CN107365542A - One kind blade coating sliver paint and preparation method thereof - Google Patents
One kind blade coating sliver paint and preparation method thereof Download PDFInfo
- Publication number
- CN107365542A CN107365542A CN201610311549.1A CN201610311549A CN107365542A CN 107365542 A CN107365542 A CN 107365542A CN 201610311549 A CN201610311549 A CN 201610311549A CN 107365542 A CN107365542 A CN 107365542A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- sliver
- water
- blade coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind blade coating sliver paint and preparation method thereof, the preparation method for scratching sliver paint is as follows：(1) water, hydroxypropyl cellulose, multiple poly- silicon MPS 6 are mixed into slurry；(2) silicone acrylic emulsion is sequentially added, coalescents, ethylene glycol, non-ionic wetting agent, ammonium salt dispersant, bactericide, defoamer, AMP 95, the modest water-based thickeners of WT 102 of moral is diluted with water；(3) XMG High Viscosity Bentonites are slowly added to the mode winnowed again to stir, make base-material；(4) compound sliver and color sand are added in base-material, is stirred in mineral varnish tank as finished product paint.Present invention blade coating sliver paint, it is air after applying on the wall, elegance, light, easy for construction, it is the remarkable high-tech product of a kind of environmental protection, energy-saving safety performance, cost is low, practical, is adapted to popularization and application.
Description
Technical field
The present invention relates to coating to scratch field, particularly a kind of blade coating sliver paint and preparation method thereof.
Background technology
Coating is a kind of more long construction material of history, with the development of society, the kind of coating now
Class is also more and more；People often like selecting environment-protecting and non-poisonous water paint, water paint group substantially
As water, filler, emulsion and other auxiliary addition agents etc., but due to selecting different material, proportioning difference
The effect brought is also different, and the order of addition of the also one various raw materials of technical barrier also can be to production
Product have an impact, so needing to invent a kind of low, environment-protecting and non-poisonous, the easy for construction water paint of volatility
Meet the market requirement.
But also have since the cladding lithotome of skin, after tiling is halted by country, imitate stone
Material coating arises at the historic moment.Water-water and water bag sliver paint coating, although with lithotome similarity up to 95%
More than, but because too thin, after some coats wall, three, five years with regard to bulge, cracking, peeling, due to depositing
In above mentioned problem, people in actual use with having thickness, the true mineral varnish for having intensity and spraying sliver paint,
The needs of common engineering can be met.The small sliver allowed in spraying paint sliver paint becomes big sliver, but big rock
Piece blocks up muzzle, want transform spray gun it is too difficult, have to change construction technology for blade coating.
The content of the invention
The invention aims to solve the above problems, by studying for many years, with physicochemical colloid
Based on technology and surface active process, solve in blade coating that the big big sliver of sliver sinks, small sliver floats,
It is layered a series of problems such as film forming, there is provided the high natural-like stone of a kind of " blade coating sliver paint ", be coated in wall
It is air after upper, elegance, light, easy for construction, it is the remarkable high-tech of a kind of environmental protection, energy-saving safety performance
Skill product, cost is low, practical, is adapted to popularization and application.
Realize the above-mentioned purpose present invention it is a kind of scratch sliver paint and preparation method thereof technical scheme be：
A kind of formula for scratching sliver paint is made up of the raw material of following parts by weight：Water：43870 parts, hydroxypropyl
Base cellulose：382-400 parts, multiple poly- silicon MPS-6:559-785 parts, silicone acrylic emulsion：48000-55000
Part, coalescents：1180-1500 parts, ethylene glycol：1180-3000 parts, non-ionic wetting agent：764.8
- 1000 parts, ammonium salt dispersant：589.7-700 parts add 826-950 parts water to dilute, bactericide：764.8-1000
Part, defoamer：112 parts, AMP-95:1200-1500 parts, the modest WT-102 water-based thickeners of moral：700-943
Part, XMG High Viscosity Bentonites：580-1000 parts；
The preparation method for scratching sliver paint is as follows：
(1) by 43870 parts of water, 382-400 parts hydroxypropyl cellulose, 559 parts -785 parts multiple poly- silicon MPS-6:
Mixing rotates 30 minutes in 700 revs/min of beater, breaks into slurry；
(2) 48000-55000 parts silicone acrylic emulsion, 1180-1500 parts coalescents, 1180-3000 are sequentially added
Part ethylene glycol, 764.8-1000 parts non-ionic wetting agent, with 826-950 parts water dilute ammonium salt dispersant
589.7-700 part, bactericide：764.8-1000 part, defoamer：112 parts, 1200-1500 part AMP-95,
The modest WT-102 water-based thickeners of 700-943 part morals；
(3) 580-1000 part XMG High Viscosity Bentonites are slowly added to the mode winnowed again；Rear middling speed is added to stir
Mix 30 minutes, make base-material；
(4) compound sliver and color sand are added in base-material, is stirred in mineral varnish tank as finished product paint.
