JP2012091943A - Aerogel - Google Patents
Aerogel Download PDFInfo
- Publication number
- JP2012091943A JP2012091943A JP2010238692A JP2010238692A JP2012091943A JP 2012091943 A JP2012091943 A JP 2012091943A JP 2010238692 A JP2010238692 A JP 2010238692A JP 2010238692 A JP2010238692 A JP 2010238692A JP 2012091943 A JP2012091943 A JP 2012091943A
- Authority
- JP
- Japan
- Prior art keywords
- airgel
- solvent
- gel
- present
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、新規なエアロゲルに関する。詳しくは、断熱性に優れ、可視光透過性にも優れた新規なエアロゲルを提供するものである。 The present invention relates to a novel aerogel. Specifically, the present invention provides a novel airgel that is excellent in heat insulation and visible light permeability.
エアロゲルは、断熱性、透明性に優れた材料であり、各種断熱用途や窓用の材料として有用に用いられる。エアロゲルの製法としては、アルコキシシランを原料として加水分解し、重縮合して得られるゲル状化合物を、分散媒の超臨界条件で乾燥する方法がある（特許文献１）。あるいは、ケイ酸アルカリ金属塩を原料とし、陽イオン交換樹脂を通過させるか、鉱酸を添加することでゾルを作成し、ゲル化させた後に、分散媒の超臨界条件で乾燥する方法がある（特許文献２）。 Airgel is a material excellent in heat insulation and transparency, and is usefully used as a material for various heat insulation applications and windows. As a method for producing an airgel, there is a method in which a gel compound obtained by hydrolysis and polycondensation using alkoxysilane as a raw material is dried under supercritical conditions of a dispersion medium (Patent Document 1). Alternatively, there is a method in which an alkali metal silicate salt is used as a raw material, passed through a cation exchange resin, or a sol is prepared by adding a mineral acid, gelled, and then dried under supercritical conditions of a dispersion medium. (Patent Document 2).
上記の超臨界条件により乾燥したエアロゲルは、超臨界状態にするためにかかるコストが多大であり、用途は特殊なものに限定される。そのため、コスト低減を目的とした常圧乾燥法が提案されている（特許文献３）。 The airgel dried under the above supercritical conditions has a large cost for making it in a supercritical state, and its use is limited to special ones. Therefore, a normal pressure drying method for the purpose of cost reduction has been proposed (Patent Document 3).
エアロゲルの用途は、様々であるが、樹脂や硝子板の間に、大きさが数ミリ程度のエアロゲルの粒体を挟んで使用する採光断熱材の用途がある。その採光断熱材の用途においては、優れた断熱性と透明性が要求される。また、住宅等の一般建築物に用いる場合には、コスト面からの要求により、常圧乾燥法により製造されたエアロゲルを用いることが好ましい。特許文献３に記載された方法により製造されたエアロゲルは、断熱性は優れているものの透明性においては未だ改善の余地があった。 There are various uses of airgel, but there is a use of a daylighting heat insulating material in which airgel particles having a size of several millimeters are sandwiched between a resin and a glass plate. In the use of the daylighting heat insulating material, excellent heat insulating properties and transparency are required. Moreover, when using for general buildings, such as a house, it is preferable to use the airgel manufactured by the normal pressure drying method by the request | requirement from a cost viewpoint. Although the airgel manufactured by the method described in Patent Document 3 has excellent heat insulation properties, there is still room for improvement in transparency.
従って本発明の目的は、優れた断熱性と透明性を有するエアロゲルを提供することにある。 Accordingly, an object of the present invention is to provide an airgel having excellent heat insulation and transparency.
本発明者らは、上記の課題を解決するために鋭意検討を重ねた結果、常圧乾燥法によるエアロゲルの製法において、ゲルを熟成する際の条件が、その物性に極めて大きな影響を与えることを見出した。そしてさらに検討を進めた結果、上記課題を解決するエアロゲルを得られることを見出し、本発明を完成させるに至った。 As a result of intensive studies to solve the above problems, the present inventors have found that the conditions for aging the gel in the airgel production method by the atmospheric pressure drying method have a great influence on the physical properties. I found it. As a result of further studies, it was found that an airgel that solves the above problems can be obtained, and the present invention has been completed.
即ち、本発明は、ＢＥＴ法による比表面積が４００〜７００ｍ２／ｇ、ＢＪＨ法による細孔容積及び細孔直径のピークが各々４〜８ｍｌ／ｇ、１０〜３０ｎｍ、ふるい分け法による粒径が０．５〜４ｍｍの範囲内にあり、かつＤ６５光源での全光線透過率（ＪＩＳ−Ｋ７３６１−１）が６０％以上であることを特徴とする疎水性エアロゲルである。 That is, according to the present invention, the specific surface area by the BET method is 400 to 700 m 2 / g, the pore volume and pore diameter peaks by the BJH method are 4 to 8 ml / g, 10 to 30 nm, and the particle size by the sieving method is 0. It is a hydrophobic airgel characterized by having a total light transmittance (JIS-K7361-1) of 60% or more with a D65 light source in a range of 0.5 to 4 mm.
本発明は、断熱性に優れ、かつ可視光域の光透過率にも優れたエアロゲルである。そのため、採光用断熱材として、極めて有用に用いることが可能である。 The present invention is an airgel having excellent heat insulation properties and excellent light transmittance in the visible light region. Therefore, it can be used very effectively as a heat insulating material for daylighting.
