JP2000026218A - Controlling agent for underfloor harmful insect and controlling method - Google Patents
Controlling agent for underfloor harmful insect and controlling methodInfo
- Publication number
- JP2000026218A JP2000026218A JP10210314A JP21031498A JP2000026218A JP 2000026218 A JP2000026218 A JP 2000026218A JP 10210314 A JP10210314 A JP 10210314A JP 21031498 A JP21031498 A JP 21031498A JP 2000026218 A JP2000026218 A JP 2000026218A
- Authority
- JP
- Japan
- Prior art keywords
- colemanite
- underfloor
- particles
- controlling
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は床下害虫防除剤およ
び防除方法に係り、シロアリやごきぶりなどの床下害虫
を半永久的に効率よく防除することのできる防除剤およ
び防除方法を提供しようとするものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an underfloor pest controlling agent and a controlling method, and an object thereof is to provide a controlling agent and a controlling method capable of semi-permanently and efficiently controlling underfloor pests such as termites and dusting. is there.
【0002】[0002]
【従来の技術】シロアリやごきぶりなどの床下害虫は人
類の生活環境を害することが明かであることから斯うし
た床下害虫を防除することについては従来から各方面に
おいて種々の検討が重ねられて来たが、今日においても
好ましい技術が未だ確立されるに到っていない。2. Description of the Related Art Since it is clear that underfloor pests such as termites and cockroaches harm the living environment of human beings, various studies have been made in various fields on controlling such underfloor pests. However, even today, favorable technologies have not yet been established.
【0003】即ち、このような防除剤としては有機リン
酸系のものがよく採用されており、家屋その他の建築物
における床下その他の害虫の進出ないし通過する可能性
の高い個所に散布し或いは噴霧することが一般的であっ
て、そのための機器、手法や部材その他については各種
の提案が重ねられている。[0003] That is, as such a controlling agent, an organic phosphoric acid-based one is often employed, and is sprayed or sprayed on a house or other building where there is a high possibility that pests may enter or pass under the floor or other pests. In general, various proposals have been made for devices, methods, members, and the like therefor.
【0004】[0004]
【発明が解決しようとする課題】然しそうした多くの努
力、研究にも拘わらず、今日においても充分な成果が得
られるに到っていないことは明かである。即ちこのよう
に好ましい防除効果が得られない理由としては以下の如
くである。However, despite the many efforts and researches, it is clear that sufficient results have not been obtained even today. That is, the reason why such a favorable control effect cannot be obtained is as follows.
【0005】 前記した有機リン酸系などの殺虫作用
の強力なものはその取扱いや作業者に対する有害性が高
く、また人の生活環境を阻害する傾向などがあり、それ
らを防止する装備ないし設備を用いることが必要であっ
て、しかも、それらの不利のないような防除剤は好まし
い殺虫や防除効果を求めることができない。従って何れ
にしても斯様な事情の中間的措置となり有効且つ完全な
防除としては疑義の残るようなことで満足せざるを得な
い。[0005] Those having a strong insecticidal action, such as the above-mentioned organophosphates, are highly harmful to handling and workers, and also tend to inhibit human living environments. Control agents that need to be used and that do not have such disadvantages cannot provide favorable insecticidal and controlling effects. Therefore, in any case, it becomes an intermediate measure under such circumstances, and effective and complete pest control must be satisfied because there remains doubt.
【0006】 薬効ないし耐用(あるいは保証)期間
を充分に得ることができず、特に半永久的な耐用期間を
有する建築物においてそれに相当した耐用期間を求める
ことが困難で、反覆した防除施工を重ねざるを得ず、し
かも往々にして虫害を受けることとなり、一旦発生した
虫害は回復し得ない損害を与える。従って居住者等は新
築時においては固より防除処理後においてもシロアリな
どの虫害に対する注意ないし恐怖感に悩まされることと
なる。[0006] It is not possible to obtain a sufficient medicinal effect or a useful (or guaranteed) period, and particularly in a building having a semi-permanent useful period, it is difficult to find a corresponding useful period. And the insects are often damaged by insects, and the insect damage once caused irreparable damage. Therefore, when newly constructed, the resident or the like is bothered by the caution or fear of insect damage such as termites even after the control treatment.
【0007】 なお前記ととは実地的には不可分
的な関係を有することが一般的であって、強力な薬効な
いし耐用期間をもった防除剤はより完全な前記の装備
ないし設備を必要とし、従ってまたより強力な薬効をも
ったものは成程化学的に充分製造し得ることが知られて
いても作業者や居住者ないし周辺に致命的影響を与える
ことも確認され、例えば5年以上の耐用性を有する防除
剤はそうした致命的問題点がより明確化することとなる
ので実際の使用が制限されることは一般に知られている
通りである。[0007] In general, the above-mentioned substances generally have an inseparable relationship, and a controlling agent having a strong medicinal effect or a long service life requires more complete equipment or equipment, Therefore, even if it is known that a substance with a stronger medicinal effect can be produced chemically enough, it has been confirmed that it has a fatal effect on workers, residents and surroundings, for example, for more than 5 years. It is generally known that the use of a tolerable controlling agent limits the practical use because such a fatal problem becomes more apparent.
【0008】 コスト高であって、防除剤自体がそれ
なりに高価であり、しかも特別な機器ないし装備その他
を必要とし、また耐用期間があることから反覆施工する
ことが必要であるなどの事情からして必然的にコストア
ップとならざるを得ないし、更には上述の如くで必ずし
も充分な防除効果を期待できず、常に不安感を懐かざる
を得ない。[0008] The cost is high, the pesticide itself is reasonably expensive, and it requires special equipment, equipment, and the like. Inevitably, the cost must be increased, and furthermore, as described above, a sufficient control effect cannot be expected, and the feeling of anxiety must be always felt.
【0009】[0009]
【課題を解決するための手段】本発明は上記したような
従来技術における課題を解消することについて検討を重
ねて創案されたものであって、天然に産出する石材を用
い、しかもこれを特定粒度条件により、破砕ままの状態
で採用することによりシロアリ等の習性を利用して有効
な防除効果を的確且つ低コストに得しめることに成功し
たものであって、以下の如くである。DISCLOSURE OF THE INVENTION The present invention has been made by studying to solve the above-mentioned problems in the prior art, and uses a naturally produced stone material, and furthermore, uses a specific particle size. Depending on the conditions, by adopting it in a crushed state, it has succeeded in obtaining an effective control effect accurately and at low cost by utilizing the habits of termites and the like, as follows.
