CN103788800B - A kind of composite biomass coating - Google Patents
A kind of composite biomass coating Download PDFInfo
- Publication number
- CN103788800B CN103788800B CN201410066410.6A CN201410066410A CN103788800B CN 103788800 B CN103788800 B CN 103788800B CN 201410066410 A CN201410066410 A CN 201410066410A CN 103788800 B CN103788800 B CN 103788800B
- Authority
- CN
- China
- Prior art keywords
- particle
- nano
- coating
- radiation
- biomass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of composite biomass coating, it is stirred 1 hour by the material mixing of following weight/mass percentage composition and prepares: the magnetic nanoparticle of biological particles particle, 3%～5%, 20%～40% of 20%～30% acrylic resin modified, 20%～the butyl glycol ether of the dispersant of the levelling agent of the antisettling agent of fine hair powder, 0.5%～1.5%, 0.1%～0.3%, 0.3%～0.5%, 15%～25% of the titanium dioxide of 30%, 2%～4%.This case introduces biomass energy and radiation resistance material in coating simultaneously, the wooden structures Han porous of the biological particles in coating, it can heat and moisture preserving again can harmful gas in active adsorption air；Radiation resistance material in coating can effectively absorb electric radiation and the heat radiation of surrounding, to ensure the life and health of human body；This product not only natural environmental-protective is pollution-free, also can effectively remove the radiation of indoor harmful gas and health risk.
Description
Technical field
The present invention relates to paint field, particularly to the compound life of a kind of environment friendly and pollution-free absorbable radiation
Material coating.
Background technology
At present, along with in world wide, the continuous of computer networking technology breaks through and development, network spreads all over
The every nook and cranny of our life, the mobile phone all used every day such as us, notebook computer etc., but correspondingly,
We also having approached in an environment being full of radiation and pollution ourselves.How in our daily life
Work alleviates suffered amount of radiation and is always the topic that people are interested.
Biomass energy is the clean energy resource that a class is environment friendly and pollution-free.Nowadays, people are to biomass energy
Utilization also few, in most cases, biomass energy is only carried out by we as a kind of fuel
Burn to obtain certain heat energy.Available biomass energy is mainly forestry " three remain thing ", and (timber adds
Work residue, forest harvesting residue, producing material residue), various wooden leftover bits and pieces, wood wastes,
Agricultural crop straw and shrub etc..How biomass energy is carried out maximized utilization the most instantly
The hot that people are urgently to be resolved hurrily.
Summary of the invention
For above-mentioned some mentioned problems, this case develops a kind of composite biomass coating, in its formula
With the addition of the nano-particle material of absorbable radiation so that this coating itself not only environmental protection but also radiation can be absorbed,
Can be widely applied to all kinds of house ornamentation and frock coating.
Technical scheme is summarized as follows:
A kind of composite biomass coating, it is stirred 1 hour system by the material mixing of following weight/mass percentage composition
:
Wherein, described biological particles particle is prepared by following methods: dry biomass material to aqueous
Rate is 15wt%～20wt% and is crushed to the particle diameter of biomass material between 3mm～5mm, with follow-up
Continue and this biomass material is dried to moisture content less than 10wt%, and be again crushed to the grain of biomass material
Footpath is less than 1.5mm, obtains biological particles particle；
Described magnetic nanoparticle is made up of the material of following weight/mass percentage composition: the ferroso-ferric oxide of 40% is received
Rice grain, the Barium monoxide nano-particle of 15%, the lanthanum sesquioxide nano-particle of 10%, three oxidations two of 12%
Yttrium nano-particle, the europiumsesquioxide nano-particle of 8%, the yttria nano-particle of 15%；
Described antisettling agent is selected from aerosil, polyolefin-wax, castor oil hydrogenated or a combination thereof；
Described levelling agent is selected from polydimethyl siloxane fluid, organic-silicon-modified polydimethyl siloxane fluid or a combination thereof；
Described dispersant is selected from p-methyl benzenesulfonic acid sodium, oleyl amine sodium acetate, Polyethylene Glycol or its group
Close.
Preferably, described composite biomass coating, described ferroferric oxide nano granules, Barium monoxide
Nano-particle, lanthanum sesquioxide nano-particle, yttrium oxide nano-particle, europiumsesquioxide nanometer
Grain, the particle diameter of yttria nano-particle are 90nm～150nm.
Preferably, described composite biomass coating, described biomass material selected from wooden leftover bits and pieces,
The processing of wooden waste products, timber produced wood flour, wheat stalk, corn straw, broomcorn straw, cotton
Line rod, rice straw, bean stalk, Pericarppium arachidis hypogaeae or a combination thereof.
The invention has the beneficial effects as follows: in coating, introduce biomass energy and radiation resistance material simultaneously, be coated with
Biological particles in material wooden structures Han porous, it can heat and moisture preserving again can be in active adsorption air
Harmful gas；Radiation resistance material in coating can effectively absorb electric radiation and the heat radiation of surrounding, to ensure
The life and health of human body；This product not only natural environmental-protective is pollution-free, also can effectively remove indoor harmful gas and
The radiation of health risk.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail, to make those skilled in the art join
Book word can be implemented according to this as directed.
