CN108948989A - A kind of end silylated polyether water-repellent paint and preparation method thereof - Google Patents
A kind of end silylated polyether water-repellent paint and preparation method thereof Download PDFInfo
- Publication number
- CN108948989A CN108948989A CN201810623145.5A CN201810623145A CN108948989A CN 108948989 A CN108948989 A CN 108948989A CN 201810623145 A CN201810623145 A CN 201810623145A CN 108948989 A CN108948989 A CN 108948989A
- Authority
- CN
- China
- Prior art keywords
- parts
- silylated polyether
- repellent paint
- water
- end according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-repellent paints, its mass parts composition are as follows: 50~200 parts of silylated polyether resin, 20~150 parts of plasticizer, 40~180 parts of filler material of end, 0~150 part of pigment, 0.2~30 part of light stabilizer, 0.2~50 part of deicer, 0.5~55 part of adhesion promoter, 0.5~24 part of catalyst, 0.5~15 part of defoaming agent, 0.2~8 part of dispersing agent, the invention also discloses preparation methods.Present invention process is simple and reliable, has excellent performance, and has very extensive application prospect.
Description
Technical field
The present invention relates to building water-proof paint technical fields, and in particular to a kind of end silylated polyether water-repellent paint and its preparation
Method.
Technical background
Building water-proof paint is also known as coating film waterproof material, is that (liquid, thick liquid, pulvis add water scene to mix to amorphous material
Powder scene is added to mix and stir with liquid) coatings such as brush, scrape, smear, spray through scene and constructs, it can be in the formation of works surface cure with waterproof
The film material of ability.Since the end of the year 50 of 20th century, building water-proof paint starts large-scale use.
Different according to the substance of film-forming, building water-proof paint can be divided into organic, inorganic and organic-inorganic again
Complex class.Inorganic building water-proof paint has when ensuring of introduction, M1500, waterproof treasured, HM1500, TM1500 of country's research and development
And cement based penetration crystallization type water proofing paint.Organo-mineral complexing class has polymer cement waterproof paint.Organic buildings waterproof
Coating variety is more, and development can substantially be divided into three phases.First stage is the various emulsified asphalt coating of exploitation, from 20th century
The fifties is this just emulsified asphalt coating based on emulsifier develops the emulsification of asphalt by lime.These coating were once
The use of large area is obtained in waterproofing work, but because its waterproof effect is general, film service life is short, to environment dirt
Dye and the harm to human health, have been put into obsolete product, dosage is fewer and fewer mostly.Second stage is that exploitation polymer changes
Property asphalt waterproofing paint.There is solvent type chloroprene rubber asphalt waterproofing coating in middle 1960s, occur the seventies
There is emulsion type (cationic) chloroprene rubber waterproof coating, emulsion type the beginning of the eighties in emulsion type reclaimed rubber asphalt waterproofing paint
Butadiene-styrene rubber water-repellent paint, SBS rubber asphalt solvent-type waterproofing paint, butadiene acrylonitrile rubber cream water-repellent paint etc..Phase III is synthesis
The appearance of high molecular water-proof paint, as oleic series water-repellent paint, acrylic acid-acrylic it is fine-styrene multi-component copolymer emulsion type
Coating, aqueous EPDM water-repellent paint, polyurethane water-proof paint, spray polyurea waterproofing coating etc..
Currently on the market using in wider building water-proof paint, applied with polyurethane water-proof paint, polymer cement waterproof
Material, water-proof acrylic acid paint, based on modified waterproof asphalt material.According to statistical data in 2015, national building water-proof paint
Total sales volume is 380,000 tons, in which: polyurethane water-proof paint accounts for 43%, and polymer cement waterproof paint accounts for 37%, polyacrylic water-proof
Coating accounts for 8.5%, and modified waterproof asphalt material accounts for 5.5%, other class water-repellent paints account for 5%.