本発明のエアロゲルは、ＢＥＴ法による比表面積が４００〜７００ｍ２／ｇ、好ましくは４００〜６００ｍ２／ｇである。比表面積が大きいほど、エアロゲルを構成するシリカの一次粒子径が小さいことを示し、より少ない量でエアロゲルの骨格構造を形成することが可能であるため、断熱性を向上させる上で好ましい。比表面積がこの範囲より小さい場合には、十分な断熱性能を得ることはできない。また、この範囲を超えて大きいものを得ることは、困難である。 Airgel of the present invention has a specific surface area of 400~700m 2 / g, according to BET method is preferably 400-600m 2 / g. A larger specific surface area indicates that the primary particle diameter of silica constituting the airgel is smaller, and it is possible to form a skeleton structure of the airgel with a smaller amount, which is preferable in improving the heat insulation. When the specific surface area is smaller than this range, sufficient heat insulating performance cannot be obtained. Also, it is difficult to obtain a large size exceeding this range.
なお当該ＢＥＴ法によるエアロゲルの比表面積は、測定対象のサンプルを、１ｋＰａ以下の真空下において、２００℃の温度で３時間以上乾燥させ、その後、液体窒素温度における窒素の吸着側のみの吸着等温線を取得し、ＢＥＴ法により解析して求めた値である。 Incidentally, the specific surface area of the airgel by the BET method is such that the sample to be measured is dried at 200 ° C. for 3 hours or more under a vacuum of 1 kPa or less, and then the adsorption isotherm only on the nitrogen adsorption side at the liquid nitrogen temperature. This is a value obtained by obtaining and analyzing by the BET method.
本発明のエアロゲルは、ＢＪＨ法による細孔容積が４〜８ｍｌ／ｇ、好ましくは４〜６ｍｌ／ｇである。細孔容積が４ｍｌ／ｇ以下である場合には、十分な断熱性能を得ることはできない。またこの範囲を超えて大きなものを得ることは、困難である。 The airgel of the present invention has a pore volume by the BJH method of 4 to 8 ml / g, preferably 4 to 6 ml / g. When the pore volume is 4 ml / g or less, sufficient heat insulating performance cannot be obtained. Moreover, it is difficult to obtain a large product beyond this range.
当該ＢＪＨ法によるエアロゲルの細孔容積は、前記の比表面積測定の際と同様に吸着等温線を取得し、ＢＪＨ法により解析して得られたものである。 The pore volume of the airgel by the BJH method is obtained by obtaining an adsorption isotherm in the same manner as in the specific surface area measurement and analyzing by the BJH method.
本発明のエアロゲルの細孔直径のピークは、同じくＢＪＨ法による解析で１０〜３０ｎｍ、好ましくは１５〜２５ｎｍの範囲にある。気体分子の平均自由工程は、０℃、１００ｋＰａにおいて１００ｎｍ程度であるが、本発明のエアロゲルの細孔直径はこの大きさよりも小さいため、効果的に気体分子同士の衝突による伝熱を抑制することができる。細孔直径がこの範囲を超えて小さい場合には、エアロゲルの密度が大きくなり、断熱性能が悪くなる。また、細孔直径がこの範囲を超えて大きい場合には、可視光透過性が悪くなる。 The peak of the pore diameter of the airgel of the present invention is also in the range of 10 to 30 nm, preferably 15 to 25 nm, similarly analyzed by the BJH method. The mean free path of gas molecules is about 100 nm at 0 ° C. and 100 kPa, but the airgel of the present invention has a pore diameter smaller than this size, and therefore effectively suppresses heat transfer due to collision between gas molecules. Can do. When the pore diameter is smaller than this range, the density of the airgel increases and the heat insulation performance deteriorates. Further, when the pore diameter is larger than this range, the visible light transmittance is deteriorated.
当該ＢＪＨ法によるエアロゲルの細孔直径は、細孔容積と同様に吸着等温線をＢＪＨ法により解析して得られたものである。 The pore diameter of the airgel by the BJH method is obtained by analyzing the adsorption isotherm by the BJH method in the same manner as the pore volume.
本発明のエアロゲルは、粒状であり、ふるい分け法により測定される粒径が４ｍｍを超える粒子を含まない。粒径が大きな粒子が含まれると、例えば断熱窓に用いるに際して樹脂や硝子板の間に挟むことが困難になるため、本発明においては、４ｍｍを超える粒子を含まないようにするものである。さらに粒径の大きな粒子が存在すると該粒子に起因して断熱性が低下する傾向にあり、その点からも実質的に十分な断熱性を得るために４ｍｍを超える粒子を含まないようにするべきである。 The airgel of the present invention is granular and does not contain particles having a particle size measured by a sieving method exceeding 4 mm. When particles having a large particle diameter are included, for example, when used for a heat insulating window, it is difficult to sandwich them between a resin and a glass plate. Therefore, in the present invention, particles exceeding 4 mm are not included. Furthermore, if there is a particle having a larger particle size, the heat insulating property tends to be reduced due to the particle, and from this point, in order to obtain a substantially sufficient heat insulating property, particles larger than 4 mm should not be included. It is.
