CN107556891A - A kind of Men Yeyong water-based finishing varnish - Google Patents
A kind of Men Yeyong water-based finishing varnish Download PDFInfo
- Publication number
- CN107556891A CN107556891A CN201710842980.3A CN201710842980A CN107556891A CN 107556891 A CN107556891 A CN 107556891A CN 201710842980 A CN201710842980 A CN 201710842980A CN 107556891 A CN107556891 A CN 107556891A
- Authority
- CN
- China
- Prior art keywords
- water
- percent
- kinds
- yeyong
- men
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Men Yeyong water-based finishing varnish, its component and mass percent are as follows：Water-base resin 60~80, amino resins 6~12, rheology modified auxiliary agent 1~5, wetting and dispersing auxiliary agent 0.1~1, cosolvent 2~6, deionized water 8~20；Also include defoamer, mass percentage content is 0.1~0.5%；Also include Ph conditioning agents, mass percentage content is 0.2~1.0%；Also include levelling agent, mass percentage content is 0.2~1.0%.Men Yeyong water-based finishing varnish of the present invention, is mono-component aqueous baking vanish, does not contain the organic solvents such as benzene,toluene,xylene and heavy metal, non-ignitable not quick-fried, belongs to environmentally friendly machine；Adhesive force is good, and hardness is high；Paint film is plentiful, and gloss is high；Have good workability, meet the construction requirement of door industry production；Extremely low VOC, uses water-dilutable completely；Product has the advantages of high-performance, low cost, low stain.
Description
Technical field
The present invention relates to the water-based stoving paint of technical field of paint preparation, and in particular to a kind of aqueous, environmental protective, adhesive force are good, hardness
It is high, paint film is plentiful, gloss is high, workability is excellent is mainly used in the metalwork surface such as iron skill door, antitheft door Lacquer finish decoration
Men Yeyong water-based finishing varnish.
Background technology
In recent years, antitheft door production industry grows rapidly with the rise of real-estate market, has also driven antitheft door painting
The development of material.Baking vanish is because its is easy for construction, quick, and film performance is excellent, can meet the requirement of various occasions, and one
Since straight very big share has been occupied in antitheft door field of coating.With the pressure of environmental protection policy, consumer's environmental consciousness constantly carries
Rise, provinces and cities especially in all parts of the country have put into effect VOC emission limit standard, and encouragement uses non-solvent coating, to environmental protection such as water paints
The development of coating brings opportunity, therefore promotes the development of water-based stoving paint.No matter water-based stoving paint is gone back in film physical property
It is on decorative coating film, can even reaches the effect as solvent-borne type baking vanish in terms of workability in theory.
The development of the water-based special coating varnish of door industry and the shared market share are increasing year by year, and market prospects are optimistic.Cause
The water-based door industry that this develops a kind of aqueous, environmental protective, adhesive force is good, hardness is high, paint film is plentiful, gloss is high, workability is excellent is special
Coating varnish has very high economic benefit and social benefit.
The content of the invention
For above-mentioned the deficiencies in the prior art, present invention seek to address that traditional solvent-borne baking vanish VOC content is high, dirty to environment
Contaminate the problem of serious, there is provided a kind of water-based covers of Men Yeyong for being mainly used in the metalwork surface such as iron skill door, antitheft door Lacquer finish decoration
Light varnish.
In order to solve the above-mentioned technical problem, present invention employs following technical scheme：
A kind of Men Yeyong water-based finishing varnish, it is characterised in that：Its component and mass percentage content are as follows：
| Composition | Percentage by weight（%） |
| Water-base resin | 60~80 |
| Amino resins | 6~12 |
| Rheology modified auxiliary agent | 1~5 |
| Wetting and dispersing auxiliary agent | 0.1~1 |
| Cosolvent | 2~6 |
| Deionized water | 8~22 |
Wherein water-base resin is：Any of aqueous alkide resin, water-based acrylic resin, aqueous polyester resin, or wherein
Any two, or three kinds be each greater than 0 percent arbitrary proportion mix；
Wherein amino resins is：Height methyl-etherified melamine resin, full Amino resin, part methyl-etherified amino
Any of resin, or two of which, or three kinds be each greater than 0 percent arbitrary proportion mix；
Wherein rheology modified auxiliary agent is：Rheology modified wax emulsion, polyamide wax, Compositional type polyamide wax, modified gas phase titanium dioxide
Any of silicon, or wherein any two, it is or wherein wantonly three kinds, or four kinds mixed with the arbitrary proportion for being each greater than 0 percent
Close；
Wherein wetting and dispersing auxiliary agent is：Any of acetylenic glycols nonionic surface active agent, BYK-190, BYK-346, or
Wherein any two, or three kinds be each greater than 0 percent arbitrary proportion mix；
Wherein cosolvent is：Any of butyl glycol ether, propylene glycol monomethyl ether, butanol, or wherein any two, or three kinds with each
From the arbitrary proportion mixing more than 0 percent.