Polyurethane water-proof paint has excellent elasticity and low temperature flexibility, and yield is high, type is more, but also has current difficulty
The shortcomings that overcome.Maximum dosage is tar polyurethane waterproofing paint, Pitch-Polyurethane Water Proofing Coating and coumarone tree
Rouge modified polyurethane paint, and mostly two-component.Although tar polyurethane waterproofing paint have reactivity, it is at low cost,
It is easy to spread, but wherein containing volatile substances such as a large amount of anthracene, naphthalene, phenols, it is serious to pollute environment and be detrimental to health,
Current provinces and cities many at home, which have begun, to be forbidden to use.Pitch-Polyurethane Water Proofing Coating joined asphalt, have outer
The advantages that seeing smooth, glossy, good leveling property, elongation percentage increase, but disadvantage is also clearly.Asphalt is without active
Hydrogen only plays filler effect in coating；And wherein the heterocyclic compounds such as sulphur, oxygen, nitrogen have certain toxicity；Due to hating for pitch
Water effect affects to the recoatability of coating.Coumarone indene resin modified polyurethane water-repellent paint is to improve tar oil type
With the shortcomings that pitch type on develop, although properties have some improvement, the polyurethane coating of these three types is equal
There is deeper color, tar oil type and pitch type are black, and coumarone indene resin modified version is that coffee color arrives dark brown, which also limits
Its use scope.Although white polyurethane water-repellent paint, aqueous polyurethane water-repellent paint, single group have also been developed currently on the market
Divide polyurethane water-proof paint, although these coating solve the problems, such as existing: first is that coating property some aspects also need
It improves；Second price is higher, and acceptance level is smaller；Third is also the most key problem, and curing mechanism is still identical, system
In still containing free isocyanide ester, such as TDI, MDI, toxicity is big, easily carcinogenic.Its resistance to ag(e)ing is also relatively poor, sunlight irradiation
Easy xanthochromia down.Although and one-can urethane coating easy construction, thickness are also easy to produce bubble when applying, generate paint film defect, lead
Cause waterproof hidden danger.And the polyurethane/polyurea water-repellent paint and pure polyurea water-proof developed by polyurethane water-proof paint technology applies
Material also deposits identical problem.
Pigments and fillers and auxiliary agent mixing are added generally using acrylate polymer emulsion as film forming matter in water-proof acrylic acid paint
Made of water-based mono-component water-repellent paint.It has the characteristics that easy for construction, aqueous, environmental protective, but due to its membrane formation mechanism be with
With the continuous evolution of moisture, polymer particle is closer to each other as viscous particle for the volatilization of moisture, and polymer particle occurs
Plastic deformation and cohesion and form a film, completely physical action, therefore limit execution conditions and its film performance.It is modified
Pitch class water-repellent paint can be divided into solvent type and emulsion type, and the pollution of solvent type modified waterproof asphalt material is big, gradually now
It eliminates；Emulsion type modified waterproof asphalt material is although cheap, but resistance to ag(e)ing, weather-proof poor, and is black
Or Dark grey, it is restricted its use.
Currently, the development trend of building water-proof paint industry is Devoting Major Efforts To Developing high-performance, high durable water-repellent paint, develop ring
Guarantor's type water-repellent paint.The development of high-performance, high durable water-repellent paint is conducive to improve the time limit of setting up defences of buildings waterproof, extends and build
The investment built the object service life, reduce maintenance cost in the unit time.So the water-repellent paint of mainstream such as polyurethane is anti-currently on the market
Water paint, water-proof acrylic acid paint, modified waterproof asphalt material, it is difficult to fully meet the needs of industry development, the present invention is directed to
Such phenomenon develops a kind of end silylated polyether high-performance waterproof paint, meets the needs of market and industry development.
Invention particular content:
It is an object of the present invention to provide a kind of end silylated polyether high-performance waterproof paints, and it is comprehensive, economical to have performance
The advantages that environmentally friendly.
