CN106281115A - A kind of wrapping paper adhesive - Google Patents
A kind of wrapping paper adhesive Download PDFInfo
- Publication number
- CN106281115A CN106281115A CN201610741440.1A CN201610741440A CN106281115A CN 106281115 A CN106281115 A CN 106281115A CN 201610741440 A CN201610741440 A CN 201610741440A CN 106281115 A CN106281115 A CN 106281115A
- Authority
- CN
- China
- Prior art keywords
- parts
- wrapping paper
- raw material
- following raw
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wrapping paper adhesive, it includes host and auxiliary agent.Described host forms according to the parts by weight of following raw material: epoxy resin 10 30 parts, organic siliconresin 20 40 parts, 5 20 parts of silicone rubber, neoprene 30 50 parts；Described auxiliary agent forms according to the parts by weight of following raw material: diaminodiphenyl-methane 13 parts, ditridecyl phthalate 25 parts, 15 parts of asbestos, polyimides 2 10 parts, dibasic lead phosphite 13 parts, hindered phenol 12 parts, modified rosin resin 13 parts and other additives.The wrapping paper adhesive of the present invention utilizes the interaction of rubber and synthetic resin greatly to strengthen its cementability and toughness, improves the service life of wrapping paper.
Description
Technical field
The present invention relates to a kind of wrapping paper adhesive.
Background technology
Along with the economic development of China, material flow industry have also been obtained quickly development.Owing to needing the article of circulation more to come
The most, the demand for packaging carton is the most increasing.Therefore, the demand for the adhesive used by wrapping paper material is also got over
Come the biggest.
Some multi-functional wrapping paper adhesives also arise at the historic moment, and are currently used for carton adhesive kind a lot, have three
Aldehyde glue and white glue with vinyl etc..Some adhesive are producing and can discharge free state formaldehyde in application process, endanger human body and environment
Evil is serious；Some adhesive, resistance to water and moisture-proof are poor, easily moisture absorption in humid air, and adhesive strength is the highest；At high temperature
Use can produce creep, makes glue-joint strength decline, and stores easy freezing below-5 DEG C, makes emulsion be destroyed, therefore leads
Cause its application the most limited.
Therefore a kind of cementability is good, and the wrapping paper adhesive of good toughness is urgently by demand.
Summary of the invention
The purpose of the present invention is that provides a kind of cementability good to solve the problems referred to above, and toughness is strong, improves simultaneously
The wrapping paper adhesive in the service life of wrapping paper.
To achieve these goals, the present invention is achieved by the following technical solutions: a kind of wrapping paper adhesive, it
Including host and auxiliary agent；Described host forms according to the parts by weight of following raw material: epoxy resin 10-30 part, organosilicon tree
Fat 20-40 part, silicone rubber 5-20 part, neoprene 30-50 part；Described auxiliary agent forms according to the parts by weight of following raw material: two
Aminodiphenylmethane 1-3 part, ditridecyl phthalate 2-5 part, asbestos 1-5 part, polyimides 2-10 part, two alkali formula phosphorous acid
Lead 1-3 part, hindered phenol 1-2 part, modified rosin resin 1-3 part and other additives.
Further, a kind of wrapping paper adhesive, it includes host and auxiliary agent；Described host is according to following raw material
Parts by weight form: epoxy resin 15-25 part, organic siliconresin 25-35 part, silicone rubber 5-15 part, neoprene 25-45 part；
Described auxiliary agent according to following raw material parts by weight form: diaminodiphenyl-methane 1-3 part, ditridecyl phthalate 2-5 part,
Asbestos 1-5 part, polyimides 3-8 part, dibasic lead phosphite 1-3 part, hindered phenol 1-2 part, modified rosin resin 1-3 part and
Other additives.
Further, a kind of wrapping paper adhesive, it includes host and auxiliary agent；Described host is according to following raw material
Parts by weight composition: epoxy resin 20 parts, organic siliconresin 30 parts, 10 parts of silicone rubber, neoprene 40 parts；Described auxiliary agent is pressed
Parts by weight according to following raw material form: diaminodiphenyl-methane 2 parts, ditridecyl phthalate 3 parts, 3 parts of asbestos, polyamides are sub-
Amine 5 parts, dibasic lead phosphite 2 parts, hindered phenol 1 part, modified rosin resin 2 parts and other additives.
Especially, described epoxy resin, organic siliconresin, silicone rubber, the weight ratio of neoprene are 2-3:3-4:1-2:
3-4。
Particularly, other additives described are by coupling agent, initiator, accelerator, viscosifier, polymerization inhibitor, age resistor, network
One or more mixing compositions in mixture, emulsifying agent.
The method have the advantages that the wrapping paper adhesive of the present invention utilizes rubber and synthesis tree in sum
The interaction of fat greatly strengthens its cementability and toughness, improves the service life of wrapping paper.
