CN105885238A - Flame retardant polypropylene plastic film - Google Patents
Flame retardant polypropylene plastic film Download PDFInfo
- Publication number
- CN105885238A CN105885238A CN201610491240.5A CN201610491240A CN105885238A CN 105885238 A CN105885238 A CN 105885238A CN 201610491240 A CN201610491240 A CN 201610491240A CN 105885238 A CN105885238 A CN 105885238A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- flame retardant
- flame
- plastic film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of plastic products and discloses a flame retardant polypropylene plastic film. The flame retardant polypropylene plastic film is composed of the following components in parts by weight: 55-65 parts of polypropylene resin, 10-25 parts of polypropylene, 5-8 parts of polypropylene glycol, 3-8 parts of methyl methacrylate, 4 parts of magnesium stearate, 5 parts of a propenyl thermoplastic elastomer, 3 parts of a dibutyl phthalate plasticizer, 3 parts of a corn fiber toughening agent and 4 parts of a zinc borate flame retardant. The flame retardant polypropylene plastic film is added with the inorganic zinc borate flame retardant, so that a thin film has good flame retardant property and also has the advantages of light plastic, stable chemical properties, high hardness and good impact resistance.
Description
Technical field
The present invention relates to a kind of plastic foil, particularly relate to a kind of flame-retardant polypropylene plastics film.
Background technology
At present, along with expanding economy, plastics are widely used in industry and life.Chinese Plastics film industry is in a flourish stage, it is reported, the demand of Chinese Plastics film every year by with more than 9% speed increment.And along with various new materials, new equipment and new technology are constantly emerged in large numbers, the plastic sheeting promoting China towards diversification of varieties, customizations and is possessed multi-functional composite membrane direction develops.Polypropylene as a big class of versatile material, the feature such as processing little with its proportion, easy, corrosion-resistant, nontoxic and high comprehensive performance and be used widely, all there is inflammable problem in present most polypropylene film.
Summary of the invention
It is an object of the invention to provide a kind of flame-retardant polypropylene plastics film, by inventing the formula of a kind of polypropylene plastic film and there is inflammable problem by adding fire retardant solution polypropylene plastic film.
For achieving the above object, the present invention adopts the following technical scheme that
A kind of flame-retardant polypropylene plastics film, this plastic foil is made up of following component in parts by weight: acrylic resin 55-65 part, polypropylene 10-25 part, POLYPROPYLENE GLYCOL 5-8 part, methyl methacrylate 3-8 part, magnesium stearate 4 parts, 5 parts of propylene-based thermoplastic's elastomer, 3 parts of plasticizer, toughener 3 parts, fire retardant 4 parts.
Further, described acrylic resin is low density polypropylene resin, weight average molecular weight 9000-12000 of acrylic resin.
Further, described plasticizer is dibutyl phthalate.
Further, described toughener is zein fiber.
Further, described fire retardant is Firebrake ZB.
Owing to using technique scheme, there is advantages that
The polypropylene plastic film of the present invention makes film have good fire resistance by the interpolation of inorganic combustion inhibitor Firebrake ZB, has plastics light weight, stable chemical performance simultaneously；Hardness high-impact can wait advantage well.
Detailed description of the invention
Embodiment one
A kind of flame-retardant polypropylene plastics film, this plastic foil is made up of following component in parts by weight: acrylic resin 55 parts, polypropylene 17 parts, POLYPROPYLENE GLYCOL 5 parts, methyl methacrylate 4 parts, magnesium stearate 4 parts, 5 parts of propylene-based thermoplastic's elastomer, 3 parts of plasticizer, toughener 3 parts, fire retardant 4 parts.
Further, described acrylic resin is low density polypropylene resin, weight average molecular weight 9000-12000 of acrylic resin.
Further, described plasticizer is dibutyl phthalate.
Further, described toughener is zein fiber.
Further, described fire retardant is Firebrake ZB.
Embodiment two
A kind of flame-retardant polypropylene plastics film, this plastic foil is made up of following component in parts by weight: acrylic resin 58 parts, polypropylene 12 parts, POLYPROPYLENE GLYCOL 6 parts, methyl methacrylate 5 parts, magnesium stearate 4 parts, 5 parts of propylene-based thermoplastic's elastomer, 3 parts of plasticizer, toughener 3 parts, fire retardant 4 parts.
Further, described acrylic resin is low density polypropylene resin, weight average molecular weight 9000-12000 of acrylic resin.
Further, described plasticizer is dibutyl phthalate.
Further, described toughener is zein fiber.
Further, described fire retardant is Firebrake ZB.
Embodiment three
A kind of flame-retardant polypropylene plastics film, this plastic foil is made up of following component in parts by weight: acrylic resin 60 parts, polypropylene 11 parts, POLYPROPYLENE GLYCOL 6 parts, methyl methacrylate 4 parts, magnesium stearate 4 parts, 5 parts of propylene-based thermoplastic's elastomer, 3 parts of plasticizer, toughener 3 parts, fire retardant 4 parts.
Further, described acrylic resin is low density polypropylene resin, weight average molecular weight 9000-12000 of acrylic resin.
Further, described plasticizer is dibutyl phthalate.
Further, described toughener is zein fiber.
Further, described fire retardant is Firebrake ZB.
The foregoing is only the better embodiment of the present invention; protection scope of the present invention is not limited with above-mentioned embodiment; in every case those of ordinary skill in the art modify or change according to the equivalence that disclosed content is made, and all should include in the protection domain described in claims.
Claims (5)
1. a flame-retardant polypropylene plastics film, this plastic foil is made up of following component in parts by weight: acrylic resin 55-65 part, polypropylene 10-25 part, POLYPROPYLENE GLYCOL 5-8 part, methyl methacrylate 3-8 part, magnesium stearate 4 parts, 5 parts of propylene-based thermoplastic's elastomer, 3 parts of plasticizer, toughener 3 parts, fire retardant 4 parts.
A kind of flame-retardant polypropylene plastics film the most according to claim 1, it is characterised in that: described acrylic resin is low density polypropylene resin, weight average molecular weight 9000-12000 of acrylic resin.
A kind of flame-retardant polypropylene plastics film the most according to claim 1, it is characterised in that: described plasticizer is dibutyl phthalate.
A kind of flame-retardant polypropylene plastics film the most according to claim 1, it is characterised in that: described toughener is zein fiber.
A kind of flame-retardant polypropylene plastics film the most according to claim 1, it is characterised in that: described fire retardant is Firebrake ZB.