CN106896425A - 保护膜及应用该保护膜的偏光板 - Google Patents
保护膜及应用该保护膜的偏光板 Download PDFInfo
- Publication number
- CN106896425A CN106896425A CN201611044646.5A CN201611044646A CN106896425A CN 106896425 A CN106896425 A CN 106896425A CN 201611044646 A CN201611044646 A CN 201611044646A CN 106896425 A CN106896425 A CN 106896425A
- Authority
- CN
- China
- Prior art keywords
- diaphragm
- protective layer
- degree
- polarizing film
- shaft angle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种保护膜及应用该保护膜的偏光板。保护膜包括保护层。保护层具有一介于0度至20度之间的轴角度。保护层更具有X轴及迟相轴，其中轴角度是迟相轴与X轴向所夹成的角度。本发明的保护层本身的轴角度较低，因此保护膜具有低眩光、低彩虹纹或甚至无眩光或无彩虹纹等优良特性。如此一来，即使以倾斜角度观察偏光板，保护膜仍不致产生过强的眩光或甚至不产生眩光，使眼睛可清楚观察到保护膜底下的偏光膜的质量状况。
Description
技术领域
本发明是有关于一种保护膜及应用其的偏光板，且特别是有关于一种具有低轴角的保护膜及应用其的偏光板。
背景技术
传统的偏光板包括偏光膜及保护膜，保护膜形成于偏光膜上。在检验上，通常是以目测观察保护膜底下的偏光膜是否具有缺陷。然而，保护膜通常会反光，其产生的眩光会阻碍眼睛对偏光膜的检验。
因此，亟需提出一种新的技术去改善现有保护膜的眩光问题。
发明内容
本发明提出一种保护膜及应用该保护膜的偏光板，以改善现有技术中保护膜的炫光问题。
本发明的目的是这样实现的，一种保护膜，该保护膜包括：
一保护层，具有一介于0度至20度之间的轴角度，其中该保护层更具有一X轴及一迟相轴，且该轴角度是该迟相轴与该X轴向所夹成的角度。
本发明还提供了一种保护膜，该保护膜包括：
一保护层，具有一轴角度及一X轴；
其中，往该X轴的方向看去，该保护层的宽度的中央区域的该轴角度小于靠近该保护层的两端点的该轴角度。
在一具体实施方式中，该保护层的任意两点的该轴角度之差小于20度。
在一具体实施方式中，该保护层的材料选自聚酯树脂、烯烃树脂、乙酸纤维素树脂、聚碳酸酯树脂、丙烯酸树脂、聚对苯二甲酸丁二酯、聚乙烯、聚丙烯、环烯烃树脂或其组合，其中该聚酯树脂是聚对苯二甲酸乙二酯或聚萘二甲酸乙二酯，该丙烯酸树脂是聚甲基丙烯酸甲酯。
在一具体实施方式中，该保护膜更包含：
一黏合层，形成于该保护层上；
其中，该黏合层由甲基丙烯酸共聚物制成；及/或该黏合层的表面阻抗小于1012Ω/□。
在一具体实施方式中，该保护层具有一表面处理层；及/或该保护层经电晕放电技术改质；及/或该保护层经易接着化学处理；及/或该保护层的表面阻抗小于1011Ω/□；及/或该保护膜的雾度介于0.5％至10％。
在一具体实施方式中，该保护膜更包括：
一离型层，覆盖该黏合层。
在一具体实施方式中，该保护膜的厚度介于12微米至250微米之间。
本发明还提供了一种偏光板，该偏光板包括：
