JP2006215272A - Lithographic printing original plate - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a lithographic printing original plate wherein direct drawing with laser light is provided, and high sensitivity, high printing durability and storage stability are also compatibly provided. <P>SOLUTION: The lithographic printing original plate is obtained by sequentially stacking a photosensitive layer containing (a) a sensitizer, (b) a photopolymerization initiator, (c) a compound having an ethylenically unsaturated double bond, and (d) a polymeric binder having a crosslinkable group in a side chain, and a protective layer on a hydrophilic support, wherein the mass ratio ((c)/(d)) between the compound (c) and the polymeric binder (d) contained in the photosensitive layer is 0.2-1.15. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

  The present invention relates to a negative lithographic printing plate precursor that can be directly drawn with a laser beam, and more particularly to a lithographic printing plate precursor that achieves both high sensitivity, high printing durability and storage stability.

  In general, a negative lithographic printing plate precursor is developed by coating a photosensitive composition on a roughened aluminum plate or the like, exposing a desired image, and polymerizing or crosslinking the exposed portion of the photosensitive layer. Image formation is carried out by a process of insolubilizing in the solution and eluting unexposed portions of the photosensitive layer with the developer. Conventionally, as a photosensitive composition used for such a purpose, a photopolymerizable composition is well known, and a part thereof is put into practical use. In addition, recent high-sensitivity photopolymers incorporating a photoinitiating technology that is highly sensitive to visible light have been increased in sensitivity to an area used for direct plate-making with a visible laser, and are widely used as so-called CTP plates.

However, in terms of workability, there is a growing demand for handling (lighting room) under a yellow light or a white light instead of a dark room, and accordingly, an ultraviolet-violet laser with a wavelength of 300 nm to 450 nm and 800 to 1200 nm. A highly sensitive photosensitive composition that can be used in combination with an exposure method such as an infrared laser is studied (for example, see Patent Documents 1 and 2).
JP 2000-147663 A JP 2001-133969 A

In order to pursue higher productivity in the plate-making process, it is necessary to improve the drawing speed. Therefore, higher sensitivity of the plate material has been demanded. High sensitivity makes it easy to obtain high printing durability. However, when the sensitivity is increased, the storage stability tends to deteriorate, and it is necessary to achieve both high sensitivity and storage stability for practical use.
The present invention overcomes this problem and aims to provide a lithographic printing plate precursor that can be directly drawn by a laser beam, has high sensitivity and high printing durability, and is excellent in storage stability.

  As a result of intensive studies, the present inventor has solved the above problem by increasing the mass ratio of the polymer binder having a crosslinkable group in the side chain to the compound having an ethylenically unsaturated double bond. That is, the present invention is as follows.

  1. (A) a sensitizer, (b) a photopolymerization initiator, (c) a compound having an ethylenically unsaturated double bond, and (d) a polymer having a crosslinkable group on the side chain on a hydrophilic support. A lithographic printing plate precursor comprising a photosensitive layer containing a binder and a protective layer sequentially laminated, wherein (c) a compound having an ethylenically unsaturated double bond and (d) a side chain contained in the photosensitive layer A lithographic printing plate precursor having a mass ratio ((c) / (d)) to a polymer binder having a crosslinkable group of 0.2 to 1.15.

  2. 2. The lithographic printing plate precursor as described in 1 above, wherein the polymer binder having a crosslinkable group in the side chain is a polyurethane resin having a crosslinkable group in the side chain.

  3. 3. The lithographic printing plate precursor as described in 1 or 2 above, wherein the polymer binder having a crosslinkable group in the side chain is contained in a range of 80,000 to 150,000.

  4). 4. The lithographic printing plate precursor as described in any one of 1 to 3 above, wherein the photosensitive layer contains a thiol compound represented by the following general formula (I).

  In general formula (I), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and A represents a 5-membered ring having a carbon atom together with an N = CN moiety. Alternatively, it represents an atomic group forming a 6-membered heterocycle. A may further have a substituent.

  5. The thiol compound represented by the general formula (I) is at least one selected from the group consisting of compounds represented by the following general formula (II) and general formula (III): The lithographic printing plate precursor described in 1.

  In general formulas (II) and (III), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and X represents a halogen atom, an alkoxyl group or a substituent. Represents an alkyl group which may be substituted, or an aryl group which may have a substituent.

  6). 6. The photopolymerization initiator is at least one selected from the group consisting of hexaarylbiimidazole compounds, onium salts, trihalomethyl compounds, and metallocene compounds, A lithographic printing plate precursor.

  According to the present invention, it is possible to provide a lithographic printing plate precursor capable of direct drawing with a laser beam, having high sensitivity and high printing durability, and having excellent storage stability.

[(C) Compound having ethylenically unsaturated double bond]
A compound having an ethylenically unsaturated double bond (hereinafter also referred to as an ethylenically unsaturated compound) is an addition polymerized, crosslinked, and cured by the action of a photopolymerization initiator when the photosensitive layer is irradiated with actinic rays. It is a compound which has such an ethylenically unsaturated bond. The compound containing an ethylenically unsaturated bond capable of addition polymerization can be arbitrarily selected from compounds having at least one, preferably two or more terminal ethylenically unsaturated bonds. For example, those having chemical forms such as monomers, prepolymers, that is, dimers, trimers and oligomers, or mixtures thereof.

Examples of monomers include esters of unsaturated carboxylic acids (eg, acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, maleic acid, etc.) and aliphatic polyhydric alcohol compounds, unsaturated carboxylic acids and aliphatic Examples include amides with polyvalent amine compounds.
Specific examples of the monomer of an ester of an aliphatic polyhydric alcohol compound and an unsaturated carboxylic acid include acrylic acid esters such as ethylene glycol diacrylate, triethylene glycol diacrylate, 1,3-butanediol diacrylate, and tetramethylene glycol. Diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, trimethylolpropane tri (acryloyloxypropyl) ether, trimethylolethane triacrylate, hexanediol diacrylate, 1,4-cyclohexanediol Diacrylate, tetraethylene glycol diacrylate, pentaerythritol diacrylate, pentaerythritol triacrelane , Pentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate, sorbitol triacrylate, sorbitol tetraacrylate, sorbitol pentaacrylate, sorbitol hexaacrylate, tri (acryloyloxyethyl) isocyanurate, polyester Examples include acrylate oligomers.

  Methacrylic acid esters include tetramethylene glycol dimethacrylate, triethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, ethylene glycol dimethacrylate, 1,3-butanediol dimethacrylate, Hexanediol dimethacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, dipentaerythritol dimethacrylate, dipentaerythritol hexamethacrylate, dipentaerythritol pentamethacrylate, sorbitol trimethacrylate, sorbitol tetramethacrylate, bis [ - (3-methacryloxy-2-hydroxypropoxy) phenyl] dimethyl methane, bis - [p-(methacryloxyethoxy) phenyl] dimethyl methane.

  Itaconic acid esters include ethylene glycol diitaconate, propylene glycol diitaconate, 1,5-butanediol diitaconate, 1,4-butanediol diitaconate, tetramethylene glycol diitaconate, pentaerythritol diitaconate And sorbitol tetritaconate. Examples of crotonic acid esters include ethylene glycol dicrotonate, tetramethylene glycol dicrotonate, pentaerythritol dicrotonate, and sorbitol tetradicrotonate. Examples of isocrotonic acid esters include ethylene glycol diisocrotonate, pentaerythritol diisocrotonate, and sorbitol tetraisocrotonate.

  Examples of maleic acid esters include ethylene glycol dimaleate, triethylene glycol dimaleate, pentaerythritol dimaleate, and sorbitol tetramaleate. Furthermore, the mixture of the above-mentioned ester monomer can also be mentioned. Specific examples of amide monomers of aliphatic polyvalent amine compounds and unsaturated carboxylic acids include methylene bis-acrylamide, methylene bis-methacrylamide, 1,6-hexamethylene bis-acrylamide, 1,6-hexamethylene bis. -Methacrylamide, diethylenetriamine trisacrylamide, xylylenebisacrylamide, xylylenebismethacrylamide and the like.

  As another example, the polyisocyanate compound having two or more isocyanate groups in one molecule described in JP-B-48-41708 contains a hydroxyl group represented by the following general formula (A). Examples thereof include a vinyl urethane compound containing two or more polymerizable vinyl groups in one molecule to which a vinyl monomer is added.

_{CH 2 = C (R) COOCH} 2 CH (R ') (A)
(However, R and R ′ represent H or CH _3. )

  Further, urethane acrylates as described in JP-A-51-37193 and JP-B-2-32293, JP-A-48-64183, JP-B-49-43191, JP-B-52-30490 Polyfunctional acrylates and methacrylates such as polyester acrylates and epoxy acrylates obtained by reacting an epoxy resin with (meth) acrylic acid, as described in each publication. Furthermore, Journal of Japan Adhesion Association Vo 1.20, No. 7, pages 300 to 308 (1984) as photocurable monomers and oligomers can also be used. In addition, the usage-amount of these ethylenically unsaturated bond containing compounds is 5-80 mass% normally with respect to the total mass of a photosensitive layer, Preferably it is used in 30-70 mass%.

[(D) polymer binder having a crosslinkable group in the side chain]
In the photosensitive layer of the present invention, a polymer binder having a crosslinkable group in the side chain is used.
Here, the crosslinkable group is a group that crosslinks the polymer binder in the process of radical polymerization reaction that occurs in the photosensitive layer when the lithographic printing plate precursor is exposed. Although it will not specifically limit if it is a group of such a function, For example, an ethylenically unsaturated bond group, an amino group, an epoxy group etc. are mentioned as a functional group which can be addition-polymerized. Moreover, the functional group which can become a radical by light irradiation may be sufficient, and as such a crosslinkable group, a thiol group, a halogen group, an onium salt structure etc. are mentioned, for example. Especially, an ethylenically unsaturated bond group is preferable and the functional group represented by the following general formula (1)-(3) is especially preferable.

In the general formula (1), R ^{1 to} R ³ each independently represents a monovalent organic group, and R ¹ is preferably a hydrogen atom or an alkyl group which may have a substituent. Among them, a hydrogen atom and a methyl group are preferable because of high radical reactivity. R ² and R ³ are each independently a hydrogen atom, a halogen atom, an amino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an optionally substituted alkyl group, or a substituted group. An aryl group that may have a group, an alkoxy group that may have a substituent, an aryloxy group that may have a substituent, an alkylamino group that may have a substituent, and a substituent An arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, an arylsulfonyl group which may have a substituent, and the like. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, a substituent An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.

X represents an oxygen atom, a sulfur atom, or N (R ¹² ) —, and R ¹² represents a hydrogen atom or a monovalent organic group. Here, examples of R ¹² include an alkyl group which may have a substituent. Among them, a hydrogen atom, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.

  Here, examples of the substituent that can be introduced include an alkyl group, an alkenyl group, an alkynyl group, an aryl group, an alkoxy group, an aryloxy group, a halogen atom, an amino group, an alkylamino group, an arylamino group, a carboxyl group, an alkoxycarbonyl group, A sulfo group, a nitro group, a cyano group, an amide group, an alkylsulfonyl group, an arylsulfonyl group and the like can be mentioned.

In the general formula (2), R ^{4 to} R ⁸ each independently represents a monovalent organic group, and R ^{4 to} R ⁸ are preferably a hydrogen atom, a halogen atom, an amino group, a dialkylamino group, Carboxyl group, alkoxycarbonyl group, sulfo group, nitro group, cyano group, alkyl group which may have a substituent, aryl group which may have a substituent, alkoxy group which may have a substituent, substituted An aryloxy group which may have a group, an alkylamino group which may have a substituent, an arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, a substituent Examples thereof include an arylsulfonyl group which may have a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, an alkyl group which may have a substituent, and an aryl group which may have a substituent. .

Examples of the substituent that can be introduced are the same as those in the general formula (1). Y represents an oxygen atom, a sulfur atom, or N (R ¹² ) —. R ¹² has the same meaning as R ¹² in general formula (1), and preferred examples are also the same.

In the general formula (3), R ⁹ preferably includes a hydrogen atom or an alkyl group which may have a substituent. Among them, a hydrogen atom or a methyl group has high radical reactivity. preferable. R ¹⁰ and R ¹¹ are each independently a hydrogen atom, a halogen atom, an amino group, a dialkylamino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, or an alkyl group which may have a substituent. An aryl group which may have a substituent, an alkoxy group which may have a substituent, an aryloxy group which may have a substituent, an alkylamino group which may have a substituent, a substituent An arylamino group that may have, an alkylsulfonyl group that may have a substituent, an arylsulfonyl group that may have a substituent, and the like, among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.

Here, examples of the substituent that can be introduced are the same as those in the general formula (1). Further, Z is an oxygen atom, a sulfur atom, -N (R ¹³⁾ -, or a phenylene group which may have a substituent. Examples of R ¹³ include an alkyl group which may have a substituent. Among them, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.