一方、粒径が小さな粒子は光透過率を低下させる傾向にある。従って、本発明のエアロゲルとしては、０．５ｍｍ未満の粒子が５重量％以下である必要があり、１重量％以下であることが好ましく、実質的に存在しないことが特に好ましい。ここで実質的に存在しないとは、目開き０．５ｍｍの篩上にエアロゲルをのせ、２，３度軽く振った程度では、篩を通過する粒子が存在しないことをいう。 On the other hand, particles having a small particle size tend to decrease the light transmittance. Therefore, the airgel of the present invention needs to have 5% by weight or less of particles of less than 0.5 mm, preferably 1% by weight or less, and particularly preferably substantially absent. Here, “substantially not present” means that there is no particle passing through the sieve when the airgel is placed on a sieve having an aperture of 0.5 mm and shaken a few times.
上記のような本発明のエアロゲル粒子は、その形状を特に限定されるものではなく、球状でも破砕状でも良い。 The airgel particles of the present invention as described above are not particularly limited in shape, and may be spherical or crushed.
本発明のエアロゲルは、Ｄ６５光源を用いた際の全光線透過率（以下、単に「光透過率」と記す）が６０％以上である。当該透過率の測定方法は、より具体的にはＪＩＳ−Ｋ７３６１−１に示されており、該方法により測定した値が６０％以上であればよい。即ち、光源Ｄ６５に対する全光線透過率であり、光路長１ｃｍのセルにエアロゲルを充填し、サンプルの透過光を、積分球を用いて測定した値が６０％以上であればよい。採光窓用途を考慮すると該透過率は６５％以上であることが好ましく、７０％以上であることがより好ましく、７５％以上であることが好ましい。 The airgel of the present invention has a total light transmittance (hereinafter simply referred to as “light transmittance”) of 60% or more when a D65 light source is used. More specifically, the method for measuring the transmittance is shown in JIS-K7361-1, and the value measured by the method may be 60% or more. That is, it is the total light transmittance with respect to the light source D65, the value which measured the transmitted light of a sample using the integrating sphere for the cell of 1 cm of optical path length filled with airgel should be 60% or more. Considering the daylighting window application, the transmittance is preferably 65% or more, more preferably 70% or more, and preferably 75% or more.
一方、上限は特に限定されるものではないが、粒状エアロゲルにおいて、上記測定方法で光透過率が１００％のものを得ることは困難であり、通常は９０％以下、多くの場合８５％以下であるが、断熱採光窓用途としてはこの程度あれば十分である。 On the other hand, the upper limit is not particularly limited, but in granular airgel, it is difficult to obtain a light transmittance of 100% by the above-described measurement method, usually 90% or less, often 85% or less. However, this level is sufficient for heat insulating daylighting windows.
また本発明において、疎水性であるとは、有機溶媒を含まない水に対して分散しないことをいう。親水性である場合、その表面積の大きさなどに由来して急速に大気中の水分等を吸着し、断熱性、透明性に著しい悪影響を与えるため、取扱いが困難である。 In the present invention, the term “hydrophobic” means not dispersed in water not containing an organic solvent. When it is hydrophilic, it is difficult to handle because it rapidly adsorbs moisture and the like in the atmosphere due to the size of its surface area, and has a significant adverse effect on heat insulation and transparency.
上述の物性を有する本発明の疎水性エアロゲルの製法は、特に限定されないが、本発明者等の検討によれば、以下の方法により製造することができる。 Although the manufacturing method of the hydrophobic airgel of this invention which has the above-mentioned physical property is not specifically limited, According to examination of the present inventors, it can manufacture with the following method.
即ち、本発明の疎水性エアロゲルは、シリカゾルの作成、シリカゾルのゲル化、熟成、ゲルの粉砕、溶媒置換、疎水化処理、乾燥という工程を順番に行う常圧乾燥法により製造することができる。 That is, the hydrophobic airgel of the present invention can be produced by a normal pressure drying method in which the steps of preparation of silica sol, gelation of silica sol, aging, gel pulverization, solvent replacement, hydrophobic treatment, and drying are sequentially performed.
上記各工程のうち、シリカゾルの作成工程は、公知の方法を適宜選択して実施すればよい。該シリカゾル作成の原料としては、金属アルコキシド、ケイ酸アルカリ金属塩等を使用することができる。本発明の疎水性エアロゲルの原料として使用可能な金属アルコキシドを具体的に例示すると、テトラメトキシシラン、テトラエトキシシラン等が挙げられる。また、ケイ酸アルカリ金属塩としては、ケイ酸カリウム、ケイ酸ナトリウム等が挙げられ、化学式は、以下の式１で示される。
ｍ（Ｍ２Ｏ）・ｎ（ＳｉＯ２） （式１）
（式中のｍ、ｎは正の整数を表し、Ｍはアルカリ金属原子を示す。）
上記のシリカゾル作成の原料のなかでも、安価な点でケイ酸アルカリ金属塩を好適に用いることができ、更には入手が容易であるケイ酸ナトリウムが好適である。
Among the above steps, the silica sol preparation step may be performed by appropriately selecting a known method. As raw materials for producing the silica sol, metal alkoxides, alkali metal silicates and the like can be used. Specific examples of the metal alkoxide that can be used as a raw material for the hydrophobic airgel of the present invention include tetramethoxysilane and tetraethoxysilane. Examples of the alkali metal silicate include potassium silicate and sodium silicate. The chemical formula is represented by the following formula 1.
m (M 2 O) · n (SiO 2 ) (Formula 1)
(In the formula, m and n represent a positive integer, and M represents an alkali metal atom.)
