CN108130745A - A kind of preparation method of the medical coated non-woven of antimicrobial form - Google Patents
A kind of preparation method of the medical coated non-woven of antimicrobial form Download PDFInfo
- Publication number
- CN108130745A CN108130745A CN201711384013.3A CN201711384013A CN108130745A CN 108130745 A CN108130745 A CN 108130745A CN 201711384013 A CN201711384013 A CN 201711384013A CN 108130745 A CN108130745 A CN 108130745A
- Authority
- CN
- China
- Prior art keywords
- woven
- dried
- preparation
- coating
- copolymer emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of the medical coated non-woven of antimicrobial form, include the following steps：S1, after nano silver, chitosan, titanium dioxide, biennial wormwood extract are sequentially added into acrylate copolymer emulsion, coating is stirred to get；S2, by nonwoven sample after ultraviolet lower irradiation, be soaked in acetone soln after 40 45min, rinsed repeatedly with deionized water, drying is for use；S3, coating made from step 1 is scratched using the method for the direct coating of dry method and is dried on for use non-woven fabrics in step 2；S4, the non-woven fabrics after blade coating is dried at room temperature for 5 10min；S5, non-woven fabrics dried in step 4 is dried into 18 30min in 100 130 DEG C of drying tunnel.The present invention carries out nonwoven sample using coating the coated non-woven obtained after blade coating is dry, and not only anti-microbial property is splendid, and nontoxic, soft texture, good air permeability.
Description
Technical field
The present invention relates to non-woven fabrics manufacturing technology fields, and in particular to a kind of preparation side of the medical coated non-woven of antimicrobial form
Method.
Background technology
Non-woven fabrics is a kind of non-woven cloth, it is that fiber directly is passed through gas using high polymer slice, staple fiber or long filament
Stream or mechanical networking, then by spun lacing, needle thorn or hot rolling are reinforced, the non-woven cloth finally formed by final finishing.Tool
There is soft, ventilative and planar structure tencel product, advantage is not generate Soft flocks, tough, durable, silky soft,
It is one kind of reinforcing material, and the feeling of also cotton is compared with cotton goods, the sack of non-woven fabrics is easily formed, Er Qiezao
Valency is cheap.
Medical non-woven fabrics product be using chemical fibre include polyester, polyamide, polytetrafluoroethylene (PTFE) (PTFE), polypropylene,
Medical and health use textile made of carbon fiber and glass fibre.Including disposable breathing mask, protective garment, operating coat, barrier gown, reality
Test clothes.
Because of medical particularity, medical non-woven fabrics is for performances such as the antibacterial of non-woven fabrics, dust filtering, Material claddings
It is more demanding.
Invention content
Technical problems based on background technology, the present invention propose a kind of preparation of the medical coated non-woven of antimicrobial form
Method, the present invention is environment friendly and pollution-free, and medical coated non-woven obtained has excellent anti-microbial property.
A kind of preparation method of the medical coated non-woven of antimicrobial form proposed by the present invention, includes the following steps：
S1, it after nano silver, chitosan, titanium dioxide, biennial wormwood extract are sequentially added into acrylate copolymer emulsion, stirs
Obtain coating；
S2, by nonwoven sample after ultraviolet lower irradiation, be soaked in acetone soln after 40-45min, it is anti-with deionized water
Multiple to rinse, drying is for use；
S3, coating blade coating made from step 1 is dried in step 2 by for use non-woven fabrics using the method for the direct coating of dry method
On；
S4, the non-woven fabrics after blade coating is dried at room temperature for 5-10min；
S5, non-woven fabrics dried in step 4 is dried into 18-30min in 100-130 DEG C of drying tunnel.
Preferably, in S1, acrylate copolymer emulsion is the water-dispersed acrylic ester copolymer emulsion of 50-60wt%.
Preferably, in S1, acrylate copolymer emulsion is methyl acrylate-acrylic acid ethyl ester copolymer emulsion.
Preferably, in S1, the mass fraction of biennial wormwood extract is 25-35wt%.
Preferably, in S1, the time of stirring is 60-70min.
Preferably, in S1, acrylate copolymer emulsion, nano silver, chitosan, titanium dioxide, biennial wormwood extract mass ratio
For 100-150：4-7：3-6：2-5：10-15.
Preferably, in S2, ultraviolet exposure time is 20-25min.
Preferably, in S2, a concentration of 12-20wt% of acetone soln.