一偏光膜；以及
上述的该保护膜，配置于该偏光膜上。
在一具体实施方式中，该偏光膜包括：
一第一覆盖层；
一第二覆盖层；以及
一偏光层，形成于该第一覆盖层与该第二覆盖层之间。
在一具体实施方式中，该保护膜对该偏光膜的剥离力介于0.02N/25mm至0.3N/25mm之间；及/或该保护膜对该偏光膜的剥离带电量小于3kV。
本发明的有益效果：
本发明的保护层本身的轴角度较低，因此保护膜具有低眩光、低彩虹纹或甚至无眩光或无彩虹纹等优良特性。如此一来，即使以倾斜角度观察偏光板，保护膜仍不致产生过强的眩光或甚至不产生眩光，使眼睛可清楚观察到保护膜底下的偏光膜的质量状况。
附图说明
图1为依照本发明一实施例的保护膜的示意图。
图2为依照本发明一实施例的偏光板的示意图。
图3为依照本发明另一实施例的保护膜的示意图。
其中，附图标记：
10：偏光板
100、100＇：保护膜
110：保护层
120：黏合层
130：离型层
200：偏光膜
210：第一覆盖层
220：偏光层
230：第二覆盖层
A1、A2：角度
S1：曲线
T1：厚度
X、Y、Z：坐标轴
W1：宽度
具体实施方式
请参考图1，其为依照本发明一实施例的保护膜100的示意图。保护膜100包括保护层110及黏合层120。黏合层120形成于保护层110上。
本发明的保护层110具有低轴角度，因此可产生低眩光特性。如图1所示的保护层110的宽度W1与轴角度的关系曲线S1所示，保护层110的轴角度小于一预定角度A1。预定角度A1例如是介于0至20度之间，可使保护膜100产生低眩光效果且可减少彩虹纹现象。在另一实施例中，预定角度A1可以低于15度或更低。此处的轴角度指的是在保护层110的迟相轴与保护层110的X轴向所夹成的角度，此处的迟相轴也称为慢轴。
在一实施例中，如图1所示，往X轴的方向看去，本发明实施例的保护层110宽度W1的中央区域的轴角度小于靠近保护层110的两端点的轴角度。在一实施例中，保护层110的任意两点的轴角度之差小于20度、低于15度、低于10度或低于5度。
本发明实施例的保护层110的轴角度都小于预定角度A1，因此全宽幅的保护层110原材料或保护膜100成品都可完整使用，不需特别考虑裁除边缘不符合要求的高轴角度部分材料，因此不会产生材料耗损问题(高轴角度容易产生眩光及/或彩虹纹)，且可减少工艺步骤并增加产品良率。
在本实施例中，上述X轴向例如是保护层110的宽度方向，而Z轴向为保护层110的长度延伸方向。在另一实施例中，X轴向可以是保护层110的长度延伸方向，而Z轴向可以是保护层110的宽度方向。在轴角度的测量方法上，可采用吸收轴角度测量仪对保护层110或保护膜100进行测量。吸收轴角度测量仪的型号例如型号PLS-2R。
在一实施例中，保护膜100的厚度T1例如是介于12微米至250微米之间。此外，保护层110可由聚酯树脂、烯烃树脂、乙酸纤维素树脂、聚碳酸酯树脂、丙烯酸树脂、聚对苯二甲酸丁二酯(polyethylene terephthalate,PET)、聚乙烯(polyethylene,PE)或聚丙烯(Polypropylene,PP)、环烯烃树脂或上述的组合，其中聚酯树脂例如是聚对苯二甲酸乙二酯或聚萘二甲酸乙二酯，而丙烯酸树脂例如是聚甲基丙烯酸甲酯(PMMA)。
