CN112480519A - Production method of cinerary casket storage rack with antibacterial function - Google Patents
Production method of cinerary casket storage rack with antibacterial function Download PDFInfo
- Publication number
- CN112480519A CN112480519A CN202011454230.7A CN202011454230A CN112480519A CN 112480519 A CN112480519 A CN 112480519A CN 202011454230 A CN202011454230 A CN 202011454230A CN 112480519 A CN112480519 A CN 112480519A
- Authority
- CN
- China
- Prior art keywords
- cinerary casket
- storage rack
- casket storage
- welding
- antibacterial function
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of a cinerary casket storage rack with an antibacterial function, which comprises the following steps: s1: selecting raw materials; s2: mixing; s3: molding; s4: cooling; s5: mechanically finishing; s6: surface treatment; s7: processing and finishing; s8: welding and assembling; s9: the welding treatment is characterized in that the cinerary casket storage rack is made of plastic, the antibacterial agent is added into the plastic for making the cinerary casket storage rack, the plastic material is convenient to weld, the structure is compact, the toughness is high, the antibacterial agent is non-conductive and not easy to corrode, microorganisms cannot be generated on the surface of the cinerary casket storage rack, mildew cannot be generated on the surface of the cinerary casket storage rack, the appearance of the cinerary casket storage rack is greatly improved, compared with the cinerary casket storage rack made by the existing cinerary casket storage rack making method, the cinerary casket storage rack is stable in structure, the surface is still attractive after long-term use, the mildew cannot be generated due to environmental problems, the cinerary casket cannot be corroded due to bacteria breeding, and the service life of the cinerary casket is prolonged.
Description
Technical Field
The invention relates to the technical field of funeral article manufacturing, in particular to a production method of a cinerary casket storage rack with an antibacterial function.
Background
The funeral equipment includes coffin material, cold storage, ash depositing rack, cremation machine, production equipment and material.
In the field of manufacturing of cinerary casket storage racks, most of cinerary casket storage racks in the existing manufacturing method of cinerary casket storage racks do not have a sterilization effect, so that a large number of microorganisms are bred on the cinerary casket storage racks, mildew spots are generated on the cinerary casket storage racks, the appearance is influenced, the stored cinerary casket is easily corroded, and the service life of the cinerary casket is shortened.
Disclosure of Invention
The invention aims to provide a production method of a cinerary casket storage rack with an antibacterial function, the cinerary casket storage rack is made of plastics, an antibacterial agent is added into the plastic for making the cinerary casket storage rack, the plastic material is convenient to weld, the structure is compact, the toughness is high, the plastic material is non-conductive and is not easy to corrode, the antibacterial agent is added, microorganisms cannot be generated on the surface of the cinerary casket storage rack, mildew cannot be generated on the surface of the cinerary casket storage rack, the appearance of the cinerary casket storage rack is greatly improved, compared with the cinerary casket storage rack prepared by the existing cinerary casket storage rack making method, the cinerary casket storage rack is stable in structure, the surface is still attractive after long-term use, the mildew cannot be generated due to environmental problems, the cinerary casket cannot be corroded due to breeding bacteria, the service life of the cinerary casket is prolonged, and the problems raised in the background technology are solved.
In order to achieve the purpose, the invention provides the following technical scheme: a production method of a cinerary casket storage rack with an antibacterial function comprises the following steps:
s1: selecting raw materials, namely selecting raw materials of the cinerary casket storage rack with the antibacterial function as prepared basic raw materials, wherein the raw materials of the cinerary casket storage rack with the antibacterial function comprise chitin in percentage by weight: 0.6-1%, titanium dioxide: 0.6-0.8%, cinnamon essential oil: 0.3-0.7%, horseradish essential oil: 1-1.4%, silver oxide: 0.6-1%, diethyl phthalate: 1-1.4%, zinc borate: 2.5-3.5%, cedar oil: 0.6-1%, polyimide: 0.6-1%, sodium lauramide ethyl sulfate: 0.7-1.2%, zirconium phosphate: 0.8-1%, bamboo leaf phenolic ketone: 0.4-0.8%, wollastonite fiber: 0.6-1%, antibacterial additive: 1-1.5 percent of polyethylene and the balance of polyethylene;
s2: mixing, namely sequentially adding the raw materials selected in the step S1 into a smelting furnace, and simultaneously mechanically stirring, wherein the smelting temperature of the smelting furnace is guaranteed to be 195-210 ℃ during stirring, and smelting into molten materials for later use;
s3: molding, namely performing solid solution on the material mixed in the step S2 for 1-2h at the temperature of 100-120 ℃, and then preparing the solid-dissolved material into plate-shaped plastic;
s4: cooling, namely cooling the plastic plate molded in the step S3;
s5: mechanical trimming, namely mechanically trimming the cooled plate-type plastic, and removing burrs during the molding of the plastic plate;
s6: surface treatment, namely performing surface polishing treatment on the mechanically trimmed plastic plate;
s7: machining and finishing, namely machining the plastic plate after the surface treatment is finished to form a plate of the cinerary casket storage rack, and finishing the section of the plate;
s8: welding, assembling and welding the manufactured boards of the cinerary casket storage rack after finishing trimming.