To achieve the above object, the specific technical solution of the present invention are as follows:
A kind of end silylated polyether water-repellent paint, which is characterized in that in parts by mass include following components:
50~200 parts of silylated polyether resin of end, 20~150 parts of plasticizer, 40~180 parts of filler material, 0~150 part of pigment,
0.2~30 part of light stabilizer, 0.2~50 part of deicer, 0.5~55 part of adhesion promoter, 0.5~24 part of catalyst, defoaming
0.5~15 part of agent, 0.2~8 part of dispersing agent.
Further, the end group of the end silylated polyether resin is siloxy Si-OR, and main chain is polypropylene oxide knot
Structure.
Silylated polyether high-performance waterproof paint in end of the present invention is added by resin, auxiliary agent and pigments and fillers by certain
Work technique is prepared.Wherein resin is end silylated polyether resin (MS), and end group is siloxy Si-OR, and main chain is polyoxygenated
Propylene structure.Its typical structure is
Wherein PPO=
It can be seen that from structural formula, end silylated polyether main chain is polyether segment, is similar to polyurethane, obtains after end group solidification
Si-O-Si segment, is similar to silicone structure, and film has good comprehensive performance.
Further, the plasticizer is one of ester plasticizer, isoparaffin solvent oil or its two kinds mixing
Object.
Further, the filler material is one or more of Sulfates, carbonate, silicates mixture.
Further, the pigment is inorganic pigment or organic pigment.
Further, the light stabilizer is ultraviolet absorbing agent, hindered amine light stabilizer, excited state quenchers and peroxide
Change one or more of hydrogen distintegrant.
Further, the titanium dioxide is rutile type titanium white.
Further, the deicer be oxazole alkanes, p-Methyl benzenesulfonyl isocyanate class, triethyl orthoformate class and
Organic silicon.
Further, the adhesion promoter is silane coupling agent.
Further, the catalyst is one in tin, iron, the fatty acid salt of lead, organic amine, titanate esters and its chelate
Kind is several.
Further, the defoaming agent is mineral oil defoaming agent, organic silicon defoaming agent and the polymerization without organosilicon
One or more of species defoaming agent.
Further, the dispersing agent is the polybasic carboxylic acid salt, unsaturated polycarboxylic acids and polysiloxanes of polynary glutamine
Class, arcylic acid species, polyester modification arcylic acid species, polyether phosphate copolymer analog, in high-molecular block copolymer class
One or more.
The working principle of the invention is:
End silylated polyether resin in coating is exposed in atmosphere, with atmosphere after construction in the presence of a catalyst
In hydrone react generation crosslinking, to form waterproof coating.Its specific mechanism is to be rapidly hydrolyzed into silanol group under,
Silanol group occurs bunching again and generates three-dimensional net structure, is shown below:
And filler material, which is added, can play reinforcement, reduce cost, improve the effects of application property.Sulphur is mainly used in the present invention
Hydrochlorate, silicate and carbonate filler material.It is existing for example: sulfate filler material mainly has barium sulfate.Barium sulfate is acidproof, resistance to
Alkali, fast light, heat-resisting, oil absorption is low, is good inert filler.Barium sulfate can be divided into natural and two classes of synthesis, naturally be
Blanc fixe, synthesis are blanc fixe.Blanc fixe oil absorption is low, fillibility is good, good leveling property；Blanc fixe whiteness
High, quality exquisiteness, this project will be selected by investigating to it.Silicates filler have talcum powder, kaolin, wollastonite,
Mica powder, sericite, synthetic aluminium silicate etc..Talcum powder crystal category monoclinic system is in hexagon or diamond shape.Talcum powder can improve
The storage characteristics of coating, but it is easy dusting.Kaolin property is similar with talcum powder.The main component of wollastonite is calcium metasilicate, can
To improve the wearability and weatherability of film, the reason is that thin slice is stacked in film due to his sheet and fibrous structure,
In addition to the shielding that can increase film, there are also stronger ultraviolet reflection abilities, thus improve the resistance to ag(e)ing of film.Mica
From the point of view of powder chemically forms, it is exactly silicon a part in the lattice of talcum powder replaced aluminium, anti-corruption can be improved in coating
Corrosion increases surface hardness.Sericite in powder also has similar property with synthetic aluminium silicate.Carbonate mainly has calcium carbonate.Carbon
Cost is relatively low for sour calcium, is to use more filler at present.After fatty acid is surface-treated, have with resin preferable compatible
Property, it can obviously improve the processing performance and mechanical property of sealant.Studies have shown that the calcium carbonate superfine powder through fatty acid treatment, no
But system can be made to obtain good mechanical property, moreover it is possible to provide thixotropy, system is made to obtain good rheological property.This is mainly
Since the fatty acid Long carbon chain of treated calcium carbonate surface can be twined with pfpe molecule chain at intermolecular force and segment
Knot, the dispersion effect in coating are more preferable；Discovery is tested simultaneously, when dosage is identical, calcium carbonate partial size is smaller, the drawing of sealant
It stretches intensity and elongation at break is higher, this is because particle diameter is smaller, specific surface area is bigger, the surface area with polymer contact
More, reinforcement point increases.
