JP2014222667A - Active material for nonaqueous electrolyte battery, nonaqueous electrolyte battery and battery pack - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an active material for a nonaqueous electrolyte battery containing TiO(B) improving diffusibility, in particular, an insertion/desorption property of lithium ion.SOLUTION: A nonaqueous electrolyte battery comprises: a sheath material; a cathode accommodated within the sheath material; an anode which is accommodated within the sheath material and spatially separated from the cathode and contains an active material containing a monoclinic β-type titanium composite oxide; and a nonaqueous electrolyte battery filling the inside of the sheath material. Regarding the monoclinic β-type titanium composite oxide, in a crystallite diameter calculated by a wide-angle X-ray diffraction method using X-ray source CuKα rays, when a crystallite diameter calculated from a peak with 2θ being present within 48 to 49° is defined as X and a crystallite diameter calculated from a peak with 2θ being present within 24 to 26° is defined as Y, X is greater than Y.

Description

  The present invention relates to a battery active material, a non-aqueous electrolyte battery, and a battery pack.

In recent years, titanium oxide having a monoclinic β-type structure (referred to as TiO ₂ (B)) has attracted attention as an active material for nonaqueous electrolyte batteries (see Patent Documents 1 to 3). Conventionally, spinel-type lithium titanate (Li ₄ Ti ₅ O ₁₂ ) that has been practically used has three lithium ions that can be inserted and removed per unit chemical formula. For this reason, the number of lithium ions that can be inserted / removed per titanium ion was 3/5, and 0.6 was the theoretical maximum. On the other hand, in TiO ₂ (B), the maximum number of lithium ions that can be inserted / removed per titanium ion is 1.0. Therefore, the theoretical capacity is as high as about 335 mAh / g.

However, the practical electrode capacity of TiO ₂ (B) is about 170 to 200 mAh / g as disclosed in Patent Document 1 or Patent Document 2, which is significantly lower than the theoretical capacity. This is because, despite the fact that there are many sites that can serve as Li hosts in the crystal structure of TiO ₂ (B), the diffusibility of Li ions in the solid is low, so that there are few effective mobile Li ions. Conceivable.

JP 2008-34368 A JP 2008-117625 A International Publication No. WO2009 / 028553 A1

The present invention relates to an active material for a battery containing TiO ₂ (B) with improved lithium ion diffusibility, particularly insertion / extraction characteristics, including this active material as a negative electrode active material, and has high capacity and excellent large current characteristics. It is an object of the present invention to provide a non-aqueous electrolyte battery having a non-aqueous electrolyte battery and a battery pack including a plurality of non-aqueous electrolyte batteries.

According to a first aspect of the present invention, there is provided a method for producing an active material for a battery containing a monoclinic β-type titanium composite oxide,
A step of acid-treating an alkali titanate compound to exchange alkali cations with protons;
Washing the product after the proton exchange is completed with water and drying to obtain a proton exchanger as an intermediate product;
A process for producing an active material for a battery, comprising: a step of subjecting the proton exchanger to a first heat treatment at 250 to 500 ° C. and a two-step heat treatment combining a second heat treatment at 500 to 800 ° C. Is provided.

  According to a second aspect of the present invention, a battery active material containing a monoclinic β-type titanium composite oxide, wherein the monoclinic β-type titanium composite oxide uses an X-ray source CuKα ray. In the crystallite diameter calculated by the wide-angle X-ray diffraction method, the crystallite diameter calculated from the peak where 2θ is present at 48 to 49 ° is the crystallite calculated from the peak where X2θ is present at 24 to 26 °. When the diameter is Y, the battery active material X is larger than Y.

  According to the third aspect of the present invention, an exterior material; a positive electrode accommodated in the exterior material; a spatially separated from the positive electrode, accommodated in the exterior material, and monoclinic β-type titanium composite oxide The monoclinic β-type titanium composite oxide is a wide-angle X-ray diffraction method using an X-ray source CuKα ray; and a negative electrode containing an active material contained therein; and a non-aqueous electrolyte filled in the exterior material. The crystallite size calculated from the peak where 2θ is present at 48 to 49 ° is X, and the crystallite size calculated from the peak where 2θ is present at 24 to 26 ° is Y. A non-aqueous electrolyte battery in which X is larger than Y is provided.

  According to a fourth aspect of the present invention, there is provided a battery pack comprising a plurality of the nonaqueous electrolyte batteries of the third aspect, wherein each battery is electrically connected in series, in parallel or in series and in parallel.

  According to the present invention, there is provided a battery active material that contributes to high capacity and excellent large current characteristics, a non-aqueous electrolyte battery that has high capacity and excellent large current characteristics, and a battery pack including a plurality of such non-aqueous electrolyte batteries. Can be provided.

It is sectional drawing which shows the flat type nonaqueous electrolyte battery which concerns on embodiment. It is an expanded sectional view of the A section of FIG. It is a disassembled perspective view which shows the battery pack which concerns on embodiment. It is a block diagram of the battery pack of FIG. 2 is a diagram showing an X-ray diffraction pattern of a titanium composite oxide of Example 1. FIG. It is a figure which shows the crystallite diameter in four surface orientations of the titanium complex oxide of Examples 1, 2 and Comparative Example 1. It is a schematic diagram which shows the crystal structure of a monoclinic system type β-type titanium oxide (TiO ₂ (B)).

  Hereinafter, the battery active material, the nonaqueous electrolyte battery, and the battery pack according to the present invention will be described in detail.

  The battery active material according to the embodiment includes a monoclinic β-type titanium composite oxide. The monoclinic β-type titanium composite oxide is a crystallite calculated from a peak where 2θ is present at 48 to 49 ° in a crystallite diameter calculated by a wide-angle X-ray diffraction method using an X-ray source CuKα ray. X is larger than Y, where Y is a crystallite diameter calculated from a peak having a diameter X, 2θ of 24 to 26 °.

  The wide angle X-ray diffraction method will be described below.

  The powder (sample) obtained by pulverizing the monoclinic β-type titanium composite oxide is filled in a 0.2 mm deep holder of a glass sample plate. Using a glass plate from the outside, the surface of the sample filled in the glass sample plate is smoothed by pressing with a finger at a pressure of several tens of MPa to several hundreds of MPa. At this time, care is taken so that the sample is sufficiently filled in the holder portion, and care is taken so as not to cause insufficient filling (cracking, voids) of the sample. The sample amount is filled so as to be equal to the depth (0.2 mm) of the glass holder, and care is taken so that unevenness does not occur from the reference surface of the glass holder due to excessive or insufficient filling amount.

  Moreover, the following method is more preferable in order to eliminate the shift | offset | difference of a diffraction-beam peak position and the change of intensity ratio by the filling method to a glass sample plate. That is, by applying a pressure of about 250 MPa to the sample for 15 minutes, a green compact pellet having a diameter of 10 mm and a thickness of about 2 mm is produced, and the pellet surface is measured.

