CN110028731A - A kind of sole material and preparation method thereof of shock-absorbing rebound - Google Patents
A kind of sole material and preparation method thereof of shock-absorbing rebound Download PDFInfo
- Publication number
- CN110028731A CN110028731A CN201910359622.6A CN201910359622A CN110028731A CN 110028731 A CN110028731 A CN 110028731A CN 201910359622 A CN201910359622 A CN 201910359622A CN 110028731 A CN110028731 A CN 110028731A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- shock
- plastic grain
- eva
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of sole material and preparation method thereof of shock-absorbing rebound, preparing raw material includes main glue and rubber chemicals, and the main glue includes following components by weight percent: 80-95 parts of 7350M EVA of rubber-plastic grain, 5-20 parts of rubber-plastic grain POE；The rubber chemicals include following components by weight percent: 1-2 parts of zinc oxide, 0.5-1 parts of stearic acid, 2.5-2.8 parts of foaming agent, ripe dose 0-1.5 parts, 0.8 part of crosslinking agent fast.Preparation method includes with POE elastic material and EVA material for main glue, and after mixing according to a certain percentage, in mixer mixing, open mill mill controls certain temperature and crosslinking condition, the available sole material with damping and high rebound.
Description
Technical field
The present invention relates to the sole materials and preparation method thereof of shock-absorbing rebound, and in particular to one kind is main glue by POE and EVA
The sole material and preparation method thereof for the shock-absorbing rebound being prepared.
Background technique
In order to improve the achievement of sportsman, sport footwear must be light as far as possible, so ultralightization of sport footwear and its excellent property
Being able to maintain property just becomes the Main way of movement midsole material development.One vinyl acetate co-polymer of ethylene (EvA) foaming shoe
Bottom material is because of its widespread love light, comfortable and easy to wear by people.EVA has good plasticity, fabulous elasticity, institute
With, EVA in movement midsole using extremely widespread.The middle bottom material of the various branding campaign shoes in the whole world is mostly to use
EvA and its foamed material with resin, the blend of rubber.High-elastic is the test item of a conventional need in fact, and damping
Performance G value is the footwear material of characterization movement in recent years comfortably with the important indicator of safety, and damping performance G value is test footwear material by outer
The number of footwear material Displacement-deformation when the impact force on boundary, the smaller damping performance of Displacement-deformation is better.
Ethylene-vinyl acetate copolymer (EVA) is the thermoplastic of rubber like, is had compared with polyethylene excellent
Flexibility, cold flexibility, elasticity, stress cracking resistance and good plasticity, machinability, therefore obtain extensively
Application.EVA crosslinked foaming material is the foamed material that a kind of physical property is excellent, nontoxic, due to the presence of gas phase, with density
It is low, specific strength is high, can absorb the advantages that load.But the deformation of EVA foamed material is big, and wearability is inadequate, and exists and skid, is low
The shortcomings that temperature is hardened, to limit its application.
In recent years, more to the research of EVA crosslinked foaming material both at home and abroad, mainly formula and processing technology are set
Meter, wherein the important channel that modifying agent is formula design is added.Thermoplastic polymer such as thermoplastic elastomer (TPR), ternary
EP rubbers (EPDM) etc. is commonly used for the modifying agent of EVA crosslinked foaming, and EPDM has excellent ageing-resistant performance, 110~16
0 DEG C of blend (EVA/EPDM) that can be obtained with EVA melt blending in amorphous areas partially compatible, in peroxide initiator
Under the action of, compatibility can be improved, but its viscosity is increased with the increase of EPDM amount, cannot guarantee to squeeze out well
With going on smoothly for injection technique, by biggish limitation in production application.Ethylene-octene copolymer (POE) in addition to
Have outside elasticity, recovery, obdurability and weatherability as traditional rubber, molding is equally easily worked also like thermoplastic
It is reused with recycling, and there is splendid compatibility with other plastic raw materials.The product not high to temperature classification is directly used
POE can machine-shaping, can not only improve production efficiency by a relatively large margin, can also reuse；And narrow average molecular
Mass Distribution makes material be not likely to produce flexure in injection and extrusion process；Its strand saturation, contained tertiary carbon atom is relatively
It is few, thus there is excellent heat-proof aging and anti-ultraviolet property.Therefore POE modified EVA is used, function admirable, hard can be made
Spend foaming product in extensive range.
