DE1264923B

DE1264923B - Process for applying a non-slip covering to the floor of enamelled bathtubs and shower trays

Info

Publication number: DE1264923B
Application number: DE1965A0051146
Authority: DE
Inventors: Dipl-Ing Dr Guenter Gesche; Erich Ebeling
Original assignee: Ahlmanni Carlshuette K G
Current assignee: Ahlmanni Carlshuette K G
Priority date: 1965-12-22
Filing date: 1965-12-22
Publication date: 1968-03-28

Description

BUNDESREPUBLIK DEUTSCHLANDFEDERAL REPUBLIC OF GERMANY

DEUTSCHESGERMAN

PATENTAMTPATENT OFFICE

AUSLEGESCHRIFTEDITORIAL

Int. Cl.:Int. Cl .:

C23dC23d

Deutschs Kl.: 48 c -13/00 German class: 48 c -13/00

Nummer: 1264 923Number: 1264 923

Aktenzeichen: Ä 51145 VI b/48cFile number: Ä 51145 VI b / 48c

Anmeldetag: 22. Dezember 1965Filing date: December 22, 1965

Auslegetag: 28. März 1968Opening day: March 28, 1968

Die Erfindung betrifft ein Verfahren zum Aufbringen eines rutschfesten Belages auf den Boden von emaillierten Bade- und Brausewannen.The invention relates to a method for applying a non-slip covering to the floor of enamelled bathtubs and shower trays.

Die üblichen emaillierten Badewannen haben den Nachteil, daß der Boden sehr glatt ist Und der Badende beim Aufstehen leicht ausrutschen kann.The usual enamelled bathtubs have the disadvantage that the floor is very smooth and the bather Slip easily when standing up.

Zur Vermeidung dieses Nachteiles hat man bereits dem Trägermetall der Wanne an den gewünschten Stellen eine bestimmte Profilierung gegeben. Das geschah beim Gießen einfach dadurch, daß die Formplatte mit einem entsprechenden Muster versehen wurde. Bei Verwendung von Stahlblech als Emailträger wurden die Präge- oder Ziehwerkzeuge mit Profilierungen versehen, die in dem Metall die entsprechenden Musterungen einprägten. Wenn auch die Bodenprofilierung nach dem Emaillieren erhalten " bleibt, so ist deren Oberfläche jedoch insgesamt so glatt, daß die Rutschgefähr dadurch kaum gemindert wird.To avoid this disadvantage, the carrier metal of the tub has already been attached to the desired one Make a certain profiling given. That happened when pouring simply by the fact that the mold plate has been provided with a corresponding pattern. When using sheet steel as an enamel support the embossing or drawing tools were provided with profiles, the corresponding in the metal Imprint patterns. Even if the floor profiling is preserved after enamelling "remains, so its surface is overall like that smooth so that the risk of slipping is hardly reduced.

Man hat außerdem versucht, das Problem durch nachträgliches Aufkleben von auf der Oberfläche rauhen Kunststoffstreifen zu lösen. Diese Streifen sind zwar rutschfester als emaillierte Metallmusterungen, aber ihre Dicke und die Ungenauigkeit der Aufklebung beeinträchtigen das Aussehen der Badewanne und können auch infolge des artfremden Werkstoffes nur ein Behelf sein.Attempts have also been made to remedy the problem by subsequently sticking the to loosen rough plastic strips. Although these strips are more slip-resistant than enameled metal patterns, but their thickness and the imprecision of the pasting spoil the appearance of the bathtub and can only be a makeshift because of the foreign material.

Es ist auch schon ein Verfahren bekannt, wonach man auf emaillierte oder glasierte Flächen erhabene Muster aus Email oder Glasurmasse aufgebracht und eingebrannt hat. Darüber hinaus hat man Bade- und Brausewannen mit rutschfesten Belägen versehen, indem man auf das mit dem Grundemail bedeckte Metall zunächst eine leicht schmelzbare Emailschicht und dann eine aus schwer oder nicht schmelzbaren Stoffen bestehende plastische Masse beliebig, unter Anwendung von Schablonen oder von Hand geformt, aufgetragen und das Ganze durch Brennen fest miteinander verbunden hat. Nachteilig hierbei ist aber, daß nach dem Auftragen der den Belag bildenden Substanz diese noch eingebrannt werden muß.There is also already a known method, according to which one raised on enamelled or glazed surfaces Applied and burned in patterns made of enamel or glaze mass. In addition, one has bathing and bathing Provide shower trays with non-slip coverings by covering them with the basic enamel Metal first has an easily meltable enamel layer and then one made of difficult or non-meltable Any plastic material existing, formed using templates or by hand, applied and firmly bonded the whole thing together by firing. However, the disadvantage here is that after the substance that forms the coating has been applied, it still has to be burned in.