  The measurement by the wide angle X-ray diffraction method is as follows.

<Measurement method>
The sample was packed in a standard glass holder having a diameter of 25 mm, and measurement was performed by wide-angle X-ray diffraction. The measuring equipment and conditions are shown below. The measurement environment is room temperature air (18-25 ° C.).

(1) X-ray diffractometer: Bruker AXS; D8 ADVANCE (encapsulated tube type)
X-ray source: CuKα ray (using Ni filter)
Output: 40kV, 40mA
Slit system: Div. Slit; 0.3 °
Detector: LynxEye (High-speed detector)
(2) Scan method: 2θ / θ continuous scan (3) Measurement range (2θ): 5 to 100 °
(4) Step width (2θ): 0.01712 °
(5) Counting time: 1 second / step.

<Analysis and calculation of crystallite size>
From the X-ray diffraction pattern obtained by the wide-angle X-ray diffraction method of such a monoclinic β-type titanium composite oxide, half of the peak where 2θ is present at 48 to 49 ° and half of the peak where 2θ is present at 24 to 26 °. The crystallite diameter (crystallite size) can be calculated using the Scherrer equation shown below for the value range.

  Here, K = 0.9, λ (= 0.15406 nm), βe: half-value width of the diffraction peak, and βo: correction value (0.07 °) of the half-value width.

  The method for calculating the crystallite diameter of the synthesized battery active material is as described above. In addition, for the analysis of the negative electrode (uncharged state) before assembling the electrode (coated / rolled) battery, the above-mentioned measurement was performed on the negative electrode surface, and the crystallite diameter of the active material for the battery was determined by the same method. Can be calculated.

  On the other hand, for the negative electrode of the finished battery, the crystallite diameter can be calculated by the following method. The finished battery is discharged to the rated end voltage at 0.1 C current in a 25 ° C. environment. The discharged battery is disassembled in an inert atmosphere (or in the air), and the negative electrode at the center of the electrode group is cut out. The cut negative electrode is sufficiently washed with ethyl methyl carbonate to remove the electrolyte component. Then, it is deactivated by leaving it in the atmosphere for one day (or washing with water). The above-described measurement is performed on the negative electrode in this state, and the crystallite diameter of the battery active material may be calculated by the same method.

The crystal structure of monoclinic titanium dioxide is denoted as TiO ₂ (B). The crystal structure represented by TiO ₂ (B) mainly belongs to the space group C2 / m, and shows a tunnel structure as illustrated in FIG. The detailed crystal structure of TiO ₂ (B) is described in R. Marchand, L. Brohan, M. Tournoux, Material Research.

As shown in FIG. 7, the crystal structure represented by TiO ₂ (B) has a structure in which titanium ions 53 and oxide ions 52 constitute a skeleton structure portion 51a, and the skeleton structure portions 51a are alternately arranged. . A gap portion 51b is formed between the skeleton structure portions 51a. These void portions 51b serve as host sites for insertion (insertion) of heteroatomic species. TiO ₂ (B) is also said to have host sites capable of occluding and releasing heteroatomic species on the crystal surface. TiO ₂ (B) can reversibly occlude and release lithium ions when lithium ions are inserted into and desorbed from these host sites.

When lithium ions are inserted into the void portion 51b, Ti ⁴⁺ constituting the skeleton is reduced to Ti ³⁺ , thereby maintaining the electrical neutrality of the crystal. Since TiO ₂ (B) has one Ti ⁴⁺ per chemical formula, it is theoretically possible to insert a maximum of one lithium ion between the layers. For this reason, the titanium oxide compound having a TiO ₂ (B) crystal structure can be represented by the general formula Li _x TiO ₂ (0 ≦ x ≦ 1). In this case, as described in Patent Documents 1 and 2, the theoretical capacity of 335 mAh / g, which is nearly twice that of titanium dioxide, is obtained. However, the practical electrode capacity of TiO ₂ (B) is about 170 to 200 mAh / g as described above, which is significantly lower than the theoretical capacity. This is because, despite the fact that there are many sites that can be Li hosts in the crystal structure of TiO ₂ (B), the lithium ions that are inserted into and desorbed from the Li sites are effective because the diffusivity of lithium ions in the solid is low. This is thought to be due to the fact that the number is reduced.

TiO ₂ (B) contained in the active material according to the embodiment is calculated from a peak where 2θ is present at 48 to 49 ° in a crystallite diameter calculated by a wide angle X-ray diffraction method using an X-ray source CuKα ray. X has a characteristic that X is larger than Y, where Y is the crystallite diameter calculated from the peak where X 2θ is in the range of 24 to 26 °. Such TiO ₂ (B) contributes to an excellent large current characteristic with a high capacity by being incorporated as an active material of a nonaqueous electrolyte battery.

The standard X-ray diffraction pattern of TiO ₂ (B) is described in JCPDS 46-1237 or 46-1238, and the peak where 2θ appears at 24-26 ° is the main peak attributed to the (110) plane of TiO ₂ (B). There is a peak where 2θ appears at 48 to 49 °, which is attributed to the (020) plane of TiO ₂ (B). In the X-ray diffraction pattern shown in FIG. 5 illustrated in Example 1 described later, the crystallite diameter can be calculated from each distinct peak detected. Among these peaks, the peak where 2θ appears at 48 to 49 ° is attributed to the (020) plane of TiO ₂ (B), and the crystallite diameter calculated from this peak is the crystallite calculated from other peaks. It can be seen that it is significantly larger than the diameter. The large crystallite diameter of the peak where 2θ appears at 48 to 49 ° means that the unit cells are preferentially arranged in the vector direction of the (020) plane (direction perpendicular to the (020) plane). That is, the unit cell has shape anisotropy preferentially aligned in the vector direction of the (020) plane compared to other planes, for example, the (110) plane. A plane obtained by cutting out a crystal at (020) can be represented by a schematic diagram similar to FIG. 7 described above. In the TiO ₂ (B) according to the embodiment, the (020) plane is preferentially stacked in the c-axis direction (perpendicular to the paper surface) shown in FIG. As is clear from FIG. 7, there are a large number of large void portions 51b for inserting and desorbing lithium ions on the (020) plane. In this way, unit cells are preferentially arranged in the vector direction of the (020) plane (direction perpendicular to the (020) plane), so that lithium ions can pass through a large number of voids 51b on the (020) plane to make TiO ₂ (B). And the diffusion rate is considered to be faster than other surfaces (eg, (110) surface).

As a result, TiO ₂ (B) having such characteristics effectively increases the number of lithium ions inserted into and desorbed from the Li site due to the excellent diffusibility of lithium ions in the solid. For this reason, the capacity of the nonaqueous electrolyte battery containing TiO ₂ (B) as an active material can be increased. In addition, since lithium ions can be quickly inserted and extracted from an electrode (for example, the negative electrode) containing TiO ₂ (B) having the above characteristics, a non-aqueous electrolyte battery containing TiO ₂ (B) as an active material. Can improve large current characteristics.