【0010】(1) 90wt%以上が径0.01〜6.5mm
のコレマナイト粒子であることを特徴とした床下害虫防
除剤。(1) A diameter of 0.01 to 6.5 mm is 90% by weight or more.
An underfloor pest control agent, characterized in that it is colemanite particles.
【0011】(2) 95wt%以上が径0.9〜4.5mm、
好ましくは径1.0〜3.0mmのコレマナイト粒子であるこ
とを特徴とした床下害虫防除剤。(2) 95% by weight or more has a diameter of 0.9 to 4.5 mm,
An underfloor pest control agent, which is preferably colemanite particles having a diameter of 1.0 to 3.0 mm.
【0012】(3) 95wt%以上が径0.01〜1.5m
m、好ましくは径0.01〜0.8mmのコレマナイト粒子で
あることを特徴とした床下害虫防除剤。(3) A diameter of 0.01 to 1.5 m is 95% by weight or more.
m, preferably a colemanite particle having a diameter of 0.01 to 0.8 mm.
【0013】(4) ゼオライト、セピオライト、アタ
パルジャイト、シリカゲル、珪藻土、鹿沼土、木炭のよ
うな多孔質粉粒材に前記(1)〜(3)項の何れか1つ
に記載した防除剤を2〜50wt%配合したことを特徴と
する床下害虫防除剤。(4) The control agent according to any one of the above (1) to (3) is added to a porous powdery material such as zeolite, sepiolite, attapulgite, silica gel, diatomaceous earth, Kanuma soil, and charcoal. An underfloor pest control agent, characterized by containing up to 50% by weight.
【0014】(5) 95wt%以上が径0.01〜6.5mm
のコレマナイト粒子を地層上の必要部位に厚さ0.8cm以
上の層として形成することを特徴とする床下害虫防除方
法。(5) A diameter of 0.01 to 6.5 mm is 95% by weight or more.
Forming a layer having a thickness of 0.8 cm or more at a required portion on the stratum.
【0015】(6) 90wt%以上が径0.6〜6.5mm、
好ましくは0.8〜4.5mmのコレマナイト粒子を地層上の
必要部位に厚さ1cm以上の層として形成することを特徴
とする床下害虫防除方法。(6) 90% by weight or more has a diameter of 0.6 to 6.5 mm,
A method for controlling underfloor pests, which preferably comprises forming colemanite particles having a thickness of 0.8 to 4.5 mm at a required portion on a formation as a layer having a thickness of 1 cm or more.
【0016】[0016]
【発明の実施の形態】上記したような本発明によるもの
の具体的な実施態様について説明すると本発明者等は床
下害虫として、困難性の著しいことが一般的に認識され
ているシロアリやゴキブリを主体とした防除について多
年に亘り実地的な検討を重ね、即ちクロルデンや有機リ
ン系の防除材を採用するようなことについても検討を重
ねて来たが、発癌性その他の人体に対する有害性が不可
避的であり、ハウスシック症候群や防除施工時における
隣接住宅の影響などをも含めて考慮するならば好ましい
ものとなし得ない。一方本発明者側においてはトルコや
アメリカ或いは中国などで得られるコレマナイトをガラ
ス製造用として相当に入手し破砕し供給して来たが、こ
のコレマナイトがホウ酸カルシウムを主体とした鉱物で
あることからこのコレマナイトを上記のような床下害虫
防除に用いることが有利であるとする可能性が推測され
た。BEST MODE FOR CARRYING OUT THE INVENTION The specific embodiments of the present invention as described above will be described. The inventors of the present invention mainly use termites and cockroaches as underfloor pests, which are generally recognized to be extremely difficult. For many years, i.e., the use of chlordane and organophosphorus-based control materials has been studied, but carcinogenicity and other harm to the human body are inevitable. However, it is not preferable if the house sick syndrome and the influence of the adjacent house at the time of pest control are taken into consideration. On the other hand, on the inventor's side, colemanite obtained in Turkey, the United States or China, etc. has been considerably obtained, crushed and supplied for glass production, but since colemanite is a mineral mainly composed of calcium borate, It was presumed that it was advantageous to use this colemanite for controlling underfloor pests as described above.
【0017】即ち、コレマナイト(コールマン石)にお
ける防虫有効成分としては前記ホウ酸カルシウムである
が、天然鉱物であるコレマナイトの破砕まま粒子におい
てはこのホウ酸カルシウムの地層中ないし地表上の水分
存在下における溶出量がその他の天然または人工のホウ
酸カルシウム含有物質に比較して著しく低いことが後述
する本発明者の入念な実地的試験分析結果から推測さ
れ、つまりシロアリなどに対する防虫効果が確認され
た。しかもこの天然に産出するコレマナイトは人工的な
合成コレマナイトその他の鉱物や化学的製品における溶
出量の少なくとも10分の1、場合によっては200分
の1またはそれ以下であることが知られ、このことは地
層上における散布ないし層状物として防虫施工する場合
において半永久的な防虫効果の期待されると推定され
た。That is, calcium borate is an effective insect repellent component in colemanite (Colemanite). In the as-crushed particles of colemanite, a natural mineral, the calcium borate is in the presence of water in the stratum or on the ground surface. It was inferred from the results of elaborate practical test analysis by the present inventor described later that the amount of dissolution was significantly lower than that of other natural or artificial calcium borate-containing substances. In other words, the insect repellent effect against termites and the like was confirmed. Moreover, this naturally occurring colemanite is known to be at least one-tenth, and in some cases less than one-hundredth, less than the amount eluted in artificial synthetic colemanite and other minerals and chemical products. It was presumed that semi-permanent insect repellent effect was expected when insect repelling was applied as a spray or layered material on the stratum.
