CN103667803B - 一种铝合金箔及其加工工艺 - Google Patents

一种铝合金箔及其加工工艺 Download PDF

Info

Publication number
CN103667803B
CN103667803B CN201310618896.5A CN201310618896A CN103667803B CN 103667803 B CN103667803 B CN 103667803B CN 201310618896 A CN201310618896 A CN 201310618896A CN 103667803 B CN103667803 B CN 103667803B
Authority
CN
China
Prior art keywords
alloy foil
cold rolling
aluminum alloy
low
complete processing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310618896.5A
Other languages
English (en)
Other versions
CN103667803A (zh
Inventor
童根荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou cubic metal products Co., Ltd.
Original Assignee
HUZHOU SHENGJI METAL PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUZHOU SHENGJI METAL PRODUCT CO Ltd filed Critical HUZHOU SHENGJI METAL PRODUCT CO Ltd
Priority to CN201310618896.5A priority Critical patent/CN103667803B/zh
Publication of CN103667803A publication Critical patent/CN103667803A/zh
Application granted granted Critical
Publication of CN103667803B publication Critical patent/CN103667803B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种铝合金箔,包括以下组分且各组分的质量百分比为:铁0.8-1.3%、硅0.6-1.1%、铜0.2-0.3%、锰0.2-0.3%、镁0.2-0.3%,其余为铝和不可避免的杂质。本发明还公开了一种铝合金箔的加工工艺,1)严格保证各种组分的质量百分比在规定范围内;2)低温退火前通过多次冷轧使得铝合金箔的强度高;3)低温退火后通过两次冷轧将铝合金箔加工到所需厚度,且两次冷轧的方向相互垂直使得铝合金箔的厚度均匀,表面质量均匀稳定。

Description

一种铝合金箔及其加工工艺
技术领域
本发明涉及金属冶炼技术领域,具体涉及一种铝合金箔及其加工工艺。
背景技术
随着人们生活水平的提高,快餐、西餐等得到了快速发展,应用于快餐、西餐的食品容器的制造领域也得到了较快发展,为了减少塑料制品引起的白色污染,铝箔容器得到食品包装行业的青睐,然而现有技术中的铝箔容器强度低、质量差。
发明内容
本发明所要解决的问题是提供一种铝合金箔及其加工工艺,加工出的铝合金箔强度高,质量稳定。
为了解决上述技术问题,本发明采用如下技术方案:一种铝合金箔,包括以下组分且各组分的质量百分比为:铁0.8-1.3%、硅0.6-1.1%、铜0.2-0.3%、锰0.2-0.3%、镁0.2-0.3%,其余为铝和不可避免的杂质。
改进的,铝合金箔的平均结晶粒径为11-16μm。
一种铝合金箔的加工工艺,铝合金箔包括铁0.8-1.3%、硅0.6-1.1%、铜0.2-0.3%、锰0.2-0.3%、镁0.2-0.3%,其余为铝和不可避免的杂质,包括以下步骤:
(1)将铝合金的溶液以250-350℃/s冷却速度铸造成6-10mm厚度铝合金锭;
(2)先通过热轧将铝合金锭轧成2mm,再进行5-7次冷轧将2mm的铝合金锭轧为0.1-0.2mm的铝合金片,然后清洗掉表面的杂物;
(3)将清洗后的铝合金片进行低温退火,低温退火温度为255-275℃;
(4)再通过两次冷轧将低温退火后的铝合金片轧为5-12μm;
(5)对5-12μm的铝合金片进行高温退火,高温退火温度为310-340℃。
改进的,步骤(2)中每次冷轧轧掉的厚度为0.3-0.4mm。
改进的,步骤(4)中两次冷轧的方向相互垂直。
有益效果:
采用上述技术方案后,该发明一种铝合金箔及其加工工艺:1)严格保证各种组分的质量百分比在规定范围内;2)低温退火前通过多次冷轧使得铝合金箔的强度高;3)低温退火后通过两次冷轧将铝合金箔加工到所需厚度,且两次冷轧的方向相互垂直使得铝合金箔的厚度均匀,表面质量均匀稳定。
具体实施方式
实施例一:
一种铝合金箔,包括以下组分且各组分的质量百分比为:铁0.8-1.3%、硅0.6-1.1%、铜0.2-0.3%、锰0.2-0.3%、镁0.2-0.3%,其余为铝和不可避免的杂质,铝合金箔的平均结晶粒径为11-16μm。
实施例二:
如实施例一所述的一种铝合金箔的加工工艺,包括以下步骤:
(1)将铝合金的溶液以250-350℃/s冷却速度铸造成6-10mm厚度铝合金锭;
(2)先通过热轧将铝合金锭轧成2mm,再进行5-7次冷轧将2mm的铝合金锭轧为0.1-0.2mm的铝合金片,每次冷轧轧掉的厚度为0.3-0.4mm,然后清洗掉表面的杂物;
(3)将清洗后的铝合金片进行低温退火,低温退火温度为255-275℃;
(4)再通过两次冷轧将低温退火后的铝合金片轧为5-12μm,两次冷轧的方向相互垂直;
(5)对5-12μm的铝合金片进行高温退火,高温退火温度为310-340℃。
除上述优选实施例外,本发明还有其他的实施方式,本领域技术人员可以根据本发明作出各种改变和变形,只要不脱离本发明的精神,均应属于本发明所附权利要求所定义的范围。

Claims (2)

1.一种铝合金箔的加工工艺,铝合金箔包括铁0.8-1.3%、硅0.6-1.1%、铜0.2-0.3%、锰0.2-0.3%、镁0.2-0.3%,其余为铝和不可避免的杂质,其特征在于:包括以下步骤:
(1)将铝合金的熔液以250-350℃/s冷却速度铸造成6-10mm厚度铝合金锭;
(2)先通过热轧将铝合金锭轧成2mm,再进行5-7次冷轧将2mm的铝合金锭轧为0.1-0.2mm的铝合金片,然后清洗掉表面的杂物;
(3)将清洗后的铝合金片进行低温退火,低温退火温度为255-275℃;
(4)再通过两次冷轧将低温退火后的铝合金片轧为5-12μm;
(5)对5-12μm的铝合金片进行高温退火,高温退火温度为310-340℃。
2.根据权利要求1所述一种铝合金箔的加工工艺,其特征在于:步骤(4)中两次冷轧的方向相互垂直。
CN201310618896.5A 2013-11-27 2013-11-27 一种铝合金箔及其加工工艺 Active CN103667803B (zh)