Further feature is：Also include defoamer, mass percentage content is 0.1~0.5%；The defoamer is that have
Machine polymer, polyether siloxane copolymer emulsion it is any, or two of which is to be each greater than 0 percent arbitrary proportion
Mixing.
Also include Ph conditioning agents, mass percentage content is 0.2~1.0%；Ph conditioning agents are：Multifunction amine AMP-95 is helped
Any of agent, dimethylethanolamine, ammoniacal liquor, or wherein any two, or three kinds to be each greater than 0 percent any ratio
Example mixing.
Also include levelling agent, mass percentage content is 0.2~1.0%；Levelling agent is：Polyether siloxane copolymer, high score
Son amount aqueous emulsion of dimethyl polysiloxane fluid, any of organic-silicon-modified polysiloxanes, or wherein any two, or three kinds with respective
Arbitrary proportion mixing more than 0 percent.
Men Yeyong water-based finishing varnish of the present invention, compared with the prior art, there are following features：
Men Yeyong water-based finishing varnish of the present invention, mainly by the water-base resin of special modification, amino resins, functional aid, go
Ionized water etc. forms, and is mono-component aqueous baking vanish, has as follows a little：
（1）The organic solvents such as benzene,toluene,xylene and heavy metal are not contained, it is non-ignitable not quick-fried, belong to environmentally friendly machine.
（2）Adhesive force is good, and hardness is high.
（3）Paint film is plentiful, and gloss is high.
（4）Have good workability, meet the construction requirement of door industry production.
（5）Extremely low VOC, uses water-dilutable completely.
（6）Product has the advantages of high-performance, low cost, low stain.
Embodiment
With reference to specific embodiment, the present invention is described in further detail.Wherein, for description using it is all as above,
Under, the exemplary term such as left and right, it is therefore intended that help reader to understand, without being intended for limiting.
The Men Yeyong water-based finishing varnish of the present invention, is mainly helped by the water-base resin, amino resins, feature of special modification
Agent, deionized water etc. form, and its component and mass percentage content are as follows：
| Composition | Percentage by weight（%） |
| Water-base resin | 60~80 |
| Amino resins | 6~12 |
| Rheology modified auxiliary agent | 1~5 |
| Wetting and dispersing auxiliary agent | 0.1~1 |
| Cosolvent | 2~6 |
| Deionized water | 8~22 |
Also include defoamer, mass percentage content is 0.1~0.5%.
Also include Ph conditioning agents, mass percentage content is 0.2~1%.
Also include levelling agent, mass percentage content is 0.1~1%.
Wherein water-base resin is：Any of aqueous alkide resin, water-based acrylic resin, aqueous polyester resin, or
Two of which, or three kinds be each greater than 0 percent arbitrary proportion mix；
Wherein amino resins is：Height methyl-etherified melamine resin（Height methyl-etherified refer in resin dissociate methylol it is few,
Methyl-etherified degree is high, and molecular weight is small.）, full Amino resin, part Amino resin（Part methyl-etherified refers to resin
Reactive group in structure has methoxy and methylol）Any of, or two of which, or three kinds to be each greater than hundred
/ zero arbitrary proportion mixing；
Wherein rheology modified auxiliary agent is：Rheology modified wax emulsion, polyamide wax, Compositional type polyamide wax, modified gas phase titanium dioxide
Any of silicon, or two of which, or three kinds be each greater than 0 percent arbitrary proportion mix；
Wherein wetting and dispersing auxiliary agent is：Acetylenic glycols nonionic surface active agent, BYK-190（BYK is that German Bi Ke chemistry is public
Department）, any of BYK-346, or two of which, or three kinds mixed with the arbitrary proportion for being each greater than 0 percent；
Wherein Ph conditioning agents are：Multifunction amine AMP-95 auxiliary agents（2-amino-2-methyl-1-propanol, DOW Chemical product）, diformazan
Any of ethylethanolamine, ammoniacal liquor, or two of which, or three kinds be each greater than 0 percent arbitrary proportion mix；
Wherein levelling agent is：Polyether siloxane copolymer, HMW aqueous emulsion of dimethyl polysiloxane fluid, organic-silicon-modified poly- silica
Any of alkane, or two of which, or three kinds be each greater than 0 percent arbitrary proportion mix；
Wherein defoamer is：Organic polymer, polyether siloxane copolymer emulsion it is any, or two of which with each greater than
0 percent arbitrary proportion mixing；Organic polymer such as BYK-011, BYK-022, BYK-024 etc.；
Wherein cosolvent is：Any of butyl glycol ether, propylene glycol monomethyl ether, butanol, or two of which, or three kinds with respective
Arbitrary proportion mixing more than 0 percent；
Wherein deionized water can be factory's self-control as solvent.