【0018】なお、このように地層上における施工条件
での溶出量が少ないコレマナイトにおいて、このものを
シロアリ等に適用した場合の防虫ないし殺虫効果が相当
に高い。前記したように水分との遭遇条件下においては
溶出の少ないコレマナイト中ホウ酸分が上記害虫に対し
て好ましい防虫ないし殺虫作用の得られる事由の仔細に
ついては必ずしも明らかとなし得ないが、シロアリなど
の建築物床下における害虫の体液ないし虫体形成物質が
コレマナイト中ホウ酸ないしホウ酸カルシウム等を吸収
し易い関係にあるものと推定される。即ち実験的に接触
後少なくとも数時間以内から震え、麻痺などの中毒症状
や殺虫効果の得られることが種々の実験によって確認さ
れた。In addition, in the case of colemanite which has a small amount of elution under construction conditions on the stratum, the insect repellent or insecticidal effect when it is applied to termites or the like is considerably high. As mentioned above, under the conditions of encounter with moisture, the boric acid content in colemanite with little elution is not necessarily clear about the details of the reason why the preferred insect repellent or insecticidal action can be obtained for the above pests, but it is not always clear, but such as termites It is presumed that the body fluid of the insect pest or the substance forming the insect body under the floor of the building is in a relationship easily absorbing boric acid or calcium borate in colemanite. That is, various experiments confirmed that toxic symptoms such as trembling and paralysis and an insecticidal effect were obtained experimentally within at least several hours after contact.
【0019】然して、本発明者等はこのようなコレマナ
イトについて実地的に仔細な検討を重ね、このものを上
記のような防除材として採用する場合の好ましい形態に
ついて実地的な検討を重ねた結果、その破砕粒度として
は施用条件、特にシロアリ等に対する殺虫作用侵入経路
の如何によって変化するが、一般的には6.5mm以下で0.
01mm以上のものを主体とすることが好ましい防除効果
をもたらす所以であることを確認した。即ち上記のよう
なコレマナイト粒子を用いることによりその他の有機リ
ン系などの殺蟻剤を用いた場合のように作業者に対する
薬害などの影響を回避し得るが、その散布時の取扱いと
共にシロアリなどの習性ないし実際の防除処理状態など
からして害虫の皮膚からの侵入、口部からの侵入、経気
門からの侵入の如き経路如何からすれば好ましいコレマ
ナイト鉱石粉粒の程度がそれなりに異なることを知っ
た。なお本発明におけるコレマナイト粉粒は前記鉱石を
破砕しただけの破砕ままのものであり、篩別分級以上に
薬液その他の処理を受けないものである。However, the present inventors have conducted detailed studies on such colemanite on a practical basis, and have conducted on-site studies on a preferable form when this is used as a controlling material as described above. The size of the crushed particles varies depending on the application conditions, particularly the route of insecticide invasion of termites and the like.
It was confirmed that the main component having a thickness of 01 mm or more provided a preferable controlling effect. In other words, by using the colemanite particles as described above, it is possible to avoid the effects of phytotoxicity on workers as in the case of using other organophosphorus termites, etc. Depending on the habit or the actual control state, the degree of the preferred colemanite ore powder particles may differ depending on the route of infestation of the pests through the skin, through the mouth, and through the esophagus. Knew. The colemanite powder particles in the present invention are crushed as the ore is merely crushed, and are not subjected to a chemical solution or other treatment beyond the classification by sieving.
【0020】即ちコレマナイト粒子は硼酸や硼砂と異り
水に対するホウ酸カルシウムの溶解性が殆んどないこと
は上述の如くで、該粒子が必要以上に微細な場合は飛散
損失が大であって、取扱いに困難が多く、また例えば口
部からの侵入を目的とした場合には0.5mm未満のような
微粉であるとシロアリなどが排除して進み易いことにな
り、反対に5mm以上のような粗大粒度のものは迂回して
進むこととなるのに対し、0.5〜5mmの場合にはシロア
リ等がそれらの回避処置を採り難いものの如くで、しか
も取扱い時における損失も少なく、シロアリ等が衝突し
た該粒子を舐めることとなる。つまりシロアリがコレマ
ナイトを舐めることによって硼素として口部からシロア
リの体内に取込まれ、その食毒効果によって少なくとも
数日程度で巣内に戻り死亡することとなり、更にその死
体を他のシロアリが食し、同様の食毒効果によって死滅
し、全体が壊滅することとなり的確な駆除が自然的に図
られる。That is, as described above, colemanite particles have little solubility of calcium borate in water unlike boric acid and borax. If the particles are finer than necessary, scattering loss is large. However, there are many difficulties in handling, and for example, in the case of intrusion from the mouth, if it is fine powder of less than 0.5 mm, termites etc. will be easily removed and it will be easy to advance, and conversely, if it is more than 5 mm In the case of 0.5 to 5 mm, it is difficult for termites and the like to take measures to avoid them. Licks the collided particles. In other words, by termites licking colemanite, they are taken into the body of the termites as boron from the mouth and return to the nest within at least a few days due to its poisoning effect, and other termites eat the corpses, It is killed by the same poisoning effect, and the whole is destroyed, so that accurate extermination is naturally achieved.
【0021】これに対しシロアリ等の皮膚または経気門
から体内に侵入し、あるいはシロアリなどが分泌する液
によって虫体に付着侵入せしめて駆除と共に殺虫を図る
ような場合においては施用時ないし通風の如きで有効成
分が飛散、損失することを適当に阻止した条件下で、で
きるだけ微粉状であることが好ましい侵入を得しめる所
以であり、少なくとも分泌分によってシロアリ等の皮膚
に付着し得ること、呼吸時における気体の流れでの侵入
を可能ならしめることなどが要件であるから上記の場合
よりは微粉であることが好ましい。On the other hand, in the case of invasion into the body through the skin or the respiratory tract of termites or the like, or by adhering and invading the insect body by the liquid secreted by the termites, etc., the insects are killed together with the extermination. This is the reason why it is preferable that the active ingredient is in the form of fine powder as much as possible under conditions that appropriately prevent scattering and loss of the active ingredient as described above. It is preferable to use fine powder than in the above case, since it is necessary to make it possible to enter by the flow of gas at the time.
