CN109503109A - A kind of assembled architecture finishing partition material and preparation method thereof - Google Patents

A kind of assembled architecture finishing partition material and preparation method thereof Download PDF

Info

Publication number
CN109503109A
CN109503109A CN201811535363.XA CN201811535363A CN109503109A CN 109503109 A CN109503109 A CN 109503109A CN 201811535363 A CN201811535363 A CN 201811535363A CN 109503109 A CN109503109 A CN 109503109A
Authority
CN
China
Prior art keywords
parts
assembled architecture
core material
architecture finishing
partition material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811535363.XA
Other languages
Chinese (zh)
Inventor
杨雪
佘金波
冯身强
魏英杰
安偲玮
傅毅
黄丽萍
舒勤
刘国宏
王旭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Jiangong Industrialization Building Co Ltd
Original Assignee
Chengdu Jiangong Industrialization Building Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Jiangong Industrialization Building Co Ltd filed Critical Chengdu Jiangong Industrialization Building Co Ltd
Priority to CN201811535363.XA priority Critical patent/CN109503109A/en
Publication of CN109503109A publication Critical patent/CN109503109A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of assembled architecture finishing partition materials, including panel and core material, for the panel using Cement fibre reinforcing plate or without continuous calcium silicate board, the core material includes: polystyrene, cement, flyash, volcanic rock, inorganic magnesium salt, fire retardant, thickener, air entraining agent and water;Firstly, weighing raw material in proportion, stir evenly, core material slurry is made;Core material slurry obtained above is poured into assembled wallboard mold, bar frame is put into, is paved, vibrated and rolled and carry out molding, then natural curing is for 24 hours under the conditions of 25 DEG C;The core material blank good to above-mentioned maintenance carries out demoulding, and natural curing seven days, and the core material that assembled architecture finishing uses partition material is made;Core material obtained above is installed in conjunction with panel, obtains assembled architecture finishing partition material.Assembling type partition wall material of the invention has many advantages, such as intensity height, shock resistance, sound-insulating and heat-insulating, fire prevention.