此外，保护膜100的保护层110上可形成表面处理层，例如是防止表面污染的防污层、防止表面产生静电效应的抗静电层、防止划痕的硬涂层等。上述的抗静电层例如是(a)具有四级铵盐、吡啶鎓、伯氨基、仲氨基、叔氨基等阳离子基的各种阳离子抗静电剂；(b)具有磺酸碱基、硫酸酯碱基、磷酸酯碱基、膦酸碱基等的阴离子基的阴离子抗静电剂；(c)氨基酸类、氨基硫酸酯类等的两性抗静电剂；(d)氨基醇类、甘油类、聚乙二醇类等的非离子抗静电剂；(e)使如上所述的抗静电剂高分子量化得到的高分子型抗静电剂等。
在另一实施例中，也可以在保护层110的表面上以电晕放电技术对表面进行改质，以增加黏合层120与保护层110之间的黏着性。或者，可在保护层110上进行易接着化学处理，使黏合层120容易接着于保护层110，也可减少或甚至避免残胶量。
此外，黏合层120可由例如是甲基丙烯酸共聚物材料制成，例如是可包含但不限于官能基的材料，如甲基丙烯酸甲酯、甲基丙烯酸乙酯、甲基丙烯酸丁酯、甲基丙烯酸2-乙基己酯等材料。
图2为依照本发明一实施例的偏光板10的示意图。偏光板10包括保护膜100及偏光膜200，其中保护膜100配置于偏光膜200上。在一实施例中，可对上述保护膜100裁切为适当尺寸后，贴附于偏光膜200上，以形成偏光板10。
偏光膜200包括第一覆盖层210、偏光层220及第二覆盖层230，其中偏光层220形成于第一覆盖层210与第二覆盖层230之间。保护膜100通过黏合层120黏合于偏光膜200的第一覆盖层210上，其中黏合层120位于第一覆盖层210与保护层110之间。
偏光层220可为吸附配向的二色性色素的聚乙烯醇(polyvinyl alcohol,PVA)薄膜或由液晶材料掺附具吸收染料分子所形成。聚乙烯醇可通过皂化聚乙酸乙烯酯而形成。在一些实施例中，聚乙酸乙烯酯可为乙酸乙烯酯的单聚物或乙酸乙烯酯及其它单体的共聚物等。上述其它单体可为不饱和羧酸类、烯烃类、不饱和磺酸类或乙烯基醚类等。在另一些实施例中，聚乙烯醇可为经改质的聚乙烯醇，例如，经醛类改质的聚乙烯甲醛、聚乙烯乙醛或聚乙烯丁醛等。
第一覆盖层210与第二覆盖层230的材料可选自于由三醋酸纤维素(TriacetateCellulose，TAC)、聚甲基丙烯酸甲酯(Polymethylmethacrylate，PMMA)、聚乙烯对苯二甲酸酯(Polyethylene Terephthalate，PET)、聚丙稀(Polypropylene，PP)、环烯烃聚合物(Cyclo Olefin Polymer，COP)、聚碳酸酯(Polycarbonate，PC)或上述任意组合所组成的一族群。
如图2所示，以眼睛倾斜一角度A2通过保护膜100检查底下的偏光膜200的偏光层220是否具有缺陷，其中角度A2例如是45度，然亦可大于45度，如60度至80度之间，或小于45度，如接近0度。由于本发明实施例的保护膜100具有低眩光特性或无眩光特性，因此即使以倾斜角度观察偏光板10，保护膜100仍不致产生过强的眩光或甚至不产生眩光，使眼睛可清楚观察到保护膜100底下的偏光膜200的质量状况。
此外，保护膜100的雾度可介于0.5％至10％之间，较佳为介于0.5％至7％之间，最佳为介于0.5％至5％之间；如此保护膜100可具有优良的透光性。
保护膜100对偏光膜200(例如是其第一覆盖层210)的剥离力可介于0.02牛顿(N)/25毫米(mm)至0.3N/25mm之间，较佳为介于0.03N/25mm至0.2N/25mm之间，最佳为介于0.04N/25mm至0.15N/25mm之间；如此一来，在偏光板10贴合于基板之后，保护膜100容易自偏光膜200撕除。此外，以保护膜100的抗静电能力来说，保护层110的表面阻抗小于1011Ω/□，黏合层120的表面阻抗小于1012Ω/□，而黏合层120对偏光膜200的剥离带电量小于3kV(千伏)，较佳为小于1kV，最佳为小于0.5kV；如此可减少或甚至避免静电伤害保护膜100及/或偏光膜200。