【0022】但し、実際の施用時においては常に前記の
ような、口部からの侵入、皮膚面からの侵入、経気門か
らの侵入の如きを明確に区分して利用することが必要条
件となるものでないから、それらの2つまたは3つを共
に意図した粒度のものを採用してよいことは当然であ
り、何れにしても適切な防虫ないし殺虫効果を達成する
ことができる。However, at the time of actual application, it is necessary to always clearly distinguish and use the above-mentioned invasion from the mouth, invasion from the skin surface, and invasion from the trans-spiral. It is natural that two or three of them may have the intended particle size, and in any case, an appropriate insect repellent or insecticidal effect can be achieved.
【0023】従って本発明のものは地域全般において施
行してよいことは当然であるが、また各戸単位で施行す
ることによっても好ましい効果を得ることが可能で、施
工中および施工後において作業者の人体に影響を来すこ
とが殆んどなく、自然的且つ有効なシロアリ駆除がで
き、またその他の害虫としてもゴキブリ、ダニ、ノミ、
シラミ等に対しても有効であり、蠅や蚊に対してもそれ
なりの駆除効果が得られる。Therefore, it is obvious that the present invention can be applied to the whole area, but it is also possible to obtain a favorable effect by applying to each house. It has almost no effect on the human body, can be used to control natural and effective termites, and as other pests, cockroaches, mites, fleas,
It is also effective against lice, etc., and can provide a certain control effect against fly and mosquitoes.
【0024】[0024]
【実施例】実施例1 具体的な施工態様について説明すると、本発明者等は鹿
児島県日置郡吹上町今田に存在する京都大学木質科学研
究所白蟻試験地において自然的環境下において長期に亘
るシロアリ防除効果の試験を実施した。即ち径1〜3mm
を主体として調整されたコレマナイトの粒材を準備し、
また試験設備1として図5に示すように径45cmの円筒
状塩化ビニ−ル管4を用い、該管4の底部5〜8cmを地
中に埋め、上端側開口部に蓋5を施すようにされたもの
を採用した。試験材3としては径22〜27cmで厚さが
3.5〜5cmとされた立枯れ松材(誘蟻性の高い木材)の
横断面材(輪切り材)を採用し、このものを上記試験設
備1内に装入された厚さが10〜30mmの前記コレマナ
イト粒材6上に原則的には2枚重ねた状態でセットし試
験することとした。Example 1 To explain a specific construction mode, the present inventors have found that termites have been used for a long time in a natural environment at the Kyoto University Wood Science Research Institute termite test site located in Imada, Fukiage-cho, Hioki-gun, Kagoshima Prefecture. A test of the control effect was conducted. That is, diameter 1-3mm
Prepare the colemanite granules adjusted mainly with
As shown in FIG. 5, a cylindrical vinyl chloride pipe 4 having a diameter of 45 cm is used as the test equipment 1, and the bottom 5 to 8 cm of the pipe 4 is buried in the ground, and a lid 5 is provided at the opening on the upper end side. What was done was adopted. Test material 3 has a diameter of 22 to 27 cm and a thickness of
A cross section material (round cut material) of 3.5m to 5cm dead pine wood (wood with high ant attractiveness) was adopted, and this was inserted into the test facility 1 with a thickness of 10 to 10cm. In principle, two sheets were set on the colemanite granules 6 of 30 mm and the test was performed.
【0025】なお上記のような試験設備1は上記した試
験地において図6に示すように配設し、それら試験設備
1の前後、左右の如きには断面的に1辺が3cm程度で、
長さが30cm程度として製作された同じく立枯れ松材に
よる誘蟻杭2を配設して試験地全般にシロアリを誘導す
る条件を形成したものとし、試験設備1にシロアリを誘
い集合し易い条件を形成した。なお図5、6において各
設備1に附された符号はA〜Cが区分であって、それに
付された0〜3がコレマナイト粒材の有無および層厚を
示すものであり、0はコレマナイト粒材のないもの、1
〜3はコレマナイト粒材が10mm、20mmまたは30mm
の厚さとされたことを示すものである。またこの試験は
前記白蟻試験地において同時に実施された他の防除剤に
ついての試験設備11も併せて実施されていることは図
6に示す如くである。The test equipment 1 as described above is disposed at the above-mentioned test site as shown in FIG. 6, and one side of the test equipment 1 is about 3 cm in cross section before, after, right and left.
The conditions for inducing termites throughout the test site by arranging termite stakes 2 made of the same withered pine wood manufactured to have a length of about 30 cm were formed. Was formed. In FIGS. 5 and 6, the reference numerals assigned to the respective facilities 1 are A to C, and 0 to 3 attached thereto indicate the presence or absence and the layer thickness of the colemanite particles, and 0 indicates the colemanite particles. Without material, 1
-3 are colemanite granules of 10mm, 20mm or 30mm
It is shown that the thickness was determined. As shown in FIG. 6, this test was also performed at the test facility 11 for other control agents simultaneously performed at the termite test site.
【0026】なお上記のような防蟻施工は試験結果を得
ることを主目的とした実施であることから同一の条件下
で本発明によるコレマナイト粒材を用いない(前記添字
が「0」)の外は上記同様として実施した比較例などに
ついても併せて入梅直前の時期を選び施工したが、本発
明によるものは前記コレマナイト粒材が10mm以下の層
厚であると、相当の期間(例えば10年)に亘り安定且
つ的確に試験することが実地的に困難であることから、
この層厚10mmをベースとし、併せて層厚20mm、30
mmの場合も適宜に実施したことは前述した添付図面代用
写真の符号について説明した通りである。Since the termite control as described above is performed mainly for obtaining test results, the colemanite granules according to the present invention are not used under the same conditions (the subscript is "0"). In the case of the comparative example, etc., which was carried out in the same manner as described above, the time immediately before entering the plum was also selected and applied. However, according to the present invention, if the colemanite granule has a layer thickness of 10 mm or less, a considerable period (for example, 10 years) ), It is practically difficult to test stably and accurately over
Based on this layer thickness of 10 mm, the layer thickness of 20 mm, 30
The case of mm is appropriately performed as described with reference to the above-mentioned reference numerals of the substitute photographs for drawings.
