JP3261260B2 - Fire protection interior materials - Google Patents

Fire protection interior materials

Info

Publication number
JP3261260B2
JP3261260B2 JP14172394A JP14172394A JP3261260B2 JP 3261260 B2 JP3261260 B2 JP 3261260B2 JP 14172394 A JP14172394 A JP 14172394A JP 14172394 A JP14172394 A JP 14172394A JP 3261260 B2 JP3261260 B2 JP 3261260B2
Authority
JP
Japan
Prior art keywords
flame
retardant
wood
workability
rock wool
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP14172394A
Other languages
Japanese (ja)
Other versions
JPH0813750A (en
Inventor
悟 小西
宏明 碓氷
有弘 足立
悦郎 大槻
豪 永田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Panasonic Electric Works Co Ltd
Original Assignee
Matsushita Electric Works Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Matsushita Electric Works Ltd filed Critical Matsushita Electric Works Ltd
Priority to JP14172394A priority Critical patent/JP3261260B2/en
Publication of JPH0813750A publication Critical patent/JPH0813750A/en
Application granted granted Critical
Publication of JP3261260B2 publication Critical patent/JP3261260B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【産業上の利用分野】この発明は、防火内装材に関する
ものである。さらに詳しくは、この発明は、一般住宅、
集合住宅、公共施設、その他居住空間に用いられる、木
質感とともに高い防火性を有し、軽量で、かつ、十分な
強度と優れた意匠性、施工性、および加工性とを有する
新しい防火内装材に関するものである。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fire protection interior material. More specifically, the present invention
A new fireproof interior material that is used in apartment houses, public facilities, and other living spaces, has a woody feel and high fire resistance, is lightweight, and has sufficient strength and excellent design, workability, and workability. It is about.

【0002】[0002]

【従来の技術】従来、一般住宅、集合住宅、さらに、そ
の他各種の居住空間には、壁材をはじめ天井材、軒下天
井材等として、木材に代わってケイ酸カルシウム、石こ
うボード、ALCパネル等の各種素材からなる無機質材
が利用されている。
2. Description of the Related Art Conventionally, as a wall material, a ceiling material, a ceiling material under an eave, and the like, calcium silicate, a gypsum board, an ALC panel, and the like are used in ordinary houses, apartment houses, and various other living spaces. Inorganic materials made of various materials are used.

【0003】この無機質素材からなる内装材は、木材に
比べ、耐湿性、耐候性に優れ、防火性が良好であるとと
もに、ユニット化や生産が比較的容易であり、コストダ
ウンを図ることができ、その上、居住空間の意匠性が良
好であるという特徴を有している。
[0003] The interior material made of this inorganic material has excellent moisture resistance and weather resistance and good fire resistance as compared with wood, and is relatively easy to unitize and produce, so that the cost can be reduced. In addition, it has the feature that the design of the living space is good.

【0004】[0004]

【発明が解決しようとする課題】しかしながら、従来の
非木質系の無機質系内装材には、たとえばケイ酸カルシ
ウム板や石こうボードのように、一般的に内装用の面材
として使用するには重量が重く、また、割れ、欠け等が
生じやすいため、施工や加工性に難点があった。また、
ロックウールシージング材は天井材等として使用されて
いるが、素材としての強度が小さいため、ある程度強度
が要求される壁材としての使用は難しく、また、天井材
として使用する場合、そのサイズは、たとえば3尺×6
尺等の大きなサイズでは用いることができないという欠
点がある。さらに、石こうボードには、壁紙を貼った内
装用途ではボード自体に強度がないため、壁紙を剥がす
と石こうボードそのものも取り替える必要があるという
不都合があった。
However, conventional non-wooden inorganic interior materials such as calcium silicate boards and gypsum boards are generally not suitable for use as interior facing materials. However, it is heavy, and it is easy to crack, chip, etc., so there is a problem in construction and workability. Also,
Rock wool sheathing material is used as a ceiling material, etc., but its strength as a material is small, so it is difficult to use it as a wall material that requires some strength, and when used as a ceiling material, its size is For example, 3 × 6
There is a disadvantage that it cannot be used with a large size such as a shaku. Further, the gypsum board has a disadvantage that the gypsum board itself needs to be replaced when the wallpaper is peeled off because the board itself has no strength in the interior use where the wallpaper is applied.

