CN102585619B - Environment-friendly emulsion paint with high solid volume content - Google Patents
Environment-friendly emulsion paint with high solid volume content Download PDFInfo
- Publication number
- CN102585619B CN102585619B CN201210016148.5A CN201210016148A CN102585619B CN 102585619 B CN102585619 B CN 102585619B CN 201210016148 A CN201210016148 A CN 201210016148A CN 102585619 B CN102585619 B CN 102585619B
- Authority
- CN
- China
- Prior art keywords
- emulsion paint
- revs
- component
- minutes
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an environment-friendly emulsion paint with high solid volume content, which comprises the following components in percentage by weight: 30.0-40.0% of styrene acrylic emulsion, 0.8%-2% of dispersing agent, 0.2%-1% of wetting agent, 0.1%-0.5% of defoamer, 1.0%-10.0% of propylene glycol, 30.0%-40.0% of color filler, 1.5%-2.0% of film forming adjuvant, 0.02%-0.05% of antiseptic bactericide, 0.1%-0.2% of pH modifier, 0.2%-2.0% of thickener and balance of water. According to the invention, the solid volume content of the emulsion paint can be effectively improved; and the emulsion paint is non-toxic, harmless and low in VOC (volatile organic compound) content. Therefore, the emulsion paint disclosed by the invention is an excellent-performance waterborne environment-friendly emulsion paint, and can be widely applied to the coating construction of various wall surfaces.
Description
Technical field
The present invention relates to a kind of environmental protection wall surface paint for building, be specifically related to one and there is high volume and admittedly contain, can improve film thickness and reduce carbon emission, save the environment friendly emulsion paint of use cost.
Background technology
International community, causes global air temperature warming, Melting Glaciers:, sea-level rise etc. to ascribe surging of CO2 to Greenhouse effect, so destroyed the global environment that the mankind depend on for existence now.In order to contain excessive emissions CO2, balance of plant has been signed Kyoto Protocol and " Copenhagen letter of intent ", in November, 2009, Chinese Government proposed, will decline on the basis of 2005 target of 40%-45% of the year two thousand twenty per GDP carbon emission amount, indicates that from then on China go on low-carbon economy development.Also include the Chinese government's 12 energy-saving and emission-reduction important goals simultaneously in.Find out that thus the global environment that the reduction of CO2 is depended on for existence to us is how important.
As everyone knows, in traditional emulsion paint, the content of water is at 20%-50%, even higher, and within 2010, Architectural Paint in China ultimate production reaches 3,520,000 tons, and wherein water content approximately reaches ten thousand tons of 70.4-176.To liberate ten tons of trucies as example, fully loaded per 100 km oil consumption is 20 liters, the carbon emission amount of 1 liter of 93# gasoline of burning is about 3.8kg, suppose that emulsion paint product needed per ton betransported 1000km and could be used, emulsion paint in 2010 is because the carbon emission amount of transport of water is up to ten thousand tons of 5.4-13.4, with the common tree growing 50 years, every day can absorbing carbon dioxide 5.023kg, by there being every year 3/4 time can carry out photosynthesis, every year can absorbing carbon dioxide 1.375 tons, need the trees of ten thousand age of trees of 3.92-9.75 more than 50 years can run out of consequent carbon emission.Add processing, the carbon emission amount of processing, actual carbon emission amount will be far above this.
After emulsion paint construction finishes to treat volatilizable thing volatilization; the paint film of staying building surface is only the effective constituent of protection body of wall; conventionally admittedly contain and weigh with volume; therefore how to reduce the content of water in emulsion paint; the volume that improves product contains admittedly, not only greatly reduces the carbon emission of bringing thus, meets national energy-saving and reduces discharging policy; also can reduce costs, be of value to raising Social benefit and economic benefit simultaneously.
Summary of the invention
The environment friendly emulsion paint that the object of the present invention is to provide a kind of high volume admittedly to contain, its use can reduce carbon emission, reduces costs.
For achieving the above object, the present invention adopts following technical scheme:
The environment friendly emulsion paint that high volume contains admittedly, its component and content (percentage meter by weight) are as follows:
Described benzene emulsion is one or more the mixture in the TL-615B of the good BLJ-818 of ROHM AND HAAS DC-420, Poly, sunrise.
Described dispersion agent is selected from least one in SN5027, SN5029, SN5040, the Clariant KANALENE92 of Sheng Nuopuke.