【0027】上述した試験のスタートしてから約1カ年
後においてそれぞれの試験設備(塩化ビニル管)内にお
ける状況ないし誘蟻片の状態を観察したが、比較例およ
び本発明例によるものは何れもシロアリの進入した痕跡
および蟻道の形成が認められた。然し本発明によるもの
は図1の添付図面代用写真に示す如くであって、蟻土な
どの付着が殆んどなく、また食害は全く認められないも
のであった。これに対し比較例のものは図3の図面代用
写真の如くであって相当量の蟻土付着があり、また誘蟻
板における食害もそれなりに確認された。About one year after the start of the above-mentioned test, the condition in each test facility (vinyl chloride pipe) or the state of the ant piece was observed. Traces of termites and the formation of ant trails were observed. However, according to the present invention, as shown in the attached drawing substitute photograph in FIG. 1, there was almost no adhesion of ant soil and the like, and no harm was found. On the other hand, in the case of the comparative example, as shown in the drawing substitute photograph of FIG. 3, a considerable amount of ant soil was adhered, and the damage to the termite plate was confirmed as such.
【0028】ところで本発明者等は上記した図1と図3
に示すように本発明によるコレマナイト粒材の防蟻特性
が確認されたので、このものの長期有効性について別に
検討することとし、前記のような径1〜3mmのコレマナ
イト粉粒について一般的な施用条件が床下ないし家屋外
周部における湿度の比較的高い条件であり、斯うした湿
度によってB、Caなどの殺蟻成分の溶出される環境であ
ることが有効期間を支配する決定的条件であることに鑑
み、極端に旺盛な成分溶出条件として3日間の水中浸漬
後における溶出成分を測定したが、Caの溶出量は54mg
/リットル、Bは51mg/リットルであり、また10日
間の水中浸漬後におけるCaの溶出量は97mg/リット
ル、Bは103mg/リットルであった。これに対しこの
ような成分溶出についての比較例として合成コレマナイ
ト、ウレキサイト、ボラックスおよびポリックアシッド
の溶出試験結果は次の表1に示す如くであった。By the way, the present inventors have shown in FIGS.
As shown in the above, the termite-control properties of the colemanite granules according to the present invention were confirmed, so that the long-term effectiveness of the colemanite granules was separately examined, and the general application conditions for colemanite powder having a diameter of 1 to 3 mm as described above were used. Is a relatively high humidity condition under the floor or in the surrounding area of the house, and it is a decisive condition governing the validity period that an environment in which anticidal components such as B and Ca are eluted by such humidity. In view of this, as an extremely vigorous component elution condition, the elution component after immersion in water for 3 days was measured.
/ L, B was 51 mg / L, the amount of Ca eluted after immersion in water for 10 days was 97 mg / L, and B was 103 mg / L. On the other hand, the results of dissolution tests of synthetic cholemanite, urexite, borax and polyc acid as comparative examples for such component dissolution were as shown in Table 1 below.
【0029】[0029]
【表1】[Table 1]
【0030】即ち、本発明において採用するコレマナイ
ト鉱石は比較材に対し、CaおよびBの溶出量は10分の
1〜70分の1と頗る僅少であり、これらの結果は表1
における比較材のものも同様の防虫目的で充分実用され
ているものであって、本発明によるコレマナイト粒子が
床下条件より水分を極端に大とした水中での溶出がこの
ように少ないことは一般的に湿気はあっても水没するこ
とのない住宅床下に対する使用条件下で適切に半永久的
耐用性を有するものであることが数値的にも確認され
た。That is, the amount of Ca and B eluted from the colemanite ore employed in the present invention is very small, ie, 1/10 to 1/70 of the comparative material, and these results are shown in Table 1.
The comparative material in the above is also sufficiently used for the same insect repellent purpose, and it is general that the colemanite particles according to the present invention are less dissolved in water whose water content is extremely higher than the underfloor condition. It was also numerically confirmed that the material had an appropriate semi-permanent durability under the conditions of use under the floor of a house that was not submerged even if it was humid.
【0031】なお、上述したような試験条件下で、コレ
マナイト粒子の層圧を20mmと図1のものの2倍とした
ものは図2として示す如くで、図1のものに比較して何
れも食害がないとしても図1のものより更に付着物の少
ないものであった。Under the test conditions described above, the colemanite particles having a layer pressure of 20 mm, which is twice as large as that of FIG. 1, are shown in FIG. Even if there was no, there was still less deposits than in FIG.
【0032】即ちこれらの図1や図2に示されたような
試験実施の結果からして、本発明によるものは少なくと
も10mm以上のコレマナイト粒子層を形成することによ
り相当の長い期間に亘る変化に対応でき、好ましい防蟻
結果の得られることが明らかであり、実際の建造物に採
用した場合には少なくとも10年を超える防蟻効果の得
られることが本発明者等の各種防蟻試験結果から推定で
きたので引続き試験を継続することとした。That is, based on the results of the tests shown in FIGS. 1 and 2, it can be seen that the present invention is capable of changing over a considerably long period of time by forming a colemanite particle layer of at least 10 mm or more. It is clear that a favorable termite control result can be obtained, and it can be seen from the results of various termite control tests by the present inventors that the termite control effect of at least 10 years can be obtained when employed in an actual building. Since the estimation was successful, the test was continued.
【0033】実施例2 また、上記した実施例1と同じ京都大学木質科学研究所
白蟻試験地において内径19.4cmの上記したところより
は小さい塩化ビニール管を用いた試験設備1aを符号D
〜Gとして配設したことは図6の如くであって、上述し
たところと同様に試験材料および餌木を設定して試験し
たが、約2年を経過した時点においても次の表2に示す
如くで実施例1と同様に好ましい防蟻結果が確認され、
やはり10年以上の半永久的で有効且つ適切な防蟻効果
が推定でき、引続き試験を継続することとした。なお前
記符号D〜Gに対する添字0〜3はコレマナイト粒材が
ないもの(0)と10mm、20mmおよび30mmの層厚を
示すことは前述したところと同じである。Example 2 In the same manner as in Example 1 above, a test facility 1a using a vinyl chloride tube smaller than the above with an inner diameter of 19.4 cm at the termite test site at the Institute of Wood Science, Kyoto University is denoted by D.
As shown in FIG. 6, the test materials and bait were set in the same manner as described above, and the test was conducted. However, even after about 2 years, the results are shown in Table 2 below. As in Example 1, favorable results of termite control were confirmed,
Again, a semi-permanent, effective and appropriate termite control effect for more than 10 years could be estimated, and the test was continued. It should be noted that the subscripts 0 to 3 with respect to the reference signs D to G indicate the layer thickness of 10 mm, 20 mm and 30 mm without the colemanite grain material (0), as described above.