The polymer binder having the crosslinkable group in the side chain of the present invention not only functions as a film-forming agent for the photosensitive layer but also needs to be dissolved in a developer, preferably an alkali developer, so that it is soluble in alkaline water. Or it is preferable that it is a swelling organic polymer. Therefore, the polymer binder of the present invention preferably has an alkali-soluble group such as a carboxyl group in the side chain in addition to the crosslinkable group.
When the polymer binder having a crosslinkable group in the side chain is a water-soluble organic polymer, water development is possible.

Examples of the polymer binder of the present invention include those described in JP-A-59-53836 and JP-A-59-71048, such as allyl groups and (meth) acryloyl groups in the side chain. Examples include (meth) acrylic acid copolymers, itaconic acid copolymers, crotonic acid copolymers, maleic acid copolymers, partially esterified maleic acid copolymers having a crosslinkable group.
In addition, as the polymer binder of the present invention, there are also those obtained by adding a cyclic acid anhydride to an addition polymer having a crosslinkable group and a carboxyl group in the side chain, a polyurethane, an acidic cellulose derivative, and a hydroxyl group. Useful.
Among the above, (meth) acrylic acid copolymer and polyurethane are more preferable. In particular, the polyurethane resin can suppress the development damage of the exposed area without lowering the developability of the unexposed area even if the acid value of the photosensitive layer is low, and has both good stain resistance and high printing durability. It is preferable in that
The polyurethane resin having a crosslinkable group in the side chain will be described in more detail below.

The polyurethane resin having a crosslinkable group in the side chain particularly preferably used in the present invention includes (i) a diisocyanate compound, (ii) a diol compound having a carboxyl group, (iii) a diisocyanate compound having a crosslinkable group, and if necessary. (Iv) It can be obtained by subjecting a diol compound having no carboxyl group to a polyaddition reaction.
The diisocyanate compound and diol compound, which are raw materials for the polyurethane resin, will be described below.

(I) Diisocyanate Compound Examples of the diisocyanate compound include a diisocyanate compound represented by the formula (4).

          OCN-L-NCO (4)

  In the formula, L represents a divalent aliphatic or aromatic hydrocarbon group which may have a substituent. If necessary, L may have other functional groups that do not react with isocyanate groups, such as carbonyl, ester, urethane, amide, and ureido groups. More specifically, L is a divalent aliphatic or aromatic hydrocarbon group which may have a single bond or a substituent (for example, alkyl, aralkyl, aryl, alkoxy and halogeno groups are preferred). Indicates. Preferably an alkylene group having 1 to 20 carbon atoms, an arylene group having 6 to 15 carbon atoms, and more preferably an alkylene group having 1 to 8 carbon atoms is shown. If necessary, L may have another functional group that does not react with an isocyanate group, for example, carbonyl, ester, urethane, amide, ureido, or ether group.

  Specific examples include the following. That is, 2,4-tolylene diisocyanate, dimer of 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, p-xylylene diisocyanate, m-xylylene diisocyanate, 4,4′-diphenylmethane diisocyanate Aromatic diisocyanate compounds such as 1,5-naphthylene diisocyanate, 3,3′-dimethylbiphenyl-4,4′-diisocyanate; hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, lysine diisocyanate, dimer acid diisocyanate, etc. Aliphatic diisocyanate compounds; isophorone diisocyanate, 4,4′-methylenebis (cyclohexyl isocyanate), methylcyclohexane-2,4 (or 2,6) diisocyanate Nitrate, cycloaliphatic diisocyanate compounds such as 1,3- (isocyanatomethyl) cyclohexane, etc .; reaction product of diol and diisocyanate such as adduct of 1 mol of 1,3-butylene glycol and 2 mol of tolylene diisocyanate The diisocyanate compound etc. which are are mentioned.

  A diisocyanate compound may be used independently and may be used in combination of 2 or more type. It is preferable to use a combination of two or more in terms of the balance between printing durability and stain resistance, and at least one aromatic diisocyanate compound (L is an aromatic group) and aliphatic diisocyanate compound (L is an aliphatic group). It is particularly preferred to use each species.

  The amount of diisocyanate used is preferably 0.8 to 1.2, more preferably 0.9 to 1.1 in terms of molar ratio to the diol compound. If the diisocyanate compound is used in excess relative to the diol compound, and the isocyanate group remains at the polymer end, the isocyanate group finally remains by treating with an alcohol or amine after completion of the urethanization reaction. It is preferable that they are synthesized in a form that does not.

(Ii) Diol compound having at least one carboxyl group As the diol compound having at least one carboxyl group, a diol compound of formula (5), (6), (7) and / or tetracarboxylic dianhydride is used. Examples thereof include compounds opened with a diol compound. The diol compound used to ring-open the carboxylic dianhydride can be used.

R ₁ represents a hydrogen atom, a substituent (for example, cyano, nitro, halogen atom (—F, —Cl, —Br, —I), —CONH ₂ , —COOR ₁₁₃ , —OR ₁₁₃ , —NHCONHR ₁₁₃ , —NHCOOR _113). , -NHCOR ₁₁₃ , -OCONHR ₁₁₃ (wherein R ₁₁₃ represents an alkyl group having 1 to 10 carbon atoms and an aralkyl group having 7 to 15 carbon atoms). And may be an alkyl, aralkyl, aryl, alkoxy, or aryloxy group, preferably a hydrogen atom, an alkyl having 1 to 8 carbon atoms, or an aryl group having 6 to 15 carbon atoms. L ₁₀ , L ₁₁ and L ₁₂ may be the same or different, and may have a single bond or a substituent (for example, alkyl, aralkyl, aryl, alkoxy and halogeno groups are preferred). A divalent aliphatic or aromatic hydrocarbon group is shown. Preferably an alkylene group having 1 to 20 carbon atoms, an arylene group having 6 to 15 carbon atoms, and more preferably an alkylene group having 1 to 8 carbon atoms is shown. If necessary, L ₁₀ , L ₁₁ , and L ₁₂ may have other functional groups that do not react with isocyanate groups, such as carbonyl, ester, urethane, amide, ureido, and ether groups. A ring may be formed by 2 or 3 of R ₁ , L ₁₀ , L ₁₁ and L ₁₂ . Ar represents a trivalent aromatic hydrocarbon group which may have a substituent, preferably an aromatic group having 6 to 15 carbon atoms.

  Specific examples of the diol compound having a carboxyl group represented by the formula (5), (6) or (7) include those shown below.

  3,5-dihydroxybenzoic acid, 2,2-bis (hydroxymethyl) propionic acid, 2,2-bis (2-hydroxyethyl) propionic acid, 2,2-bis (3-hydroxypropyl) propionic acid, Bis (hydroxymethyl) acetic acid, bis (4-hydroxyphenyl) acetic acid, 2,2-bis (hydroxymethyl) butyric acid, 4,4-bis (4-hydroxyphenyl) pentanoic acid, tartaric acid, N, N-dihydroxyethylglycine N, N-bis (2-hydroxyethyl) -3-carboxy-propionamide and the like.

  Moreover, as a preferable tetracarboxylic dianhydride used in the production | generation of the at least 1 sort (s) of diol compound which has an at least 1 carboxyl group, what is shown by Formula (8), (9), (10) is mentioned.

In the formula, L ₂₁ is a divalent aliphatic or aromatic hydrocarbon which may have a single bond or a substituent (for example, alkyl, aralkyl, aryl, alkoxy, halogeno, ester, amide groups are preferred). A group, —CO—, —SO—, —SO ₂ —, —O— or —S—; Preferably, it represents a single bond, a divalent aliphatic hydrocarbon group having 1 to 15 carbon atoms, —CO—, —SO ₂ —, —O— or —S—. R ₂ and R ₃ may be the same or different and each represents a hydrogen atom, alkyl, aralkyl, aryl, alkoxy, or halogeno group. Preferably, a hydrogen atom, a C1-C8 alkyl, a C6-C15 aryl, a C1-C8 alkoxy, or a halogeno group is shown. _{Two of} L ₂₁ , R ₂ and R ₃ may be bonded to form a ring. R ₄ and R ₅ may be the same or different and each represents a hydrogen atom, alkyl, aralkyl, aryl or halogeno group. Preferably a hydrogen atom, a C1-C8 alkyl, or a C6-C15 aryl group is shown. Two of L ₂₁ , R ₄ and R ₅ may be bonded to form a ring. L ₂₂ and L ₂₃ may be the same or different and each represents a single bond, a double bond, or a divalent aliphatic hydrocarbon group. Preferably a single bond, a double bond, or a methylene group is shown. A represents a mononuclear or polynuclear aromatic ring. An aromatic ring having 6 to 18 carbon atoms is preferable.

Specific examples of the compound represented by the formula (8), (9) or (10) include those shown below.

That is, pyromellitic dianhydride, 3,3 ′, 4,4′-benzophenone tetracarboxylic dianhydride, 3,3 ′, 4,4′-diphenyltetracarboxylic dianhydride, 2,
3,6,7-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 4,4′-sulfonyldiphthalic dianhydride, 2,2-bis (3
, 4-Dicarboxyphenyl) propane dianhydride, bis (3,4-dicarboxyphenyl) ether dianhydride, 4,4 ′-[3,3 ′-(alkylphosphoryldiphenylene)
-Bis (iminocarbonyl)] diphthalic dianhydride, an aromatic tetracarboxylic dianhydride such as an adduct of hydroquinone diacetate and trimet anhydride, an adduct of diacetyldiamine and trimet anhydride; 5- (2 , 5-Dioxotetrahydrofuryl) -3-methyl-3-cyclohexene-1,2-dicarboxylic acid anhydride (Dainippon Ink & Chemicals, Epiklone B-4400), 1,2,3,4 Cycloaliphatic tetracarboxylic dianhydrides such as cyclopentanetetracarboxylic dianhydride, 1,2,4,5-cyclohexanetetracarboxylic dianhydride, tetrahydrofuran tetracarboxylic dianhydride; Aliphatic tetracarboxylic acids such as 4-butanetetracarboxylic dianhydride and 1,2,4,5-pentanetetracarboxylic dianhydride Thing, and the like.

  By ring-opening these tetracarboxylic dianhydrides with a diol compound, (ii) at least one diol compound having at least one carboxyl group can be synthesized. However, it is also possible to synthesize the polyurethane resin of the present invention by first reacting the diol compound with (i) the diisocyanate compound and reacting this reactant with the tetracarboxylic dianhydride. Methods are also encompassed by aspects of the present invention. That is, as a method for introducing a structural unit derived from tetracarboxylic dianhydride and a diol compound into a polyurethane resin, there are the following methods.

a) A method of reacting an alcohol-terminated compound obtained by ring-opening tetracarboxylic dianhydride with a diol compound and a diisocyanate compound.
b) A method of reacting an alcohol-terminated urethane compound obtained by reacting a diisocyanate compound under an excess of a diol compound with tetracarboxylic dianhydride.

  Of the at least one diol compound having at least one carboxyl group, the compound represented by the general formula (5) is more preferable because of high solvent solubility and easy synthesis. Further, at least one diol compound having at least one carboxyl group, the polyurethane resin binder has a carboxyl group of 0.2 to 4.0 meq / g, preferably 0.3 to 3.0 meq / g, more preferably Introduced into the polyurethane resin binder in such an amount as having a range of 0.4 to 2.0 meq / g, particularly preferably 0.5 to 1.5 meq / g, most preferably 0.6 to 1.2 meq / g. . Accordingly, the content in the polyurethane resin binder having a structure derived from at least one diol compound having at least one carboxyl group is the number of carboxyl groups, what is used as the other diol component, and the acid of the polyurethane resin binder obtained. Although it is appropriately selected depending on the value, molecular weight, developer composition, pH, etc., for example, it is 5 to 45 mol%, preferably 10 to 40 mol%, more preferably 15 to 35 mol%.

(Iii) Diisocyanate compound having a crosslinkable group As the diisocyanate compound having a crosslinkable group, for example, a triisocyanate compound and 1 equivalent of a monofunctional alcohol or monofunctional amine compound having a crosslinkable group are subjected to an addition reaction. There is a product obtained.
Examples of the triisocyanate compound include those shown below, but are not limited thereto.

  Examples of the monofunctional alcohol or monofunctional amine compound having a crosslinkable group include those shown below, but are not limited thereto.

  Here, as a method for introducing a crosslinkable group into the side chain of the polyurethane resin, a method using a diisocyanate compound containing a crosslinkable group in the side chain as a raw material for producing the polyurethane resin is suitable. Examples of the diisocyanate compound that can be obtained by addition reaction of a triisocyanate compound and one equivalent of a monofunctional alcohol having a crosslinkable group or a monofunctional amine compound having a crosslinkable group in the side chain include, for example, Although the following are mentioned, it is not limited to this.

(Iv) Other diol compound As a method for introducing an unsaturated group into the side chain of the polyurethane resin, in addition to the above-described method, a diol compound containing an unsaturated group in the side chain is used as a raw material for polyurethane resin production. A method is also suitable. Such a diol compound may be a commercially available one such as trimethylolpropane monoallyl ether, a halogenated diol compound, a triol compound, an aminodiol compound, a carboxylic acid containing an unsaturated group, and an acid. It may be a compound that is easily produced by a reaction with a chloride, isocyanate, alcohol, amine, thiol, or alkyl halide compound. Specific examples of these compounds include, but are not limited to, the compounds shown below.