TiO ₂ (B) has a crystallite diameter calculated from a peak where 2θ is present at 48 to 49 ° in a crystallite diameter calculated by a wide-angle X-ray diffraction method using an X-ray source CuKα ray. When the crystallite diameter calculated from the peak existing in the range of 24 to 26 ° is Y, it is more preferable that X and Y satisfy the relationship of the following formula (1).

X / Y ≧ 1.27 (1)
A non-aqueous electrolyte battery containing TiO ₂ (B) whose crystallite diameters X and Y satisfy the formula (1) as an active material can further improve large current characteristics. A more preferable relationship between the crystallite diameters X and Y satisfies the following formula (2).

1.27 ≦ X / Y ≦ 50 (2)
When X / Y exceeds 50, the particle size of the TiO ₂ (B) powder increases, the specific surface area of the powder decreases, and the contact area between the active material and the electrolytic solution, that is, the area where lithium ions can be occluded decreases. There is a fear.

The crystallite diameter X is preferably 20 nm or more. If the crystallite diameter X is less than 20 nm, the proportion of unit cells that are preferentially aligned in the vector direction of the (020) plane may be reduced, and high current characteristics may be impaired. A more preferable crystallite diameter X is 30 nm or more and 1 μm or less. TiO ₂ (B) having such a crystallite diameter X can smoothly diffuse lithium ions in a solid.

The primary particle diameter of TiO ₂ (B) is preferably 30 nm or more and 1 μm or less. It is easy to handle in industrial production as it is 30 nm or more. When the thickness is 1 μm or less, diffusion of lithium ions in the solid can proceed smoothly.

TiO ₂ (B) preferably has a specific surface area of 5 m ² / g or more and 50 m ² / g or less. TiO ₂ (B) having a specific surface area of 5 m ² / g or more can sufficiently secure a lithium ion storage / release site. TiO ₂ (B) of 50 m ² / g or less is easy to handle in industrial production.

TiO ₂ (B) may contain 1000 ppm or less of impurities inevitable in production.

  Next, the manufacturing method of the active material for batteries which concerns on embodiment is demonstrated.

First, an alkali titanate compound such as Na ₂ Ti ₃ O ₇ , K ₂ Ti ₄ O ₉ , or Cs ₂ Ti ₅ O ₁₂ is prepared as a starting material. The alkali titanate compound can be synthesized by a general solid phase reaction method by mixing a substance containing Ti and a substance containing an alkali element such as Na, K, or Cs at a predetermined ratio. The method for synthesizing the starting material is not limited to any method or crystal shape. Note that potassium titanate of K ₂ Ti ₄ O ₉ can be synthesized by, for example, a flux method.

  The starting material is washed thoroughly with pure water to remove impurities from the alkali titanate compound, and then acid-treated to exchange alkali cations for protons. Each sodium ion, potassium ion, and cesium ion in sodium titanate, potassium titanate, and cesium titanate can be exchanged for protons without destroying the crystal structure. Proton exchange by acid treatment is performed, for example, by adding 1 M hydrochloric acid to the starting material and stirring. The acid treatment is desirably performed until the proton exchange is sufficiently completed. During proton exchange, an alkaline solution or an acid solution may be added to the solution to adjust the pH. After the proton exchange is completed, it is washed again with pure water.

The starting material is preferably pulverized in advance with a ball mill before proton exchange. This grinding can perform a smooth proton exchange. The pulverization conditions can be performed by using zirconia balls having a diameter of about 10 to 15 mm per 100 cm ² container and rotating the zirconia balls for about 1 to 3 hours at a rotation speed of 600 to 1000 rpm. The pulverization for 1 hour or less is not preferable because the starting material is not sufficiently pulverized. In addition, pulverization for 3 hours or more, particularly longer than 6 hours is not preferable because the mechanochemical reaction proceeds and phase separation into a compound different from the target product occurs.

Next, the product after proton exchange is washed with water and dried to synthesize a proton exchanger as an intermediate product. Subsequently, TiO ₂ (B) is produced by heat-treating the proton exchanger.

A preferable heat treatment temperature is 250 ° C to 800 ° C. In the heat treatment, it is preferable to reduce the rate of temperature increase up to 400 ° C. When the rate of temperature increase is high, the dehydration process becomes non-uniform and it becomes difficult to synthesize uniform TiO ₂ (B). A preferable temperature increase rate is 200 ° C./hour or less. The lower limit value of the heating rate is not limited. From the viewpoint of productivity, the lower limit value of the heating rate is preferably 10 ° C./hour.

  As for heat processing, it is more preferable to perform the two-step heat processing which combines the 1st heat processing of 250-500 degreeC, and the 2nd heat processing of 500-800 degreeC, for example. The first heat treatment can promote uniform crystallization, and the second heat treatment can immediately increase the crystallinity while suppressing the generation of an impurity phase.

In such a two-stage heat treatment, when the temperature of the first heat treatment is less than 250 ° C., the crystallinity is lowered, the amount of impurity phases such as H ₂ Ti ₈ O ₁₇ is increased, and the electric capacity is increased. May decrease. When the temperature of the second heat treatment exceeds 800 ° C., the crystallinity is improved and the impurity phase such as H ₂ Ti ₈ O ₁₇ is reduced. However, the amount of the anatase TiO ₂ phase which is another impurity phase is mixed. There is a risk that the electric capacity will increase and the electric capacity will decrease. The heat treatment time at a constant temperature may be about 30 minutes to 24 hours, preferably 1 to 3 hours.

  The two-stage heat treatment can improve crystallinity while suppressing the amount of impurity phases mixed. However, the specific surface area tends to decrease during the second heat treatment performed at a high temperature. In order to increase the crystallinity while maintaining the specific surface area in the first heat treatment, it is preferable to coat the substance after the first heat treatment with a carbon precursor and then perform the second heat treatment. The coating of the carbon precursor can be performed, for example, by the following method.

  A predetermined amount of saccharose is added to pure water and dissolved, and a solution diluted with ethanol is prepared. A carbon precursor coating material can be obtained by adding the material after the first heat treatment to the diluted solution and volatilizing the solvent while stirring.

By covering the substance after the first heat treatment with the carbon precursor, sintering between the substances (between particles) can be suppressed during the second heat treatment, so that the specific surface area after the first heat treatment can be maintained. It becomes. If the second heat treatment is performed in the air, the carbon precursor disappears as the second heat treatment proceeds, and only the target TiO ₂ (B) can be produced. If the second heat treatment is performed in an inert atmosphere, it becomes possible to produce TiO ₂ (B) coated with carbon.

  The active material for a battery according to the embodiment can be used not only for a negative electrode described later but also for a positive electrode. Even if applied to any of them, the capacity of the active material is increased and a large current characteristic is improved when used in a battery. Contribute to.