The present invention carries out nonwoven sample using coating the coated non-woven obtained after blade coating is dry not only anti-microbial property
Splendid and nontoxic, soft texture, good air permeability.The present invention using acrylate copolymer emulsion, nano silver, chitosan, titanium dioxide,
Biennial wormwood extract is mixed to prepare coating, wherein, nano silver can show skin effect and quantum effect, the nano silver of below 25nm
Grain size is also smaller than bacterium (hundreds of nanometers), viral (tens nanometer), thus it can be used for breathing with penetration cell wall and they
Base enzyme combines, and bacterium, virus is made to be choked to death, and by itself and the chitosan with antibacterial action, biennial wormwood extract mating reaction,
Antibacterial wide spectrum, effect enhance, and improve the antibacterial effect of non-woven fabrics；Acrylate copolymer emulsion is added, introduces ester group, improves nonwoven
The hydrophobicity of cloth reduces the growth of bacterium, further improves the antibacterial effect of non-woven fabrics；Titanium dioxide is added, is not easy non-woven fabrics
It cracks, is non-discolouring, and having larger percentage of elongation and preferably resistance to acid and alkali.
Specific embodiment
In the following, technical scheme of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of preparation method of the medical coated non-woven of antimicrobial form, includes the following steps：
S1, it after nano silver, chitosan, titanium dioxide, biennial wormwood extract are sequentially added into acrylate copolymer emulsion, stirs
Obtain coating；
S2, by nonwoven sample after ultraviolet lower irradiation, be soaked in acetone soln after 45min, with deionized water repeatedly
It rinses, drying is for use；
S3, coating blade coating made from step 1 is dried in step 2 by for use non-woven fabrics using the method for the direct coating of dry method
On；
S4, the non-woven fabrics after blade coating is dried at room temperature for 5min；
S5, non-woven fabrics dried in step 4 is dried into 18min in 130 DEG C of drying tunnel.
Embodiment 2
A kind of preparation method of the medical coated non-woven of antimicrobial form, includes the following steps：
S1, it after nano silver, chitosan, titanium dioxide, biennial wormwood extract are sequentially added into acrylate copolymer emulsion, stirs
Obtain coating；
S2, by nonwoven sample after ultraviolet lower irradiation, be soaked in acetone soln after 40min, with deionized water repeatedly
It rinses, drying is for use；
S3, coating blade coating made from step 1 is dried in step 2 by for use non-woven fabrics using the method for the direct coating of dry method
On；
S4, the non-woven fabrics after blade coating is dried at room temperature for 10min；
S5, non-woven fabrics dried in step 4 is dried into 30min in 100 DEG C of drying tunnel；
Wherein, in S1, acrylate copolymer emulsion is the water-dispersed acrylic ester copolymer emulsion of 60wt%.
Embodiment 3
A kind of preparation method of the medical coated non-woven of antimicrobial form, includes the following steps：
S1, it after nano silver, chitosan, titanium dioxide, biennial wormwood extract are sequentially added into acrylate copolymer emulsion, stirs
Obtain coating；
S2, by nonwoven sample after ultraviolet lower irradiation, be soaked in acetone soln after 42min, with deionized water repeatedly
It rinses, drying is for use；
S3, coating blade coating made from step 1 is dried in step 2 by for use non-woven fabrics using the method for the direct coating of dry method
On；
S4, the non-woven fabrics after blade coating is dried at room temperature for 6min；
S5, non-woven fabrics dried in step 4 is dried into 20min in 120 DEG C of drying tunnel；
Wherein, in S1, acrylate copolymer emulsion is the water-dispersed acrylic ester copolymer emulsion of 50wt%；
In S1, acrylate copolymer emulsion is methyl acrylate-acrylic acid ethyl ester copolymer emulsion.