The main component of coating disclosed by the invention is end silylated polyether resin, and main chain is propylene oxide polyethers flexible
Segment, end group is the siloxy with reactivity, therefore the solidification process of coating is the moisture in siloxy group and air
Reaction is realized by its hydrolysis and condensation be crosslinked in the presence of a catalyst, to obtain the elastomer with cross-linked structure.End group
The hydrolysis-condensation reaction speed of siloxy and the completeness of reaction influence workability and service performance to a certain extent, packet
Include coating surface drying time, elongation percentage and caking property etc..In general, hydrolyzable alkoxy number more more then moons are easy on silane
Hydrolytic condensation, much faster than dialkoxy silicane hydrolytic condensation such as trialkoxy silane, the former can not have to catalyst
Vulcanization crosslinking and the latter is carried out to need to there is crosslinking that could be relatively good in catalyst.Coating is from liquid to solid chemical reaction
Process are as follows: end of the chain Si-OR group first in air water occur hydrolysis generate Si-OH, obtained Si-OH again with Si-
Condensation forms Si-O-Si key between OR condensation or two Si-OH, while releasing by-product H2O or CH3OH, eventually form with
Si-O-Si key is network cross-linked point, is the cross-linked structure of propylene oxide polyether segment flexible between crosslinking points.Sealing glue solidifying
In the process, it is that condensation reaction is hydrolyzed with steam in the Si-OR group that outer layer is contacted with air first, forms chemical crosslinking, reach
It is attached on finger to adhesion without adhesiver, this process is the surface drying process of glue, and the time of experience is surface drying time.Metallic tin, iron,
Fatty acid salt, organic amine, titanate esters and its chelate of lead etc. can promote the crosslinking of end silylated polyether resin.
Due to the curing mechanism of this coating be coating coating after with the moisture in air under the effect of the catalyst with end silicon
Hydrolysis occurs for alkane, and then is crosslinked last film forming, therefore this coating needs to keep anhydrous state during storage, so plus
It is necessary for entering deicer.Common deicer has oxazole alkanes, p-Methyl benzenesulfonyl isocyanate class, triethyl orthoformate class
And organic silicon.
The addition of other components also has optimization castering action to the respective performances of coating in this coating.
The utility model has the advantages that
The present invention has such as compared with existing polyurethane water-proof paint, water-proof acrylic acid paint, Emulsificated asphalt water-proof painting material
Lower advantage:
(1) weatherability and durability
It holds silylated polyether performed polymer molecular weight height and narrowly distributing, unsaturated bond content is very low；The Si-O-Si formed after solidification
The effects of segment is to heat, oxygen, moisture is stablized；Flexible polyether segments between crosslinking points can effectively adjust film by molecular motion
The shrinkage stress that inside generates, it is sufficiently stable to oxygen, ozone, ultraviolet light, so film is weather-proof, UV resistant performance is very good.
