CN101240135B - 一种简易涂装的仿金属氟碳漆 - Google Patents
一种简易涂装的仿金属氟碳漆 Download PDFInfo
- Publication number
- CN101240135B CN101240135B CN2008100014687A CN200810001468A CN101240135B CN 101240135 B CN101240135 B CN 101240135B CN 2008100014687 A CN2008100014687 A CN 2008100014687A CN 200810001468 A CN200810001468 A CN 200810001468A CN 101240135 B CN101240135 B CN 101240135B
- Authority
- CN
- China
- Prior art keywords
- paint
- dimethylbenzene
- component
- agent
- fluorocarbon paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种外墙简易涂装的仿金属氟碳漆及制备方法，它含有单独包装的组份A、组份B及组份C。其中组份A(漆)有：氟碳树脂、防沉剂、醋酸乙烯纤维素浆、消泡剂、醋酸丁酯、二甲苯、氟碳改性聚丙烯酸流平剂、有机改性硅氧烷增滑流平剂、金属颜料浆、光稳定剂、紫外线吸收剂UV-1，组份B有：固化剂；组份C有：稀释剂，详细配比及其制备方法见说明书。本发明的优点是：1.造价较低；2.涂装简易，不需要面漆罩光；3.色彩与光泽均匀；4.超久的耐候性；5.优异的耐化学性；6.杰出的耐污染性。本发明适合于外墙表面的涂饰和保护。
Description
技术领域
本发明公开了一种外墙简易涂装的仿金属氟碳漆及制备方法。
技术背景
目前应用于外墙高性能涂装的产品主要有铝塑板、玻璃幕墙、磁砖等，不但消耗大量资源、污染环境、还存在安全隐患。现在市场上出现的仿金属氟碳漆也存在氟碳树脂含量低、抗化学性差、丰满度差、色彩与光泽不均匀、施工工序复杂、需要面漆罩光、造价高等缺点。
发明内容
本发明的目的是提供一种底、面漆通用的简易涂装的仿金属氟碳漆，不但简化了施工工序，提高了施工宽容性，降低了整体的施工造价，还解决了色彩与光泽不均匀、丰满度差等缺点。
本发明是这样实现的：一种简易涂装的仿金属氟碳漆及制备方法，配方配比：
组分A：
氟碳树脂 65-75份
防沉剂 8-12份
醋酸乙烯纤维素浆 5-8份
消泡剂 0.2-0.5份
醋酸丁酯 2-8份
二甲苯 2-10份
氟碳改性聚丙烯酸流平剂 0.1-0.5份
有机改性硅氧烷增滑流平剂0.1-0.3份
金属颜料浆 7-10份
光稳定剂 0.1-0.5份
紫外线吸收剂UV-1 0.1-0.5份
所述的防沉剂是将聚酰胺蜡与二甲苯按4∶1的比例先搅拌均匀制成。
所述的醋酸乙烯纤维素浆是将醋酸乙烯纤维素与二甲苯按4∶1的比例溶解均匀制成。
所述的金属颜料浆是将金属颜料粉(如铝银粉、金铜粉)与醋酸丁酯按3∶1先溶解均匀制成。
工艺程序是将氟碳树脂投入分散缸中并加进防沉剂、醋酸乙烯纤维素浆，消泡剂在800转/分钟的转速下搅拌5分钟，然后依次投入醋酸丁酯、二甲苯、氟碳改性聚丙烯酸流平剂、有机改性硅氧烷增滑流平剂、金属颜料浆、光稳定剂、紫外线吸收剂UV-1，再按1000-1200转/分钟的转速高速分散10-15分钟，待金属颜料浆完全分散均匀，检测合格后出料，即制成组分A成品。