Der vorliegenden Erfindung liegt daher die Aufgabe zugrunde, ein Verfahren zum Aufbringen eines rutschfesten Belages auf den Boden von emaillierten Bade- und Brausewannen zu schaffen, bei welchem ein nachträgliches Einbrennen des Belages nicht erforderlich ist.The present invention is therefore based on the object of a method for applying a to create non-slip covering on the floor of enamelled bathtubs and shower trays, which a subsequent burn-in of the covering is not necessary.

Somit betrifft die vorliegende Erfindung ein Verfahren zum Aufbringen eines rutschfesten Belages auf den Boden von emaillierten Bade- und Brausewannen durch Aufspritzen einer feuerfesten Substanz auf die freien Oberflächen des mit einer Schablone bedeck-Verfahren zum Aufbringen eines rutschfesten
Belages auf den Boden von emaillierten Bade-
und BrausewannenThus, the present invention relates to a method for applying a non-slip covering to the floor of enamelled bathtubs and shower trays by spraying a fireproof substance onto the free surfaces of the method for applying a non-slip covering with a stencil
On the floor of enamelled bath
and shower trays

Anmelder:Applicant:

Ahlmann — Carlshütte K. G., 2370 RendsburgAhlmann - Carlshütte K. G., 2370 Rendsburg

Als Erfinder benannt:. .
Dipl.-Ing. Dr. Günter Gesehe,
Erich Ebeling, 2370 BüdelsdorfNamed as inventor :. .
Dipl.-Ing. Dr. Günter Gesehe,
Erich Ebeling, 2370 Büdelsdorf

ten Wannenbodens. Es ist dadurch gekennzeichnet, daß die feuerfeste Substanz in breiigem oder flüssigem Zustand in einer Brenngas-Sauerstoff-Flamme während des Aufspritzens auf den kalten oder heißen Wannenboden geschmolzen wird.th tub bottom. It is characterized in that the refractory substance in pulpy or liquid Condition in a fuel gas-oxygen flame during spraying on the cold or hot The bottom of the pan is melted.

Zur Durchführung des Verfahrens wird die fertig emaillierte Wanne mit einer im Bereich des Bodens ausgeschnittenen Schablone bedeckt und die feuerfeste Substanz auf die freien Bodenflächen z. B. mit' einer an sich bekannten Spritzpistole oder einer automatischen Spritzvorrichtung aufgebracht; der Abstand zwischen Spritzpistole und der zu behandelnden Oberfläche sowie die Zeitdauer des Aufspritzens kann je nach der gewünschten Intensität des Auftrages und der dadurch erzielten Rauhigkeit variiert werden. Die feuerfeste Substanz wird in der heißen Brenngas-Sauerstoff-Flamme der Spritzvorrichtung geschmolzen, mittels Preßluft zerstäubt und auf die freie Emailfläche aufgetragen. Die feinen teigigen bis flüssigen Teilchen bleiben bei dem Auftreffen auf die Emailschicht auf dieser haften und bilden nach dem Erstarren eine rauhe, rutschfeste Fläche. Da das geschmolzene Gut von einem starken Luftstrom begleitet wird, erfolgt keine wesentliche Erwärmung des Grundemails, auf das der Belag aufgetragen wird. Ein erneutes Einschmelzen des Emails und die damit verbundene Glättung der Oberfläche wird somit vermieden.To carry out the process, the finished enamelled tub is fitted with one in the area of the floor cut template covered and the refractory substance on the free floor surfaces z. B. with ' applied to a known spray gun or an automatic spray device; the distance between the spray gun and the surface to be treated and the duration of the spraying can be varied depending on the desired intensity of the order and the roughness achieved thereby. the refractory substance is melted in the hot fuel gas-oxygen flame of the spray device, atomized by means of compressed air and applied to the free enamel surface. The fine doughy to liquid When they hit the enamel layer, particles stick to it and form after Solidify a rough, non-slip surface. Since the molten material is accompanied by a strong flow of air, there is no significant heating of the base enamel on which the covering is applied. A renewed melting of the enamel and the associated smoothing of the surface is thus avoided.

Der Wegfall des Einbrennens nach dem Aufbringen des Belages stellt sowohl vom technischen als auch vom wirtschaftlichen Standpunkt aus gesehen einen erheblichen Fortschritt dar. Durch den Fortfall einer Arbeitsstufe wird die Herstellung der mit rutschfesten Belägen versehenen Wannen sehr vereinfacht, und Zeit-, Kosten- und Arbeitsaufwand werden wesentlich herabgesetzt.The elimination of baking after the covering has been applied represents both a technical and a from an economic point of view, too, represents a considerable advance one work step, the production of the tubs provided with non-slip coverings is very much simplified, and time, cost, and labor are significantly reduced.