  Still other diol compounds include ethylene glycol compounds represented by the following general formula (A ′).

HO— (CH ₂ CH ₂ O) _n —H (A ′)
(In the formula, n represents an integer of 1 or more.)

  Moreover, the random copolymer and block copolymer of ethylene oxide and propylene oxide which have a hydroxyl group at the terminal are also mentioned.

  Furthermore, ethylene oxide adducts of bisphenol A (addition number of ethylene oxide 27 to 100), ethylene oxide adducts of bisphenol F (ethylene oxide addition number of 22 to 100), ethylene oxide adducts of hydrogenated bisphenol A (addition of ethylene oxide) The ethylene oxide adduct of hydrogenated bisphenol F (the number of addition of ethylene oxide is 18 or more and 100 or less) can also be used. More specifically, the ethylene glycol compound represented by the general formula (A ′) is preferable in terms of soiling property, n is more preferably an ethylene glycol compound having 2 to 50, and n is an ethylene glycol compound having 3 to 30. More preferably, an ethylene glycol compound having n of 4 to 10 is particularly preferable.

  Specifically, 1,2-propylene glycol, di-1,2-propylene glycol, tri-1,2-propylene glycol, tetra-1,2-propylene glycol, hexa-1,2-propylene glycol, 1, 3-propylene glycol, di-1,3-propylene glycol, tri-1,3-propylene glycol, tetra-1,3-propylene glycol, 1,3-butylene glycol, di-1,3-butylene glycol, tri- 1,3-butylene glycol, hexa-1,3-butylene glycol, polypropylene glycol having an average molecular weight of 400, polypropylene glycol having an average molecular weight of 700, polypropylene glycol having an average molecular weight of 1000, polypropylene glycol having an average molecular weight of 2000, and polypropylene having an average molecular weight of 3000 Glycol, average molecular weight 4000 polypropylene glycol, neopentyl glycol, 2-butene-1,4-diol, 2,2,4-trimethyl-1,3-pentanediol, 1,4-bis-β-hydroxyethoxycyclohexane 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, cyclohexanedimethanol, tricyclodecane dimethanol, hydrogenated bisphenol A , Hydrogenated bisphenol F, ethylene oxide adduct of bisphenol A (ethylene oxide addition number of 26 or less), ethylene oxide adduct of bisphenol F (ethylene oxide addition number of 21 or less), hydrogenated bisphenol A ethylene oxide adduct (ethyleneoxy ), Hydrogenated bisphenol F ethylene oxide adduct (ethylene oxide addition number 17 or less), bisphenol A propylene oxide adduct, bisphenol F propylene oxide adduct, hydrogenated bisphenol A propylene oxide Adduct, propylene oxide adduct of hydrogenated bisphenol F, hydroquinone dihydroxyethyl ether, p-xylylene glycol, dihydroxyethyl sulfone, bis (2-hydroxyethyl) -2,4-tolylene dicarbamate, 2,4-tolylene- Examples thereof include bis (2-hydroxyethylcarbamide), bis (2-hydroxyethyl) -m-xylylene dicarbamate, and bis (2-hydroxyethyl) isophthalate.

  Moreover, the polyether diol compound of the compound represented by a following formula (A), (B), (C), (D) or (E) can also be used conveniently.

In the formula, R ₆ represents a hydrogen atom or a methyl group. However, in formula (A), R ₆ represents a methyl group. X represents the following group.

  a, b, c, d, e, f, and g each represent an integer of 2 or more. Preferably it is an integer of 2-100.

  Furthermore, the polyester diol compound represented by Formula (11) or (12) can also be mentioned as a specific example.

In the formula, L ₁ , L ₂ and L ₃ may be the same or different and each represents a divalent aliphatic or aromatic hydrocarbon group, and L ₄ represents a divalent aliphatic hydrocarbon group. Preferably, L ₁ , L ₂ and L ₃ each represents an alkylene group, an alkenylene group, an alkynylene group or an arylene group, and L ₄ represents an alkylene group. In addition, L ₁ , L ₂ , L ₃ , and L ₄ contain other functional groups that do not react with isocyanate groups, such as ether, carbonyl, ester, cyano, olefin, urethane, amide, ureido group, or halogen atoms. May be. n1 and n2 are each an integer of 2 or more, preferably an integer of 2 to 100.

  Furthermore, the polycarbonate diol compound represented by Formula (13) can also be mentioned as a specific example.

In the formula, L ₅ may be the same or different and each represents a divalent aliphatic or aromatic hydrocarbon group. Preferably, L ₅ represents an alkylene group, an alkenylene group, an alkynylene group or an arylene group. In addition, other functional groups that do not react with the isocyanate group, such as ether, carbonyl, ester, cyano, olefin, urethane, amide, ureido group or halogen atom may be present in L ₅ . n3 is an integer greater than or equal to 2, respectively, Preferably the integer of 2-100 is shown.

  Specific examples of the diol compound represented by the formula (11), (12) or (13) include those shown below. N in the specific examples is an integer of 2 or more.

Furthermore, a diol compound that does not have a carboxyl group and may have another substituent that does not react with isocyanate can also be used.

Examples of such diol compounds include those shown below.
_{HO-L 6 -O-CO-} L 7 -CO-O-L 6 -OH (14)
_{HO-L 7 -CO-O-} L 6 -OH (15)

In the formula, L ₆ and L ₇ may be the same as or different from each other, and a substituent (eg, alkyl, aralkyl, aryl, alkoxy, aryloxy, halogen atom (—F, —Cl, —Br, —I), A divalent aliphatic hydrocarbon group, an aromatic hydrocarbon group or a heterocyclic group which may have a group. If necessary, L ₆ and L ₇ may have another functional group that does not react with an isocyanate group, for example, carbonyl, ester, urethane, amide, ureido group and the like. Note that L ₆ and L ₇ may form a ring.

  Specific examples of the compound represented by the formula (14) or (15) include those shown below.

  Moreover, the diol compound shown below can also be used conveniently.

In the formula, R ₇ and R ₈ may be the same or different, and may be an alkyl group which may have a substituent, preferably cyano, nitro, halogen atom (—F, —Cl, —Br, —I _{), - CONH 2, -COOR,} -OR, ( wherein, R represents may be identical or different from each other, alkyl groups having 1 to 10 carbon atoms, ant 7-15 carbon atoms - group, aralkyl group An alkyl group having 1 to 10 carbon atoms which may have each group as a substituent.

  Specific examples of the diol compound represented by the formula (16) include those shown below.

Examples of the formula (17) include 2-butyne-1,4-diol, and examples of the formula (18) include cis-2-butene-1,4-diol and trans-2-butene-1,4-diol. It is done.
Moreover, the diol compound shown to following formula (19), (20) can also be used conveniently.
_{HO-L 8 -NH-CO-} L 9 -CO-NH-L 8 -OH (19)
_{HO-L 9 -CO-NH-} L 8 -OH (20)

In the formula, L ₈ and L ₉ may be the same as or different from each other, and a substituent (eg, alkyl, aralkyl, aryl, alkoxy, aryloxy, halogen atom (—F, —Cl, —Br, —I), A divalent aliphatic hydrocarbon group, an aromatic hydrocarbon group or a heterocyclic group which may have a group. If necessary, L ₈ and L ₉ may have other functional groups that do not react with isocyanate groups, such as carbonyl, ester, urethane, amide, ureido groups and the like. Note that L ₈ and L ₉ may form a ring.

  Specific examples of the compound represented by the formula (19) or (20) include those shown below.

Furthermore, diol compounds represented by the following formulas (21) and (22) can also be suitably used.
_{HO-Ar 2 - (L 16} -Ar 3) n -OH (21)
_{HO-Ar 2 -L 16 -OH (} 22)

In the formula, L ₁₆ represents a divalent aliphatic hydrocarbon group which may have a substituent (eg, alkyl, aralkyl, aryl, alkoxy, aryloxy and halogeno groups are preferable). If necessary, L ₁₆ may have another functional group that does not react with an isocyanate group, such as an ester, urethane, amide, or ureido group.

Ar ₂ and Ar ₃ may be the same or different and each represents a divalent aromatic hydrocarbon group which may have a substituent, preferably an aromatic group having 6 to 15 carbon atoms. n represents an integer of 0 to 10.
Specific examples of the diol compound represented by the formula (21) or (22) include those shown below.

That is, catechol, resorcin, hydroquinone, 4-methylcatechol, 4-t-butylcatechol, 4-acetylcatechol, 3-methoxycatechol, 4-phenylcatechol, 4-methylresorcin, 4-ethylresorcin, 4-t-butyl Resorcin, 4-hexyl resorcin, 4-chloro resorcin, 4-benzyl resorcin, 4-acetyl resorcin, 4-carbomethoxy resorcin, 2-methyl resorcin, 5-methyl resorcin, t-butyl hydroquinone, 2,5-di-t -Butylhydroquinone, 2,5-di-t-amylhydroquinone, tetramethylhydroquinone, tetrachlorohydroquinone, methylcarboaminohydroquinone, methylureidohydroquinone, methylthiohydroquinone, benzonor Runene-3,6-diol, bisphenol A, bisphenol S, 3,3′-dichlorobisphenol S, 4,4′-dihydroxybenzophenone, 4,4′-dihydroxybiphenyl, 4,4′-thiodiphenol, 2, 2′-dihydroxydiphenylmethane, 3,4-bis (p-hydroxyphenyl) hexane, 1,4-bis (2- (p-hydroxyphenyl) propyl) benzene, bis (4-hydroxyphenyl) methylamine, 1,3 -Dihydroxynaphthalene, 1,4-dihydroxynaphthalene, 1,5-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, 1,5-dihydroxyanthraquinone, 2-hydroxybenzyl alcohol, 4-hydroxybenzyl alcohol, 2-hydroxy-3, 5-di-t-butylbenzyl Alcohol, 4-hydroxy-3,5-di-t-butylbenzyl alcohol, 4-hydroxyphenethyl alcohol, 2-hydroxyethyl-4-hydroxybenzoate, 2-hydroxyethyl-4-hydroxyphenyl acetate, resorcin mono-2- And hydroxyethyl ether. The diol compound shown below can also be used conveniently.

(V) Other amino group-containing compounds In the polyurethane resin binder of the present invention, the following formulas (31) and (32
) May be combined with a diisocyanate compound to form a urea structure and incorporated into the structure of the polyurethane resin.

In the formula, R ₁₀₆ and R ₁₀₆ ^′ may be the same or different, and each may be a hydrogen atom, a substituent (for example, alkoxy, halogen atom (—F, —Cl, —Br, —I), ester, carboxyl group, etc. An alkyl group, an aralkyl group and an aryl group which may have a hydrogen atom, a C1-C8 alkyl which may have a carboxyl group as a substituent, An aryl group having 6 to 15 carbon atoms is shown. L ₁₇ has a substituent (for example, each group such as alkyl, aralkyl, aryl, alkoxy, aryloxy, halogen atom (—F, —Cl, —Br, —I), carboxyl group and the like is included). And a divalent aliphatic hydrocarbon group, aromatic hydrocarbon group or heterocyclic group. If necessary, L ₁₇ may have another functional group that does not react with an isocyanate group, such as a carbonyl group, an ester group, a urethane group or an amide group. Two of R ₁₀₆ , L ₁₇ and R _{106 ′} may form a ring.

  Specific examples of the compounds represented by the formulas (31) and (32) include those shown below.

  That is, ethylenediamine, propylenediamine, tetramethylenediamine, pentamethylenediamine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, dodecamethylenediamine, propane-1,2-diamine, bis (3-aminopropyl) methylamine, 1 , 3-bis (3-aminopropyl) tetramethylsiloxane, piperazine, 2,5-dimethylpiperazine, N- (2-aminoethyl) piperazine, 4-amino-2,2-6,6-tetramethylpiperidine, N , N-dimethylethylenediamine, lysine, L-cystine, isophoronediamine, and the like; o-phenylenediamine, m-phenylenediamine, p-phenylenediamine, 2,4-tolylenediamine, benzidine, o- Toluidine, o-dianisidine, 4-nitro-m-phenylenediamine, 2,5-dimethoxy-p-phenylenediamine, bis- (4-aminophenyl) sulfone, 4-carboxy-o-phenylenediamine, 3-carboxy-m -Aromatic diamine compounds such as phenylenediamine, 4,4'-diaminophenyl ether, 1,8-naphthalenediamine, etc .; 2-aminoimidazole, 3-aminotriazole, 5-amino-1H-tetrazole, 4-aminopyrazole 2-aminobenzimidazole, 2-amino-5-carboxy-triazole, 2,4-diamino-6-methyl-S-triazine, 2,6-diaminopyridine, L-histidine, DL-tryptophan, adenine, etc. Heterocyclic amine compounds; ethanolamine, N Methylethanolamine, N-ethylethanolamine, 1-amino-2-propanol, 1-amino-3-propanol, 2-aminoethoxyethanol, 2-aminothioethoxyethanol, 2-amino-2-methyl-1-propanol P-aminophenol, m-aminophenol, o-aminophenol, 4-methyl-2-aminophenol, 2-chloro-4-aminophenol, 4-methoxy-3-aminophenol, 4-hydroxybenzylamine, 4 -Amino-1-naphthol, 4-aminosalicylic acid, 4-hydroxy-N-phenylglycine, 2-aminobenzyl alcohol, 4-aminophenethyl alcohol, 2-carboxy-5-amino-1-naphthol, L-tyrosine, etc. Such as amino alcohol or amino Nord compound.