If the polyurethane water-proof paint used now, water-proof acrylic acid paint etc. use under exposed environment, generally in 3 to five years
It begins to aging phenomenon occur, lost waterproof action completely in 80 to ten years.According to Japan experiments have shown that, silylated polyether (MS)
Building water-proof paint Acceptable life can be up to 30 years or more in exposed situation.It is non-to be conducive to improve setting for buildings waterproof
The anti-time limit extends Building life cycle, reduces the investment of maintenance cost in the unit time, to realize energy-saving and emission-reduction, realizes green
The original intention of building.
(2) adhesive force is good
End silylated polyether end group is siloxy Si-OR, is hydrolyzed into Si-OH under moisture effect, can be with the hydroxyl of substrate surface
Base or metal oxide form chemical bond or hydrogen bond action, it is made to generate good adhesive force to substrate.
(3) heat resistance and cold resistance
High energy Si-O-Si key is formed after holding silylated polyether sealing glue solidifying, assigns the preferable heat resistance of sealant；Polyethers master
Chain has excellent flexibility, and glass transition temperature is lower, assigns sealant excellent cold resistance.
(4) application property
End silylated polyether backbone structure is the pure polyether structure of macromolecular, urethane bond and urea without high cohesion energy
Key, intermolecular force are smaller；Methyl structural increases intermolecular distance on main chain, further decreases intermolecular active force；
The flexibility of molecular backbone itself is preferable simultaneously, therefore when relative molecular mass is larger, viscosity is still lower, viscosity with temperature
Variation it is small, have good process operability.
(5) feature of environmental protection
It holds silylated polyether viscosity low, there is good process operability；No isocyano and other stimulations time and nuisance
Matter, it is environmentally protective, it can satisfy the use of each harsh environment.
Specific embodiment:
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to invention into
Row is further described.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to limit
The fixed present invention.
Embodiment one
A kind of end silylated polyether high-performance waterproof paint and preparation method thereof is as follows:
185 parts of end silylated polyether resins, 30 parts of two isodecyls of phthalic acid are added in the reaction kettle for having corresponding function
Ester, 5 parts of Tinuvin1130,2 parts of Tinuvin144,2 parts of KS-66,1 part of BYK-P104S, 50 parts of ultra-fine sulfuric acid dried
Barium, 10 parts of superfine light calcium carbonates dried, 5 parts of rutile type titanium whites dried start to turn in 15~55rpm
It mixed under speed, stir 5~60min；Then it is evacuated to 0.3MPa or less to be suitably worth, continues to stir and begin to warm up
Suitably it is worth between to 80~150 DEG C, is cooled to 40~60 DEG C hereinafter, 18 parts of Isopars are added after holding 30~300min
Oil, 3 parts of acrylic triethoxysilanes, 2 parts of aminopropyl diethoxymethylsilanes, 2.5 parts of phthalic acid dibutyl tins,
Continue to vacuumize 5~50min of stirring at 10~45rpm, then discharges, packs.
Due to the related standard of current country, industry, area still end silylated polyether high-performance waterproof paint, inventor according to
The relevant regulations of standard and standard law similar in country, temporary drawing up the enterprise standard, and the product of the present embodiment is tested, it surveys
Test result is as shown in table 1:
Table 1
As seen from the table, the product of the present embodiment reaches the requirement of the over-all properties in company standard.
