CN107686276A - Environment-friendly type steam-aerated concrete plate caulking agent - Google Patents
Environment-friendly type steam-aerated concrete plate caulking agent Download PDFInfo
- Publication number
- CN107686276A CN107686276A CN201710880439.1A CN201710880439A CN107686276A CN 107686276 A CN107686276 A CN 107686276A CN 201710880439 A CN201710880439 A CN 201710880439A CN 107686276 A CN107686276 A CN 107686276A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- steam
- environment
- aerated concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly type steam-aerated concrete plate caulking agent, by weight including following component：5 30 parts of architecture adhesion agent, 10 40 parts of powdered whiting, 30 50 parts of sand, 5 15 parts of water, 0.5 2 parts of waterproofing agent, 0.1 0.5 parts of polypropylene fibre, 0.3 1 parts of water-loss reducer, 0.1 0.5 parts of antifreezing agent, 0.3 1 parts of defoamer, 0.5 1 parts of fireproof agent, 0.5 1.5 parts of preservative.Acted synergistically between each component, there is preferable caking property and pliability, the characteristic that steam-aerated concrete plate can be overcome to absorb water, make that there is preferably connection between sheet material, the infiltration of the aggressive substances such as moisture is reduced, sheet material is not ftractureed in use, improves the service life of wall；Site operation is can be directly used for without stirring, the airborne dust of site operation is reduced, there is the feature of environmental protection.
Description
Technical field
The present invention relates to a kind of caulking agent, more particularly to a kind of environment-friendly type steam-aerated concrete plate caulking agent.
Background technology
Air entrained concrete extensively should because it has the advantages that lightweight, porous, sound insulation, insulation, fire protecting performance are good
With being a kind of novel wall material.Sheet material is when mounted according to detailing requiments and self-deformation feature, it is necessary to set certain amount
Expansion or contraction joints, can also form installation piece during board material splice.Need to carry out jointing processing to the plate stitch of formation after installing.Make
When carrying out filleting with cement mortar, the moisture in mortar is easily quickly absorbed by plate surface, cause filleting mortar without intensity or
As phenomena such as powdered, easily cracking at plate stitch, connection is not close at plate stitch, influences the performance of sheet material.
Therefore, it is necessary to work out the special caulking agent of air entrained concrete sheet material, to ensure that there is preferably connection between sheet material,
Sheet material is not ftractureed in use, improve the service life of wall.
The content of the invention
In view of this, it is an object of the invention to provide a kind of special caulking agent of air entrained concrete sheet material, to ensure sheet material
Between have preferably connection, sheet material is not ftractureed in use, improve the service life of wall.In particular by with
Lower technical scheme is realized：
The environment-friendly type steam-aerated concrete plate caulking agent of the present invention, by weight including following component：Build gluing
Agent 5-30 parts, powdered whiting 10-40 parts, sand 30-50 parts, water 5-15 parts, waterproofing agent 0.5-2 parts, polypropylene fibre 0.1-0.5
Part, water-loss reducer 0.3-1 parts, antifreezing agent 0.1-0.5 parts, defoamer 0.3-1 parts, fireproof agent 0.5-1 parts, preservative 0.5-1.5 parts.
Further, the architecture adhesion agent uses polymer emulsion.
Further, the polymer emulsion is acrylic emulsion.
Further, the polymer emulsion is vinyl copolymer emulsion
Further, the sand is fine sand of the diameter in below 0.6mm.
Further, the waterproofing agent uses capillary crystalline waterproofing agent.
Further, the polypropylene fibre is 0.6mm chopped fiber.
Beneficial effects of the present invention：The environment-friendly type steam-aerated concrete plate caulking agent of the present invention, assist between each component
Same-action, there is preferable caking property and pliability, the characteristic that steam-aerated concrete plate can be overcome to absorb water, make between sheet material
With preferable connection, the infiltration of the aggressive substances such as moisture is reduced, sheet material is not ftractureed in use, improves wall
Service life；Site operation is can be directly used for without stirring, the airborne dust of site operation is reduced, there is the feature of environmental protection；The present invention its
His beneficial effect will combine to be further detailed in embodiment in detail below.