  As the polymer binder of the present invention, in addition to the above-mentioned polyurethane resin obtained by introducing a crosslinkable group into the side chain during the polyurethane synthesis, a polyurethane having a carboxyl group as described in JP-A-2003-270775 is highly effective. Polyurethane resins obtained by introducing crosslinkable groups by molecular reaction can also be used.

  The total amount of the polymer binder in the photosensitive layer and the binder polymer that may be used in combination is usually 10 to 90% by mass, preferably 20 to 80% by mass, based on the total mass of nonvolatile components in the photosensitive layer. %, More preferably in the range of 30 to 70% by mass.

  The molecular weight of the polymer binder in the present invention is in the range of 80,000 to 150,000, more preferably 100,000 to 130,000, and still more preferably 100,000 to 130,000.

  When the molecular weight of the polymer binder is 60,000 or less, image forming properties are poor and printing durability tends to be inferior. On the other hand, when the molecular weight of the polymer binder is 150,000 or more, the image formability and printing durability are good, but not only the developability is deteriorated, but also the coated surface is deteriorated due to an increase in the coating solution viscosity.

[Mass ratio of compound having ethylenically unsaturated double bond / polymer binder having crosslinkable group in side chain]
The mass ratio ((c) / (d)) of the compound (c) having an unsaturated double bond contained in the photosensitive layer and the polymer binder (d) having a crosslinkable group in the side chain is high sensitivity.・ It is very important to achieve both high printing durability and storage stability. In the present invention, the mass ratio ((c) / (d)) of the component (c) and the component (d) is in the range of 0.2 to 1.15, preferably in the range of 0.3 to 0.95. .

  When the mass ratio ((c) / (d)) is less than 0.2, developability deteriorates and a clear image cannot be obtained. On the other hand, when the mass ratio ((c) / (d)) exceeds 1.15, the storage stability is lowered, and further, the sensitivity is lowered and sufficient printing durability cannot be obtained.

  In a polymer binder system that does not have a crosslinkable group in a conventionally used side chain, in general, when the mass of the compound / polymer binder having an ethylenically unsaturated double bond is high, the image forming property is excellent. High sensitivity and high printing durability can be obtained, but storage stability tends to deteriorate. However, the present inventors have found that a polymer binder system having a crosslinkable group in the side chain can achieve both high sensitivity / high printing durability and storage stability when the mass ratio is low. Although the mechanism of this phenomenon has not been clarified, the use of a polymer binder having a crosslinkable group in the side chain changes the compatibility, leading to high reactivity and inhibition of migration of photosensitive components in the layer. I believe this is the result.

[(B) Photopolymerization initiator]
The photopolymerization initiator (hereinafter also simply referred to as polymerization initiator) used in the present invention is at least one selected from the group consisting of hexaarylbiimidazole compounds, onium salts, trihalomethyl compounds, and metallocene compounds. In particular, hexaarylbiimidazole compounds are preferred.

Examples of the hexaarylbiimidazole polymerization initiator include lophine dimers described in JP-B Nos. 45-37377 and 44-86516, such as 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-bromophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o, p-dichlorophenyl) ) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-chlorophenyl) -4,4', 5,5'-tetra (m-methoxyphenyl) biimidazole, 2 , 2'-bis (o, o'-dichlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-nitrophenyl) -4,4', 5,5 ′ − Traphenylbiimidazole, 2,2'-bis (o-methylphenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-trifluorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole and the like.

  The trihalomethyl compound is preferably trihalomethyl-s-triazine, 2,4,6-tris (trichloromethyl) -s-triazine, 2-methoxy-4,6-bis (trichloromethyl) -s-triazine, 2- Trimethyl compounds described in JP-A-58-29803 such as amino-4,6-bis (trichloromethyl) -s-triazine, 2- (P-methoxystyryl) -4,6-bis (trichloromethyl) -s-triazine and the like. Examples thereof include s-triazine derivatives having a halogen-substituted methyl group.

  Examples of the onium salt include onium salts represented by the following general formula (IV).

In general formula (IV), R ¹¹ , R ¹² and R ¹³ may be the same or different and each represents a hydrocarbon group having 20 or less carbon atoms which may have a substituent. Preferable substituents include a halogen atom, a nitro group, an alkyl group having 12 or less carbon atoms, an alkoxy group having 12 or less carbon atoms, or an aryloxy group having 12 or less carbon atoms. Z ⁻ represents a counter ion selected from the group consisting of halogen ion, perchlorate ion, tetrafluoroborate ion, hexafluorophosphate ion, carboxylate ion, and sulfonate ion, preferably perchlorate ion, hexa Fluorophosphate ions, carboxylate ions, and aryl sulfonate ions.

As the titanocene compound, for example, known compounds described in JP-A Nos. 59-152396 and 61-151197 can be appropriately selected and used.
Specifically, di-cyclopentadienyl-Ti-di-chloride, di-cyclopentadienyl-Ti-bis-phenyl, di-cyclopentadienyl-Ti-bis-2,3,4,5, 6-pentafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2, 4,6-trifluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,4-difluoro Phen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,4,5,6-pentafluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2, 3, 5, 6 Tetrafluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,4-difluorophen-1-yl, bis (cyclopentadienyl) -bis (2,6-difluoro-3- ( Pyrid-1-yl) phenyl) titanium and the like.

The polymerization initiator in the present invention is suitably used alone or in combination of two or more.
The amount of the polymerization initiator used in the photosensitive layer in the present invention is preferably 0.01 to 20% by mass, more preferably 0.1 to 15% by mass, based on the total solid content of the photosensitive layer. More preferably, it is 1.0 mass%-10 mass%.

[(A) Sensitizer]
The photosensitive layer of the present invention can contain a sensitizer corresponding to the wavelength of the exposure light source.
Hereinafter, the sensitizer having an absorption maximum in the wavelength range of 300 nm to 500 nm will be described. Examples of such a sensitizer include merocyanine dyes represented by the following general formula (V), benzopyrans and coumarins represented by the following general formula (VI), and fragrances represented by the following general formula (VII). And anthracenes represented by the following general formula (VIII). The general formula (IV) is sometimes called a sensitizing aid.

(In the formula, A represents an S atom or NR ₆ , R ₆ represents a monovalent non-metallic atomic group, Y represents a basic nucleus of the dye in cooperation with the adjacent A and the adjacent carbon atom. A non-metallic atomic group, X ₁ and X ₂ each independently represent a monovalent non-metallic atomic group, and X ₁ and X ₂ may combine with each other to form an acidic nucleus of the dye.)

(In the formula, = Z represents a carbonyl group, a thiocarbonyl group, an imino group or an alkylidene group represented by the partial structural formula (1 ′), and X ₁ and X ₂ have the same meanings as in the general formula (V)). And R _{7 to} R ₁₂ each independently represents a monovalent nonmetallic atomic group.)

(In the formula, Ar ₃ represents an aromatic group or a heteroaromatic group which may have a substituent, and R ₁₃ represents a monovalent nonmetallic atomic group. More preferred R ₁₃ represents an aromatic group or It is a heteroaromatic group, and Ar ₃ and R ₁₃ may be bonded to each other to form a ring.)

(In the formula, X ₃ , X ₄ and R _{14 to} R ₂₁ each independently represent a monovalent non-metallic atomic group, and more preferable X ₃ and X ₄ are electron donating groups having a negative Hammett's substituent constant. .)

In the general formulas (V) to (VIII), preferred examples of the monovalent nonmetallic atomic group represented by X ₁ to X ₄ and R ₆ to R ₂₁ include a hydrogen atom, an alkyl group (for example, a methyl group, Ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group, tridecyl group, hexadecyl group, octadecyl group, eicosyl group, isopropyl group, isobutyl group , S-butyl group, t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group, 2-norbornyl group, chloromethyl group , Bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxymethyl group, methoxy ester Toxiethyl group, allyloxymethyl group, phenoxymethyl group, methylthiomethyl group, tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N-cyclohexylcarbamoyloxyethyl Group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbonylethyl group, allyloxycarbonylbutyl group, chloro Phenoxycarbonylmethyl group, carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, -Methyl-N- (sulfophenyl) carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfa Moylpropyl group, N-methyl-N- (phosphonophenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methyl Phosphonatobutyl group, tolylphosphonohexyl group, tolylphosphonatohexyl group, phosphonooxypropyl group, phosphonatoxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group P-methylbenzyl group , Cinnamyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, etc.), aryl group ( For example, phenyl group, biphenyl group, naphthyl group, tolyl group, xylyl group, mesityl group, cumenyl group, chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group , Acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylaminophenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl Phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group, cyanophenyl group, sulfophenyl group, sulfonatophenyl group, phosphonophenyl group, phosphonatophenyl group, etc.), heteroaryl group (for example, thiophene, thiathrene) , Furan, pyran, isobenzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indoyl, indazole, purine, quinolidine, isoquinoline, phthalazine , Naphthyridine, quinazoline, cynoline, pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthroline, phthalazine, phenalzadi , Phenoxazine, furazane, phenoxazine, etc.), alkenyl group (eg, vinyl group, 1-propenyl group, 1-butenyl group, cinnamyl group, 2-chloro-1-ethenyl group, etc.), alkynyl group (eg, ethynyl group) 1-propynyl group, 1-butynyl group, trimethylsilylethynyl group, etc.), halogen atom (-F, -Br, -Cl, -I), hydroxyl group, alkoxy group, aryloxy group, mercapto group, alkylthio group, arylthio group Alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group, N-alkyl-N-arylamino group, Acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcal Vamoyloxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, arylsulfoxy group, acylthio group, acylamino group, N- Alkylacylamino group, N-arylacylamino group, ureido group, N′-alkylureido group, N ′, N′-dialkylureido group, N′-arylureido group, N ′, N′-diarylureido group, N '-Alkyl-N'-arylureido group, N-alkylureido group, N-arylureido group, N'-alkyl-N-alkylureido group, N'-alkyl-N-arylureido group, N', N ' -Dialkyl-N-alkylureido groups, N ', N'-dialkyl-N-arylurees Group, N′-aryl-N-alkylureido group, N′-aryl-N-arylureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N-aryl Ureido group, N′-alkyl-N′-aryl-N-alkylureido group, N′-alkyl-N′-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl- N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group, formyl group, acyl group, carboxyl group , Alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-al Rucarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, alkylsulfinyl group, arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group , Sulfo group (—SO ₃ H) and its conjugate base group (hereinafter referred to as sulfonate group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N-alkylsulfinamoyl group, N, N-dialkylsulfina Moyl group, N-arylsulfinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfur group Famoyl group, N-a A reelsulfamoyl group, an N, N-diarylsulfamoyl group, an N-alkyl-N-arylsulfamoyl group, a phosphono group (—PO ₃ H ₂ ) and a conjugate base group thereof (hereinafter referred to as a phosphonate group), Dialkyl phosphono group (—PO ₃ (alkyl) ₂ ), diaryl phosphono group (—PO ₃ (aryl) ₂ ), alkylaryl phosphono group (—PO ₃ (alkyl) (aryl)), monoalkyl phosphono group (—PO ₃ H (alkyl)) and its conjugate base group (hereinafter referred to as alkylphosphonate group), monoarylphosphono group (—PO ₃ H (aryl)) and its conjugate base group (hereinafter referred to as arylphosphonate) referred to as group), phosphonooxy group (-OPO ₃ H ₂₎ and its conjugated base group (hereinafter referred to as phosphonophenyl group , Dialkyl phosphonooxy group _{(-OPO 3 (alkyl) 2)} , diaryl phosphonooxy group _{(-OPO 3 (aryl) 2)} , alkylaryl phosphonooxy group _{(-OPO 3 (alkyl) (aryl} )), mono Alkylphosphonooxy group (—OPO ₃ H (alkyl)) and its conjugate base group (hereinafter referred to as alkylphosphonateoxy group), monoarylphosphonooxy group (—OPO ₃ H (aryl)) and its conjugate base Groups (hereinafter referred to as arylphosphonatooxy groups), cyano groups, nitro groups, and the like. Among the above substituents, hydrogen atoms, alkyl groups, aryl groups, halogen atoms, alkoxy groups, and acyl groups are particularly preferred. preferable.

  Examples of the basic nucleus of the dye formed together with A adjacent to Y in the general formula (V) and the adjacent carbon atom include 5-, 6-, and 7-membered nitrogen-containing or sulfur-containing heterocycles. A 5- or 6-membered heterocyclic ring is preferable.