Embodiment 4
A kind of preparation method of the medical coated non-woven of antimicrobial form, includes the following steps：
S1, it after nano silver, chitosan, titanium dioxide, biennial wormwood extract are sequentially added into acrylate copolymer emulsion, stirs
Obtain coating；
S2, by nonwoven sample after ultraviolet lower irradiation, be soaked in acetone soln after 43min, with deionized water repeatedly
It rinses, drying is for use；
S3, coating blade coating made from step 1 is dried in step 2 by for use non-woven fabrics using the method for the direct coating of dry method
On；
S4, the non-woven fabrics after blade coating is dried at room temperature for 7min；
S5, non-woven fabrics dried in step 4 is dried into 25min in 110 DEG C of drying tunnel；
Wherein, in S1, acrylate copolymer emulsion is the water-dispersed acrylic ester copolymer emulsion of 55wt%；
In S1, acrylate copolymer emulsion is methyl acrylate-acrylic acid ethyl ester copolymer emulsion；
In S1, the mass fraction of biennial wormwood extract is 25wt%；
In S1, the time of stirring is 60min；
In S1, acrylate copolymer emulsion, nano silver, chitosan, titanium dioxide, biennial wormwood extract mass ratio be 100：7：
3：5：10；
In S2, ultraviolet exposure time is 25min；
In S2, a concentration of 12wt% of acetone soln.
Embodiment 5
A kind of preparation method of the medical coated non-woven of antimicrobial form, includes the following steps：
S1, it after nano silver, chitosan, titanium dioxide, biennial wormwood extract are sequentially added into acrylate copolymer emulsion, stirs
Obtain coating；
S2, by nonwoven sample after ultraviolet lower irradiation, be soaked in acetone soln after 44min, with deionized water repeatedly
It rinses, drying is for use；
S3, coating blade coating made from step 1 is dried in step 2 by for use non-woven fabrics using the method for the direct coating of dry method
On；
S4, the non-woven fabrics after blade coating is dried at room temperature for 9min；
S5, non-woven fabrics dried in step 4 is dried into 27min in 125 DEG C of drying tunnel；
Wherein, in S1, acrylate copolymer emulsion is the water-dispersed acrylic ester copolymer emulsion of 58wt%；
In S1, acrylate copolymer emulsion is methyl acrylate-acrylic acid ethyl ester copolymer emulsion；
In S1, the mass fraction of biennial wormwood extract is 35wt%；
In S1, the time of stirring is 70min；
In S1, acrylate copolymer emulsion, nano silver, chitosan, titanium dioxide, biennial wormwood extract mass ratio be 150：4：
6：2：15；
In S2, ultraviolet exposure time is 20min；
In S2, a concentration of 20wt% of acetone soln.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of preparation method of the medical coated non-woven of antimicrobial form, which is characterized in that include the following steps：
S1, it after nano silver, chitosan, titanium dioxide, biennial wormwood extract are sequentially added into acrylate copolymer emulsion, stirs to get
Coating；
S2, by nonwoven sample after ultraviolet lower irradiation, be soaked in acetone soln after 40-45min, rushed repeatedly with deionized water
It washes, drying is for use；
S3, coating made from step 1 is scratched using the method for the direct coating of dry method and is dried on for use non-woven fabrics in step 2；
S4, the non-woven fabrics after blade coating is dried at room temperature for 5-10min；
S5, non-woven fabrics dried in step 4 is dried into 18-30min in 100-130 DEG C of drying tunnel.
2. the preparation method of the medical coated non-woven of antimicrobial form according to claim 1, which is characterized in that in S1, acrylic acid
Ester copolymer emulsion is the water-dispersed acrylic ester copolymer emulsion of 50-60wt%.
3. the preparation method of the medical coated non-woven of antimicrobial form according to claim 1 or claim 2, which is characterized in that in S1, propylene
Acid esters copolymer emulsion is methyl acrylate-acrylic acid ethyl ester copolymer emulsion.
4. according to the preparation method of the medical coated non-woven of any one of the claim 1-3 antimicrobial forms, which is characterized in that S1
In, the mass fraction of biennial wormwood extract is 25-35wt%.
5. according to the preparation method of the medical coated non-woven of any one of the claim 1-4 antimicrobial forms, which is characterized in that S1
In, the time of stirring is 60-70min.
6. according to the preparation method of the medical coated non-woven of any one of the claim 1-5 antimicrobial forms, which is characterized in that S1
In, acrylate copolymer emulsion, nano silver, chitosan, titanium dioxide, biennial wormwood extract mass ratio be 100-150：4-7：3-6：
2-5：10-15.
7. according to the preparation method of the medical coated non-woven of any one of the claim 1-6 antimicrobial forms, which is characterized in that S2
In, ultraviolet exposure time is 20-25min.
8. according to the preparation method of the medical coated non-woven of any one of the claim 1-7 antimicrobial forms, which is characterized in that S2
In, a concentration of 12-20wt% of acetone soln.