CN107793639A - 一种防虫蛀塑料编织袋的生产方法 - Google Patents
一种防虫蛀塑料编织袋的生产方法 Download PDFInfo
- Publication number
- CN107793639A CN107793639A CN201711049194.4A CN201711049194A CN107793639A CN 107793639 A CN107793639 A CN 107793639A CN 201711049194 A CN201711049194 A CN 201711049194A CN 107793639 A CN107793639 A CN 107793639A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven
- woven bag
- bag
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种防虫蛀塑料编织袋的生产方法，将聚丙烯、线性低密度聚乙烯、聚苯乙烯、苯胺甲基三乙氧基硅烷、石灰石、环氧树脂、十溴二苯醚、助剂、添加母料依次加入混合机中，在温度为79℃下进行混合均匀，得到混合物，将混合物以100kg/min的加料速度加入到挤出机中进行挤出，然后冷却成型，即得到生产编织袋的涂覆编织布；首先将预热辊筒的温度预热至85℃，冷却棍的温度调至25℃，然后以口膜至生产编织袋的涂覆编织布间隙为120mm将生产编织袋的涂覆编织布放入螺杆挤出机中进行挤出，得到编织袋涂覆布的扁丝；利用圆筒编织机采用平模方法将步骤Ⅲ得到的编织袋涂覆布的扁丝进行编织，然后依次经过切割、裁断和缝纫，即得到塑料编织袋。
Description
技术领域
本发明涉及一种防虫蛀塑料编织袋的生产方法。
背景技术
塑料编织袋按主要材料构成为聚丙烯袋、聚乙烯袋；按缝制方法分为缝底袋、缝边底袋。目前广泛应用于肥料、化工产品等物品的一种包装材料。目前广泛应用于肥料、化工产品等物品的一种包装材料。堆放在库房中很容易被虫咬破而导致内装物漏出。
发明内容
针对现有技术存在的不足，本发明目的是提供一种防虫蛀塑料编织袋的生产方法，以解决上述背景技术中提出的问题。
本发明解决其技术问题是通过以下技术方案实现的：
一种防虫蛀塑料编织袋，包括聚丙烯100份、线性低密度聚乙烯50份、聚苯乙烯20份、苯胺甲基三乙氧基硅烷10份、石灰石5份、环氧树脂2份、十溴二苯醚0.5份、助剂5份、添加母料5份。
该防虫蛀塑料编织袋的制作方法具体如下：
Ⅰ、将聚丙烯100份、线性低密度聚乙烯50份、聚苯乙烯20份、苯胺甲基三乙氧基硅烷10份、石灰石5份、环氧树脂2份、十溴二苯醚0.5份、助剂5份、添加母料5份依次加入混合机中，在温度为79℃下进行混合均匀，得到混合物；
Ⅱ、将混合物以100kg/min的加料速度加入到挤出机中进行挤出，然后冷却成型，即得到生产编织袋的涂覆编织布；
Ⅲ、首先将预热辊筒的温度预热至85℃，冷却棍的温度调至25℃，然后以口膜至生产编织袋的涂覆编织布间隙为120mm将步骤Ⅱ得到的生产编织袋的涂覆编织布放入螺杆挤出机中进行挤出，得到编织袋涂覆布的扁丝；
Ⅳ、利用圆筒编织机采用平模方法将步骤Ⅲ得到的编织袋涂覆布的扁丝进行编织，然后依次经过切割、裁断和缝纫，即得到塑料编织袋。
所述助剂由下列重量份的原料制成：邻苯二甲酸酯40％、粘土20％、明矾15％、促进剂DM 5％、己二醇二丙烯酸酯5％、交联剂TAC5％、抗氧剂1010 4％、阳起石4％、二茂铁3％、二硼化钒2％
