CN110330239A - A kind of processing technology of patterned single side abnormity doubling glass - Google Patents
A kind of processing technology of patterned single side abnormity doubling glass Download PDFInfo
- Publication number
- CN110330239A CN110330239A CN201910580796.5A CN201910580796A CN110330239A CN 110330239 A CN110330239 A CN 110330239A CN 201910580796 A CN201910580796 A CN 201910580796A CN 110330239 A CN110330239 A CN 110330239A
- Authority
- CN
- China
- Prior art keywords
- plate
- glass
- single side
- doubling
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of processing technology of patterned single side abnormity doubling glass provided by the invention, the following steps are included: the first film film is placed in the plane of single side special-shaped glass plate, positive deformation area of the pattern is formed in the middle part of the first web plate after overexposure, development, drying；Positive deformation pattern is obtained by printing flat glass support plate surface；Reversal deformation pattern is drawn out, the second film film is produced according to the shape of reversal deformation pattern；Reversal deformation area of the pattern is formed in the middle part of the second web plate after overexposure, development, drying；Reversal deformation pattern is obtained by printed glass backplate surface；Single side special-shaped glass plate, doubling plate, glass film plates are successively folded and obtain single side abnormity doubling glass after setting pressing.Processing technology of the invention, easy to operate, obtained single side abnormity doubling inside glass has a reversal deformation pattern, when viewing, under the double influence of material refraction and surface radian deviation, can visually go back the true shape of original pattern.
Description
Technical field
The present invention relates to glass working arts fields, and in particular to a kind of processing of patterned single side abnormity doubling glass
Technique.
Background technique
For Glass Craft, generally in order to improve its ornamental value, need to make decorative pattern, text or pattern inside it,
It is integrated glass by what is obtained after glass metal melting, cooling due to restricted, such as common float glass of glass processing procedure,
It is difficult to make decorative pattern etc. inside it.Then there is a kind of doubling glass, decorative pattern, text or pattern are first printed on glass bottom
On plate, then utilize doubling technique by special-shaped glass and glass film plates pressing and forming.However, since the surface of special-shaped glass is not advised
Then property is bent, and the refractive index of glass is generally 1.5 or so, so that decorative pattern, text of the people in terms of shaped face side internally
Or when pattern, under the double influence of material refraction and surface radian deviation, decorative pattern, text or the pattern meeting visually seen
A degree of deformation occurs, influences visual effect.
Summary of the invention
In view of the above problems, the present invention provides a kind of processing technology of patterned single side abnormity doubling glass, operation letter
Single, obtained single side abnormity doubling inside glass has a reversal deformation pattern, inclined in material refraction and surface radian when viewing
Under the double influence of difference, the true shape of original pattern can be visually gone back.
To achieve the above object, the present invention solves by the following technical programs:
A kind of processing technology of patterned single side abnormity doubling glass, comprising the following steps:
S1 produces the first film film according to pattern form；
S2 prepares single side special-shaped glass plate, the first web plate, one layer of photoresists is coated on the first web plate, by single side special-shaped glass plate
Special-shaped placed face down, then single side special-shaped glass plate is placed on the upside of the first web plate, makes the plane of single side special-shaped glass plate
It is parallel with the first web plate upper surface；
First film film is placed in the plane of single side special-shaped glass plate by S3, the photoresists edge after overexposure, development, drying
Hardening removes the unhardened photoresists in middle part, and positive deformation area of the pattern is formed in the middle part of the first web plate；
S4 prepares flat glass support plate, is printed on flat glass support plate using the first web plate, flat glass support plate surface obtains
Forward direction deformation pattern；
S5 draws out the reversal deformation pattern with its mirror image according to forward direction deformation pattern, and according to the shape system of reversal deformation pattern
Make the second film film；
S6 prepares the second web plate, and one layer of photoresists are coated on the second web plate, the first film film is placed on the second web plate, passes through
Photoresists border sclerosis after overexposure, development, drying removes the unhardened photoresists in middle part, is formed reversely in the middle part of the second web plate
Deform area of the pattern；
S7 prepares glass film plates, is printed on glass film plates using the second web plate, glass film plates surface obtains reversal deformation pattern；
S8 prepares doubling plate, and by single side special-shaped glass plate abnormity, face-up, glass film plates pattern layer is arranged upward, then by single side
Special-shaped glass plate, doubling plate, glass film plates successively fold set pressing after obtain single side abnormity doubling glass.