  When the battery active material according to the embodiment is used for the positive electrode, the active material of the negative electrode as the counter electrode can be a metallic lithium, a lithium alloy, or a carbon-based material such as graphite or coke.

  Next, the nonaqueous electrolyte battery according to the embodiment will be described.

The nonaqueous electrolyte battery according to the embodiment includes an exterior material, a positive electrode accommodated in the exterior material, and an active material that is spatially separated from the positive electrode in the exterior material, for example, via a separator. Hereinafter, the exterior material, the negative electrode, the positive electrode, the separator, and the nonaqueous electrolyte, which are constituent members of the nonaqueous electrolyte battery, will be described in detail.

1) Exterior material The exterior material is formed from a laminate film having a thickness of 0.5 mm or less. Further, a metal container having a thickness of 1.0 mm or less is used as the exterior material. The metal container is more preferably 0.5 mm or less in thickness.

  Examples of the shape of the exterior material include a flat type (thin type), a square type, a cylindrical type, a coin type, and a button type. As the exterior material, for example, a small battery exterior material loaded on a portable electronic device or a large battery exterior material loaded on a two- to four-wheeled vehicle or the like is used depending on the battery size.

  As the laminate film, a multilayer film in which a metal layer is interposed between resin layers is used. The metal layer is preferably an aluminum foil or an aluminum alloy foil for weight reduction. For the resin layer, for example, a polymer material such as polypropylene (PP), polyethylene (PE), nylon, polyethylene terephthalate (PET) can be used. The laminate film can be molded into the shape of an exterior material by sealing by heat sealing.

  The metal container is made from aluminum or an aluminum alloy. The aluminum alloy is preferably an alloy containing elements such as magnesium, zinc, and silicon. When transition metals such as iron, copper, nickel and chromium are contained in the alloy, the amount is preferably 100 ppm or less.

2) Negative electrode The negative electrode includes a current collector and a negative electrode layer formed on one or both sides of the current collector and including an active material, a conductive agent, and a binder.

  As the active material, the battery active material containing the monoclinic β-type titanium composite oxide described above is used. The monoclinic β-type titanium composite oxide is a crystallite calculated from a peak where 2θ is present at 48 to 49 ° in a crystallite diameter calculated by a wide-angle X-ray diffraction method using an X-ray source CuKα ray. X is larger than Y, where Y is the crystallite diameter calculated from the peak where the diameter is X and 2θ is in the range of 24 to 26 °. The relationship between the crystallite diameters X and Y preferably satisfies the above-described formula (1) or formula (2).

In such a monoclinic β-type titanium composite oxide, as described above, lithium ions diffuse smoothly into the TiO ₂ (B) through the (020) plane, and the diffusion rate is on the other plane (for example, (110) ) Surface) will be faster. As a result, the nonaqueous electrolyte battery including the negative electrode including the active material containing the monoclinic β-type titanium composite oxide has a high capacity and excellent large current characteristics.

  The conductive agent improves the current collection performance of the active material and suppresses the contact resistance with the current collector. Examples of the conductive agent include acetylene black, carbon black, and graphite.

  The binder can bind the active material and the conductive agent. Examples of the binder include polytetrafluoroethylene (PTFE), polyvinylidene fluoride, fluorine-based rubber, and styrene butadiene rubber.

  The active material, conductive agent and binder in the negative electrode layer are preferably blended in a proportion of 70% to 96% by weight, 2% to 28% by weight and 2% to 28% by weight, respectively. . When the amount of the conductive agent is less than 2% by weight, the current collecting performance of the negative electrode layer is lowered, and the large current characteristics of the nonaqueous electrolyte battery may be lowered. On the other hand, when the amount of the binder is less than 2% by weight, the binding property between the negative electrode layer and the current collector is lowered, and the cycle characteristics may be lowered. On the other hand, the conductive agent and the binder are each preferably 28% by weight or less in order to increase the capacity.

  The current collector is an aluminum foil that is electrochemically stable in a potential range nobler than 1.0 V or an aluminum alloy foil containing elements such as Mg, Ti, Zn, Mn, Fe, Cu, Si. It is preferable.

  The negative electrode is produced, for example, by suspending an active material, a conductive agent, and a binder in a commonly used solvent to prepare a slurry, applying the slurry to a current collector, drying, and then pressing. The The negative electrode may also be produced by forming an active material, a conductive agent and a binder in the form of a pellet to form a negative electrode layer, which is formed on a current collector.

3) Positive electrode The positive electrode includes a current collector and a positive electrode layer formed on one or both sides of the current collector and including an active material, a conductive agent, and a binder.

  As the active material, for example, an oxide, a polymer, or the like can be used.

Examples of the oxide include manganese occluded lithium (MnO ₂ ), iron oxide, copper oxide, nickel oxide and lithium manganese composite oxide (for example, Li _x Mn ₂ O ₄ or Li _x MnO ₂ ), lithium nickel composite oxide. (Eg, Li _x NiO ₂ ), lithium cobalt composite oxide (Li _x CoO ₂ ), lithium nickel cobalt composite oxide (eg, LiNi _1-y Co _y O ₂ ), lithium manganese cobalt composite oxide (eg, Li _x Mn _y) Co _{1 -y} O ₂ ), spinel-type lithium manganese nickel composite oxide (Li _x Mn _{2 -y} Ni _y O ₄ ), lithium phosphorous oxide having an olipine structure (eg, Li _x FePO ₄ , Li _x Fe _{1 -y) Mn y PO 4, Li x CoPO} 4), using ferrous sulfate _{(Fe 2 (SO 4) 3} ), or vanadium oxides (e.g. V ₂ O ₅₎ be able to. Here, x and y are preferably 0 <x ≦ 1 and 0 ≦ y ≦ 1.

  As the polymer, for example, a conductive polymer material such as polyaniline or polypyrrole, or a disulfide polymer material can be used. Sulfur (S) and carbon fluoride can also be used as the active material.

Preferred active materials include lithium manganese composite oxide (Li _x Mn ₂ O ₄ ), lithium nickel composite oxide (Li _x NiO ₂ ), lithium cobalt composite oxide (Li _x CoO ₂ ), and lithium nickel cobalt having a high positive electrode voltage. complex oxide _{(Li x Ni 1-y coyO} 2), spinel type lithium-manganese-nickel composite oxide _{(Li x Mn 2-y Ni} y O 4), lithium manganese cobalt composite oxide _{(Li x Mn y Co 1-} y O ₂ ) or lithium iron phosphate (Li _x FePO ₄ ). Here, x and y are preferably 0 <x ≦ 1 and 0 ≦ y ≦ 1.

  A more preferable active material is a lithium cobalt composite oxide or a lithium manganese composite oxide. Since these active materials have high ion conductivity, diffusion of lithium ions in the positive electrode active material is unlikely to be a rate-determining step in combination with the negative electrode active material described above. For this reason, the said active material is excellent in compatibility with the lithium titanium complex oxide in the said negative electrode active material.

