CN102634918A - Bamboo charcoal fiber fabric - Google Patents
Bamboo charcoal fiber fabric Download PDFInfo
- Publication number
- CN102634918A CN102634918A CN2012101249258A CN201210124925A CN102634918A CN 102634918 A CN102634918 A CN 102634918A CN 2012101249258 A CN2012101249258 A CN 2012101249258A CN 201210124925 A CN201210124925 A CN 201210124925A CN 102634918 A CN102634918 A CN 102634918A
- Authority
- CN
- China
- Prior art keywords
- silk
- bamboo
- master batch
- bamboo charcoal
- carbon fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bamboo charcoal fiber fabric which comprises surface yarns and bottom yarns, wherein the surface yarns are DTYs (Draw Textured Yarns) and account for 60-80% of the weight of the fabric; the bottom yarns are POYs (Polyester Pre-Oriented Yarns) and account for 20-40% of the weight of the fabric; and the DTYs are formed by the steps of dissolving slice raw materials in a spinning solution added with bamboo charcoal master batch and color master batch, extruding, filtering and then spraying through a spinneret plate. Through adding the bamboo charcoal master batch and the color master batch in the surface yarns, the bamboo charcoal fiber fabric is green and environment-friendly, is high in color fastness and uniform in color, has the heath care functions of inhibiting and resisting bacteria, generating negative ions, emitting far infrared rays, resisting ultraviolet rays and the like, is clean and is free of pollution because a dyeing process is reduced in a weaving process, realizes the purposes of saving energy, reducing emission and lowering the cost, and can be naturally degraded.
Description
Technical field
The present invention relates to the weaving face fabric technical field, particularly relate to a kind of bamboo-carbon fibre lining.
Background technology
As everyone knows, the face weave process mainly comprises spinning, and weft knitting, warp braiding are made; Typing; Technologies such as dyeing and finishing, dyeing and finishing technology wherein can produce a large amount of dyeing waste waters, and environment is caused harm to a certain degree; Though present technological level is constantly improved innovation, but still can't eradicate this type pollution.
Existing textiles because the fiber species that adopts is single, lacks health care, can't satisfy consumer's requirement.In the last few years, the weaving face fabric field constantly started the fiber revolution both at home and abroad, and the functional health textiles becomes the market mainstream.Therefore, the textiles that the bamboo charcoal regenerated celulose fibre is processed is very popular, and it not only has nature and environmental protection characteristic, and multiple functions such as far infrared, anion, heat accumulation thermal are more arranged, and the very suitable system of knitting wears next to the skin clothes.The function of bamboo-carbon fibre has permanent, does not receive the influence of washing times.
Existing bamboo-carbon fibre lining is mainly used in underwear product, shirt, T-shirt, socks, towel, bedding and CRUX dress etc.; Bamboo-carbon fibre is natural to give full play to, environmental protection, multi-functional excellent specific property; Bamboo-carbon fibre is that the textile product exploitation provides brand-new raw material material, has also increased new shining point for production marketing simultaneously.
Yet; This type bamboo charcoal lining is in the filament spinning process, to have added the bamboo charcoal master batch, makes typing through weft knitting, warp braiding then; Again with grey cloth dyeing and finishing, post processing; So not only caused a large amount of dischargings of dyeing waste water, and can influence each functional characteristic of bamboo charcoal lining, mainly shown as: the look strong degree is poor, color spot is arranged.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of bamboo-carbon fibre lining; Environmental protection, the look strong degree is high, and color and luster is even; And have bacteriostasis antibiosis, produce anion, health care such as emitting far-infrared, uvioresistant; Reduce dyeing in the face weave process, cleanliness without any pollution, this falls in the realization energy-saving and emission-reduction.
For solving the problems of the technologies described above; The technical scheme that the present invention adopts is: a kind of bamboo-carbon fibre lining is provided, comprises face silk and end silk, said silk is DTY terylene texturing silk; Account for the 60-80% of lining weight; Silk of the said end is the POY polyester filament, accounts for the 20-40% of lining weight, said DTY terylene texturing silk for the section raw material in the spinning solution that has added bamboo charcoal master batch and Masterbatch, dissolve, again through extruding, filtration after spinnerets spray.
In preferred embodiment of the present invention, said the DTY terylene texturing silk that silk is 50-400D, silk of the said end is the POY polyester filament of 50-500D.
In preferred embodiment of the present invention, said bamboo charcoal master batch is the white master batch of bamboo charcoal.
In preferred embodiment of the present invention, said section raw material is a moisture less than 0.003% PET section, PA66 section or PP section.
In preferred embodiment of the present invention, the temperature when said section raw material dissolves in the spinning solution that has added bamboo charcoal master batch and Masterbatch is 280-300 ℃.
In preferred embodiment of the present invention, the pressure during said the extruding is 9-12MPa.
In preferred embodiment of the present invention, selecting precision for use during said filtration is the stainless steel nonwoven fabric metal filter screen of 15-30 μ m.
In preferred embodiment of the present invention, the spray silk speed when said spinnerets sprays is 3000-3200m/min.
The invention has the beneficial effects as follows: a kind of bamboo-carbon fibre lining of the present invention; Bamboo charcoal master batch and Masterbatch have been added in its face silk; The honeycomb microporous structure that each root bamboo-carbon fibre silk is run through inside and outside all being; Make the bamboo-carbon fibre lining have bacteriostasis antibiosis, soft and smooth soft warm, hydroscopic fast-drying, ventilative, produce health cares such as anion, emitting far-infrared, uvioresistant, but also natural degradation simultaneously; And just adopt Masterbatch painted to filament in the spray silk stage; For road, back process reduces dyeing; Do not produce dyeing waste water, clean environment firendly, pollution-free more realizes that this falls in energy-saving and emission-reduction; The formed filament pigment of spinning is distributed in the inside of silk thread structure, makes look strong degree height, the color and luster of fabric lining even.
