CN100489206C - Heat insulation board and its producing method - Google Patents
Heat insulation board and its producing method Download PDFInfo
- Publication number
- CN100489206C CN100489206C CNB2006100538842A CN200610053884A CN100489206C CN 100489206 C CN100489206 C CN 100489206C CN B2006100538842 A CNB2006100538842 A CN B2006100538842A CN 200610053884 A CN200610053884 A CN 200610053884A CN 100489206 C CN100489206 C CN 100489206C
- Authority
- CN
- China
- Prior art keywords
- cement
- weight portions
- layer
- cementing agent
- warming plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The heat insulating board includes antiwear cement layer, organic foam layer and outside reinforcing layer comprising hollow powder, sand, cement and adhesive mixed together. The production process of the heat insulating board includes the following steps: smearing emulsion adhesive to the surface of organic foam board and painting demolding agent to the inside of the mold; pouring cement slurry into the mold to form the antiwear cement layer; pouring the mixture of light hollow powder, sand, cement, foaming agent and adhesive into the mold to form the reinforcing layer; setting foamed polystyrene board, covering one mixture layer, drying and demolding. The heat insulating board has multifunction, excellent heat insulating effect, light weight, high compression strength, low cost and other advantages.
Description
Technical field
The present invention relates to constructional materials, particularly a kind of warming plate that is used for roofing or metope and preparation method thereof.
Background technology
The traditional architecture industry uses vermiculite as heat-barrier material, but because its construction trouble, and effect of heat insulation is undesirable again and be eliminated gradually in new norm of construction.Use polystyrene foam plate to become main flow as the thermal isolation material, this material heat-proof quality is good, and light weight is inexpensive; Its shortcoming is cracky and contraction, must show at it to add a cover surface layer.But because its cracky causes big difficulty for again the construction of surface layer.Usually can only overlay one deck wire gauze so that construction causes the raising of cost so again.For example, notification number is that 2222195 Chinese patent discloses a kind of light roof warming plate, it comprises contains polystyrol plastic foam plate layer, high strength cement mortar layer, it is characterized in that on above-mentioned foam layer, being provided with tempering plastic bonding agent layer, the alkali glass screen grid layer of cloth of high adhesion stress, and on this alkali glass screen grid layer of cloth, establish a floor height adhesion stress tempering plastic bonding agent layer again, be high-intensity cement sand bed then, above-mentioned multilayer shape structural slab is combined into one under certain pressure, and smooth moulding.Its weak point is that cost is higher, the inconvenience of making, construct.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, provide a kind of simple in structure, the intensity height, easy to make, lower-cost warming plate and preparation method thereof.
The present invention solves the problems of the technologies described above the technical scheme that is adopted:
A kind of warming plate comprises antiwear cement layer and the organic foam plate that is positioned under the antiwear cement layer, it is characterized in that: have by light hollow powder, sand, cement, blowing agent and cementing agent around described organic foam plate and mix the enhancement layer that constitutes.
For optimizing technique scheme, the measure that the present invention taked also comprises:
Described antiwear cement layer is the coloured cement wearing layer.
Described organic foam plate is styrenic foams plate or polystyrene foam plate.
The thickness of described antiwear cement layer is 1～5 millimeter, and the organic foam plate thickness is 15～25 millimeters, and the thickness of enhancement layer is 3～27 millimeters.
A kind of preparation method of warming plate is characterized in that comprising the steps:
Earlier smear the cementing agent emulsion on organic foam plate surface, air dry 60～120 minutes;
Be coated with the warming plate mould inner surface with release agent;
Make wear-resisting cement paste by following prescription:
Toner 8～20 weight portions, white cement 300～400 weight portions, cementing agent emulsion 15～30 weight portions, defoamer 2～5 weight portions,
Pour the raw material of said components into mixer and stir, be poured on the wear-resisting cement paste of making and make antiwear cement layer, air dry 30～60 minutes in the warming plate mould;
Make mixture by following prescription:
Cement 500～650 weight portions, quartz sand 200～300 weight portions, light hollow powder 55～80 weight portions, cementing agent 15～30 weight portions, blowing agent 4～8 weight portions, water 120～200 weight portions,
Pouring the raw material of said components into mixer stirs, the described mixture of making is poured in the warming plate mould makes enhancement layer, place the styrenic foams plate that coats cementing agent then, cover the mixture that one deck is made again on the surface of styrenic foams plate;
Air dry after 24～48 hours the demoulding get final product.
The technical scheme that the present invention can also adopt is:
The step that the raw material of described wear-resisting cement paste component is poured mixer into is:
Pour toner and white cement earlier into, pour the cementing agent emulsion again into after stirring and defoamer stirs.
The step that the raw material of described component of mixture is poured mixer into is:
Pour blowing agent and water earlier into, pour cement after stirring again into, quartz sand, light hollow powder and cementing agent stir.
Described cementing agent is an acrylic polymer, and described blowing agent is a polyoxyethylene alkyl phenyl ether sulfate, and described defoamer is a tributyl phosphate.
The prescription of described cementing agent emulsion is cementing agent 1 weight portion, water 2.5 weight portions.
Because the present invention has taked above-mentioned technical measures, it compared with prior art has following advantage:
1. a plate is multi-functional, waterproof, wear-resisting, decoration, fire-retardant, anti-white ant;
2. heat-insulating and energy-saving efficiently reaches effect cool in summer and warm in winter;
3. in light weight, compressive strength is high;
4. simple in structure, easy to make, cost is lower, easy construction.
Below be main performance index of the present invention:
Description of drawings
Fig. 1 is the structural representation of the embodiment of the invention.
The specific embodiment
Below in conjunction with accompanying drawing the present invention is described in further detail.