A kind of composite biomass coating, it is stirred 1 hour system by the material mixing of following weight/mass percentage composition
:
Wherein, biological particles particle is prepared by following methods: by biomass material drying to moisture content be
15wt%～20wt% is also crushed to the particle diameter of biomass material between 3mm～5mm, continues thereafter with this
Biomass material is dried to moisture content less than 10wt%, and the particle diameter being again crushed to biomass material is less than
1.5mm, obtains biological particles particle；Oven temperature is at 80～120 DEG C.Pulverize due to raw material for the first time
Water content is high, pulverizes not thorough, after the particle after once pulverizing is dried again, and can be effectively by former
Material is crushed to required Particle size requirements.
Biomass material is selected from wooden leftover bits and pieces, wooden waste products, the produced wood flour of timber processing, little
Wheat Straw, corn straw, broomcorn straw, cotton stem, rice straw, bean stalk, Pericarppium arachidis hypogaeae or a combination thereof.
Magnetic nanoparticle is made up of the material of following weight/mass percentage composition: the ferriferrous oxide nano of 40%
Grain, the Barium monoxide nano-particle of 15%, the lanthanum sesquioxide nano-particle of 10%, the yttrium oxide of 12% are received
Rice grain, the europiumsesquioxide nano-particle of 8%, the yttria nano-particle of 15%；Ferroso-ferric oxide
Nano-particle, Barium monoxide nano-particle, lanthanum sesquioxide nano-particle, yttrium oxide nano-particle,
Europiumsesquioxide nano-particle, the particle diameter of yttria nano-particle are 90nm～150nm.
Antisettling agent is selected from aerosil, polyolefin-wax, castor oil hydrogenated or a combination thereof；Levelling agent
Selected from polydimethyl siloxane fluid, organic-silicon-modified polydimethyl siloxane fluid or a combination thereof；Dispersant is selected to first
Base benzene sulfonic acid sodium salt, oleyl amine sodium acetate, Polyethylene Glycol or a combination thereof；Butyl glycol ether is this product institute
High boiling solvent, its stable performance, dissolubility is good.
Embodiment 1
A kind of composite biomass coating, it is stirred 1 hour system by the material mixing of following weight/mass percentage composition
:
Embodiment 2
A kind of composite biomass coating, it is stirred 1 hour system by the material mixing of following weight/mass percentage composition
:
Embodiment 3
A kind of composite biomass coating, it is stirred 1 hour system by the material mixing of following weight/mass percentage composition
:
Embodiment 4
A kind of composite biomass coating, it is stirred 1 hour system by the material mixing of following weight/mass percentage composition
:
Embodiment 5
A kind of composite biomass coating, it is stirred 1 hour system by the material mixing of following weight/mass percentage composition
:
Although embodiment of the present invention are disclosed as above, but it is not restricted to description and embodiment party
Listed utilization in formula, it can be applied to various applicable the field of the invention completely, for being familiar with ability
For the personnel in territory, be easily achieved other amendment, therefore without departing substantially from claim and etc. homotype
Enclosing under limited general concept, the present invention is not limited to specific details.
Claims (1)
1. a composite biomass coating, it is characterised in that it is mixed by the material of following weight/mass percentage composition
Close stirring to prepare for 1 hour:
Wherein, described biological particles particle is prepared by following methods: dry biomass material to aqueous
Rate is 15wt%～20wt% and is crushed to the particle diameter of biomass material between 3mm～5mm, with follow-up
Continue and this biomass material is dried to moisture content less than 10wt%, and be again crushed to the grain of biomass material
Footpath is less than 1.5mm, obtains biological particles particle；
Described magnetic nanoparticle is made up of the material of following weight/mass percentage composition: the ferroso-ferric oxide of 40% is received
Rice grain, the Barium monoxide nano-particle of 15%, the lanthanum sesquioxide nano-particle of 10%, three oxidations two of 12%
Yttrium nano-particle, the europiumsesquioxide nano-particle of 8%, the yttria nano-particle of 15%；
Described antisettling agent is selected from aerosil, polyolefin-wax, castor oil hydrogenated or a combination thereof；
Described levelling agent is selected from polydimethyl siloxane fluid, organic-silicon-modified polydimethyl siloxane fluid or a combination thereof；
Described dispersant is selected from p-methyl benzenesulfonic acid sodium, oleyl amine sodium acetate, Polyethylene Glycol or its group
Close；
Described ferroferric oxide nano granules, Barium monoxide nano-particle, lanthanum sesquioxide nano-particle, three
Y 2 O nano-particle, europiumsesquioxide nano-particle, the particle diameter of yttria nano-particle are
90nm～150nm；
Described biomass material selected from wooden leftover bits and pieces, wooden waste products, the produced wood flour of timber processing,
Wheat stalk, corn straw, broomcorn straw, cotton stem, rice straw, bean stalk, Pericarppium arachidis hypogaeae or a combination thereof.