Preferably, the compound sliver addition of the addition is big and piece is big, it can effectively stop that ultraviolet bangs
Hit, can effectively extend the coating life-span；After being made, first sample is taken to mix colours, with sample presentation sample similarity up to 95%
More than.
The construction technology of blade coating sliver paint of the present invention is to start construction in putty aspect, specific a kind of
The construction technology step for scratching sliver paint is as follows：
(1) bottom closing paint：By the embedding polishing of putty aspect batch, one is brushed in then dedusting, then putty aspect after dedusting
To twice bottom closing paint, brush uniformly, dosage is 250 parts every square metre；
(2) frame bar：The putty aspect for scribbling bottom closing paint is divided into grid with frame bar, the present invention uses 2~3mm
Thick double-sided foam tape is as frame bar；
(3) sliver paint is scratched：Brush scratches sliver paint, dosage 4000 together in point trellised putty aspect
Every square metre of part；
(4) finish：Scratch and brush one after sliver paint applies after 48 hours to twice finish, dosage is 250 parts every
Square metre.
In summary, by adopting the above-described technical solution, the beneficial effects of the invention are as follows：This practicality scratches rock
Piece paint formula and construction technology, it is air after applying on the wall, elegance, light, easy for construction, be a kind of environmental protection,
The remarkable high-tech product of energy-saving safety performance, cost is low, practical, and suitable popularization and application are adapted to promote
Using.
Embodiment
Embodiment 1：
A kind of formula for scratching sliver paint is by water：43870g, hydroxypropyl cellulose：382g, multiple poly- silicon MPS-6:
559g, silicone acrylic emulsion：48000g, coalescents：1180g, ethylene glycol：1180g, non-ionic wetting agent：
764.8g ammonium salt dispersant：589.7g adds 826g water to dilute, bactericide：764.8g, defoamer：112g,
AMP-95:1200g, the modest WT-102 water-based thickeners of moral：700g, XMG High Viscosity Bentonite：580g；
The preparation method for scratching sliver paint is as follows：
(1) by 43870g water, 382g hydroxypropyl celluloses, the multiple poly- silicon MPS-6 of 559g:In 700 revs/min beat
Mixing rotates 30 minutes in pulp grinder, breaks into slurry；
(2) sequentially add 48000g silicone acrylic emulsions, 1180g coalescents, 1180g ethylene glycol, 764.8g it is non-from
Sub- wetting agent, with 826g water ammonium salt dispersant 589.7g, bactericide 764.8g, defoamer 112g are diluted,
The modest WT-102 water-based thickeners of 1200g AMP-95,700g morals；
(3) 580g XMG High Viscosity Bentonites are slowly added to the mode winnowed again；Rear moderate-speed mixer 30 is added to divide
Clock, make base-material；
(4) compound sliver and color sand are added in base-material, is stirred in mineral varnish tank as finished product paint.
The compound sliver addition added is big and piece is big, can effectively stop that ultraviolet bombards, can effectively prolong
The long coating life-span；After being made, first sample is taken to mix colours, with sample presentation sample similarity up to more than 95%.
The construction technology of blade coating sliver paint is to start construction in putty aspect, a kind of specific blade coating sliver paint
Construction technology step it is as follows：
(1) bottom closing paint：By the embedding polishing of putty aspect batch, one is brushed in then dedusting, then putty aspect after dedusting
To twice bottom closing paint, brush uniformly, dosage is 250 parts every square metre；
(2) frame bar：The putty aspect for scribbling bottom closing paint is divided into grid with frame bar, the present invention uses 2~3mm
Thick double-sided foam tape is as frame bar；
(3) sliver paint is scratched：Brush scratches sliver paint, dosage 4000 together in point trellised putty aspect
Every square metre of part；
(4) finish：Scratch and brush one after sliver paint applies after 48 hours to twice finish, dosage is 250 parts every
Square metre.
