JP2015013436A - Laser printing card - Google Patents

Abstract

PROBLEM TO BE SOLVED: To realize various coloring states except normal black coloring when a card is manufactured by using laser-printable base materials for the card, and characters are printed on a card surface.SOLUTION: This laser printing card 1 is characterized by providing pattern printing 104 and transparent overprinting 105 by offset printing after forming a transparent offset anchor layer 103 on a laser coloring layer 102 of a base material 100 for the card whose support layer 101 is white, or providing the pattern printing and the transparent overprinting by the offset printing after forming a silver printing layer 106 and a white printing layer 107 by silkscreen printing, etc., on the laser coloring layer of the base material for the card, and after that, irradiating laser beams from a transparent overprint surface to print silver or white characters on the surfaces of the silver printing layer or the white printing layer, and to print white or black characters on the laser coloring layer.

Description

The present invention relates to a laser printing card. Specifically, in a card using a card base material that has a color layer that is colored by laser beam irradiation on the surface layer, in addition to the color development characteristics of the base material itself, a print layer is further added to the card surface to display various color development states. The present invention relates to a laser printing card made possible.

In recent years, in a contact IC card for a specific application where a decorative element is not required, such as an in-vehicle ETC card or a SIM card, a simple single-layer card is a trial instead of a conventional multi-layer card. Has been used. In the card of such a configuration, although color printing and display printing on the front and back surfaces are performed, the user name, card number, and expiration date are not the method by character embossing as in the past, but the surface layer of the card substrate Substituting the color-developing layer possessed by the laser by irradiating it with a laser and printing it in black.

However, the color-developing layer of the card substrate is manufactured for the purpose of producing a black color, and it is not possible to produce different colors or combine various colors. For this reason, even if it is a simple card, the display may be difficult to view due to the pattern on the card surface, or may be monotonous and not preferred by the user.
Therefore, the present invention intends to change the color development state of the printing by providing an ink layer used for printing on the card surface and combining the ink layer and the laser printing conditions when performing laser printing on the card. Is.

Patent Document 1 and Patent Document 2 are prior art documents describing that a card substrate itself has a coloring layer that develops color by irradiation with a laser beam.
Patent Document 1 describes a card sheet having a support layer and a color developing layer that develops color by laser beam irradiation on at least one surface. The color developing layer before color development is required to have visible light permeability and to be made of a polyester resin. Examples of the color former include various metals that form colored metal oxides by heat generated by photothermal conversion, but are not particularly limited.
Patent Document 2 describes a card sheet comprising a color-forming layer resin mainly composed of a polycarbonate resin or a polymer alloy of a polycarbonate resin and a substantially non-crystalline aromatic polyester resin, and an adhesive layer. Yes.

As for the color former, as in Patent Document 1, various metals and light absorbers that form colored metal oxides by heat generation are mentioned, but are not particularly limited. However, in the examples, a tin-based color former is used.

JP 2004-148642 A Japanese Patent Laid-Open No. 2004-243865

When performing laser printing on a card, it is an object to intentionally change the color of printing by combining ink used for printing and laser printing conditions.
Normally, black color is produced when printing is performed using a laser coloring substrate, but ink containing metal such as Al (aluminum) or TiO ₂ (titanium oxide) at the time of printing (silver or white for silk screen printing) ), And the color development degree of the laser coloring layer is changed by adjusting the laser printing conditions and the metal content of the ink layer to enable printing of gray characters and white characters.

The first of the gist of the present invention is that a transparent support is formed on the laser color-developing layer of a card substrate having a white support layer and a laser color-developing layer that develops black color by laser beam irradiation on at least one outer surface of the support layer. After forming an offset anchor layer, pattern printing by offset printing and transparent overprint printing are provided, and laser beam irradiation is performed on the transparent overprint printing surface to print white to black characters on the laser coloring layer surface. In the laser printing card, which is characterized by what has been done.

According to a second aspect of the present invention, there is provided a white support layer and at least one outer surface of the support layer, on the laser color forming layer of the card substrate having a laser color developing layer that develops a black color by laser beam irradiation. After forming a silver print layer and a white print layer by screen printing, pattern printing by offset printing and transparent overprint printing are provided, and laser beam irradiation is performed from the transparent overprint printing surface, and the white printing layer surface is white. The laser printing card is characterized in that the character printing is performed, the silver character printing is performed on the silver printing layer surface, or the white or black character printing is performed on the laser coloring layer surface.