S9: and (4) welding, namely finishing the protruding part of the welding part after welding and assembling are finished, and thus obtaining the cinerary casket storage rack with the antibacterial function.
Preferably, the preparation method of the antibacterial additive comprises the following steps: mixing silicon dioxide 16-20%, kaolin 15-18%, zinc borate 12-15%, Chinese herbal medicine 5-10% and water 37-52%, decocting, and filtering to obtain the antibacterial additive.
Preferably, the Chinese herbal medicine contains 9-10% of nutgrass flatsedge, 5-6% of branches of merchant, 5-6% of ligusticum sinense oliver, 10-11% of rhizoma arisaematis, 6-7% of radix bupleuri, 5-6% of cortex toonae sinensis, 6-7% of rhizoma cyrtomii, 7-8% of evodia lepta, 10-11% of pyrrosia lingua, 7-8% of schisandra chinensis, 8-9% of murraya paniculata, 9-10% of pangolin nails and the balance of semen strychni.
Preferably, the plastic sheet is formed in step S3 by extrusion molding, and the die temperature is 175-190 ℃.
Preferably, the plate is cooled by air cooling in the step S4, and the cooling time is 0.5 to 1 hour.
Preferably, the polishing method in step S6 is polishing by chemical polishing.
Preferably, the welding method in step S8 is welding with a welding rod, when the welding rod is used, the end face of the welded end is made into a seam with a certain shape, the welding rod melt drips into the seam, and the two welded parts are connected into a whole.
Preferably, the deburring method in the mechanical trimming in the step S5 is to perform deburring by using a high-pressure water jet method.
Preferably, the welding process in step S9 includes cutting, grinding and polishing.
Compared with the prior art, the invention has the beneficial effects that: the manufacturing method of the cinerary casket storage rack with the antibacterial function is strictly controlled, and the high and low temperature resistance, the structural strength and the antibacterial performance of the material can be obviously improved by strictly controlling the manufacturing process parameters of the cinerary casket storage rack with the antibacterial function and adding chitin, titanium dioxide, cinnamon essential oil, horseradish essential oil, silver oxide, diethyl phthalate, zinc borate, cedar wood oil, polyimide, lauramide ethyl sodium sulfate, zirconium phosphate, bamboo leaf phenolic ketone, wollastonite fiber material and antibacterial additive. This cinerary casket is deposited and the structure is fine and close, toughness is high, it is not electrically conductive, be difficult for by the corruption, antibiotic effect, make cinerary casket storage rack surface can not produce the microorganism, cinerary casket storage rack surface can not produce the mildew, make this cinerary casket storage rack's outward appearance promote greatly, it is firm to compare the cinerary casket storage rack structure that current cinerary casket storage rack preparation method prepared, the surface is still pleasing to the eye after long-term the use, can not produce the mildew because of environmental problem, make cinerary casket can not lead to the box body to be corroded because of breeding the bacterium, cinerary casket's life has been increased.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is further described in detail with reference to the following embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
The invention provides a method for producing a cinerary casket storage rack with an antibacterial function, which comprises the following raw materials in percentage by weight and specific embodiment data as shown in the following table 1:
the weight percentages and specific example data of the components in the Chinese herbal medicines in the raw materials are as follows:
example 1
A production method of a cinerary casket storage rack with an antibacterial function comprises the following steps:
s1: selecting raw materials, namely selecting raw materials of the cinerary casket storage rack with the antibacterial function as prepared basic raw materials, wherein the raw materials of the cinerary casket storage rack with the antibacterial function comprise chitin in percentage by weight: 0.6%, titanium dioxide: 0.6%, cinnamon essential oil: 0.3%, horseradish essential oil: 1%, diethyl phthalate: 1, zinc borate: 2.5%, cedar oil: 0.6%, polyimide: 0.6%, antimicrobial additive: 1%, and polyethylene 91.8%;
s2: mixing, namely sequentially adding the raw materials selected in the step S1 into a smelting furnace, and simultaneously mechanically stirring, wherein the smelting temperature of the smelting furnace is guaranteed to be 195 ℃ during stirring, and smelting into a molten material for later use;
s3: molding, namely dissolving the material mixed in the step S2 in a solid manner for 1 hour at the temperature of 100 ℃, and then preparing the material subjected to solid solution into a plate-shaped plastic;
s4: cooling, namely cooling the plastic plate molded in the step S3;
s5: mechanical trimming, namely mechanically trimming the cooled plate-type plastic, and removing burrs during the molding of the plastic plate;
s6: surface treatment, namely performing surface polishing treatment on the mechanically trimmed plastic plate;
s7: machining and finishing, namely machining the plastic plate after the surface treatment is finished to form a plate of the cinerary casket storage rack, and finishing the section of the plate;
s8: welding, assembling and welding the manufactured boards of the cinerary casket storage rack after finishing trimming.