  The active material preferably has a primary particle size of 100 nm to 1 μm. When the primary particle diameter is 100 nm or more, it is easy to handle in industrial production. When the primary particle size is 1 μm or less, diffusion of lithium ions in the solid can proceed smoothly.

The active material preferably has a specific surface area of 0.1 m ² / g or more and 10 m ² / g or less. When the specific surface area is 0.1 m ² / g or more, sufficient lithium ion storage / release sites can be secured. When it is 10 mm ² / g or less, it is easy to handle in industrial production, and good charge / discharge cycle performance can be secured.

  The conductive agent improves the current collection performance of the active material and suppresses the contact resistance with the current collector. Examples of the conductive agent include carbonaceous materials such as acetylene black, carbon black, and graphite.

  The binder binds the active material and the conductive agent. Examples of the binder include polytetrafluoroethylene (PTFE), polyvinylidene fluoride, and fluorine-based rubber.

  The active material, conductive agent and binder in the positive electrode layer are preferably blended at a ratio of 80% to 95% by weight, 3% to 18% by weight and 2% to 17% by weight, respectively. . The conductive agent can exert the above-described effects by setting the amount to 3% by weight or more. By making the amount of the conductive agent 18% by weight or less, decomposition of the non-aqueous electrolyte on the surface of the conductive agent under high temperature storage can be reduced. Sufficient positive electrode strength can be obtained by setting the binder to an amount of 2% by weight or more. By setting the amount of the binder to 17% by weight or less, the amount of the binder, which is an insulating material in the positive electrode, can be reduced, and the internal resistance can be reduced.

  The current collector is preferably, for example, an aluminum foil or an aluminum alloy foil containing an element such as Mg, Ti, Zn, Mn, Fe, Cu, or Si.

  The positive electrode is produced, for example, by suspending an active material, a conductive agent, and a binder in a commonly used solvent to prepare a slurry, applying the slurry to a current collector, drying, and then applying a press. The The positive electrode may also be produced by forming an active material, a conductive agent and a binder in the form of a pellet to form a negative electrode layer on a current collector.

4) Non-aqueous electrolyte Examples of the non-aqueous electrolyte include a liquid non-aqueous electrolyte prepared by dissolving an electrolyte in an organic solvent, or a gel non-aqueous electrolyte obtained by combining a liquid electrolyte and a polymer material.

  The liquid non-aqueous electrolyte is preferably dissolved in an organic solvent at a concentration of 0.5M to 2.5M.

Examples of electrolytes are lithium perchlorate (LiClO ₄ ), lithium hexafluorophosphate (LiPF ₆ ), lithium tetrafluoroborate (LiBF ₄ ), lithium hexafluoroarsenide (LiAsF ₆ ), trifluorometasulfone Lithium salt of lithium acid (LiCF ₃ SO ₃ ), lithium salt of bistrifluoromethylsulfonylimitolithium [LiN (CF ₃ SO ₂ ) ₂ ], or a mixture thereof. The electrolyte is preferably one that is not easily oxidized even at a high potential, and LiPF ₆ is most preferred.

  Examples of organic solvents include propylene carbonate (PC), ethylene carbonate (EC), cyclic carbonates such as vinylene carbonate; chain carbonates such as diethyl carbonate (DEC), dimethyl carbonate (DMC), and methyl ethyl carbonate (MEC). Cyclic ethers such as tetrahydrofuran (THF), 2-methyltetrahydrofuran (2MeTHF), dioxolane (DOX); chain ethers such as dimethoxyethane (DME) and dietoethane (DEE); or γ-butyrolactone (GBL), acetonitrile ( AN) and sulfolane (SL). These organic solvents can be used alone or in the form of a mixed solvent.

  Examples of the polymer material include polyvinylidene fluoride, polyacrylonitrile (PAN), and polyethylene oxide (PEO).

  A preferable organic solvent is a mixed solvent in which at least two of the group consisting of propylene carbonate (PC), ethylene carbonate (EC) and (diethyl carbonate (DEC)) are mixed, or a mixture containing γ-butyrolactone (GBL). It is a solvent.

5) Separator Examples of the separator include a porous film containing polyethylene, polypropylene, cellulose, or polyvinylidene fluoride, or a synthetic resin nonwoven fabric. A preferred porous film is made of polyethylene or polypropylene, and can be melted at a constant temperature to cut off the current, thereby improving safety.

  Next, the nonaqueous electrolyte battery according to the embodiment (for example, a flat type nonaqueous electrolyte battery whose exterior material is a laminate film) will be described more specifically with reference to FIGS. FIG. 1 is a cross-sectional view of a thin nonaqueous electrolyte battery, and FIG. 2 is an enlarged cross-sectional view of part A of FIG. Each figure is a schematic diagram for promoting explanation and understanding of the invention, and its shape, dimensions, ratio, etc. are different from the actual apparatus, but these are considered in consideration of the following explanation and known techniques. The design can be changed as appropriate.

  The flat wound electrode group 1 is housed in a bag-shaped exterior material 2 made of a laminate film in which an aluminum foil is interposed between two resin layers. The flat wound electrode group 1 is formed by winding a laminate of the negative electrode 3, the separator 4, the positive electrode 5, and the separator 4 in this order from the outside in a spiral shape and press-molding. As shown in FIG. 2, the outermost negative electrode 3 has a configuration in which a negative electrode layer 3b is formed on one surface on the inner surface side of the negative electrode current collector 3a. The other negative electrode 3 is configured by forming negative electrode layers 3b on both surfaces of a negative electrode current collector 3a. As the active material in the negative electrode layer 3b, the battery active material containing the monoclinic β-type titanium composite oxide described above is used. The monoclinic β-type titanium composite oxide is a crystallite calculated from a peak where 2θ is present at 48 to 49 ° in a crystallite diameter calculated by a wide-angle X-ray diffraction method using an X-ray source CuKα ray. X is larger than Y, where Y is the crystallite diameter calculated from the peak where the diameter is X and 2θ is in the range of 24 to 26 °. The positive electrode 5 is configured by forming a positive electrode layer 3b on both surfaces of a positive electrode current collector 5a.

  In the vicinity of the outer peripheral end of the wound electrode group 1, the negative electrode terminal 6 is connected to the negative electrode current collector 3 a of the outermost negative electrode 3, and the positive electrode terminal 7 is connected to the positive electrode current collector 5 a of the inner positive electrode 5. . The negative electrode terminal 6 and the positive electrode terminal 7 are extended to the outside from the opening of the bag-shaped exterior material 2. For example, the liquid non-aqueous electrolyte is injected from the opening of the bag-shaped exterior material 2. The wound electrode group 1 and the liquid nonaqueous electrolyte are completely sealed by heat-sealing the opening of the bag-shaped outer packaging material 2 with the negative electrode terminal 6 and the positive electrode terminal 7 interposed therebetween.

