JP2002086614A - Biaxially stretched polyamide film for lamination and retort pouch using the same - Google Patents
Biaxially stretched polyamide film for lamination and retort pouch using the sameInfo
- Publication number
- JP2002086614A JP2002086614A JP2000283432A JP2000283432A JP2002086614A JP 2002086614 A JP2002086614 A JP 2002086614A JP 2000283432 A JP2000283432 A JP 2000283432A JP 2000283432 A JP2000283432 A JP 2000283432A JP 2002086614 A JP2002086614 A JP 2002086614A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- biaxially stretched
- stretched polyamide
- polyamide film
- lamination
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、バリア性を高度に
向上させた２軸延伸ポリアミドフィルムと、これを用い
たレトルトパウチに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a biaxially stretched polyamide film having a highly improved barrier property and a retort pouch using the same.
【０００２】[0002]
【従来の技術】内容物として主に食品をパウチに充填し
て密封シール後、加圧加熱により殺菌するトルト食品等
が市販されている。柔軟な積層体からなるレトルト用包
装材料（以下、レトルトパウチ）は、前記加圧加熱殺菌
に耐え、かつ、常温流通で長期にわたり、密封と内容物
の品質を保持し、味覚の劣化を起さないことが求められ
る。従来のレトルトパウチは、図３に示すように、中間
層にアルミ箔を有した次のような仕様のものであった。 ＰＥＴ／ＯＮ／ＡＬ／ＣＰＰ（ａ） ＰＥＴ／ＡＬ／ＯＮ／ＣＰＰ（ｂ） ＰＥＴ／ＡＬ／ＣＰＰ（ｃ） ［略号 ＰＥＴ：２軸延伸ポリエステルフィルム、Ｏ
Ｎ：２軸延伸ポリアミドフィルム、ＡＬ：アルミニウム
箔、ＣＰＰ：キャストポリプロピレンフィルム］ これらの積層体からなる仕様は、アルミニウム箔により
酸素、水蒸気バリアがほぼ０であると共に、遮光性が良
好であった。また、物性の面でもアルミ箔は重要であっ
た。2. Description of the Related Art Tort foods and the like, which are mainly filled with food in a pouch, hermetically sealed, sealed and then sterilized by heating under pressure, are commercially available. The retort packaging material (hereinafter referred to as “retort pouch”) composed of a flexible laminate resists the above-mentioned pressurized heat sterilization, and maintains the sealing and the quality of the contents for a long period of time at room temperature distribution, causing deterioration of taste. Not required. As shown in FIG. 3, the conventional retort pouch has an aluminum foil in an intermediate layer and has the following specifications. PET / ON / AL / CPP (a) PET / AL / ON / CPP (b) PET / AL / CPP (c) [Abbreviation PET: biaxially stretched polyester film, O
N: biaxially stretched polyamide film, AL: aluminum foil, CPP: cast polypropylene film] In the specification composed of these laminates, the aluminum foil had almost zero oxygen and water vapor barriers and good light-shielding properties. Aluminum foil was also important in terms of physical properties.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、近年、
廃棄物処理の点から、パウチを構成する積層体の素材と
してアルミニウム箔の比率の大きいレトルトパウチは分
別の問題や、これに派生するリサイクル法による企業負
担の点から、バリア性や遮光性の点でアルミニウム箔に
代替可能な素材及び加工法が求められている。アルミ箔
を用いずにガスバリア性能と遮光性を得る方法として片
面にアルミニウムを蒸着したフィルムを用いる方法が考
えられる。ただし、前記アルミニウム蒸着フィルムは、
印刷原反に使用できない。また、アルミニウムを蒸着し
たフィルムをバリア材としてアルミニウム箔に替えて用
いると、レトルトによりバリア性が低下し、バリア層と
してはアルミニウム箔を用いた場合と比較するとかなり
見劣りすることから、実際に使用されることは殆どな
い。例えば、アルミニウム蒸着した２軸延伸ポリアミド
フィルムをバリア層として用いてレトルト用包装材料と
すると、レトルトによるナイロンの吸湿、乾燥により、
バリア性の低下、遮光性の劣化等がおこることがあっ
た。また、保存中に吸湿があるため、フィルム巻き取り
の包装や保管条件を厳重にして膨潤等が発生しないよう
に注意する必要があった。本発明の目的は、アルミニウ
ム箔を用いることなく、内容物の加圧加熱殺菌が可能
で、かつ、内容物を長期に保存、流通しても内容物の変
質、変敗から保護しうるガスバリア性と遮光性を有する
フィルム及びそれを用いたレトルト用パウチを提供する
ことである。However, in recent years,
In terms of waste disposal, retort pouches with a high proportion of aluminum foil as the material of the laminate forming the pouch are difficult to separate, and due to the burden of the company due to the recycling law derived from this, the barrier properties and light shielding properties There is a need for materials and processing methods that can be substituted for aluminum foil. As a method of obtaining gas barrier performance and light shielding properties without using an aluminum foil, a method of using a film in which aluminum is vapor-deposited on one side is considered. However, the aluminum-deposited film is
Cannot be used for printing stock. In addition, when a film on which aluminum is deposited is used in place of aluminum foil as a barrier material, the barrier property is reduced by retort, and the barrier layer is actually used because it is considerably inferior to the case where aluminum foil is used. Hardly ever. For example, when a biaxially stretched polyamide film on which aluminum is deposited is used as a barrier layer to form a packaging material for retort, the moisture absorption and drying of nylon by the retort cause
In some cases, the barrier property and the light-shielding property may be deteriorated. In addition, since there is moisture absorption during storage, it has been necessary to strictly wrap and store the film winding and to keep the storage conditions strict so as not to cause swelling or the like. An object of the present invention is to provide a gas barrier that can protect contents from deterioration and deterioration even when the contents are stored and distributed for a long period of time without using aluminum foil. And a light-shielding film and a retort pouch using the same.
