CN103011891A - Preparation method for daily composite material adopting diatomite as base material - Google Patents
Preparation method for daily composite material adopting diatomite as base material Download PDFInfo
- Publication number
- CN103011891A CN103011891A CN2011102804846A CN201110280484A CN103011891A CN 103011891 A CN103011891 A CN 103011891A CN 2011102804846 A CN2011102804846 A CN 2011102804846A CN 201110280484 A CN201110280484 A CN 201110280484A CN 103011891 A CN103011891 A CN 103011891A
- Authority
- CN
- China
- Prior art keywords
- diatomite
- composite material
- adopted
- daily
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a new material preparation method, precisely to a preparation method for a daily composite material adopting diatomite as a base material. The daily composite material comprises, by weight, 79% of diatomite, 1% of tourmaline, 19% of attapulgite powder, 1% of nanometer titanium dioxide, and polyvinyl alcohol. According to the present invention, the diatomite is adopted as the base material, and mixing calcination according to a certain ratio is performed, such that silica content of the composite material is increased, and a specific surface area is increased; the attapulgite powder is adopted as a binder to coat the diatomite so as to further increase an absorption performance and a slow release performance; the tourmaline and the nanometer titanium dioxide are adopted to be loaded on the diatomite so as to increase functions of the composite material; the organic material polyvinyl alcohol is adopted as a granulating agent so as to improve strength of the product; and the composite material has characteristics of highly automatic humidity regulation, negative ion release, far infrared ray release, harmful gas absorption and excellent antibacterial property, is a environmentally friendly, energy-saving, low-carbon and green multifunctional product, and can be widely used in various fields of daily lives.
Description
Technical field
The present invention relates to the making method of a novel material, more precisely a kind of making method of the daily matrix material take diatomite as base-material.
Background technology.
Diatomite is comprised of unbodied SiO2, and contains a small amount of Fe2O3, CaO, MgO, Al2O3 and organic impurity.It is light yellow or light grey that diatomite is usually, and matter is soft, and porous is and light, and the special porousness structure of natural diatomaceous earth is the reason that diatomite has the feature physico-chemical property.Industrial being commonly used to as lagging material, filtering material abrasive substance, water glass raw material, discoloring agent etc.The rough processing of natural resource is adopted in present diatomaceous exploitation more, and as directly obtaining product behind calcining removal organic impurity, the carbon, product technological additional-value is low, about technology such as natural diatomaceous earth load nano-titanium dioxides report is arranged also.
Summary of the invention
Given this, the object of the present invention is to provide a kind of making method with daily matrix material take diatomite as base-material of hi-tech added value.
Attapulgite clay refers to a kind of clay mineral take attapulgite (attapulgite) as main ingredient.Attapulgite is a kind of crystalloid hydrous magnesium aluminium silicate mineral, have unique layer chain-like structure feature, high temperature resistant, resist the good colloidal property such as saline and alkaline and higher adsorption bleaching ability, and have certain plasticity-and cohesive force, water-absorbent is strong, tool viscosity and plasticity-when wet;
Tourmalinite also is Tourmaline.Be a kind of take boracic as main, also contain the Silicate Rocks mineral of the elements such as aluminium, sodium, iron, magnesium, lithium.Tourmalinite is the natural mineral of multielement, and main chemical compositions is SiO2TiO2CaO K2O LiO Al2O3B2O3MgO Na2O Fe2O3FeO MnO P2O5, and the tourmalinite main component has more than the 10 kind of trace elements favourable to human body such as magnesium, aluminium, iron, boron.Because it is the special polarity xln of a kind of structure, self can produce electron ion for a long time, and permanent release air negative ion and far infrared rays;
Nano titanium oxide is rutile-type white loose powder, and the shielding ultraviolet rays effect is strong, and good dispersiveness and weathering resistance are arranged, and TiO2 also has absorptive function and excellent anti-microbial property to obnoxious flavour.