所述助剂制备方法是将粘土、阳起石送入煅烧炉中在735℃下煅烧2.5小时，然后，取出，送入20％的硫酸溶液中浸泡1.5小时，过滤，得滤渣，用清水洗净，烘干、研磨成350目粉体；所得粉体与其它剩余成分混合，加热至65℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
本发明有益效果为：
本发明延长编织袋的使用寿命和提高拉伸性能，能有效防治虫蛀，编织袋不易老化，使用寿命长，拉伸力高，使得装载的物品不易产生腐败变质，不易破损，延长编织袋的使用寿命和提高拉伸性能。
具体实施方式
下面对本发明进行详细描述。
实施例：
一种防虫蛀塑料编织袋，包括聚丙烯100份、线性低密度聚乙烯50份、聚苯乙烯20份、苯胺甲基三乙氧基硅烷10份、石灰石5份、环氧树脂2份、十溴二苯醚0.5份、助剂5份、添加母料5份。
该防虫蛀塑料编织袋的制作方法具体如下：
Ⅰ、将聚丙烯100份、线性低密度聚乙烯50份、聚苯乙烯20份、苯胺甲基三乙氧基硅烷10份、石灰石5份、环氧树脂2份、十溴二苯醚0.5份、助剂5份、添加母料5份依次加入混合机中，在温度为79℃下进行混合均匀，得到混合物；
Ⅱ、将混合物以100kg/min的加料速度加入到挤出机中进行挤出，然后冷却成型，即得到生产编织袋的涂覆编织布；
Ⅲ、首先将预热辊筒的温度预热至85℃，冷却棍的温度调至25℃，然后以口膜至生产编织袋的涂覆编织布间隙为120mm将步骤Ⅱ得到的生产编织袋的涂覆编织布放入螺杆挤出机中进行挤出，得到编织袋涂覆布的扁丝；
Ⅳ、利用圆筒编织机采用平模方法将步骤Ⅲ得到的编织袋涂覆布的扁丝进行编织，然后依次经过切割、裁断和缝纫，即得到塑料编织袋。
所述助剂由下列重量份的原料制成：邻苯二甲酸酯40％、粘土20％、明矾15％、促进剂DM 5％、己二醇二丙烯酸酯5％、交联剂TAC5％、抗氧剂1010 4％、阳起石4％、二茂铁3％、二硼化钒2％。
所述助剂制备方法是将粘土、阳起石送入煅烧炉中在735℃下煅烧2.5小时，然后，取出，送入20％的硫酸溶液中浸泡1.5小时，过滤，得滤渣，用清水洗净，烘干、研磨成350目粉体；所得粉体与其它剩余成分混合，加热至65℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
尽管为说明目的公开了本发明的实施例，但是本领域的技术人员可以理解：在不脱离本发明及所附权利要求的精神和范围内，各种替换、变化和修改都是可能的，因此，本发明的范围不局限于实施例所公开的内容。
Claims (1)
1.一种防虫蛀塑料编织袋的生产方法，其特征在于，包括以下步骤：
Ⅰ、将聚丙烯100份、线性低密度聚乙烯50份、聚苯乙烯20份、苯胺甲基三乙氧基硅烷10份、石灰石5份、环氧树脂2份、十溴二苯醚0.5份、助剂5份、添加母料5份依次加入混合机中，在温度为79℃下进行混合均匀，得到混合物；
Ⅱ、将混合物以100kg/min的加料速度加入到挤出机中进行挤出，然后冷却成型，即得到生产编织袋的涂覆编织布；
Ⅲ、首先将预热辊筒的温度预热至85℃，冷却棍的温度调至25℃，然后以口膜至生产编织袋的涂覆编织布间隙为120mm将步骤Ⅱ得到的生产编织袋的涂覆编织布放入螺杆挤出机中进行挤出，得到编织袋涂覆布的扁丝；
Ⅳ、利用圆筒编织机采用平模方法将步骤Ⅲ得到的编织袋涂覆布的扁丝进行编织，然后依次经过切割、裁断和缝纫，即得到塑料编织袋。