Described wetting agent is selected from least one in WET 996, WET 997, the DOW Chemical CF-10 of Sheng Nuopuke.
It is peaceful that described defoamer is selected from NXZ, the section of Sheng Nuopuke
at least one in A10, Blackburn CF-245.
Described color stuffing is one or more the mixture in Rutile type Titanium Dioxide, dicalcium powder, kaolin, talcum powder; Rutile type Titanium Dioxide is selected from
r-902,
any in R-960, TRONOX CR-826.
Described film coalescence aid is the TEAXNAL of Yi Shiman.
Described anticorrosion and bactericidal agent is selected from the Sol of ROHM AND HAAS
mV, Sol
ePWKathon
tMthe Rocima of LXE, ROHM AND HAAS
tMat least one in 361.
Described PH conditioning agent is selected from least one in the AMP-95 of concentration 28% ammoniacal liquor, DOW Chemical.
Described thickening material is selected from least one in the ASE-60 of THICKENER 625N, ROHM AND HAAS of sub-THICKENER 629N, Sheng Nuopuke across imperial NATROSAL 250 HBR, Sheng Nuopuke.
Know-why of the present invention: the present invention has selected the benzene emulsion of the low VOC of mechanical stability excellence, this type of benzene emulsion is introduced MAA (methacrylic acid) group, for providing hydroxyl, molecular chain carries out chemically crosslinked, the carboxylic acid functional of MAA can be promoted latex mechanical stability greatly, simultaneously when pH value is transferred to alkalescence, carboxyl dissociation in copolymer emulsion, producing electric charge forms repulsion and fully stretches, mutually exclusive between polymer particle, emulsion viscosity and mechanical stability are significantly improved.
In emulsion paint technique, emulsion was added and stirring at low speed in the paint stage at present, the present invention adds place of water as dispersion medium high speed dispersion in the making beating stage emulsion, therefore good mechanical stability is the precondition that obtains excellent product performance, the usage quantity that the present invention is based on above-mentioned principle minimizing water improves small product size solid content, obtains the emulsion paint product of high performance-price ratio.
The present invention adopts A, B component, and A component is that high volume contains emulsion paint admittedly, and B component is efficient polyurethane thickener, and both use in the time using latting drown simultaneously, avoid causing viscosity to decline rapidly because being watered in a large number, guarantee product workability.
The present invention compared with prior art, has following excellent effect:
1, low VOC, APEO, guarantees that product meets environmental requirement;
2, high volume contains admittedly, can increase film thickness, effectively wall guard;
3, high latting drown ratio, paint: water=100: 40-80, cost performance is high;
4, low carbon products, meets national energy-saving and reduces discharging policy;
5, strong, the water tolerance of film adhesive, alkaline resistance properties are excellent.
Embodiment
Example 1:
A component: 100 parts of meters take 33.0 parts, water by weight, benzene emulsion TL-615B:30 part, under the rotating speed of 300～600 revs/min, drop into successively dispersion agent SN 5027:1.0 part, thickening material NATROSAL 250 HBR:0.3 parts, wetting agent WET 996:0.3 part, defoamer NXZ:0.3 part, propylene glycol: 1.2 parts, disperse 5 minutes; Under 600～1000 revs/min of rotating speeds, drop into Rutile type Titanium Dioxide
r-902:26.0 part, kaolin: 5.0 parts; Under 1000～1300 revs/min of rotating speeds, disperse 20～30 minutes; Inspection by sampling fineness≤50 micron; Under the rotating speed of 300～600 revs/min, drop into successively film coalescence aid TEAXNAL:1.5 part, anticorrosion and bactericidal agent EPWKathon
tMlXE:0.03 part, disperseed after 5 minutes, and PH conditioning agent AMP-95:0.17 part, defoamer NXZ:0.2 part, thickening material THICKENER 629N:0.4 part, disperse 5 minutes; Inspection by sampling; After qualified, filter and package.
B component: thickening material THICKENER 629N:0.6 part.
Using method: by B component in paint: water=100: 50 ratio, pre-soluble in water after, adding while stirring in A component, can use until mix.
This emulsion paint detection method, project and detected result are shown in subordinate list 1,2.
