, indicating that incineration after use is possible. The granules were collected and used as cat litter sand. In a room, 20 g of sand for this cat's toilet is added to tap water
000 milliliters of salt and 10 g of ammonia water
30 milliliters of the simulated urine in which milliliters were dissolved was added, and the portion hardened by the simulated urine was taken out. In the toilet sand in this example, the amount of toilet sand that did not solidify due to pseudo urine was 4.5 g. Therefore, the amount required for clump formation by simulated urine is 16.5 g. Therefore, the water absorption of the toilet sand of this example is (30
/16.5) times, that is, 1.95 times. In addition, this cat toilet sand was laid on the cat toilet with a thickness of 3 cm, but the cat used as a toilet as usual,
There was no problem in use. After the cat used for excretion, the part of the cat's toilet sand that the cat excreted
It could be easily taken out. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0043】例2.図1に示す装置を使用して猫砂を製
造した例である。本例において、1mm以下の粒度に粉
砕されたペットボトル粉砕粉55重量部、茶殼20重量
部、コンピュータ用の記録用紙20重量部及び高吸水性
樹脂(ハイモ株式会社製ハイモサブ500)5重量部を
リボンミキサーに入れ、水を加えて混合し、含水率40
重量%の混合物を得た。この混合物を押出し造粒装置の
押出部に入れて、直径5.5mmの開口及び30mmの
プレート厚さのダイスを通して押出し、チョッパーで適
宜裁断して造粒した。この造粒物を整粒装置で整粒し、
振動型円板の被覆装置に入れ、皿状円板を振動させなが
ら、0.4mm以下の粒度の紙粉65重量部及び150
μm以下の粒度の高吸水性樹脂35重量部の混合物の被
覆材料を、造粒物に対して10重量%の割合で造粒物表
面に散布することにより被覆した。被覆された造粒物を
整粒機でほぐして、熱風乾燥機で、水分が13%になる
まで乾燥した。得られた猫砂製品は、粒度10〜5mm
の粒状物を得た。この粒状物は、乾燥時の発熱量が50
08キロカロリー/kgであり、水分13%時の発熱量
は4、274キロカロリー/kgであった。得られた猫
砂10gに19.5gの吸尿時の、所謂使用時の濡れた
状態における発熱量は、1026キロカロリー/kgで
あり、使用後の焼却処理が可能であることを示した。こ
の粒状物を集めて、猫のトイレ用の砂とした。
Example 2 This is an example of producing cat litter using the apparatus shown in FIG. In this example, 55 parts by weight of the pulverized powder of a PET bottle pulverized to a particle size of 1 mm or less, 20 parts by weight of a tea shell, 20 parts by weight of a recording paper for a computer, and 5 parts by weight of a highly water-absorbent resin (Himosub 500 manufactured by Hymo Corporation) Into a ribbon mixer, add water and mix, water content 40
A mixture by weight was obtained. This mixture was put into an extrusion section of an extrusion granulation apparatus, extruded through a die having an opening having a diameter of 5.5 mm and a plate having a thickness of 30 mm, and appropriately cut with a chopper to perform granulation. This granulated product is sized by a sizing device,
Put into a vibrating disk coating device, vibrate the dish-shaped disk, and add 65 parts by weight of paper powder having a particle size of 0.4 mm or less and 150 parts by weight.
A coating material of a mixture of 35 parts by weight of a highly water-absorbent resin having a particle size of not more than μm was coated on the surface of the granules by spraying at a ratio of 10% by weight to the granules. The coated granules were loosened with a sizing machine and dried with a hot air drier until the water content became 13%. The resulting cat litter product has a particle size of 10-5 mm
Was obtained. This granular material has a calorific value of 50 when dried.
It was 08 kcal / kg, and the calorific value at 13% moisture was 4,274 kcal / kg. The calorific value of 109.5 g of the obtained cat litter when sucking 19.5 g of urine in a so-called wet state during use was 1026 kcal / kg, indicating that the incineration treatment after use was possible. The granules were collected and used as cat litter sand.

【0044】室内において、この猫のトイレ用の砂20
gに、水道水1000ミリリツトルに食塩10g及びア
ンモニア水10ミリリツトルを溶解した疑似尿を30ミ
リリツトルを加え、疑似尿により固まった部分を取り出
した。本例トイレ用の砂において、疑似尿により固まら
ないトイレ用の砂の量は4.5gであった。したがつ
て、疑似尿により固まり形成に必要とされた量は16.
5gである。したがつて、本例のトイレ用の砂における
吸水性は、(30/16.5)倍、即ち1.95倍であ
った。またこの猫のトイレ用の砂を猫のトイレに厚さ3
cmに敷いて使用したが、猫は普段と同様にトイレとし
て使用しており、使用の上で何等支障がなかった。猫が
排泄に使用後、この猫のトイレ用の砂の、猫が排泄した
部分については、容易に取り出すことができた。しか
も、本例の猫のトイレ用の砂は、吸水性及び脱臭性を有
し、屋内に不快な臭い発生するのを避けることができ
た。
In the room, the cat's litter 20
Then, 30 ml of pseudo urine prepared by dissolving 10 g of salt and 10 ml of aqueous ammonia in 1000 ml of tap water was added to 30 g, and a portion solidified by the pseudo urine was taken out. In the toilet sand in this example, the amount of toilet sand that did not solidify due to pseudo urine was 4.5 g. Therefore, the amount required for clump formation by the simulated urine was 16.
5 g. Therefore, the water absorbency of the toilet sand of this example was (30 / 16.5) times, that is, 1.95 times. In addition, the sand for this cat litter should be 3
The cat was used as a toilet as usual, and there was no problem in using it. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0045】例3.図1に示す装置を使用して猫砂を製
造した例である。本例において、1mm以下の粒度に粉
砕されたペットボトル粉砕粉76.5重量部、α澱粉9
重量部及び高吸水性樹脂(ハイモ株式会社製ハイモサブ
500)4.5重量部をリボンミキサーに入れ、水を加
えて混合し、含水率40重量%の混合物を得た。この混
合物を押出し造粒装置の押出部に入れて、直径5.5m
mの開口及び30mmのプレート厚さのダイスを通して
押出し、チョッパーで適宜裁断して造粒した。この造粒
物を整粒装置で整粒し、振動型円板の被覆装置に入れ、
皿状円板を振動させながら、コンピュータ用の記録用紙
を粉砕した、0.4mm以下の粒度の紙粉30重量部及
び150μm以下の粒度の高吸水性樹脂(ハイモ株式会
社製ハイモサブ500)70重量部の混合物の被覆材料
を、造粒物に対して10重量%の割合で造粒物表面に散
布することにより被覆した。被覆された造粒物を整粒機
でほぐして、熱風乾燥機で、水分が13%になるまで乾
燥した。
Example 3 This is an example of producing cat litter using the apparatus shown in FIG. In this example, 76.5 parts by weight of a pulverized PET bottle pulverized to a particle size of 1 mm or less, α-starch 9
Parts by weight and 4.5 parts by weight of a superabsorbent resin (Himosub 500, manufactured by Hymo Corporation) were put into a ribbon mixer, water was added and mixed to obtain a mixture having a water content of 40% by weight. This mixture was put into the extrusion section of an extrusion granulator, and was 5.5 m in diameter.
The mixture was extruded through a die having an opening of m and a plate thickness of 30 mm, and was appropriately cut with a chopper and granulated. This granulated product is sized by a sizing device and put into a vibration type disk coating device.
30 parts by weight of paper powder having a particle size of 0.4 mm or less and 70 parts by weight of a highly water-absorbent resin having a particle size of 150 μm or less (Himosub 500 manufactured by Hymo Co., Ltd.) Of the mixture was applied to the surface of the granules at a rate of 10% by weight with respect to the granules. The coated granules were loosened with a sizing machine and dried with a hot air drier until the water content became 13%.

【0046】得られた猫砂製品は、粒度10〜5mmの
粒状物を得た。この粒状物は、乾燥時の発熱量が517
0キロカロリー/kgであり、13%含水時の発熱量は
4313キロカロリー/kgであった。得られた猫砂1
0gに尿21gの吸尿時の、所謂使用時の濡れた状態に
おける発熱量は、1770キロカロリー/kgであり、
使用後の焼却処理が可能であることを示した。この粒状
物を集めて、猫のトイレ用の砂とした。室内において、
この猫のトイレ用の砂20gに、水道水1000ミリリ
ツトルに食塩10g及びアンモニア水10ミリリツトル
を溶解した疑似尿を30ミリリツトルを加え、疑似尿に
より固まった部分を取り出した。本例トイレ用の砂にお
いて、疑似尿により固まらないトイレ用の砂の量は4.
5gであった。したがつて、疑似尿により固まり形成に
必要とされた量は16.5gである。
The obtained cat litter product obtained granules having a particle size of 10 to 5 mm. This granular material has a heating value of 517 upon drying.
It was 0 kcal / kg, and the calorific value when 13% water was contained was 4313 kcal / kg. The obtained cat litter 1
When 21 g of urine is absorbed in 0 g, the calorific value in the wet state at the time of so-called use is 1770 kcal / kg,
It was shown that incineration after use is possible. The granules were collected and used as cat litter sand. Indoors
To 20 g of the litter for this cat, 30 ml of simulated urine obtained by dissolving 10 g of salt and 10 ml of aqueous ammonia in 1000 ml of tap water was added, and a portion solidified by the simulated urine was taken out. In the toilet sand of this example, the amount of the sand for the toilet that does not solidify due to the pseudo urine is 4.
It was 5 g. Therefore, the amount required for clump formation by simulated urine is 16.5 g.