Among the raw materials for producing the silica sol, an alkali metal silicate can be preferably used from the viewpoint of inexpensiveness, and sodium silicate which is easily available is preferable.
本発明のシリカゾル作成原料として、ケイ酸アルカリ金属塩を用いる場合には、塩酸、硫酸等の鉱酸により中和する方法か、あるいは対イオンがＨ＋とされている陽イオン交換樹脂（以下、「酸型陽イオン交換樹脂」）を用いる方法により、シリカゾルを作成することができる。これらの方法のうちでも、酸型陽イオン交換樹脂を用いた方が、透明性の良いものが得られ易い点で好ましい。 When using an alkali metal silicate as a silica sol preparation raw material of the present invention, a method of neutralizing with a mineral acid such as hydrochloric acid or sulfuric acid, or a cation exchange resin (hereinafter referred to as H +) A silica sol can be prepared by a method using an “acid-type cation exchange resin”). Among these methods, it is preferable to use an acid-type cation exchange resin because a transparent material can be easily obtained.
本発明のエアロゲルの製造において、酸型陽イオン交換樹脂を用いてシリカゾルを作成する方法は、公知の方法により行うことができ、酸型陽イオン交換樹脂を充填した充填層に適切な濃度のケイ酸アルカリ金属塩の溶液を通過させるか、あるいは、ケイ酸アルカリ金属塩の溶液に、酸型陽イオン交換樹脂を添加、混合し、アルカリ金属を除去した後に濾別するなどして酸イオン交換樹脂を分離することにより行うことができる。その際に、用いる酸型陽イオン交換樹脂の量は、溶液に含まれるアルカリ金属を交換可能な量以上を用いる必要がある。 In the production of the airgel of the present invention, a method for producing a silica sol using an acid type cation exchange resin can be performed by a known method, and a silica having an appropriate concentration in a packed bed filled with the acid type cation exchange resin. Acid-ion exchange resin by passing acid-alkali metal salt solution or adding acid-type cation exchange resin to alkali metal silicate solution, mixing, removing alkali metal, and filtering. Can be carried out by separating. At that time, the amount of the acid-type cation exchange resin to be used must be equal to or greater than the amount capable of exchanging alkali metals contained in the solution.
上記の酸型陽イオン交換樹脂としては、市販のものを使用することができる。例えば、スチレン系、アクリル系、メタクリル系等で、イオン交換性基としてスルフォン酸基やカルボキシル基が置換されたものを用いることができる。このうち、スルフォン酸基を有する、いわゆる強酸型の陽イオン交換樹脂を好適に用いることができる。 A commercially available acid-type cation exchange resin can be used. For example, styrene-based, acrylic-based, methacryl-based, or the like in which a sulfonic acid group or a carboxyl group is substituted as an ion-exchange group can be used. Among these, a so-called strong acid type cation exchange resin having a sulfonic acid group can be suitably used.
なお上記の酸型陽イオン交換樹脂は、アルカリ金属の交換に使用した後に、硫酸や塩酸を通過させることで、再生処理を行うことができる。再生に用いる酸の量は、通常は、イオン交換樹脂の交換容量に対して２〜１０倍の量が用いられる。 In addition, after using said acid type cation exchange resin for replacement | exchange of an alkali metal, a reproduction | regeneration process can be performed by letting sulfuric acid and hydrochloric acid pass. The amount of acid used for regeneration is usually 2 to 10 times the exchange capacity of the ion exchange resin.
上記のケイ酸アルカリ金属塩の溶液の濃度としては、シリカ分の濃度として、５〜１０ｇ／Ｌ程度のものを用いることが好ましい。シリカ分の濃度がこの範囲を超えて小さい場合には、ゲル化に時間がかかり、またエアロゲルの骨格構造の形成が不十分となり易く、乾燥時に収縮を起こして細孔容量が小さくなる傾向にある。また、シリカ分の濃度がこの範囲を超えて大きい場合には、エアロゲルの密度が大きくなり、シリカ自体による熱伝導が起こりやすくなるため、断熱性能が悪くなる傾向にある。 The concentration of the alkali metal silicate solution is preferably about 5 to 10 g / L as the silica concentration. When the concentration of the silica component is smaller than this range, gelation takes time, and the formation of the airgel skeleton structure tends to be insufficient, and the pore volume tends to decrease due to shrinkage during drying. . Moreover, when the density | concentration of a silica part exceeds this range, since the density of an airgel becomes large and the heat conduction by silica itself will occur easily, it exists in the tendency for heat insulation performance to worsen.
本発明のエアロゲルを製造するためには、上記の如くして作成されたシリカゾルの作成に引き続き、シリカゾルをゲル化させ、次いでその熟成を行う。本発明の疎水性エアロゲルを得るためには、このゲル化（及び熟成工程）における厳密なｐＨ管理が重要である。即ち、通常、上記の酸イオン交換樹脂によりイオン交換されたシリカゾルのｐＨは３以下である。このようなシリカゾルを中和して弱酸性〜中性とすることによりシリカゾルがゲル化するが、本発明で規定する光透過率を有する疎水性エアロゲルを得るためには、シリカゾルのｐＨを５．０〜５．８、好ましくは５．３〜５．７とすることによってゲル化させる必要がある（但し、２５℃での値である）。 In order to produce the airgel of the present invention, the silica sol is gelled and then aged after the production of the silica sol prepared as described above. In order to obtain the hydrophobic airgel of the present invention, strict pH control in this gelation (and aging step) is important. That is, usually, the pH of the silica sol ion-exchanged with the acid ion exchange resin is 3 or less. By neutralizing such a silica sol to make it weakly acidic to neutral, the silica sol is gelled. To obtain a hydrophobic airgel having the light transmittance defined in the present invention, the pH of the silica sol is set to 5. It is necessary to make it gel by setting it to 0 to 5.8, preferably 5.3 to 5.7 (however, it is a value at 25 ° C.).