  Examples of nitrogen-containing heterocycles include L. G. Brooker et al. , J. et al. Am. Chem. Soc. 73, 5326-5358 (1951). Any of those known to constitute a basic nucleus in the merocyanine dyes described in the literature and the references can be suitably used. Specific examples include thiazoles (for example, thiazole, 4-methylthiazole, 4-phenylthiazole, 5-methylthiazole, 5-phenylthiazole, 4,5-dimethylthiazole, 4,5-diphenylthiazole, 4,5- Di (p-methoxyphenylthiazole), 4- (2-thienyl) thiazole, etc.), benzothiazoles (for example, benzothiazole, 4-chlorobenzothiazole, 5-chlorobenzothiazole, 6-chlorobenzothiazole, 7- Chlorobenzothiazole, 4-methylbenzothiazole, 5-methylbenzothiazole, 6-methylbenzothiazole, 5-bromobenzothiazole, 4-phenylbenzothiazole, 5-phenylbenzothiazole, 4-methoxybenzothiazole, 5-methoxybenzo Cheer , 6-methoxybenzothiazole, 5-iodobenzothiazole, 6-iodobenzothiazole, 4-ethoxybenzothiazole, 5-ethoxybenzothiazole, tetrahydrobenzothiazole, 5,6-dimethoxybenzothiazole, 5,6-di Oxymethylenebenzothiazole, 5-hydroxybenzothiazole, 6-hydroxybenzothiazole, 6-dimethylaminobenzothiazole, 5-ethoxycarbonylbenzothiazole, etc.), naphthothiazoles (for example, naphtho [1,2] thiazole, naphtho [2 , 1] thiazole, 5-methoxynaphtho [2,1] thiazole, 5-ethoxynaphtho [2,1] thiazole, 8-methoxynaphtho [1,2] thiazole, 7-methoxynaphtho [1,2] thiazole, etc.) , Chianafuteno 7 ′, 6 ′, 4,5-thiazole (for example, 4′-methoxythianaphtheno-7 ′, 6 ′, 4,5-thiazole, etc.), oxazole (for example, 4-methyloxazole, 5-methyloxazole) 4-phenyloxazole, 4,5-diphenyloxazole, 4-ethyloxazole, 4,5-dimethyloxazole, 5-phenyloxazole, etc.), benzoxazoles (benzoxazole, 5-chlorobenzoxazole, 5-methylbenzoxazole) 5-phenylbenzoxazole, 6-methylbenzoxazole, 5,6-dimethylbenzoxazole, 4,6-dimethylbenzoxazole, 6-methoxybenzoxazole, 5-methoxybenzoxazole, 4-ethoxybenzoxazole, 5-chloroben Zoxazole, 6-methoxybenzoxazole, 5-hydroxybenzoxazole, 6-hydroxybenzoxazole, etc.), naphthoxazoles (eg, naphtho [1,2] oxazole, naphtho [2,1] oxazole, etc.), selenazoles ( For example, 4-methylselenazole, 4-phenylselenazole, etc.), benzoselenazoles (for example, benzoselenazole, 5-chlorobenzoselenazole, 5-methoxybenzoselenazole, 5-hydroxybenzoselenazole, tetrahydrobenzo Selenazole etc.), naphthoselenazoles (eg naphtho [1,2] selenazole, naphtho [2,1] selenazole etc.), thiazolines (eg thiazoline, 4-methylthiazoline etc.), 2-quinolines (eg Quinoline, 3- Tilquinoline, 5-methylquinoline, 7-methylquinoline, 8-methylquinoline, 6-chloroquinoline, 8-chloroquinoline, 6-methoxyquinoline, 6-ethoxyquinoline, 6-hydroxyquinoline, 8-hydroxyquinoline, etc.), 4 -Quinolines (eg, quinoline, 6-methoxyquinoline, 7-methylquinoline, 8-methylquinoline, etc.), 1-isoquinolines (eg, isoquinoline, 3,4-dihydroisoquinoline, etc.), 3-isoquinolines (eg, , Isoquinoline, etc.), benzimidazoles (eg, 1,3-diethylbenzimidazole, 1-ethyl-3-phenylbenzimidazole, etc.), 3,3-dialkylindolenins (eg, 3,3-dimethylindolenin, 3,3,5-trimethylindolenine, 3,3 7, - trimethyl indolenine, etc.), 2-pyridines (e.g., pyridine, 5-methyl-pyridine, etc.), 4-pyridine (for example, a pyridine, etc.) or the like.

Examples of the sulfur-containing heterocycle include a dithiol partial structure in dyes described in JP-A-3-296759.
Specific examples include benzodithiols (for example, benzodithiol, 5-t-butylbenzodithiol, 5-methylbenzodithiol, etc.), naphthodithiols (for example, naphtho [1,2] dithiol, naphtho [2,1] Dithiols, etc.), dithiols (for example, 4,5-dimethyldithiols, 4-phenyldithiols, 4-methoxycarbonyldithiols, 4,5-dimethoxycarbonylbenzodithiols, 4,5-ditrifluoromethyldithiols, 4 , 5-dicyanodithiol, 4-methoxycarbonylmethyldithiol, 4-carboxymethyldithiol and the like.

  As mentioned above, the description used for the explanation about the heterocyclic ring described above has conventionally used the name of the heterocyclic mother skeleton for the sake of convenience, but when forming the basic skeleton partial structure of the sensitizer, for example, in the case of the benzothiazole skeleton It is introduced in the form of an alkylidene-type substituent with one degree of unsaturation, such as a 3-substituted-2 (3H) -benzothiazolidene group.

  Of the sensitizers having an absorption maximum in a wavelength range of 360 nm to 450 nm, a dye more preferable from the viewpoint of high sensitivity is a dye represented by the following general formula (IX).

(In General Formula (IX), A represents an aromatic ring or a hetero ring which may have a substituent, and X represents an oxygen atom, a sulfur atom or N- (R ₃ ). R ₁ , R ₂ and R ₃ each independently represents a hydrogen atom or a monovalent nonmetallic atomic group, and A and R ₁ and R ₂ and R ₃ are bonded to each other to form an aliphatic or aromatic ring. May be.)

General formula (IX) will be described in more detail. R ₁ , R ₂ and R ₃ are each independently a hydrogen atom or a monovalent nonmetallic atomic group, preferably a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, substituted or non-substituted It represents a substituted aryl group, a substituted or unsubstituted aromatic heterocyclic residue, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted alkylthio group, a hydroxyl group, and a halogen atom.

Preferable examples of R ₁ , R ₂ and R ₃ will be specifically described. Examples of preferable alkyl groups include linear, branched, and cyclic alkyl groups having 1 to 20 carbon atoms. Specific examples thereof include a methyl group, an ethyl group, a propyl group, Butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, hexadecyl, octadecyl, eicosyl, isopropyl, isobutyl, s-butyl, Examples thereof include t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group and 2-norbornyl group. Of these, linear alkyl groups having 1 to 12 carbon atoms, branched alkyl groups having 3 to 12 carbon atoms, and cyclic alkyl groups having 5 to 10 carbon atoms are more preferable.

As the substituent of the substituted alkyl group, a monovalent nonmetallic atomic group excluding hydrogen is used, and preferred examples include a halogen atom (—F, —Br, —Cl, —I), a hydroxyl group, an alkoxy group, Aryloxy group, mercapto group, alkylthio group, arylthio group, alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group N-alkyl-N-arylamino group, acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, Reelsulfoxy group, acylthio group, acylamino group, N-alkylacylamino group, N-arylacylamino group, ureido group, N'-alkylureido group, N ', N'-dialkylureido group, N'-arylureido Group, N ′, N′-diarylureido group, N′-alkyl-N′-arylureido group, N-alkylureido group, N-arylureido group, N′-alkyl-N-alkylureido group, N′- Alkyl-N-arylureido group, N ', N'-dialkyl-N-alkylureido group, N', N'-dialkyl-N-arylureido group, N'-aryl-N-alkylureido group, N'- Aryl-N-arylureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N-ary Luureido group, N′-alkyl-N′-aryl-N-alkylureido group, N′-alkyl-N′-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl- N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group, formyl group, acyl group, carboxyl group , Alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group , Alkylsul Finyl group, arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group, sulfo group (—SO ₃ H) and its conjugate base group (hereinafter referred to as sulfonate group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N -Alkylsulfinamoyl group, N, N-dialkylsulfinamoyl group, N-arylsulfinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group, N-arylsulfamoyl group, N, N-diarylsulfamoyl group, N-alkyl-N-arylsulfamoyl group, phosphono group (-PO ₃ H ₂₎ and its conjugated base group (hereinafter, phospho Referred to as bets group), dialkyl phosphono group _{(-PO 3 (alkyl) 2)} , diaryl phosphono group _{(-PO 3 (aryl) 2)} , alkyl aryl phosphono group _{(-PO 3 (alkyl) (aryl} )) , Monoalkyl phosphono group (—PO ₃ H (alkyl)) and its conjugate base group (hereinafter referred to as alkyl phosphonate group), monoaryl phosphono group (—PO ₃ H (aryl)) and its conjugate base group (Hereinafter referred to as aryl phosphonate group), phosphonooxy group (—OPO ₃ H ₂ ) and its conjugate base group (hereinafter referred to as phosphonateoxy group), dialkyl phosphonooxy group (—OPO ₃ (alkyl)) _2), diaryl phosphonooxy group (-OPO ₃ (aryl) _2), alkylaryl phosphonooxy group (-OPO ₃ alkyl) (aryl)), monoalkyl phosphonooxy group (-OPO ₃ H (alkyl)) and its conjugated base group (hereinafter referred to as alkyl phosphonophenyl group), monoaryl phosphonooxy group (-OPO ₃ H (Aryl)) and conjugated base groups thereof (hereinafter referred to as arylphosphonatooxy groups), cyano groups, nitro groups, aryl groups, heteroaryl groups, alkenyl groups, and alkynyl groups.

  Specific examples of the alkyl group in these substituents include the above-described alkyl groups, and specific examples of the aryl group include a phenyl group, a biphenyl group, a naphthyl group, a tolyl group, a xylyl group, a mesityl group, and a cumenyl group. , Chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylamino Phenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl group, phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group Cyanophenyl group, sulfophenyl group, sulfonatophenyl group, phosphonophenyl phenyl group, phosphonophenyl phenyl group and the like.

As the preferred heteroaryl group as R ₁ , R ₂ and R ₃ , a monocyclic or polycyclic aromatic ring containing at least one of nitrogen, oxygen and sulfur atoms is used. Examples of particularly preferred heteroaryl groups Is, for example, thiophene, thiathrene, furan, pyran, isobenzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indolizine, indazole, indazole, Purine, quinolidine, isoquinoline, phthalazine, naphthyridine, quinazoline, sinoline, pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthrolin, phthalazine, phenalazine, phenoxazine, flaza And phenoxazine and the like. These may be further benzo-fused and may have a substituent.

Examples of preferable alkenyl groups as R ₁ , R ₂ and R ₃ include vinyl group, 1-propenyl group, 1-butenyl group, cinnamyl group, 2-chloro-1-ethenyl group and the like, and alkynyl Examples of the group include ethynyl group, 1-propynyl group, 1-butynyl group, trimethylsilylethynyl group and the like. Examples of G ₁ in the acyl group (G ₁ CO—) include hydrogen and the above alkyl groups and aryl groups. Among these substituents, even more preferred are halogen atoms (—F, —Br, —Cl, —I), alkoxy groups, aryloxy groups, alkylthio groups, arylthio groups, N-alkylamino groups, N, N— Dialkylamino group, acyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, acylamino group, formyl group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, sulfo group, sulfonate group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group Group, N-arylsulfa Yl group, N-alkyl-N-arylsulfamoyl group, phosphono group, phosphonate group, dialkyl phosphono group, diaryl phosphono group, monoalkyl phosphono group, alkyl phosphonate group, monoaryl phosphono group, aryl phosphine group Examples include an onato group, a phosphonooxy group, a phosphonateoxy group, an aryl group, and an alkenyl group.

  On the other hand, examples of the alkylene group in the substituted alkyl group include divalent organic residues obtained by removing any one of the hydrogen atoms on the alkyl group having 1 to 20 carbon atoms. Can include linear alkylene groups having 1 to 12 carbon atoms, branched chains having 3 to 12 carbon atoms, and cyclic alkylene groups having 5 to 10 carbon atoms.

Specific examples of preferable substituted alkyl groups as R ₁ , R ₂ and R ₃ obtained by combining the substituent and the alkylene group include chloromethyl group, bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxy Methyl group, methoxyethoxyethyl group, allyloxymethyl group, phenoxymethyl group, methylthiomethyl group, tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N -Cyclohexylcarbamoyloxyethyl group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbo Nylethyl group, allyloxycarbonylbutyl group, chlorophenoxycarbonylmethyl group, carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, N-methyl- N- (sulfophenyl) carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoylpropyl group N-methyl-N- (phosphonophenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphonatobu Group, tolylphosphonohexyl group, tolylphosphonatohexyl group, phosphonooxypropyl group, phosphonateoxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group, p -Methylbenzyl group, cinnamyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, etc. Can be mentioned.