【0047】したがって、本例のトイレ用の砂における
吸水性は、(30/16.5)倍、即ち1.95倍であ
った。またこの猫のトイレ用の砂を猫のトイレに厚さ3
cmに敷いて使用したが、猫は普段と同様にトイレとし
て使用しており、使用の上で何等支障がなかった。猫が
排泄に使用後、この猫のトイレ用の砂の、猫が排泄した
部分については、容易に取り出すことができた。しか
も、本例の猫のトイレ用の砂は、吸水性及び脱臭性を有
し、屋内に不快な臭い発生するのを避けることができ
た。
Therefore, the water absorption of the toilet sand of this example was (30 / 16.5) times, that is, 1.95 times. In addition, the sand for this cat litter should be 3
The cat was used as a toilet as usual, and there was no problem in using it. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0048】例4 図2に示す装置を使用して猫砂を製造した例である。本
例において、1mm以下の粒度に粉砕されたペットボト
ル粉砕粉75重量部、高吸水性樹脂(ハイモ株式会社製
ハイモサブ500)5重量部及びベントナイト粉10重
量部をリボンミキサーに入れ、水を加えて混合し、含水
率40重量%の混合物を得た。この混合物を押出し造粒
装置の押出部に入れて、直径5.5mmの開口及び30
mmのプレート厚さのダイスを通して押出し、チョッパ
ーで適宜裁断して造粒した。この造粒物を整粒装置で整
粒し、振動型円板の被覆装置に入れ、皿状円板を振動さ
せながら、コンピュータ用の記録用紙を粉砕した、0.
4mm以下の粒度の紙粉6.5重量部及び150μm以
下の粒度の高吸水性樹脂(ハイモ株式会社製ハイモサブ
500)3.5重量部の混合物の被覆材料を、造粒物に
対して15重量%の割合で造粒物表面に散布することに
より被覆した。被覆された造粒物を整粒機でほぐして、
熱風乾燥機で、水分が13%になるまで乾燥した。
Example 4 This is an example of producing cat litter using the apparatus shown in FIG. In this example, 75 parts by weight of a pulverized plastic bottle pulverized to a particle size of 1 mm or less, 5 parts by weight of a highly water-absorbent resin (Himosub 500 manufactured by Himo Co., Ltd.) and 10 parts by weight of bentonite powder are put into a ribbon mixer, and water is added. To obtain a mixture having a water content of 40% by weight. This mixture was put into the extrusion section of an extrusion granulation apparatus, and an opening having a diameter of 5.5 mm and 30
The mixture was extruded through a die having a plate thickness of 2 mm and was appropriately cut with a chopper and granulated. The granulated product was sized by a sizing device, placed in a vibrating disk coating device, and the recording paper for a computer was crushed while vibrating the dish-shaped disk.
A coating material of a mixture of 6.5 parts by weight of paper powder having a particle size of 4 mm or less and 3.5 parts by weight of a highly water-absorbent resin having a particle size of 150 μm or less (Himosub 500 manufactured by Himo Co., Ltd.) was added to the granulated material by 15 parts by weight. The granules were coated by spraying on the surface of the granules at a percentage of%. Loosen the coated granules with a sizing machine,
It was dried with a hot air dryer until the water content became 13%.

【0049】得られた猫砂製品は、粒度10〜5mmの
粒状物を得た。この粒状物は、乾燥時の発熱量が464
4キロカロリー/kgであり、13%含水時の発熱量は
3957キロカロリー/kgである。得られた猫砂10
gに尿15gの吸尿時の、所謂使用時の濡れた状態にお
ける発熱量は、1770キロカロリー/kgであり、使
用後の焼却処理が可能であることを示した。この粒状物
を集めて、猫のトイレ用の砂とした。室内において、こ
の猫のトイレ用の砂20gに、水道水1000ミリリツ
トルに食塩10g及びアンモニア水10ミリリツトルを
溶解した疑似尿を30ミリリツトルを加え、疑似尿によ
り固まった部分を取り出した。本例トイレ用の砂におい
て、疑似尿によりトイレ用の砂は全部が固まり、残りは
無かった。したがつて、疑似尿により固まり形成に必要
とされた猫砂の量は20gである。
The obtained cat litter product obtained granules having a particle size of 10 to 5 mm. This granular material has a heat value of 464 upon drying.
It is 4 kcal / kg, and the calorific value when 13% water is contained is 3957 kcal / kg. Cat sand 10 obtained
The calorific value in the wet state at the time of soaking when soaking 15 g of urine in 1 g was 1770 kcal / kg, indicating that incineration treatment after use was possible. The granules were collected and used as cat litter sand. In the room, 30 milliliters of pseudo urine obtained by dissolving 10 g of tap water and 10 milliliters of ammonia water in 20 milliliters of tap water and 30 milliliters of pseudo urine were added to 20 g of sand for the toilet of the cat, and a portion solidified by the pseudo urine was taken out. In the toilet sand of this example, all of the toilet sand was solidified due to pseudo urine, and there was no remainder. Therefore, the amount of cat litter required for clump formation due to pseudo urine is 20 g.

【0050】したがって、本例のトイレ用の砂における
吸水性は、(30/20)倍、即ち1.5倍であった。
またこの猫のトイレ用の砂を猫のトイレに厚さ3cmに
敷いて使用したが、猫は普段と同様にトイレとして使用
しており、使用の上で何等支障がなかった。猫が排泄に
使用後、この猫のトイレ用の砂の、猫が排泄した部分に
ついては、容易に取り出すことができた。しかも、本例
の猫のトイレ用の砂は、吸水性及び脱臭性を有し、屋内
に不快な臭い発生するのを避けることができた。
Therefore, the water absorption of the toilet sand of this example was (30/20) times, that is, 1.5 times.
In addition, this cat litter was laid on the cat litter with a thickness of 3 cm, and the cat was used as a litter as usual, so there was no problem in using the litter. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0051】例5.図2に示す装置を使用して猫砂を製
造した例である。本例において、1mm以下の粒度に粉
砕されたポリプロピレン不織布の粉砕粉30重量部、ボ
リエチレンフィルムの粉砕粉30重量%、コンピュータ
用の記録用紙を粉砕した、0.4mm以下の粒度の紙粉
15重量部及び高吸水性樹脂(ハイモ株式会社製ハイモ
サブ500)5重量部をリボンミキサーに入れ、水を加
えて混合し、含水率40重量%の混合物を得た。この混
合物を押出し造粒装置の押出部に入れて、直径5.5m
mの開口及び30mmのプレート厚さのダイスを通して
押出し、チョッパーで適宜裁断して造粒した。この造粒
物を整粒装置で整粒し、振動型円板の被覆装置に入れ、
皿状円板を振動させながら、コンピュータ用の記録用紙
を粉砕した、0.4mm以下の粒度の紙粉12重量部及
び150μm以下の粒度の高吸水性樹脂(ハイモ株式会
社製ハイモサブ500)8重量部の混合物の被覆材料
を、造粒物に対して20重量%の割合で造粒物表面に散
布することにより被覆した。被覆された造粒物を整粒機
でほぐして、熱風乾燥機で、水分が13%になるまで乾
燥した。
Example 5 This is an example in which cat sand is manufactured using the apparatus shown in FIG. In this example, 30 parts by weight of a crushed powder of a polypropylene nonwoven fabric crushed to a particle size of 1 mm or less, 30 wt% of a crushed powder of a polyethylene film, and paper powder 15 of a particle size of 0.4 mm or less crushed from recording paper for a computer. Parts by weight and 5 parts by weight of a superabsorbent resin (Himosub 500, manufactured by Hymo Corporation) were placed in a ribbon mixer, water was added and mixed to obtain a mixture having a water content of 40% by weight. This mixture was put into the extrusion section of an extrusion granulator, and was 5.5 m in diameter.
The mixture was extruded through a die having an opening of m and a plate thickness of 30 mm, and was appropriately cut with a chopper and granulated. This granulated product is sized by a sizing device and put into a vibration type disk coating device.
12 parts by weight of paper powder having a particle size of 0.4 mm or less and 8 parts by weight of a highly water-absorbent resin having a particle size of 150 μm or less (Himosub 500 manufactured by Hymo Co., Ltd.) Parts of the coating material of the mixture were coated by spraying on the surface of the granules in a proportion of 20% by weight with respect to the granules. The coated granules were loosened with a sizing machine and dried with a hot air drier until the water content became 13%.

