CN105819778A - 一种轻质、隔热、环保型复合墙体建筑材料制备方法 - Google Patents
一种轻质、隔热、环保型复合墙体建筑材料制备方法 Download PDFInfo
- Publication number
- CN105819778A CN105819778A CN201610148661.8A CN201610148661A CN105819778A CN 105819778 A CN105819778 A CN 105819778A CN 201610148661 A CN201610148661 A CN 201610148661A CN 105819778 A CN105819778 A CN 105819778A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- particles
- magnesium
- building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种轻质、隔热、环保型复合墙体建筑材料制备方法,该建筑涂料组分包括纤维素,碳纤维颗粒,橡胶颗粒,植物颗粒,低密度聚乙烯树脂,有机硅改性环氧树脂,碳酸钙,氧化镁,硅酸镁,碳酸镁钙,硼酸钙,纳米氧化硅,轻质陶瓷,EVA可再分散胶粉等。本发明提供的建筑墙体涂料,其具有抗折强度和抗压强度高的特点,且具有保温、隔音的功效,其导热系数低、节能效果好,并且具有良好的防水效果;制得的墙体材料材质轻便,成本低廉,而且绿色环保,大大节约了能源的消耗,以及生产成本,可以广泛地用于建筑施工中。
Description
技术领域
本发明涉及一种建筑用材料配方及其制备方法,具体涉及一种轻质、隔热、环保型复合墙体建筑材料制备方法。
背景技术
随着各国工业化进程的发展,地球上可供人类利用的化石燃料已日渐枯竭,世界性能源危机的出路只有两条,开发新能源的同时注意节约能源。建筑能耗在人类整个能源消耗中所占比例甚高,故建筑节能是解决我国能源问题的根本途径,而建筑节能最直接有效的方法是使用保温隔热材料。在建筑上合理采用保温隔热材料,可以减少建筑材料的用量,提高建筑施工的工业化程度,大幅度节能降耗。原来在建筑中使用的保温隔热材料,主要是基于改善居住舒适程度,如今已转移到节能上面。使用建筑保温隔热材料对缓解能源危机以及提高人民的居住水平具有重要意义。
新型的建筑材料包括的范围很广,有保温材料、隔热材料、高强度材料、会呼吸的材料等都属于新型材料。建筑材料是土木工程和建筑工程中使用的材料的统称。
建筑材料可分为结构材料、装饰材料和某些专用材料。结构材料包括木材、竹材、石材、水泥、混凝土、金属、砖瓦、陶瓷、玻璃、工程塑料、复合材料等;装饰材料包括各种涂料、油漆、镀层、贴面、各色瓷砖、具有特殊效果的玻璃等;专用材料指用于防水、防潮、防腐、防火、阻燃、隔音、隔热、保温、密封等。
目前,建筑领域所使用的粘土类和以水泥为胶凝剂的墙体建筑材料,尽管它有着强度高、耐久性好等优点,但其容重大,隔音、隔热性能差,使其应用范围受到限制。同时存在着高耗资源和燃料、工艺复杂、极易对环境造成污染。制成的建筑材料质地较松散,强度不够,且有的原料存量很少,受地域条件的限制,不适合大规模生产。
发明内容
发明目的:本发明针对现有技术中的不足,提出一种具有抗折强度和抗压强度高的特点,且具有保温、隔音的功效,其导热系数低、节能效果好,并且具有良好的防水效果;制得的墙体材料材质轻便,成本低廉,而且绿色环保,大大节约了能源的消耗,以及生产成本,可以广泛地用于建筑施工中的轻质、隔热、环保型复合墙体建筑材料制备方法。