The wear-resisting foaming shoe material of the ultralight damping of prior art Chinese invention patent and its manufacturing method, application No. is
CN201810819029.0, it discloses footwear material groups to become ethylene-vinyl acetate copolymer 0%~30%, polymer polyol
Alcohol 37%~68%, polyolefin block copolymer 10%~20%, ethylene-acrylic acid copolymer 5%~15%, anti-wear agent 5%
~10%, talcum powder 3%~8%, stearic acid 0.2%~0.6%, zinc stearate 0.3%~1.0%, zinc oxide 1.0%~
2.0%, two-(tert-butylperoxyiso-propyl) benzene 0.4%~0.6%, azodicarbonamide 4%~6%, Masterbatch 2%~
3%, gross mass 100%.The prepared wear-resisting foaming shoe material of ultralight damping had not only reached ultralight, damping comfort property, but also reached resistance to
Mill, wearing well requires, and in embodiment 4, damping G value is 8.3, rebound degree 58%.
Summary of the invention
It is an object of the invention to be modified using POE to EVA foamed material, by different rubber chemicals dosages
With the adjusting of preparation process, the foamed material of different densities and different mechanical properties can be prepared, to widening EVA and POE material
Use, stabilized product quality is of great significance.
The present invention is achieved through the following technical solutions:
A kind of sole material of shock-absorbing rebound, preparing raw material includes main glue and rubber chemicals, and the main glue includes following heavy
Amount component: 80-95 parts of 7350M EVA of rubber-plastic grain, 5-20 parts of rubber-plastic grain POE；The rubber chemicals include following heavy
Measure component: 1-2 parts of zinc oxide, 0.5-1 parts of stearic acid, 2.5-2.8 parts of foaming agent, ripe dose 0-1.5 parts fast, crosslinking agent 0.8
Part.
The main glue includes following components by weight percent: 85 parts of EVA of rubber-plastic grain 7350M, 15 parts of rubber-plastic grain POE.
The rubber chemicals include following components by weight percent: 1.5 parts of zinc oxide, 0.8 part of stearic acid, and 2.6 parts of foaming agent,
It is ripe dose 1 part, 0.8 part of crosslinking agent fast.
The foaming agent is azodicarbonamide.
Described fast ripe dose is combination one or two kinds of in TAIC and TMPTMA.
The crosslinking agent is DCP.
A kind of preparation method of the sole material of shock-absorbing rebound, which is characterized in that comprise the steps of:
Step 1: raw material is weighed according to following weight: 80-95 parts of 7350M EVA of rubber-plastic grain, 5-20 parts of rubber-plastic grain POE；
It is 1-2 parts of zinc oxide, 0.5-1 parts of stearic acid, 2.5-2.8 parts of foaming agent, ripe dose 0-1.5 parts, 0.8 part of crosslinking agent fast；
Step 2: putting into 80-95 parts of rubber-plastic grain 7350M EVA into mixer, and 5-20 parts of rubber-plastic grain POE are kneaded to equal
It is even；
Step 3: to 90 DEG C -110 DEG C of cause of mixer temperature liter, zinc oxide 1-2 parts of investment of cleaning dust, 0.5-1 parts of stearic acid,
2.5-2.8 parts of foaming agent, fast ripe dose of 0-1.5 parts of mixing 1-3min；It is risen to mixer temperature and causes 110 DEG C -115 DEG C, be put into material
On mill board, Luntai spacing 0.5mm speed Bao Erci, triangle bag plays three mixings, and uniformly volume is granulated with pelletizer is entered；
Step 4: 0.8 part of crosslinking agent is added later, is vulcanized, 150 DEG C -200 DEG C of curing temperature, vulcanization time 300 seconds -500
Second.
The rubber-plastic grain 7350M EVA is 85 parts, and rubber-plastic grain POE is 15 parts.
The zinc oxide is 1.5 parts, and stearic acid is 0.8 part, and foaming agent is 2.6 parts, and fast ripe dose is 1 part.
The foaming agent is azodicarbonamide, and described fast ripe dose is group one or two kinds of in TAIC and TMPTMA
It closes, the crosslinking agent is DCP.
The beneficial effects of the present invention are: control EVA is 80-95 parts in EVA/POE foaming system, POE is 5-20 parts,
The sole material being prepared by the adjusting to different rubber chemicals dosages and preparation process, can satisfy movement foaming shoe
The comprehensive performance requirement of bottom material.