【０００４】[0004]
【課題を解決するための手段】本発明は、２軸延伸した
ポリアミドフィルムの片面にアルミ蒸着層が設けられ、
他の面にアルミ蒸着、酸化アルミ蒸着、シリカ蒸着、Ｐ
ＶＤＣコート、ＰＶＡコートから選ばれるハイバリアコ
ート層が設けられていることを特徴とする積層用２軸延
伸ポリアミドフィルム及び少なくとも、基材層、バリア
層、ヒートシール層からなる積層体を用いて形成され、
前記バリア層が前記積層用２軸延伸ポリアミドフィルム
からなることを特徴とするレトルトパウチである。According to the present invention, there is provided a biaxially stretched polyamide film having an aluminum vapor-deposited layer provided on one surface thereof,
Aluminum evaporation, aluminum oxide evaporation, silica evaporation, P
A biaxially stretched polyamide film for lamination characterized by being provided with a high barrier coat layer selected from a VDC coat and a PVA coat, and a laminate formed of at least a base layer, a barrier layer, and a heat seal layer. ,
The retort pouch wherein the barrier layer is made of the biaxially stretched polyamide film for lamination.
【０００５】[0005]
【発明の実施の形態】本発明者は、前記課題に対し、鋭
意研究の結果、２軸延伸したポリアミドフィルムの一方
の面にアルミ蒸着を施し、また、他の面にアルミ蒸着、
酸化アルミ蒸着、シリカ蒸着、ＰＶＤＣコート、ＰＶＡ
コートから選ばれるハイバリアコートを施すことによっ
て、従来バリア層として用いられていたアルミニウム箔
に対抗しうるバリア性と遮光性とを有する積層用２軸延
伸ポリアミドフィルムを得ることができ、また、該積層
用２軸延伸ポリアミドフィルムをレトルト用パウチの積
層体の形成におけるバリア材として利用できることを確
認し本発明を完成するに到った。図１は、本発明の積層
用２軸延伸ポリアミドフィルムの構成を説明する断面図
である。図２は、本発明の積層用２軸延伸ポリアミドフ
ィルム構成例を説明する断面図である。BEST MODE FOR CARRYING OUT THE INVENTION The inventor of the present invention has conducted intensive studies on the above-mentioned problems, and as a result of conducting extensive research, the present inventors have conducted aluminum vapor deposition on one surface of a biaxially stretched polyamide film and aluminum vapor deposition on the other surface.
Aluminum oxide deposition, silica deposition, PVDC coating, PVA
By applying a high barrier coat selected from coats, it is possible to obtain a biaxially stretched polyamide film for lamination having a barrier property and a light-shielding property that can be opposed to an aluminum foil conventionally used as a barrier layer. It has been confirmed that a biaxially stretched polyamide film for use as a barrier material in forming a laminate of a retort pouch has been completed, and the present invention has been completed. FIG. 1 is a cross-sectional view illustrating a configuration of a biaxially stretched polyamide film for lamination of the present invention. FIG. 2 is a cross-sectional view illustrating a configuration example of a biaxially stretched polyamide film for lamination of the present invention.