【0034】[0034]
【表2】[Table 2]
【0035】実施例3 島根県平田市産出の天然硬質ゼオライト(鉱物名 モル
デナイト)の径0.5〜4mmとされたもの8重量部に対し
て径0.5〜4mmのコレマナイト2重量部を配合した床下
殺蟻乾燥剤を2cm厚として前記した実施例1の場合と同
様に施工し観察したが、実施例1に準じた好ましい防蟻
効果が確認される。なお殺蟻乾燥剤の厚さは実施例1の
ものの2倍であるが、80%は天然硬質ゼオライトであ
るからコレマナイトとしては実施例1のものの半分以下
である。Example 3 2 parts by weight of colemanite having a diameter of 0.5 to 4 mm were blended with 8 parts by weight of a natural hard zeolite (mineral name: mordenite) produced from Hirata, Shimane having a diameter of 0.5 to 4 mm. The underfloor ant-killing desiccant was set to a thickness of 2 cm and constructed and observed in the same manner as in Example 1 described above, but a favorable ant-control effect according to Example 1 was confirmed. Although the thickness of the termiticide is twice as large as that of Example 1, 80% is natural hard zeolite, so that the colemanite is less than half that of Example 1.
【0036】実施例4 95wt%以上が0.01〜1.5mmの微粉とされたコレマナ
イト粉末と、予め水洗後風乾した95wt%以上が0.9〜
4.5mmの顆粒材を40×25cmのバットに厚さ1cmとし
て敷き詰め、イエシロアリとヤマトシロアリの兵アリを
250頭宛歩かせて挙動を観察した。即ちその結果はシ
ロアリの種類に関係なくコレマナイトが微粉とされたも
のは約4時間で全滅したのに対して顆粒状の場合は約1
0〜20日後に全滅した。Example 4 Cholemanite powder in which 95% by weight or more was made into a fine powder of 0.01 to 1.5 mm, and 0.9% or more in which 95% by weight or more which had been previously washed with water and air-dried was 0.9%
The 4.5 mm granules were spread over a 40 x 25 cm bat with a thickness of 1 cm, and 250 soldiers of house termites and termites were walked to observe their behavior. In other words, the results show that colemanite in the form of fine powder disappeared in about 4 hours irrespective of the type of termite, whereas about 1 hour in the case of granular form
It disappeared after 0 to 20 days.
【0037】即ち、上記したような差は電子顕微鏡によ
って観察され、微粉の場合はシロアリの身体全面、特に
腹部全面に微粒が付着しており、シロアリの分泌液によ
りコレマナイト微粉が接着するとホウ素の吸収もさるこ
とながら皮膚および経気門の呼吸を閉塞阻害した可能性
が高いのに対して、顆粒状の場合にはホウ素の体内への
吸収が擦れつく腹部および経口によるのみであるためと
推定された。That is, the above-mentioned difference is observed by an electron microscope. In the case of fine powder, fine particles adhere to the entire body of the termite, especially the entire abdomen. In addition, it is highly probable that obstruction of the respiration of the skin and the esophagus was obstructed, whereas in the case of granules, the absorption of boron into the body was only due to the rubbing abdomen and the oral route. Was.
【0038】上記したような本発明のものは90wt%以
上が径0.01〜6.5mmのコレマナイト粒子であることに
より各種の施用条件を適宜に形成せしめ、しかもそれぞ
れの条件下においてシロアリのような床下害虫を効果的
且つ長期間に亘って殺害駆除せしめる。なお前記コレマ
ナイト粒子が破砕ままであることにより製造調整が容易
で、しかも低コストに提供し得る。しかも前記のように
水または水分の存在下における溶出が少ないことから貯
蔵運搬ないし包装のような管理が容易である。In the present invention, as described above, 90% by weight or more are colemanite particles having a diameter of 0.01 to 6.5 mm, so that various application conditions can be appropriately formed. Effective and long term killing and control of underfloor pests. In addition, since the colemanite particles remain crushed, the production adjustment is easy, and it can be provided at low cost. In addition, as described above, since there is little elution in the presence of water or water, management such as storage and transportation or packaging is easy.
【0039】また本発明において95wt%以上が径0.9
〜4.5mm、好ましくは径1.0〜3.0mmのコレマナイト粒
子であることによってシロアリのような床下害虫に対し
散布時の飛散損失が少なく、しかも有効な経口方式に従
った殺害駆除を効率的に達成せしめる。In the present invention, 95% by weight or more has a diameter of 0.9.
~ 4.5mm, preferably 1.0 ~ 3.0mm diameter colemanite particles, less scattering loss when spraying underfloor pests such as termites, and more efficient killing and killing according to an effective oral method To achieve the goal.
【0040】更に本発明のものは、95wt%以上が径0.
01〜1.5mm、好ましくは径0.01〜0.8mmのコレマナ
イト粒子であることによりシロアリ等の床下害虫の身体
その他における付着性を高め身体表面または経気門から
の侵入を有効に図って的確な殺害駆除を図らしめる。Furthermore, in the case of the present invention, 95% by weight or more has a diameter of 0.2.
By using colemanite particles having a diameter of from 0.01 to 1.5 mm, preferably from 0.01 to 0.8 mm, the adherence of underfloor pests such as termites to the body and the like is enhanced, and penetration from the body surface or the respiratory tract is effectively achieved. We aim for precise killing.
【0041】なお本発明のものは、ゼオライト、セピオ
ライト、アタパルジャイト、シリカゲル、珪藻土、鹿沼
土、木炭のような多孔質粉粒材に上述したような何れか
の粒度構成の防除剤を2〜50wt%配合したことにより
多孔質粉粒材による吸湿条件下で好ましい害虫防除効果
を図り、防除効果を更に向上せしめ得る。より好ましい
防除剤の量は5〜30wt%である。According to the present invention, a porous powdery material such as zeolite, sepiolite, attapulgite, silica gel, diatomaceous earth, Kanuma earth, charcoal, and the like, are mixed with 2-50 wt% of a controlling agent having any of the above-mentioned particle sizes. By blending it, a favorable pest control effect can be achieved under moisture absorbing conditions by the porous powder material, and the control effect can be further improved. A more preferred amount of the controlling agent is 5 to 30% by weight.