According to a third aspect of the present invention, a transparent support is formed on the laser color-developing layer of a card substrate having a white support layer and a laser color-developing layer that is colored black by laser beam irradiation on at least one surface of the support layer. After forming an offset anchor layer, a gray print layer by offset printing, pattern printing, and transparent overprint printing are provided, and laser beam irradiation is performed on the transparent overprint printing surface, and gray characters are formed on the gray print layer. The laser printing card is characterized in that printing is performed or white or black characters are printed on the surface of the laser coloring layer.

According to a fourth aspect of the present invention, a silk is formed on the laser color-developing layer of a card substrate having a white support layer and a laser color-developing layer that develops a black color by laser beam irradiation on at least one surface of the support layer. After forming a silver printing layer by screen printing, pattern printing by offset printing and transparent overprint printing are provided, and laser beam irradiation is performed on the transparent overprint printing surface to print silver characters on the silver printing layer. Or a laser printing card, wherein white or black characters are printed on the surface of the laser coloring layer.

In the above, the blackening density of the laser coloring layer of the card substrate may be adjusted by the irradiation density of the laser beam, the support layer of the card substrate is made of polycarbonate resin, and the laser coloring layer is polycarbonate. And a polymer alloy resin of PET-G resin.

It is a top view which shows the form of the card | curd to which this invention is applied. It is a schematic cross section of the card | curd by 1st Embodiment. It is a schematic cross section of the card | curd by 2nd Embodiment. It is a schematic cross section of the card | curd by 3rd Embodiment. It is a schematic cross section of the card | curd by 4th Embodiment. It is sectional drawing of the base material for cards used by this invention.

FIG. 1 is a plan view showing the form of a card to which the present invention is applied.
A card to which the present invention is applied is typically a contact type IC card 1, which has a contact terminal plate 11 at a predetermined position defined by ISO, and an IC chip (not shown) is provided on the lower surface of the contact terminal plate 11. Has been implemented. On the surface of the contact type IC card 1, a card number 12, an expiration date 13, a user name 14 and the like are printed. Conventionally, embossed characters formed by pressing a type ring from the front and back of a card have been used for such printing. In the present invention, instead of this embossing, the coloring layer of the base material is laser beam printed. There is.
Accordingly, a card substrate having a laser printability on the front and back surfaces (or at least the front surface) is used. After printing on the front and back of the single-layer base material, it is cut and mounted with an IC module, and laser printed to complete the card. As in the past, after printing on the front and back core sheets, the oversheets are laminated and bonded, and can be manufactured without going through the press laminating process.

Next, the card substrate used in the present invention will be described.
FIG. 6 is a cross-sectional view of a card substrate used in the present invention. The card substrate 100 is characterized by having a white support layer 101 and a color developing layer 102 that develops a black color by laser beam irradiation on at least one surface of the support layer. In FIG. 6, the material having the color developing layer 102 on both sides of the support layer 101 is illustrated. However, in the case where printing is not provided on the back surface, the color forming layer may be provided only on the front side printing side.
Although the base material 100 for cards is not limited, in the present invention, a polymer alloy resin of a polycarbonate resin and an amorphous aromatic polyester resin (PET-G resin) is used for the front and back color developing layers 102. For the support layer 101, a polycarbonate resin is used, and a material obtained by co-extruding these three layers is used. Since a plurality of sheets formed into a sheet is not laminated and used, the sheet is formed by one extrusion molding. Therefore, even if the layer structure is three layers, it is said to be a single layer base material.

The support layer 101 is mixed with a white pigment such as titanium oxide (TiO ₂ ) to generate white reflected light. The coloring layer 102 originally functions as a conventional oversheet, and is made visible light transmissive before laser beam irradiation. Therefore, it does not contain white pigments or colored colorants. Needless to say, even after the laser beam irradiation, the portion other than the print portion is transparent. Here, “visible light transparency” refers to transparency that allows a layer disposed on the back surface of the layer to be visually recognized.
Although the color former is dispersed in the color forming layer 102, the difference between the refractive index of the resin forming the color developing layer and the refractive index of the color former to be mixed is preferably small, and the difference in refractive index is small. By doing so, the visible light transmittance of the color developing layer 102 can be enhanced.

Examples of the color former include various metals and metal compounds that form black metal oxides by heat generated by a laser beam, and thermoresponsive dyes that blacken. The coloring layer may contain a light absorber that absorbs the wavelength of the laser beam. When such a coloring layer is irradiated with a laser beam, the surrounding binder resin such as a light absorber is carbonized, and the carbonized portion exhibits a black color. Alternatively, a color former such as a metal oxide and a light absorber may be used in combination. Thus, what is necessary is just to satisfy | fill the objective, and the material in particular is not limited in this invention.