所述的组分B(固化剂)是以六亚二异氰酸酯(HDI)为基料的脂肪族异氰酸酯。
所述的组分C(稀释剂)是由醋酸丁酯、环己酮和二甲苯按2∶1∶1的比例混合而成。
按组分配比A∶B∶C＝1∶0.1∶0.3-0.5，制作的仿金属氟碳漆直接喷涂在封闭处理好的水泥建筑外墙表面上，与现有技术相比有如下特点：1.造价低；2.涂装简易，不需要面漆罩光；3.色彩与光泽均匀；4.超久的耐候性；5.优异的耐化学性；6.杰出的耐污染性。
具体实施方式
实施例1
首先按比例称取原料，将氟碳树脂65份投入分散缸中并加进防沉剂10份、醋酸乙烯纤维素浆6份、消泡剂0.2份在800转/分钟的转速下搅拌5分钟，然后依次投入醋酸丁酯6份、二甲苯4.1份、氟碳改性聚丙烯酸流平剂0.2份、有机改性硅氧烷增滑流平剂0.1份、金属颜料浆8份、光稳定剂0.2份、紫外线吸收剂UV-10.2份，再按1000-1200转/分钟的转速高速分散10-15分钟，待金属颜料浆完全分散均匀，检测合格后出料，即制成成品组分A。组分配比A(漆)∶B(固化剂)∶C(稀释剂)＝1∶0.1∶0.3-0.5。
实施例2
首先按比例称取原料，将氟碳树脂68份投入分散缸中并加进防沉剂11份、醋酸乙烯纤维素浆6份、消泡剂0.2份在800转/分钟的转速下搅拌5分钟，然后依次投入醋酸丁酯4份、二甲苯2份、氟碳改性聚丙烯酸流平剂0.2份、有机改性硅氧烷增滑流平剂0.1份、金属颜料浆8.1份、光稳定剂0.3份，紫外线吸收剂UV-10.1份，再按1000-1200转/分钟的转速高速分散10-15分钟，待金属颜料浆完全分散均匀，检测合格后出料，即制成成品组分A。组分配比A(漆)∶B(固化剂)∶C(稀释剂)＝1∶0.1∶0.3-0.5。
实施例3
首先按比例称取原料，将氟碳树脂72份投入分散缸中并加进防沉剂9份、醋酸乙烯纤维素浆5份、消泡剂0.2份在800转/分钟的转速下搅拌5分钟，然后依次投入醋酸丁酯3.1份、二甲苯2份、氟碳改性聚丙烯酸流平剂0.2份、有机改性硅氧烷增滑流平剂0.1份、金属颜料浆8份、光稳定剂0.3份，紫外线吸收剂UV-10.1份，再按1000-1200转/分钟的转速高速分散10-15分钟，待金属颜料浆完全分散均匀，检测合格后出料，即制成成品组分A。组分配比A(漆)∶B(固化剂)∶C(稀释剂)＝1∶0.1∶0.3-0.5。
主要原材料名称、技术指标：
1.氟碳树脂
外观：无色或淡黄色透明液体
固含量％：52
氟含量％：24
羟值mgKOH/g：47±5
酸值mgKOH/g：5±1
粘度(涂-4杯)s：53±5
分子量：20000
Tg，℃：35
比重g/ml：1.1～1.15
溶剂：醋酸丁酯，二甲苯
特性：低粘度
2.聚酰胺蜡，德谦Desetele.229
外观：微黄色软蜡状
固含：20％
溶剂：二甲苯
比重：0.88
3.消泡剂：EFKA-2018
4.氟碳改性聚丙烯酸流平剂：EFKA3777
有效成份：100％
5.有机改性硅氧烷增滑流平剂：EFKA3033
有效成份：15％
溶剂：醋酸丁酯
6.酯酸乙烯纤维素：CAB-551-0.2
去离子型。
7.光稳定剂：化学名称：双(1，2，2，6，6-五甲基-4-哌啶基)癸二酸酯。
8.紫外线吸收剂UV-1：