【0052】得られた猫砂製品は、粒度10〜5mmの
粒状物を得た。この粒状物は、乾燥時の発熱量が7,9
45キロカロリー/kgであり、13%含水時の発熱量
は6,829キロカロリー/kgである。得られた猫砂
10gに尿15gの吸尿時の、所謂使用時の濡れた状態
における発熱量は、1623キロカロリー/kgであ
り、使用後の焼却処理が可能であることを示した。この
粒状物を集めて、猫のトイレ用の砂とした。室内におい
て、この猫のトイレ用の砂20gに、水道水1000ミ
リリツトルに食塩10g及びアンモニア水10ミリリツ
トルを溶解した疑似尿を30ミリリツトルを加え、疑似
尿により固まった部分を取り出した。本例トイレ用の砂
において、疑似尿によりトイレ用の砂は全部が固まり、
残りは無かった。したがつて、疑似尿により固まり形成
に必要とされた猫砂の量は20gである。したがつて、
本例のトイレ用の砂における吸水性は、(30/20)
倍、即ち1.5倍であった。
The obtained cat litter product obtained granules having a particle size of 10 to 5 mm. This granular material has a heating value of 7,9 when dried.
It is 45 kcal / kg, and the calorific value at 13% water content is 6,829 kcal / kg. The calorific value in the so-called wet state at the time of sucking 15 g of urine into 10 g of the obtained cat litter during so-called use was 1,623 kcal / kg, indicating that the incineration treatment after use was possible. The granules were collected and used as cat litter sand. In the room, 30 milliliters of pseudo urine obtained by dissolving 10 g of tap water and 10 milliliters of ammonia water in 20 milliliters of tap water and 30 milliliters of pseudo urine were added to 20 g of sand for the toilet of the cat, and a portion solidified by the pseudo urine was taken out. In the toilet sand for this example, all the sand for the toilet solidifies due to pseudo urine,
There was no rest. Therefore, the amount of cat litter required for clump formation due to pseudo urine is 20 g. Therefore,
The water absorption of the toilet sand of this example is (30/20)
2 times, that is, 1.5 times.

【0053】室内において、この猫のトイレ用の砂20
gに、水道水1000ミリリツトルに食塩10g及びア
ンモニア水10ミリリツトルを溶解した疑似尿を30ミ
リリツトルを加え、疑似尿により固まった部分を取り出
した。本例トイレ用の砂において、疑似尿により固まら
ないトイレ用の砂の量は4gであった。したがつて、疑
似尿により固まり形成に必要とされた量は16gであ
る。したがつて、本例のトイレ用の砂における吸水性
は、(30/16)倍、即ち1.9倍であった。またこ
の猫のトイレ用の砂を猫のトイレに厚さ3cmに敷いて
使用したが、猫は普段と同様にトイレとして使用してお
り、使用の上で何等支障がなかった。猫が排泄に使用
後、この猫のトイレ用の砂の、猫が排泄した部分につい
ては、容易に取り出すことができた。しかも、本例の猫
のトイレ用の砂は、吸水性及び脱臭性を有し、屋内に不
快な臭い発生するのを避けることができた。
In the room, the sand 20 for this cat toilet
Then, 30 ml of pseudo urine prepared by dissolving 10 g of salt and 10 ml of aqueous ammonia in 1000 ml of tap water was added to 30 g, and a portion solidified by the pseudo urine was taken out. In the toilet sand of this example, the amount of toilet sand that did not solidify due to pseudo urine was 4 g. Thus, the amount required for clump formation by simulated urine is 16 g. Therefore, the water absorption of the toilet sand of this example was (30/16) times, that is, 1.9 times. In addition, this cat litter was laid on the cat litter with a thickness of 3 cm, and the cat was used as a litter as usual, so there was no problem in using the litter. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0054】例6.ポリエチレンテレフタレート廃材粉
を、乾燥べースで49重量部、高吸水性樹脂を乾燥べー
スで2重量部及びベントナイト粉を乾燥べースで49重
量部を混合機に入れて、水を加えて混合し、含水率40
重量%の混合物を得た。この混合物を押出し造粒装置の
押出部に入れて、直径5.5mmの開口及び25mmの
プレート厚さのダイスを通して押し出し適宜裁断して造
粒した。この造粒物にベントナイト粉17重量部を一様
に振りかけて、造粒物表面を一様に被覆した。被覆され
た造粒物を熱風乾燥機で、水分が13%になるまで乾燥
し、平均直径6mm、長さ7〜10mmの粒状物を得
た。この粒状物は、乾燥時の発熱量が2,287キロカ
ロリー/kgであった。また13%含水時の発熱量は1
907kcal/kgであり、この粒状物を集めて、猫
のトイレ用の砂とした。室内において、この猫のトイレ
用の砂に35℃の温度の塩化ナトリウム1%の疑似尿を
加えたが、本体重量の1〜1.5倍の吸水性があった。
またこの猫のトイレ用の砂を猫のトイレに厚さ3cmに
敷いて使用したが、猫は普段と同様にトイレとして使用
しており、使用の上で何等支障がなかった。猫が排泄に
使用後、この猫のトイレ用の砂の、猫が排泄した部分に
ついては、容易に取り出すことができた。しかも、本例
の猫のトイレ用の砂は、吸水性及び脱臭性を有し、屋内
に不快な臭い発生するのを避けることができた。
Example 6 49 parts by weight of polyethylene terephthalate waste material powder on a dry basis, 2 parts by weight of a superabsorbent resin on a dry basis, and 49 parts by weight of bentonite powder on a dry basis are put into a mixer, and water is added. To mix, water content 40
A mixture by weight was obtained. The mixture was put into an extrusion section of an extrusion granulation apparatus, extruded through a die having a diameter of 5.5 mm and a die having a plate thickness of 25 mm, and appropriately cut to be granulated. 17 parts by weight of bentonite powder was uniformly sprinkled on the granules to uniformly coat the surface of the granules. The coated granules were dried with a hot air drier until the water content became 13% to obtain granules having an average diameter of 6 mm and a length of 7 to 10 mm. This particulate matter had a heating value of 2,287 kcal / kg when dried. The amount of heat generated when 13% water is contained is 1
It was 907 kcal / kg and the granules were collected and used as cat litter sand. In the room, 1% pseudo-urine of sodium chloride at a temperature of 35 ° C. was added to the sand for the toilet of the cat, but the water absorption was 1 to 1.5 times the body weight.
In addition, this cat litter was laid on the cat litter with a thickness of 3 cm, and the cat was used as a litter as usual, so there was no problem in using the litter. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0055】例7.ポリエチレンテレフタレート廃材粉
50重量部、ハイモ株式会社製の高吸水性樹脂ハイモサ
ブ500(登録商標)1重量部及びベントナイト粉49
重量部を混合機に入れて、水を加えて混合し、含水率4
0重量%の混合物を得た。この混合物を押し出し造粒装
置の押出部に入れて、直径5.5mmの開口及び25m
mの厚さのダイスを通して押し出し、適宜裁断して造粒
した。この造粒物に、0.4mmに粉砕した紙粉20重
量部、高吸水性樹脂10重量部及びベントナイト粉70
重量部の混合物を、造粒物に対し17重量%の割合で一
様にまぶして、造粒物表面を一様に被覆した。ベントナ
イト粉で被覆された造粒物の上に、10倍に希釈したポ
リエチレングリコール希釈溶液を噴霧した。この造粒物
を熱風乾燥機で水分が13%になるまで乾燥して、平均
直径6mm、長さ6〜15mmの粒状物を得た。この粒
状物は、乾燥時の発熱量が、2497キロカロリー/k
gであった。また13重量%の含水時に発熱量は208
8kcal/kgであり、この粒状物を集めて、猫のト
イレ用の砂とした。室内において、この猫のトイレ用の
砂に35℃の温度の塩化ナトリウム1%の疑似尿を加え
たが、本体重量の1〜1.5倍の吸水性があった。また
この猫のトイレ用の砂を猫のトイレに厚さ3cmに敷い
て使用したが、猫は普段と同様にトイレとして使用して
おり、使用の上で何等支障がなかった。猫が排泄に使用
後、この猫のトイレ用の砂の、猫が排泄した部分につい
ては、容易に取り出すことができた。しかも、本例の猫
のトイレ用の砂は、吸水性及び脱臭性を有し、屋内に不
快な臭い発生するのを避けることができた。
Example 7 50 parts by weight of polyethylene terephthalate waste material powder, 1 part by weight of super water-absorbent resin Hymosub 500 (registered trademark) manufactured by Hymo Co., Ltd. and bentonite powder 49
Put parts by weight into a mixer, add water and mix, water content 4
A 0% by weight mixture was obtained. This mixture was put into the extrusion section of an extrusion granulator, and an opening having a diameter of 5.5 mm and 25 m
It was extruded through a m-thick die, cut appropriately, and granulated. 20 parts by weight of paper powder pulverized to 0.4 mm, 10 parts by weight of a superabsorbent resin, and 70 parts of bentonite powder
A part by weight of the mixture was uniformly sprinkled at a ratio of 17% by weight with respect to the granules to uniformly coat the surface of the granules. A 10-fold diluted solution of polyethylene glycol was sprayed on the granules coated with bentonite powder. The granulated product was dried with a hot air drier until the water content became 13% to obtain a granulated product having an average diameter of 6 mm and a length of 6 to 15 mm. This granular material has a calorific value of 2,497 kcal / k when dried.
g. The calorific value is 208 when 13% by weight of water is contained.
It was 8 kcal / kg and the granules were collected and used as cat litter sand. In the room, 1% pseudo-urine of sodium chloride at a temperature of 35 ° C. was added to the sand for the toilet of the cat, but the water absorption was 1 to 1.5 times the body weight. In addition, this cat litter was laid on the cat litter with a thickness of 3 cm, and the cat was used as a litter as usual, so there was no problem in using the litter. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0056】例8.紙おむつの不良品を粉砕し風簸によ
り分級して得た、ポリエチレン、ポリプロピレン、離型
紙及びエラスチックゴムを含む紙おむつのプラスチック
廃物を、乾燥べースで50重量部、パルプスラッジりの
再燃焼焼却灰を乾燥べースで47重量部及び吸水性樹脂
3重量%の混合物を混合機に入れて、水を加えて混合
し、含水率40重量%の混合物を得た。この混合物の含
水率は35.5重量%であり、この混合物を押出し造粒
装置の押出部に入れて、直径5.5mmの開口及び25
mmの厚さのダイスを通して押し出し適宜裁断して造粒
した。この造粒物に、紙粉55重量部及び吸水性樹脂4
5重量部の混合物を、造粒物に対して13重量%の割合
で一様に振りかけて、造粒物表面全体を一様に被覆し
た。被覆された造粒物を熱風乾燥機で、水分が13%に
なるまで乾燥し、平均直径6mm、長さ7〜10mmの
粒状物を得た。この粒状物は、乾燥時の発熱量が4,9
44キロカロリー/kgであった。また13%含水時の
発熱量が4218kca1/kgであり、この粒状物を
集めて、猫のトイレ用の砂とした。室内において、この
猫のトイレ用の砂に35℃の温度の塩化ナトリウム1%
の疑似尿を加えたが、本体の1〜3倍の吸水性があっ
た。またこの猫のトイレ用の砂を猫のトイレに厚さ3c
mに敷いて使用したが、猫は普段と同様にトイレとして
使用しており、使用の上で何等支障がなかった。猫が排
泄に使用後、この猫のトイレ用の砂の、猫が排泄した部
分については、容易に取り出すことができた。しかも、
本例の猫のトイレ用の砂は、吸水性及び脱臭性を有し、
屋内に不快な臭い発生するのを避けることができた。
Example 8 Waste plastic diapers, including polyethylene, polypropylene, release paper and elastic rubber, obtained by crushing defective diapers and classifying them by elutriation. Was mixed in a mixer with 47 parts by weight of a dry base and 3% by weight of a water-absorbent resin, and water was added and mixed to obtain a mixture having a water content of 40% by weight. The water content of this mixture was 35.5% by weight, and the mixture was put into the extruding section of an extrusion granulating apparatus, and an opening having a diameter of 5.5 mm and a diameter of 25 mm was added.
The mixture was extruded through a die having a thickness of mm to be appropriately cut and granulated. 55 parts by weight of paper powder and water absorbent resin 4
5 parts by weight of the mixture was uniformly sprinkled at a ratio of 13% by weight with respect to the granules to uniformly coat the entire surface of the granules. The coated granules were dried with a hot air drier until the water content became 13% to obtain granules having an average diameter of 6 mm and a length of 7 to 10 mm. This granular material has a calorific value of 4.9 when dried.
It was 44 kcal / kg. The calorific value when 13% water was contained was 4218 kcal / kg, and the granules were collected and used as sand for cat litter. In the room, 1% sodium chloride at a temperature of 35 ° C.
Was added, but the water absorption was 1 to 3 times that of the main body. In addition, the sand for this cat litter is put on the cat litter with a thickness of 3c.
The cat was used as a toilet as usual, and there was no problem in using it. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover,
The cat litter sand of this example has water absorbency and deodorant properties,
The generation of unpleasant odors indoors was avoided.