The support layer 101 and the coloring layer 102 may be made of substantially the same resin composition material. The support layer 101 and the color forming layer 102 can also be formed from a resin composition mainly composed of a polycarbonate resin or a polymer alloy of a polycarbonate resin and a substantially non-crystalline aromatic polyester resin. By using such a resin composition, the heat resistance of the card can be improved, and the color development layer can be prevented from expanding or deforming even when irradiated with a laser beam.

In the present invention, the polycarbonate resin means a resin composition whose main component is polycarbonate. Polycarbonate resins include those produced from bisphenol A synthesized from bisphenol and acetone by interfacial polymerization, transesterification, pyridine, etc., bisphenol A and dicarboxylic acid derivatives such as tele (iso) phthalic acid dichloride, etc. Polyester carbonate obtained by copolymerization with bisphenol A, derivatives of bisphenol A, such as those obtained by polymerization of tetramethylbisphenol A and the like.

In the present invention, the substantially non-crystalline aromatic polyester-based resin refers to a dehydration condensate of a component such as an aromatic dicarboxylic acid and a diol component. Among them, the crystallinity is low, and it is frequently used in practice such as press fusion. This means that even if the thermal processing is performed, the white turbidity and poor fusion due to crystallization are not caused. In addition, in this invention, PBT (polybutylene terephthalate) etc. are contained in what resembles an amorphous aromatic polyester-type resin, for example.

In order to obtain a predetermined card thickness by the support layer 101 and the color layers 102 on the front and back sides, the total thickness of the card substrate 100 is set to about 0.8 mm, and the thickness of the color layer 102 on one side is 65 μm. To the extent. Accordingly, when the color developing layers are provided on both the front and back surfaces, the central support layer 101 is 670 μm.

Embodiments of the present invention will be described below with reference to the drawings.
FIG. 2 is a schematic cross-sectional view of the card according to the first embodiment. A hole B1 shown in the figure explains a printing state by a laser beam. However, the depth is actually several μm, and even a fine character width is not visually recognized as a hole. The same applies to the subsequent examples.
The card of the first embodiment has a white support layer 101 and at least one surface of the support layer having a color development layer 102 that develops a black color by laser beam irradiation on the laser color development layer 102 of the card substrate 100. In addition, after the transparent offset anchor layer 103 is formed, the pattern printing 104 by offset printing and the transparent overprint printing 105 by offset printing are provided.
Then, laser beam irradiation is performed on the surface of the transparent overprint 105, and the overprint 105, the pattern print 104, and the anchor layer 103 are removed by the beam, and white or black characters are printed on the surface of the laser coloring layer 102. It is characterized by that. This is because the pattern printing 104 and the transparent overprint printing 105 by offset printing are very thin layers, and are easily burned out or gasified by the laser beam.

White to black means white and black, and also includes gray of each stage that changes in the middle from white to black. In the case of white, if the pattern printing 104 and the transparent overprint printing 105 by offset printing on the coloring layer 102 are removed, the white color of the supporting layer 101 can be seen and the white color appears. Although this is not the case, the effect is substantially the same as when white printing is performed, so this is expressed.
In claim 1, “a laser coloring layer that develops black color by laser beam irradiation” refers to a case where the coloring layer 102 is completely colored, and is transparent when not irradiated.
However, if the offset anchor layer 103 is also removed, and the beam reaches the color forming layer 102 as in the hole B1, and the color developing layer 102 is colored even slightly, it becomes light gray.
The density of the coloring layer varies depending on the output of the laser beam to be irradiated and the irradiation density dpi (number of dots per inch). Usually, the output (laser power) is kept constant and is mainly adjusted by dpi. This is because the blackening density increases as the number of dots increases.
Since the laser coloring layer 102 has a thickness of 50 to 100 μm (in this example, 65 μm), the laser coloring layer 102 is not burnt down even if it is blackened by laser beam irradiation.

In the first embodiment, the offset anchor layer 103 is a coating material for improving the fixing of the offset printing ink to the base material, and is printed and applied in a thin layer of 1 to 2 μm or less. Usually, an ultraviolet (UV) curable acrylic transparent ink is used.
The same UV curable ink is used for the pattern printing 104 and the transparent overprint printing 105 by offset printing. The pattern printing 104 employs various colors to correspond to various patterns. Including transparent overprint printing, the thickness is about 0.1 to 3 μm.