【0005】しかも、これら内装材には、意匠性の点で
も制約があった。それと言うのも、従来、内装材の表面
にシートを貼ることにより意匠性を表現しているが、こ
のシート貼りは、現場施工となるため面倒で、また、し
わの発生、はがれという欠点があったからである。この
ような意匠性の問題を解消するために、塗装が一案とし
て考えられるが、セメント、石こう系の材料には、一般
にアルカリ性を示す物が多く、水分と作用して塗装の耐
久性に悪影響を及ぼしたり、塗料の吸い込みムラや表面
強度が弱い等の仕上りに悪影響を及ぼしたりすることが
多かった。
[0005] Moreover, these interior materials have limitations in terms of design. This is because the design is conventionally expressed by sticking a sheet on the surface of the interior material, but this sheet sticking is troublesome because it is performed on site, and has the drawbacks of wrinkling and peeling. This is because the. In order to solve such design problems, painting can be considered as an idea. However, many cement and gypsum-based materials generally show alkalinity, and adversely affect the durability of the coating by acting with moisture. In many cases, or adversely affect the finish such as unevenness in the suction of the paint and low surface strength.

【0006】このように、従来の無機質系で非木質系の
内装材には、意匠性、施工性、および加工性について制
約が大きいのが実情であった。一方、近年になって、居
住空間についての関心の高まりとともに、やわらかさや
暖かみといった木質感が見直されてきており、内装材に
関しても木材の持つ特徴を生かすことへの需要が広がっ
てきている。
[0006] As described above, the conventional inorganic and non-wooden interior materials are largely limited in design, workability, and workability. On the other hand, in recent years, with the growing interest in living spaces, the sense of woodiness such as softness and warmth has been reviewed, and demand for interior materials to utilize the characteristics of wood has been expanding.

【0007】ただ、木材には、ユニット化による生産性
の向上の点において難点があるだけでなく、燃えやすい
ため、内装材としての使用には、室内等における出火や
火災の拡大を防止することのできる防火性、耐火災性の
向上が必要となる。そこで、木材の上記欠点を解消し、
その特徴である木質感を室内に生かしていくための方策
として、木材そのものを難燃処理した難燃合板を使用す
ることや、木材と非木質系内装材とを積層化して使用す
ることが考えられる。
[0007] However, since wood is not only difficult to improve in productivity due to unitization, it is also flammable. It is necessary to improve the fire resistance and fire resistance. Therefore, the above disadvantages of wood are solved,
As a measure to make the most of the characteristic wooden texture in the room, it is conceivable to use flame-resistant plywood made of wood itself and to laminate wood and non-wood interior materials. Can be

【0008】しかしながら、そのような難燃合板や積層
化という工夫にもかかわらず、重量の増大、施工上の大
きな制約、さらに、無機質系材料を用いることによる割
れや欠けが生じやすいという加工上の欠点が懸念され、
実用上満足することのできる改善はこれまでに実現され
ていない。
[0008] However, despite the ingenuity of such a flame-retardant plywood and lamination, there is an increase in weight, a great restriction in construction, and a processing in which cracks and chips are likely to occur due to the use of inorganic materials. There are concerns about shortcomings,
No practically satisfactory improvement has been realized so far.

【0009】この発明は、以上の通りの事情に鑑みてな
されたものであって、木材の有する木質感を有し、しか
も、軽量で、十分な強度を有し、割れや欠けの発生が少
ない施工性および加工性が良好であり、かつ、防火性と
意匠性に優れた新しい防火内装材を提供することを目的
としている。
The present invention has been made in view of the above circumstances, and has a woody feel of wood, is lightweight, has sufficient strength, and has little occurrence of cracks and chips. It is an object of the present invention to provide a new fireproof interior material having good workability and workability, and excellent fireproofness and design.