【0057】例9.例3の紙おむつのプラスチック廃物
を、乾燥べースで20重量部、水分65重量%の茶殻6
0重量郡、パルプスラッジりの再燃焼焼却灰を乾燥べー
スで17重量部及び吸水性樹脂3重量%の混合物を混合
機に入れて混合した。混合物の含水率は39重量%であ
り、この混合物を押出し造粒装置の押出部に入れて、直
径5.5mmの開口及び25mmの厚さのダイスを通し
て押し出し適宜裁断して造粒した。この造粒物に紙粉5
0重量部、パルプスラッジ再燃焼焼却灰10重量部及び
吸水性樹脂40重量部の混合物を、該造粒物に対して1
3重量%の割合で振りかけて、造粒物表面を一様に被覆
した。被覆された造粒物を熱風乾燥機で、水分が13%
になるまで乾燥し、平均直径6mm、長さ7〜10mm
の粒状物を得た。この粒状物は、乾燥時の発熱量が50
64キロカロリー/kgであった。また13%含水時の
発熱量が4323kcal/kgであり、この粒状物を
集めて、猫のトイレ用の砂とした。室内において、この
猫のトイレ用の砂に35℃の温度の塩化ナトリウム1%
の疑似尿を加えたが、本体重量の1〜3倍の吸水性があ
った。またこの猫のトイレ用の砂を猫のトイレに厚さ3
cmに敷いて使用したが、猫は普段と同様にトイレとし
て使用しており、使用の上で何等支障がなかった。猫が
排泄に使用後、この猫のトイレ用の砂の、猫が排泄した
部分については、容易に取り出すことができた。しか
も、本例の猫のトイレ用の砂は、吸水性及び脱臭性を有
し、屋内に不快な臭い発生するのを避けることができ
た。
Example 9 20 parts by weight of the plastic waste of the disposable diaper of Example 3 on a dry basis, and 65% by weight of moisture in a tea shell 6
0 weight group, reburning incineration ash of pulp sludge was mixed with a mixture of 17 parts by weight of a dry base and 3% by weight of a water absorbent resin in a mixer. The water content of the mixture was 39% by weight, and the mixture was put into an extrusion section of an extrusion granulation apparatus, extruded through an opening having a diameter of 5.5 mm and a die having a thickness of 25 mm, and appropriately cut and granulated. Paper powder 5
A mixture of 0 parts by weight, 10 parts by weight of pulp sludge reburning incinerated ash and 40 parts by weight of a water-absorbent resin was added to the granulated product in an amount of 1 part.
By sprinkling at a ratio of 3% by weight, the surface of the granulated material was uniformly coated. The coated granules are dried with a hot air dryer to a moisture content of 13%.
Dried until average diameter 6mm, length 7-10mm
Was obtained. This granular material has a calorific value of 50 when dried.
It was 64 kcal / kg. The calorific value when 13% water was contained was 4323 kcal / kg, and the granules were collected and used as sand for cat litter. In the room, 1% sodium chloride at a temperature of 35 ° C.
Was added, but the water absorption was 1-3 times the body weight. In addition, the sand for this cat litter should be 3
The cat was used as a toilet as usual, and there was no problem in using it. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0058】例10.例3の紙おむつのプラスチック廃
物を、乾燥べースで37重量部、水分65重量%の茶殻
37重量部、ベントナイトを乾燥べースで23重量部及
び吸水性樹脂3重量%の混合物に水36kgを加えて混
合した。混合物の含水率は44重量%であり、この混合
物を押出し造粒装置の押出部に入れて、直径5.5mm
の開口及び25mmの厚さのダイスを通して押し出し、
適宜裁断して造粒した。この造粒物にベントナイト粉2
0重量部、0.4mmの篩を通した紙粉50重量部及び
吸水性樹脂30重量部の混合物を、造粒物に対して13
重量%の割合で一様に振りかけて、造粒物表面を一様に
被覆した。被覆された造粒物を熱風乾燥機で、水分が1
2%になるまで乾燥し、平均直径6mm、長さ7〜10
mmの粒状物を得た。この粒状物は、乾燥時の発熱量が
5667キロカロリー/kgであった。また12%含水
時の発熱量が4847kcal/kgであり、この粒状
物を集めて、猫のトイレ用の砂とした。室内において、
この猫のトイレ用の砂に35℃の温度の塩化ナトリウム
1%の疑似尿を加えたが、本体重量の1〜3倍の吸水性
があった。またこの猫のトイレ用の砂を猫のトイレに厚
さ3cmに敷いて使用したが、猫は普段と同様にトイレ
として使用しており、使用の上で何等支障がなかった。
猫が排泄に使用後、この猫のトイレ用の砂の、猫が排泄
した部分については、容易に取り出すことができた。し
かも、本例の猫のトイレ用の砂は、吸水性及び脱臭性を
有し、屋内に不快な臭い発生するのを避けることができ
た。
Example 10 The plastic waste of the disposable diaper of Example 3 was mixed with 37 parts by weight of a dry base, 37 parts by weight of tea leaves having a water content of 65% by weight, and bentonite in a mixture of 23 parts by weight on a dry basis and 3% by weight of a water-absorbent resin, and 36 kg of water. Was added and mixed. The water content of the mixture was 44% by weight, and the mixture was put into an extrusion section of an extrusion granulator, and was 5.5 mm in diameter.
Extruded through an opening and a 25 mm thick die,
Granulation was performed by appropriately cutting. Bentonite powder 2
0 parts by weight, a mixture of 50 parts by weight of paper powder passed through a 0.4 mm sieve and 30 parts by weight of a water-absorbent resin was added to
The granulated material was uniformly sprinkled at a ratio of% by weight to uniformly coat the surface of the granulated material. The coated granules are dried with hot air
Dried to 2%, average diameter 6mm, length 7-10
mm was obtained. This particulate matter had a calorific value of 5667 kcal / kg when dried. The calorific value when containing 12% water was 4847 kcal / kg, and the granules were collected and used as sand for cat litter. Indoors
To the litter of the cat was added 1% pseudo urine of sodium chloride at a temperature of 35 ° C., and the water absorption was 1-3 times the body weight. In addition, this cat litter was laid on the cat litter with a thickness of 3 cm, and the cat was used as a litter as usual, so there was no problem in using the litter.
After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors.