Embodiment two:
A kind of end silylated polyether high-performance waterproof paint and preparation method thereof is as follows:
150 parts of end silylated polyether resins, 25 parts of different nonyls of phthalic acid two are added in the reaction kettle for having corresponding function
Ester, 5 parts of Tinuvin1130,2 parts of Tinuvin144,2 parts of KS-66,1 part of BYK-P104S, 50 parts of ultra-fine sulfuric acid dried
Barium, 30 parts of superfine light calcium carbonates dried, 25 parts of rutile type titanium whites dried start to turn in 15~55rpm
It mixed under speed, stir 5~60min；Then it is evacuated to 0.3MPa or less to be suitably worth, continues to stir and begin to warm up
Suitably it is worth between to 80~150 DEG C, is cooled to 40~60 DEG C hereinafter, 28 parts of Isopars are added after holding 30~300min
Oil, 2.6 parts of acrylic triethoxysilanes, 2 parts of aminopropyl diethoxymethylsilanes, 2.2 parts of dibutyl tin dilaurates,
Continue to vacuumize 5~50min of stirring at 10~45rpm, then discharges, packs.
End properties reach the over-all properties requirement in company standard, testing result such as table 2 by test:
Table 2
Embodiment three:
A kind of end silylated polyether high-performance waterproof paint and preparation method thereof is as follows:
100 parts of end silylated polyether resins, 15 parts of two isodecyls of phthalic acid are added in the reaction kettle for having corresponding function
Ester, 4 parts of Tinuvin1130,2.7 parts of Tinuvin144,2 parts of KS-66,2 parts of BYK-P104S, 100 parts of ultra-fine sulphur dried
Sour barium, 30 parts of superfine light calcium carbonates dried, 25 parts of rutile type titanium whites dried start 15~55rpm's
It mixed under revolving speed, stir 5~60min；Then it is evacuated to 0.3MPa or less to be suitably worth, continues to stir and start to add
Heat is cooled to 40~60 DEG C hereinafter, 1.5 parts of isoparaffins are added after holding 30~300min to being suitably worth between 80~150 DEG C
Solvent naphtha, 2.6 parts of acrylic triethoxysilanes, 18 parts of aminopropyl diethoxymethylsilanes, 1.5 parts of di lauric dibutyls
Tin continues to vacuumize 5~50min of stirring at 10~45rpm, then discharges, packs.
End properties reach the over-all properties requirement in company standard, testing result such as table 3 by test:
Table 3
Example IV:
A kind of end silylated polyether high-performance waterproof paint and preparation method thereof is as follows:
135 parts of end silylated polyether resins, 18 parts of two isodecyls of phthalic acid are added in the reaction kettle for having corresponding function
Ester, 4 parts of Tinuvin1130,2.5 parts of Tinuvin144,2 parts of KS-66,2 parts of BYK-P104S, 100 parts of ultra-fine sulphur dried
Sour barium, 35 parts of superfine light calcium carbonates dried, 20 parts of rutile type titanium whites dried start 15~55rpm's
It mixed under revolving speed, stir 5~60min；Then it is evacuated to 0.3MPa or less to be suitably worth, continues to stir and start to add
Heat holds to being suitably worth between 80~150 DEG C and is cooled to 40~60 DEG C after 30~300min hereinafter, that 17 parts of isoparaffins are added is molten
Agent oil, 2.6 parts of acrylic triethoxysilanes, 15 parts of aminopropyl diethoxymethylsilanes, 1.5 parts of di lauric dibutyls
Tin continues to vacuumize 5~50min of stirring at 10~45rpm, then discharges, packs.
End properties reach the over-all properties requirement in company standard, testing result such as table 4 by test:
Table 4
Embodiment five:
A kind of end silylated polyether high-performance waterproof paint and preparation method thereof is as follows:
200 parts of end silylated polyether resins, 35 parts of two isodecyls of phthalic acid are added in the reaction kettle for having corresponding function
Ester, 5 parts of Tinuvin1130,2.7 parts of Tinuvin144,2 parts of KS-66,2 parts of BYK-P104S, 25 parts of ultra-fine sulfuric acid dried
Barium, 30 parts of superfine light calcium carbonates dried, 75 parts of rutile type titanium whites dried start to turn in 15~55rpm
It mixed under speed, stir 5~60min；Then it is evacuated to 0.3MPa or less to be suitably worth, continues to stir and begin to warm up
Suitably it is worth between to 80~150 DEG C, is cooled to 40~60 DEG C hereinafter, 40 parts of Isopars are added after holding 30~300min
Oil, 6 parts of acrylic triethoxysilanes, 20 parts of aminopropyl diethoxymethylsilanes, 20 parts of dibutyl tin dilaurates, after
It is continuous to vacuumize 5~50min of stirring at 10~45rpm, it then discharges, pack.