【0010】[0010]

【課題を解決するための手段】この発明は、上記の課題
を解決するものとして、内部がロックウールからなり、
表面側に難燃・不燃シート、難燃処理木材が順次積層さ
れ、裏面側に難燃未処理木材、難燃・不燃シートが順次
積層された内装材であり、表面が塗装仕上げされている
ことを特徴とする防火内装材を提供する。
According to the present invention, as an object to solve the above-mentioned problems, the inside is made of rock wool,
An interior material in which a flame-retardant / non-combustible sheet and flame-retardant treated wood are sequentially laminated on the front side, and a flame-retardant untreated wood and a flame-retardant / non-combustible sheet are successively laminated on the back side, and the surface is painted. The present invention provides a fireproof interior material characterized by:

【0011】またこの発明は、内部がロックウールから
なり、表面側に難燃・不燃シート、難燃処理木材が順次
積層され、裏面側に難燃・不燃シート、難燃未処理木材
が順次積層された内装材であり、表面が塗装仕上げされ
ていることを特徴とする防火内装材をも提供する。
Further, according to the present invention, the inside is made of rock wool, and a flame-retardant / non-combustible sheet and a flame-retardant treated wood are sequentially laminated on the front side, and a flame-retardant / non-combustible sheet and a flame-retardant untreated wood are laminated sequentially on the back side. Also provided is a fireproof interior material characterized in that the surface is painted and finished.

【0012】[0012]

【作用】この発明の防火内装材は、内部がロックウール
からなり、表層に難燃処理した難燃処理木材が配設され
ているため、軽量であり、しかも、十分な強度を有し、
割れや欠けの発生が少ない施工性および加工性が良好で
あり、かつ、高い防火性をも有する。その上、この発明
の防火内装材は、表面を塗装仕上げすることができ、塗
装には、種々の塗装(木材ではクリア塗装、着色塗装の
何れも可能だが、一般に他の材料ではクリア塗装は少な
い)が可能であり、その結果、高い意匠性が付与可能と
なっている。
The interior material of the fire-resistant material of the present invention is made of rock wool, and the flame-retardant wood treated by the flame-retardant treatment is disposed on the surface layer, so that it is lightweight and has sufficient strength.
It has good workability and workability with less occurrence of cracks and chips, and also has high fire protection. In addition, the fireproof interior material of the present invention can have its surface painted and painted. Various paintings (clear painting and coloring painting are possible for wood, but generally there are few clear paintings for other materials). ) Is possible, and as a result, high designability can be imparted.

【0013】木材を難燃処理する方法、そのために使用
する薬剤、薬剤含有率には、特段の制限はない。たとえ
ば、一般的な方法として、難燃処理剤の溶液の減圧加圧
含浸、浸漬、塗布、または防火塗料の塗布等が例示さ
れ、薬剤には、燐系、硼酸系の薬剤が例示される。別の
難燃処理法としては、反応して水に不溶な不燃性無機物
を生成させるアニオン、カチオンをそれぞれ含有する薬
剤を別々に含浸させることにより、木材中に不溶性不燃
性無機物を生成させる方法が例示される。
There are no particular restrictions on the method of flame retarding wood, the chemicals used therefor, and the chemical content. For example, as a general method, impregnation under reduced pressure of a solution of a flame retardant, an immersion, application, or application of a fire retardant paint, etc., are exemplified, and examples of the agent include phosphorus-based and boric acid-based agents. As another flame-retardant treatment method, a method of producing an insoluble incombustible inorganic substance in wood by separately impregnating a chemical containing an anion and a cation, which react to form an insoluble inorganic substance insoluble in water, respectively. Is exemplified.