Description

A kind of assembled architecture finishing partition material and preparation method thereof
Technical field
The present invention relates to assembled architecture technical field, in particular to a kind of assembled architecture finishing partition material and its Preparation method.
Background technique
Building industrialization and housing industrialization and Urbanization Construction require actively to promote prefabricated construction.Assembling type partition wall It is building industrialization important component.Current assembling type partition wall is generally made of ordinary portland cement, there is condensation The disadvantage that hardening is slow, demoulding time is long, production efficiency is low.And much enterprises are in order to accelerate production efficiency, using steam curing Method shorten striking time, but this needs complicated steaming and cultivating equipment, and enterprise needs to put into huge fund.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of assembled architecture finishing partition material and preparation method thereof, Assembling type partition wall material of the invention has many advantages, such as intensity height, shock resistance, sound-insulating and heat-insulating, fire prevention.
To achieve the above object, The technical solution adopted by the invention is as follows:
A kind of assembled architecture finishing partition material, including panel and core material, the panel are enhanced using Cement fibre Plate or without continuous calcium silicate board;
The core material includes the raw material of following parts by weight: 10 parts -12 parts of polystyrene, 100 parts -120 parts of cement, fine coal Grey 30 parts -50 parts, 30 parts -50 parts of volcanic rock, 100 parts -120 parts of inorganic magnesium salt, 0.5 part -1 part of additive, 50 parts -70 parts of water.
Preferably, the core material includes the raw material of following parts by weight: 11 parts of polystyrene, 110 parts of cement, flyash 40 Part, 40 parts of volcanic rock, 110 parts of inorganic magnesium salt, 0.75 part of additive, 60 parts of water.
Preferably, the inorganic magnesium salt includes magnesia, magnesium silicate, magnesium chloride and magnesium sulfate, the magnesia, silicic acid The weight ratio of magnesium, magnesium chloride and magnesium sulfate is 2.5:1:1:1.Magnesia has good heat resistance, insulating properties, stability and benefit When strong increasing tougheness, magnesia and polystyrene are used in combination, tensile strength and the shock resistance that can be obviously improved base material are strong Degree, improves the mechanical strength of wallboard;When magnesia and cement are used cooperatively, flexural strength and the shock resistance of wallboard can be improved Intensity.
Preferably, the magnesia is dead burned magnesia.Magnesium element content 91%-93% in dead burned magnesia, element silicon Content 2.7%-3.5%, calcium element content 1.8%-2%, fineness is between -200 mesh of 90 mesh, magnesium elements in dead burned magnesia Content is high, is conducive to the intensity for improving assembling type partition wall material.
Preferably, the additive includes fire retardant, thickener and air entraining agent, the fire retardant, thickener and air entraining agent Weight ratio be 2:1:1.
Preferably, the fire retardant is MCA fire retardant.The anti-of assembling type partition wall wallboard can be improved in addition MCA fire retardant Fire.
Preferably, the thickener is inorganic thickening agent, specially fume colloidal silica, sodium bentonite, organic swelling One or more of soil or diatomite.Inorganic thickening agent can increase substantially the moulding viscosity of slurry, yield stress and face Boundary's strain, increases the stickiness of slurry, to increase the resistance of lightweight aggregate particle floating, is conducive to particle in the slurry steady It is fixed.
Preferably, the air entraining agent is rosin tree lipid air entraining agent.The introduced bubble of rosin tree lipid air entraining agent uniformly, Stablize, there is extraordinary compatibility with cement.Air entraining agent is added can introduce suitable bubble in the slurry, can reduce slurry The density of material, reduces the gap of particles of aggregates and slurry density, to reduce aggregate buoyancy, improves aggregate in partition wall wallboard The uniformity in portion improves the durability of partition wall.
Preferably, the polystyrene is the granular foam polystyrene of partial size 1mm-5mm.
The present invention also provides a kind of preparation methods of assembled architecture finishing partition material, and its technical solution is as follows:
A kind of assembled architecture finishing preparation method of partition material, comprising the following steps:
S1: weigh in proportion polystyrene, cement, flyash, volcanic rock, magnesia, magnesium silicate, magnesium chloride, magnesium sulfate, Fire retardant, thickener, air entraining agent and water, stir evenly, and core material slurry is made;
S2: core material slurry obtained above is poured into assembled wallboard mold, bar frame is put into, paved, vibrated Molding is carried out with rolling, then natural curing is for 24 hours under the conditions of 20 DEG C -30 DEG C;
S3: the core material blank good to above-mentioned maintenance carries out demoulding, and natural curing seven days, and assembled architecture finishing is made and uses The core material of partition material;
S4: core material obtained above is installed in conjunction with panel, obtains assembled architecture finishing partition material.
The beneficial effects of the present invention are:
1, assembled architecture finishing of the invention has largely used granules of polystyrene with partition material, has good guarantor Warm nature energy, heat loss rate are far below brick wall masonry, substantially increase the energy-saving effect of building, and all raw material is all free of pair Human harmful substance belongs to the environment-friendly products that state key is recommended to use, exempts to plaster, be 1/6 weight of brick wall masonry, has section The advantages of energy, environmental protection, lightweight.
2, assembled architecture finishing of the invention has excellent waterproof, fire protecting performance with partition material.
3, assembled architecture finishing partition material of the invention is by cement, granular polystyrene, inorganic magnesium salt and bar frame The good combination of materials of equal plurality of stable performance forms, and intensity is high, is unlikely to deform, endurance quality is good.
4, the density of assembled architecture of the invention finishing partition material is high, easily reflects, and has extremely strong soundproof effect.