【0059】例11.ペットボトル粉砕粉を、乾燥べー
スで37重量部、パルプスラッジ再燃焼焼却灰を乾燥べ
ースで20重量部、水分65重量%の茶殻40重量部、
ベントナイトを乾燥べースで23重量部及び吸水性樹脂
3重量%の混合物に水を加えて混合した。混合物の含水
率は32重量%であり、この混合物を押出し造粒装置の
押出部に入れて、直径5.5mmの開口及び25mmの
厚さのダイスを通して押し出し、適宜裁断して造粒し
た。この造粒物にベントナイト粉25重量部、パルプス
ラッジ再燃焼焼却灰25重量部及び吸水性樹脂50重量
部の混合物を、造粒物に対して15重量%の割合で振り
かけて、造粒物表面を一様に被覆した。被覆された造粒
物を熱風乾燥機で、水分が12%になるまで乾燥し、平
均直径6mm、長さ7〜10mmの粒状物を得た。この
粒状物は、乾燥時の発熱量が3595キロカロリー/k
gであった、また12%含水時の発熱量が3045kc
al/kgであり、この粒状物を集めて、猫のトイレ用
の砂とした。
Example 11 37 parts by weight of the pulverized powder of PET bottles on a dry basis, 20 parts by weight of pulp sludge reburning incinerated ash on a dry basis, 40 parts by weight of tea husks having a water content of 65% by weight,
Bentonite was mixed with a mixture of 23 parts by weight of a dry base and 3% by weight of a water-absorbent resin by adding water. The water content of the mixture was 32% by weight, and the mixture was put into an extrusion section of an extrusion granulation apparatus, extruded through an opening having a diameter of 5.5 mm and a die having a thickness of 25 mm, and cut and granulated as appropriate. A mixture of 25 parts by weight of bentonite powder, 25 parts by weight of pulp sludge reburning incinerated ash and 50 parts by weight of a water-absorbent resin was sprinkled on the granulated material at a ratio of 15% by weight to the granulated material, and the surface of the granulated material was sprinkled. Was uniformly coated. The coated granules were dried with a hot air drier until the water content became 12% to obtain granules having an average diameter of 6 mm and a length of 7 to 10 mm. This granular material has a calorific value of 3595 kcal / k when dried.
g and the calorific value when containing 12% water is 3045 kc.
al / kg, and collected the granules to provide sand for cat litter.

【0060】室内において、この猫のトイレ用の砂に3
5℃の温度の塩化ナトリウム1%の疑似尿を加えたが、
本体重量の1〜3倍の吸水性があった。またこの猫のト
イレ用の砂を猫のトイレに厚さ3cmに敷いて使用した
が、猫は普段と同様にトイレとして使用しており、使用
の上で何等支障がなかった。猫が排泄に使用後、この猫
のトイレ用の砂の、猫が排泄した部分については、容易
に取り出すことができた。しかも、本例の猫のトイレ用
の砂は、吸水性及び脱臭性を有し、屋内に不快な臭い発
生するのを避けることができた。これらの実施例におい
ては、ポリエチレンテレフタレート廃材粉及び紙おむつ
のプラスチック廃材粉等のプラスチック廃材粉を使用す
るが、これらポリエチレンテレフタレートの一部を他の
プラスチック廃材で代えることができる。湿っているプ
ラスチック廃材を原料とする場合は、含有する水分によ
り造粒できれば、外部から水を供給する必要がない。し
かし含有する水分が必要以上に多いときは、同一又は他
のプラスチック廃材の脱水又は乾燥されているものを加
えて、水分を調整するのが好ましい。
In the room, 3
I added pseudo urine of 1% sodium chloride at a temperature of 5 ° C,
There was 1-3 times the water absorption of the body weight. In addition, this cat litter was laid on the cat litter with a thickness of 3 cm, and the cat was used as a litter as usual, so there was no problem in using the litter. After the cat used it for excretion, the portion of the cat toilet sand that the cat excreted could be easily removed. Moreover, the cat litter of the present example had water absorption and deodorization properties, and was able to avoid generation of unpleasant odor indoors. In these embodiments, plastic waste powder such as polyethylene terephthalate waste powder and plastic waste powder of disposable diapers is used, but a part of the polyethylene terephthalate can be replaced with other plastic waste. When wet plastic waste is used as the raw material, there is no need to supply water from the outside if the granulation can be performed using the contained moisture. However, when the water content is larger than necessary, it is preferable to adjust the water content by adding dewatered or dried same or other plastic waste materials.

【0061】[0061]

【発明の効果】本発明は、動物用の排泄物処理材は、プ
ラスチック廃材粉に、無機質配合材料を加えて動物用排
泄物処理材とするので、従来の動物の排泄物処理材に比
して、焼却処理が容易であり、廉価な動物用排泄物処理
材を提供することができる。また、本発明によると、そ
の儘廃棄物として処理されていた該プラスチック廃材を
有効利用することができ、かつ高い発熱量の故にその侭
廃棄されていた高い発熱量のブラスチック廃材を動物用
排泄物処理材とすることにより低発熱量化させることが
でき、灰分量を少なくして焼却処理を可能とさせる。従
来の排泄物処理材に比して、廃棄物処理が容易である。
According to the present invention, the animal excrement disposal material is an animal excrement disposal material obtained by adding an inorganic compounding material to a plastic waste material powder. As a result, it is possible to provide an inexpensive animal excrement disposal material that can be easily incinerated and inexpensive. Further, according to the present invention, it is possible to effectively use the plastic waste material that has been treated as waste as it is, and to excrete a high calorific value plastic waste material that has been discarded as it is because of its high calorific value. By using a material to be treated, the calorific value can be reduced, and the amount of ash is reduced to enable incineration. Waste disposal is easier than conventional waste disposal materials.

【0062】以上のように、本発明は、従来の動物の廃
棄物処理材に比して、プラスチック廃材の廃棄に係る問
題点と、従来の使用済みの動物の排泄物処理材の非可燃
性に係る廃棄処理の間題点を一挙に解決すると共に、動
物の皮膚に寄生する害虫を駆除するものであり、資源の
有効利用、プラスチック廃材粉のコストの軽減及び環境
廃棄物の処理の軽減等の点で有意義なものである。
[0062] As described above, the present invention has the problems associated with the disposal of plastic waste material and the non-flammability of the conventional animal excrement disposal material as compared with the conventional animal waste disposal material. And at the same time eliminate the problems associated with waste disposal, and eliminate pests that infest the animal skin, effectively use resources, reduce the cost of plastic waste powder, and reduce the disposal of environmental waste. It is significant in the point.

【図面の簡単な説明】[Brief description of the drawings]

【図1】本発明の一実施例の動物用排泄物処理材を製造
する工程を示す概略の流れ工程図である。
FIG. 1 is a schematic flow chart showing a process of manufacturing an animal excrement disposal material according to one embodiment of the present invention.

【図2】本発明の他の一実施例の動物用排泄物処理材を
製造する工程を示す概略の流れ工程図である。
FIG. 2 is a schematic flow chart showing a process of manufacturing an animal excrement disposal material according to another embodiment of the present invention.

