CN107433322A - 一种铸造涂料 - Google Patents

一种铸造涂料 Download PDF

Info

Publication number
CN107433322A
CN107433322A CN201710373204.3A CN201710373204A CN107433322A CN 107433322 A CN107433322 A CN 107433322A CN 201710373204 A CN201710373204 A CN 201710373204A CN 107433322 A CN107433322 A CN 107433322A
Authority
CN
China
Prior art keywords
parts
ethanol
coating
weight ratio
titanium dioxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710373204.3A
Other languages
English (en)
Inventor
彭朝阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yuzhou City Shuo Machinery Manufacturing Plant
Original Assignee
Yuzhou City Shuo Machinery Manufacturing Plant
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yuzhou City Shuo Machinery Manufacturing Plant filed Critical Yuzhou City Shuo Machinery Manufacturing Plant
Priority to CN201710373204.3A priority Critical patent/CN107433322A/zh
Publication of CN107433322A publication Critical patent/CN107433322A/zh
Pending legal-status Critical Current

Abstract

本发明提出了一种铸造涂料，该涂料由以下重量份数的原料制成：石墨粉40‑45份、硅藻土6‑10份、十二烷基磺酸钠10‑12份、二氧化钛3‑6份、粘结剂2‑4份、丙烯酸树酯8‑12份、硬脂酰胺6‑15份、乙醇10‑25份，其中所述硬脂酰胺与所述乙醇的重量比为1:1.5，所述丙烯酸树酯与所述二氧化钛的重量比为2：1。其有益效果是：本发明的石墨粉铸造涂料以石墨粉为主要原料，隔热效果好，其他原料的合适配比得到的涂料提高了附着力，从而防止铸件的粘砂现象，经试验证明，硬脂酰胺与乙醇的重量比为1:1.5，涂料的悬浮性能较，丙烯酸树酯与二氧化钛的重量比为2：1时，涂料的耐火性较好。

Description

一种铸造涂料
技术领域
本发明涉及铸造领域，特别是指一种铸造涂料。
背景技术
是重力型金属铸造的基础涂料，适用于所有金属模具。铸造涂料颗粒相对较粗，但绝热性能好，可防止铸造时铸件缺肉和冷隔。适于细薄截面铸件和大平面铸件，也适用于供料口、轮毂、活塞、连杆、气缸等；一般情况下，铸造涂料的涂挂方法有刷、浸、淋、喷或浸淋相结合几种，其中浸涂法具有生产效率高、节省涂料、涂层均匀以及对涂料的要求不高、操作简便、不需要特殊设备等优点，在实际应用中深受欢迎。
发明内容
本发明为解决现有的问题，提出一种铸造涂料。
本发明的技术方案是这样实现的：
一种铸造涂料，该涂料由下列重量份的原料组成：石墨粉40-45份、硅藻土6-10份、十二烷基磺酸钠10-12份、二氧化钛3-6份、粘结剂2-4份、丙烯酸树酯8-12份、硬脂酰胺6-15份、乙醇10-25份，其中所述硬脂酰胺与所述乙醇的重量比为1:1.5，所述丙烯酸树酯与所述二氧化钛的重量比为2：1。
所述所述硅藻土中二氧化硅的含量大于百分之93%，氧化铁的含量为1.3-1.5%。
所述粘结剂为环氧树脂、酚醛树脂、聚酰亚胺中的一种或几种。
石墨粉42份、硅藻土9份、十二烷基磺酸钠10份、二氧化钛5份、粘结剂4份、丙烯酸树酯10份、硬脂酰胺8份、乙醇12份。
本发明的有益效果是：本发明的石墨粉铸造涂料以石墨粉为主要原料，隔热效果好，其他原料的合适配比得到的涂料提高了附着力，从而防止铸件的粘砂现象，经试验证明，硬脂酰胺与乙醇的重量比为1:1.5，涂料的悬浮性能较，丙烯酸树酯与二氧化钛的重量比为2：1时，涂料的耐火性较好。
具体实施方式
下面将结合本发明的实施例，对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有付出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本实施例中，一种铸造涂料，该涂料由下列重量份的原料组成：石墨粉42份、硅藻土9份、十二烷基磺酸钠10份、二氧化钛5份、粘结剂4份、丙烯酸树酯10份、硬脂酰胺8份、乙醇12份，其中所述硬脂酰胺与所述乙醇的重量比为1:1.5，丙烯酸树酯与二氧化钛的重量比为2：1，硅藻土中二氧化硅的含量大于百分之93%，氧化铁的含量为1.3-1.5%；粘结剂为环氧树脂、酚醛树脂、聚酰亚胺中的一种或几种，以上的范围值适于质量较大或者体积较大的铸造件。
实施例2
本实施例中，该涂料由下列重量份的原料组成：石墨粉40份、硅藻土10份、十二烷基磺酸钠10份、二氧化钛3份、粘结剂4份、丙烯酸树酯6份、硬脂酰胺11份、乙醇16份，其中所述硬脂酰胺与所述乙醇的重量比为1:1.5，丙烯酸树酯与二氧化钛的重量比为2：1，硅藻土中二氧化硅的含量大于百分之93%，氧化铁的含量为1.3-1.5%；粘结剂为环氧树脂、酚醛树脂、聚酰亚胺中的一种或几种，以上的范围值适于质量较大或者体积较大的铸造件。
本发明的制备方法是：将石墨粉和二氧化钛、硅藻土和十二烷基硫酸钠按照比例置于球磨机中干法球磨3h，其中，料球比为1:4.5，得到粉碎后的物料与丙烯酸树脂和硬脂酰胺一起置于搅拌机中充分搅拌混合，最后缓慢加入乙醇，充分搅拌后得到石墨粉铸造涂料。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.一种铸造涂料，其特征在于：该涂料由下列重量份的原料组成：石墨粉40-45份、硅藻土6-10份、十二烷基磺酸钠10-12份、二氧化钛3-6份、粘结剂2-4份、丙烯酸树酯8-12份、硬脂酰胺6-15份、乙醇10-25份，其中所述硬脂酰胺与所述乙醇的重量比为1:1.5，所述丙烯酸树酯与所述二氧化钛的重量比为2：1。
2.根据权利要求1所述的铸造涂料，其特征在于：所述所述硅藻土中二氧化硅的含量大于百分之93%，氧化铁的含量为1.3-1.5%。
3.根据权利要求1所述的铸造涂料，其特征在于：所述粘结剂为环氧树脂、酚醛树脂、聚酰亚胺中的一种或几种。
4.根据权利要求1或3所述的铸造涂料，其特征在于：石墨粉42份、硅藻土9份、十二烷基磺酸钠10份、二氧化钛5份、粘结剂4份、丙烯酸树酯10份、硬脂酰胺8份、乙醇12份。
CN201710373204.3A 2017-05-24 2017-05-24 一种铸造涂料 Pending CN107433322A (zh)