  The negative electrode terminal is made of, for example, a material having electrical stability and conductivity in a range where the potential with respect to the lithium ion metal is 0.5 V or more and 3.0 V or less. Specifically, aluminum or an aluminum alloy containing an element such as Mg, Ti, Zn, Mn, Fe, Cu, or Si can be given. In order to reduce the contact resistance with the negative electrode current collector, the negative electrode terminal is preferably made of the same material as the negative electrode current collector.

  The positive electrode terminal is made of a material having electrical stability and conductivity in a range of a potential of 3.0 to 5.0 V with respect to the lithium ion metal. Specifically, aluminum or an aluminum alloy containing an element such as Mg, Ti, Zn, Mn, Fe, Cu, or Si can be given. The positive electrode terminal is preferably made of the same material as that of the positive electrode current collector in order to reduce contact resistance with the positive electrode current collector.

  Next, the battery pack according to the embodiment will be described in detail.

  The battery pack according to the embodiment includes a plurality of the nonaqueous electrolyte batteries (unit cells) described above, and each unit cell is electrically connected in series, in parallel, or in series and in parallel.

  Such a battery pack has excellent cycle characteristics.

  Monoclinic titanium dioxide contained in the negative electrode active material has a crystallite diameter calculated from a peak where 2θ is present at 48 to 49 °, and a crystallite calculated from a peak where 2θ is present at 24 to 26 °. When the diameter is Y, X is larger than Y, and the unit cell is preferentially aligned in the vector direction of the (020) plane (direction perpendicular to the (020) plane). The used nonaqueous electrolyte battery can improve the large current characteristics. As a result, a battery pack incorporating a plurality of such batteries can improve charge / discharge cycle performance even when charging / discharging with a large current.

  Next, the battery pack according to the embodiment will be specifically described with reference to FIGS. 3 and 4. As the unit cell, a flat type nonaqueous electrolyte battery shown in FIG. 1 is used.

  The plurality of single cells 21 are stacked such that the negative electrode terminal 6 and the positive electrode terminal 7 extending to the outside are aligned in the same direction, and are fastened with an adhesive tape 22 to constitute an assembled battery 23. These unit cells 21 are electrically connected to each other in series as shown in FIG.

  The printed wiring board 24 is disposed to face the side surface of the unit cell 21 from which the negative electrode terminal 6 and the positive electrode terminal 7 extend. On the printed wiring board 24, as shown in FIG. 4, a thermistor 25, a protection circuit 26, and a terminal 27 for energizing external devices are mounted. An insulating plate (not shown) is attached to the surface of the protection circuit board 24 facing the assembled battery 23 in order to avoid unnecessary connection with the wiring of the assembled battery 23.

  The positive electrode side lead 28 is connected to the positive electrode terminal 7 positioned at the lowermost layer of the assembled battery 23, and the tip thereof is inserted into the positive electrode side connector 29 of the printed wiring board 24 and electrically connected thereto. The negative electrode side lead 30 is connected to the negative electrode terminal 6 located in the uppermost layer of the assembled battery 23, and the tip thereof is inserted into the negative electrode side connector 31 of the printed wiring board 24 and electrically connected thereto. These connectors 29 and 31 are connected to the protection circuit 26 through wirings 32 and 33 formed on the printed wiring board 24.

  The thermistor 25 is used to detect the temperature of the unit cell 21, and the detection signal is transmitted to the protection circuit 26. The protection circuit 26 can cut off the plus side wiring 34a and the minus side wiring 34b between the protection circuit 26 and the energization terminal 27 to the external device under a predetermined condition. The predetermined condition is, for example, when the temperature detected by the thermistor 25 is equal to or higher than a predetermined temperature. The predetermined condition is when the overcharge, overdischarge, overcurrent, etc. of the cell 21 are detected. This detection of overcharge or the like is performed for each single cell 21 or the entire single cell 21. When detecting each single cell 21, the battery voltage may be detected, or the positive electrode potential or the negative electrode potential may be detected. In the latter case, a lithium electrode used as a reference electrode is inserted into each unit cell 21. In the case of FIG. 3 and FIG. 4, a voltage detection wiring 35 is connected to each single cell 21, and a detection signal is transmitted to the protection circuit 26 through these wirings 35.

  Protective sheets 36 made of rubber or resin are disposed on the three side surfaces of the assembled battery 23 excluding the side surfaces from which the positive electrode terminal 7 and the negative electrode terminal 6 protrude.

  The assembled battery 23 is stored in a storage container 37 together with the protective sheets 36 and the printed wiring board 24. That is, the protective sheet 36 is disposed on each of the inner side surface in the long side direction and the inner side surface in the short side direction of the storage container 37, and the printed wiring board 24 is disposed on the inner side surface on the opposite side in the short side direction. The assembled battery 23 is located in a space surrounded by the protective sheet 36 and the printed wiring board 24. The lid 38 is attached to the upper surface of the storage container 37.

  In addition, instead of the adhesive tape 22, a heat shrink tape may be used for fixing the assembled battery 23. In this case, protective sheets are arranged on both side surfaces of the assembled battery, the heat shrinkable tape is circulated, and then the heat shrinkable tape is heat shrunk to bind the assembled battery.

  3 and 4 show the configuration in which the unit cells 21 are connected in series, but in order to increase the battery capacity, they may be connected in parallel, or a combination of series connection and parallel connection may be used. The assembled battery packs can be further connected in series and in parallel.

  Moreover, the aspect of a battery pack is changed suitably by a use. The battery pack is preferably one that exhibits excellent cycle characteristics when a large current is taken out. Specific examples include a power source for a digital camera, a vehicle for a two- to four-wheel hybrid electric vehicle, a two- to four-wheel electric vehicle, an assist bicycle, and the like. In particular, the vehicle-mounted one is suitable.

  As described above, a mixed solvent in which at least two of the group consisting of propylene carbonate (PC), ethylene carbonate (EC) and diethyl carbonate (DEC) are mixed, or a non-aqueous electrolyte containing γ-butyrolactone (GBL). By using it, a nonaqueous electrolyte battery excellent in high temperature characteristics can be obtained. A battery pack provided with an assembled battery having a plurality of such nonaqueous electrolyte batteries is particularly suitable for in-vehicle use.

  Hereinafter, examples will be described, but the present invention is not limited to the examples described below unless the gist of the present invention is exceeded.

Example 1
<Preparation of positive electrode>
First, 90% by weight of lithium nickel composite oxide (LiNi _0.82 Co _0.15 Al _0.03 O ₂ ) powder as the positive electrode active material, 5% by weight of acetylene black and 5% by weight of polyvinylidene fluoride as the conductive agent were added to N-methylpyrrolidone (NMP). In addition, the slurry is applied to both sides of a current collector made of an aluminum foil having a thickness of 15 μm, dried, and pressed to form a positive electrode layer having a positive electrode layer density of 3.15 g / cm ³ . Was made.