The water-base resin of the present invention, the content that can be chosen are 60%, 65%, 70%, 75%, 80% etc., can meet the present invention
Needs；Amino resins, the content that can be chosen are 6%, 7%, 8%, 9%, 10%, 11%, 12% etc., can meet the need of the present invention
Will；Rheology modified auxiliary agent, the content that can be chosen are 1%, 2%, 3%, 4%, 5% etc., can meet the needs of the present invention；Wetting point
Auxiliary agent is dissipated, the content that can be chosen is 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0% etc., all
The needs of the present invention can be met；Ph conditioning agents, the content that can be chosen be 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%,
0.8%th, 0.9%, 1.0% etc., the needs of the present invention can be met；Levelling agent, the content that can be chosen be 0.1%, 0.2%, 0.3%,
0.4%th, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0% etc., the needs of the present invention can be met；Defoamer, what can be chosen contains
Measure as 0.1%, 0.2%, 0.3%, 0.4%, 0.5% etc., the needs of the present invention can be met；Cosolvent, the content that can be chosen are
2%th, 3%, 4%, 5%, 6% etc., the needs of the present invention can be met；Deionized water, the content that can be chosen be 8%, 9%, 10%, 11%,
12%th, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 11%, 22% etc., the needs of the present invention can be met.
Men Yeyong water-based finishing varnish of the present invention, baking condition are：140-170 DEG C of baking temperature, baking time 20-
50 minutes, determined according to specific material and model.
Specific embodiment 1：
Men Yeyong water-based finishing varnish of the present invention, water-base resin percentage by weight 60%, amino resins percentage by weight 10%, rheology
Modified additive percentage by weight 4%, wetting and dispersing auxiliary agent percentage by weight 0.2%, Ph conditioning agents percentage by weight 0.2%, levelling agent
Percentage by weight 0.2%, defoamer percentage by weight 0.4%, cosolvent percentage by weight 5%, deionized water weight percentage 20%,
Its manufacture craft is：Deionized water is weighed by weight percentage, is slowly added to help as rheology modified under high-speed stirred state
It is standby less than 20 microns that the aerosil of agent is allowed to fineness；Under stirring, sequentially add as special water-base resin
Aqueous alkide resin, as the full Amino resin of amino resins, the acetylenic glycols nonionic as wetting dispersing agent
Surfactant, as the dimethylethanolamine of PH conditioning agents, as the organic-silicon-modified polysiloxane leveling agents of levelling agent, make
For the organic polymer defoamer of defoamer, as co-solvents propylene glycol methyl ether and butanol and scattered rheology modified help
Agent, 30min is stirred, is filtered and packaged after the assay was approved.
Specific embodiment 2：
Men Yeyong water-based finishing varnish of the present invention, water-base resin percentage by weight 68%, amino resins percentage by weight 9%, rheology
Modified additive percentage by weight 3%, wetting and dispersing auxiliary agent percentage by weight 0.5%, Ph conditioning agents percentage by weight 0.6%, levelling agent
Percentage by weight 0.4%, defoamer percentage by weight 0.5%, cosolvent percentage by weight 2%, deionized water weight percentage 16%,
Its manufacture craft is：Deionized water is weighed by weight percentage, is slowly added to help as rheology modified under high-speed stirred state
It is standby less than 20 microns that the aerosil of agent is allowed to fineness；Under stirring, sequentially add as special water-base resin
Aqueous alkide resin, as the full Amino resin of amino resins, the acetylenic glycols nonionic as wetting dispersing agent
Surfactant, as the dimethylethanolamine of PH conditioning agents, as the organic-silicon-modified polysiloxane leveling agents of levelling agent, make
For the organic polymer defoamer of defoamer, as co-solvents propylene glycol methyl ether and butanol and scattered rheology modified help
Agent, 30min is stirred, is filtered and packaged after the assay was approved.
Specific embodiment 3：
Men Yeyong water-based finishing varnish of the present invention, water-base resin percentage by weight 78%, amino resins percentage by weight 6%, rheology
Modified additive percentage by weight 1%, wetting and dispersing auxiliary agent percentage by weight 0.1%, Ph conditioning agents percentage by weight 0.8%, levelling agent
Percentage by weight 0.7%, defoamer percentage by weight 0.5%, cosolvent percentage by weight 3%, deionized water weight percentage 10%,
Its manufacture craft is：Deionized water is weighed by weight percentage, is slowly added to help as rheology modified under high-speed stirred state
It is standby less than 20 microns that the aerosil of agent is allowed to fineness；Under stirring, sequentially add as special water-base resin
Aqueous alkide resin, as the full Amino resin of amino resins, the acetylenic glycols nonionic as wetting dispersing agent
Surfactant, as the dimethylethanolamine of PH conditioning agents, as the organic-silicon-modified polysiloxane leveling agents of levelling agent, make
For the organic polymer defoamer of defoamer, as co-solvents propylene glycol methyl ether and butanol and scattered rheology modified help
Agent, 30min is stirred, is filtered and packaged after the assay was approved.