【０００６】本発明の積層用２軸延伸ポリアミドフィル
ムは、図１に示すように、２軸延伸ポリアミドフィルム
２の片面にアルミニウムの蒸着層３を形成し、他の面
に、ハイバリアコート層４を設けるものである。前記ア
ルミニウムの蒸着層３を形成することによって、バリア
性とともに透明フィルムである２軸延伸ポリアミドフィ
ルム２に遮光性が付与される。２軸延伸ポリアミドフィ
ルム２は、フィルムとして強度があり、パウチの積層体
の構成フィルムとして積層されると、パウチの落下強
度、耐屈曲強度等に優れた効果を示すものであり、ま
た、２軸延伸ポリアミドフィルムは、乾燥状態において
は良好なガスバリア性を示すフィルムであるが、フィル
ムとして吸湿性があり、吸湿した状態でのバリア性が低
下することが知られている。そのため、２軸延伸ポリア
ミドフィルムは吸湿の怖れのない条件での使用が好まし
い。In the biaxially stretched polyamide film for lamination of the present invention, as shown in FIG. 1, an aluminum vapor deposition layer 3 is formed on one surface of a biaxially stretched polyamide film 2 and a high barrier coat layer 4 is formed on the other surface. It is provided. By forming the aluminum vapor deposition layer 3, the light-shielding property is given to the biaxially stretched polyamide film 2 which is a transparent film as well as the barrier property. The biaxially stretched polyamide film 2 has strength as a film, and when laminated as a constituent film of a pouch laminate, exhibits excellent effects such as pouch drop strength and bending strength. The stretched polyamide film is a film exhibiting good gas barrier properties in a dry state, but is known to have hygroscopicity as a film and to have a reduced barrier property in a moisture-absorbed state. Therefore, it is preferable to use the biaxially stretched polyamide film under the condition that there is no fear of moisture absorption.
【０００７】そして、本発明者は、２軸延伸ポリアミド
フィルムのバリア性を更に向上させる方法について研究
の結果、前述のようにその片面にアルミニウムを蒸着
し、他の面にハイバリアコート層を設けることによっ
て、水分の２軸延伸ポリアミドフィルム中への浸入（吸
湿）が阻止できて、バリア性が安定することを見出し
た。As a result of research on a method for further improving the barrier properties of the biaxially stretched polyamide film, the present inventors have found that, as described above, aluminum is vapor-deposited on one side and a high barrier coat layer is provided on the other side. By this, it was found that infiltration (moisture absorption) of water into the biaxially stretched polyamide film could be prevented, and the barrier property was stabilized.
【０００８】本発明のハイバリアコートとしては、２軸
延伸ポリアミドフィルムのバリア性を前記アルミニウム
の蒸着層とともにアルミニウム箔のレベルまで向上させ
得るものを研究した結果、次のような層形成により、実
質的にガスバリア性がゼロに近いフィルムとすることが
できた。その層とは、具体的には、アルミニウム蒸着
層、シリカ蒸着層、ＰＶＤＣコート層、ＰＶＡバリアコ
ート層から選ばれる１層以上のハイバリアコート層から
選ばれる。[0008] As a high barrier coat of the present invention, a study was made on a material capable of improving the barrier properties of a biaxially stretched polyamide film to the level of an aluminum foil together with the aluminum vapor-deposited layer. In addition, a film having gas barrier properties close to zero could be obtained. Specifically, the layer is selected from one or more high barrier coat layers selected from an aluminum vapor-deposited layer, a silica vapor-deposited layer, a PVDC coat layer, and a PVA barrier coat layer.
【０００９】このようにして得られる積層用２軸延伸ポ
リアミドフィルムは、バリア性、遮光性を必要とする多
くの食品、医薬品等の包装材料における積層体のバリア
層として巾広く利用できるが、レトルト用パウチにおい
て大きな効果を示すものである。以下、前記積層用２軸
延伸ポリアミドフィルムを積層した包装材料とそれを用
いたレトルト用パウチ等について説明する。[0009] The biaxially stretched polyamide film for lamination thus obtained can be widely used as a barrier layer of a laminate in packaging materials for many foods, pharmaceuticals and the like that require barrier properties and light shielding properties. It shows a great effect in a pouch for use. Hereinafter, a packaging material obtained by laminating the above-described biaxially stretched polyamide film for lamination and a retort pouch using the same will be described.
【００１０】本発明の積層用２軸延伸ポリアミドフィル
ムをレトルト用パウチに適用する場合、レトルト用パウ
チを形成する積層体は、図２に示すように、少なくと
も、基材層６、積層用２軸延伸ポリアミドフィルム（バ
リア層）１、シーラント層８から構成され、前記基材層
６とバリア層１、バリア層１とシーラント層８のそれぞ
れはドライラミネート法により接着された接着層９が形
成されラミネートされる。When the biaxially stretched polyamide film for lamination of the present invention is applied to a pouch for retort, a laminate for forming the pouch for retort includes, as shown in FIG. An adhesive layer 9 composed of a stretched polyamide film (barrier layer) 1 and a sealant layer 8, and the base layer 6 and the barrier layer 1, and the barrier layer 1 and the sealant layer 8 each bonded by a dry lamination method, is formed and laminated. Is done.
