CN106675103A - Environment-friendly activated calcium carbonate - Google Patents
Environment-friendly activated calcium carbonate Download PDFInfo
- Publication number
- CN106675103A CN106675103A CN201510752630.9A CN201510752630A CN106675103A CN 106675103 A CN106675103 A CN 106675103A CN 201510752630 A CN201510752630 A CN 201510752630A CN 106675103 A CN106675103 A CN 106675103A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- parts
- environment
- friendly
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses environment-friendly activated calcium carbonate. The environment-friendly activated calcium carbonate is prepared from the following raw materials in parts by weight: 90 to 110 parts of calcium carbonate, 3 to 4 parts of polyethylene wax, 10 to 12 parts of shell powder, 0.1 to 0.3 part of sodium hyaluronate, 0.2 to 0.4 part of lecithin, 2 to 4 parts of polyether polyol, 3.3 to 4.5 parts of anilmomethyl triethoxy, 3 to 5 parts of copper stearate, 0.1 to 0.2 part of sodium alga acid, 2 to 2.5 parts of styrene and a proper amount of deionized water. The formula adopts environment-friendly non-toxic raw materials, safe and non-toxic components are added, and high-molecular polymer enables that the strength enhancement, toughness enhancement and high-temperature and low-temperature resistance of the product are greatly improved.
Description
Technical field
The present invention relates to Calcium Carbonate field, more particularly to a kind of environment-friendly active Calcium Carbonate.
Background technology
Calcium Carbonate is a kind of highly important functional inorganic filling, be widely used in plastics, rubber,
The industrial circle such as coating and papermaking.In the application of Calcium Carbonate, most products belong to the category of polymer,
Such as plastics, rubber, adhesive, coating etc., and occupy the important market share..However, dispersant
With the addition of surface modifier so that nano-calcium carbonate temperature is diminished significantly using window, reason is conventional
Dispersant and coupling agent are easily decomposes at high temperature, cause bubble, cracking, defect, deformation etc., and not
Beneficial to environmental protection；Activated Calcium carbonate is with Calcium Carbonate as base material, using polyfunctional surfactant and compound height
Effect processing aid, is modified activation processing and forms to inorganic powder surface.Calcium Carbonate after modified process
Powder body, surface forms a kind of special cladding structure, can significantly improve in the polymer matrixs such as polyolefin
Dispersibility and affinity, and interface interaction can be produced and between polymer matrix, so as to improve the anti-impact of product
Hit intensity, is a kind of incremental filling additive of function admirable.
A kind of environment-friendly active Calcium Carbonate disclosed by the invention, it is obtained by the raw material of following weight parts：Carbonic acid
Calcium 90-110, Tissuemat E 3-4, conch meal 10-12, hyaluronate sodium 0.1-0.3, lecithin
0.2-0.4, polyether polyol 2-4, anilinomethyl triethoxy 3.3-4.5, copper stearate 3-5, Sargassum
Sour sodium 0.1-0.2, styrene 2-2.5, appropriate deionized water.Inventive formulation adopts environment-protecting asepsis raw material,
Addition safety non-toxic composition, with high molecular polymer make product enhancing, toughness reinforcing, high temperature resistant it is low it is cold can be all
Improve a lot.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of environment-friendly active Calcium Carbonate, it is
It is obtained by the raw material of following weight parts：Calcium Carbonate 90-110, Tissuemat E 3-4, conch meal 10-12,
Hyaluronate sodium 0.1-0.3, lecithin 0.2-0.4, polyether polyol 2-4, anilinomethyl triethoxy
3.3-4.5, copper stearate 3-5, sodium alginate 0.1-0.2, styrene 2-2.5, appropriate deionized water.
A kind of preparation method of environment-friendly active Calcium Carbonate of the present invention is comprised the following steps：
(1) by Calcium Carbonate add homogenizer after, add Tissuemat E, conch meal, hyaluronate sodium,
Lecithin, polyether polyol, anilinomethyl triethoxy, copper stearate, sodium alginate, are warming up to 80-90 DEG C
Between stir, insulation 20-30 minutes after pour out.
(2) appropriate deionized water, stirring is added to form suspension and pour out the material poured out while hot；
(3) suspension is mixed with styrene, is stirred 20 minutes, dried, be ground into fine powder.
The invention has the beneficial effects as follows：Formula adopts environment-protecting asepsis raw material, adds safety non-toxic composition, with height
Molecularly Imprinted Polymer makes product cold can all improve a lot enhancing, toughness reinforcing, high temperature resistant are low.
Specific embodiment
Specific embodiment：A kind of environment-friendly active Calcium Carbonate, it is obtained by the raw material of following weight parts：Calcium Carbonate
90-110, Tissuemat E 3-4, conch meal 10-12, hyaluronate sodium 0.1-0.3, lecithin 0.2-0.4,
Polyether polyol 2-4, anilinomethyl triethoxy 3.3-4.5, copper stearate 3-5, sodium alginate 0.1-0.2,
Styrene 2-2.5, appropriate deionized water.
A kind of preparation method of environment-friendly active Calcium Carbonate of the present invention is comprised the following steps：
(1) by Calcium Carbonate add homogenizer after, add Tissuemat E, conch meal, hyaluronate sodium,
Lecithin, polyether polyol, anilinomethyl triethoxy, copper stearate, sodium alginate, are warming up to 80-90 DEG C
Between stir, insulation 20-30 minutes after pour out.
(2) appropriate deionized water, stirring is added to form suspension and pour out the material poured out while hot；
(3) suspension is mixed with styrene, is stirred 20 minutes, dried, be ground into fine powder.
Inventive formulation adopts environment-protecting asepsis raw material, adds safety non-toxic composition, and with high molecular polymer product is made
Product cold can all improve a lot enhancing, toughness reinforcing, high temperature resistant are low.
Obviously, above-described embodiment is only intended to clearly illustrate example, and not to embodiment
Limit.For those of ordinary skill in the field, it can also be made on the basis of the above description
The change or variation of its multi-form.There is no need to be exhaustive to all of embodiment.And by
Among this obvious change extended out or variation are still in the protection domain of the invention.
Claims (2)
1. a kind of environment-friendly active Calcium Carbonate, it is characterised in that：It is obtained by the raw material of following weight parts：Carbonic acid
Calcium 90-110, Tissuemat E 3-4, conch meal 10-12, hyaluronate sodium 0.1-0.3, lecithin
0.2-0.4, polyether polyol 2-4, anilinomethyl triethoxy 3.3-4.5, copper stearate 3-5, Sargassum
Sour sodium 0.1-0.2, styrene 2-2.5, appropriate deionized water.
2. a kind of environment-friendly active Calcium Carbonate according to claim 1, it is characterised in that：Preparation method include with
Lower step：
(1) Calcium Carbonate is added after homogenizer, adds Tissuemat E, conch meal, hyaluronate sodium, ovum
Phospholipid, polyether polyol, anilinomethyl triethoxy, copper stearate, sodium alginate, are warming up to 80-90 DEG C
Between stir, insulation 20-30 minutes after pour out.
(2) appropriate deionized water, stirring is added to form suspension and pour out the material poured out while hot；
(3) suspension is mixed with styrene, is stirred 20 minutes, dried, be ground into fine powder.