CN1896023A - Production of color-enamel sand - Google Patents
Production of color-enamel sand Download PDFInfo
- Publication number
- CN1896023A CN1896023A CN 200510041035 CN200510041035A CN1896023A CN 1896023 A CN1896023 A CN 1896023A CN 200510041035 CN200510041035 CN 200510041035 CN 200510041035 A CN200510041035 A CN 200510041035A CN 1896023 A CN1896023 A CN 1896023A
- Authority
- CN
- China
- Prior art keywords
- color
- glaze
- enamel
- production method
- basalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Production of glazed colored sand is carried out by compounding ceramic frit and ceramic pigment proportionally, adding into water and latent solvent, mixing, ball grinding to produce frit, agitating frit with dried basalt and calcining in high-temperature kiln. It has high silicon content, better high-temperature resistance and adsorptive performance and no fading.
Description
Affiliated technical field
The present invention relates to a kind of production method of material of construction, particularly be used for the production method of brick wall surface-treated color-enamel sand.
Background technology
The color-enamel sand that is used at present brick wall performance processing both at home and abroad is to utilize Chinese pottery glaze Technology, form through sintering, the choosing difference of raw materials for sintering adopted different production methods, useful quartzite sand burning on the market, but quartz sand the secondary thermal expansion can occur when temperature surpasses about 530 ℃ in making processes, makes product slight crack occur; Also useful grouan sintering, but granite sand temperature in sintering process can soften 800 ℃ of left and right sides Shi Shi matter, the production method of these two kinds of color-enamel sands can cause all that color-enamel sand is strong to the surface adhesion force of wall brick, color comes off easily.
Summary of the invention
The present invention is the deficiency that overcomes above-mentioned technology, and the production method of the more stable color-enamel sand of a kind of performance is provided.
The technical scheme that the present invention takes is: prepare in proportion earlier, add an amount of water and solubility promoter and mix, behind ball milling, make glaze with ceramic clinker and beramic color, again with the basalt stirring of the glaze made and oven dry after High-temp. kiln be sintered into.
The present invention utilizes silicon content height, high temperature resistant, the basalt that there is pore on the surface and the glaze sintering of making, and makes the color-enamel sand adsorptive power strong, and is bright-colored and do not fade.
Embodiment 1
With ceramic clinker and beramic color be by weight percentage: ceramic clinker 50%: the ratio preparation of beramic color 3%, it is mixed to add an amount of water and solubility promoter, put into the ball mill ball milling, the ball milling time is 10 hours, is made into glaze with conventional ceramic glaze technology.With the basalt of above-mentioned glaze of making and oven dry be by weight percentage: glaze 5%, basalt 85% stirs, and puts into the High-temp. kiln calcining, and calcining temperature is 700 ℃, and calcination time is to obtain 12～40 purpose color-enamel sands after 4 hours.
Embodiment 2
With ceramic clinker and beramic color be by weight percentage: ceramic clinker 60%: the ratio preparation of beramic color 5%, it is mixed to add an amount of water and solubility promoter, put into the ball mill ball milling, the ball milling time is 15 hours, is made into glaze with conventional ceramic glaze technology.With the basalt of above-mentioned glaze of making and oven dry be by weight percentage: glaze 10%, basalt 90% stirs, and puts into the High-temp. kiln calcining, and calcining temperature is 800 ℃, and calcination time is to obtain 12～40 purpose color-enamel sands after 4 hours.
Embodiment 3
With ceramic clinker and beramic color be by weight percentage: ceramic clinker 70%: the ratio preparation of beramic color 6%, it is mixed to add an amount of water and solubility promoter, put into the ball mill ball milling, the ball milling time is 20 hours, is made into glaze with conventional ceramic glaze technology.With the basalt of above-mentioned glaze of making and oven dry be by weight percentage: glaze 15%, basalt 95% stirs, and puts into the High-temp. kiln calcining, and calcining temperature is 1000 ℃, and calcination time is to obtain 12～40 purpose color-enamel sands after 4 hours.
Claims (4)
1, a kind of production method of color-enamel sand, it is characterized in that: prepare in proportion with ceramic clinker and beramic color earlier, it is mixed to add an amount of water and solubility promoter, makes glaze behind ball milling, again with the basalt stirring of the glaze made and oven dry after High-temp. kiln be sintered into.
2, the production method of color-enamel sand according to claim 1, it is characterized in that: the weight percent of described ceramic clinker, beramic color is: ceramic clinker 50～70%: beramic color 3～6%, glaze of making and basaltic weight percent are: glaze 5～15%, basalt 85～95%.
3, the production method of color-enamel sand according to claim 1 is characterized in that: described calcining temperature is 700～1000 ℃.
4, the production method of color-enamel sand according to claim 1 is characterized in that: the described ball milling time is 10～20 hours, and calcination time is 4.