<Synthesis of titanium composite oxide>
First, potassium carbonate (K ₂ CO ₃ ) and anatase-type titanium oxide (TiO ₂ ) were mixed and baked at 1000 ° C. for 24 hours to synthesize K ₂ Ti ₄ O ₉ . The obtained K ₂ Ti ₄ O ₉ was dry-pulverized with zirconia beads for about 3 hours to adjust the particle size, and then washed with pure water to obtain a proton exchange precursor. The obtained proton exchange precursor was put into a 1M hydrochloric acid solution and subjected to ultrasonic dispersion for 120 hours in an environment at 25 ° C. to obtain a proton exchanger.

  The obtained proton exchanger was heated from room temperature to 350 ° C. at a heating rate of 100 ° C./hour in the atmosphere, and baked at 350 ° C. for 3 hours (first heat treatment). Subsequently, after heating up to 500 ° C. at 200 ° C./hour, baking was performed at 500 ° C. for 1 hour (second heat treatment). A titanium composite oxide was synthesized by these two-stage heat treatments.

  About the obtained titanium complex oxide, the XRD measurement was implemented on the above-mentioned conditions. As a result, the X-ray diffraction pattern shown in FIG. 5 was obtained. From this X-ray diffraction pattern, a crystallite diameter (X) calculated from a peak where 2θ is present at 48 to 49 ° and a crystallite diameter (Y) calculated from a peak where 2θ is present at 24 to 26 ° are calculated. did. The conditions for the synthesis of the titanium composite oxide are shown in Table 1 below, and the results of the crystallite diameters X, Y and X / Y are shown in Table 2 below.

<Production of negative electrode>
N-methylpyrrolidone (NMP) was added to and mixed with 80% by weight of the obtained titanium composite oxide powder, 10% by weight of acetylene black and 10% by weight of polyvinylidene fluoride as a conductive agent to prepare a slurry. This slurry was applied to both surfaces of a current collector made of an aluminum foil having a thickness of 15 μm, dried, and pressed to prepare a negative electrode having a negative electrode layer density of 1.6 g / cm ³ .

<Preparation of liquid nonaqueous electrolyte>
A liquid nonaqueous electrolyte was prepared by dissolving 1 mol / L of LiPF ₆ as an electrolyte in a mixed solvent of ethylene carbonate (EC) and diethyl carbonate (DEC) (volume ratio 1: 2).

<Production of electrode group>
After laminating a positive electrode, a separator made of a polyethylene porous film having a thickness of 25 μm, a negative electrode, and a separator in this order, they were wound in a spiral shape. This was heated and pressed at 90 ° C. to produce a flat electrode group having a width of 30 mm and a thickness of 1.8 mm. Thickness obtained by laminating and bonding the obtained electrode group with a stretched nylon film having a thickness of 25 μm, an aluminum sheet having a thickness of 40 μm, and a linear low-density polyethylene film having a thickness of 30 μm in this order via a urethane adhesive. It was stored in a pack made of a 0.1 mm laminated film and vacuum dried at 80 ° C. for 24 hours.

  After injecting the liquid non-aqueous electrolyte into the laminated film pack containing the electrode group, the pack is completely sealed by heat sealing, having the structure shown in FIG. 1, having a width of 35 mm, a thickness of 2 mm, and a height. A 65 mm nonaqueous electrolyte secondary battery was assembled.

(Examples 2 to 5)
The titanium composite oxide was synthesized under the conditions shown in Table 1 below for the pulverization time, proton exchange time, temperature / time of the first heat treatment, temperature increase rate, and temperature / time of the second heat treatment, and temperature increase rate. A nonaqueous electrolyte secondary battery was assembled in the same manner as in Example 1 except that the obtained titanium composite oxide was used as the active material for the negative electrode.

  In Examples 3 to 5, a solution in which 3% by weight of saccharose was dissolved in a pure water / ethanol mixed solution was prepared, and the substance obtained by the first heat treatment was added to this solution, and the solvent was stirred while stirring. The carbon precursor coating material was volatilized to undergo a second heat treatment.

(Comparative Examples 1-3)
The temperature rise rate during the first heat treatment is 300 ° C./hour, and the titanium composite is subjected to the pulverization time, proton exchange time, and time and temperature of the heat treatment (first heat treatment) under the conditions shown in Table 1 below. A nonaqueous electrolyte secondary battery was assembled in the same manner as in Example 1 except that the oxide was synthesized and the obtained titanium composite oxide was used as the negative electrode active material.

About each battery of Examples 1-5 and Comparative Examples 1-3, 0.2C discharge capacity and 2C discharge capacity were measured in a 25 degreeC environment, and the ratio (%) of 2C discharge capacity with respect to 0.2C discharge capacity Was determined as a capacity retention rate (%). The results are shown in Table 2 below.

(Examples 6 to 12)
The titanium composite oxide was synthesized under the conditions shown in Table 3 below for the pulverization time, proton exchange time, and the time / temperature and heating rate of the heat treatment (first heat treatment). A nonaqueous electrolyte secondary battery was assembled in the same manner as in Example 1 except that it was used as the negative electrode active material.

  In addition, the crystallite diameter in four surface orientations of the titanium composite oxide obtained in Examples 2 and 12 and Comparative Example 1 is shown in FIG.

About each battery of Examples 6-12, 0.2C discharge capacity and 2C discharge capacity were measured in the environment of 25 degreeC, and the ratio (%) of 2C discharge capacity with respect to 0.2C discharge capacity was a capacity maintenance rate (% ). The results are shown in Table 4 below. Table 4 below also shows the results of the batteries of Comparative Examples 1 to 3 described above.

  As apparent from Table 1 to Table 4, in the crystallite diameter calculated by the wide-angle X-ray diffraction method using the X-ray source CuKα ray, the crystallite diameter calculated from the peak where 2θ is present at 48 to 49 °. Is a crystallite diameter calculated from a peak at which 2θ is 24 to 26 °, and Y is a crystal of the batteries of Examples 1 to 12 using a titanium composite oxide larger than Y as a negative electrode active material. High negative electrode capacity and high capacity retention ratio (good large current performance) as compared with the batteries of Comparative Examples 1 to 3 in which the titanium composite oxides having the child diameters X and Y of X / Y ≦ 1 are used as the negative electrode active material ). In particular, it can be seen that the batteries of Examples 3 to 5, 9, 11, and 12 having a crystallite diameter (X) of 30 nm or more show a higher capacity retention rate.

  As mentioned above, although embodiment of this invention was described, this invention is not restricted to these, In the category of the summary of the invention as described in a claim, it can change variously. In addition, the present invention can be variously modified without departing from the scope of the invention in the implementation stage. Furthermore, various inventions can be formed by appropriately combining a plurality of constituent elements disclosed in the embodiment.

The present invention relates to a non-aqueous electrolyte battery active material, a non-aqueous electrolyte battery, and a battery pack.