Embodiment
The environment-friendly type steam-aerated concrete plate caulking agent of the present invention, by weight including following component：Build gluing
Agent 5-30 parts, powdered whiting 10-40 parts, sand 30-50 parts, water 5-15 parts, waterproofing agent 0.5-2 parts, polypropylene fibre 0.1-0.5
Part, water-loss reducer 0.3-1 parts, antifreezing agent 0.1-0.5 parts, defoamer 0.3-1 parts, fireproof agent 0.5-1 parts, preservative 0.5-1.5 parts.
Polypropylene fibre intensity is high, acidproof, alkaline-resisting, antimicrobial.Waterproofing agent can use capillary crystalline waterproof agent, and water-loss reducer can be adopted
With starch ether, antifreezing agent can use ethylene glycol, and defoamer can use organic silicon defoamer, and fireproof agent can use three oxidations
Two aluminium, preservative can use sodium benzoate and Kathon CG.
In the present embodiment, the architecture adhesion agent uses polymer emulsion.The caulking agent prepared using polymer emulsion, profit
With air entrained concrete it is hygroscopic the characteristics of, with scattering and disappearing for binding agent moisture, produce cross-linked structure inside slurry, and poly-
Caulking agent intensity is higher caused by chemical bond between adduct molecule.
In the present embodiment, the polymer emulsion is acrylic emulsion.Acrylic emulsion is nontoxic, non-stimulated, to human body without
Evil, meets environmental requirement.
In the present embodiment, the polymer emulsion is vinyl copolymer emulsion.Vinyl is total to
Caulking agent adhesion strength performance is more excellent made from poly- emulsion.
In the present embodiment, the sand be diameter in below 0.6mm fine sand, the Yellow River sand can be used.It is made using fine sand
Caulking agent it is more uniform, filleting effect is more preferable.
In the present embodiment, the waterproofing agent uses capillary crystalline waterproofing agent.It is impervious using capillary crystalline waterproofing agent
Can be more excellent, when carrying out filleting using cement mortar, prevent the moisture in mortar too fast and filleting mortar is caused by plate surface absorption
It is cracking at plate stitch without intensity or as powdered, connect not close at plate stitch, influence the performance of sheet material.
In the present embodiment, the polypropylene fibre is 0.6mm chopped fiber.
The technical scheme of invention is further described with reference to specific embodiment.
Embodiment one
Environment-friendly type steam-aerated concrete plate caulking agent in the present embodiment, by weight including following component：
Vinyl copolymer emulsion：9.8 part
Powdered whiting：24.4 parts
The Yellow River sand：48.8 parts
Water：14.6 parts
Waterproofing agent：1.4 part
Polypropylene fibre：0.2 part
Water-loss reducer：0.3 part
Antifreezing agent：0.1 part
Defoamer：0.3 part
Fireproof agent：0.5 part
Preservative：0.5 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and the intensity requirement of decorative mortar.The caulking agent glues
Knotting strength is 0.64MPa, adhesion strength 0.67MPa after heat ageing, adhesion strength 0.51MPa after 70 DEG C of high temperature, is bonded after immersion
Intensity 0.49MPa.
In the present embodiment, vinyl copolymer emulsion is replaced by acrylic emulsion, the intensity of gained caulking agent
Decrease, but still meet《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam pressure is added
The intensity requirement of gas concrete masonry units and decorative mortar.
Embodiment two
A kind of environment-friendly type steam-aerated concrete plate caulking agent, by weight including following component：
Vinyl copolymer emulsion：17.3 parts
Powdered whiting：23.1 parts
The Yellow River sand：46.2 parts
Water：11.1 parts
Waterproofing agent：1.2 part
Polypropylene fibre：0.1 part
Water-loss reducer：0.2 part
Antifreezing agent：0.2 part
Defoamer：0.5 part
Fireproof agent：0.5 part
Preservative：0.8 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and the intensity requirement of decorative mortar.The caulking agent glues
Knotting strength is 0.97MPa, adhesion strength 0.99MPa after heat ageing, adhesion strength 0.62MPa after 70 DEG C of high temperature, is bonded after immersion
Intensity 0.54MPa.
In the present embodiment, vinyl copolymer emulsion is replaced by acrylic emulsion, the intensity of gained caulking agent
Decrease, but still meet《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam pressure is added
The intensity requirement of gas concrete masonry units and decorative mortar.
