JP2018123209A - スタッドレスタイヤ用ゴム組成物 - Google Patents
スタッドレスタイヤ用ゴム組成物 Download PDFInfo
- Publication number
- JP2018123209A JP2018123209A JP2017014944A JP2017014944A JP2018123209A JP 2018123209 A JP2018123209 A JP 2018123209A JP 2017014944 A JP2017014944 A JP 2017014944A JP 2017014944 A JP2017014944 A JP 2017014944A JP 2018123209 A JP2018123209 A JP 2018123209A
- Authority
- JP
- Japan
- Prior art keywords
- resin particles
- mass
- rubber
- rubber composition
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
10%圧縮強度(MPa)=2.8×荷重(N)/{π×粒子径(mm)×粒子径(mm)}
なお、10%圧縮強度は、試験温度25℃において、試験用圧子として直径100μmの平面圧子を使用し、負荷速度0.71mN/秒の条件で測定したときの値とする。
復元率(%)=[復元量(μm)/粒子径(μm)]×100
なお、復元率は、試験温度25℃において、試験用圧子として直径100μmの平面圧子を使用し、負荷速度0.71mN/秒の条件で測定したときの値とする。
樹脂粒子-B
イオン交換水200質量部に、塩化ナトリウム50質量部、ポリビニルピロリドン0.3質量部、シリカ有効成分20質量%であるコロイダルシリカ30質量部およびエチレンジアミン四酢酸・4Na塩を0.02質量部を加えて混合した後、pHを2.8〜3.2に調整することで水性分散媒を調製した。
得られた樹脂粒子‐Bは、真球状の粒子であり、平均粒径13μm、10%圧縮強度0.04MPa、復元率23%、ガラス転移温度−37℃であった。
シリカ有効成分20質量%であるコロイダルシリカの量を5質量部に変更し、エチレングリコールジメタクリレートをトリメチロールプロパントリメタクリレートに変更する以外は、樹脂粒子‐Bと同様に調製して、樹脂粒子-Cを得た。
イオン交換水200質量部に、塩化ナトリウム50質量部、低分子ノニオン界面活性剤であるアジピン酸‐ジエタノールアミン縮合物(濃度50質量%)0.5質量部、シリカ有効成分20質量%であるコロイダルシリカ20質量部を加えて混合した後、pHを2.8〜3.2に調整することで水性分散媒を調製した。
イオン交換水200質量部に、塩化ナトリウム50質量部、低分子ノニオン界面活性剤であるアジピン酸‐ジエタノールアミン縮合物(濃度50質量%)0.5質量部、シリカ有効成分20質量%であるコロイダルシリカ20質量部を加えて混合した後、pHを2.8〜3.2に調整することで水性分散媒を調製した。
表2に記載の共通組成を有し、表1に記載の樹脂粒子を配合した10種類のスタッドレスタイヤ用ゴム組成物(実施例1〜6、標準例、比較例1〜3)を調製するにあたり、硫黄、加硫促進剤、熱膨張性マイクロカプセルおよび樹脂粒子を除く成分を1.7Lのバンバリーミキサーで5分間混練し、145℃に達したとき放出しマスターバッチとした。得られたマスターバッチに、硫黄、加硫促進剤、熱膨張性マイクロカプセルおよび樹脂粒子を加えて70℃のオープンロールで混練することにより、10種類のスタッドレスタイヤ用ゴム組成物を得た。なお、表1に記載の樹脂粒子の配合量は、表2に記載のジエン系ゴム100質量部に対する質量部として表されている。
得られた加硫ゴム試験片を偏平円柱状の台ゴムに貼り付け、インサイドドラム型氷上摩擦試験機を用いて、測定温度−1.5℃、荷重5.5kg/cm2、ドラム回転速度25km/hの条件で氷上摩擦係数を測定した。得られた氷上摩擦係数を、標準例の値を100とする指数にして、「氷上性能」の欄に示した。この指数値が大きいほど氷上摩擦係数が大きく氷上性能が優れることを意味する。
得られた加硫ゴム試験片をJIS K6264に準拠して、ランボーン摩耗試験機(岩本製作所社製)を使用して、温度20℃、荷重39N、スリップ率30%、時間4分の条件で摩耗量を測定した。得られた結果は標準例の逆数を100にする指数とし、「耐摩耗性」の欄に示した。この指数が大きいほど耐摩耗性が優れることを意味し、指数が95以上であれば実用することができる。
・樹脂粒子−A:松本油脂製薬(株)製「マツモトマイクロスフェアーM‐305」(メタクリル酸メチルクロスポリマー(架橋PMMA)、真球状、平均粒径10μm、10%圧縮強度13.93MPa、復元率5%、ガラス転移温度135℃
・樹脂粒子−B〜E:上述した調製方法により得た樹脂微粒子
・天然ゴム:RSS#3
・ブタジエンゴム:日本ゼオン(株)製ポリブタジエンゴムNipol BR1220
・カーボンブラック:東海カーボン(株)製カーボンブラックシースト6、窒素吸着比表面積が115m2/g
・シリカ:日本シリカ工業(株)製Nipsil AQ
・カップリング剤:硫黄含有シランカップリング剤、デクサ社製Si69
・酸化亜鉛:正同化学工業社製酸化亜鉛3種
・ステアリン酸:NOF社製ビーズステアリン酸
・老化防止剤:フレキシス社製6PPD
・アロマオイル:富士興産(株)製アロマオイル
・マイクロカプセル:熱膨張性マイクロカプセル、松本油脂製薬(株)製マツモトマイクロスフェアーF−100
・硫黄:鶴見化学工業(株)製金華印油入微粉硫黄
・加硫促進剤:大内新興化学工業(株)製ノクセラー CZ−G
Claims (3)
- ジエン系ゴム100質量部、カーボンブラックおよび/または白色充填剤30〜100質量部、および樹脂粒子0.5〜30質量部を含み、前記樹脂粒子の平均粒子径が3〜70μm、10%圧縮強度が0.001〜0.5MPa、ガラス転移温度が−30℃以下であることを特徴とするスタッドレスタイヤ用ゴム組成物。
- 前記樹脂粒子がアクリル系樹脂粒子であることを特徴とする請求項1に記載のスタッドレスタイヤ用ゴム組成物。
- 請求項1または2に記載のスタッドレスタイヤ用ゴム組成物からなるトレッド部を有するスタッドレスタイヤ。