【符号の説明】[Explanation of symbols]

1 ポリエチレンテレフタレート廃材粉用の計量ホッパ
ー 2 ポリエチレンテレフタレート廃材粉供給用コンベヤ
装置のコンベヤベルト 3 高吸水性樹脂の計量ホッパー 4 高吸水性樹脂供給用のコンベヤ装置のコンベヤベル
ト 5 ポリエチレンテレフタレート廃材粉供給用のコンベ
ヤベルトの搬出口 6 高吸水性樹脂供給用のコンベヤベルトの搬出口 7 ポリエチレンテレフタレート廃材粉と高吸水性樹脂
の混合物搬送用のコンベヤベルト 8 コンベヤベルト7の出口側 9 混合装置 10 ベントナイト用の計量ホッパー 11 ベントナイト供給用のコンベヤ装置のコンベヤベ
ルト 12 コンベヤベルト11の出口側 13 混合装置7の混合物出口 14 混合物搬送用のコンベヤベルト 15 押出し造粒装置 16 予備混合装置 17 水の供給管 18 ダイス 19 円形篩 20 造粒物搬送用のコンベヤ装置のコンベヤベルト 21 円形篩19の篩上出口 22 円形篩19の篩上搬送用のコンベヤ装置のコンベ
ヤベルト 23 振動型整粒機 24 円形篩19の篩下出口 25 円形篩19の篩下粒子搬送用のコンベヤ装置のコ
ンベヤベルト 26 篩 27 篩26の篩下搬送用のコンベヤ装置のコンベヤベ
ルト 28 篩26の篩上出口 29 篩26の篩上搬送用のコンベヤ装置のコンベヤベ
ルト 30 第一の造粒物被覆装置 31 第一の造粒物被覆装置30の入口の篩 32 第二の造粒物被覆装置 33 第一の造粒物被覆装置30の出口の篩分装置 34 第一の造粒物被覆装置30の散布用定量供給器 35 第二散布用噴霧装置 36 第一被覆材料散布用ホッパー 37 被覆液タンク 38 被覆造粒物搬送用のコンベヤ装置のコンベヤベル
ト 39 乾燥装置 40 乾燥物出口 41 乾燥造粒物搬送用のコンベヤ装置のコンベヤベル
ト 42 製品タンク 43 製品搬送用のコンベヤ装置のコンベヤベルト 44 袋詰め領域
DESCRIPTION OF SYMBOLS 1 Measuring hopper for polyethylene terephthalate waste powder 2 Conveyor belt of conveyor device for supplying polyethylene terephthalate waste powder 3 Metering hopper for superabsorbent resin 4 Conveyor belt of conveyor device for supplying superabsorbent resin 5 For supplying polyethylene terephthalate waste powder Conveyor belt carry-out port 6 Conveyor belt carry-out port for supplying superabsorbent resin 7 Conveyor belt for transporting a mixture of polyethylene terephthalate waste material powder and superabsorbent resin 8 Outlet side of conveyor belt 7 9 Mixing device 10 Measuring for bentonite Hopper 11 Conveyor belt of conveyor device for supplying bentonite 12 Outlet side of conveyor belt 11 Mixture outlet of mixing device 7 Conveyor belt for transporting mixture 15 Extrusion granulating device 16 Premixing device 17 Water supply pipe 18 Chair 19 Circular sieve 20 Conveyor belt of conveyor device for conveying granulated material 21 Outlet on circular sieve 19 for conveyor 22 Conveyor belt of conveyor device for circular sieve 19 for conveying on sieve 23 Vibrating type granulator 24 of circular sieve 19 Under-sieve outlet 25 Conveyor belt of a conveyor device for transferring under-size particles of the circular sieve 19 26 Sieve 27 Conveyor belt of a conveyor device for transferring of under-size sieve 26 28 Out-of-sieve outlet of sieve 26 29 For on-sieve transfer of sieve 26 Conveyor belt of conveyor device 30 First granulated material coating device 31 Screen of inlet of first granulated material coating device 30 32 Second granulated material coating device 33 Exit of first granulated material coating device 30 Sieving device 34 Spraying quantitative feeder of first granulated material coating device 30 35 Second spraying device 36 Hopper for spraying first coating material 37 Coating liquid tank 38 Coating device for conveying coated granulated material Conveyor belt 39 drying device 40 dry product outlet 41 dry granulation conveyor belt 44 bags stuffed region of the conveyor belt 42 product tank 43 product conveyor for conveying the conveyor device for conveying the Beya device