Specific examples of preferred aryl groups as R ₁ , R ₂ and R ₃ include those in which 1 to 3 benzene rings form a condensed ring, and those in which a benzene ring and a 5-membered unsaturated ring form a condensed ring. Specific examples include a phenyl group, a naphthyl group, an anthryl group, a phenanthryl group, an indenyl group, an acenaphthenyl group, and a fluorenyl group. Among these, a phenyl group and a naphthyl group are more preferable. .

Specific examples of preferred substituted aryl groups as R ₁ , R ₂ and R ₃ include those having a monovalent non-metallic atomic group excluding hydrogen as a substituent on the ring-forming carbon atom of the aryl group described above. . Examples of preferred substituents include the alkyl groups, substituted alkyl groups, and those previously shown as substituents in the substituted alkyl group. Preferred examples of such a substituted aryl group include biphenyl group, tolyl group, xylyl group, mesityl group, cumenyl group, chlorophenyl group, bromophenyl group, fluorophenyl group, chloromethylphenyl group, trifluoromethylphenyl group. Hydroxyphenyl group, methoxyphenyl group, methoxyethoxyphenyl group, allyloxyphenyl group, phenoxyphenyl group, methylthiophenyl group, tolylthiophenyl group, ethylaminophenyl group, diethylaminophenyl group, morpholinophenyl group, acetyloxyphenyl group, Benzoyloxyphenyl group, N-cyclohexylcarbamoyloxyphenyl group, N-phenylcarbamoyloxyphenyl group, acetylaminophenyl group, N-methylbenzoylaminophenyl group, carbo Cyphenyl group, methoxycarbonylphenyl group, allyloxycarbonylphenyl group, chlorophenoxycarbonylphenyl group, carbamoylphenyl group, N-methylcarbamoylphenyl group, N, N-dipropylcarbamoylphenyl group, N- (methoxyphenyl) carbamoylphenyl group N-methyl-N- (sulfophenyl) carbamoylphenyl group, sulfophenyl group, sulfonatophenyl group, sulfamoylphenyl group, N-ethylsulfamoylphenyl group, N, N-dipropylsulfamoylphenyl group, N-tolylsulfamoylphenyl group, N-methyl-N- (phosphonophenyl) sulfamoylphenyl group, phosphonophenyl group, phosphonatophenyl group, diethylphosphonophenyl group, diphenylphosphono Enyl group, methylphosphonophenyl group, methylphosphonatophenyl group, tolylphosphonophenyl group, tolylphosphonatophenyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallylphenyl group, 2- Examples thereof include a methylpropenylphenyl group, a 2-propynylphenyl group, a 2-butynylphenyl group, and a 3-butynylphenyl group.

Next, A in the general formula (IX) will be described. A represents an aromatic ring or a hetero ring which may have a substituent. Specific examples of the aromatic ring or hetero ring which may have a substituent include R ₁ and R in the general formula (IX) similar to those described in ₂ and R ₃ can be exemplified.

  The sensitizer represented by the general formula (IX) of the present invention includes an acidic nucleus as shown above, an acidic nucleus having an active methylene group, a substituted or unsubstituted aromatic ring or heterocyclic ring, These can be synthesized by referring to Japanese Patent Publication No. 59-28329.

  Preferred specific examples (D1) to (D38) of the compound represented by the general formula (IX) are shown below. In addition, an isomer with a double bond connecting an acidic nucleus and a basic nucleus is not limited to either isomer.

[Thiol compound]
In the photosensitive layer of the present invention, a thiol compound represented by the following general formula (I) can be used as a chain transfer agent. By using this thiol compound, a lithographic printing plate precursor having excellent storage stability, high sensitivity and high printing durability can be obtained.

  In general formula (I), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and A represents a 5-membered ring having a carbon atom together with an N = CN moiety. Alternatively, it represents an atomic group that forms a 6-membered heterocycle, and A may further have a substituent.

  More preferably, those represented by the following general formula (II) or general formula (III) are used.

  In general formulas (II) and (III), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and X represents a halogen atom, an alkoxyl group or a substituent. The alkyl group which may have or the aryl group which may have a substituent is represented.

  Specific examples of the compound represented by formula (I) are shown below, but the present invention is not limited to these.

  The amount of these thiol compounds used is preferably 0.01 to 20% by mass, more preferably 0.1 to 15% by mass, based on the total solid content of the photosensitive layer. More preferably, it is 1.0-10 mass%.

[Thermal polymerization inhibitor]
Further, in the present invention, in addition to the basic components described above, a small amount of thermal polymerization is prohibited in order to prevent unnecessary thermal polymerization of a polymerizable ethylenically unsaturated bond-containing compound during the production or storage of a lithographic printing plate precursor. It is desirable to add an agent. Suitable thermal polymerization inhibitors include haloid quinone, p-methoxyphenol, di-t-butyl-p-cresol, pyrogallol, t-butylcatechol, benzoquinone, 4,4-thiobis (3-methyl-6-t-butylphenol) 2,2′-methylenebis (4-methyl-6-tert-butylphenol), N-nitrosophenylhydroxylamine cerium salt, N-nitrosophenylhydroxylamine aluminum salt and the like.
The addition amount of the thermal polymerization inhibitor is preferably about 0.01% by mass to about 5% by mass with respect to the total solid content constituting the photosensitive layer.

[Other additives]
If necessary, a higher fatty acid derivative such as behenic acid or behenic acid amide is added to the photosensitive layer of the present invention to prevent polymerization inhibition due to oxygen, and the surface of the photosensitive layer is dried during the coating process. May be unevenly distributed. The addition amount of the higher fatty acid derivative or the like is preferably about 0.5% by mass to about 10% by mass with respect to the total solid content constituting the photosensitive layer.
Further, a colorant may be added for the purpose of coloring the photosensitive layer. Examples of the colorant include phthalocyanine pigments (CI Pigment Blue 15: 3, 15: 4, 15: 6, etc.), azo pigments, pigments such as carbon black and titanium oxide, ethyl violet, crystal violet, There are azo dyes, anthraquinone dyes, and cyanine dyes. The addition amount of the dye and the pigment is preferably about 0.5% by mass to about 20% by mass based on the total solid content of the photosensitive layer. In addition, in order to improve the physical properties of the cured film, an additive such as an inorganic filler or a plasticizer such as dioctyl phthalate, dimethyl phthalate, or tricresyl phosphate may be added. These addition amounts are preferably 10% by mass or less based on the total solid content of the photosensitive layer.

[Support]
As the hydrophilic support of the present invention, a conventionally known hydrophilic support used in a lithographic printing plate can be used without limitation. The support used is preferably a dimensionally stable plate, for example, paper, paper laminated with plastic (eg, polyethylene, polypropylene, polystyrene, etc.), metal plate (eg, aluminum, zinc). , Copper, etc.), plastic films (eg, cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose butyrate, cellulose acetate butyrate, cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.), Paper or plastic film etc. on which such metals are laminated or vapor-deposited are included. Appropriate known physical and chemical treatments are applied to these surfaces for the purpose of imparting hydrophilicity and improving strength as necessary. You may give it.

  In particular, preferred supports include paper, polyester film or aluminum plate, among which dimensional stability is good, relatively inexpensive, and a surface with excellent hydrophilicity and strength is provided by surface treatment as required. An aluminum plate which can be used is particularly preferred. A composite sheet in which an aluminum sheet is bonded to a polyethylene terephthalate film as described in Japanese Patent Publication No. 48-18327 is also preferable.

  The aluminum substrate is a metal plate mainly composed of dimensionally stable aluminum. In addition to a pure aluminum plate, an alloy plate containing aluminum as a main component and containing a trace amount of foreign elements, or aluminum (alloy) is laminated or Selected from vapor-deposited plastic film or paper.

In the following description, the above-mentioned substrates made of aluminum or an aluminum alloy are generically used as an aluminum substrate. Examples of the foreign element contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of the foreign element in the alloy is 10% by mass or less. In the present invention, a pure aluminum plate is suitable, but completely pure aluminum is difficult to manufacture in terms of refining technology, and therefore may contain a slightly different element.
Thus, the composition of the aluminum plate applied to the present invention is not specified, and conventionally known and used materials such as JIS A 1050, JIS A 1100, JIS A 3103, and JIS A 3005 are appropriately used. It can be used. The thickness of the aluminum substrate used in the present invention is about 0.1 mm to 0.6 mm, preferably 0.15 mm to 0.4 mm, particularly preferably 0.2 mm to 0.3 mm. This thickness can be appropriately changed according to the size of the printing press, the size of the printing plate, and the user's desire. The aluminum substrate may be subjected to a substrate surface treatment described later as necessary. Of course, it may not be applied.

The aluminum substrate is usually roughened. Examples of the roughening treatment method include mechanical roughening, chemical etching, and electrolytic grain as disclosed in JP-A-56-28893. Electrochemical roughening method that further electrochemically roughens in hydrochloric acid or nitric acid electrolyte solution, and a wire brush grain method in which the aluminum surface is scratched with a metal wire, and a pole in which the aluminum surface is grained with a polishing ball and an abrasive. A mechanical roughening method such as a grain method or a brush grain method in which the surface is roughened with a nylon brush and an abrasive can be used, and the above roughening methods can be used alone or in combination. Among them, a method usefully used for roughening is an electrochemical method in which roughening is chemically carried out in hydrochloric acid or nitric acid electrolyte, and a suitable anodic electricity is 50 C / dm ^{2 to} 400 C / dm ² . It is a range. To be more specific, in the electrolytic solution containing from 0.1 to 50% by weight hydrochloric acid or nitric acid, the temperature 20 to 80 ° C., for 1 second to 30 minutes, at a current density of 100C / dm ² ~400C / dm ² It is preferable to perform alternating current and / or direct current electrolysis.

  The roughened aluminum substrate may be chemically etched with acid or alkali. Etching agents suitably used are caustic soda, sodium carbonate, sodium aluminate, sodium metasilicate, sodium phosphate, potassium hydroxide, lithium hydroxide, etc., and preferred ranges of concentration and temperature are 1 to 50% by mass, 20 to 100 ° C. Pickling is performed to remove dirt (smut) remaining on the surface after etching. As the acid used, nitric acid, sulfuric acid, phosphoric acid, chromic acid, hydrofluoric acid, borohydrofluoric acid and the like are used. In particular, as a method for removing smut after the electrochemical surface roughening treatment, it is preferably brought into contact with 15 to 65 mass% sulfuric acid at a temperature of 50 to 90 ° C. as described in JP-A-53-12739. Examples thereof include an alkali etching method described in Japanese Patent Publication No. 48-28123. After the processing as described above, the method condition is not particularly limited as long as the center line average group Ra Ra of the processing surface is 0.2 to 0.5 μm.

The aluminum substrate that has been roughened as described above is then anodized to form an oxide film. In the anodizing treatment, sulfuric acid, phosphoric acid, oxalic acid, or an aqueous solution of boric acid / sodium borate is used alone or in combination as a main component of an electrolytic bath. In this case, the electrolyte solution may of course contain at least components normally contained in at least an Al alloy plate, an electrode, tap water, groundwater and the like. Further, the second and third components may be added. Here, the second and third components are, for example, metal ions such as Na, K, Mg, Li, Ca, Ti, Al, V, Cr, Mn, Fe, Co, Ni, Cu, and Zn, and ammonium ions. Examples include cations, nitrate ions, carbonate ions, chloride ions, phosphate ions, fluorine ions, sulfite ions, titanate ions, silicate ions, borate ions and the like, and the concentration is 0 to 10,000 ppm. May be included. There are no particular limitations on the conditions for the anodizing treatment, but the treatment is preferably performed by direct current or alternating current electrolysis at a treatment liquid temperature of 10 to 70 ° C. and a current density of 0.1 to 40 A / m ² at 30 to 500 g / liter. . The thickness of the formed anodic oxide film is in the range of 0.5 to 1.5 μm. Preferably it is the range of 0.5-1.0 micrometer.

  Further, after these treatments, a water-soluble resin such as polyvinyl phosphonic acid, a polymer or copolymer having a sulfo group in the side chain, polyacrylic acid, a water-soluble metal salt (for example, zinc borate) or yellow Also suitable are those primed with dyes, amine salts and the like. Further, a sol-gel treated substrate in which a functional group capable of causing an addition reaction by a radical as disclosed in JP-A-7-159983 is covalently used.

  Other preferred examples include those in which a water-resistant hydrophilic layer is provided as a surface layer on an arbitrary support. Examples of such a surface layer include a layer composed of an inorganic pigment and a binder described in US Pat. No. 3,055,295 and JP-A-56-13168, and a hydrophilic swelling described in JP-A-9-80744. A layer, a sol-gel film made of titanium oxide, polyvinyl alcohol, silicic acid or the like described in JP-A-8-507727 can be raised. These hydrophilic treatments are performed to make the surface of the support hydrophilic, in order to prevent harmful reactions of the photosensitive layer provided thereon, and to improve the adhesion of the photosensitive layer, etc. It is to be given.