技术方案:本发明所述的一种轻质、隔热、环保型复合墙体建筑材料,包括如下质量份的组分组成:
纤维素5-10份,碳纤维颗粒10-15份,橡胶颗粒20-25份,植物颗粒20-30份,低密度聚乙烯树脂15-40份,有机硅改性环氧树脂5-8份,碳酸钙5-15份,氧化镁0.5-2份,硅酸镁0.6-0.8份,碳酸镁钙10-15份,硼酸钙5-8份,纳米氧化硅5-10份,轻质陶瓷5-10份,EVA可再分散胶粉1.5-1.7份,浮石15-35份,泥炭土3-5份,水泥20-55份,生石灰8-12份,长石粉5-10份,粉煤灰35-45份,聚-4-甲基-1-戊烯7-12份,聚苯乙烯磺酸5-9份,丁基橡胶7-11份,热稳定剂1-3份,防水剂0.3-0.8份,增韧剂1-3份,发泡剂0.1-1份,交联剂0.1-0.5份,硅烷基憎水剂0.2-0.3份、润湿剂2.3-2.5份、添加剂1-2份。
进一步的,所述植物颗粒为麦秸或玉米秸等植物组织粉碎后粒径在10-30mm的颗粒。
进一步的,所述纤维素为甲基纤维素、羟丙基甲基纤维素、羟乙基纤维素按照1-3:1-2:1-2组成的混合物。
进一步的,所述湿润剂为琥珀酸二辛脂磺酸钠与烷基磺酸钠其重量比为1:15。
进一步的,所述添加剂是乙烯-乙酸乙烯酯共聚乳液与碳酸钙按照2-3:1-2组成的混合物。
进一步的,所述热稳定剂为硬脂酸锌。
进一步的,所述防水剂为无机铝盐。
进一步的,所述增韧剂为乙丙橡胶,发泡剂为碳黑,交联剂为过氧化二异丙苯。
本发明还公开了一种轻质、隔热、环保型复合墙体建筑材料的制备方法,包括如下步骤:
(1)按照原料配比取浮石、泥炭土、水泥、生石灰、长石粉、粉煤灰、轻质陶瓷、硅酸镁在混料机中进行充分混合,粉碎制成均匀的混合料A;
(2)按照原料配比取纤维素、碳纤维颗粒、橡胶颗粒、植物颗粒、低密度聚乙烯树脂、有机硅改性环氧树脂、碳酸钙、氧化镁、碳酸镁钙、硼酸钙、纳米氧化硅在混料机中进行充分混合均匀,制得混合料B;
(3)将上述混合料A和混合料B进行充分混合,并放置24-48小时;
(4)在泡料池中加入所要制取建筑材料重量的40-60%的水,再通入蒸气加热13-15h,控制水温50-75℃,将上述步骤(3)的混合料加入,搅拌均匀得到混合液A;
(5)按照原料配比取EVA可再分散胶粉、聚-4-甲基-1-戊烯、聚苯乙烯磺酸、丁基橡胶、热稳定剂、防水剂、增韧剂、发泡剂、交联剂、硅烷基憎水剂、润湿剂混合,加剩下重量的水,在搅拌机中混合均匀,制成均匀的混合液B;
(6)将混合液A和B混合均匀,将蒸气通入加热,使液体温度达到85-90℃,加入添加剂,不得有悬浮杂质,达到清彻透明为止;
(7)将所得混合物再加压进行成型,加压压力为16MPa-24MPa,加压时间为5-8h,冷却后放置6-18h,得到复合墙体建筑材料。
有益效果:本发明提供的建筑墙体涂料,其具有抗折强度和抗压强度高的特点,且具有保温、隔音的功效,其导热系数低、节能效果好,并且具有良好的防水效果;制得的墙体材料材质轻便,成本低廉,而且绿色环保,大大节约了能源的消耗,以及生产成本,可以广泛地用于建筑施工中。
具体实施方式
下面结合具体实施例对本发明作进一步说明:
实施例1
一种轻质、隔热、环保型复合墙体建筑材料,包括如下质量份的组分组成:
纤维素5份,碳纤维颗粒10份,橡胶颗粒20份,植物颗粒20份,低密度聚乙烯树脂15份,有机硅改性环氧树脂5份,碳酸钙5份,氧化镁0.5份,硅酸镁0.6份,碳酸镁钙10份,硼酸钙5份,纳米氧化硅5份,轻质陶瓷5份,EVA可再分散胶粉1.5份,浮石15份,泥炭土3份,水泥20份,生石灰8份,长石粉5份,粉煤灰35份,聚-4-甲基-1-戊烯7份,聚苯乙烯磺酸5份,丁基橡胶7份,热稳定剂1份,防水剂0.3份,增韧剂1份,发泡剂0.1份,交联剂0.1份,硅烷基憎水剂0.2份、润湿剂2.3份、添加剂1份。
