CN106042703B - A kind of polypropylene film offset plate and its manufacturing method - Google Patents

A kind of polypropylene film offset plate and its manufacturing method Download PDF

Info

Publication number
CN106042703B
CN106042703B CN201610329036.3A CN201610329036A CN106042703B CN 106042703 B CN106042703 B CN 106042703B CN 201610329036 A CN201610329036 A CN 201610329036A CN 106042703 B CN106042703 B CN 106042703B
Authority
CN
China
Prior art keywords
coating
polypropylene film
preparation
water
added
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201610329036.3A
Other languages
Chinese (zh)
Other versions
CN106042703A (en
Inventor
张翠琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YINGKOU SPECIAL PAPER INDUSTRY Co Ltd
Original Assignee
YINGKOU SPECIAL PAPER INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YINGKOU SPECIAL PAPER INDUSTRY Co Ltd filed Critical YINGKOU SPECIAL PAPER INDUSTRY Co Ltd
Priority to CN201610329036.3A priority Critical patent/CN106042703B/en
Publication of CN106042703A publication Critical patent/CN106042703A/en
Application granted granted Critical
Publication of CN106042703B publication Critical patent/CN106042703B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of polypropylene film offset plate and its manufacturing method, the present invention relates to offset plate paper and its manufacturing methods.By the preparation of water-soluble resin slurry, the preparation of coating color, the preparation of plate coating, coating process and cut with packaging etc. processes be process.The present invention substitutes wood pulp paper base version using polypropylene film, it can be saved timber resources, 5 times of printing or more can be improved again, utilize polypropylene film double spread, it can two-sided Plate making printing, hectograph utilization rate is improved, with water-soluble resin slurry solvent instead of organic solvent, pernicious gas is solved and human body is damaged and to environmental pollution problem.Polypropylene film offset plate preparation method is simple, low in cost, is a kind of ideal offset plate.