化学名称：N-(乙氧基羰基苯基)-N’-甲基-N’-苯基甲醚
9.固化剂：化学名称：六亚二异氰酸酯(HDI)N-75
按标准HG/T3792-2005I型标准抽样检验，其主要性能指标如下表1。
| 序号 | 项目 | 技术指标 | 检验结果 |
| 1 | 容器中状态 | 搅拌后均匀无硬块 | 搅拌后均匀无硬块 |
| 2 | 细度，μm | 商定 | 35 |
| 3 | 溶剂可溶物氟含量，％ | ≥18 | 21 |
| 4 | 涂膜外观 | 正常 | 正常 |
| 5 | 适用期(5h) | 通过 | 通过 |
| 6 | 重涂性 | 重涂无障碍 | 重涂无障碍 |
| 7 | 附着力，级 | ≤1 | 1 |
| 8 | 耐酸性(168H) | 无异常 | 无异常 |
| 9 | 耐砂浆性(24H) | 无异常 | 无异常 |
| 序号 | 项目 | 技术指标 | 检验结果 |
| 10 | 耐水性(168H) | 无异常 | 无异常 |
| 11 | 耐湿冷热循环性(10次) | 无异常 | 无异常 |
| 12 | 耐洗刷性，次 | ≥10000 | 12000 |
| 13 | 耐污染性 | 通过 | 通过 |
| 14 | 耐溶剂擦拭性，次(二甲苯) | ≥100 | 120 |
| 15 | 耐人工气候老化性 | 2500小时不起泡、不脱落、不开裂 | 5000小时不起泡、不脱落、不开裂 |
| 商定 | 粉化：1级 | ||
| 商定 | 变色：1级 | ||
| 商定 | 失光：1级 |
Claims (6)
1.一种简易涂装的仿金属氟碳漆，其特征在于其配方配比：
组分A：
氟碳树脂 65-75份
防沉剂 8-12份
醋酸乙烯纤维素浆 5-8份
消泡剂 0.2-0.5份
醋酸丁酯 2-8份
二甲苯 2-10份
氟碳改性聚丙烯酸流平剂 0.1-0.5份
有机改性硅氧烷增滑流平剂 0.1-0.3份
金属颜料浆 7-10份
光稳定剂 0.1-0.5份
紫外线吸收剂UV-1 0.1-0.5份。
2.如权利要求1所述的一种简易涂装的仿金属氟碳漆，其特征之处在于：防沉剂是将聚酰胺蜡与二甲苯按4∶1的比例先搅拌均匀制成。
3.如权利要求1所述的一种简易涂装的仿金属氟碳漆，其特征之处在于：醋酸乙烯纤维素浆是将醋酸乙烯纤维素与二甲苯按4∶1的比例溶解均匀制成。
4.如权利要求1所述的一种简易涂装的仿金属氟碳漆，其特征之处在于：金属颜料浆是将金属颜料粉与醋酸丁酯按3∶1先溶解均匀制成。
5.如权利要求1所述的一种简易涂装的仿金属氟碳漆，其特征之处在于：组分B(固化剂)：是以六亚甲基二异氰酸酯(HDI)为基料的脂肪族异氰酸酯；组分C(稀释剂)：是由醋酸丁酯、环己酮和二甲苯按2∶1∶1的比例混合而成，按组分配比A∶B∶C＝1∶0.1∶0.3-0.5，制作的仿金属氟碳漆直接喷涂在封闭处理好的水泥建筑外墙表面。
6.如权利要求1所述的一种简易涂装的仿金属氟碳漆的制备方法，其特征之处在于：按比例称取原料，将氟碳树脂投入分散缸中并加进防沉剂、醋酸乙烯纤维素浆，消泡剂，在800转/分钟的转速下搅拌5分钟，然后依次投入醋酸丁酯、二甲苯、氟碳改性聚丙烯酸流平剂、有机改性硅氧烷增滑流平剂、金属颜料浆、光稳定剂、紫外线吸收剂UV-1，再按1000-1200转/分钟的转速高速分散10-15分钟，待金属颜料浆完全分散均匀，检测合格后出料，即制成成品组分A。