FIG. 3 is a cross-sectional view of a card according to the second embodiment. Holes B2, B3, and B4 shown in the figure explain the printing state by the laser beam.
The card of the second embodiment has a white support layer 101 and at least one surface of the support layer, on the color forming layer of the card substrate 100 having a color developing layer 102 that develops a black color by laser beam irradiation. After the silver printing layer 106 and the white printing layer 107 are formed by silk screen printing, the pattern printing 104 by offset printing and the transparent overprint printing 105 by offset printing are provided.
The configuration of the card substrate 100 is the same as that of the first embodiment, and is different from the first embodiment in that a silver print layer 106 and a white print layer 107 are formed on the laser coloring layer 102 by silk screen printing. doing.

Since the silver printing layer 106 and the white printing layer 107 are silk screen printing, they are thicker printing layers than offset printing. In silver printing ink, finely flaky aluminum foil is usually dispersed. Thereafter, as in the first embodiment, pattern printing 104 by offset printing and transparent overprint printing 105 by offset printing are performed.
Then, laser beam irradiation is performed on the surface of the transparent overprint print 105, and the transparent overprint print 105 and the pattern print 104 are removed by the beam. Further, if laser irradiation is performed so that the beam reaches the white print layer 107 by silk screen printing as in the hole B2, the print is white and deeper to the silver print layer 106 as in the hole B3. If so, the print will appear silver.
Since the printing layer by silk screen printing is relatively thick (2 to 3 μm) and contains aluminum foil powder or titanium oxide (TiO ₂ ), the silver printing layer 106 and the white printing layer 107 are likely to remain. is there.
If the laser beam is irradiated to such an extent that both the silver print layer 106 and the white print layer 107 disappear as in the hole B4, the color developing layer 102 is exposed, and the color developing layer 102 is irradiated with the beam. At this stage, as described above, the coloring layer 102 prints white to black characters depending on the irradiation amount.

FIG. 4 is a cross-sectional view of a card according to the third embodiment. Holes B5 and B6 shown in the figure explain the printing state by the laser beam.
The card of the third embodiment has a white support layer 101 and at least one surface of the support layer, on the color forming layer of the card substrate 100 having a color developing layer 102 that develops black color by laser beam irradiation. After the transparent offset anchor layer 103 is formed, the gray print layer 108, the pattern print 104, and the transparent overprint print 105 are provided by offset printing. The gray printing layer 108 by offset printing is an ink obtained by mixing a white ink and a black ink, and white titanium oxide (TiO ₂ ) is contained. Therefore, even in the offset printing, it is difficult to disappear by a laser beam.

As shown in the hole B5, the laser beam is irradiated to such an extent that the pattern printing 104 and the transparent overprint printing 105 by offset printing disappear, and if the gray printing layer 108 is exposed, the printed characters are gray and the beam is further irradiated. Then, when the hole B6 is formed, the laser coloring layer 102 is exposed, and when the coloring layer 102 is irradiated with a beam, the coloring layer 102 exhibits white to black character printing depending on the irradiation amount. .

FIG. 5 is a cross-sectional view of a card according to the fourth embodiment. Holes B7 and B8 shown in the figure explain the printing state by the laser beam.
The card of the fourth embodiment has a white support layer 101 and at least one surface of the support layer on the color forming layer of the card substrate 100 having a color developing layer 102 that develops black color by laser beam irradiation. After the silver printing layer 106 is formed by silk screen printing, the pattern printing 104 by offset printing and the transparent overprint printing 105 are provided.

When the laser beam is irradiated to such an extent that the pattern printing 104 and the transparent overprint printing 105 by offset printing disappear, as in the hole B7, and the silver printing layer 106 by silk screen printing is exposed, the printed characters have a silver color, When the beam is further irradiated to form a hole B8, the laser coloring layer 102 is exposed. When the beam is irradiated on the coloring layer 102, the coloring layer 102 prints white to black characters depending on the amount of irradiation. Will be presented.

Next, laser printing on the card will be described.
Laser printing on the card is performed using a card issuing machine. The card issuer uses a model equipped with a laser printer as one of various modules.
A fiber laser (oscillation wavelength: 1.06 μm) is used for the laser beam.
The pulse energy is 10 mJ, and the size per black spot imprinted with the laser beam is 20 to 90 μm in diameter.
The blackening density of the laser coloring layer 102 can be changed by the output of the laser beam and the irradiation density dpi (number of dots per inch), but is usually adjusted by the irradiation density dpi while keeping the output constant. That is, if dpi is small, it becomes a gray close to white, and as the dpi increases, the density increases and blackens. Therefore, gradation printing is also possible.