Specifically, the refractive index of the single side special-shaped glass plate is 1.5~1.55.
Specifically, the shaped face of the single side special-shaped glass plate is waveform curved surface.
Specifically, the doubling plate is PVB plate, refractive index 1.488.
Specifically, the doubling plate with a thickness of 0.5~0.7mm.
The beneficial effects of the present invention are:
A kind of processing technology of patterned single side abnormity doubling glass of the invention, can be completed by simple silk-screen process
Production, it is easy to operate, the principle reversely reflected is utilized and makes reversal deformation pattern in single side abnormity doubling inside glass, so that
People in terms of shaped face side internally when, material refraction and surface radian deviation double influence under, can be visually
The also true shape of original pattern.
Detailed description of the invention
Fig. 1 is the flow diagram of step S1~S5 in the present invention.
Fig. 2 is the flow diagram of step S6~S7 in the present invention.
Fig. 3 is the flow diagram of step S8 in the present invention.
Appended drawing reference are as follows: the first film film 1, single side special-shaped glass plate 2, the first web plate 3, positive deformation area of the pattern
31, flat glass support plate 4, positive deformation pattern 41, the second film film 5, the second web plate 6, reversal deformation area of the pattern 61, glass
Glass bottom plate 7, reversal deformation pattern 71, doubling plate 8.
Specific embodiment
Below with reference to embodiment and attached drawing, the present invention is described in further detail, but embodiments of the present invention are unlimited
In this.
It is as shown in Figs. 1-3:
A kind of processing technology of patterned single side abnormity doubling glass, comprising the following steps:
S1 produces the first film film 1 according to pattern form；
S2 prepares single side special-shaped glass plate 2, the first web plate 3, one layer of photoresists is coated on the first web plate 3, by single side abnormity glass
Then single side special-shaped glass plate 2 is placed in 3 upside of the first web plate, makes single side special-shaped glass plate by the special-shaped placed face down of glass plate 2
2 plane is parallel with 3 upper surface of the first web plate；
First film film 1 is placed in the plane of single side special-shaped glass plate 2 by S3, the photoresists side after overexposure, development, drying
Edge hardening removes the unhardened photoresists in middle part, and positive deformation area of the pattern 31 is formed in the middle part of the first web plate 3；
S4 prepares flat glass support plate 4, is printed on flat glass support plate 4 using the first web plate 3,4 surface of flat glass support plate
Obtain positive deformation pattern 41；
S5 draws out the reversal deformation pattern 71 with its mirror image according to forward direction deformation pattern 41, and according to reversal deformation pattern 71
Shape produces the second film film 5；
S6 prepares the second web plate 6, and one layer of photoresists are coated on the second web plate 6, the first film film 1 is placed in the second web plate 6
On, the photoresists border sclerosis after overexposure, development, drying removes the unhardened photoresists in middle part, 6 middle part shape of the second web plate
At reversal deformation area of the pattern 61；
S7 prepares glass film plates 7, is printed on glass film plates 7 using the second web plate 6,7 surface of glass film plates obtains reversal deformation
Pattern 71；
S8 prepares doubling plate 8, and by 2 abnormity of single side special-shaped glass plate, face-up, 7 pattern layer of glass film plates is arranged upward, then will
Single side special-shaped glass plate 2, doubling plate 8, glass film plates 7 are successively folded set pressing after obtain single side abnormity doubling glass, people are from different
When shape face side is seen to the reversal deformation pattern 71 of single side abnormity doubling inside glass, reflected in 2 material of single side special-shaped glass plate
Under the double influence of surface radian deviation, the true shape of original pattern can be visually gone back.