Purpose of the present invention is achieved through the following technical solutions: a kind of making method of the daily matrix material take diatomite as base-material, wherein the matrix material take diatomite as base-material comprises diatomite, tourmalinite, Attapulgite stone flour, nano titanium oxide, polyvinyl alcohol, the weight percent of material is:
Granularity is 500 order diatomite 79%
1250 order tourmalinite 1%
325 order Attapulgite stone flours 19%
Nano titanium oxide 1%
Its making method is:
1, with diatomite material at 100 ℃, dry 2h;
2, getting weight is 79% diatomite, tourmalinite 1% and 19% Attapulgite stone flour mixing granulation on tablets press, is shaped to the spherical grain of 3mm particle:
3, be shaped to 3mm spheroidal particle bag shoe nano titanium oxide 1%;
4, get 0.05% polyvinyl alcohol, mixing 2% water is liquid adhesive, with 100% above-mentioned materials physical mixed;
5, the material after moulding is compound, at 600 ℃ of roasting 2h, after the cooling finished product.
The present invention adopts the matrix material take diatomite as base-material, comprise diatomite, tourmalinite, the Attapulgite stone flour, nano titanium oxide, polyvinyl alcohol, baking mixed by proportioning, the dioxide-containing silica of matrix material improves, specific surface area increases, utilize the Attapulgite stone flour to coat diatomite as tackiness agent, further improve absorption property and improve simultaneously sustained release performance, adopt tourmalinite, nano titanium oxide loads on the diatomite, increase the function of matrix material, adopting the organic materials polyvinyl alcohol is granulating agent, improved the intensity of product, the matrix material that makes by the present invention, has higher automatic humidifying function, anion releasing and far infrared function, to obnoxious flavour absorptive function and excellent anti-microbial property, it is a kind of environmental protection, energy-conservation, low-carbon (LC), green multifunctional product can be widely used in the numerous areas of daily life.
Embodiment
Embodiment 1,
A kind of making method of the matrix material take diatomite as base-material, wherein the matrix material take diatomite as base-material comprises diatomite, tourmalinite, Attapulgite stone flour, nano titanium oxide, the weight of material is:
Granularity is 500 order diatomite 79kg
1250 order tourmalinite 1kg
325 order Attapulgite stone flour 19kg
Nano titanium oxide 1kg
Its making method is:
1, with diatomite material at 100 ℃, dry 2h;
2, get diatomite 79kg, tourmalinite 1kg and Attapulgite stone flour 19kg mixing granulation on tablets press, be shaped to the spherical grain of Φ 3mm particle:
3, be shaped to Φ 3mm spheroidal particle Yan Bao shoe nano titanium oxide 1kg;
4, get the 0.05kg polyvinyl alcohol, mixing 2kg water is liquid adhesive, with 100% above-mentioned materials physical mixed;
5, the material after moulding is compound, at 600 ℃ of roasting 2h, after the cooling finished product.
Claims (1)
1. the making method of the daily matrix material take diatomite as base-material, it is characterized in that: the matrix material take diatomite as base-material comprises diatomite, tourmalinite, Attapulgite stone flour, nano titanium oxide, polyvinyl alcohol, the weight percent of material is:
Granularity is 500 order diatomite 79%
1250 order tourmalinite 1%
325 order Attapulgite stone flours 19%
Nano titanium oxide 1%
Its making method is:
(1), with diatomite material at 100 ℃, dry 2h;
(2), to get weight be 79% diatomite, tourmalinite 1% and 19% Attapulgite stone flour mixing granulation on tablets press, is shaped to the spherical grain of Φ 3mm particle:
(3), be shaped to 3mm spheroidal particle bag shoe nano titanium oxide 1%;
(4), get 0.05% polyvinyl alcohol, mixing 2% water is liquid adhesive, with 100% above-mentioned materials physical mixed;
(5), the material after moulding is compound, at 600 ℃ of roasting 2h, after the cooling finished product.