【0014】塗装仕上げには、大きく分類して、塗装面
がフラットな塗装と塗装面が凹凸のある塗装があるが、
特に限定されない。塗装面が凹凸のある塗装模様として
は、たとえば砂壁模様、繊維模様、凹凸模様、凸部処理
模様、クレーター模様、ゆず肌模様、スチップル模様、
スタッコ模様等が例示されるが、これらに限定されな
い。これら凹凸感のある塗装仕上げは、意匠性の観点か
ら有効である。たとえば、スタッコ調の凹凸感のある模
様を表現する塗装としてスパッタ塗装が知られており、
その凹凸感によりたとえば壁紙の様なエンボス調の模様
を作ることが可能である。特に、最近の一般住宅等の内
装用途では、凹凸感のある模様は高級感があり、好まれ
る傾向にあるため、スパッタ塗装は好ましい。
[0014] The paint finish is roughly classified into two types: a paint having a flat paint surface and a paint having an uneven paint surface.
There is no particular limitation. As the painted pattern with a painted surface having irregularities, for example, a sand wall pattern, a fiber pattern, an irregular pattern, a convex processing pattern, a crater pattern, a yuzu skin pattern, a stipple pattern,
Stucco patterns and the like are exemplified, but not limited to these. These uneven finishes are effective from the viewpoint of design. For example, sputter coating is known as a paint that expresses a stucco-like uneven pattern,
It is possible to create an embossed pattern such as a wallpaper, for example, by the unevenness. In particular, in interior applications such as recent general homes, sputter coating is preferable because patterns with unevenness have a high-class appearance and tend to be preferred.

【0015】塗料も特に限定されず、たとえば、木材に
一般的に使用される、水性塗料、油性塗料、繊維素塗
料、天然樹脂塗料、合成樹脂塗料等が例示されるが、木
材以外に使用されている塗料を用いることもできる。内
部のロックウール(総称)についても特に限定はされな
いが、市販のロックウール綿、ロックウールシージング
板等が好適である。その厚みは、6〜40mm程度、比
重は、200〜600kg/m3 が入手のしやすさ、コ
ストの点から好ましい。
The paint is not particularly limited. Examples thereof include water paint, oil paint, cellulose paint, natural resin paint, and synthetic resin paint which are generally used for wood. Paints can be used. Although there is no particular limitation on the inner rock wool (general term), commercially available rock wool cotton, rock wool sizing plate, and the like are preferable. The thickness is preferably about 6 to 40 mm, and the specific gravity is preferably 200 to 600 kg / m 3 in terms of availability and cost.

【0016】この発明の防火内装材は、加工性、施工性
等を保持しつつ、強度および防火性を向上させるため
に、表層部および裏層部に難燃・不燃性シートを有す
る。この難燃・不燃シートにより、軽量で、しかも良好
な意匠性、施工性、および加工性という特長を損なうこ
となく、強度および防火性の向上が可能となる。これ
は、木材という可燃物が同量であっても、難燃・不燃シ
ートにより加熱時の炭化層がしっかりと保持され、炭化
層が炎を遮断するとともに熱を断熱することにより、防
火性が向上するためと考えられる。
The fireproof interior material of the present invention has a flame-retardant / non-flammable sheet in the surface layer and the back layer in order to improve the strength and fire resistance while maintaining workability, workability and the like. The flame-retardant / non-flammable sheet can improve strength and fire resistance without deteriorating the features of light weight and good designability, workability, and workability. This is because even if the amount of combustible wood is the same, the flame retardant / non-combustible sheet firmly holds the carbonized layer during heating, and the carbonized layer blocks the flame and insulates the heat, thus improving the fire resistance. It is thought to improve.