Embodiment three
A kind of environment-friendly type steam-aerated concrete plate caulking agent, by weight including following component：
Vinyl copolymer emulsion：23.3 parts
Powdered whiting：23.3 parts
The Yellow River sand：46.6 parts
Water：4.7 part
Waterproofing agent：0.7 part
Polypropylene fibre：0.1 part
Water-loss reducer：0.1 part
Antifreezing agent：0.3 part
Defoamer：0.5 part
Fireproof agent：0.7 part
Preservative：1.2 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and the intensity requirement of decorative mortar.The caulking agent glues
Knotting strength is 1.03MPa, adhesion strength 1.02MPa after heat ageing, adhesion strength 0.65MPa after 70 DEG C of high temperature, is bonded after immersion
Intensity 0.59MPa.
In the present embodiment, vinyl copolymer emulsion is replaced by acrylic emulsion, the intensity of gained caulking agent
Decrease, but still meet《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam pressure is added
The intensity requirement of gas concrete masonry units and decorative mortar.
Example IV
A kind of environment-friendly type steam-aerated concrete plate caulking agent, by weight including following component：
Acrylic emulsion：17.4 parts
Powdered whiting：23.2 parts
The Yellow River sand：46.3 parts
Water：11.6 parts
Polypropylene fibre：0.1 part
Water-loss reducer：0.2 part
Antifreezing agent：0.2 part
Defoamer：0.5 part
Fireproof agent：0.5 part
Preservative：1.2 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) to the intensity requirement of steam-pressing aero-concrete masonry mortar.The adhesion strength of the caulking agent
For 0.86MPa, adhesion strength 0.84MPa after heat ageing, adhesion strength 0.59MPa after 70 DEG C of high temperature, adhesion strength after immersion
0.51MPa。
In the present embodiment, acrylic emulsion is replaced by vinyl copolymer emulsion, gained caulking agent is still full
Foot《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and wiped one's face
The intensity requirement of mortar.
Embodiment five
Environment-friendly type steam-aerated concrete plate caulking agent in the present embodiment, by weight including following component：
Vinyl copolymer emulsion：5 parts
Powdered whiting：10 parts
The Yellow River sand：30 parts
Water：5 parts
Waterproofing agent：0.5 part
Polypropylene fibre：0.1 part
Water-loss reducer：0.3 part
Antifreezing agent：0.1 part
Defoamer：0.5 part
Fireproof agent：0.5 part
Preservative：0.5 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and the intensity requirement of decorative mortar.The caulking agent glues
Knotting strength is 0.64MPa, adhesion strength 0.66MPa after heat ageing, adhesion strength 0.49MPa after 70 DEG C of high temperature, is bonded after immersion
Intensity 0.45MPa.
In the present embodiment, vinyl copolymer emulsion is replaced by acrylic emulsion, the intensity of gained caulking agent
Decrease, but still meet《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam pressure is added
The intensity requirement of gas concrete masonry units and decorative mortar.
Embodiment six
Environment-friendly type steam-aerated concrete plate caulking agent in the present embodiment, by weight including following component：
Vinyl copolymer emulsion：5 parts
Powdered whiting：20 parts
The Yellow River sand：40 parts
Water：10 parts
Waterproofing agent：1.5 part
Polypropylene fibre：0.3 part
Water-loss reducer：0.5 part
Antifreezing agent：0.1 part
Defoamer：0.3 part
Fireproof agent：0.5 part
Preservative：1 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and the intensity requirement of decorative mortar.The caulking agent glues
Knotting strength is 0.43MPa, adhesion strength 0.45MPa after heat ageing, adhesion strength 0.39MPa after 70 DEG C of high temperature, is bonded after immersion
Intensity 0.31MPa.
In the present embodiment, vinyl copolymer emulsion is replaced by acrylic emulsion, the intensity of gained caulking agent
Decrease, but still meet《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam pressure is added
The intensity requirement of gas concrete masonry units and decorative mortar.
Embodiment seven
Environment-friendly type steam-aerated concrete plate caulking agent in the present embodiment, by weight including following component：
Vinyl copolymer emulsion：30 parts
Powdered whiting：40 parts
The Yellow River sand：50 parts
Water：15 parts
Waterproofing agent：2 parts
Polypropylene fibre：0.5 part
Water-loss reducer：1 part
Antifreezing agent：0.3 part
Defoamer：0.7 part
Fireproof agent：0.7 part
Preservative：1.5 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and the intensity requirement of decorative mortar.The caulking agent glues
Knotting strength is 0.98MPa, adhesion strength 1.01MPa after heat ageing, adhesion strength 0.67MPa after 70 DEG C of high temperature, is bonded after immersion
Intensity 0.63MPa.