进一步的,所述植物颗粒为麦秸或玉米秸等植物组织粉碎后粒径在10-30mm的颗粒。
进一步的,所述纤维素为甲基纤维素、羟丙基甲基纤维素、羟乙基纤维素按照1:1:1组成的混合物。
进一步的,所述湿润剂为琥珀酸二辛脂磺酸钠与烷基磺酸钠其重量比为1:15。
进一步的,所述添加剂是乙烯-乙酸乙烯酯共聚乳液与碳酸钙按照2:1组成的混合物。
进一步的,所述热稳定剂为硬脂酸锌。
进一步的,所述防水剂为无机铝盐。
进一步的,所述增韧剂为乙丙橡胶,发泡剂为碳黑,交联剂为过氧化二异丙苯。
本发明还公开了一种轻质、隔热、环保型复合墙体建筑材料的制备方法,包括如下步骤:
(1)按照原料配比取浮石、泥炭土、水泥、生石灰、长石粉、粉煤灰、轻质陶瓷、硅酸镁在混料机中进行充分混合,粉碎制成均匀的混合料A;
(2)按照原料配比取纤维素、碳纤维颗粒、橡胶颗粒、植物颗粒、低密度聚乙烯树脂、有机硅改性环氧树脂、碳酸钙、氧化镁、碳酸镁钙、硼酸钙、纳米氧化硅在混料机中进行充分混合均匀,制得混合料B;
(3)将上述混合料A和混合料B进行充分混合,并放置24小时;
(4)在泡料池中加入所要制取建筑材料重量的40%的水,再通入蒸气加热13-15h,控制水温50℃,将上述步骤(3)的混合料加入,搅拌均匀得到混合液A;
(5)按照原料配比取EVA可再分散胶粉、聚-4-甲基-1-戊烯、聚苯乙烯磺酸、丁基橡胶、热稳定剂、防水剂、增韧剂、发泡剂、交联剂、硅烷基憎水剂、润湿剂混合,加剩下60%重量的水,在搅拌机中混合均匀,制成均匀的混合液B;
(6)将混合液A和B混合均匀,将蒸气通入加热,使液体温度达到85℃,加入添加剂,不得有悬浮杂质,达到清彻透明为止;
(7)将所得混合物再加压进行成型,加压压力为16MPa,加压时间为5h,冷却后放置6h,得到复合墙体建筑材料。
实施例2
一种轻质、隔热、环保型复合墙体建筑材料,包括如下质量份的组分组成:
纤维素10份,碳纤维颗粒15份,橡胶颗粒25份,植物颗粒30份,低密度聚乙烯树脂40份,有机硅改性环氧树脂8份,碳酸钙15份,氧化镁2份,硅酸镁0.8份,碳酸镁钙15份,硼酸钙8份,纳米氧化硅10份,轻质陶瓷10份,EVA可再分散胶粉1.7份,浮石35份,泥炭土5份,水泥55份,生石灰12份,长石粉10份,粉煤灰45份,聚-4-甲基-1-戊烯12份,聚苯乙烯磺酸9份,丁基橡胶11份,热稳定剂3份,防水剂0.8份,增韧剂3份,发泡剂1份,交联剂0.5份,硅烷基憎水剂0.3份、润湿剂2.5份、添加剂2份。
进一步的,所述植物颗粒为麦秸或玉米秸等植物组织粉碎后粒径在10-30mm的颗粒。
进一步的,所述纤维素为甲基纤维素、羟丙基甲基纤维素、羟乙基纤维素按照3:2:2组成的混合物。
进一步的,所述湿润剂为琥珀酸二辛脂磺酸钠与烷基磺酸钠其重量比为1:15。
进一步的,所述添加剂是乙烯-乙酸乙烯酯共聚乳液与碳酸钙按照3:2组成的混合物。
进一步的,所述热稳定剂为硬脂酸锌。
进一步的,所述防水剂为无机铝盐。
进一步的,所述增韧剂为乙丙橡胶,发泡剂为碳黑,交联剂为过氧化二异丙苯。
本发明还公开了一种轻质、隔热、环保型复合墙体建筑材料的制备方法,包括如下步骤:
(1)按照原料配比取浮石、泥炭土、水泥、生石灰、长石粉、粉煤灰、轻质陶瓷、硅酸镁在混料机中进行充分混合,粉碎制成均匀的混合料A;
(2)按照原料配比取纤维素、碳纤维颗粒、橡胶颗粒、植物颗粒、低密度聚乙烯树脂、有机硅改性环氧树脂、碳酸钙、氧化镁、碳酸镁钙、硼酸钙、纳米氧化硅在混料机中进行充分混合均匀,制得混合料B;
(3)将上述混合料A和混合料B进行充分混合,并放置24-48小时;