Description

A kind of polypropylene film offset plate and its manufacturing method
Technical field
The present invention relates to offset plate paper and its manufacturing methods, specifically using polypropylene film as base version, with water-soluble resin Slurry is the offset plate and its manufacturing method of solvent manufacture.
Background technique
For a long time, the zinc oxide offset plate paper both at home and abroad for gently printing all is to make version with paper base, using toluene, diformazan The raw materials such as benzene, first methyl esters, first butyl ester are configured to the adhesive of organic solvent type, then are configured to coating, coating system with zinc oxide etc. At millboard.This millboard, first is that solvent for use contains the composition that is harmful to the human body, the volatilization meeting pair of pernicious gas in production process Operator will cause the harm on body and the pollution to surrounding enviroment.Since these organic solvents are inflammable volatile, so Want especially careful in storage, transportational process.Second is that paper base version is manufactured by raw material of wood pulp, with the shortage of timber resources, Not only price is rising steadily, and also increases the consumption of timber resources.Third is that existing zinc oxide printing plate paper is all single side coating, user It is used only once and just throws away millboard, customer using cost is high.
Summary of the invention
For above situation, the object of the present invention is to provide a kind of polypropylene film offset plate and its manufacturing methods, with poly- Acrylic sheet is version base, and using water-soluble resin slurry as solvent, two-sided coating coating overcomes and asks existing for above-mentioned zinc oxide printing plate paper Topic.
The purpose of the present invention is what is be achieved through the following technical solutions.The system of preparation, coating color including resin slurry Standby, plate coating preparation, coating process, is cut and six parts of packaging the selection of polypropylene film.
The preparation of 1 resin slurry
1.1 technical formula
Polyvinyl alcohol (PVA-1799) 13-15kg
Purified water 160-170kg
1.2 preparation method
The purified water of formula ratio 85%-90% is added in container (or reaction kettle), starts to stir, heat simultaneously, make water Temperature rise is to 25-27 DEG C；Then the direct cloth of PVA is spread in vortex while stirring, is not allowed on PVA floats on the surface, because staying in table PVA may agglomerate and be not easy to disperse on face；The solid material being attached on stirring blade and chamber wall is washed down to continue to stir, it is sufficiently mixed It is bonded to and is homogenized；It is heated to 90-95 DEG C with steam again, 25-30min is at least stirred at this temperature, dissolves PVA sufficiently.Most Surplus purified water is added afterwards, is cooled to room temperature while stirring, it is spare.
The preparation of 2 coating colors
2.1 colorant formulas
Purified water 68kg
Ethyl alcohol 3.5-4.0kg
Pigment (methylenum careuleum or rose-red) 0.1-0.2kg
The preparation of 2.2 colorants
Purified water and ethyl alcohol are added in a reservoir, then pigment is put into alcohol water and is sufficiently stirred, is uniformly dispersed, storage 24 is small When more than, dissolve pigment sufficiently, it is spare.
The preparation of 3 plate coating
The formula of 3.1 coating
The preparation of 3.2 coating
According to formula, resin slurry is added in a kettle, stirring is heated up to 90-95 DEG C, mixing time 30-35min, Be added in colloid mill together with purified water, colorant after taking-up, then Jiang Gao ling soil, barium sulfate, calgon, precipitated calcium carbonate, Zinc oxide is added in colloid mill, and jitter time 2-3 hours.Defoaming agent is added portionwise in optic vesicle foam situation, then crosses 200 meshes, standby With.
The selection of 4 polypropylene films
It chooses with a thickness of 125-135g/m2, the polypropylene film coiled strip that width is 850-950mm, film is two-sided through hair side Process, to meet the technique requirement of coating coating.
5 coating process
Coating is using single coating head coating machine.The tow sides coated version coating on polypropylene film.Coating machine driving speed Degree control is 8-10 meter per second, and speed speed directly affects the quality of coating；Using 0.6 steel wire scraper, (0.6 is wound around for coating The steel wire diameter of scraper is 0.6 millimeter), the thickness of coating is controlled, coated coating dosage is every square metre of 7g-8g；Coating machine Drying uses bridge-type baking oven, and channel is 20 meters long, and drying temperature is 100 DEG C -105 DEG C, and the high polypropylene film of temperature is easy to split version, temperature Spend low easily dirty version.Make the water content 4.5-7% for being coated with hectograph, smoothness reaches 80s-120s；Specific gravity is 1.2-1.4.It is positive and negative The technique of two sides coating is just the same, guarantees that the coating weight of version is consistent.
6 cut and pack
Winding up roller after winding is cut out with hilted broadsword cut paper is disconnected, is cut into the vanning factory of various specifications model.
The beneficial effects of the present invention are first is that, instead of wood pulp paper base version, can be saved timber using polypropylene film Resource, and 5 times of printing or more can be improved；Second is that using polypropylene film double spread, can two-sided Plate making printing, improve hectograph benefit With rate；Third is that solving pernicious gas instead of organic solvent with water-soluble solvent and being damaged to human body and to environmental pollution problem. Polypropylene film offset plate preparation method is simple, low in cost, is a kind of ideal offset plate.
Detailed description of the invention
The present invention is without attached drawing.
Embodiment
The preparation of 1 resin slurry
Formula ratio 140kg purified water is added in a kettle, carries out agitation heating, water temperature is made to rise to 27 DEG C；Then side is stirred It mixes side to be directly spread in vortex 15kg PVA, mix to being homogenized；93 DEG C are heated to steam again, constant temperature stirs 30 minutes； Finally 25kg purified water is added, is cooled to room temperature while stirring, it is spare.
The preparation of 2 coating colors
68kg purified water and 3.5kg ethyl alcohol are added in a reservoir, then 0.1kg pigment (methylenum careuleum or rose-red) is put into alcohol It is dispersed with stirring in water uniformly, it is storage 24 hours or more, spare.
The preparation of 3 plate coating
160kg resin slurry is added in a kettle, stirring is heated up to 95 DEG C, and mixing time is 35 minutes, after taking-up with 120kg purified water, 70kg colorant are added in colloid mill together, then by 80kg Gao ling native (200 mesh of paste), 7.5kg barium sulfate, 1.32kg calgon, 10.5kg precipitated calcium carbonate, 4.5kg zinc oxide are added in colloid mill, and jitter time 2.5 hours.Divide 3 Then secondary addition defoaming agent 2550ml crosses 200 meshes, spare.
The selection of 4 polypropylene films
It chooses with a thickness of 125g/m2, the polypropylene film coiled strip that width is 850mm, film is two-sided through hair side process, To meet the technique requirement of coating coating.
5 coating process
Coating is using single coating head coating machine.The tow sides coated version coating on polypropylene film.Coating machine driving speed Degree control is 9 meter per seconds；Coating uses 0.6 steel wire scraper, and coating layer thickness is every square metre of 7g；The drying of coating machine uses bridge Formula baking oven, channel is 20 meters long, and drying temperature is 105 DEG C.Make the water content 4.5-5.5% for being coated with hectograph, smoothness reaches 90s-110s；Specific gravity is 1.2-1.3.The technique of tow sides coating is just the same.
6 cut and pack
Winding up roller after winding is cut out with hilted broadsword cut paper is disconnected, is cut into the vanning factory of various specifications model.