In the present embodiment, vinyl copolymer emulsion is replaced by acrylic emulsion, the intensity of gained caulking agent
Decrease, but still meet《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam pressure is added
The intensity requirement of gas concrete masonry units and decorative mortar.
Embodiment eight
Environment-friendly type steam-aerated concrete plate caulking agent in the present embodiment, by weight including following component：
Vinyl copolymer emulsion：30 parts
Powdered whiting：20 parts
The Yellow River sand：30 parts
Water：5 parts
Waterproofing agent：0.5 part
Polypropylene fibre：0.1 part
Water-loss reducer：0.3 part
Antifreezing agent：0.5 part
Defoamer：1.0 part
Fireproof agent：1.0 part
Preservative：0.5 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and the intensity requirement of decorative mortar.The caulking agent glues
Knotting strength is 1.36MPa, adhesion strength 1.41MPa after heat ageing, adhesion strength 0.86MPa after 70 DEG C of high temperature, is bonded after immersion
Intensity 0.91MPa.
In the present embodiment, vinyl copolymer emulsion is replaced by acrylic emulsion, the intensity of gained caulking agent
Decrease, but still meet《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam pressure is added
The intensity requirement of gas concrete masonry units and decorative mortar.
Embodiment nine
Environment-friendly type steam-aerated concrete plate caulking agent in the present embodiment, by weight including following component：
Vinyl copolymer emulsion：30 parts
Powdered whiting：20 parts
The Yellow River sand：40 parts
Water：10 parts
Waterproofing agent：1.5 part
Polypropylene fibre：0.3 part
Water-loss reducer：0.5 part
Antifreezing agent：0.4 part
Defoamer：0.8 part
Fireproof agent：0.8 part
Preservative：1 part
Because steam-pressing aero-concrete pasty polymer caulking agent does not have clear and definite standard, therefore reference《Ceramic wall and floor bricks
Adhesive》The detection method of paste adhesive in (JC/T 547-2005), and《Steam-pressing aero-concrete masonry mortar with
Decorative mortar》(JC890-2001) steam-pressing aero-concrete is built by laying bricks or stones and the intensity requirement of decorative mortar.The caulking agent glues
Knotting strength is 1.05MPa, adhesion strength 1.08MPa after heat ageing, adhesion strength 0.72MPa after 70 DEG C of high temperature, is bonded after immersion
Intensity 0.75MPa.
In the present embodiment, vinyl copolymer emulsion is replaced by acrylic emulsion, the intensity of gained caulking agent
Decrease, but still meet《Steam-pressing aero-concrete masonry mortar and decorative mortar》(JC890-2001) steam pressure is added
The intensity requirement of gas concrete masonry units and decorative mortar.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of technical solution of the present invention, it all should cover at this
Among the right of invention.
Claims (7)
1. a kind of environment-friendly type steam-aerated concrete plate caulking agent, it is characterised in that by weight including following component：Building
Adhesive 5-30 parts, powdered whiting 10-40 parts, sand 30-50 parts, water 5-15 parts, waterproofing agent 0.5-2 parts, polypropylene fibre
0.1-0.5 parts, water-loss reducer 0.3-1 parts, antifreezing agent 0.1-0.5 parts, defoamer 0.3-1 parts, fireproof agent 0.5-1 parts, preservative
0.5-1.5 parts.
2. environment-friendly type steam-aerated concrete plate caulking agent according to claim 1, it is characterised in that：The building adhesive
Stick uses polymer emulsion.
3. environment-friendly type steam-aerated concrete plate caulking agent according to claim 2, it is characterised in that：The polymer
Emulsion is acrylic emulsion.
4. environment-friendly type steam-aerated concrete plate caulking agent according to claim 2, it is characterised in that：The polymer
Emulsion is vinyl copolymer emulsion.
5. environment-friendly type steam-aerated concrete plate caulking agent according to claim 1, it is characterised in that：The sand is straight
Fine sand of the footpath in below 0.6mm.
6. environment-friendly type steam-aerated concrete plate caulking agent according to claim 1, it is characterised in that：The waterproofing agent
Using capillary crystalline waterproofing agent.
7. environment-friendly type steam-aerated concrete plate caulking agent according to claim 1, it is characterised in that：The polypropylene
Fiber is 0.6mm chopped fiber.