Specific embodiment 4：
Men Yeyong water-based finishing varnish of the present invention, water-base resin percentage by weight 80%, amino resins percentage by weight 6%, rheology
Modified additive percentage by weight 1%, wetting and dispersing auxiliary agent percentage by weight 0.1%, Ph conditioning agents percentage by weight 0.8%, levelling agent
Percentage by weight 0.7%, defoamer percentage by weight 0.5%, cosolvent percentage by weight 2%, deionized water weight percentage 9%,
Its manufacture craft is：Deionized water is weighed by weight percentage, is slowly added to help as rheology modified under high-speed stirred state
It is standby less than 20 microns that the aerosil of agent is allowed to fineness；Under stirring, sequentially add as special water-base resin
Aqueous alkide resin, as the full Amino resin of amino resins, the acetylenic glycols nonionic as wetting dispersing agent
Surfactant, as the dimethylethanolamine of PH conditioning agents, as the organic-silicon-modified polysiloxane leveling agents of levelling agent, make
For the organic polymer defoamer of defoamer, as co-solvents propylene glycol methyl ether and butanol and scattered rheology modified help
Agent, 30min is stirred, is filtered and packaged after the assay was approved.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention rather than restriction technologies side
Case, although the present invention is described in detail with reference to preferred embodiment by applicant, one of ordinary skill in the art should manage
Solution, technical scheme is modified for those or equivalent substitution, without departing from the objective and scope of the technical program,
It all should cover among scope of the presently claimed invention.
Claims (4)
- A kind of 1. Men Yeyong water-based finishing varnish, it is characterised in that：Its component and mass percentage content are as follows：
Composition Percentage by weight（%） Water-base resin 60~80 Amino resins 6~12 Rheology modified auxiliary agent 1~5 Wetting and dispersing auxiliary agent 0.1~1 Cosolvent 2~6 Deionized water 8~22 Wherein water-base resin is：Any of aqueous alkide resin, water-based acrylic resin, aqueous polyester resin, or wherein Any two, or three kinds be each greater than 0 percent arbitrary proportion mix；Wherein amino resins is：Height methyl-etherified melamine resin, full Amino resin, part methyl-etherified amino Any of resin, or two of which, or three kinds be each greater than 0 percent arbitrary proportion mix；Wherein rheology modified auxiliary agent is：Rheology modified wax emulsion, polyamide wax, Compositional type polyamide wax, modified gas phase titanium dioxide Any of silicon, or wherein any two, it is or wherein wantonly three kinds, or four kinds mixed with the arbitrary proportion for being each greater than 0 percent Close；Wherein wetting and dispersing auxiliary agent is：Any of acetylenic glycols nonionic surface active agent, BYK-190, BYK-346, or Wherein any two, or three kinds be each greater than 0 percent arbitrary proportion mix；Wherein cosolvent is：Any of butyl glycol ether, propylene glycol monomethyl ether, butanol, or wherein any two, or three kinds with each From the arbitrary proportion mixing more than 0 percent. - 2. Men Yeyong water-based finishing varnish according to claim 1, it is characterised in that：Also include defoamer, mass percent Content is 0.1~0.5%；The defoamer be organic polymer, polyether siloxane copolymer emulsion it is any, or wherein two Kind is mixed with the arbitrary proportion for being each greater than 0 percent.
- 3. Men Yeyong water-based finishing varnish according to claim 1, it is characterised in that：Also include Ph conditioning agents, quality percentage It is 0.2~1.0% than content；Ph conditioning agents are：Any of multifunction amine AMP-95 auxiliary agents, dimethylethanolamine, ammoniacal liquor, Or wherein any two, or three kinds be each greater than 0 percent arbitrary proportion mix.
- 4. according to any Men Yeyong water-based finishing varnish of claim 1-3, it is characterised in that：Also include levelling agent, quality Degree is 0.2~1.0%；Levelling agent is：Polyether siloxane copolymer, HMW aqueous emulsion of dimethyl polysiloxane fluid, have Any of machine Si modification polysiloxanes, or wherein any two, or three kinds mixed with the arbitrary proportion for being each greater than 0 percent Close.