Detailed description of the invention
Specific embodiment 1: a kind of wrapping paper adhesive, it includes host and auxiliary agent；Host is according to following raw material
Parts by weight form: epoxy resin 10 parts, organic siliconresin 20 parts, 5 parts of silicone rubber, neoprene 30 parts；Auxiliary agent is according to following
Raw material parts by weight composition: diaminodiphenyl-methane 1 part, ditridecyl phthalate 2 parts, 1 part of asbestos, polyimides 2 parts,
Dibasic lead phosphite 1 part, hindered phenol 1 part, modified rosin resin 1 part and other additives, wherein other additives be by
One or more mixing groups in coupling agent, initiator, accelerator, viscosifier, polymerization inhibitor, age resistor, chelating agent, emulsifying agent
Become.
Specific embodiment 2: a kind of wrapping paper adhesive, it includes host and auxiliary agent；Host is according to following raw material
Parts by weight form: epoxy resin 20 parts, organic siliconresin 30 parts, 10 parts of silicone rubber, neoprene 40 parts；Auxiliary agent is according to following
Raw material parts by weight composition: diaminodiphenyl-methane 2 parts, ditridecyl phthalate 3 parts, 3 parts of asbestos, polyimides 5 parts,
Dibasic lead phosphite 2 parts, hindered phenol 1 part, modified rosin resin 2 parts and other additives, wherein other additives be by
One or more mixing groups in coupling agent, initiator, accelerator, viscosifier, polymerization inhibitor, age resistor, chelating agent, emulsifying agent
Become.
Specific embodiment 3: a kind of wrapping paper adhesive, it includes host and auxiliary agent；Host is according to following raw material
Parts by weight form: epoxy resin 30 parts, organic siliconresin 40 parts, 20 parts of silicone rubber, neoprene 50 parts；Described auxiliary agent according to
The parts by weight composition of following raw material: diaminodiphenyl-methane 3 parts, ditridecyl phthalate 5 parts, 5 parts of asbestos, polyimides
10 parts, dibasic lead phosphite 3 parts, hindered phenol 2 parts, modified rosin resin 3 parts and other additives, wherein other additives
It is by one or more mixing in coupling agent, initiator, accelerator, viscosifier, polymerization inhibitor, age resistor, chelating agent, emulsifying agent
Composition.
Embodiment provided above is the better embodiment of the present invention, is only used for the convenient explanation present invention, not to this
Bright make any pro forma restriction, any art has usually intellectual, if without departing from the carried skill of the present invention
In the range of art feature, utilize the Equivalent embodiments that the done local of disclosed technology contents is changed or modified, and
Without departing from the technical characteristic content of the present invention, all still fall within the range of the technology of the present invention feature.
Claims (5)
1. a wrapping paper adhesive, it is characterised in that: it includes host and auxiliary agent；Described host is according to following raw material
Parts by weight form: epoxy resin 10-30 part, organic siliconresin 20-40 part, silicone rubber 5-20 part, neoprene 30-50 part；
Described auxiliary agent according to following raw material parts by weight form: diaminodiphenyl-methane 1-3 part, ditridecyl phthalate 2-5 part,
Asbestos 1-5 part, polyimides 2-10 part, dibasic lead phosphite 1-3 part, hindered phenol 1-2 part, modified rosin resin 1-3 part with
And other additives.
2. a wrapping paper adhesive, it is characterised in that: it includes host and auxiliary agent；Described host is according to following raw material
Parts by weight form: epoxy resin 15-25 part, organic siliconresin 25-35 part, silicone rubber 5-15 part, neoprene 25-45 part；
Described auxiliary agent according to following raw material parts by weight form: diaminodiphenyl-methane 1-3 part, ditridecyl phthalate 2-5 part,
Asbestos 1-5 part, polyimides 3-8 part, dibasic lead phosphite 1-3 part, hindered phenol 1-2 part, modified rosin resin 1-3 part and
Other additives.
3. a wrapping paper adhesive, it is characterised in that: it includes host and auxiliary agent；Described host is according to following raw material
Parts by weight form: epoxy resin 20 parts, organic siliconresin 30 parts, 10 parts of silicone rubber, neoprene 40 parts；Described auxiliary agent according to
The parts by weight composition of following raw material: diaminodiphenyl-methane 2 parts, ditridecyl phthalate 3 parts, 3 parts of asbestos, polyimides
5 parts, dibasic lead phosphite 2 parts, hindered phenol 1 part, modified rosin resin 2 parts and other additives.
4. according to a kind of wrapping paper adhesive described in claim 1 or 2 or 3, it is characterised in that: described epoxy resin, have
Machine silicones, silicone rubber, the weight ratio of neoprene are 2-3:3-4:1-2:3-4.
5. according to a kind of wrapping paper adhesive described in claim 1 or 2 or 3, it is characterised in that: other additives described are
By one or more the mixing groups in coupling agent, initiator, accelerator, viscosifier, polymerization inhibitor, age resistor, chelating agent, emulsifying agent
Become.