809 520/384809 520/384

Bei empfindlichen Emails können sich nach dem Aufspritzen auf die kalte Wanne im Verlauf des Verfahrens Risse bilden. Um diesen Nachteil zu vermeiden, wird in solchen Fällen der Belag auf die noch heiße Wanne aufgespritzt. Nach einer-besonderen Ausführungsfopn der Erfindung wird beim Aufspritzen auf den heißen Wannenboden die Wanne vor dem Aufspritzen des Belages zur thermischen Isolierung in einen kastenartigen Rahmen eingesetzt. Dieser Rahmen hat die Aufgabe, die Temperatur der von der Emaillierung noch heißen Wanne möglichst konstant zu halten, damit während des Auftragens keine Risse in der Emailoberfläche entstehen und die aufgespritzte feuerfeste Substanz auf der Emailoberfläche gut haftet.In the case of sensitive enamels, after spraying onto the cold tub during the Procedure cracks form. In order to avoid this disadvantage, the covering is placed on the still hot tub sprayed on. According to a special embodiment of the invention, during spraying on the hot tub floor before spraying the topping for thermal Insulation set in a box-like frame. The purpose of this framework is to monitor the temperature of the Keep the hot tub as constant as possible from the enamelling, so during the application there are no cracks in the enamel surface and the sprayed-on refractory substance on the enamel surface adheres well.

Nach einer weiteren bevorzugten Ausführungsform der Erfindung wird als feuerfeste Substanz wenigstens ein Metalloxyd und/oder eine keramische Masse bzw. Tonerde oder Emailpulver aufgespritzt. Zweckmäßigerweise wählt man eine Substanz, die ohnehin Bestandteil der Emailmässe ist, doch können auch andere Stoffe, wie Quarz oder Feldspat, eingesetzt werden.According to a further preferred embodiment of the invention, the refractory substance is at least a metal oxide and / or a ceramic mass or alumina or enamel powder is sprayed on. Appropriately If you choose a substance that is already part of the enamel, but you can too other substances such as quartz or feldspar can be used.

Nach einer besonderen Ausführungsform der Erfindung werden der feuerfesten Substanz feuerfeste Pigmente zugesetzt. Man erhält auf diese Weise einen farbigen rutschfesten Belag, der auch durch eine in der Wanne befindliche Wassersäule gut sichtbar ist. Darüber hinaus können ein- und mehrfarbige Dekors auf die Emailoberfläche aufgebracht werden. Bisher mußten die Emails nach Auftragen der Dekors durch Abziehbilder oder eine Farbspritzpistole ein zweites Mal gebrannt werden. Diese Arbeitsweise war insbesondere bei Puderemaillierungen mit Nachteilen behaftet, da sich beim Einbrennen häufig Risse bildeten. Bei dem erfindungsgemäßen Aufspritzen einer gefärbten feuerfesten geschmolzenen Substanz erübrigt sich das nachträgliche Einbrennen.According to a particular embodiment of the invention, the refractory substances are refractory Pigments added. In this way, a colored, non-slip covering is obtained, which is also covered by an in the water column located in the tub is clearly visible. In addition, single and multi-colored decorations can be used can be applied to the enamel surface. Previously, the emails had to go through after the decorations were applied Decals or a paint spray gun can be fired a second time. This way of working was special with powder enamelling with disadvantages tainted, as cracks often formed during baking. When spraying according to the invention a colored refractory molten substance does not require subsequent baking.

Nach dem erfindungsgemäßen Verfahren können auf die freien Bodenflächen der Wanne auch Metalle aufgespritzt werden. Als solche kommen z. B. Nickel, Kobalt oder Kupfer in Frage.. .According to the method according to the invention, metals can also be used on the free bottom surfaces of the tub be sprayed on. As such come z. B. nickel, cobalt or copper in question ...

Das erfindungsgemäße Verfahren erstreckt sich ganz allgemein auf die Herstellung rutschfester Beläge auf emaillierten Gegenständen. Als feuerfeste Substanz sind alle Stoffe geeignet, die in einer heißen Flamme, aufgeschmolzen bzw. zähflüssig' gemaeht werden können und auf der Emailschicht haften bleiben. Im allgemeinen wird die feuerfeste Substanz mit einer in der Emailindustrie üblichen Kornfeinheit verwendet, d. h. die Korngrößen liegen unter 0,1 mm.The method according to the invention extends quite generally to the production of non-slip coverings on enamelled objects. All substances that are hot in one are suitable as a refractory substance Flame, melted or viscous' machined and adhere to the enamel layer stay. In general, the refractory substance is made with a grain fineness common in the enamel industry used, d. H. the grain sizes are less than 0.1 mm.

Claims

Patent claims:

1. Method of applying a non-slip covering to the floor of enamelled Bathtubs and shower trays by spraying a fire-resistant substance onto the free surfaces of the tub bottom covered with a 'template, characterized in that the refractory substance in pulpy or liquid state in a fuel gas-oxygen flame during spraying on the cold one or hot tub bottom is melted.

2. The method according to claim 1, characterized in that when spraying onto the hot tub bottom the tub before the coating is sprayed on for thermal insulation is inserted into a box-like frame.

3. The method according to claim 1 or 2, characterized in that at least as a refractory substance a metal oxide and / or a ceramic mass or alumina or enamel powder is sprayed on.

4. The method according to any one of claims 1 to 3, characterized in that the refractory Substance refractory pigments are added.