[Coating solution]
In coating the photosensitive layer, the above components are dissolved in a solvent to prepare a coating solution. Solvents used here include acetone, methyl ethyl ketone, cyclohexane, ethyl acetate, ethylene dichlorite, tetrahydrofuran, toluene, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol dimethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether. , Acetylacetone, cyclohexanone, diacetone alcohol, ethylene glycol monomethyl ether acetate, ethylene glycol ethyl ether acetate, ethylene glycol monoisopropyl ether, ethylene glycol monobutyl ether acetate, 3-methoxypropanol, methoxymethoxyethanol, diethylene glycol monomethyl ether, Ethylene glycol monoethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate-3-methoxypropyl acetate, N, N-dimethylformamide, dimethyl sulfoxide, γ-butyrolactone, methyl lactate, lactic acid There are organic solvents such as ethyl. These solvents can be used alone or in combination.
The density | concentration of the solid content in a coating solution is 1-50 mass% normally.

  In order to improve the coating surface quality, a surfactant, for example, a fluorine-based surfactant described in JP-A-62-170950 can be added. A preferable addition amount is 0.01 to 1% by mass, and more preferably 0.05 to 0.5% by mass in the material solid content of the entire photosensitive layer.

The coverage of the photosensitive layer in the weight after drying is generally about 0.1 to about 10 g / m ^2, preferably from 0.3 to 5 g / m ^2, more preferably 0.5 to 3 g / m ^2.

[Middle layer]
In the lithographic printing plate precursor according to the invention, an intermediate layer may be provided for the purpose of improving the adhesion and soiling between the photosensitive layer and the support. Specific examples of such an intermediate layer include JP-B-50-7481, JP-A-54-72104, JP-A-59-101651, JP-A-60-149491, JP-A-60-232998, JP-A-3-56177, JP-A-4-282737, JP-A-5-16558, JP-A-5-246171, JP-A-7-159983, JP-A-7-314937, JP-A-8-202025, Special Kaihei 8-320551, JP 9-34104, JP 9-236911, JP 9-269593, JP 10-69092, JP 10-115931, JP 10-161317, JP 10-260536, JP-A-10-282682, JP-A-11-84684, JP-A-11-38635, JP-A-11-38629, JP 10-282645, JP 10-301262, JP 11-24277, JP 11-109641, JP 10-319600, JP 11-327152, JP 2000-10292, JP Examples described in JP 2000-235254 A, JP 2000-352824 A, JP 2001-209170 A, and the like.

[Protective layer (oxygen barrier layer)]
The lithographic printing plate precursor according to the invention is preferably provided with a protective layer (oxygen blocking layer) on the photosensitive layer in order to block diffusion and penetration of oxygen that hinders the polymerization reaction during exposure. The protective layer used in the present invention preferably has an oxygen permeability A at 25 ° C. and 1 atm of 1.0 ≦ A ≦ 20 (cc / m ² · day). If the oxygen permeability A is less than 1.0 (cc / m ² · day) and is extremely low, unnecessary polymerization reaction may occur during production and raw storage, and unnecessary fogging and image lines may occur during image exposure. The problem that fatness arises arises. Conversely, when the oxygen permeability A exceeds 20 (cc / m ² · day) and is too high, the sensitivity is lowered. In addition to the oxygen permeability described above, the properties desired for the protective layer further do not substantially inhibit the transmission of light used for exposure, have excellent adhesion to the photosensitive layer, and are easy in the development process after exposure. It is desirable that it can be removed. Such a protective layer has been conventionally devised and described in detail in US Pat. No. 3,458,311 and Japanese Patent Publication No. 55-49729.

As a material that can be used for the protective layer, for example, a water-soluble polymer compound having relatively excellent crystallinity is preferably used. Specifically, polyvinyl alcohol, vinyl alcohol / vinyl phthalate copolymer, vinyl acetate / vinyl are used. Examples include water-soluble polymers such as alcohol / vinyl phthalate copolymer, vinyl acetate / crotonic acid copolymer, polyvinyl pyrrolidone, acidic celluloses, gelatin, gum arabic, polyacrylic acid, polyacrylamide, etc. Or they can be mixed. Of these, the use of polyvinyl alcohol as the main component gives the best results in terms of basic properties such as oxygen barrier properties and development removability.

  The polyvinyl alcohol used for the protective layer may be partially substituted with an ester, an ether, and an acetal as long as it contains an unsubstituted vinyl alcohol unit for having necessary oxygen barrier properties and water solubility. Similarly, some of them may have other copolymer components. Specific examples of polyvinyl alcohol include those that are hydrolyzed by 71 to 100 mol% and have a polymerization repeating unit in the range of 300 to 2400. Specifically, Kuraray Co., Ltd. PVA-105, PVA-110, PVA-117, PVA-117H, PVA-120, PVA-124, PVA-124H, PVA-CS, PVA-CST, PVA-HC, PVA-203, PVA-204, PVA-205, PVA-210, PVA-217, PVA-220, PVA-224, PVA-217EE, PVA-217E, PVA-220E, PVA-224E, PVA-405, PVA- 420, PVA-613, L-8 and the like, and these can be used alone or in combination. In a preferred embodiment, the content of polyvinyl alcohol in the protective layer is 20 to 95% by mass, and more preferably 30 to 90% by mass.

  As a component used by mixing with polyvinyl alcohol, polyvinyl pyrrolidone or a modified product thereof is preferable from the viewpoint of oxygen barrier properties and development removability, and the content in the protective layer is 3.5 to 80% by mass, preferably 10 to 60%. It is 15 mass%, More preferably, it is 15-30 mass%.

Components of the protective layer (selection of PVA, use of additives), coating amount, and the like are selected in consideration of fogging, adhesion, and scratch resistance in addition to oxygen barrier properties and development removability. In general, the higher the hydrolysis rate of the PVA used (the higher the content of the unsubstituted vinyl alcohol unit in the protective layer), the thicker the film thickness, the higher the oxygen barrier property, which is advantageous in terms of sensitivity. However, when the oxygen barrier property is extremely increased, there arises a problem that unnecessary polymerization reaction occurs during production and raw storage, and unnecessary fogging and image line thickening occur during image exposure. The oxygen permeability A of the protective layer in the present invention at 25 ° C. and 1 atm must be 1.0 ≦ A ≦ 20 (cc / m ² · day), preferably 1.5 ≦ A ≦ 12 ( cc / m ² · day), more preferably 2.0 ≦ A ≦ 8.0 (cc / m ² · day). The molecular weight of the (co) polymer such as polyvinyl alcohol (PVA) can be in the range of 2000 to 10 million, preferably in the range of 20,000 to 3 million.

  As another composition of the protective layer, glycerin, dipropylene glycol and the like can be added in an amount corresponding to several mass% with respect to the (co) polymer to provide flexibility. Anionic surfactants such as sodium acid salts; amphoteric surfactants such as alkylaminocarboxylates and alkylaminodicarboxylates; nonionic surfactants such as polyoxyethylene alkylphenyl ethers to the (co) polymer Mass% can be added. The thickness of the protective layer is suitably 0.5 to 5 μm, particularly 1 to 3 μm.

In addition, adhesion to the image area and scratch resistance are extremely important in handling the plate. That is, when a hydrophilic layer made of a water-soluble polymer is laminated on an oleophilic polymer layer, film peeling due to insufficient adhesion tends to occur, and the peeled part causes defects such as poor film hardening due to inhibition of oxygen polymerization. On the other hand, various proposals have been made to improve the adhesion between these two layers. For example, in U.S. Patent Application No. 292,501 and U.S. Patent Application No. 44,563, an acrylic emulsion or a water-insoluble vinyl pyrrolidone-vinyl acetate copolymer is contained in a hydrophilic polymer mainly composed of polyvinyl alcohol. It is described that sufficient adhesiveness can be obtained by mixing 20 to 60% by mass and laminating on a polymerization layer. Any of these known techniques can be applied to the protective layer in the present invention. Such a coating method of the protective layer is described in detail in, for example, US Pat. No. 3,458,311 and JP-B-55-49729.

The coating amount of the protective layer is a dry weight, generally 0.1 to 10 g / m ^2, preferably from 0.5 to 5 g / m ^2.

[Plate making method]
Next, the plate making method of the lithographic printing plate precursor according to the invention will be described in detail. The above-described lithographic printing plate precursor is subjected to image exposure and then developed with an alkaline aqueous solution. Below, the developing solution used for the plate making method of this invention is demonstrated.

(Developer)
The developer used in the plate-making method of the lithographic printing plate precursor according to the invention is not particularly limited. For example, it contains an inorganic alkali salt and a nonionic surfactant, and usually has a pH of 11.0 to 12.7. Those are preferably used.

  The inorganic alkali salt can be used as appropriate. For example, sodium hydroxide, potassium, ammonium, lithium, sodium silicate, potassium, ammonium, lithium, tribasic sodium phosphate, potassium, ammonium Inorganic alkaline agents such as sodium carbonate, potassium, ammonium, sodium hydrogen carbonate, potassium, ammonium, sodium borate, potassium, and ammonium. These may be used alone or in combination of two or more.

In the case of using silicate, developability can be achieved by adjusting the mixing ratio and concentration of silicon oxide SiO ₂ which is a component of silicate and alkali oxide M ₂ O (M represents an alkali metal or ammonium group). Can be easily adjusted. Among the alkaline aqueous solutions, those having a mixing ratio (SiO ₂ / M ₂ O: molar ratio) of the silicon oxide SiO ₂ and the alkali oxide M ₂ O of 0.5 to 3.0 are preferable, and 1.0 to 2 0.0 is preferred. The addition amount of the SiO ₂ / M ₂ O is preferably 1 to 10% by mass, more preferably 3 to 8% by mass, and most preferably 4 to 7% by mass with respect to the mass of the alkaline aqueous solution. When this concentration is within the above-mentioned range, there is no decrease in developability and processing capacity, no precipitation or crystal formation, no gelation during neutralization during waste liquid, and no trouble in waste liquid processing.

  Further, an organic alkali agent may be supplementarily used in order to finely adjust the alkali concentration and supplement the solubility of the photosensitive layer. Examples of the organic alkali agent include monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, monoisopropylamine, diisopropylamine, triisopropylamine, n-butylamine, monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, Examples thereof include diisopropanolamine, ethyleneimine, ethylenediamine, pyridine, tetramethylammonium hydroxide and the like. These alkali agents are used alone or in combination of two or more.

The surfactant can be used as appropriate. For example, nonionic surfactants having a polyoxyalkylene ether group, polyoxyethylene alkyl esters such as polyoxyethylene stearate, sorbitan monolaurate, sorbitan monostearate Nonionic surfactants such as sorbitan alkyl esters such as sorbitan distearate, sorbitan monooleate, sorbitan sesquioleate, sorbitan trioleate, and monoglyceride alkyl esters such as glycerol monostearate and glycerol monooleate; Alkyl benzene sulfonates such as sodium acetate, sodium butyl naphthalene sulfonate, sodium pentyl naphthalene sulfonate, sodium hexyl naphthalene sulfonate Anion interfaces such as alkyl naphthalene sulfonates such as sodium, sodium octyl naphthalene sulfonate, alkyl sulfates such as sodium lauryl sulfate, alkyl sulfonates such as sodium dodecyl sulfonate, and sulfosuccinate esters such as sodium dilauryl sulfosuccinate Activators: Alkyl betaines such as lauryl betaine and stearyl betaine, amphoteric surfactants such as amino acids, and the like can be mentioned. Particularly preferred are nonionic surfactants having a polyoxyalkylene ether group.

  As the surfactant containing a polyoxyalkylene ether group, those having the structure of the following general formula (X) are preferably used.

R ₄₀ —O— (R ₄₁ —O) _pH (X)

In the formula, R ₄₀ is an alkyl group having 3 to 15 carbon atoms, an aromatic hydrocarbon group having 6 to 15 carbon atoms, or a heteroaromatic ring group having 4 to 15 carbon atoms (in addition, the substituent is 1 to 20 carbon atoms). An alkylene group, a halogen atom such as Br, Cl, or I, an aromatic hydrocarbon group having 6 to 15 carbon atoms, an aralkyl group having 7 to 17 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, or an alkyl group having 2 to 20 carbon atoms An alkoxy-carbonyl group and an acyl group having 2 to 15 carbon atoms.), R ₄₁ represents an alkylene group having 1 to 100 carbon atoms, and p represents an integer of 1 to 100. Each of these groups may have a substituent, and examples of the substituent include an alkyl group having 1 to 20 carbon atoms and an aromatic hydrocarbon group having 6 to 15 carbon atoms.

  In the definition of the above formula (X), specific examples of the “aromatic hydrocarbon group” include phenyl group, tolyl group, naphthyl group, anthryl group, biphenyl group, phenanthryl group and the like, and “heteroaromatic ring” Specific examples of the “group” include furyl group, thionyl group, oxazolyl group, imidazolyl group, pyranyl group, pyridinyl group, acridinyl group, benzofuranyl group, benzothionyl group, benzopyranyl group, benzooxazolyl group, benzoimidazolyl group, and the like. It is done.