The refractive index of single side special-shaped glass plate 2 is 1.5~1.55, in order to reduce the refractive index due to materials at two layers as far as possible
The vision deviation of pattern position caused by difference, doubling plate 8 answer selective refraction rate and 2 refractive index close of single side special-shaped glass plate
Material, preferably, doubling plate 8 are PVB plate, refractive index 1.488, although PVB plate and single side special-shaped glass plate 2
Refractive index has minimum deviation, but general impacts are little, and PVB plate is more mature as the means of doubling material, can subtract
The technological parameters the time it takes such as temperature, pressure are adjusted when pressing less, improve production efficiency.
Preferably, the shaped face of single side special-shaped glass plate 2 is waveform curved surface.
In order to further avoid the refractive index difference bring vision due to single side special-shaped glass plate 2 and doubling plate 8
Influence, and both can guarantee the stability after pressing, preferably, doubling plate 8 with a thickness of 0.5~0.7mm.
Above embodiments only express one embodiment of the present invention, and the description thereof is more specific and detailed, but can not
Therefore limitations on the scope of the patent of the present invention are interpreted as.It should be pointed out that for those of ordinary skill in the art,
Without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to protection model of the invention
It encloses.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (5)
1. a kind of processing technology of patterned single side abnormity doubling glass, which comprises the following steps:
S1 produces the first film film (1) according to pattern form；
S2 prepares single side special-shaped glass plate (2), the first web plate (3), one layer of photoresists is coated on the first web plate (3), by single side
Single side special-shaped glass plate (2) is then placed on the upside of the first web plate (3), makes list by the special-shaped placed face down of special-shaped glass plate (2)
The plane of face special-shaped glass plate (2) is parallel with the first web plate (3) upper surface；
First film film (1) is placed in the plane of single side special-shaped glass plate (2) by S3, photosensitive after overexposure, development, drying
Glue border sclerosis removes the unhardened photoresists in middle part, forms positive deformation area of the pattern (31) in the middle part of the first web plate (3)；
S4 prepares flat glass support plate (4), is printed on flat glass support plate (4) using the first web plate (3), flat glass support plate
(4) surface obtains positive deformation pattern (41)；
S5 draws out the reversal deformation pattern (71) with its mirror image according to forward direction deformation pattern (41), and according to reversal deformation pattern
(71) shape produces the second film film (5)；
S6 prepares the second web plate (6), and one layer of photoresists are coated on the second web plate (6), the first film film (1) is placed in second
On web plate (6), the photoresists border sclerosis after overexposure, development, drying removes the unhardened photoresists in middle part, the second web plate
(6) middle part forms reversal deformation area of the pattern (61)；
S7 prepares glass film plates (7), is printed on glass film plates (7) using the second web plate (6), glass film plates (7) surface obtains
Reversal deformation pattern (71)；
S8 prepares doubling plate (8), and by single side special-shaped glass plate (2) abnormity, face-up, glass film plates (7) pattern layer is arranged upward,
Then single side special-shaped glass plate (2), doubling plate (8), glass film plates (7) are successively folded and obtains single side abnormity doubling glass after setting pressing
Glass.
2. a kind of processing technology of patterned single side abnormity doubling glass according to claim 1, which is characterized in that institute
The refractive index for stating single side special-shaped glass plate (2) is 1.5~1.55.
3. a kind of processing technology of patterned single side abnormity doubling glass according to claim 1, which is characterized in that institute
The shaped face for stating single side special-shaped glass plate (2) is waveform curved surface.
4. a kind of processing technology of patterned single side abnormity doubling glass according to claim 1, which is characterized in that institute
Stating doubling plate (8) is PVB plate, refractive index 1.488.
5. a kind of processing technology of patterned single side abnormity doubling glass according to claim 4, which is characterized in that institute
State doubling plate (8) with a thickness of 0.5~0.7mm.