CN102516687A - Modifier for processing polyvinyl chloride power liner - Google Patents
Modifier for processing polyvinyl chloride power liner Download PDFInfo
- Publication number
- CN102516687A CN102516687A CN2011104054562A CN201110405456A CN102516687A CN 102516687 A CN102516687 A CN 102516687A CN 2011104054562 A CN2011104054562 A CN 2011104054562A CN 201110405456 A CN201110405456 A CN 201110405456A CN 102516687 A CN102516687 A CN 102516687A
- Authority
- CN
- China
- Prior art keywords
- modifier
- polyvinyl chloride
- parts
- electric power
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a modifier for processing a polyvinyl chloride power liner. The modifier comprises the following components in parts by weight: 2.5-3 parts of chlorinated polyvinyl chloride, 1.2-2.2 parts of rubber plastic modifier, 3-4 parts of calcium zinc stabilizer, 0.1-0.4 parts of epoxy soybean oil, 0.2-0.4 parts of white oil, 0.2-0.4 parts of molybdate red, and 45-55 parts of light calcium carbonate. The invention has simple process, convenient operation and low cost, and can be widely applicable for the processing field of polyvinyl chloride power liners.
Description
Technical field
The present invention relates to a kind of processing of plastic properties-correcting agent, particularly relate to a kind of modifier that is used for SE electric power bushing pipe.
Background technology
Up to now; The prescription of traditional modifier that is used for SE electric power bushing pipe, being used for of producing, SE electric power bushing pipe fragility was big, toughness and intensity difference; And production cost is higher; The demand that can not adapt to market has limited its application, and this is the problem that the present invention will solve.
Summary of the invention
The objective of the invention is provides a kind of modifier that is used for SE electric power bushing pipe in order to overcome the deficiency of above-mentioned background technology, makes that it has that technology is simple, simple operation, cheap characteristics.
To achieve these goals, technical scheme of the present invention is such:
A kind of modifier that is used for SE electric power bushing pipe provided by the invention, described modifier comprises following component and weight part: chlorinated polyvinyl chloride 2.5～3; Rubber and plastic properties-correcting agent 1.2～2.2; Calcium zinc stabilizer 3～4; Epoxy soybean oil 0.1～0.4; White oil 0.2～0.4; Molybdenum red 0.2～0.4; Light calcium carbonate 45～55.
In technique scheme, described modifier comprises following component and weight part: chlorinated polyvinyl chloride 2.6～2.9; Rubber and plastic properties-correcting agent 1.3～2.0; Calcium zinc stabilizer 3.1～3.8; Epoxy soybean oil 0.15～0.35; White oil 0.25～0.38; Molybdenum red 0.25～0.38; Light calcium carbonate 48～54.
In technique scheme, described modifier comprises following component and weight part: chlorinated polyvinyl chloride 2.8; Rubber and plastic properties-correcting agent 1.8; Calcium zinc stabilizer 3.2; Epoxy soybean oil 0.3; White oil 0.3; Molybdenum red 0.35; Light calcium carbonate 50.
In technique scheme, described rubber and plastic properties-correcting agent is to be composited by ethylene vinyl acetate and aluminic acid lipoprotein coupling agent, and its proportioning is an ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=1.5～2.5: 0.5～1.
In technique scheme, described proportioning is an ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=2: 0.8.
The modifier that is used for SE electric power bushing pipe of the present invention has following beneficial effect: novel, technology is simple, simple operation, cheap, pollution-free; Remove the Methyl methacrylate-butadiem-styrene copolymer in traditional production SE electric power bushing pipe prescription; The rubber and plastic properties-correcting agent that adds equivalent; Do not influence transparency, can increase the quantity of weighting material, effectively reduce and produce SE electric power bushing pipe supplementary material cost; Improve electric power bushing pipe intensity and toughness, improve the quality of product.The present invention can industrialized mass production, can be widely used in the manufacture field of SE electric power bushing pipe.
Embodiment
The modifier that is used for the SE electrical casing pipe of the present invention is combined specific embodiment, its technical scheme is described in detail as follows, but this embodiment should not be construed as limitation of the present invention.
Embodiment 1
Modifier of the present invention is joined by follow procedure system:
One, produces each component of modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent
Get ethylene vinyl acetate 1.5, aluminic acid lipoprotein coupling agent 0.5 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of each component and weight part:
Chlorinated polyvinyl chloride 2.5, rubber and plastic properties-correcting agent 1.2, calcium zinc stabilizer 3, epoxy soybean oil 0.1, white oil 0.2, molybdenum red 0.2, light calcium carbonate 45, subsequent use.