According to a first aspect of the present invention, there is provided an active material for a non-aqueous electrolyte battery containing a monoclinic β-type titanium oxide or a monoclinic β-type titanium composite oxide, the monoclinic β-type The titanium oxide or the monoclinic β-type titanium composite oxide is calculated from the peak where 2θ is present at 48 to 49 ° in the crystallite diameter calculated by the wide-angle X-ray diffraction method using the X-ray source CuKα ray. the crystallite diameter X, when 2θ is the crystallite size calculated from peak present in 24 to 26 ° Y, the X is rather greater than the Y, and the monoclinic β-type titanium oxide Alternatively, an active material for a non-aqueous electrolyte battery in which the monoclinic β-type titanium composite oxide is coated with carbon is provided.

According to a second aspect of the present invention, an exterior material; a positive electrode housed in the exterior material; a monoclinic system according to the first aspect, housed in the exterior material and spatially separated from the positive electrode. There is provided a nonaqueous electrolyte battery comprising: a negative electrode including an active material containing a β-type titanium composite oxide; and a nonaqueous electrolyte filled in the exterior material.

According to a third aspect of the present invention, there is provided a battery pack comprising a plurality of the nonaqueous electrolyte batteries of the second aspect, wherein each battery is electrically connected in series, in parallel or in series and in parallel.

It is sectional drawing which shows the flat type nonaqueous electrolyte battery which concerns on embodiment. It is an expanded sectional view of the A section of FIG. It is a disassembled perspective view which shows the battery pack which concerns on embodiment. It is a block diagram of the battery pack of FIG. 2 is a diagram showing an X-ray diffraction pattern of a titanium composite oxide of Example 1. FIG. It is a figure which shows the crystallite diameter in four surface orientations of the titanium complex oxide of the reference examples 2 and 9 and the comparative example 1. FIG. It is a schematic diagram which shows the crystal structure of a monoclinic system type β-type titanium oxide (TiO ₂ (B)).

( Reference Example 1)
<Preparation of positive electrode>
First, 90% by weight of lithium nickel composite oxide (LiNi _0.82 Co _0.15 Al _0.03 O ₂ ) powder as the positive electrode active material, 5% by weight of acetylene black and 5% by weight of polyvinylidene fluoride as the conductive agent were added to N-methylpyrrolidone (NMP). In addition, the slurry is applied to both sides of a current collector made of an aluminum foil having a thickness of 15 μm, dried, and pressed to form a positive electrode layer having a positive electrode layer density of 3.15 g / cm ³ . Was made.

( Reference Example 2, Examples 1 to 3 )
The titanium composite oxide was synthesized under the conditions shown in Table 1 below for the pulverization time, proton exchange time, temperature / time of the first heat treatment, temperature increase rate, and temperature / time of the second heat treatment, and temperature increase rate. A nonaqueous electrolyte secondary battery was assembled in the same manner as in Reference Example 1 except that the obtained titanium composite oxide was used as the negative electrode active material.

In Examples 1 to 3 , a solution in which 3% by weight of saccharose was dissolved in a pure water / ethanol mixed solution was prepared, and the substance obtained by the first heat treatment was added to this solution, and the solvent was stirred while stirring. The carbon precursor coating material was volatilized to undergo a second heat treatment.

(Comparative Examples 1-3)
The temperature rise rate during the first heat treatment is 300 ° C./hour, and the titanium composite is subjected to the pulverization time, proton exchange time, and time and temperature of the heat treatment (first heat treatment) under the conditions shown in Table 1 below. A nonaqueous electrolyte secondary battery was assembled in the same manner as in Reference Example 1 except that the oxide was synthesized and the obtained titanium composite oxide was used as the negative electrode active material.

For the batteries of Reference Examples 1 and 2, Examples 1 to 3 and Comparative Examples 1 to 3 , the 0.2C discharge capacity and the 2C discharge capacity were measured under an environment of 25 ° C. The capacity ratio (%) was determined as the capacity maintenance ratio (%). The results are shown in Table 2 below.

( Reference Examples 3-9 )
The titanium composite oxide was synthesized under the conditions shown in Table 3 below for the pulverization time, proton exchange time, and the time / temperature and heating rate of the heat treatment (first heat treatment). A nonaqueous electrolyte secondary battery was assembled in the same manner as in Reference Example 1 except that it was used as the negative electrode active material. In Table 3 below, the synthesis conditions of the titanium composite oxides of Comparative Examples 1 to 3 described above are also shown.

In addition, the crystallite diameter in four surface orientations of the titanium composite oxide obtained in Reference Examples 2 and 9 and Comparative Example 1 is shown in FIG.

For each battery of Reference Examples 3 to 9 , the 0.2C discharge capacity and the 2C discharge capacity were measured in an environment of 25 ° C., and the ratio (%) of the 2C discharge capacity to the 0.2C discharge capacity was determined as the capacity maintenance ratio (% ). The results are shown in Table 4 below. Table 4 below also shows the results of the batteries of Comparative Examples 1 to 3 described above.

As apparent from Table 1 to Table 4, in the crystallite diameter calculated by the wide-angle X-ray diffraction method using the X-ray source CuKα ray, the crystallite diameter calculated from the peak where 2θ is present at 48 to 49 °. Where X is the crystallite diameter calculated from the peak at 2θ of 24 to 26 °, and X is Reference Examples 1 to 9 and Example 1 using a titanium composite oxide larger than Y as the negative electrode active material. The batteries of 3 to 3 have a higher negative electrode capacity and a higher capacity retention ratio than the batteries of Comparative Examples 1 to 3 using a titanium composite oxide having crystallite diameters X and Y of X / Y ≦ 1 as a negative electrode active material. It can be seen that (good large current performance) is exhibited. In particular, it can be seen that the batteries of Examples 1 to 3 and Reference Examples 6 , 8 , and 9 having a crystallite diameter (X) of 30 nm or more show a higher capacity retention rate.

Claims (4)

A method for producing an active material for a nonaqueous electrolyte battery containing monoclinic β-type titanium oxide,
A step of acid-treating an alkali titanate compound to exchange alkali cations with protons;
Washing the product after the proton exchange is completed with water and drying to obtain a proton exchanger as an intermediate product;
A non-aqueous electrolyte battery active material comprising a step of subjecting the proton exchanger to a first heat treatment at 250 to 500 ° C. and a two-step heat treatment combining a second heat treatment at 500 to 800 ° C. Manufacturing method.   The method for producing an active material for a non-aqueous electrolyte battery according to claim 1, wherein the substance after the first heat treatment is coated with a carbon precursor, and then the second heat treatment is performed.   The coating of the carbon precursor on the substance after the first heat treatment is performed by introducing the substance after the first heat treatment into a solution composed of pure water, ethanol and saccharose. Item 3. A method for producing an active material for a nonaqueous electrolyte battery according to Item 2.   The method for producing an active material for a water electrolyte battery according to claim 1, wherein the alkali titanate compound is pulverized before the acid treatment.