Example 1
A transparent laser color developing layer 102 having a total thickness of 800 μm and a central support layer 101 made of a white polycarbonate resin having a thickness of 670 μm and a black colorant made of a molybdenum compound made of a PET-G resin having a thickness of 65 μm on both sides. A contact-type IC card was manufactured using a card base 100 (manufactured by Mitsubishi Plastics Co., Ltd.) 100 coextruded on the entire surface.
First, an offset anchor ink made of an acrylic UV curable ink is printed on the color developing layer 102 surface of the card substrate 100 to form a transparent offset anchor layer 103. Pattern printing 104 by offset printing made of a UV-curable ink and transparent overprint printing 105 on the entire surface were performed. Each ink film thickness is less than 1 μm (see FIG. 2).
In addition, only normal offset printing is performed on the back surface side coloring layer 102 of the card substrate 100, and laser printing is not performed. The following examples are the same, and the description is omitted.

After cutting into individual card sizes, an IC module was mounted, encoding was performed with a card issuing machine (“MX6000” manufactured by Nippon Data Card Co., Ltd.), and laser printing was performed with the laser module of the same machine. The laser module has a fiber laser with a laser power of 24 W, and can print at a resolution of 200 to 1000 dpi.
First, when the card number print of the first line is irradiated with a laser beam at 300 dpi with a laser power of 24 W from the surface of the transparent overprint print 105, the anchor layer 103, the pattern print 104 and the transparent overprint print 105 by offset printing disappear, A character string in which the coloring layer 102 was printed in gray was obtained. Next, when the expiration date of the second row and the user name of the third row are similarly irradiated with a laser beam at 500 dpi of the same output from the transparent overprint printing surface, the color development layer 102 surface of the card substrate 100 is dark. A laser printing card 1 having a gray character string was obtained.

(Example 2)
A contact type IC card was manufactured using the same card substrate 100 as in Example 1.
First, a silver print layer 106 and a white print layer (acrylic UV curable ink) 107 are formed on the surface of the color developing layer 102 of the card substrate 100 using silk screen printing ink (acrylic UV curable ink). did. The silver ink contains scaly aluminum foil powder, and the white ink contains a titanium oxide pigment. The film thickness of the ink layer is in the range of 2 to 3 μm.
From the white printed layer 107, pattern printing 104 by offset printing made of acrylic ultraviolet curable ink and transparent overprint printing 105 on the entire surface were performed. The ink film thickness is less than 1 μm (see FIG. 3).

After cutting into individual card sizes, an IC module was mounted, encoding was performed with the same card issuing machine as in Example 1, and then laser printing was performed with the laser module.
First, when the card number printing of the first line is irradiated with a laser beam at 300 dpi of output 24 W from the transparent overprint printing surface, transparent overprint printing 105 and picture printing 104 by offset printing, the white printing layer 107, silver printing Since the layer 106 disappeared, the coloring layer 102 of the card substrate 100 was exposed, and the coloring layer 102 did not develop color, a white character string formed with the card substrate 100 that was white was obtained. . Next, when the laser beam is irradiated with 500 dpi of the same output from the transparent overprint printing surface in the same manner, the expiration date of the second row and the user name of the third row are displayed on the color developing layer 102 surface of the card substrate 100. A laser printing card 1 having a character string was obtained.

Example 3
A contact type IC card was manufactured using the same card substrate 100 as in Example 1.
First, an offset anchor ink made of an acrylic ultraviolet curable ink was printed on the surface of the laser coloring layer 102 on the surface side of the card substrate 100 to form a transparent offset anchor layer 103. Subsequently, gray printing layer 108 and pattern printing 104 by offset printing made of acrylic ultraviolet curable ink, and transparent overprint printing 105 on the entire surface were performed. Each ink film thickness is less than 1 μm (see FIG. 4).

After cutting into individual card sizes, an IC module was mounted, encoding was performed with the same card issuing machine as in Example 1, and then laser printing was performed with the laser module.
First, when the card number printing of the first line is irradiated with a laser beam at 400 dpi of output 24 W from the transparent overprint printing surface, the transparent overprint printing 105 and the picture printing 104 by offset printing disappear, and the offset gray printing layer A gray print by 108 was seen, and a gray printed character string was obtained. Further, when the laser beam is irradiated at 500 dpi of the same output (24 W) from the transparent overprint printing surface in the same manner as the expiration date of the second row and the user name of the third row, the coloring layer 102 surface of the card substrate 100 As a result, a laser printing card 1 having a gray character string due to color development was obtained.