Claims (21)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂とを含有して粒状に形成され
ていることを特徴とする動物用排泄物処理材。
1. A plastic waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polypropylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder, a polyester waste material powder, or two or more kinds of these waste material powders; An animal excrement disposal material characterized by being formed in a granular form containing a smaller amount of a water-absorbent resin than the plastic waste material powder.
【請求項2】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂と、小麦粉、澱粉、コーンス
ターチ、カルボキシメチルセルロース、プルラン若しく
はゼラチン又はこれら二以上の潤滑、接着及び保水機能
を有する配合物質とを含有して粒状に形成されているこ
とを特徴とする動物用排泄物処理材。
2. A plastic waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polypropylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder, a polyester waste material powder, or two or more kinds of these waste material powders; A water-absorbent resin in a smaller amount than the plastic waste powder, and flour, starch, corn starch, carboxymethylcellulose, pullulan or gelatin or a mixture of two or more of these having a lubricating, adhesive and water-retaining function are formed into granules. An animal excrement disposal material, characterized in that:
【請求項3】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂とを含有して粒状に形成され
ている粒状芯部を有すると共に、紙粉及び吸水性樹脂を
含有して粒状芯部の表面上に形成されている被覆層部を
有し、前記粒状芯部と被覆層部とにより粒状に形成され
ていることを特徴とする動物用排泄物処理材。
3. A plastic waste powder having a particle size of 3 mm or less, a polyethylene waste powder, a polyethylene waste powder, a polyacrylonitrile waste powder, a nylon waste powder or a polyester waste powder, or a plastic waste powder composed of two or more of these waste powders; A coating formed on the surface of the granular core containing the paper dust and the water-absorbing resin while having a granular core containing the water-absorbing resin in a smaller amount than the plastic waste material powder. An animal excrement disposal material having a layer portion, wherein the material is formed in a granular shape by the granular core portion and the covering layer portion.
【請求項4】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂と、小麦粉、澱粉、コーンス
ターチ、カルボキシメチルセルロース、プルラン若しく
はゼラチン又はこれら二以上の潤滑、接着及び保水機能
を有する配合物質とを含有して粒状に形成されている粒
状芯部を有すると共に、紙粉及び吸水性樹脂を含有して
粒状芯部の表面上に形成されている被覆層部を有し、前
記粒状芯部と被覆層部とにより粒状に形成されているこ
とを特徴とする動物用排泄物処理材。
4. A plastic waste powder having a particle size of 3 mm or less, a polyethylene waste powder, a polypropylene waste powder, a polyacrylonitrile waste powder, a nylon waste powder or a polyester waste powder, or a plastic waste powder composed of two or more of these waste powders; A water-absorbent resin in a smaller amount than the plastic waste powder, and flour, starch, corn starch, carboxymethylcellulose, pullulan or gelatin or a mixture of two or more of these having a lubricating, adhesive and water-retaining function are formed into granules. Having a granular core portion, having a coating layer portion formed on the surface of the granular core portion containing paper powder and a water-absorbing resin, and being formed in a granular shape by the granular core portion and the coating layer portion. An animal excrement disposal material, characterized in that:
【請求項5】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂とを含有して粒状に形成され
ている粒状芯部を有すると共に、紙粉及び吸水性樹脂を
含有して粒状芯部の表面上に形成されている被覆層部を
有し、前記粒状芯部と被覆層部とにより粒状に形成され
ており、前記粒状芯部若しくは前記被覆層部又は前記粒
状芯部及び前記被覆層部に防黴剤が含有されていること
を特徴とする動物用排泄物処理材。
5. A plastic waste powder composed of two or more kinds of polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder having a particle size of 3 mm or less; A coating formed on the surface of the granular core containing the paper dust and the water-absorbing resin while having a granular core containing the water-absorbing resin in a smaller amount than the plastic waste material powder. It has a layer portion, and is formed in a granular form by the granular core portion and the coating layer portion, wherein the granular core portion or the coating layer portion or the granular core portion and the coating layer portion contain a fungicide. An animal excrement disposal material, characterized in that:
【請求項6】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂と、小麦粉、澱粉、コーンス
ターチ、カルボキシメチルセルロース、プルラン若しく
はゼラチン又はこれら二以上の潤滑、接着及び保水機能
を有する配合物質とを含有して粒状に形成されている粒
状芯部を有すると共に、紙粉及び吸水性樹脂を含有して
粒状芯部の表面上に形成されている被覆層部を有し、前
記粒状芯部と被覆層部とにより粒状に形成されており、
前記粒状芯部若しくは前記被覆層部又は前記粒状芯部及
び前記被覆層部に防黴剤が含有されていることを特徴と
する動物用排泄物処理材。
6. A plastic waste powder composed of two or more kinds of polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder having a particle size of 3 mm or less; A water-absorbent resin in a smaller amount than the plastic waste powder, and flour, starch, corn starch, carboxymethylcellulose, pullulan or gelatin or a mixture of two or more of these having a lubricating, adhesive and water-retaining function are formed into granules. Having a granular core, having a coating layer portion formed on the surface of the granular core portion containing paper powder and a water-absorbing resin, and being formed in a granular shape by the granular core portion and the coating layer portion. Yes,
An animal excrement disposal material, wherein the granular core, the coating layer, or the granular core and the coating layer contain an antifungal agent.
【請求項7】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂とを含有して粒状に形成され
ている粒状芯部を有すると共に、紙粉及び吸水性樹脂を
含有して粒状芯部の表面上に形成されている被覆層部を
有し、前記粒状芯部と被覆層部とにより粒状に形成され
ており、前記粒状芯部若しくは前記被覆層部又は前記粒
状芯部及び前記被覆層部に蒸散性ピレスロイド系防虫剤
が含有されていることを特徴とする動物用排泄物処理
材。
7. A plastic waste powder composed of two or more kinds of polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder having a particle size of 3 mm or less; A coating formed on the surface of the granular core containing the paper dust and the water-absorbing resin while having a granular core containing the water-absorbing resin in a smaller amount than the plastic waste material powder. Having a layer portion, the granular core portion and the coating layer portion are formed in a granular form, and the particulate core portion or the coating layer portion or the particulate core portion and the coating layer portion have a transpirable pyrethroid-based insect repellent. An animal excrement disposal material characterized by being contained.
【請求項8】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂と、小麦粉、澱粉、コーンス
ターチ、カルボキシメチルセルロース、プルラン若しく
はゼラチン又はこれら二以上の潤滑、接着及び保水機能
を有する配合物質とを含有して粒状に形成されている粒
状芯部を有すると共に、紙粉及び吸水性樹脂を含有して
粒状芯部の表面上に形成されている被覆層部を有し、前
記粒状芯部と被覆層部とにより粒状に形成されており、
前記粒状芯部若しくは前記被覆層部又は前記粒状芯部及
び前記被覆層部に蒸散性ピレスロイド系防虫剤が含有さ
れていることを特徴とする動物用排泄物処理材。
8. A plastic waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polyethylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder, a polyester waste material powder, or two or more of these waste material powders; A water-absorbent resin in a smaller amount than the plastic waste powder, and flour, starch, corn starch, carboxymethylcellulose, pullulan or gelatin or a mixture of two or more of these having a lubricating, adhesive and water-retaining function are formed into granules. Having a granular core, having a coating layer portion formed on the surface of the granular core portion containing paper powder and a water-absorbent resin, and being formed in a granular shape by the granular core portion and the coating layer portion. Yes,
An animal excrement disposal material, characterized in that the particulate core or the coating layer, or the particulate core and the coating layer, contain a transpirable pyrethroid-based insect repellent.
【請求項9】 3mm以下の粒度のポリエチレンテレフ
タレート廃材粉、ポリエチレン廃材粉、ポリプロピレン
廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材粉
若しくはポリエステル廃材粉又はこれら廃材粉の二種以
上からなるプラスチック廃材粉と、前記プラスチック廃
材粉より少量の吸水性樹脂とを含有して粒状に形成され
ている粒状芯部を有すると共に、紙粉及び吸水性樹脂を
含有して粒状芯部の表面上に形成されている被覆層部を
有し、前記粒状芯部と被覆層部とにより粒状に形成され
ており、前記粒状芯部若しくは前記被覆層部又は前記粒
状芯部及び前記被覆層部に防黴剤が含有されており、さ
らに前記粒状芯部若しくは前記被覆層部又は前記粒状芯
部及び前記被覆層部には、蒸散性ピレスロイド系防虫剤
が含有されていることを特徴とする動物用排泄物処理
材。
9. A plastic waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polypropylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder, a polyester waste material powder, or two or more kinds of these waste material powders; A coating formed on the surface of the granular core containing the paper dust and the water-absorbing resin while having a granular core containing the water-absorbing resin in a smaller amount than the plastic waste material powder. It has a layer portion, and is formed in a granular form by the granular core portion and the coating layer portion, wherein the granular core portion or the coating layer portion or the granular core portion and the coating layer portion contain a fungicide. The particulate core or the coating layer, or the particulate core and the coating layer, may further contain a transpirable pyrethroid-based insect repellent. An animal excrement disposal material characterized by the following.
【請求項10】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、前記プラスチック
廃材粉より少量の吸水性樹脂と、小麦粉、澱粉、コーン
スターチ、カルボキシメチルセルロース、プルラン若し
くはゼラチン又はこれら二以上の配合物質とを含有して
粒状に形成されている粒状芯部を有すると共に、紙粉及
び吸水性樹脂を含有して粒状芯部の表面上に形成されて
いる被覆層部を有し、前記粒状芯部と被覆層部とにより
粒状に形成されており、前記粒状芯部若しくは前記被覆
層部又は前記粒状芯部及び前記被覆層部に防黴剤が含有
されており、さらに前記粒状芯部若しくは前記被覆層部
又は前記粒状芯部及び前記被覆層部には、蒸散性ピレス
ロイド系防虫剤が含有されていることを特徴とする動物
用排泄物処理材。
10. A plastic waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polypropylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder, a polyester waste material powder, or two or more kinds of these waste material powders; A paper core having a granular core portion containing a small amount of a water-absorbent resin than the plastic waste material powder, wheat flour, starch, corn starch, carboxymethyl cellulose, pullulan or gelatin or a compound of two or more thereof, and It has a coating layer portion formed on the surface of the granular core portion containing powder and a water-absorbing resin, and is formed in a granular shape by the granular core portion and the coating layer portion, and the granular core portion or the The coating layer portion or the granular core portion and the coating layer portion contain a fungicide, An animal excrement disposal material, wherein the granular core or the coating layer, or the granular core and the coating layer, contain a transpirable pyrethroid-based insect repellent.
【請求項11】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂とを
含有して粒状に形成されていることを特徴とする動物用
排泄物処理材。
11. A plastic waste powder having a particle size of 3 mm or less, a polyethylene waste powder, a polyethylene waste powder, a polyacrylonitrile waste powder, a nylon waste powder or a polyester waste powder, or a plastic waste powder composed of two or more of these waste powders; An animal excrement disposal material characterized in that it is formed into a granular form containing an inorganic compounding material powder and a smaller amount of a water-absorbing resin than the plastic waste material powder.