【００１１】前記基材層６としては、機械的強度があ
り、寸法安定性、耐熱性、耐水性等に優れたフィルムが
用いられ、具体的には、２軸延伸ポリエステルフィル
ム、２軸延伸ポリアミドフィルム、２軸延伸ポリプロピ
レンフィルム等を用いることができる。また、シーラン
ト層としては、ヒートシール性が安定し、レトルト処理
における加熱に対する耐熱性等を有する材質から選択す
るが、シーラント層として用いられる樹脂として具体的
には、中、高密度ポリエチレン、キャストポリプロピレ
ン等である。As the base layer 6, a film having mechanical strength and excellent in dimensional stability, heat resistance, water resistance and the like is used. Specifically, a biaxially oriented polyester film, a biaxially oriented polyamide A film, a biaxially stretched polypropylene film, or the like can be used. In addition, the sealant layer is selected from materials having stable heat sealing properties and heat resistance to heating in retort treatment, but specific examples of the resin used as the sealant layer include medium, high-density polyethylene and cast polypropylene. And so on.
【００１２】また、前記ドライラミネートに用いる接着
剤としては、ウレタン系接着剤が好ましい。ウレタン系
接着剤としては、レトルト用として使用されているタイ
プのものであればいずれも利用することが可能であり、
たとえば、２液反応型ポリウレタン系接着剤としてポリ
エステルポリオールなどの水酸基を有するポリオール成
分とジイソシアネートなどのイソシアネート基を有する
ポリイソシアネート成分とからなり、水酸基とイソシア
ネート基の反応でウレタン結合を形成し硬化するもの等
を用いることができる。前記ウレタン系接着剤のコート
量は、乾燥重量として０．５〜５．０ｇ/ｍ2程度が適当
である。The adhesive used for the dry lamination is preferably a urethane-based adhesive. As the urethane-based adhesive, any type can be used as long as it is used for retort.
For example, a two-component reactive polyurethane-based adhesive comprising a polyol component having a hydroxyl group such as a polyester polyol and a polyisocyanate component having an isocyanate group such as a diisocyanate, and forming a urethane bond by a reaction between the hydroxyl group and the isocyanate group to be cured. Etc. can be used. The coating amount of the urethane-based adhesive is suitably about 0.5 to 5.0 g / m 2 as a dry weight.
【００１３】以上に説明したようにして積層され、製袋
したレトルト用パウチに内容物を充填、密封してレトル
ト処理をすると、バリア層として用いた２軸延伸ポリア
ミドは、レトルトによるナイロンの吸湿による膨潤、乾
燥がなく、バリア性能、遮光性の劣化が損なわれず、ま
た、２層にわたってバリアフィルムを重ねた場合に生ず
る接着障害（外観の劣化、接着強度の低下）が発生しな
い。また、バリア層のレトルトによる劣化、デラミネー
ションは、基材側からの水、油等の透過により引き起こ
されることから、当該仕様では、レトルト後のデラミネ
ーションやバリア性の低下が防止できることを見出し
た。When the retort treatment is performed by filling the contents of the laminated and bagged retort pouch as described above, sealing the biaxially stretched polyamide, the biaxially stretched polyamide used as the barrier layer absorbs the moisture of nylon by the retort. There is no swelling, no drying, no deterioration in barrier performance and light-shielding properties, and no adhesion failure (deterioration in appearance and reduction in adhesive strength) that occurs when a barrier film is laminated over two layers. In addition, since the deterioration and delamination of the barrier layer due to retort are caused by permeation of water, oil, and the like from the base material side, the present specification has found that delamination and decrease in barrier properties after retort can be prevented. .
【００１４】２軸延伸ポリアミドフィルムの片面にアル
ミニウム蒸着を施し、他の面にアルミニウム蒸着、酸化
アルミニウム蒸着、シリカ蒸着、ＰＶＤＣコート、ＰＶ
Ａバリアコートから選ばれるハイバリアコートを施すこ
とによって、レトルトによるナイロンの吸湿、乾燥がな
く、バリア性能、遮光性の劣化等が損なわれず、バリア
フィルムを２層かさねた場合に生じる接着障害（外観の
劣化、接着強度の低下）が発生しない。また、片面にア
ルミニウム蒸着をほどこした２軸延伸ポリアミドフィル
ムをバリア層とした時には、レトルトによる劣化、デラ
ミネーションは、基材の非蒸着面側からの水、油等の透
過により引き起されることから、本発明の積層用２軸延
伸ポリアミドフィルムをバリア層とした積層体仕様とし
たレトルトパウチでは、前記ハイバリアコート層が存在
しているために、レトルト後のデラミネーションやバリ
ア性の劣化を防止できる。One side of the biaxially stretched polyamide film is subjected to aluminum deposition, and the other side is subjected to aluminum deposition, aluminum oxide deposition, silica deposition, PVDC coating, PVD coating.