5, assembled architecture of the invention finishing is high with partition material intensity, hanging performance is good.
Specific embodiment
The embodiment of the present invention is described in detail below.
Embodiment 1
A kind of assembled architecture finishing partition material, including panel and core material, the panel are enhanced using Cement fibre Plate or without continuous calcium silicate board;
The core material includes the raw material of following parts by weight: 10 parts of polystyrene, 100 parts of cement, 30 parts of flyash, volcano 30 parts of rock, 55 parts of magnesia, 22 parts of magnesium silicate, 22 parts of magnesium chloride, 2.2 parts of magnesium sulfate, 0.25 part of MCA fire retardant, organic swelling 0.13 part of soil, 0.13 part of rosin tree lipid air entraining agent and 50 parts of water.
The present embodiment assembled architecture finishing with partition material the preparation method is as follows:
S1: weigh in proportion polystyrene, cement, flyash, volcanic rock, magnesia, magnesium silicate, magnesium chloride, magnesium sulfate, MCA fire retardant, organobentonite, rosin tree lipid air entraining agent and water, stir evenly, and core material slurry is made;
S2: core material slurry obtained above is poured into assembled wallboard mold, bar frame is put into, paved, vibrated Molding is carried out with rolling, then natural curing is for 24 hours under the conditions of 25 DEG C;
S3: the core material blank good to above-mentioned maintenance carries out demoulding, and natural curing seven days, and assembled architecture finishing is made and uses The core material of partition material;
S4: core material obtained above is installed in conjunction with panel, obtains assembled architecture finishing partition material.
Assembled architecture finishing partition wall in the present embodiment, 1000 DEG C of high temperature, 240 minutes combustion experiments are without breakage;42dB Soundproof effect meets China national sound insulation measurement standard GBJ121-88;Single-point hanging force is 53Kg.
Embodiment 2
A kind of assembled architecture finishing partition material, including panel and core material, the panel are enhanced using Cement fibre Plate or without continuous calcium silicate board;
The core material includes the raw material of following parts by weight: 12 parts of polystyrene, 120 parts of cement, 50 parts of flyash, volcano 50 parts of rock, 65 parts of magnesia, 26 parts of magnesium silicate, 26 parts of magnesium chloride, 2.6 parts of magnesium sulfate, 0.5 part of MCA fire retardant, vapor phase method hard charcoal Black 0.25 part, 0.25 part of rosin tree lipid air entraining agent and 70 parts of water.
The present embodiment assembled architecture finishing with partition material the preparation method is as follows:
S1: weigh in proportion polystyrene, cement, flyash, volcanic rock, magnesia, magnesium silicate, magnesium chloride, magnesium sulfate, MCA fire retardant, organobentonite, rosin tree lipid air entraining agent and water, stir evenly, and core material slurry is made;
S2: core material slurry obtained above is poured into assembled wallboard mold, bar frame is put into, paved, vibrated Molding is carried out with rolling, then natural curing is for 24 hours at 20 °C;
S3: the core material blank good to above-mentioned maintenance carries out demoulding, and natural curing seven days, and assembled architecture finishing is made and uses The core material of partition material;
S4: core material obtained above is installed in conjunction with panel, obtains assembled architecture finishing partition material.
Assembled architecture finishing partition wall in the present embodiment, 1000 DEG C of high temperature, 240 minutes combustion experiments are without breakage;41dB Soundproof effect meets China national sound insulation measurement standard GBJ121-88;Single-point hanging force is 52.5Kg.
Embodiment 3
A kind of assembled architecture finishing partition material, including panel and core material, the panel are enhanced using Cement fibre Plate or without continuous calcium silicate board;
The core material includes the raw material of following parts by weight: 11 parts of polystyrene, 110 parts of cement, 40 parts of flyash, volcano 40 parts of rock, 60 parts of magnesia, 24 parts of magnesium silicate, 24 parts of magnesium chloride, 2.4 parts of magnesium sulfate, 0.4 part of MCA fire retardant, diatomite 0.2 Part, 0.2 part of rosin tree lipid air entraining agent and 60 parts of water.
The present embodiment assembled architecture finishing with partition material the preparation method is as follows:
S1: weigh in proportion polystyrene, cement, flyash, volcanic rock, magnesia, magnesium silicate, magnesium chloride, magnesium sulfate, MCA fire retardant, organobentonite, rosin tree lipid air entraining agent and water, stir evenly, and core material slurry is made;
S2: core material slurry obtained above is poured into assembled wallboard mold, bar frame is put into, paved, vibrated Molding is carried out with rolling, then natural curing is for 24 hours under the conditions of 30 DEG C;
S3: the core material blank good to above-mentioned maintenance carries out demoulding, and natural curing seven days, and assembled architecture finishing is made and uses The core material of partition material;
S4: core material obtained above is installed in conjunction with panel, obtains assembled architecture finishing partition material.
Assembled architecture finishing partition wall in the present embodiment, 1000 DEG C of high temperature, 240 minutes combustion experiments are without breakage; 41.5dB soundproof effect meets China national sound insulation measurement standard GBJ121-88;Single-point hanging force is 53Kg.
1000 DEG C of the traditional brick wall masonry combustion experiment of high temperature 240 minutes cracks;Soundproof effect is generally 35dB;Single-point Hanging force is 50Kg.
Assembled architecture finishing partition wall of the present invention and traditional brick wall masonry performance comparison are as follows:
1000 DEG C of high temperature, 240 minutes combustion experiments Soundproof effect Single-point hanging force
Traditional brick wall masonry It cracks 35dB 50Kg
Embodiment 1 Without breakage 42dB 53Kg
Embodiment 2 Without breakage 41dB 52.5Kg
Embodiment 3 Without breakage 41.5dB 53Kg
A specific embodiment of the invention above described embodiment only expresses, the description thereof is more specific and detailed, but simultaneously Limitations on the scope of the patent of the present invention therefore cannot be interpreted as.It should be pointed out that for those of ordinary skill in the art For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to guarantor of the invention Protect range.