图3为依照本发明另一实施例的保护膜100＇的示意图。在本实施例中，保护膜100＇除了包含保护层110及黏合层120外，更包含离型层130，其中黏合层120形成于保护层110与离型层130之间，且离型层130覆盖黏合层120。由于离型层130覆盖黏合层120，可避免黏合层120露出而自黏或黏附到其它物体上。离型层130在保护膜100＇配置于偏光膜200(偏光膜200绘示于图2)之前，会先自黏合层120上撕除，以露出黏合层120，使黏合层120可黏合在偏光膜200上。
此外，离型层130可例如是表面涂有离型剂的聚对苯二甲酸乙二醇酯薄膜，离型剂例如是但不限于硅树脂。另外，在轴角度的测量方法上，可采用吸收轴角度测量仪对保护层110或保护膜100＇进行测量。
综上可知，本发明实施例的保护层本身的轴角度较低的，因此保护膜具有低眩光、低彩虹纹或甚至无眩光或无彩虹纹等优良特性。如此一来，即使以倾斜角度观察偏光板，保护膜仍不致产生过强的眩光或甚至不产生眩光，使眼睛可清楚观察到保护膜底下的偏光膜的质量状况。
当然，本发明还可有其它多种实施例，在不背离本发明精神及其实质的情况下，熟悉本领域的技术人员可根据本发明作出各种相应的改变和变形，但这些相应的改变和变形都应属于本发明权利要求的保护范围。
Claims (11)
1.一种保护膜，其特征在于，该保护膜包括：
一保护层，具有一介于0度至20度之间的轴角度，其中该保护层更具有一X轴及一迟相轴，且该轴角度是该迟相轴与该X轴向所夹成的角度。
2.一种保护膜，其特征在于，该保护膜包括：
一保护层，具有一轴角度及一X轴；
其中，往该X轴的方向看去，该保护层的宽度的中央区域的该轴角度小于靠近该保护层的两端点的该轴角度。
3.如权利要求1或2所述的保护膜，其特征在于，该保护层的任意两点的该轴角度之差小于20度。
4.如权利要求1或2所述的保护膜，其特征在于，该保护层的材料选自聚酯树脂、烯烃树脂、乙酸纤维素树脂、聚碳酸酯树脂、丙烯酸树脂、聚对苯二甲酸丁二酯、聚乙烯、聚丙烯、环烯烃树脂或其组合，其中该聚酯树脂是聚对苯二甲酸乙二酯或聚萘二甲酸乙二酯，该丙烯酸树脂是聚甲基丙烯酸甲酯。
5.如权利要求1或2所述的保护膜，其特征在于，更包含：
一黏合层，形成于该保护层上；
其中，该黏合层由甲基丙烯酸共聚物制成；及/或该黏合层的表面阻抗小于1012Ω/□。
6.如权利要求1或2所述的保护膜，其特征在于，该保护层具有一表面处理层；及/或该保护层经电晕放电技术改质；及/或该保护层经易接着化学处理；及/或该保护层的表面阻抗小于1011Ω/□；及/或该保护膜的雾度介于0.5％至10％。
7.如权利要求5所述的保护膜，其特征在于，更包括：
一离型层，覆盖该黏合层。
8.如权利要求1、2或7所述的保护膜，其特征在于，该保护膜的厚度介于12微米至250微米之间。
9.一种偏光板，其特征在于，该偏光板包括：
一偏光膜；以及
权利要求1、2或7所述的该保护膜，配置于该偏光膜上。
10.如权利要求9所述的偏光板，其特征在于，该偏光膜包括：
一第一覆盖层；
一第二覆盖层；以及
一偏光层，形成于该第一覆盖层与该第二覆盖层之间。
11.如权利要求9所述的偏光板，其特征在于，该保护膜对该偏光膜的剥离力介于0.02N/25mm至0.3N/25mm之间；及/或该保护膜对该偏光膜的剥离带电量小于3kV。