【0017】難燃・不燃シートには、たとえば、ロック
ウール、難燃性樹脂、セラミック、ガラス、金属類等が
例示されるが、重量の大きいものは、内装材の総重量に
反映されるばかりでなく、取り扱い上好ましくない。ま
た、施工性および加工性を考慮すれば、極端に切断、切
削しにくい材料もまた好ましくない。これらの観点、コ
スト等からすると、難燃・不燃シートには、ガラス繊維
シートが一般的に好適であると考えられる。
Examples of the flame-retardant / non-combustible sheet include rock wool, flame-retardant resin, ceramics, glass, metals and the like, but those having a large weight are reflected only in the total weight of the interior material. However, it is not preferable in handling. Considering workability and workability, a material that is extremely difficult to cut or cut is also not preferable. From these viewpoints, costs, and the like, it is considered that a glass fiber sheet is generally suitable for a flame-retardant / non-flammable sheet.

【0018】[0018]

【実施例】以下、実施例を示し、さらに詳しくこの発明
の防火内装材について説明する。 (実施例1、2) 図1および図2、そして、表1に示される構成を有する
サンプルを製造した。実施例1に示されるサンプルは、
内部がロックウールシージング板(32)であり、表面
側に難燃・不燃シート(34)、難燃処理木材(31)
が順次積層され、裏面側に難燃未処理木材(33)、難
燃・不燃シート(34)が順次積層され、表面が塗装仕
上げされている。実施例2に示されるサンプルは、内部
がロックウール(44)であり、表面側に難燃・不燃シ
ート(45)、難燃処理木材(43)が順次積層され、
裏面側に難燃・不燃シート(45)、難燃未処理木材
(46)が順次積層され、表面が塗装仕上げされてい
る。
The present invention will be described in more detail with reference to the following examples. Examples 1 and 2 Samples having the configurations shown in FIGS. 1 and 2 and Table 1 were manufactured. The sample shown in Example 1
The inside is a rock wool sheathing plate (32), and a flame-retardant / non-combustible sheet (34) and a flame-retardant treated wood (31) on the surface side
Are sequentially laminated, a non-combustible untreated wood (33) and a flame-retardant / non-combustible sheet (34) are sequentially laminated on the back side, and the surface is painted. In the sample shown in Example 2, the inside is rock wool (44), and a flame-retardant / non-combustible sheet (45) and a flame-retardant treated wood (43) are sequentially laminated on the surface side,
A flame-retardant / non-combustible sheet (45) and a flame-retardant untreated wood (46) are sequentially laminated on the back side, and the surface is painted.

【0019】[0019]

【表1】 [Table 1]

【0020】以上のサンプルについて、その比重、強度
(最大破壊強度)、釘引抜き荷重、および防火性を評価
した。強度(最大破壊荷重)については、長さ200m
m×幅15mmのサンプルにより曲げ試験を実施し、最
大破壊荷重を求めた。L方向:試験サンプルの長さ方向
が、表層の難燃処理木材の繊維方向と平行、およびW方
向:試験サンプルの長さ方向が、表層の難燃処理木材の
繊維方向と直角の2方向について、各n=3で強度試験
を実施した。評価は、L方向≧60kgf、かつW方向
≧30kgfの場合を○、L、Wのいずれかが左記値を
下回る場合を△、L、Wともに下回る場合を×で示す。
なお、市販の石こうボードの最大破壊荷重は、L方向=
53kgf、W方向=23kgfである。
The specific gravity, strength (maximum breaking strength), nail pulling load, and fire resistance of the above samples were evaluated. For strength (maximum breaking load), length 200m
A bending test was performed on a sample having a size of mx 15 mm in width, and the maximum breaking load was determined. L direction: the length direction of the test sample is parallel to the fiber direction of the flame retardant treated wood on the surface layer, and the W direction: the length direction of the test sample is two directions perpendicular to the fiber direction of the flame retardant treated wood on the surface layer. The strength test was carried out for each n = 3. In the evaluation, the case where L direction ≧ 60 kgf and the W direction ≧ 30 kgf is indicated by 、, the case where any of L and W is below the left value is indicated by Δ, and the case where both L and W are below is indicated by X.
The maximum breaking load of a commercial gypsum board is L direction =
53 kgf, W direction = 23 kgf.