【0042】また本発明では、95wt%以上が径0.01
〜6.5mmのコレマナイト粒子を地層上の必要部位に厚さ
0.8cm以上の層として形成することによって好ましい半
永久的床下害虫の駆除を的確に達成せしめ得る。In the present invention, 95% by weight or more has a diameter of 0.01%.
~ 6.5mm thick colemanite particles at the required location on the stratum
By forming the layer as a layer of 0.8 cm or more, preferable semi-permanent pest control can be accurately achieved.
【0043】更に本発明では、90wt%以上が径0.6〜
6.5mm、好ましくは0.8〜4.5mmのコレマナイト粒子を
地層上の必要部位に厚さ1cm以上の層として形成するこ
とによって飛散損失の少ない条件下で上記したように半
永久的な床下害虫駆除を有効に達成せしめる。Further, in the present invention, 90% by weight or more has a diameter of 0.6 to 0.6%.
By forming colemanite particles of 6.5 mm, preferably 0.8 to 4.5 mm in a layer of a thickness of 1 cm or more on necessary portions on the formation, a semi-permanent underfloor pest as described above under conditions of low scattering loss. Effectively achieve extermination.
【0044】[0044]
【発明の効果】上記したような本発明によるときは天然
に産出するコレマナイト鉱石を用い、これを適度に砕化
したものとして有効な床下害虫の防除を達成するもので
あり、特に半永久的に効率のよい防除を達成するもので
あるから信頼性が高く、撒布その他の取扱いが容易であ
って原材が天然産出物であり、単に破砕するだけで特別
な加工などを必要としないことと相俟って頗る経済的低
コストに従来技術において困難とならざるを得ない防除
効果を有効に達成することができ、しかも少なくとも数
時間程度の短時間に殺害効果を確認でき、しかも上記の
ように半永久的であるから施工者、利用者に充分な安心
感を与え得るなどの従来技術で求め得ない格別の効果を
有しており、工業的にその効果の大きい発明である。According to the present invention, as described above, naturally occurring colemanite ore is used, which is appropriately crushed to achieve effective control of underfloor pests, and especially semipermanently efficient. It is highly reliable because it achieves good control, it is easy to scatter and handle, and the raw material is a natural product, which is simply crushed and does not require special processing. Therefore, it is possible to effectively achieve the control effect that must be made difficult by the conventional technology at a very economical low cost, and at the same time, the killing effect can be confirmed in a short time of at least several hours, and as described above, it is semi-permanent. Therefore, the present invention has an extraordinary effect that cannot be obtained by the conventional technology, such as giving a sufficient sense of security to the installer and the user, and is an industrially significant invention.
【図面の簡単な説明】[Brief description of the drawings]
【図1】本発明における実施例1による防蟻状態を示し
た図面代用写真であって、コレマナイト粒子層厚10mm
の場合の施工3カ月後の状態を示すものである。FIG. 1 is a drawing-substitute photograph showing a termite-proof state according to Example 1 of the present invention, showing a colemanite particle layer thickness of 10 mm.
3 shows the state three months after the construction.
【図2】図1と同様な施工1年後の防蟻状態を示したコ
レマナイト粒子層厚10mmの場合の図面代用写真であ
る。FIG. 2 is a photograph as a substitute for a drawing in the case of a colemanite particle layer thickness of 10 mm, showing a termite-proof state one year after construction similar to FIG.
【図3】本発明によるコレマナイト粒子を全く用いない
比較例の場合の施工3カ月後の状態を示した図面代用写
真である。FIG. 3 is a photograph substituted for a drawing, showing a state three months after construction in a comparative example using no colemanite particles according to the present invention.
【図4】図3に示したものの施工1年後の状態を示した
図面代用写真である。FIG. 4 is a drawing substitute photograph showing a state of one year after the construction shown in FIG.
【図5】本発明者等の行った白蟻試験地での試験設備配
設状態の1例についての断面図と平面図を併せて示した
説明図である。FIG. 5 is an explanatory diagram showing both a cross-sectional view and a plan view of an example of a state in which test equipment is installed at a termite test site performed by the present inventors.
【図6】本発明者等の行った試験場における実施例1、
2の各試験設備配設状態を示す平面図である。FIG. 6 is a diagram showing a first embodiment of the present invention in a test site performed by the present inventors.
FIG. 4 is a plan view showing a state of disposition of each test facility of No. 2;
【符号の説明】 A1、B1、C1、F1、G1 コレマナイト粒材層の厚さ10mm
の場合 A2、B2、C2、D2、E2 同じくコレマナイト粒材層厚20
mmの場合 A3、C3、G3、F3 同じくコレマナイト粒材層厚30mmの
場合 A0、B0、C0、D0、E0、F0、G0 コレマナイト粒材を用い
ない比較例の場合 1 試験装置(比較的大径塩化ビニル管) 1a 試験装置(比較的小径塩化ビニル管) 2 誘蟻杭 3 試験材 4 塩化ビニル管 5 蓋 6 コレマナイト粒材 11 試験地において同時に実施された他の試験装置[Description of Signs] A 1 , B 1 , C 1 , F 1 , G 1 Thickness of colemanite particle layer 10 mm
In the case of A 2 , B 2 , C 2 , D 2 , and E 2, the colemanite grain material layer thickness is also 20.
A 3 , C 3 , G 3 , F 3 In the case of a colemanite particle layer thickness of 30 mm A 0 , B 0 , C 0 , D 0 , E 0 , F 0 , G 0 Comparison without colemanite particles In the case of an example 1 Test equipment (relatively large-diameter vinyl chloride pipe) 1a Test equipment (relatively small-diameter vinyl chloride pipe) 2 Attraction pile 3 Test material 4 Vinyl chloride pipe 5 Lid 6 Coremanite granule 11 Other test equipment
─────────────────────────────────────────────────────
────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成10年7月17日(1998.7.1
7)[Submission date] July 17, 1998 (1998.7.1)
7)
【手続補正1】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】図面の簡単な説明[Correction target item name] Brief description of drawings
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【図面の簡単な説明】[Brief description of the drawings]
【図1】本発明における実施例1による防蟻状態を示し
た図面代用写真であって、コレマナイト粒子層厚10m
mの場合の施工1年後の状態を示すものである。FIG. 1 is a drawing-substitute photograph showing a termite-proof state according to Example 1 of the present invention, showing a colemanite particle layer thickness of 10 m.