By applying the high barrier coat selected from the A barrier coat, there is no moisture absorption and drying of the nylon by the retort, the barrier performance, the deterioration of the light-shielding property, etc. are not impaired, and the adhesion failure caused when the barrier film is stacked in two layers (appearance of appearance) Degradation and decrease in adhesive strength) do not occur. In addition, when a biaxially stretched polyamide film on one side of which aluminum is deposited is used as a barrier layer, deterioration and delamination due to retort are caused by permeation of water, oil, etc. from the non-deposited side of the substrate. Therefore, in the retort pouch according to the present invention, in which the biaxially stretched polyamide film for lamination is used as a barrier layer in the laminate specification, since the high barrier coat layer is present, delamination after retort and deterioration of barrier properties are prevented. it can.
【００１５】また、本発明の積層用２軸延伸ポリアミド
フィルムは、片面にアルミニウム蒸着層、他の面に前記
ハイバリアコートが施されているため、フィルムとして
防湿性があり、保存中の吸湿が少なくフィルム巻き取り
の包装や保管条件を緩和しても、積層用のフィルムとし
ての品質が低下することがなくなった。The biaxially stretched polyamide film for lamination of the present invention has a moisture-proof property as a film because it has an aluminum vapor-deposited layer on one side and the high barrier coat on the other side, and has a low moisture absorption during storage. Even if the packaging and storage conditions for film winding are relaxed, the quality of the film for lamination does not deteriorate.
【００１６】本発明の積層用２軸延伸ポリアミドフィル
ムをバリア層として用いたレトルトパウチは、通常のレ
トルト殺菌条件に耐え得るものである。レトルト処理は
つぎのようにして行なわれる。食品を充填し密封包装し
たパウチをスペーサープレートに整列載置して加圧過熱
殺菌槽に挿入し、殺菌条件として、熱水又は過熱蒸気を
前記槽内に導入して、所定の加熱殺菌条件により殺菌を
行う。前記所定の加熱殺菌条件は、内容物の種類、内容
量、流通の範囲、温度等の条件により異なるが、内容物
の中心温度が１１５〜１２５度として１〜１０分程度保
持することになる。前記温度に維持してパウチ内を滅菌
した後、槽内において、内容物温度を１００℃以下に降
温して槽から取出す。本発明の積層用２軸延伸ポリアミ
ドフィルムは、それをバリア材としてレトルト用パウチ
に用いた場合においてもレトルト処理の際の温度上昇や
冷却によるパウチとしてのバリア性の低下もなく、アル
ミニウム箔代替として実用可能なバリア材である。The retort pouch using the biaxially stretched polyamide film for lamination of the present invention as a barrier layer can withstand ordinary retort sterilization conditions. The retort processing is performed as follows. Food-filled and sealed pouches are aligned and placed on a spacer plate and inserted into a pressurized superheat sterilization tank.As sterilization conditions, hot water or superheated steam is introduced into the tank, and according to predetermined heat sterilization conditions. Perform sterilization. The predetermined heat sterilization conditions vary depending on conditions such as the type, the content, the range of distribution, and the temperature of the contents. After maintaining the above temperature and sterilizing the inside of the pouch, the temperature of the contents is lowered to 100 ° C. or lower in the tank, and the pouch is taken out of the tank. The biaxially stretched polyamide film for lamination of the present invention has no barrier property as a pouch due to temperature rise or cooling during retort treatment even when it is used as a barrier material in a retort pouch, and as an aluminum foil substitute. It is a practical barrier material.