【請求項12】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂と、
小麦粉、澱粉、コーンスターチ、カルボキシメチルセル
ロース、プルラン若しくはゼラチン又はこれら二以上の
潤滑、接着及び保水機能を有する配合物質とを含有して
粒状に形成されていることを特徴とする動物用排泄物処
理材。
12. A plastic waste powder composed of two or more kinds of polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder having a particle size of 3 mm or less; Inorganic blended material powder, a smaller amount of water-absorbent resin than the plastic waste material powder,
An animal excrement disposal material characterized by being formed in a granular form containing wheat flour, starch, corn starch, carboxymethylcellulose, pullulan or gelatin, or a compounded substance having two or more of these having lubricating, adhesive and water retaining functions.
【請求項13】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂とを
含有して粒状に形成されている粒状芯部を有すると共
に、紙粉及び吸水性樹脂を含有して粒状芯部の表面上に
形成されている被覆層部を有し、前記粒状芯部と被覆層
部とにより粒状に形成されていることを特徴とする動物
用排泄物処理材。
13. A plastic waste powder composed of two or more kinds of polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder having a particle size of 3 mm or less; It has a granular core portion that is formed in a granular form containing an inorganic compounding material powder and a smaller amount of a water-absorbent resin than the plastic waste material powder, and contains paper powder and a water-absorbent resin on the surface of the granular core portion. An animal excrement disposal material, characterized in that it has a coating layer portion formed on the surface thereof and is formed in a granular shape by the granular core portion and the coating layer portion.
【請求項14】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂と、
小麦粉、澱粉、コーンスターチ、カルボキシメチルセル
ロース、プルラン若しくはゼラチン又はこれら二以上の
潤滑、接着及び保水機能を有する配合物質とを含有して
粒状に形成されている粒状芯部を有すると共に、紙粉及
び吸水性樹脂を含有して粒状芯部の表面上に形成されて
いる被覆層部を有し、前記粒状芯部と被覆層部とにより
粒状に形成されていることを特徴とする動物用排泄物処
理材。
14. A plastic waste powder composed of two or more kinds of polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder having a particle size of 3 mm or less; Inorganic blended material powder, a smaller amount of water-absorbent resin than the plastic waste material powder,
It has a granular core formed of wheat flour, starch, cornstarch, carboxymethylcellulose, pullulan or gelatin or a compound having two or more of these having lubricating, adhesive and water-retaining functions. An animal excrement disposal material comprising: a resin-containing coating layer formed on the surface of a granular core, wherein the granular core and the coating layer are formed in a granular form. .
【請求項15】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂とを
含有して粒状に形成されている粒状芯部を有すると共
に、紙粉及び吸水性樹脂を含有して粒状芯部の表面上に
形成されている被覆層部を有し、前記粒状芯部と被覆層
部とにより粒状に形成されており、前記粒状芯部若しく
は前記被覆層部又は前記粒状芯部及び前記被覆層部に防
黴剤が含有されていることを特徴とする動物用排泄物処
理材。
15. A plastic waste powder having a particle size of 3 mm or less, a polyethylene waste powder, a polyethylene waste powder, a polyacrylonitrile waste powder, a nylon waste powder or a polyester waste powder, or a plastic waste powder composed of two or more of these waste powders; It has a granular core portion that is formed in a granular form containing an inorganic compounding material powder and a smaller amount of a water-absorbent resin than the plastic waste material powder, and contains paper powder and a water-absorbent resin on the surface of the granular core portion. And a granular layer formed by the granular core portion and the coating layer portion. The granular core portion or the coating layer portion or the granular core portion and the coating layer portion are prevented from forming. An animal excrement disposal material containing a fungicide.
【請求項16】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂と、
小麦粉、澱粉、コーンスターチ、カルボキシメチルセル
ロース、プルラン若しくはゼラチン又はこれら二以上の
潤滑、接着及び保水機能を有する配合物質とを含有して
粒状に形成されている粒状芯部を有すると共に、紙粉及
び吸水性樹脂を含有して粒状芯部の表面上に形成されて
いる被覆層部を有し、前記粒状芯部と被覆層部とにより
粒状に形成されており、前記粒状芯部若しくは前記被覆
層部又は前記粒状芯部及び前記被覆層部に防黴剤が含有
されていることを特徴とする動物用排泄物処理材。
16. A plastic waste powder composed of two or more kinds of polyethylene terephthalate waste powder, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder having a particle size of 3 mm or less; Inorganic compound material powder, a smaller amount of water-absorbent resin than the plastic waste material powder,
It has a granular core formed of wheat flour, starch, cornstarch, carboxymethylcellulose, pullulan or gelatin or a compound having two or more of these having lubricating, adhesive and water-retaining functions. It has a coating layer portion formed on the surface of the granular core portion containing a resin, and is formed in a granular shape by the granular core portion and the coating layer portion, and the granular core portion or the coating layer portion or An animal excrement disposal material, wherein the granular core portion and the coating layer portion contain a fungicide.
【請求項17】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂とを
含有して粒状に形成されている粒状芯部を有すると共
に、紙粉及び吸水性樹脂を含有して粒状芯部の表面上に
形成されている被覆層部を有し、前記粒状芯部と被覆層
部とにより粒状に形成されており、前記粒状芯部若しく
は前記被覆層部又は前記粒状芯部及び前記被覆層部に蒸
散性ピレスロイド系防虫剤が含有されていることを特徴
とする動物用排泄物処理材。
17. A plastic waste powder comprising a polyethylene terephthalate waste powder, a polyethylene waste powder, a polypropylene waste powder, a polyacrylonitrile waste powder, a nylon waste powder or a polyester waste powder having a particle size of 3 mm or less; It has a granular core portion that is formed in a granular form containing an inorganic compounding material powder and a smaller amount of a water-absorbent resin than the plastic waste material powder, and contains paper powder and a water-absorbent resin on the surface of the granular core portion. The granular core and the coating layer are formed in a granular form, and are evaporated to the granular core or the coating layer or the granular core and the coating layer. An animal excrement disposal material comprising a pyrethroid insecticide.
【請求項18】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂と、
小麦粉、澱粉、コーンスターチ、カルボキシメチルセル
ロース、プルラン若しくはゼラチン又はこれら二以上の
潤滑、接着及び保水機能を有する配合物質とを含有して
粒状に形成されている粒状芯部を有すると共に、紙粉及
び吸水性樹脂を含有して粒状芯部の表面上に形成されて
いる被覆層部を有し、前記粒状芯部と被覆層部とにより
粒状に形成されており、前記粒状芯部若しくは前記被覆
層部又は前記粒状芯部及び前記被覆層部に蒸散性ピレス
ロイド系防虫剤が含有されていることを特徴とする動物
用排泄物処理材。
18. A plastic waste powder having a particle size of 3 mm or less, a polyethylene waste powder, a polyethylene waste powder, a polypropylene waste powder, a polyacrylonitrile waste powder, a nylon waste powder or a polyester waste powder, or a plastic waste powder composed of two or more of these waste powders; Inorganic compound material powder, a smaller amount of water-absorbent resin than the plastic waste material powder,
It has a granular core formed of wheat flour, starch, cornstarch, carboxymethylcellulose, pullulan or gelatin or a compound having two or more of these having lubricating, adhesive and water-retaining functions. It has a coating layer portion formed on the surface of the granular core portion containing a resin, and is formed in a granular form by the granular core portion and the coating layer portion, and the granular core portion or the coating layer portion or An animal excrement disposal material characterized in that the particulate core and the coating layer contain a transpirable pyrethroid-based insect repellent.
【請求項19】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂とを
含有して粒状に形成されている粒状芯部を有すると共
に、紙粉及び吸水性樹脂を含有して粒状芯部の表面上に
形成されている被覆層部を有し、前記粒状芯部と被覆層
部とにより粒状に形成されており、前記粒状芯部若しく
は前記被覆層部又は前記粒状芯部及び前記被覆層部に防
黴剤が含有されており、さらに前記粒状芯部若しくは前
記被覆層部又は前記粒状芯部及び前記被覆層部には、蒸
散性ピレスロイド系防虫剤が含有されていることを特徴
とする動物用排泄物処理材。
19. A plastic waste material powder having a particle size of 3 mm or less, a polyethylene waste material powder, a polyethylene waste material powder, a polyacrylonitrile waste material powder, a nylon waste material powder, a polyester waste material powder, or two or more kinds of these waste material powders; It has a granular core portion that is formed in a granular form containing an inorganic compounding material powder and a smaller amount of a water-absorbent resin than the plastic waste material powder, and contains paper powder and a water-absorbent resin on the surface of the granular core portion. And a granular layer formed by the granular core portion and the coating layer portion. The granular core portion or the coating layer portion or the granular core portion and the coating layer portion are prevented from forming. A fungicide is contained, and the particulate core or the coating layer or the particulate core and the coating layer further comprises a transpirable pyrethroid-based protective agent. An animal excrement disposal material containing an insecticide.
【請求項20】 3mm以下の粒度のポリエチレンテレ
フタレート廃材粉、ポリエチレン廃材粉、ポリプロピレ
ン廃材粉、ポリアクリロニトリル廃材粉、ナイロン廃材
粉若しくはポリエステル廃材粉又はこれら廃材粉の二種
以上からなるプラスチック廃材粉と、無機質配合材料粉
と、前記プラスチック廃材粉より少量の吸水性樹脂と、
小麦粉、澱粉、コーンスターチ、カルボキシメチルセル
ロース、プルラン若しくはゼラチン又はこれら二以上の
潤滑、接着及び保水機能を有する配合物質とを含有して
粒状に形成されている粒状芯部を有すると共に、紙粉及
び吸水性樹脂を含有して粒状芯部の表面上に形成されて
いる被覆層部を有し、前記粒状芯部と被覆層部とにより
粒状に形成されており、前記粒状芯部若しくは前記被覆
層部又は前記粒状芯部及び前記被覆層部に防黴剤が含有
されており、さらに前記粒状芯部若しくは前記被覆層部
又は前記粒状芯部及び前記被覆層部には、蒸散性ピレス
ロイド系防虫剤が含有されていることを特徴とする動物
用排泄物処理材。
20. Polyethylene terephthalate waste powder having a particle size of 3 mm or less, polyethylene waste powder, polypropylene waste powder, polyacrylonitrile waste powder, nylon waste powder or polyester waste powder, or plastic waste powder composed of two or more of these waste powders; Inorganic blended material powder, a smaller amount of water-absorbent resin than the plastic waste material powder,
It has a granular core formed of wheat flour, starch, cornstarch, carboxymethylcellulose, pullulan or gelatin or a compound having two or more of these having lubricating, adhesive and water-retaining functions. It has a coating layer portion formed on the surface of the granular core portion containing a resin, and is formed in a granular shape by the granular core portion and the coating layer portion, and the granular core portion or the coating layer portion or The granular core portion and the coating layer portion contain a fungicide, and the granular core portion or the coating layer portion or the granular core portion and the coating layer portion contain a transpirable pyrethroid-based insect repellent. An animal excrement disposal material characterized in that it is made.
【請求項21】 無機質配合材料粉が、ベントナイト、
ゼオライト、パルプスラッジの再燃焼灰、バーミキュラ
イト又はパーライトの粉体であることを特徴とする請求
項6乃至10の何れか一項に記載の動物用排泄物処理
材。
21. The inorganic compounded material powder is bentonite,
The animal excrement disposal material according to any one of claims 6 to 10, wherein the material is zeolite, pulp sludge reburnt ash, vermiculite, or perlite powder.
JP2000099701A 1995-07-25 2000-03-31 Animal waste treatment material containing plastic waste material and method for producing the same Expired - Lifetime JP3315394B2 (en)