【0021】釘引抜き荷重については、径1.0mm、
長さ40mmの釘を試験片に貫通するように打ち込み、
そのときの引抜き荷重を測定した。評価は、3.5kg
f以上を○、2.0〜3.5kgfを△、2.0kgf
以下を×で示す。なお、市販の5.5mm、3.0mm
厚の合板の釘引抜き荷重は、それぞれ3.5kg、2.
0kgである。防火性は、JISA1321表面試験に
準じて評価した。評価指標は次の通りである。 ○:準不燃性能を有している。 △:準不燃性から難燃以下の間の性能。 ×:難燃以下。 結果は、表2に示した通りである。
The nail pulling load was 1.0 mm in diameter,
A 40 mm long nail is driven into the test piece,
The pulling load at that time was measured. Evaluation is 3.5kg
f or more is ○, 2.0-3.5 kgf is Δ, 2.0 kgf
The following is indicated by x. In addition, commercially available 5.5 mm, 3.0 mm
The nail pull-out load of thick plywood is 3.5 kg and 2.
0 kg. Fire resistance was evaluated according to the JIS 1321 surface test. The evaluation indicators are as follows. :: Semi-flammable performance. Δ: Performance between quasi-incombustibility and flame retardancy or less. ×: Not more than flame retardant. The results are as shown in Table 2.

【0022】[0022]

【表2】 [Table 2]

【0023】実施例1および2に示されるサンプルは、
表2から理解されるように、軽量で、十分な強度と良好
な防火性能を有し、意匠性に優れた防火内装材であると
確認される。 (比較例1、2) 図3および図4、そして、表1に示される構成を有する
サンプルを製造した。比較例1に示されるサンプルは、
内部がロックウールシージング板(52)であり、表層
に難燃処理木材(51)が、裏層に難燃未処理木材(5
3)が、それぞれ配設され、表面が塗装仕上げされてい
ないものである。比較例2に示されるサンプルは、内部
がロックウール(55)であり、表層部に難燃処理木材
(54)が2枚、裏層部に難燃処理木材(56)が2
枚、それぞれ積層され、表面が塗装仕上げされていない
ものである。
The samples shown in Examples 1 and 2
As understood from Table 2, it is confirmed that it is a fireproof interior material which is lightweight, has sufficient strength and good fire protection performance, and is excellent in design. Comparative Examples 1 and 2 Samples having the configurations shown in FIGS. 3 and 4 and Table 1 were manufactured. The sample shown in Comparative Example 1
The inside is a rock wool sheathing plate (52), the flame retardant treated wood (51) is on the surface layer, and the flame retardant untreated wood (5) is on the back layer.
3) are each disposed and the surface is not painted. The sample shown in Comparative Example 2 had rock wool (55) inside, two flame-retardant woods (54) on the surface layer, and two flame-retardant woods (56) on the back layer.
Sheets, each of which is laminated and whose surface is not painted.

【0024】以上のサンプルについても、その比重、強
度(最大破壊強度)、釘引抜き荷重、および防火性を評
価し、その結果を表2に合わせて示した。表2から確認
されるように、比較例1に示されるサンプルは、実施例
1、2に示されるサンプルと比べ、強度が劣り、比較例
2に示されるサンプルは、防火内装材として重要な防火
性能が劣る。しかも、両サンプルとも表面が塗装仕上げ
されていないため、意匠性も劣る。
The specific gravity, strength (maximum breaking strength), nail pulling load, and fire resistance of the above samples were evaluated. The results are shown in Table 2. As confirmed from Table 2, the sample shown in Comparative Example 1 was inferior in strength to the samples shown in Examples 1 and 2, and the sample shown in Comparative Example 2 was an important fire protection material as a fire protection interior material. Poor performance. In addition, since the surfaces of both samples are not painted, the design is inferior.