【００１７】[0017]
【実施例】次に、本発明の積層用２軸延伸ポリアミドフ
ィルムとそれを用いたレトルト用パウチについて、実施
例により、更に具体的に説明する。なお、略号は次の通
りである。 ［ＰＥＴ、ＯＮ、ＣＰＰは前記、ＡＤ：ウレタン系接着
剤、ＶＭ：アルミニウム蒸着膜］ １．積層体の作成 ［実施例１］１５μｍの２軸延伸ナイロンフィルムの両
面に１×１０―4ｍｍＨｇの真空下で５０ｎｍのアルミ
蒸着層を形成させた。このナイロンを用いて、 ＰＥＴ１２・印刷／ＡＤ／ＶＭ・ＯＮ１５・ＶＭ／ＡＤ
／ＣＰＰ７０ ＰＥＴ：Ｅ５１０２（東洋紡株式会社製 商品名） ＡＤ：ウレタン系接着剤 ＤＩＣ ＬＸ７０３／ＫＲ９
０（大日本インキ化学工業株式会社製 商品名）、塗布
量３．５ｇ／ｍ2。 ＣＰＰ：ＺＫ９３Ｋ（東レ株式会社製 商品名） エージング条件：４０℃×３日 の仕様の積層体を得た。 ［実施例２］１５μｍの２軸延伸ナイロンフィルムの一
方の面に１×１０―4ｍｍＨｇの真空下で５０ｎｍのア
ルミ蒸着層を形成させ、他の面に１×１０―4ｍｍＨｇ
の真空下で４０ｎｍのアルミ酸化物蒸着層を形成させ
た。このナイロンを用いて、 ＰＥＴ１２・印刷／ＡＤ／ＶＭ・ＯＮ１５・ＶＭ／ＡＤ
／ＣＰＰ７０ ＰＥＴ：Ｅ５１０２（東洋紡株式会社製 商品名） ＡＤ：ウレタン系接着剤 ＤＩＣ ＬＸ７０３Ａ／ＫＲ
９０大日本インキ化学工業株式会社製 商品名）、塗布
量３．５ｇ／ｍ2。 ＣＰＰ：ＺＫ９３Ｋ（東レ株式会社製 商品名） エージング条件：４０℃×３日 の仕様の積層体を得た。 ［比較例１］２軸延伸ナイロンの一方の面に、１×１０
―4ｍｍＨｇの真空下で５０ｎｍのアルミ蒸着層を形成
させた。この材料を用いて、 ＰＥＴ１２・印刷／ＡＤ／ＶＭ・ＯＮ１５／ＡＤ／ＣＰ
Ｐ７０ ＰＥＴ：Ｅ５１０２（東洋紡株式会社製 商品名） ＡＤ：ウレタン系接着剤 ＤＩＣ ＬＸ７０３Ａ／ＫＲ
９０大日本インキ化学工業株式会社製 商品名）、塗布
量３．５ｇ／ｍ2。 ＣＰＰ：ＺＫ９３Ｋ（東レ株式会社製 商品名） エージング条件：４０℃×３日 の仕様の積層体を得た。 ［比較例２］２軸延伸ナイロンの一方の面に、１×１０
―4ｍｍＨｇの真空下で５０ｎｍのアルミ蒸着層を形成
させ、ＰＥＴ１２μｍの一方の面に、１×１０―4ｍｍ
Ｈｇの真空下で４０ｎｍのアルミ酸化物蒸着層を形成さ
せた。この材料を用いて、 ＰＥＴ１２（アルミ酸化物蒸着面 商品名）・印刷／Ａ
Ｄ／ＶＭ・ＯＮ１５／ＡＤ／ＣＰＰ７０ ＰＥＴ：Ｅ５１０２（東洋紡株式会社製 商品名） ＡＤ：ウレタン系接着剤 ＤＩＣ ＬＸ７０３Ａ／ＫＲ
９０大日本インキ化学工業株式会社製 商品名）、塗布
量３．５ｇ／ｍ2。 ＣＰＰ：ＺＫ９３Ｋ（東レ株式会社製 商品名） エージング条件：４０℃×３日 の仕様の積層体を得た。 ２．製袋、充填、レトルト殺菌処理 前記実施例１、２及び比較例１、２に記載の仕様の各積
層体を１２０ｍｍ巾×１８０ｍｍ長さの４方シールタイ
プのパウチとし、内容物として、蒸留水２００ｍｌを充
填して密封した。前記パウチの寸法は外寸（シール巾は
いずれも１０ｍｍとした）。充填し密封したパウチを熱
水式レトルト釜に載置し、パウチの中心温度が１２１
℃、３分の加熱条件として殺菌した。 ＜評価方法＞EXAMPLES Next, the biaxially stretched polyamide film for lamination of the present invention and the pouch for retort using the same will be described more specifically with reference to examples. The abbreviations are as follows. [PET, ON and CPP are AD: urethane-based adhesive, VM: evaporated aluminum film] Creating Example 1 laminate to form a 50nm aluminum deposited layer under a vacuum of 1 × 10- 4 mmHg on both surfaces of the biaxially oriented nylon film of 15 [mu] m. Using this nylon, PET12 ・ Print / AD / VM ・ ON15 ・ VM / AD
/ CPP70 PET: E5102 (trade name, manufactured by Toyobo Co., Ltd.) AD: urethane-based adhesive DIC LX703 / KR9
0 (trade name, manufactured by Dainippon Ink and Chemicals, Incorporated), coating amount 3.5 g / m 2 . CPP: ZK93K (trade name, manufactured by Toray Industries, Inc.) Aging condition: A laminate having a specification of 40 ° C. × 3 days was obtained. Example 2 to form a 50nm aluminum deposited layer under a vacuum of 1 × 10- 4 mmHg to one side of the biaxially stretched nylon film of 15μm, 1 × 10- 4 mmHg on the other side
An aluminum oxide vapor deposition layer having a thickness of 40 nm was formed under the vacuum described above. Using this nylon, PET12 ・ Print / AD / VM ・ ON15 ・ VM / AD
/ CPP70 PET: E5102 (trade name, manufactured by Toyobo Co., Ltd.) AD: Urethane-based adhesive DIC LX703A / KR
Nippon Ink Chemical Industry Co., Ltd. 90, trade name: 3.5 g / m 2 . CPP: ZK93K (trade name, manufactured by Toray Industries, Inc.) Aging condition: A laminate having a specification of 40 ° C. × 3 days was obtained. [Comparative Example 1] 1 × 10
An aluminum deposited layer of 50 nm was formed under a vacuum of 4 mmHg. Using this material, PET12 ・ Print / AD / VM ・ ON15 / AD / CP
P70 PET: E5102 (trade name, manufactured by Toyobo Co., Ltd.) AD: Urethane adhesive DIC LX703A / KR