In addition, the part of (R ₄₁ —O) p in the formula (X) may be two or three groups within the above range. Specific examples include random or block combinations of ethyleneoxy and propyleneoxy groups, ethyleneoxy and isopropyloxy groups, ethyleneoxy and butyleneoxy groups, ethyleneoxy groups and isobutylene groups, and the like. . In the present invention, the surfactant having a polyoxyalkylene ether group is used alone or in combination, and it is effective to add 1 to 30% by mass, preferably 2 to 20% by mass in the developer. If the addition amount is small, the developability may be deteriorated. On the other hand, if the amount is too large, the development damage becomes strong and the printing durability of the printing plate may be deteriorated.

  Examples of the nonionic surfactant having a polyoxyalkylene ether group represented by the formula (X) include polyoxyethylene alkyl ethers such as polyoxyethylene lauryl ether, polyoxyethylene cetyl ether, and polyoxyethylene stearyl ether. Polyoxyethylene aryl ethers such as polyoxyethylene phenyl ether and polyoxyethylene naphthyl ether, polyoxyethylene alkyl aryl ethers such as polyoxyethylene methyl phenyl ether, polyoxyethylene octyl phenyl ether and polyoxyethylene nonyl phenyl ether Kind.

  These surfactants can be used alone or in combination. Further, the content of these surfactants in the developer is preferably in the range of 0.1 to 20% by mass in terms of active ingredients.

  The pH of the developer used in the plate-making method of the present invention is usually 11.0 to 12.7, preferably 11.5 to 12.5, from the viewpoint of damage during image formation and development of the exposed area.

  Moreover, it is preferable that the electrical conductivity of the developing solution used by this invention is 3-30 mS / cm. If the ratio is lower than normal, the elution of the photosensitive layer components on the surface of the aluminum plate support becomes difficult and printing may be accompanied by stains. Conversely, if the range is exceeded, the salt concentration is high, so the elution rate of the photosensitive layer is increased. This is because the film is extremely slow and a remaining film may be formed in the unexposed area. Particularly preferred conductivity is in the range of 5-20 mS / cm.

(Exposure and development processing)
The lithographic printing plate precursor in the present invention is, for example, a carbon arc lamp, a high-pressure mercury lamp, a xenon lamp, a metal halide lamp, a fluorescent lamp, a tungsten lamp, a halogen lamp, a helium cadmium laser, an argon ion laser, an FD / YAG laser, a helium neolaser, Image exposure is performed with a conventionally known actinic ray such as a semiconductor laser (300 to 600 nm). From the point of suitability for bright room, a semiconductor laser that emits light in the wavelength range of 300 to 500 nm is preferable. After image exposure, an image can be formed on the surface of the aluminum plate support by developing.
A heating process for 1 second to 5 minutes may be performed at a temperature of 50 ° C. to 140 ° C. for the purpose of increasing the curing rate of the photosensitive layer between image exposure and development. When the heating temperature is within the above range, there is an effect of increasing the curing rate, and no residual film is formed due to dark polymerization in the unexposed area.

  In addition, as described above, a protective layer is provided on the photosensitive layer of the lithographic printing plate precursor according to the invention, and the removal of the protective layer and the removal of the unexposed portion of the photosensitive layer are simultaneously performed using a developer. Or a method of removing the protective layer with water or warm water first, and then removing the unexposed photosensitive layer by development. Japanese Patent Application Laid-Open No. 10-10754 discloses such water or warm water. And the like, and the organic solvents described in JP-A-8-278636 can be contained.

  The development of the lithographic printing plate precursor in the present invention with the developer is carried out by immersing the exposed lithographic printing plate precursor in the developer at a temperature of about 0 to 60 ° C., preferably about 15 to 40 ° C., according to a conventional method. For example, rubbing with a brush.

Further, when developing using an automatic developing machine, the developing solution becomes fatigued according to the amount of processing, so that the processing capability may be restored using a replenishing solution or a fresh developing solution. The lithographic printing plate precursor thus developed is washed with water or a surfactant as described in JP-A Nos. 54-8002, 55-1115045, 59-58431, etc. And a desensitizing solution containing gum arabic, starch derivatives and the like. In the present invention, these treatments can be used in various combinations for the post-treatment of the lithographic printing plate precursor.
The printing plate obtained by the above treatment can be improved in printing durability by post-exposure treatment or heating treatment such as burning according to the method described in JP-A-2000-89478.
The planographic printing plate obtained by such processing is loaded on an offset printing machine and used for printing a large number of sheets.

  EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited to these.

[Examples 1-5 and Comparative Examples 1-2]
(Method for producing aluminum support)
An aluminum plate having a thickness of 0.3 mm was etched by being immersed in 10% by mass sodium hydroxide at 60 ° C. for 25 seconds, washed with running water, neutralized and washed with 20% by mass nitric acid, and then washed with water. This was subjected to an electrolytic surface roughening treatment in a 1% by mass nitric acid aqueous solution using a sinusoidal alternating waveform current at an anode time electricity of 300 coulomb / dm ² . Subsequently, after dipping in a 1% by mass aqueous sodium hydroxide solution at 40 ° C. for 5 seconds and then in a 30% by mass sulfuric acid aqueous solution and desmutting at 60 ° C. for 40 seconds, the current density in a 20% by mass sulfuric acid aqueous solution was 2A / current density. Anodization was performed for 2 minutes so that the thickness of the anodized film was 2.7 g / m ² under the condition of dm ² . When the surface roughness was measured, it was 0.3 μm (Ra display according to JIS B0601).

(Formation of intermediate layer)
The aluminum plate thus treated was first coated with the next intermediate layer solution using a bar coater and then dried at 80 ° C. for 20 seconds. A coating amount of the intermediate layer after drying was 10 mg / m ^2.

Intermediate layer solution ・ 100g of the following sol solution
・ Methanol 900g

Sol solution ・ Phosmer PE (Unichemical Co., Ltd.) 5g
・ Methanol 45g
・ Water 10g
・ 85% phosphoric acid 5g
・ Tetraethoxysilane 20g
・ 3-Methacryloxypropyltrimethoxysilane 15g

(Formation of photosensitive layer)
On the intermediate layer, a high-sensitivity photopolymerizable composition P-1 having the following composition was applied so that the dry coating mass was 1.4 g / m ² and dried at 100 ° C. for 1 minute to form a photosensitive layer. did.

Photopolymerizable composition P-1
-Ethylenically unsaturated bond-containing compound (monomer) (A-1) Table 1 amount-Polymer binder (B-1) Table 1 amount-Sensitizer (C-1) 0.21 part by mass-Polymerization start Agent (D-1) 0.81 parts by mass Chain transfer agent (2-mercapto-N-phenylbenzimidazole) 0.30 parts by mass Thermal polymerization inhibitor (N-nitrosophenylhydroxylamine) 0.05 parts by mass ε-phthalocyanine dispersion 0.76 parts by mass Fluorine-based nonionic surfactant Megafac F780 0.05 parts by mass (Dainippon Ink Chemical Co., Ltd.)
・ Methyl ethyl ketone 58 parts by mass ・ Propylene glycol monomethyl ether acetate 53 parts by mass

(Formation of protective layer)
A mixed aqueous solution of polyvinyl alcohol (saponification degree: 98 mol%, polymerization degree: 500) and polyvinylpyrrolidone (BASF Corp., Rubiscor K-30) is applied to the surface of the photosensitive layer with a wire bar. It was dried at 125 ° C. for 75 seconds with a drying apparatus. The content of polyvinyl alcohol / polyvinylpyrrolidone was 4/1% by mass, and the coating amount (the coating amount after drying) was 2.45 g / m ² .

[Evaluation]
(1) Coating surface shape The coating surface shape of a lithographic printing plate precursor prepared by sequentially laminating a photosensitive layer and a protective layer on a hydrophilic support was visually confirmed.

(2) Sensitivity and printing durability The obtained lithographic printing plate precursor was adjusted with Vx9600CTP (light source wavelength: 405 nm) manufactured by Fuji Photo Film Co., Ltd. so that the exposure amount on the photosensitive material was 0.05 mJ / cm ^2. Then, a gray scale was pasted on the printing plate and exposed from above. (The gray scale is made so that the amount of light changes by 1 / √2, and the higher the gray scale level is, the higher the sensitivity is.) The gray scale level is visually read to evaluate the sensitivity. Thereafter, a PS processor IP850HD (preheat temperature 115 ° C., 15 seconds) manufactured by G & J Co., which was charged with an alkali developer having the following composition was used, and the liquid temperature was maintained at 25 ° C. and development was performed for 28 seconds. The obtained lithographic printing plate was printed on a Lithrone printing machine manufactured by Komori Corporation using DIC-GEOS (N) ink manufactured by Dainippon Ink & Chemicals, Inc. Printing durability was evaluated based on the number of printed sheets when it was visually recognized that the film started to become thinner.

Alkaline developer composition Potassium hydroxide 0.15g
・ Polyoxyethylene naphthyl ether (n = 13) 5.0 g
・ Chillest 400 (chelating agent) 0.1 g
・ Water 94.75g

(3) Stability over time Except for using a lithographic printing plate precursor that was sealed with aluminum kraft paper together with interleaving paper and left to stand at 60 ° C for 3 days, exposure, development and printing were performed in the same way as in the sensitivity evaluation. The dot area ratio on the printed material was measured. Next, the difference (Δ%) between the halftone dot area ratio with leaving at 60 ° C. for 3 days and the halftone dot area ratio without leaving at 60 ° C. for 3 days was determined and used as an index of storage safety. The smaller the absolute value of Δ%, the less the influence of forced aging, that is, the higher the storage safety.
The results are shown in Table 1 below.

The mass ratio ((c) of the component (c) compound having an ethylenically unsaturated double bond and (d) a polymer binder having a crosslinkable group in the side chain, which is a feature of the present invention, is contained in the photosensitive layer. ) / (D)) can be adjusted to a range of 0.2 to 1.15, and exposure can be performed under a high sensitivity condition of 0.05 mJ / cm ^{2, and as} is clear from Table 1, sensitivity, printing durability and storage are preserved. It became possible to achieve both stability. However, the lithographic printing plate precursors of the comparative examples were unsatisfactory in terms of storage stability and printing durability under high sensitivity conditions.

[Examples 6 to 10 and Comparative Examples 3 to 4]
A lithographic printing plate precursor was prepared in the same manner as in Examples 1 to 5, except that the photopolymerizable composition P-1 was replaced with the following P-2.
The results are shown in Table 2 below.

Photopolymerizable composition P-2
-Ethylenically unsaturated bond-containing compound (monomer) (A-1) Table 2 amount-Polymer binder (B-1) Table 2 amount-Sensitizer (C-2) 0.1 part by mass-Polymerization start Agent (D-2) 0.15 parts by mass Additive (C-3) 0.2 parts by mass ε-phthalocyanine dispersion 1.5 parts by mass Thermal polymerization inhibitor: N-nitrosophenylhydroxylamine 0.01 Parts by mass ・ Fluorine-based nonionic surfactant: 0.02 parts by mass of MegaFac F780 (manufactured by Dainippon Ink & Chemicals, Inc.)
・ Methyl ethyl ketone 20.0 mass parts ・ Propylene glycol monomethyl ether 40.0 mass parts

The mass ratio ((c) of the component (c) compound having an ethylenically unsaturated double bond and (d) a polymer binder having a crosslinkable group in the side chain, which is a feature of the present invention, is contained in the photosensitive layer. ) / (D) is adjusted in the range of 0.2 to 1.15, exposure can be performed under a high sensitivity condition of 0.05 mJ / cm ² , as in Table 1. -It has become possible to achieve both high printing durability and storage stability.

Claims (6)

  (A) a sensitizer, (b) a photopolymerization initiator, (c) a compound having an ethylenically unsaturated double bond, and (d) a polymer having a crosslinkable group on the side chain on a hydrophilic support. A lithographic printing plate precursor comprising a photosensitive layer containing a binder and a protective layer sequentially laminated, wherein (c) a compound having an ethylenically unsaturated double bond and (d) a side chain contained in the photosensitive layer A lithographic printing plate precursor having a mass ratio ((c) / (d)) to a polymer binder having a crosslinkable group of 0.2 to 1.15.   The lithographic printing plate precursor as claimed in claim 1, wherein the polymer binder having a crosslinkable group in the side chain is a polyurethane resin having a crosslinkable group in the side chain.   The lithographic printing plate precursor according to claim 1 or 2, wherein the polymer binder having a crosslinkable group in the side chain is contained in a range of 80,000 to 150,000. The lithographic printing plate precursor as claimed in any one of claims 1 to 3, wherein the photosensitive layer contains a thiol compound represented by the following general formula (I).

[In the general formula (I), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and A is a 5-membered carbon atom together with an N = CN moiety. It represents an atomic group forming a ring or a 6-membered heterocycle. A may further have a substituent. ] The thiol compound represented by the general formula (I) is at least one selected from the group consisting of compounds represented by the following general formula (II) and general formula (III). 4. The lithographic printing plate precursor as described in 4.

[In General Formulas (II) and (III), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and X represents a halogen atom, an alkoxyl group or a substituent. The alkyl group which may have or the aryl group which may have a substituent is represented. ]   The photopolymerization initiator is at least one selected from the group consisting of a hexaarylbiimidazole compound, an onium salt, a trihalomethyl compound and a metallocene compound. The lithographic printing plate precursor described.