Specific embodiment
Experimental material: foaming agent: azodicarbonamide；It is ripe dose fast: Triallyl isocyanurate (TAIC) and three hydroxyl first
Base propane trimethyl acrylic ester (TMPTMA)；Crosslinking agent: cumyl peroxide (DCP).
Embodiment one: the preparation method 1 of the sole material of shock-absorbing rebound
Step 1: weigh following components: 80 parts of EVA of rubber-plastic grain 7350M, 20 parts of rubber-plastic grain POE；It is 2 parts of zinc oxide, stearic
1 part of acid, azodicarbonamide 2.8,1.5 parts of TAIC, 0.8 part of DCP.
Step 2: the aniseed prepared in step 1 is kneaded to uniform；Aniseed includes: 80 parts of EVA of rubber-plastic grain 7350M,
20 parts of rubber-plastic grain POE.
Step 3: being risen to mixer temperature and cause 90 DEG C, cleaned dust investment small powder and be kneaded 60 seconds；Small powder includes: zinc oxide
(99.7%)
2 parts, 1 part of stearic acid (ST/A), 2.8 parts of azodicarbonamide, 1.5 parts of TAIC.
Step 4: being risen to mixer temperature and cause 100 DEG C, second of cleaning dust is kneaded 90 seconds.
Step 5: being risen to mixer temperature and cause 110-115 DEG C, be put on mill board to material, Luntai spacing 0.5mm speed is thin
Secondary, triangle bag plays three mixings, and uniformly volume is granulated with pelletizer is entered.
Step 6: being added DCP0.8 parts, vulcanized, 150 DEG C of curing temperature, vulcanization time 500 seconds.
Embodiment two: the preparation method 2 of the sole material of shock-absorbing rebound
Step 1: weigh following components: 85 parts of EVA of rubber-plastic grain 7350M, 15 parts of rubber-plastic grain POE；1.5 parts of zinc oxide, firmly
0.8 part of resin acid, azodicarbonamide 2.6,1 part of TMPTMA, 0.8 part of DCP.
Step 2: the aniseed prepared in step 1 is kneaded to uniform；Aniseed includes: 85 parts of EVA of rubber-plastic grain 7350M,
15 parts of rubber-plastic grain POE.
Step 3: being risen to mixer temperature and cause 90 DEG C, cleaned dust investment small powder and be kneaded 60 seconds；Small powder includes: zinc oxide
(99.7%)
1.5 parts, 0.8 part of stearic acid (ST/A), 2.6 parts of azodicarbonamide, 1 part of TMPTMA.
Step 4: being risen to mixer temperature and cause 100 DEG C, second of cleaning dust is kneaded 60 seconds.
Step 5: being risen to mixer temperature and cause 110-115 DEG C, be put on mill board to material, Luntai spacing 0.5mm speed is thin
Secondary, triangle bag plays three mixings, and uniformly volume is granulated with pelletizer is entered.
Step 6: being added DCP0.8 parts, vulcanized, 175 DEG C of curing temperature, vulcanization time 400 seconds.
Embodiment three: the preparation method 3 of the sole material of shock-absorbing rebound
Step 1: weigh following components: 95 parts of EVA of rubber-plastic grain 7350M, 5 parts of rubber-plastic grain POE；It is 1 part of zinc oxide, stearic
0.5 part of acid, azodicarbonamide 2.5,0.8 part of DCP.
Step 2: the aniseed prepared in step 1 is kneaded to uniform；Aniseed includes: 95 parts of EVA of rubber-plastic grain 7350M,
5 parts of rubber-plastic grain POE.
Step 3: being risen to mixer temperature and cause 90 DEG C, cleaned dust investment small powder and be kneaded 30 seconds；Small powder includes: zinc oxide
(99.7%)
1 part, 0.5 part of stearic acid (ST/A), 2.5 parts of azodicarbonamide.
Step 4: being risen to mixer temperature and cause 110 DEG C, second of cleaning dust is kneaded 30 seconds.
Step 5: being risen to mixer temperature and cause 110-115 DEG C, be put on mill board to material, Luntai spacing 0.5mm speed is thin
Secondary, triangle bag plays three mixings, and uniformly volume is granulated with pelletizer is entered.
Step 6: being added DCP0.8 parts, vulcanized, 200 DEG C of curing temperature, vulcanization time 300 seconds.