Claims (10)

1. a kind of assembled architecture finishing partition material, which is characterized in that including panel and core material, the panel uses cement Fibre reinforcement plate or without continuous calcium silicate board;
The core material includes the raw material of following parts by weight: 10 parts -12 parts of polystyrene, 100 parts -120 parts of cement, flyash 30 Part -50 parts, 30 parts -50 parts of volcanic rock, 100 parts -120 parts of inorganic magnesium salt, 0.5 part -1 part of additive, 50 parts -70 parts of water.
2. assembled architecture finishing partition material according to claim 1, which is characterized in that the core material includes following The raw material of parts by weight: 11 parts of polystyrene, 40 parts of flyash, 40 parts of volcanic rock, 110 parts of inorganic magnesium salt, adds 110 parts of cement Add 0.75 part of agent, 60 parts of water.
3. assembled architecture according to claim 1 finishing partition material, which is characterized in that the inorganic magnesium salt includes Magnesia, magnesium silicate, magnesium chloride and magnesium sulfate, the magnesia, magnesium silicate, magnesium chloride and magnesium sulfate weight ratio be 2.5:1: 1:1.
4. assembled architecture finishing partition material according to claim 3, which is characterized in that the magnesia is reheating Magnesia.
5. assembled architecture finishing partition material according to claim 1, which is characterized in that the additive includes resistance Agent, thickener and air entraining agent are fired, the weight ratio of the fire retardant, thickener and air entraining agent is 2:1:1.
6. assembled architecture finishing partition material according to claim 5, which is characterized in that the fire retardant is MCA Fire retardant.
7. assembled architecture finishing partition material according to claim 5, which is characterized in that the thickener is inorganic One or more of thickener, specially fume colloidal silica, sodium bentonite, organobentonite or diatomite.
8. assembled architecture finishing partition material according to claim 5, which is characterized in that the air entraining agent is rosin Resinae air entraining agent.
9. assembled architecture finishing partition material according to claim 1, which is characterized in that the polystyrene is grain The granular foam polystyrene of diameter 1mm-5mm.
10. any one of -9 assembled architecture finishings preparation method of partition material, feature exist according to claim 1 In, comprising the following steps:
S1: polystyrene, cement, flyash, volcanic rock, magnesia, magnesium silicate, magnesium chloride, magnesium sulfate, fire-retardant is weighed in proportion Agent, thickener, air entraining agent and water, stir evenly, and core material slurry is made;
S2: core material slurry obtained above is poured into assembled wallboard mold, bar frame is put into, is paved, vibrated and rolled Pressure carries out molding, and then natural curing is for 24 hours under the conditions of 20 DEG C -30 DEG C;
S3: the core material blank good to above-mentioned maintenance carries out demoulding, and natural curing seven days, and assembled architecture finishing is made and uses partition wall The core material of material;
S4: core material obtained above is installed in conjunction with panel, obtains assembled architecture finishing partition material.
CN201811535363.XA 2018-12-14 2018-12-14 A kind of assembled architecture finishing partition material and preparation method thereof Pending CN109503109A (en)