The specific embodiment
Set forth in detail in the face of preferred embodiment of the present invention down, thereby protection scope of the present invention is made more explicit defining so that advantage of the present invention and characteristic can be easier to it will be appreciated by those skilled in the art that.
The embodiment of the invention comprises:
A kind of bamboo-carbon fibre lining; Comprise face silk and end silk; Said silk is DTY terylene texturing silk, accounts for the 60-80% of lining weight, and silk of the said end is the POY polyester filament; Account for the 20-40% of lining weight, said DTY terylene texturing silk for the section raw material in the spinning solution that has added bamboo charcoal master batch and Masterbatch, dissolve, again through extruding, filtration after spinnerets spray.
Wherein, said the DTY terylene texturing silk that silk is 50-400D, silk of the said end is the POY polyester filament of 50-500D.
Embodiment one:
A kind of bamboo-carbon fibre lining; Comprise face silk and end silk; Said silk is 167D/36F DTY terylene texturing silk, accounts for 65% of lining weight, and silk of the said end is a 265D/36F POY polyester filament; Account for 35% of lining weight, said DTY terylene texturing silk for the section raw material in the spinning solution that has added bamboo charcoal master batch and Masterbatch, dissolve, again through extruding, filtration after spinnerets spray.
Wherein, Said bamboo charcoal master batch is the white master batch of bamboo charcoal; Said section raw material is a moisture less than 0.003% PET section, and the temperature when said section raw material dissolves in the spinning solution that has added bamboo charcoal master batch and Masterbatch is 280 ℃, and the pressure during said the extruding is 10MPa; Selecting precision for use during said filtration is the stainless steel nonwoven fabric metal filter screen of 30 μ m, and the spray silk speed during said spinnerets ejection is 3200m/min.
Embodiment two:
A kind of bamboo-carbon fibre lining; Comprise face silk and end silk; Said silk is 150D/96F DTY terylene texturing silk, accounts for 70% of lining weight, and silk of the said end of end silk is a 75D/36F POY polyester filament; Account for 30% of lining weight, said DTY terylene texturing silk for the section raw material in the spinning solution that has added bamboo charcoal master batch and Masterbatch, dissolve, again through extruding, filtration after spinnerets spray.
Wherein, Said bamboo charcoal master batch is the white master batch of bamboo charcoal; Said section raw material is a moisture less than 0.003% PA66 section, and the temperature when said section raw material dissolves in the spinning solution that has added bamboo charcoal master batch and Masterbatch is 290 ℃, and the pressure during said the extruding is 8.5MPa; Selecting precision for use during said filtration is the stainless steel nonwoven fabric metal filter screen of 25 μ m, and the spray silk speed during said spinnerets ejection is 3100m/min.
Bamboo-carbon fibre lining of the present invention; Can be made into household textiless such as carpet, woollen blanket, nightwear, bathrobe; Have good skin-friendly, hygroscopicity and gas permeability, can be antibacterial, antibiotic, remove mite and deodorization, arthritis, scapulohumeral periarthritis, insomnia etc. are had good improvement effect.
The present invention has disclosed a kind of bamboo-carbon fibre lining; Bamboo charcoal master batch and Masterbatch have been added in its face silk; The honeycomb microporous structure that each root bamboo-carbon fibre silk is run through inside and outside all being; Make the bamboo-carbon fibre lining have bacteriostasis antibiosis, soft and smooth soft warm, hydroscopic fast-drying, ventilative, produce health cares such as anion, emitting far-infrared, uvioresistant, but also natural degradation simultaneously; And just adopt Masterbatch painted to filament in the spray silk stage; For road, back process reduces dyeing; Do not produce dyeing waste water, clean environment firendly, pollution-free more realizes that this falls in energy-saving and emission-reduction; The formed filament pigment of spinning is distributed in the inside of silk thread structure, makes look strong degree height, the color and luster of fabric lining even.
The above is merely embodiments of the invention; Be not so limit claim of the present invention; Every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; Or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (8)
1. bamboo-carbon fibre lining; It is characterized in that, comprise face silk and end silk, said silk is DTY terylene texturing silk; Account for the 60-80% of lining weight; Silk of the said end is the POY polyester filament, accounts for the 20-40% of lining weight, said DTY terylene texturing silk for the section raw material in the spinning solution that has added bamboo charcoal master batch and Masterbatch, dissolve, again through extruding, filtration after spinnerets spray.
2. bamboo-carbon fibre lining according to claim 1 is characterized in that, said the DTY terylene texturing silk that silk is 50-400D, and silk of the said end is the POY polyester filament of 50-500D.
3. bamboo-carbon fibre lining according to claim 1 is characterized in that, said bamboo charcoal master batch is the white master batch of bamboo charcoal.
4. bamboo-carbon fibre lining according to claim 1 is characterized in that, said section raw material is a moisture less than 0.003% PET section, PA66 section or PP section.
5. bamboo-carbon fibre lining according to claim 1 is characterized in that, the temperature when said section raw material dissolves in the spinning solution that has added bamboo charcoal master batch and Masterbatch is 280-300 ℃.
6. bamboo-carbon fibre lining according to claim 1 is characterized in that, the pressure during said the extruding is 9-12MPa.
7. bamboo-carbon fibre lining according to claim 1 is characterized in that, selecting precision for use during said filtration is the stainless steel nonwoven fabric metal filter screen of 15-30 μ m.
8. bamboo-carbon fibre lining according to claim 1 is characterized in that, the spray silk speed when said spinnerets sprays is 3000-3200m/min.