Footwear material performance evaluation: to footwear material obtained by above-described embodiment 1,2 and 3, performance test results such as the following table 1 is carried out.
| Physical property | Standard | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Rebound degree % | DIN53513 | 58 | 62 | 60 |
| Damping G value | ASTM F1614-99 | 8.3 | 8.8 | 8.5 |
Experimental result: it is detected according to the rebound degree and G value of standard brick, the excellent damping resilience performance of the material of embodiment 2, table
Bright: POE elastic material and EVA material, after ratio mixing, in mixer mixing, open mill mill controls certain temperature
And crosslinking condition, the available sole material with damping and high rebound can satisfy the comprehensive of movement foaming sole material
Close performance requirement.
Claims (10)
1. a kind of sole material of shock-absorbing rebound, preparing raw material includes main glue and rubber chemicals, which is characterized in that the master
Glue includes following components by weight percent: 80-95 parts of 7350M EVA of rubber-plastic grain, 5-20 parts of rubber-plastic grain POE；The rubber helps
Agent includes following components by weight percent: it is 1-2 parts of zinc oxide, 0.5-1 parts of stearic acid, 2.5-2.8 parts of foaming agent, ripe dose 0-1.5 parts fast,
0.8 part of crosslinking agent.
2. a kind of sole material of shock-absorbing rebound according to claim 1, which is characterized in that the main glue includes following
Components by weight percent: 85 parts of EVA of rubber-plastic grain 7350M, 15 parts of rubber-plastic grain POE.
3. a kind of sole material of shock-absorbing rebound according to claim 1, which is characterized in that the rubber chemicals include
Following components by weight percent: 1.5 parts of zinc oxide, 0.8 part of stearic acid, 2.6 parts of foaming agent, ripe dose 1 part, 0.8 part of crosslinking agent fast.
4. a kind of sole material of shock-absorbing rebound according to claim 1, which is characterized in that the foaming agent is azo
Diformamide.
5. a kind of sole material of shock-absorbing rebound according to claim 1, which is characterized in that described fast ripe dose is TAIC
With combination one or two kinds of in TMPTMA.
6. a kind of sole material of shock-absorbing rebound according to claim 1, which is characterized in that the crosslinking agent is DCP.
7. a kind of preparation method comprising any sole material of claim 1-6, which is characterized in that include following step
It is rapid:
Step 1: raw material is weighed according to following weight: 80-95 parts of 7350M EVA of rubber-plastic grain, 5-20 parts of rubber-plastic grain POE；
It is 1-2 parts of zinc oxide, 0.5-1 parts of stearic acid, 2.5-2.8 parts of foaming agent, ripe dose 0-1.5 parts, 0.8 part of crosslinking agent fast；
Step 2: putting into 80-95 parts of rubber-plastic grain 7350M EVA into mixer, and 5-20 parts of rubber-plastic grain POE are kneaded to equal
It is even；
Step 3: to 90 DEG C -110 DEG C of cause of mixer temperature liter, zinc oxide 1-2 parts of investment of cleaning dust, 0.5-1 parts of stearic acid,
2.5-2.8 parts of foaming agent, fast ripe dose of 0-1.5 parts of mixing 1-3min；It is risen to mixer temperature and causes 110 DEG C -115 DEG C, be put into material
On mill board, Luntai spacing 0.5mm speed Bao Erci, triangle bag plays three mixings, and uniformly volume is granulated with pelletizer is entered；
Step 4: 0.8 part of crosslinking agent is added later, is vulcanized, 150 DEG C -200 DEG C of curing temperature, vulcanization time 300 seconds -500
Second.
8. a kind of preparation method of the sole material of shock-absorbing rebound according to claim 7, which is characterized in that the rubber
Plastic pellet 7350M EVA is 85 parts, and rubber-plastic grain POE is 15 parts.
9. a kind of preparation method of the sole material of shock-absorbing rebound according to claim 7, which is characterized in that the oxygen
Changing zinc is 1.5 parts, and stearic acid is 0.8 part, and foaming agent is 2.6 parts, and fast ripe dose is 1 part.
10. a kind of preparation method of the sole material of shock-absorbing rebound according to claim 7, which is characterized in that described
Foaming agent is azodicarbonamide, and described fast ripe dose is one or two kinds of combination in TAIC and TMPTMA, the crosslinking
Agent is DCP.