It shows the state one year after the construction in the case of m.
【図2】図1と同様な施工1年後の防蟻状態を示したコ
レマナイト粒子層厚20mmの場合の図面代用写真であ
る。FIG. 2 is a photograph as a substitute for a drawing in the case of a colemanite particle layer thickness of 20 mm, showing a termite-proof state one year after construction similar to FIG.
【図3】本発明によるコレマナイト粒子を全く用いない
比較例の場合の施工3カ月後の状態を示した図面代用写
真である。FIG. 3 is a photograph substituted for a drawing, showing a state three months after construction in a comparative example using no colemanite particles according to the present invention.
【図4】図3に示したものの施工1年後の状態を示した
図面代用写真である。FIG. 4 is a drawing substitute photograph showing a state of one year after the construction shown in FIG.
【図5】本発明者等の行った白蟻試験地での試験設備配
設状態の1例についての断面図と平面図を併せて示した
説明図である。FIG. 5 is an explanatory diagram showing both a cross-sectional view and a plan view of an example of a state in which test equipment is installed at a termite test site performed by the present inventors.
【図6】本発明者等の行った試験場における実施例1、
2の各試験設備配設状態を示す平面図である。FIG. 6 is a diagram showing a first embodiment of the present invention in a test site performed by the present inventors.
FIG. 4 is a plan view showing a state of disposition of each test facility of No. 2;
【符号の説明】 A1、B1、C1、F1、G1コレマナイト粒材層の厚
さ10mmの場合 A2、B2、C2、D2、E2同じくコレマナイト粒材
層厚20mmの場合 A3、C3、G3、F3 同じくコレマナイト粒材層厚
30mmの場合 A0、B0、C0、D0、E0、F0、G0コレマナイ
ト粒材を用いない比較例の場合 1 試験装置(比較的大径塩化ビニル管) 1a 試験装置(比較的小径塩化ビニル管) 2 誘蟻杭 3 試験材 4 塩化ビニル管 5 蓋 6 コレマナイト粒材 11 試験地において同時に実施された他の試験装置[Description of Signs] A 1 , B 1 , C 1 , F 1 , G 1 In the case where the thickness of the colemanite particle layer is 10 mm A 2 , B 2 , C 2 , D 2 , E 2 The colemanite particle layer thickness is also 20 mm Comparative examples if not used a 3, C 3, G 3 , F 3 likewise the case of colemanite grained material layer thickness 30mm a 0, B 0, C 0, D 0, E 0, F 0, G 0 colemanite grain material In the case of 1 Test equipment (relatively large-diameter vinyl chloride pipe) 1a Test equipment (relatively small-diameter vinyl chloride pipe) 2 Termite pile 3 Test material 4 Vinyl chloride pipe 5 Lid 6 Coremanite granule 11 Simultaneously performed at test site Other test equipment
───────────────────────────────────────────────────── フロントページの続き (72)発明者 横山 茂樹 広島県豊田郡安芸津町大字三津字榊山5563 番地の4 昭和鉱業株式会社安芸津工場内 (72)発明者 水戸 洋彦 東京都渋谷区代々木3丁目1番2号 昭和 鉱業株式会社技術開発部内 Fターム(参考) 4H011 AC01 AC02 AC03 BA01 BB18 BB20 BC18 BC20 ────────────────────────────────────────────────── ─── Continuing on the front page (72) Inventor Shigeki Yokoyama 5563, Sakakiyama, Mitsu, Atsutsu-cho, Toyota-gun, Hiroshima Prefecture Inside the Akizu Plant of Showa Mining Co., Ltd. (72) Inventor Hirohiko Mito 3-1-1 Yoyogi, Shibuya-ku, Tokyo No. 2 Showa Mining Co., Ltd. Technology Development Department F-term (reference) 4H011 AC01 AC02 AC03 BA01 BB18 BB20 BC18 BC20
Claims (6)
マナイト粒子であることを特徴とした床下害虫防除剤。1. An underfloor pest control agent, wherein 90% by weight or more of the colemanite particles have a diameter of 0.01 to 6.5 mm.
くは径1.0〜3.0mmのコレマナイト粒子であることを特
徴とした床下害虫防除剤。2. An underfloor pest control agent, wherein 95% by weight or more of the colemanite particles have a diameter of 0.9 to 4.5 mm, preferably 1.0 to 3.0 mm.
しくは径0.01〜0.8mmのコレマナイト粒子であること
を特徴とした床下害虫防除剤。3. An underfloor pest control agent, wherein 95% by weight or more are colemanite particles having a diameter of 0.01 to 1.5 mm, preferably 0.01 to 0.8 mm.
ャイト、シリカゲル、珪藻土、鹿沼土、木炭のような多
孔質粉粒材に請求項1〜3の何れか1つに記載した防除
剤を2〜50wt%配合したことを特徴とする床下害虫防
除剤。4. A porous powdery material such as zeolite, sepiolite, attapulgite, silica gel, diatomaceous earth, Kanuma earth, charcoal, and 2 to 50% by weight of the controlling agent according to any one of claims 1 to 3. An underfloor pest control agent, characterized in that:
マナイト粒子を地層上の必要部位に厚さ0.8cm以上の層
として形成することを特徴とする床下害虫防除方法。5. A method for controlling underfloor pests, comprising forming colemanite particles having a diameter of 0.01 to 6.5 mm at 95% by weight or more as a layer having a thickness of 0.8 cm or more at a required site on a formation.
くは0.8〜4.5mmのコレマナイト粒子を地層上の必要部
位に厚さ1cm以上の層として形成することを特徴とする
床下害虫防除方法。6. A method of forming colemanite particles having a diameter of 0.6 to 6.5 mm, preferably 0.8 to 4.5 mm, in a thickness of 1 cm or more at a required portion on the formation, wherein 90% by weight or more is formed. Underfloor pest control method.