CN103936352A - High-strength heat insulation mortar containing asbestos fiber - Google Patents
High-strength heat insulation mortar containing asbestos fiber Download PDFInfo
- Publication number
- CN103936352A CN103936352A CN201410120371.3A CN201410120371A CN103936352A CN 103936352 A CN103936352 A CN 103936352A CN 201410120371 A CN201410120371 A CN 201410120371A CN 103936352 A CN103936352 A CN 103936352A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- magnesium silicate
- insulation mortar
- fibrous magnesium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses high-strength heat insulation mortar containing asbestos fiber. The high-strength heat insulation mortar is prepared from the following raw materials in parts by weight: 3-5 parts of silicon dioxide powder, 0.1-0.2 part of borax, 1-2 parts of sodium lauryl polyoxyethylene ether sulfate, 3-5 parts of silicon carbide powder, 3-5 parts of ceramsite, 2-4 parts of shell powder, 3-5 parts of asbestos fiber, 3.5-6.5 parts of Guar gum, 30-40 parts of gypsum, 100-110 parts of cement, 110-120 parts of vitreous micro-beads, 0.6-0.8 part of mineral oil, 4-6 parts of calcium carbonate, 20-26 parts of quartz sand, 2-3 parts of calcium lignosulfonate, 3-5 parts of chitosan, 8-10 parts of redispersible latex powder, 1-2 parts of cellulose ether, 0.5-1.3 parts of sodium lauryl sulfate, 15-20 parts of filler and an appropriate amount of water.
Description
Technical field
The present invention relates to thermal insulation mortar field, is exactly a kind of high-strength insulation mortar that contains fibrous magnesium silicate.
Background technology
Thermal insulation mortar refers to and is mixed by isolation-type lagging material and mortar material, for constructing a kind of material of construction of building surface thermal insulation layer.
Fibrous magnesium silicate (asbestos fiber) can be made into yarn, line, rope, cloth, packing etc., as material or the wadding of the parts such as transmission, insulation, heat insulation, insulation, sealing, be mainly used to make asbestos plate architectural, asbestos paper PLASTIC LAMINATED, the materials such as insulating pipe and kiln pad and insulation, solar heat protection, insulation, sound insulation, sealing.Fibrous magnesium silicate can be made with cement mixing the asbestos-cement productss such as asbestos cement tile, plate, roofing board, asbestos tube.Asbestos and pitch fusion can be made asbetumen goods, the putty of using as semi-rigid asbestos-bitumen sheet, cloth (malthoid), paper, brick and liquid asbestos paint, pointing cement pavement and dilatation fissure etc.The plastic bonding such as asbestos and phenolic aldehyde, polypropylene in national defence, can make the anti-ablator of rocket, aircraft wing, fuel tank, rocket afterbody blast tube and torpedo high speed transmitter, sound insulation, lagging material in boats and ships, automobile and aircraft, tank, warship oceangoing ship, after asbestos and various rubber mix pressing mold, also can make the sealing material of liquid rocket engine web member.
Summary of the invention
The object of the present invention is to provide a kind of high-strength insulation mortar that contains fibrous magnesium silicate.
Above-mentioned purpose realizes by following scheme:
A kind of high-strength insulation mortar that contains fibrous magnesium silicate, it is characterized in that: it is to be made by the raw material of following weight parts: silicon dioxide powder 3-5, borax 0.1-0.2, laureth sodium sulfovinate 1-2, carborundum powder 3-5, haydite 3-5, oyster shell whiting 2-4, fibrous magnesium silicate 3-5, guar gum 3.5-6.5, gypsum 30-40, cement 100-110, glass bead 110-120, mineral oil 0.6-0.8, calcium carbonate 4-6, quartz sand 20-26, calcium lignin sulphonate 2-3, chitosan 3-5, redispersable latex powder 8-10, ether of cellulose 1-2, sodium lauryl sulphate 0.5-1.3, stopping composition 15-20, suitable quantity of water,
Stopping composition is made up of the raw material of following weight part: wilkinite 15-20, useless ceramic tile 7-10, fluorite ore ground-slag 5-8, phosphorus ore slag 4-6, bamboo carbon powder 1-2, aluminium nitride powder 2-4, fatty alcohol-polyoxyethylene ether 1-2, Silane coupling agent KH550 2-4, butyl acrylate 2-4, phenyl glycidyl ether 1-2,3-aminopropyl trimethoxysilane 2-3, tri (propylene glycol) diacrylate 2-3, citric acid 1-2;
The preparation method of stopping composition mixes wilkinite, useless ceramic tile, fluorite ore ground-slag, phosphorus ore slag, then puts into the sodium hydroxide solution that concentration is 10-15%, soaks 4-6 hour, taking-up deionized water wash is dried, and puts into calcining furnace and calcine 1-2 hour at 900-950 DEG C, cooling, put into 10-12% hydrochloric acid soln and soak 4-6 hour, filter and take out, deionized water wash, dries, after mixing with other surplus stock again, at 30-35 DEG C, be incubated 1-2 hour, cooling, to obtain final product.