S9: and (4) welding, namely finishing the protruding part of the welding part after welding and assembling are finished, and thus obtaining the cinerary casket storage rack with the antibacterial function.
The preparation method of the antibacterial additive comprises the following steps: mixing silicon dioxide 16%, kaolin 15%, zinc borate 12%, Chinese herbal medicine 5% and water 52%, decocting, filtering to obtain the antibacterial additive, wherein the Chinese herbal medicine contains Cyperus rotundus 9%, Phytolacca acinosa 5%, Artemisia annua 5%, arisaema consanguineum 10%, Bupleurum chinense 6%, Centratheria sinensis 6%, evodia lepta 7%, Pyrrosia microphylla 10%, Schisandra chinensis 7%, Murrayamine 8%, Shanzhui 9%, and semen Strychni 13%, the plastic sheet molding in step S3 adopts an extrusion molding mode, the die head temperature is 175 ℃, the cooling mode of the sheet in step S4 adopts air cooling, the cooling time is 0.5h, the polishing method in step S6 adopts chemical polishing, the welding method in step S8 adopts welding rod welding, when welding rods are used, the end face of the welded end is made into a seam with a fixed shape, the welding rods are dripped into the seam, two welded pieces are connected into a whole, the deburring method in the step S5 mechanical trimming adopts a high-pressure water jet method to perform deburring, and the welding processing mode in the step S9 comprises cutting, grinding and polishing.
Example 2
A production method of a cinerary casket storage rack with an antibacterial function comprises the following steps:
s1: selecting raw materials, namely selecting raw materials of the cinerary casket storage rack with the antibacterial function as prepared basic raw materials, wherein the raw materials of the cinerary casket storage rack with the antibacterial function comprise chitin in percentage by weight: 0.8%, titanium dioxide: 0.7%, cinnamon essential oil: 0.5%, horseradish essential oil: 1.2%, diethyl phthalate: 1.2%, zinc borate: 3%, cedar oil: 0.8%, polyimide: 0.8%, antimicrobial additive: 1.3 percent of polyethylene and 89.7 percent of polyethylene;
s2: mixing, namely sequentially adding the raw materials selected in the step S1 into a smelting furnace, and simultaneously mechanically stirring, wherein the smelting temperature of the smelting furnace is ensured to be 203 ℃ during stirring, and smelting into a molten material for later use;
s3: molding, namely dissolving the material mixed in the step S2 for 1.5h at 110 ℃, and then preparing the material subjected to solution into a plate-shaped plastic;
s4: cooling, namely cooling the plastic plate molded in the step S3;
s5: mechanical trimming, namely mechanically trimming the cooled plate-type plastic, and removing burrs during the molding of the plastic plate;
s6: surface treatment, namely performing surface polishing treatment on the mechanically trimmed plastic plate;
s7: machining and finishing, namely machining the plastic plate after the surface treatment is finished to form a plate of the cinerary casket storage rack, and finishing the section of the plate;
s8: welding, assembling and welding the manufactured boards of the cinerary casket storage rack after finishing trimming.
S9: and (4) welding, namely finishing the protruding part of the welding part after welding and assembling are finished, and thus obtaining the cinerary casket storage rack with the antibacterial function.