Claims (3)

  1. It 1. a kind of polypropylene film offset plate, is made of base version and plate coating, it is characterized in that using polypropylene film as base version, Base version is two-sided with using water-soluble resin slurry as the paint coatings of solvent；
    The formula of the plate coating are as follows:
    The formula of the resin slurry are as follows:
    Polyvinyl alcohol 13-15kg
    Purified water 160-170kg；
    The formula of the colorant are as follows:
    Purified water 68kg
    Ethyl alcohol 3.5-4.0kg
    Pigment 0.1-0.2kg.
  2. 2. polypropylene film offset plate as described in claim 1, the Gao ling soil is 200 mesh of paste, barium sulfate, lightweight carbonic acid Calcium is pure, the polyvinyl alcohol PVA-1799 of chemistry, and pigment is methylenum careuleum or rose-red.
  3. 3. a kind of polypropylene film offset plate manufacturing method of any of claims 1 or 2, it is characterized in that:
    (1) preparation of resin slurry
    1.1 technical formula
    Polyvinyl alcohol 13-15kg
    Purified water 160-170kg
    1.2 preparation method
    The purified water of formula ratio 85%-90% is added in a kettle, starts to stir, heat simultaneously, water temperature is made to rise to 25-27 ℃；Then PVA is directly spread in vortex while stirring, is fully mixed to and is homogenized；It is heated to 90-95 DEG C with steam again, 25-30min is stirred at a temperature of this, and finally surplus purified water is added, is cooled to room temperature while stirring, it is spare；
    (2) preparation of coating color
    2.1 colorant formulas
    Purified water 68kg
    Ethyl alcohol 3.5-4.0kg
    Pigment 0.1-0.2kg
    The preparation of 2.2 colorants
    Purified water and ethyl alcohol are added in a reservoir, then pigment is put into alcohol water and be sufficiently stirred, is uniformly dispersed, store 24 hours with On, it is spare；
    (3) preparation of plate coating
    The formula of 3.1 coating
    The preparation of 3.2 coating
    Be added resin slurry in a kettle, stirring is heated up to 90-95 DEG C, mixing time 30-35min, after taking-up with purification Water, colorant are added in colloid mill together, then glue is added in Gao ling soil, barium sulfate, calgon, precipitated calcium carbonate, zinc oxide In body mill, jitter time 2-3 hours, defoaming agent was added portionwise in optic vesicle foam situation, then crossed 200 meshes, spare；
    (4) selection of polypropylene film
    It selects with a thickness of 125-135g/m2, width be 850-950mm polypropylene film coiled strip, film it is two-sided through hair side technique at Reason；
    (5) coating process
    Using single coating head coating machine, the control of coating machine running speed is 8-10 meter per second, and coating is using winding scraper steel wire diameter For the steel wire scraper of 0.6mm, coated coating dosage is every square metre of 7g-8g；The drying of coating machine uses bridge-type baking oven, and channel is long 20 meters, drying temperature is 100 DEG C -105 DEG C, and the water content for being coated with hectograph is 4.5%-7%, and smoothness reaches 80s-120s；Than Weight is 1.2-1.4；The technique of tow sides coating is identical.
CN201610329036.3A 2016-05-13 2016-05-13 A kind of polypropylene film offset plate and its manufacturing method Expired - Fee Related CN106042703B (en)