Two, the preparation of said modifier
1, batch mixing: above-mentioned each ingredients weight parts for preparing is mixed, drop into mixing and stirring in the kneader together, heating can stop to heat to 135 ℃, subsequent use;
2, discharging is packed: can discharging packing, i.e. finished product---described modifier after the above-mentioned batch mixing that processes is cooled to normal temperature.
Embodiment 2
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, produces each component of modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent
Get ethylene vinyl acetate 2, aluminic acid lipoprotein coupling agent 0.8 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of each component and weight part:
Chlorinated polyvinyl chloride 2.8, rubber and plastic properties-correcting agent 1.8, calcium zinc stabilizer 3.2, epoxy soybean oil 0.3, white oil 0.3, molybdenum red 0.35, light calcium carbonate 50, subsequent use.
Embodiment 3
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, produces each component of modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent
Get ethylene vinyl acetate 1.8, aluminic acid lipoprotein coupling agent 0.6 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of each component and weight part:
Chlorinated polyvinyl chloride 2.6, rubber and plastic properties-correcting agent 1.3, calcium zinc stabilizer 3.1, epoxy soybean oil 0.15, white oil 0.25, molybdenum red 0.25, light calcium carbonate 48, subsequent use.
Embodiment 4
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, produces each component of modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent
Get ethylene vinyl acetate 2.5, aluminic acid lipoprotein coupling agent 1 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of each component and weight part:
Chlorinated polyvinyl chloride 3, rubber and plastic properties-correcting agent 2.2, calcium zinc stabilizer 4, epoxy soybean oil 0.4, white oil 0.4, molybdenum red 0.4, light calcium carbonate 55, subsequent use.
Embodiment 5
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, produces each component of modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent
Get ethylene vinyl acetate 2.5, aluminic acid lipoprotein coupling agent 1 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of each component and weight part:
Chlorinated polyvinyl chloride 2.9, rubber and plastic properties-correcting agent 2.0, calcium zinc stabilizer 3.8, epoxy soybean oil 0.35, white oil 0.38, molybdenum red 0.38, light calcium carbonate 54, subsequent use.
Obviously, those skilled in the art can carry out various changes and modification to the present invention and not break away from the spirit and scope of the present invention.Like this, belong within the scope of claim of the present invention and equivalent technologies thereof if of the present invention these are revised with modification, then the present invention also is intended to comprise these changes and modification interior.
The content of not doing in this specification sheets to describe in detail belongs to this area professional and technical personnel's known prior art.
Claims (5)
1. modifier that is used for SE electric power bushing pipe, it is characterized in that: described modifier comprises following component and weight part: chlorinated polyvinyl chloride 2.5～3; Rubber and plastic properties-correcting agent 1.2～2.2; Calcium zinc stabilizer 3～4; Epoxy soybean oil 0.1～0.4; White oil 0.2～0.4; Molybdenum red 0.2～0.4; Light calcium carbonate 45～55.
2. the modifier that is used for SE electric power bushing pipe according to claim 1 is characterized in that: described modifier comprises following component and weight part: chlorinated polyvinyl chloride 2.6～2.9; Rubber and plastic properties-correcting agent 1.3～2.0; Calcium zinc stabilizer 3.1～3.8; Epoxy soybean oil 0.15～0.35; White oil 0.25～0.38; Molybdenum red 0.25～0.38; Light calcium carbonate 48～54.
3. the modifier that is used for SE electric power bushing pipe according to claim 1 is characterized in that: described modifier comprises following component and weight part: chlorinated polyvinyl chloride 2.8; Rubber and plastic properties-correcting agent 1.8; Calcium zinc stabilizer 3.2; Epoxy soybean oil 0.3; White oil 0.3; Molybdenum red 0.35; Light calcium carbonate 50.
4. according to each described modifier that is used for SE electric power bushing pipe in the claim 1 to 3; It is characterized in that: described rubber and plastic properties-correcting agent is to be composited by ethylene vinyl acetate and aluminic acid lipoprotein coupling agent, and its proportioning is an ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=1.5～2.5: 0.5～1.
5. the modifier that is used for SE electric power bushing pipe according to claim 4 is characterized in that: described proportioning is an ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=2: 0.8.