Described a kind of high-strength insulation mortar that contains fibrous magnesium silicate, is characterized in that:
Preparation method is:
Cement, glass bead, haydite, fibrous magnesium silicate, chitosan, sodium lauryl sulphate are mixed, under 100-200 rev/min, stir 5-7 minute, take out, then with the whole raw material blendings of residue after, 400-500 rev/min is at the uniform velocity stirred 6-8 minute, after packaging and get final product.
Beneficial effect of the present invention is: the thermal conductivity that effectively reduces mortar of the present invention, and intensity is high, and the mechanical property of mortar is strong, easy to use, and preparation method is simple, and raw material is easy to get.
Embodiment
A kind of high-strength insulation mortar that contains fibrous magnesium silicate, it is to be made by the raw material of following weight kg: silicon dioxide powder 5, borax 0.1, laureth sodium sulfovinate 1, carborundum powder 5, haydite 5, oyster shell whiting 4, fibrous magnesium silicate 5, guar gum 3.5, gypsum 35, cement 110, glass bead 120, mineral oil 0.8, calcium carbonate 6, quartz sand 26, calcium lignin sulphonate 3, chitosan 5, redispersable latex powder 10, ether of cellulose 1, sodium lauryl sulphate 0.5, stopping composition 20, suitable quantity of water;
Stopping composition is made up of the raw material of following weight kg: wilkinite 20, useless ceramic tile 7, fluorite ore ground-slag 8, phosphorus ore slag 6, bamboo carbon powder 2, aluminium nitride powder 4, fatty alcohol-polyoxyethylene ether 1, Silane coupling agent KH550 4, butyl acrylate 4, phenyl glycidyl ether 2,3-aminopropyl trimethoxysilane 3, tri (propylene glycol) diacrylate 3, citric acid 1;
The preparation method of stopping composition mixes wilkinite, useless ceramic tile, fluorite ore ground-slag, phosphorus ore slag, then to put into concentration be 15% sodium hydroxide solution, soaks 6 hours, taking-up deionized water wash is dried, and puts into calcining furnace and at 950 DEG C, calcines 2 hours, cooling, putting into 12% hydrochloric acid soln soaks 6 hours, filter and take out, deionized water wash, dries, after mixing with other surplus stock again, at 35 DEG C, be incubated 2 hours, cooling, to obtain final product.
Described a kind of high-strength insulation mortar that contains fibrous magnesium silicate, preparation method is:
Cement, glass bead, haydite, fibrous magnesium silicate, chitosan, sodium lauryl sulphate are mixed, under 100 revs/min, stir 7 minutes, take out, then with the whole raw material blendings of residue after, 500 revs/min are at the uniform velocity stirred 8 minutes, after packaging and get final product.
Products obtained therefrom test result is as follows:
Claims (2)
1. a high-strength insulation mortar that contains fibrous magnesium silicate, it is characterized in that: it is to be made by the raw material of following weight parts: silicon dioxide powder 3-5, borax 0.1-0.2, laureth sodium sulfovinate 1-2, carborundum powder 3-5, haydite 3-5, oyster shell whiting 2-4, fibrous magnesium silicate 3-5, guar gum 3.5-6.5, gypsum 30-40, cement 100-110, glass bead 110-120, mineral oil 0.6-0.8, calcium carbonate 4-6, quartz sand 20-26, calcium lignin sulphonate 2-3, chitosan 3-5, redispersable latex powder 8-10, ether of cellulose 1-2, sodium lauryl sulphate 0.5-1.3, stopping composition 15-20, suitable quantity of water,
Stopping composition is made up of the raw material of following weight part: wilkinite 15-20, useless ceramic tile 7-10, fluorite ore ground-slag 5-8, phosphorus ore slag 4-6, bamboo carbon powder 1-2, aluminium nitride powder 2-4, fatty alcohol-polyoxyethylene ether 1-2, Silane coupling agent KH550 2-4, butyl acrylate 2-4, phenyl glycidyl ether 1-2,3-aminopropyl trimethoxysilane 2-3, tri (propylene glycol) diacrylate 2-3, citric acid 1-2;
The preparation method of stopping composition mixes wilkinite, useless ceramic tile, fluorite ore ground-slag, phosphorus ore slag, then puts into the sodium hydroxide solution that concentration is 10-15%, soaks 4-6 hour, taking-up deionized water wash is dried, and puts into calcining furnace and calcine 1-2 hour at 900-950 DEG C, cooling, put into 10-12% hydrochloric acid soln and soak 4-6 hour, filter and take out, deionized water wash, dries, after mixing with other surplus stock again, at 30-35 DEG C, be incubated 1-2 hour, cooling, to obtain final product.
2. a kind of high-strength insulation mortar that contains fibrous magnesium silicate according to claim 1, is characterized in that:
Preparation method is:
Cement, glass bead, haydite, fibrous magnesium silicate, chitosan, sodium lauryl sulphate are mixed, under 100-200 rev/min, stir 5-7 minute, take out, then with the whole raw material blendings of residue after, 400-500 rev/min is at the uniform velocity stirred 6-8 minute, after packaging and get final product.