本発明者等の推定によれば、ゲル化後の熟成時のｐＨが特定の範囲であることにより、極めて高い光透過率を有するエアロゲルを得ることができ、ゲル化時点でのｐＨの影響は軽微なのではないかと推測しているが、一旦ゲル化したもののｐＨを調整（変更）することは多大な困難を伴うため、ｐＨ調整の容易なゲル化直前の段階で上記ｐＨに調整するものである。なおシリカゾルのｐＨは、市販のガラス電極を有するｐＨメーターを用て行えばよい。市販のｐＨメーターには温度補正機能を有するものもあり、このようなｐＨメーターを用いれば、前記範囲のｐＨに調製することがより容易である。 According to the estimation by the present inventors, an aerogel having an extremely high light transmittance can be obtained when the pH at the time of aging after gelation is in a specific range, and the influence of pH at the time of gelation is Although it is speculated that it is slight, it is very difficult to adjust (change) the pH of the gel once it is gelled, so it is adjusted to the pH just before gelation where pH adjustment is easy. is there. In addition, what is necessary is just to perform pH of silica sol using the pH meter which has a commercially available glass electrode. Some commercially available pH meters have a temperature correction function. If such a pH meter is used, it is easier to adjust the pH to the above range.
シリカゾルのｐＨをこの範囲に調整するには、シリカゾルに塩基を添加すればよい。当該塩基としては、アンモニア水、水酸化ナトリウム、水酸化カリウム、ケイ酸アルカリ金属塩等を用いることができる。最終的に得られる疎水性エアロゲルに不純物が混入しにくい点でアンモニアを用いることが好ましい。なお上記のゲル化にかかる時間は、温度やシリカゾルの濃度にもよるが、例えば、ｐＨを５．０に調整した場合、温度５０℃、シリカゾル中のシリカ濃度が８０ｇ／Ｌの場合には、数分後にはゲル化が起こる。 In order to adjust the pH of the silica sol within this range, a base may be added to the silica sol. As the base, aqueous ammonia, sodium hydroxide, potassium hydroxide, alkali metal silicate, and the like can be used. Ammonia is preferably used because impurities are hardly mixed into the finally obtained hydrophobic airgel. The time required for the gelation depends on the temperature and the concentration of the silica sol. For example, when the pH is adjusted to 5.0, when the temperature is 50 ° C. and the silica concentration in the silica sol is 80 g / L, Gelation occurs after a few minutes.
このようにしてゲル化された直後のゲルはその透明性（光透過率）があまり高くないが、熟成が進むにつれて透明性が増大する。しかしながら、熟成が進行しすぎると再度、透明性が低下していくため、適切な熟成時間とする必要がある。 The gel immediately after gelation in this way is not so high in transparency (light transmittance), but the transparency increases as aging progresses. However, since the transparency is lowered again when the aging progresses too much, it is necessary to set an appropriate aging time.
本発明の疎水性エアロゲルを製造するに際して、所望の光透過率を得るための熟成時間に影響を与える因子としては、ｐＨ及び温度が挙げられる。ｐＨは高いほど熟成が早く進行し、温度は高温ほど熟成が早くなる。従って、後述する実施例、比較例の開示に従い、適切な温度及び時間を設定することは当業者には容易であろう。具体的に一例を挙げると、ゲル化時のｐＨを５．５、熟成温度５０℃とした場合には、４〜２０時間が好適であり、更には８〜１６時間が好適である。 In producing the hydrophobic airgel of the present invention, pH and temperature are factors that influence the aging time for obtaining a desired light transmittance. The higher the pH, the faster the ripening, and the higher the temperature, the faster the aging. Therefore, it will be easy for those skilled in the art to set an appropriate temperature and time according to the disclosure of Examples and Comparative Examples described later. As a specific example, when the pH during gelation is 5.5 and the aging temperature is 50 ° C., 4 to 20 hours is preferable, and 8 to 16 hours is more preferable.
なお、熟成温度の範囲としては、３０〜８０℃が好適である。熟成温度がこの範囲を外れて高い場合には、温度を上昇させるために必要な熱量が多大となり、また熟成反応の進行が早いため、光透過率の高い時点で熟成を中止することが困難となりやすい。一方、熟成温度がこの範囲を超えて低い場合には、透明性を得るために必要な熟成時間が長くなるため、工業的に好ましくない。特に好ましくは４０〜６０℃である。 In addition, as a range of aging temperature, 30-80 degreeC is suitable. If the ripening temperature is high outside this range, the amount of heat required to raise the temperature becomes large, and the ripening reaction proceeds quickly, making it difficult to stop ripening at a point where the light transmittance is high. Cheap. On the other hand, when the aging temperature is lower than this range, the aging time necessary for obtaining transparency is prolonged, which is not industrially preferable. Especially preferably, it is 40-60 degreeC.