The preparation method of the antibacterial additive comprises the following steps: mixing 18% of silicon dioxide, 16.5% of kaolin, 13.5% of zinc borate, 8% of Chinese herbal medicines and 44% of water, decocting, filtering to obtain the antibacterial additive, wherein the Chinese herbal medicines comprise 9.5% of nutgrass flatsedge, 5.5% of branches of Shanghai, 5.5% of rhizoma arisaematis, 6.5% of radix bupleuri, 5.5% of cortex toonae sinensis, 6.5% of rhizoma Osmundae, 7.5% of evodia trifoliata, 10.5% of pyrrosia microphylla, 7.5% of schisandra chinensis, 8.5% of murraya paniculata, 9.5% of pangolin nail and 7% of semen strychni, the plastic plate is formed in the step S3 in an extrusion forming mode, the die head temperature is 180 ℃, the plate is cooled in an air cooling mode in the step S4, the cooling time is 0.8h, the polishing method in the step S6 adopts a chemical polishing method, the step S8 adopts welding rod for welding, when the welding rod is used, the end face of the welding rod is made, two welded pieces are connected into a whole, the deburring method in the step S5 mechanical trimming adopts a high-pressure water jet method to perform deburring, and the welding processing mode in the step S9 comprises cutting, grinding and polishing.
Example 3
A production method of a cinerary casket storage rack with an antibacterial function comprises the following steps:
s1: selecting raw materials, namely selecting raw materials of the cinerary casket storage rack with the antibacterial function as prepared basic raw materials, wherein the raw materials of the cinerary casket storage rack with the antibacterial function comprise chitin in percentage by weight: 1%, titanium dioxide: 0.8%, cinnamon essential oil: 0.7%, horseradish essential oil: 1.4%, diethyl phthalate: 1.4%, zinc borate: 3.5%, cedar oil: 1%, polyimide: 1%, antibacterial additive: 1.5%, and polyethylene 87.7%;
s2: mixing, namely sequentially adding the raw materials selected in the step S1 into a smelting furnace, and simultaneously mechanically stirring, wherein the smelting temperature of the smelting furnace is ensured to be 210 ℃ during stirring, and smelting into a molten material for later use;
s3: molding, namely performing solid solution on the material mixed in the step S2 for 2 hours at the temperature of 120 ℃, and then preparing the solid-dissolved material into plate-shaped plastic;
s4: cooling, namely cooling the plastic plate molded in the step S3;
s5: mechanical trimming, namely mechanically trimming the cooled plate-type plastic, and removing burrs during the molding of the plastic plate;
s6: surface treatment, namely performing surface polishing treatment on the mechanically trimmed plastic plate;
s7: machining and finishing, namely machining the plastic plate after the surface treatment is finished to form a plate of the cinerary casket storage rack, and finishing the section of the plate;
s8: welding, assembling and welding the plastic plates of the manufactured cinerary casket storage rack after finishing trimming.
S9: and (4) welding, namely finishing the protruding part of the welding part after welding and assembling are finished, and thus obtaining the cinerary casket storage rack with the antibacterial function.
The preparation method of the antibacterial additive comprises the following steps: mixing 20% of silicon dioxide, 18% of kaolin, 15% of zinc borate, 10% of Chinese herbal medicines and 37% of water, decocting, filtering to obtain the antibacterial additive, wherein the Chinese herbal medicines comprise 10% of nutgrass flatsedge, 6% of branches of Shanghai, 6% of rhizoma ligustici wallichii, 11% of rhizoma arisaematis, 7% of radix bupleuri, 6% of Ailanthus altissima, 7% of rhizoma cyrtomii, 8% of pyrrosia microphylla, 8% of Chinese magnoliavine fruit, 9% of Jireming, 10% of pangolin nail and 1% of semen strychni, the plastic plate is formed in the step S3 in an extrusion forming mode, the die head temperature is 190 ℃, the plate is cooled in the step S4 in an air cooling mode, the cooling time is 1h, the polishing method in the step S6 adopts a chemical polishing method, the welding method in the step S8 adopts welding rod welding, when welding rods are used, the end faces, two welded pieces are connected into a whole, the deburring method in the step S5 mechanical trimming adopts a high-pressure water jet method to perform deburring, and the welding processing mode in the step S9 comprises cutting, grinding and polishing.