Nippon Ink Chemical Industry Co., Ltd. 90, trade name: 3.5 g / m 2 . CPP: ZK93K (trade name, manufactured by Toray Industries, Inc.) Aging condition: A laminate having a specification of 40 ° C. × 3 days was obtained. Comparative Example 2 1 × 10
- 4 mmHg to form an aluminum deposition layer of 50nm in vacuum of, on one surface of PET12μm, 1 × 10- 4 mm
An aluminum oxide deposited layer of 40 nm was formed under a vacuum of Hg. Using this material, PET12 (aluminum oxide vapor deposition surface product name), printing / A
D / VM · ON15 / AD / CPP70 PET: E5102 (trade name, manufactured by Toyobo Co., Ltd.) AD: Urethane-based adhesive DIC LX703A / KR
Nippon Ink Chemical Industry Co., Ltd. 90, trade name: 3.5 g / m 2 . CPP: ZK93K (trade name, manufactured by Toray Industries, Inc.) Aging condition: A laminate having a specification of 40 ° C. × 3 days was obtained. 2. Bag-making, filling, and retort sterilization treatment Each of the laminates having the specifications described in Examples 1 and 2 and Comparative Examples 1 and 2 was converted into a pouch of 120 mm width × 180 mm length of a four-sided seal type, and the content was distilled water. 200 ml was filled and sealed. The dimensions of the pouch were external dimensions (the seal width was 10 mm in each case). The filled and sealed pouch is placed on a hot water type retort kettle, and the temperature of the center of the pouch is 121.
Sterilization was performed at a heating temperature of 3 ° C. for 3 minutes. <Evaluation method>
【００１８】（１）外観検査 レトルト処理の前後の積層体表面を目視にて観察した。 （２）ガスバリア性 レトルト前後の積層体の酸素透過度を測定した。 酸素透過度測定法：ＪＩＳ Ｋ７１２６ Ｂ法 測定装置：ＭＯＤＥＲＮ ＣＯＮＴＲＯＬ，ＩＮＣ．製
ＯＸ−ＴＲＡＮ ２／２０ ＜結果＞(1) Appearance inspection The surface of the laminate before and after the retort treatment was visually observed. (2) Gas Barrier Property The oxygen permeability of the laminate before and after the retort was measured. Oxygen permeability measurement method: JIS K7126 B method Measurement device: MODERN CONTROL, INC. OX-TRAN 2/20 <Result>
【００１９】結果は、表１及び表２に示す通りであっ
た。The results are as shown in Tables 1 and 2.
【表１】 [Table 1]
【表２】 本発明の積層用２軸延伸ポリアミドフィルムを用いた場
合、レトルト前後のガスバリア性も、酸素透過度として
１．０ｃｃ／ｍ2・ｄａｙ以下で、レトルト食品用包装
材料としての機能を有する。また、レトルト前後の外観
とも良好であった。比較例１、２において２軸延伸ポリ
アミドフィルムの片面にアルミニウム蒸着したものをバ
リア層とし、比較例２の基材として２軸延伸ポリエステ
ルフィルムに酸化アルミニウムを蒸着したものを用いた
が、いずれもバリア性は、酸素透過度として１．０ｃｃ
／ｍ2・ｄａｙ以上となり、特に比較例１は、レトルト
処理により酸素透過度が大きくなりバリア性の低下が明
らかであった。[Table 2] When the biaxially stretched polyamide film for lamination of the present invention is used, the gas barrier property before and after retort has an oxygen permeability of 1.0 cc / m 2 · day or less, and has a function as a packaging material for retort foods. The appearance before and after the retort was also good. In Comparative Examples 1 and 2, a biaxially stretched polyamide film on which aluminum was vapor-deposited on one surface was used as a barrier layer, and a biaxially stretched polyester film on which aluminum oxide was vapor-deposited was used as a base material of Comparative Example 2. The property is 1.0cc as oxygen permeability
/ M 2 · day or more, and particularly in Comparative Example 1, the oxygen permeability increased due to the retort treatment, and the barrier property was clearly reduced.