本発明の疎水性エアロゲルを高収率で得るためには、上記の熟成工程に引き続き、ゲルを粉砕することが好ましい。このゲルの粉砕により、粒径をできるだけ０．５〜４ｍｍに近づけておくことが、最後に行われるエアロゲルの分級の収率を向上させる上で好ましい。それに対し、次に述べる溶媒置換及び疎水化処理の後に粉砕を行うと、粉砕により疎水化処理されていない破断面が新たに生じることになり好ましくない。 In order to obtain the hydrophobic airgel of the present invention in a high yield, it is preferable to pulverize the gel following the aging step. By pulverizing the gel, it is preferable to keep the particle size as close to 0.5 to 4 mm as possible in order to improve the yield of the last airgel classification. On the other hand, if the pulverization is performed after the solvent substitution and the hydrophobization treatment described below, a fracture surface that has not been hydrophobized by the pulverization is newly generated, which is not preferable.
上記のゲルの粉砕は、例えばヘンシャル型のミキサーにゲルを入れるか、あるいはミキサー内でゲル化させ、ミキサーを適度な回転数と時間で運転することにより行うことができる。 The above-mentioned gel pulverization can be performed, for example, by putting the gel in a Hench type mixer or by making the gel in the mixer and operating the mixer at an appropriate rotation speed and time.
本発明の疎水性エアロゲルを製造するには、上記の粉砕工程に引き続き、溶媒置換が行われる。この溶媒置換は上記方法で得たゲルを乾燥するに際し、乾燥収縮を起こさないよう、ゲルの作成に用いた水を、表面張力の小さな溶媒に置き換えるものである。直接水を表面張力の小さな溶媒に置き換えることは困難なため、通常はこの溶媒置換は、２段階で行なわれる。１段目に用いる溶媒の選定基準としては、水、及び２段目の溶媒置換に用いられる溶媒に対して馴染みが良いことが挙げられる。１段目は、メタノール、エタノール、イソプロピルアルコール、アセトン等を用いることができ、好適には、エタノールを用いることができる。また２段目に用いる溶媒の選定基準としては、引き続き行われる疎水化処理に用いられる処理剤と反応しないこと、乾燥収縮を起こさないために表面張力が小さいことが挙げられる。２段目に用いる溶媒としては、ヘキサン、ジクロロメタン、メチルエチルケトン等を用いることができ、好適にはヘキサンを用いることができる。むろん必要に応じて、上記１段目の溶媒置換と２段目の溶媒置換との間に、更なる溶媒置換を行っても構わない。 In order to produce the hydrophobic airgel of the present invention, solvent replacement is carried out following the above pulverization step. This solvent replacement replaces the water used for preparing the gel with a solvent having a small surface tension so that drying shrinkage does not occur when the gel obtained by the above method is dried. Since it is difficult to directly replace water with a solvent having a low surface tension, this solvent replacement is usually performed in two steps. The selection criteria for the solvent used in the first stage may be familiarity with water and the solvent used for the second stage solvent replacement. In the first stage, methanol, ethanol, isopropyl alcohol, acetone or the like can be used, and ethanol can be preferably used. The selection criteria for the solvent used in the second stage include that it does not react with the treating agent used in the subsequent hydrophobization treatment and that the surface tension is small so as not to cause drying shrinkage. As the solvent used in the second stage, hexane, dichloromethane, methyl ethyl ketone or the like can be used, and hexane can be preferably used. Of course, if necessary, further solvent substitution may be performed between the first-stage solvent substitution and the second-stage solvent substitution.
上記の１段目の溶媒置換は、公知の方法により行うことができる。例えば、ゲルに対して一定量溶媒を加え一定時間置いた後に溶媒を抜くことを繰り返す方法や、カラムに入れたゲルに対して溶媒を一定量通過させる方法等が挙げられる。置換に用いる溶媒を節約する上では、カラムを用いた方法が好ましい。また、カラムにより置換を行う場合には、効率を上げる目的で、０．２〜１．０ＭＰａ程度の加圧下で行うことができる。 The first-stage solvent replacement can be performed by a known method. For example, a method of repeatedly adding a certain amount of solvent to the gel and leaving it for a certain time and then removing the solvent, a method of allowing a certain amount of solvent to pass through the gel placed in the column, and the like can be mentioned. In order to save the solvent used for substitution, a method using a column is preferred. Moreover, when replacing by a column, it can carry out under the pressurization of about 0.2-1.0 Mpa for the purpose of raising efficiency.
上記の１段目の溶媒置換に用いられる溶媒の量としては、ゲル中の水分を十分に置換できる量とすることが好ましい。置換後のゲル中の含水率としては、シリカ分に対して１０％以下とすることが好ましい。上記のカラムによる方法を採用する場合には、ゲルの容量に対して５〜１０倍の量の溶媒を用いることができる。 The amount of the solvent used for the first-stage solvent replacement is preferably an amount that can sufficiently replace the water in the gel. The water content in the gel after substitution is preferably 10% or less with respect to the silica content. When employing the above-described column method, the solvent can be used in an amount 5 to 10 times the volume of the gel.