Example 2:
A component: 100 parts of meters take 27.0 parts, water by weight, benzene emulsion DC-420:32 part, under the rotating speed of 300～600 revs/min, drop into successively dispersion agent SN 5029:0.8 part, thickening material NATROSAL 250 HBR:0.1 parts, wetting agent WET 997:0.5 part, defoamer
a10:0.3 part, propylene glycol: 1.0 parts, disperse 5 minutes; Under 600～1000 revs/min of rotating speeds, drop into Rutile type Titanium Dioxide
r-902:25.8 part, talcum powder: 10.0 parts; Under 1000～1300 revs/min of rotating speeds, disperse 20～30 minutes; Inspection by sampling fineness≤50 micron; Under the rotating speed of 300～600 revs/min, drop into successively film coalescence aid TEAXNAL:1.6 part, anticorrosion and bactericidal agent EPWKathon
tMlXE:0.05 part, disperseed after 5 minutes, and PH conditioning agent AMP-95:0.15 part, defoamer CF-245:0.2 part, thickening material THICKENER 629N:0.1 part, disperse 5 minutes; Inspection by sampling; After qualified, filter and package.
B component: thickening material THICKENER 625N:0.4 part.
Using method: by B component in paint: water=100: 54 ratio, pre-soluble in water after, adding while stirring in A component, can use until mix.
This emulsion paint detection method, project and detected result are shown in subordinate list 1,2.
Example 3:
100 parts of meters take 22.0 parts, water by weight, benzene emulsion BLJ-818:40 part, under the rotating speed of 300～600 revs/min, drop into successively dispersion agent Dispersant 5040:1.0 part, thickening material NATROSAL 250 HBR:0.2 parts, wetting agent CF-10:0.2 part, defoamer
a10:0.2 part, propylene glycol: 1.0 parts, disperse 5 minutes; Under 600～1000 revs/min of rotating speeds, drop into Rutile type Titanium Dioxide
18.0 parts of R-902:15.0 part, dicalcium powders; Under 1000～1300 revs/min of rotating speeds, disperse 20～30 minutes; Inspection by sampling fineness≤50 micron; Under the rotating speed of 300～600 revs/min, drop into successively film coalescence aid TEAXNAL:1.8 part, anticorrosion and bactericidal agent EPWKathon
tMlXE:0.04 part, disperseed after 5 minutes, and PH conditioning agent AMP-95:0.16 part, defoamer DEFOAMER 154S:0.2 part, disperse 5 minutes; Inspection by sampling; After qualified, filter and package.
B component: thickening material THICKENER 625N:0.2 part.
Using method: by B component in paint: water=100: 60 ratio, pre-soluble in water after, adding while stirring in A component, can use until mix.
This emulsion paint detection method, project and detected result are shown in subordinate list 1,2.
Three case study on implementation of the environment friendly emulsion paint that a kind of high volume of the present invention contains admittedly according to requirements after latting drown by GB/9756-2009 and GB 18582-2008 standard testing, test result is as following table 1:
Environment friendly emulsion paint technical performance index and test result that table 1 high volume contains admittedly
It is as shown in table 2 that three case study on implementation A components of the environment friendly emulsion paint that a kind of high volume of the present invention contains admittedly detect data
The environment friendly emulsion paint test result that table 2 high volume contains admittedly
Claims (1)
1. the preparation method of the environment friendly emulsion paint that a high volume contains admittedly, it is characterized in that: A component: 100 parts of meters take 33.0 parts, water by weight, benzene emulsion TL-615B:30 part, under the rotating speed of 300～600 revs/min, drop into successively dispersion agent SN 5027:1.0 part, thickening material NATROSOL 250HBR:0.3 part, wetting agent WET 996:0.3 part, defoamer NXZ:0.3 part, propylene glycol: 1.2 parts, disperse 5 minutes; Under 600～1000 revs/min of rotating speeds, drop into Rutile type Titanium Dioxide
-902:26.0 part, kaolin: 5.0 parts; Under 1000～1300 revs/min of rotating speeds, disperse 20～30 minutes; Inspection by sampling fineness≤50 micron; Under the rotating speed of 300～600 revs/min, drop into successively film coalescence aid TEXANOL:1.5 part, anticorrosion and bactericidal agent EPW Kathon
tMlXE:0.03 part, disperseed after 5 minutes, and pH adjusting agent AMP-95:0.17 part, defoamer NXZ:0.2 part, thickening material THICKENER 629N:0.4 part, disperse 5 minutes; Inspection by sampling; After qualified, filter and package;
B component: thickening material THICKENER 629N:0.6 part;
Using method: by B component in paint: the ratio of water=100:50, pre-soluble in water after, adding while stirring in A component, can use until mix.