CN102728783B - Molding sand using dextrin as binder and preparation method thereof - Google Patents
Molding sand using dextrin as binder and preparation method thereof Download PDFInfo
- Publication number
- CN102728783B CN102728783B CN201210186992.2A CN201210186992A CN102728783B CN 102728783 B CN102728783 B CN 102728783B CN 201210186992 A CN201210186992 A CN 201210186992A CN 102728783 B CN102728783 B CN 102728783B
- Authority
- CN
- China
- Prior art keywords
- dextrin
- sand
- molding sand
- parts
- gypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a molding sand using dextrin as binder and a preparation method thereof. The method is as below: weighing raw materials of 30-40 parts of recycling sand, 40-50 parts of quartz sand,10-20 parts of vermiculite, 5-10 parts of steel fiber, 3-8parts of furan resin, 3-5 parts of dextrin, 1-3 parts of gypsum and a proper amount of water; mixing the raw materials evenly; carrying out dry mixing for 3-5 minutes; then adding water; carrying out wet mixing for 5-8 minutes; and then drying at 250-350 DEG C; and carrying out alloy casting mold casting to obtain the molding sand. The molding sand using dextrin as binder of the invention has reasonable formula; usage of steel fiber can increase the strength of the molding sand; meanwhile, the usage of gypsum and dextrin increases the adhesion and reduces broken rate.
Description
Technical field
The present invention relates to casting technology field, be specifically related to a kind of molding sand that dextrin is binding agent and preparation method thereof of take.
Background technology
The effect of molding sand in Foundry Production is very important, the casting wasted product causing because of the poor quality of molding sand accounts for 30~50% of the total waste product of foundry goods, conventionally the requirement of molding sand is had to intensity and heat endurance, mobility, plasticity, gas permeability and collapsibility, after casting solidification, whether molding sand easily destroys, the performance of whether easily removing from foundry goods.
At present, in the preparation process of molding sand, generally by fresh sand, old sand, binding agent and auxiliary material, be mixed by a certain percentage.
Summary of the invention
In order to alleviate shortcomings and deficiencies of the prior art, the object of the present invention is to provide a kind of molding sand that dextrin is binding agent and preparation method thereof of take.Of the present invention to take the sand formulation that dextrin is binding agent reasonable, adopts steel fibre can increase sand bond, meanwhile, adopts gypsum, dextrin to increase caking property, and percentage of damage declines.
The present invention adopts following technical scheme to achieve these goals:
The molding sand that the dextrin of take is binding agent, the weight portion of its constitutive material is: return sand 30-40, quartz sand 40-50, vermiculite 10-20, steel fibre 5-10, furane resins 3-8, dextrin 3-5, gypsum 1-3 and water are appropriate
The molding sand that the dextrin of take is binding agent, the weight portion of its constitutive material is that return sand 35, quartz sand 45, vermiculite 15, steel fibre 8, furane resins 5, dextrin 4, gypsum 2 and water are appropriate.
Beneficial effect of the present invention:
Of the present invention to take the sand formulation that dextrin is binding agent reasonable, adopts steel fibre can increase sand bond, meanwhile, adopts gypsum, dextrin to increase caking property, and percentage of damage declines.
The specific embodiment
Embodiment 1: the molding sand that the dextrin of take is binding agent, the weight portion of its constitutive material is: return sand 40, quartz sand 50, vermiculite 20, steel fibre 10, furane resins 8, dextrin 5, gypsum 3 and water are appropriate.
The preparation method of the molding sand that the dextrin of take is binding agent, comprising: by the weight portion of constitutive material, take return sand, quartz sand, vermiculite, steel fibre, furane resins, dextrin and gypsum, mix, be dry mixed 3-5 minute, then add water, wet mixing 5-8 minute.
Embodiment 2: the molding sand that the dextrin of take is binding agent, the weight portion of its constitutive material is that return sand 35, quartz sand 45, vermiculite 15, steel fibre 8, furane resins 5, dextrin 4, gypsum 2 and water are appropriate.
The preparation method of the molding sand that the dextrin of take is binding agent, comprising: by the weight portion of constitutive material, take return sand, quartz sand, vermiculite, steel fibre, furane resins, dextrin and gypsum, mix, be dry mixed 3-5 minute, then add water, wet mixing 5-8 minute.
Embodiment 3: the molding sand that the dextrin of take is binding agent, the weight portion of its constitutive material is: return sand 40, quartz sand 50, vermiculite 20, steel fibre 10, furane resins 8, dextrin 5, gypsum 3 and water are appropriate.
The preparation method of the molding sand that the dextrin of take is binding agent, comprising: by the weight portion of constitutive material, take return sand, quartz sand, vermiculite, steel fibre, furane resins, dextrin and gypsum, mix, be dry mixed 3-5 minute, then add water, wet mixing 5-8 minute.
The moulding-sand property that the present invention makes: green compression strength >=0.13Mpa, gas permeability >=82, moisture 3.3-3.8, compact rate of molding 45-55, shatter index (j :) 83-85%.
Claims (2)
1. the molding sand that the dextrin of take is binding agent, is characterized in that the weight portion of its constitutive material is: return sand 30-40, quartz sand 40-50, vermiculite 10-20, steel fibre 5-10, furane resins 3-8, dextrin 3-5, gypsum 1-3 and water are appropriate.
2. according to claim 1ly take the molding sand that dextrin is binding agent, the weight portion that it is characterized in that its constitutive material is that return sand 35, quartz sand 45, vermiculite 15, steel fibre 8, furane resins 5, dextrin 4, gypsum 2 and water are appropriate.