上記の２段目の溶媒置換についても、１段目の溶媒置換と同様の方法で行うことができ、１段目に用いた溶媒を十分置換できる量で行うことができる。カラムによる方法を採用する場合には、ゲルの容量に対して５〜１０倍量の溶媒を用いることができる。 The second-stage solvent replacement can be performed in the same manner as the first-stage solvent replacement, and can be performed in an amount that can sufficiently replace the solvent used in the first stage. When the column method is employed, 5 to 10 times as much solvent as the gel volume can be used.
なお上記の置換のために用いた溶媒は、回収し、蒸留等の精製を行った後に、繰り返し使用することが、溶媒にかかる費用を節約する上で好ましい。 The solvent used for the above substitution is preferably recovered and used repeatedly after purification such as distillation in order to save the cost for the solvent.
本発明の疎水性エアロゲルを製造するには、上記の溶媒置換の後に、疎水化処理を行う。疎水化処理に用いる処理剤としては、一般式（２）ＲｎＳｉＸ４−ｎ（Ｒは、炭化水素基、Ｘは、アルコキシ基又はハロゲン原子、ｎは１〜２の整数）で示される構造のものを用いる。好ましくは、Ｘが塩素原子であるジアルキルジクロロシラン、モノアルキルトリクロロシランである。より透明性の良いエアロゲルを得るためには、上記一般式（２）で示されるもののうち、Ｒとしてはメチル基のものを採用することが好ましい。原料コストや反応性を考慮するとジメチルジクロロシランを最も好適に用いることができる。 In order to produce the hydrophobic airgel of the present invention, a hydrophobic treatment is performed after the solvent substitution. As the treating agent used for the hydrophobizing treatment, a structure represented by the general formula (2) R n SiX 4-n (R is a hydrocarbon group, X is an alkoxy group or a halogen atom, and n is an integer of 1 to 2). Use one. Preferred are dialkyldichlorosilane and monoalkyltrichlorosilane in which X is a chlorine atom. In order to obtain an airgel with better transparency, among those represented by the general formula (2), it is preferable to employ a methyl group as R. Considering raw material cost and reactivity, dimethyldichlorosilane can be most preferably used.
上記の疎水化処理の際に使用する処理剤の量としては、処理剤の種類にもよるが、例えばジメチルジクロロシランを処理剤として用いる場合には、疎水化前のエアロゲル（シリカ成分）１００重量部に対して５０〜１５０重量部が好適である。 The amount of the treatment agent used in the above hydrophobic treatment depends on the kind of the treatment agent. For example, when dimethyldichlorosilane is used as the treatment agent, 100 wt. The amount is preferably 50 to 150 parts by weight with respect to parts.
上記の疎水化処理の条件は、前記置換処理後のゲルを含む液に対して、一定量の溶媒を追加した後に疎水化処理剤を加え、一定時間反応させることにより行うことができる。疎水化処理剤としてジメチルジクロロシランを用い、処理温度を５０℃とした場合には、１２時間程度以上保持することで行うことできる。この際の追加溶媒としては、前記溶媒置換の際の２段目の溶媒としての要求物性を満たすものであればよい。また該溶媒の追加量としては、ゲルの容量に対して０．５〜２倍程度の量とすることができる。 The conditions for the above-described hydrophobizing treatment can be performed by adding a certain amount of solvent to the liquid containing the gel after the substitution treatment, adding a hydrophobizing agent, and reacting for a predetermined time. When dimethyldichlorosilane is used as the hydrophobizing agent and the treatment temperature is 50 ° C., the treatment can be performed by holding for about 12 hours or more. In this case, any additional solvent may be used as long as it satisfies the required physical properties as the second-stage solvent in the solvent replacement. The additional amount of the solvent can be about 0.5 to 2 times the gel volume.
本発明の疎水性エアロゲルを製造するには、上記の疎水化処理の後に、濾別し、未反応の処理剤を溶媒で洗浄した後に、乾燥する。この際の洗浄溶媒としても、前記溶媒置換の際の２段目の溶媒としての要求物性を満たすものであればよい。洗浄が十分に行われたか否かは、例えば、洗浄後に分離した溶媒中の疎水化剤の有無を分析するなどして把握できる。乾燥する際の温度は、溶媒の沸点以上で、表面処理剤の分解温度以下であることが好ましく、圧力は常圧、或いは減圧下で行うことが好ましい。 In order to produce the hydrophobic airgel of the present invention, after the hydrophobization treatment, it is filtered off, the unreacted treating agent is washed with a solvent, and then dried. Any washing solvent may be used as long as it satisfies the physical properties required as the second-stage solvent in the solvent replacement. Whether or not the washing has been sufficiently performed can be grasped by, for example, analyzing the presence or absence of the hydrophobizing agent in the solvent separated after the washing. The drying temperature is preferably not less than the boiling point of the solvent and not more than the decomposition temperature of the surface treatment agent, and the pressure is preferably normal or reduced.
このようにして製造された疎水性エアロゲルを最終的に本発明のエアロゲルとするためには、上記の乾燥工程の後に、例えば、篩を用いた分級操作により、粒径を０．５〜４ｍｍに調整すればよい。 In order to finally make the hydrophobic airgel produced in this way into the aerogel of the present invention, the particle size is reduced to 0.5 to 4 mm by, for example, classification operation using a sieve after the drying step. Adjust it.