End properties reach the over-all properties requirement in company standard, testing result such as table 4 by test:
Table 4
Find out from above example, present invention process is simple and reliable, has excellent performance.Thinking of the present invention is novel, has very big
Novelty, have very extensive application prospect.
The foregoing is merely the preferred embodiment of invention, be not intended to limit the present invention, it is all the spirit and principles in the present invention it
Modifications, equivalent substitutions and improvements made by interior etc., should all be included in the protection scope of the present invention.Attempt accordingly to the present invention
Make limitation in any form, therefore all have any modification or change for making the related present invention under identical spirit,
The scope that the invention is intended to protect should be all included in.
Claims (13)
1. a kind of end silylated polyether water-repellent paint, which is characterized in that in parts by mass include following components:
50~200 parts of silylated polyether resin of end, 20~150 parts of plasticizer, 40~180 parts of filler material, 0~150 part of pigment, light is steady
Determine 0.2~30 part of agent, 0.2~50 part of deicer, 0.5~55 part of adhesion promoter, 0.5~24 part of catalyst, defoaming agent 0.5
~15 parts, 0.2~8 part of dispersing agent.
2. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the end of the end silylated polyether resin
Base is siloxy Si-OR, and main chain is polypropylene oxide structure.
3. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the plasticizer is esters plasticising
One of agent, isoparaffin solvent oil or its two kinds mixture.
4. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the filler material be Sulfates,
One or more of carbonate, silicates mixture.
5. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the pigment is inorganic pigment or has
Machine pigment.
6. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the light stabilizer is ultraviolet light suction
Receive one or more of agent, hindered amine light stabilizer, excited state quenchers and hydrogen peroxide distintegrant.
7. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the titanium dioxide is rutile type titanium
White powder.
8. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the deicer be oxazole alkanes,
P-Methyl benzenesulfonyl isocyanate class, triethyl orthoformate class and organic silicon.
9. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the adhesion promoter is silane
Coupling agent.
10. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the catalyst is tin, iron, lead
One or more of fatty acid salt, organic amine, titanate esters and its chelate.
11. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the defoaming agent is mineral oils
One or more of defoaming agent, organic silicon defoaming agent and polymer-like antifoams without organosilicon.
12. silylated polyether water-repellent paint in end according to claim 1, which is characterized in that the dispersing agent is polynary aminoacyl
The polybasic carboxylic acid salt of amine, unsaturated polycarboxylic acids and polysiloxane-based, arcylic acid species, polyester modification arcylic acid species,
One or more of polyether phosphate copolymer analog, high-molecular block copolymer class.
13. such as the preparation method of the described in any item end silylated polyether water-repellent paints of claim 1~12, which is characterized in that packet
Include following processing step: in the reaction kettle for having corresponding function be added 50~200 parts of end silylated polyether resins, plasticizer 20~
A part in 150 parts, the filling for 0.2~30 part of light stabilizer, 0.5~15 part of defoaming agent, 0.2~8 part of dispersing agent, dried
40~180 parts of material, dried 0~150 part of pigment, start to be mixed under the revolving speed of 15~55rpm, stir 5~
60min；Then it is evacuated to 0.3MPa or less to be suitably worth, it is suitable between 80~150 DEG C to continue to stir and begin heat to
Value holds and is cooled to 40~60 DEG C after 30~300min hereinafter, another part, deicer 0.2~50 in 20~150 parts of plasticizer
Part, 0.5~55 part of adhesion promoter, 0.5~24 part of catalyst continue to vacuumize 5~50min of stirring at 10~45rpm,
Then it discharges, pack.