Embodiment 2：
A kind of formula for scratching sliver paint is by water：43870g, hydroxypropyl cellulose：400g, multiple poly- silicon
MPS-6:785g, silicone acrylic emulsion：55000g, coalescents：1500g, ethylene glycol：3000g, it is non-from
Sub- wetting agent 1000g, ammonium salt dispersant：700g adds 950g water to dilute, bactericide 1000g, defoamer
112g, AMP-95:1500g, the modest WT-102 water-based thickeners of moral：943g, XMG High Viscosity Bentonite：
1000g；
The preparation method for scratching sliver paint is as follows：
(1) 43870g water, 400g hydroxypropyl celluloses, 785g are answered into poly- silicon MPS-6, in 700 revs/min beat
Mixing rotates 30 minutes in pulp grinder, breaks into slurry；
(2) sequentially add 55000g silicone acrylic emulsions, 1500g coalescents, 3000g ethylene glycol, 1000g it is non-from
Sub- wetting agent, with 950g water dilute ammonium salt dispersant 700g, bactericide 1000g, defoamer 112g, 1500g
The modest WT-102 water-based thickeners of AMP-95,943g moral；
(3) 580-1000g XMG High Viscosity Bentonites are slowly added to the mode winnowed again；Rear middling speed is added to stir
Mix 30 minutes, make base-material；
(4) compound sliver and color sand are added in base-material, is stirred in mineral varnish tank as finished product paint.
Beneficial effects of the present invention：
Blade coating sliver paint of the invention a kind of, it is air after applying on the wall, elegance, light, easy for construction, it is a kind of
The remarkable high-tech product of environmental protection, energy-saving safety performance, cost is low, practical, is adapted to popularization and application.
It is the performance comparision for scratching sliver paint and lithotome, spraying sliver paint below：
Scratch the performance comparision of sliver paint and lithotome：
Sliver paint is scratched compared with spraying sliver paint：
Above-mentioned technical proposal only embodies the optimal technical scheme of technical solution of the present invention, the art
Technical staff embodies the principle of the present invention, category to some variations that some of which part may be made
Within protection scope of the present invention.
Claims (3)
1. one kind blade coating sliver paint, it is characterised in that：Formula is made up of the raw material of following parts by weight：Water：
43870 parts, hydroxypropyl cellulose：382-400 parts, multiple poly- silicon MPS-6:559-785 parts, silicone acrylic emulsion：
48000-55000 parts, coalescents：1180-1500 parts, ethylene glycol：1180-3000 parts, nonionic profit
Humectant 764.8-1000 parts, ammonium salt dispersant：589.7-700 parts add 826-950 parts water to dilute, bactericide
764.8-1000 part, 112 parts of defoamer, AMP-95:1200-1500 parts, the water-based thickenings of the modest WT-102 of moral
Agent：700-943 parts, XMG High Viscosity Bentonites：580-1000 parts；
The preparation method for scratching sliver paint is as follows：
(1) by 43870 parts of water, 382-400 parts hydroxypropyl cellulose, 559 parts -785 parts multiple poly- silicon MPS-6:
Mixing rotates 30 minutes in 700 revs/min of beater, breaks into slurry；
(2) 48000-55000 parts silicone acrylic emulsion, 1180-1500 parts coalescents, 1180-3000 are sequentially added
Part ethylene glycol, 764.8-1000 parts non-ionic wetting agent, with 826-950 parts water dilute ammonium salt dispersant
589.7-700 parts, bactericide 764.8-1000 parts, 112 parts of defoamer, 1200-1500 parts AMP-95,
The modest WT-102 water-based thickeners of 700-943 part morals；
(3) 580-1000 part XMG High Viscosity Bentonites are slowly added to the mode winnowed again；Rear middling speed is added to stir
Mix 30 minutes, make base-material；
(4) compound sliver and color sand are added in base-material, is stirred in mineral varnish tank as finished product paint.
2. a kind of blade coating sliver paint preparation method according to claim 1, it is characterised in that described to add
The compound sliver addition entered is big and piece is big, can effectively stop that ultraviolet bombards, can effectively extend coating
Life-span；After being made, first sample is taken to mix colours, with sample presentation sample similarity up to more than 95%.
3. one kind blade coating sliver paint, it is characterised in that：Construction technology is to start construction in putty aspect,
A kind of construction technology step of specific blade coating sliver paint is as follows：
(1) bottom closing paint：By the embedding polishing of putty aspect batch, one is brushed in then dedusting, then putty aspect after dedusting
To twice bottom closing paint, brush uniformly, dosage is 250 parts every square metre；
(2) frame bar：The putty aspect for scribbling bottom closing paint is divided into grid with frame bar, the present invention uses 2~3mm
Thick double-sided foam tape is as frame bar；
(3) sliver paint is scratched：Brush scratches sliver paint, dosage 4000 together in point trellised putty aspect
Every square metre of part；
(4) finish：Scratch and brush one after sliver paint applies after 48 hours to twice finish, dosage is 250 parts every
Square metre.