Example 4
A contact type IC card was manufactured using the same card substrate 100 as in Example 1.
First, on the surface of the coloring layer 102 on the surface side of the card substrate 100, a silver printing layer 106 was formed by silk screen printing ink (acrylic ultraviolet curable ink). The silver ink contains scaly aluminum foil powder. The film thickness of the ink layer is in the range of 2 to 3 μm.
Pattern printing 104 by offset printing made of acrylic ultraviolet curable ink and transparent overprint printing 105 on the entire surface were performed on the silver print layer 106. The ink film thickness is less than 1 μm (see FIG. 5).

After cutting into individual card sizes, an IC module was mounted, encoding was performed with the same card issuing machine as in Example 1, and then laser printing was performed with the laser module.
First, when the card number printing of the first line is irradiated with a laser beam at 300 dpi with an output of 24 W from the transparent overprint printing surface, the transparent overprint printing 105 and the picture printing 104 by the offset printing, and the silver print layer 106 disappear. Since the coloring layer 102 of the card substrate 100 was exposed and the coloring layer 102 did not develop color, a white character string formed of the card substrate 100 that was white was obtained. When the laser beam is irradiated with the expiration date of the second line and the user name of the third line from the transparent overprint printing surface at the same output of 500 dpi, a dark gray character string is formed on the surface of the coloring layer 102 of the card substrate 100. Laser printing card 1 was obtained.

The contact IC cards obtained in Examples 1 to 4 have sufficient practicality as ETC cards and contact IC cards for applications such as ordinary credit cards, and the visibility and durability of printing are also good. It was enough. In addition, it was able to withstand the demand for heat resistance.

DESCRIPTION OF SYMBOLS 1 Contact type IC card, laser printing card 11 Contact terminal board 12 Card number 13 Expiration date 14 User name 100 Card base material 101 Support layer 102 Color development layer 103 Offset anchor layer 104 Pattern printing by offset printing 105 Transparent over by offset printing Print printing 106 Silver printing layer by silk screen printing 107 White printing layer by silk screen printing
108 Gray printing layer by offset printing

Claims (6)

A transparent offset anchor layer is formed on the laser color-developing layer of the card substrate having a white support layer and a laser color-developing layer that is colored black by laser beam irradiation on at least one outer surface of the support layer. Laser printing characterized in that pattern printing by offset printing and transparent overprint printing are provided, and laser beam irradiation is performed from above the transparent overprint printing surface, thereby printing white to black characters on the laser coloring layer surface card. Silver printing layer and white printing by silk screen printing on the laser coloring layer of the card substrate having a white supporting layer and at least one outer surface of the supporting layer having a laser coloring layer that develops black color by laser beam irradiation After forming the layer, pattern printing by offset printing and transparent overprint printing are provided, and laser beam irradiation is performed on the transparent overprint printing surface to print white characters on the white printing layer surface, or the silver color A laser printing card, wherein silver characters are printed on a printed layer surface, or white or black characters are printed on the laser coloring layer surface. A transparent offset anchor layer is formed on the laser color-developing layer of the card substrate having a white support layer and a laser color-developing layer that develops a black color by laser beam irradiation on at least one surface of the support layer. A gray printing layer by offset printing, pattern printing, and transparent overprint printing, and laser beam irradiation is performed on the transparent overprint printing surface to print gray characters on the gray printing layer, or the laser coloring layer surface A laser printing card, wherein white or black characters are printed on the card. A silver print layer by silk screen printing is formed on the laser color development layer of the card substrate having a white color support layer and a laser color development layer that develops a black color by laser beam irradiation on at least one surface of the support layer. Then, pattern printing by offset printing and transparent overprint printing are provided, and laser beam irradiation is performed on the transparent overprint printing surface to print silver characters on the silver printing layer, or white on the laser coloring layer surface. A laser printing card characterized by printing black characters. The laser printing card according to any one of claims 1 to 4, wherein the blackening density of the laser coloring layer of the card substrate is adjusted by the irradiation density of the laser beam. The support layer of the card substrate is made of a polycarbonate resin, and the laser coloring layer is made of a polymer alloy resin of polycarbonate and a PET-G resin, according to any one of claims 1 to 4. Laser printing card.

Images