【0025】[0025]

【発明の効果】以上詳しく説明した通り、この発明によ
り、木材の有する木質感を有し、しかも、軽量で、十分
な強度を有し、割れや欠けの発生が少ない施工性および
加工性が良好であり、かつ、防火性と意匠性に優れた新
しい防火内装材が提供される。
As described in detail above, according to the present invention, the wood has a woody feel, is lightweight, has sufficient strength, and has good workability and workability with less occurrence of cracks and chips. And a new fireproof interior material excellent in fireproofness and design.

【図面の簡単な説明】[Brief description of the drawings]

【図1】実施例1で製造されたサンプルを示した断面図
である。
FIG. 1 is a cross-sectional view showing a sample manufactured in Example 1.

【図2】実施例2で製造されたサンプルを示した断面図
である。
FIG. 2 is a cross-sectional view showing a sample manufactured in Example 2.

【図3】比較例1で製造されたサンプルを示した断面図
である。
FIG. 3 is a cross-sectional view showing a sample manufactured in Comparative Example 1.

【図4】比較例2で製造されたサンプルを示した断面図
である。
FIG. 4 is a cross-sectional view showing a sample manufactured in Comparative Example 2.

【符号の説明】[Explanation of symbols]

31、43、51、54、56 難燃処理木材 32、52 ロックウールシージング板 33、46、53 難燃未処理木材 34、45 難燃・不燃シート 44、55 ロックウール 31, 43, 51, 54, 56 Flame retardant treated wood 32, 52 Rock wool sizing plate 33, 46, 53 Flame retardant untreated wood 34, 45 Flame retardant / non-combustible sheet 44, 55 Rock wool

フロントページの続き (72)発明者 大槻 悦郎 大阪府門真市大字門真1048番地 松下電 工株式会社内 (72)発明者 永田 豪 大阪府門真市大字門真1048番地 松下電 工株式会社内 (56)参考文献 特開 昭52−119629(JP,A) 特開 平3−112604(JP,A) 実開 平3−82709(JP,U) (58)調査した分野(Int.Cl.7,DB名) E04F 13/08 - 13/18 E04B 1/94 Continued on the front page (72) Inventor Etsuo Otsuki 1048 Kadoma Kadoma, Osaka Prefecture Inside Matsushita Electric Works Co., Ltd. (72) Inventor Go Nagata 1048 Odaka Kazuma Kadoma City Osaka Prefecture Inside Matsushita Electric Works Co., Ltd. (56) Reference Document JP-A-52-119629 (JP, A) JP-A-3-112604 (JP, A) JP-A-3-82709 (JP, U) (58) Fields investigated (Int. Cl. 7 , DB name) E04F 13/08-13/18 E04B 1/94

Claims (2)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 内部がロックウールからなり、表面側に
難燃・不燃シート、難燃処理木材が順次積層され、裏面
側に難燃未処理木材、難燃・不燃シートが順次積層され
た内装材であり、表面が塗装仕上げされていることを特
徴とする防火内装材。
1. An interior in which the inside is made of rock wool, and a flame-retardant / non-combustible sheet and a flame-retardant treated wood are sequentially laminated on the front side, and a flame-retardant untreated wood and a flame-retardant / non-combustible sheet are successively laminated on the back side. A fire-resistant interior material characterized by a painted surface.
【請求項2】 内部がロックウールからなり、表面側に
難燃・不燃シート、難燃処理木材が順次積層され、裏面
側に難燃・不燃シート、難燃未処理木材が順次積層され
た内装材であり、表面が塗装仕上げされていることを特
徴とする防火内装材。
2. An interior in which the inside is made of rock wool, a flame-retardant / non-combustible sheet and a flame-retardant treated wood are sequentially laminated on the front side, and a flame-retardant / non-combustible sheet and a flame-retardant untreated wood are laminated sequentially on the back side. A fire-resistant interior material characterized by a painted surface.
JP14172394A 1994-06-23 1994-06-23 Fire protection interior materials Expired - Fee Related JP3261260B2 (en)