In summary, the following steps: the manufacturing method of the cinerary casket storage rack with the antibacterial function is strictly controlled, and the high and low temperature resistance, the structural strength and the antibacterial performance of the material can be obviously improved by strictly controlling the manufacturing process parameters of the cinerary casket storage rack with the antibacterial function and adding chitin, titanium dioxide, cinnamon essential oil, horseradish essential oil, silver oxide, diethyl phthalate, zinc borate, cedar wood oil, polyimide, lauramide ethyl sodium sulfate, zirconium phosphate, bamboo leaf phenolic ketone, wollastonite fiber material and antibacterial additive. This cinerary casket is deposited and the structure is fine and close, toughness is high, it is not electrically conductive, be difficult for by the corruption, antibiotic effect, make cinerary casket storage rack surface can not produce the microorganism, cinerary casket storage rack surface can not produce the mildew, make this cinerary casket storage rack's outward appearance promote greatly, it is firm to compare the cinerary casket storage rack structure that current cinerary casket storage rack preparation method prepared, the surface is still pleasing to the eye after long-term the use, can not produce the mildew because of environmental problem, make cinerary casket can not lead to the box body to be corroded because of breeding the bacterium, cinerary casket's life has been increased.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (9)
1. A production method of a cinerary casket storage rack with an antibacterial function is characterized in that: the method comprises the following steps:
s1: selecting raw materials, namely selecting raw materials of the cinerary casket storage rack with the antibacterial function as prepared basic raw materials, wherein the raw materials of the cinerary casket storage rack with the antibacterial function comprise chitin in percentage by weight: 0.6-1%, titanium dioxide: 0.6-0.8%, cinnamon essential oil: 0.3-0.7%, horseradish essential oil: 1-1.4%, diethyl phthalate: 1-1.4%, zinc borate: 2.5-3.5%, cedar oil: 0.6-1%, polyimide: 0.6-1%, antibacterial additive: 1-1.5 percent of polyethylene and the balance of polyethylene;
s2: mixing, namely sequentially adding the raw materials selected in the step S1 into a smelting furnace, and simultaneously mechanically stirring, wherein the smelting temperature of the smelting furnace is guaranteed to be 195-210 ℃ during stirring, and smelting into molten materials for later use;
s3: molding, namely performing solid solution on the material mixed in the step S2 for 1-2h at the temperature of 100-120 ℃, and then preparing the solid-dissolved material into plate-shaped plastic;
s4: cooling, namely cooling the plastic plate molded in the step S3;
s5: mechanical trimming, namely mechanically trimming the cooled plate-type plastic, and removing burrs during the molding of the plastic plate;
s6: surface treatment, namely performing surface polishing treatment on the mechanically trimmed plastic plate;
s7: machining and finishing, namely machining the plastic plate after the surface treatment is finished to form a plate of the cinerary casket storage rack, and finishing the section of the plate;
s8: welding, assembling and welding the manufactured boards of the cinerary casket storage rack after finishing trimming.
S9: and (4) welding, namely finishing the protruding part of the welding part after welding and assembling are finished, and thus obtaining the cinerary casket storage rack with the antibacterial function.
2. The method for manufacturing the cinerary casket storage shelf with antibacterial function as claimed in claim 1, wherein: the preparation method of the antibacterial additive comprises the following steps: mixing silicon dioxide 16-20%, kaolin 15-18%, zinc borate 12-15%, Chinese herbal medicine 5-10% and water 37-52%, decocting, and filtering to obtain the antibacterial additive.
3. The method for manufacturing the cinerary casket storage shelf with antibacterial function as claimed in claim 2, wherein: the Chinese herbal medicine comprises 9-10% of nutgrass flatsedge, 5-6% of branches of merchant, 5-6% of ligusticum sinense oliver, 10-11% of rhizoma arisaematis, 6-7% of radix bupleuri, 5-6% of cortex toonae sinensis, 6-7% of cyrtomium rhizome, 7-8% of bitter orange trifoliate, 10-11% of pyrrosia lingua, 7-8% of schisandra chinensis, 8-9% of murraya paniculata, 9-10% of pangolin scales and the balance of semen str.
4. The method for manufacturing the cinerary casket storage shelf with antibacterial function as claimed in claim 1, wherein: the plastic plate is formed in step S3 by extrusion molding, and the die temperature is 175-190 ℃.
5. The method for manufacturing the cinerary casket storage shelf with antibacterial function as claimed in claim 1, wherein: and in the step S4, the plate is cooled by air cooling, and the cooling time is 0.5-1 h.
6. The method for manufacturing the cinerary casket storage shelf with antibacterial function as claimed in claim 1, wherein: the polishing method in step S6 is polishing by chemical polishing.
7. The method for manufacturing the cinerary casket storage shelf with antibacterial function as claimed in claim 1, wherein: the welding method in the step S8 is welding by adopting a welding rod, when the welding rod is used, the end face of the end to be welded is made into a joint with a fixed shape, the welding rod melt drips into the joint, and the two parts to be welded are connected into a whole.
8. The method for manufacturing the cinerary casket storage shelf with antibacterial function as claimed in claim 1, wherein: the deburring method in the mechanical trimming in the step S5 adopts a high-pressure water jet method to deburr.
9. The method for manufacturing the cinerary casket storage shelf with antibacterial function as claimed in claim 1, wherein: the welding process in step S9 includes cutting, grinding and polishing.