【００２０】[0020]
【発明の効果】２軸延伸ポリアミドフィルムの強度を生
かして、その片面にアルミニウム蒸着、別の面にハイバ
リアコート層を設けることによってアルミニウム箔に代
替し得るバリア性と遮光性を有するフィルムとすること
ができた。また、このフィルムをバリア層として積層し
たレトルト用包装材料からなるレトルトパウチは、従来
積層体の中のアルミニウムを分別する必要はなく、廃棄
処理が容易である。By making use of the strength of the biaxially stretched polyamide film, aluminum is deposited on one side and a high barrier coat layer is provided on the other side to form a film having a barrier property and a light-shielding property that can be substituted for aluminum foil. Was completed. In addition, a retort pouch made of a packaging material for a retort in which this film is laminated as a barrier layer does not need to separate aluminum in a conventional laminate, and is easily disposed of.
【図１】本発明の積層用２軸延伸ポリアミドフィルムの
構成を説明する断面図である。FIG. 1 is a cross-sectional view illustrating a configuration of a biaxially stretched polyamide film for lamination of the present invention.
【図２】本発明の積層用２軸延伸ポリアミドフィルム構
成例を説明する断面図である。FIG. 2 is a cross-sectional view illustrating a configuration example of a biaxially stretched polyamide film for lamination of the present invention.
【図３】従来技術によるレトルト用パウチ構成例を説明
する断面図である。FIG. 3 is a cross-sectional view illustrating a configuration example of a conventional retort pouch.
１ 積層用２軸延伸ポリアミドフィルム ２ ２軸延伸ポリアミドフィルム ３ アルミニウム蒸着層 ４ ハイバリアコート層 ５ 積層体 ６ 基材層 ７ バリア層 ８ ヒートシール層 ９ 接着層 １０ ２軸延伸ポリエステルフィルム １１ アルミニウム箔 １２ ポリオレフィン系シーラント １３ 印刷層 DESCRIPTION OF SYMBOLS 1 Biaxially stretched polyamide film for lamination 2 Biaxially stretched polyamide film 3 Aluminum vapor deposition layer 4 High barrier coat layer 5 Laminated body 6 Base layer 7 Barrier layer 8 Heat seal layer 9 Adhesive layer 10 Biaxially stretched polyester film 11 Aluminum foil 12 Polyolefin System sealant 13 printing layer
フロントページの続き Ｆターム(参考） 3E067 AA11 AB01 AB81 BA12A BB12A BB14A BB18A BB25A CA05 CA06 CA12 CA24 EE48 GC01 3E086 AD01 BA04 BA13 BA15 BA33 BB02 BB05 BB21 BB51 CA01 CA27 CA28 4F100 AA19C AA20C AB10B AB10C AK15C AK16C AK46A AK51G AT00D BA03 BA05 BA07 BA10B BA10C BA10E BA13 CC00C EH46C EH66B EH66C EJ38A GB17 GB23 JD02C JL12E JM02B JM02C Continued on the front page F-term (reference) 3E067 AA11 AB01 AB81 BA12A BB12A BB14A BB18A BB25A CA05 CA06 CA12 CA24 EE48 GC01 3E086 AD01 BA04 BA13 BA15 BA33 BB02 BB05 BB21 BB51 CA01 CA27 CA28 4F100 AA10B ATCAB AK13 BA10B BA10C BA10E BA13 CC00C EH46C EH66B EH66C EJ38A GB17 GB23 JD02C JL12E JM02B JM02C
Claims (2)
アルミ蒸着層が設けられ、他の面にアルミ蒸着、酸化ア
ルミ蒸着、シリカ蒸着、ＰＶＤＣコート、ＰＶＡコート
から選ばれるハイバリアコート層が設けられていること
を特徴とする積層用２軸延伸ポリアミドフィルム。1. A biaxially stretched polyamide film provided with an aluminum vapor-deposited layer on one side and a high barrier coat layer selected from aluminum vapor-deposited, aluminum oxide-deposited, silica-deposited, PVDC-coated and PVA-coated on the other side. A biaxially stretched polyamide film for lamination, characterized in that:
ール層からなる積層体を用いて形成され、前記バリア層
が請求項１に記載の積層用２軸延伸ポリアミドフィルム
からなることを特徴とするレトルトパウチ。2. A laminate comprising at least a laminate comprising a base material layer, a barrier layer and a heat seal layer, wherein the barrier layer comprises the biaxially stretched polyamide film for lamination according to claim 1. Retort pouch to do.