With reference to Fig. 1, the superiors of the present invention are coloured cement wearing layer 1, and below antiwear cement layer 1 is styrenic foams plate 3, fill by light hollow powder (floating powder), sand, cement and cementing agent around styrenic foams plate 3 and mix the enhancement layer 2 that constitutes.The thickness of antiwear cement layer 1 is 5 millimeters, and the thickness of styrenic foams plate 3 is 25 millimeters, and the thickness of the top and following enhancement layer 2 of styrenic foams plate 3 is respectively 12.5 millimeters, and the thickness of the enhancement layer 2 of styrenic foams plate 3 sides is 5 millimeters.The specification of warming plate is: long 300 millimeters, wide 300 millimeters, high 55 millimeters.
The preparation method of warming plate:
Embodiment 1:
Earlier smear the cementing agent emulsion on organic foam plate 3 surfaces, air dry 60～120 minutes; The prescription of cementing agent emulsion is cementing agent 1Kg, water 2.5Kg.Cementing agent is an acrylic polymer.
Be coated with the warming plate mould inner surface with release agent; Release agent with silicate of soda precipitation or sodium phosphate all can, the most frequently used still used oil.
Make wear-resisting cement paste by following prescription:
Toner 8Kg, white cement 300Kg, cementing agent emulsion 15Kg, cementing agent is an acrylic polymer, defoamer 2Kg, defoamer are tributyl phosphates.
Earlier pour the toner of said components and white cement into mixer and stir, pour cementing agent emulsion and defoamer again into and stir, become cement paste.Be poured on making antiwear cement layer 1 in the mould that adapts with warming plate appearance and size, air dry 30～60 minutes with the wear-resisting cement paste of making.
Make mixture by following prescription:
Cement 500Kg, quartz sand 200Kg, light hollow powder 55Kg, cementing agent 15Kg, blowing agent 4Kg, water 120Kg.Wherein cementing agent is an acrylic polymer, and blowing agent is a polyoxyethylene alkyl phenyl ether sulfate.
Pour the blowing agent in the raw material of said components and water into mixer earlier and stir, pour cement again into, quartz sand, light hollow powder and cementing agent stir, resulting mixture.The described mixture of making is poured on making enhancement layer 2 in the warming plate mould, places the styrenic foams plate 3 that coats cementing agent then, cover the mixture that one deck is made again on the surface of styrenic foams plate 3.
Air dry after 24 hours the demoulding get final product.
Embodiment 2:
Make wear-resisting cement paste by following prescription:
Toner 20Kg, white cement 400Kg, cementing agent emulsion 30Kg, defoamer 5Kg.
Make mixture by following prescription:
Cement 650Kg, quartz sand 300Kg, light hollow powder 80Kg, cementing agent 30Kg, blowing agent 8Kg, water 200Kg.
Other is with embodiment 1.
Claims (8)
1, a kind of warming plate, comprise antiwear cement layer (1) and be positioned at organic foam plate (3) under the antiwear cement layer (1), it is characterized in that: around described organic foam plate (3), have and mix the enhancement layer (2) that constitutes by light hollow powder, sand, cement, blowing agent and cementing agent.
2, warming plate according to claim 1 is characterized in that: described antiwear cement layer (1) is the coloured cement wearing layer.
3, warming plate according to claim 1 and 2 is characterized in that: described organic foam plate (3) is styrenic foams plate or polystyrene foam plate.
4, warming plate according to claim 1 and 2 is characterized in that: the thickness of described antiwear cement layer (1) is 1～5 millimeter, and organic foam plate (3) thickness is 15～25 millimeters, and the thickness of enhancement layer (2) is 3～27 millimeters.
5, a kind of preparation method of warming plate is characterized in that comprising the steps:
Earlier smear the cementing agent emulsion on organic foam plate (3) surface, air dry 60～120 minutes;
Be coated with the inner surface of warming plate mould with release agent;
Make wear-resisting cement paste by following prescription:
Toner 8～20 weight portions, white cement 300～400 weight portions, cementing agent emulsion 15～30 weight portions, defoamer 2～5 weight portions,
Pour the raw material of said components into mixer and stir, be poured on the wear-resisting cement paste of making and make antiwear cement layer (1), air dry 30～60 minutes in the warming plate mould;
Make mixture by following prescription:
Cement 500～650 weight portions, quartz sand 200～300 weight portions, light hollow powder 55～80 weight portions, cementing agent 15～30 weight portions, blowing agent 4～8 weight portions, water 120～200 weight portions,
Pouring the raw material of said components into mixer stirs, the described mixture of making is poured on makes enhancement layer (2) in the warming plate mould, place the styrenic foams plate (3) that coats cementing agent then, cover the mixture that one deck is made again on the surface of styrenic foams plate (3);
Air dry after 24～48 hours the demoulding get final product.
6, the preparation method of warming plate according to claim 5 is characterized in that: the step that the raw material of described wear-resisting cement paste component is poured mixer into is:
Pour toner and white cement earlier into, pour the cementing agent emulsion again into after stirring and defoamer stirs.
The step that the raw material of described component of mixture is poured mixer into is:
Pour blowing agent and water earlier into, pour cement after stirring again into, quartz sand, light hollow powder and cementing agent stir.
7, the preparation method of warming plate according to claim 5 is characterized in that: described cementing agent is an acrylic polymer, and described blowing agent is a polyoxyethylene alkyl phenyl ether sulfate, and described defoamer is a tributyl phosphate.
8, the preparation method of warming plate according to claim 5 is characterized in that: the prescription of described cementing agent emulsion is cementing agent 1 weight portion, water 2.5 weight portions.