以下、本発明を具体的に説明するため、実施例を示すが、本発明はこれらの実施例のみに制限されるものではない。また、実施例、比較例において、比表面積、細孔容積、細孔分布の測定は、日本ベル株式会社製、ＢＥＬＳＯＲＰ−ｍａｘにより行い、熱伝導率の測定は、英弘精機株式会社製ＨＣ−０７４−２００により行った。また、透過率の測定は、日本電色株式会社製、ＮＤＨ−２０００により測定を行った。またｐＨの測定はメトラートレッド社製、セブンイージーＳ２０により行った。 EXAMPLES Hereinafter, examples will be shown to specifically describe the present invention, but the present invention is not limited to only these examples. In Examples and Comparative Examples, specific surface area, pore volume, and pore distribution are measured by BELSORP-max, manufactured by Nippon Bell Co., Ltd., and thermal conductivity is measured by HC-074 manufactured by Eihiro Seiki Co., Ltd. -200. The transmittance was measured with NDH-2000 manufactured by Nippon Denshoku Co., Ltd. The pH was measured by Seven Easy S20 manufactured by Metrator Red.
実施例１
３号ケイ酸ソーダの溶液を希釈し、ＳｉＯ２：８０ｇ／Ｌ、Ｎａ２Ｏ：２７ｇ／Ｌの濃度に調整した。この希釈したケイ酸ソーダの溶液を、予め硫酸によりＨ＋型にしたイオン交換樹脂（ローム・アンド・ハース社製、アンバーリスト、ＩＲ−１２０Ｂ）に通過させ、２Ｌのシリカゾルを取得した。このシリカゾルのｐＨは、２．８であった。
Example 1
The solution of No. 3 sodium silicate was diluted and adjusted to a concentration of SiO 2 : 80 g / L and Na 2 O: 27 g / L. The diluted sodium silicate solution was passed through an ion exchange resin (Rum & Haas, Amberlyst, IR-120B) previously made into H + type with sulfuric acid to obtain 2 L of silica sol. The pH of this silica sol was 2.8.
攪拌しながら０．１％のアンモニア水を滴下することにより、シリカゾルのｐＨを５．５に調整した。シリカゾルは、数分後には、ゲル化した。ゲルを入れた容器を５０℃の水浴に入れ、１２時間保持することにより熟成を行った。その後、ゲルを適度に砕きながら４ｍｍの篩いを通過させた。全ての粒子が４ｍｍの篩を通過するまでこの操作を行った。 The pH of the silica sol was adjusted to 5.5 by adding 0.1% ammonia water dropwise with stirring. The silica sol gelled after a few minutes. The container containing the gel was placed in a 50 ° C. water bath and aged for 12 hours. Thereafter, the gel was passed through a 4 mm sieve while being appropriately crushed. This operation was performed until all particles passed through a 4 mm sieve.
粉砕したゲルをカラムに入れ、１０Ｌのエタノールで溶媒置換した後に、１０Ｌのヘキサンにより溶媒置換を行った。ゲルにヘキサンを追加することで、全体の容量を３Ｌとし、ジメチルジクロロシラン２４０ｇを添加した。その後、５０℃において、２４時間保持した。 The crushed gel was placed in a column, and the solvent was replaced with 10 L of ethanol, followed by solvent replacement with 10 L of hexane. By adding hexane to the gel, the total volume was 3 L, and 240 g of dimethyldichlorosilane was added. Then, it hold | maintained at 50 degreeC for 24 hours.
疎水化処理後のゲルを、吸引濾過により濾別し、ヘキサン５００ｍｌで洗浄した。ゲルの乾燥を常圧下、窒素を流通させながら行った。乾燥の温度、時間は、４０℃で３時間、５０℃で２時間、１５０℃で１２時間とした。その後、粒径が０．５〜４ｍｍの粒子を篩い分けし、取得した。製造条件を表1に示す。また、このようにして得られたエアロゲルの物性を表２に示す。 The hydrophobized gel was separated by suction filtration and washed with 500 ml of hexane. The gel was dried under normal pressure while flowing nitrogen. The drying temperature and time were 40 ° C. for 3 hours, 50 ° C. for 2 hours, and 150 ° C. for 12 hours. Thereafter, particles having a particle diameter of 0.5 to 4 mm were sieved and obtained. The manufacturing conditions are shown in Table 1. Table 2 shows the physical properties of the airgel thus obtained.
実施例２〜３，比較例１〜４
ゲル化させるためのアンモニア水添加完了時のｐＨ、及び熟成時間を表1に示すように変更した以外は、実施例１と同様にして疎水性エアロゲルを製造した。得られたエアロゲルの物性を表２に示す。
Examples 2-3 and Comparative Examples 1-4
A hydrophobic airgel was produced in the same manner as in Example 1 except that the pH at the completion of addition of aqueous ammonia for gelation and the aging time were changed as shown in Table 1. Table 2 shows the physical properties of the obtained airgel.
比較例５
疎水化処理の処理剤をトリメチルクロロシランとした以外は、実施例１と同様にエアロゲルの製造を行った。得られたエアロゲルの物性を表２に示す。
Comparative Example 5
An airgel was produced in the same manner as in Example 1 except that trimethylchlorosilane was used as the hydrophobizing agent. Table 2 shows the physical properties of the obtained airgel.
比較例６
実施例１において、最終工程における篩分けの際に、０．５ｍｍの篩を通過したものの各種物性の分析結果を表２に示す。
Comparative Example 6
Table 2 shows the analysis results of various physical properties of the sample that passed through the 0.5 mm sieve in the final process in Example 1.
Claims (2)