(4)在泡料池中加入所要制取建筑材料重量的60%的水,再通入蒸气加热15h,控制水温75℃,将上述步骤(3)的混合料加入,搅拌均匀得到混合液A;
(5)按照原料配比取EVA可再分散胶粉、聚-4-甲基-1-戊烯、聚苯乙烯磺酸、丁基橡胶、热稳定剂、防水剂、增韧剂、发泡剂、交联剂、硅烷基憎水剂、润湿剂混合,加剩下重量的水,在搅拌机中混合均匀,制成均匀的混合液B;
(6)将混合液A和B混合均匀,将蒸气通入加热,使液体温度达到90℃,加入添加剂,不得有悬浮杂质,达到清彻透明为止;
(7)将所得混合物再加压进行成型,加压压力为24MPa,加压时间为8h,冷却后放置18h,得到复合墙体建筑材料。
实施例3
一种轻质、隔热、环保型复合墙体建筑材料,包括如下质量份的组分组成:
纤维素7份,碳纤维颗粒12份,橡胶颗粒22份,植物颗粒25份,低密度聚乙烯树脂30份,有机硅改性环氧树脂6份,碳酸钙10份,氧化镁1份,硅酸镁0.7份,碳酸镁钙12份,硼酸钙6份,纳米氧化硅7份,轻质陶瓷7份,EVA可再分散胶粉1.6份,浮石25份,泥炭土4份,水泥35份,生石灰10份,长石粉7份,粉煤灰40份,聚-4-甲基-1-戊烯9份,聚苯乙烯磺酸7份,丁基橡胶9份,热稳定剂2份,防水剂0.5份,增韧剂2份,发泡剂0.5份,交联剂0.3份,硅烷基憎水剂0.25份、润湿剂2.4份、添加剂1.5份。
进一步的,所述植物颗粒为麦秸或玉米秸等植物组织粉碎后粒径在10-30mm的颗粒。
进一步的,所述纤维素为甲基纤维素、羟丙基甲基纤维素、羟乙基纤维素按照2:1:1组成的混合物。
进一步的,所述湿润剂为琥珀酸二辛脂磺酸钠与烷基磺酸钠其重量比为1:15。
进一步的,所述添加剂是乙烯-乙酸乙烯酯共聚乳液与碳酸钙按照2:1组成的混合物。
进一步的,所述热稳定剂为硬脂酸锌。
进一步的,所述防水剂为无机铝盐。
进一步的,所述增韧剂为乙丙橡胶,发泡剂为碳黑,交联剂为过氧化二异丙苯。
本发明还公开了一种轻质、隔热、环保型复合墙体建筑材料的制备方法,包括如下步骤:
(1)按照原料配比取浮石、泥炭土、水泥、生石灰、长石粉、粉煤灰、轻质陶瓷、硅酸镁在混料机中进行充分混合,粉碎制成均匀的混合料A;
(2)按照原料配比取纤维素、碳纤维颗粒、橡胶颗粒、植物颗粒、低密度聚乙烯树脂、有机硅改性环氧树脂、碳酸钙、氧化镁、碳酸镁钙、硼酸钙、纳米氧化硅在混料机中进行充分混合均匀,制得混合料B;
(3)将上述混合料A和混合料B进行充分混合,并放置36小时;
(4)在泡料池中加入所要制取建筑材料重量的50%的水,再通入蒸气加热13-15h,控制水温65℃,将上述步骤(3)的混合料加入,搅拌均匀得到混合液A;
(5)按照原料配比取EVA可再分散胶粉、聚-4-甲基-1-戊烯、聚苯乙烯磺酸、丁基橡胶、热稳定剂、防水剂、增韧剂、发泡剂、交联剂、硅烷基憎水剂、润湿剂混合,加剩下重量的水,在搅拌机中混合均匀,制成均匀的混合液B;
(6)将混合液A和B混合均匀,将蒸气通入加热,使液体温度达到87℃,加入添加剂,不得有悬浮杂质,达到清彻透明为止;
(7)将所得混合物再加压进行成型,加压压力为20MPa,加压时间为6.5h,冷却后放置12h,得到复合墙体建筑材料。
本发明提供的建筑墙体涂料,其具有抗折强度和抗压强度高的特点,且具有保温、隔音的功效,其导热系数低、节能效果好,并且具有良好的防水效果;制得的墙体材料材质轻便,成本低廉,而且绿色环保,大大节约了能源的消耗,以及生产成本,可以广泛地用于建筑施工中。
以上所述,仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,虽然本发明已以较佳实施例揭露如上,然而并非用以限定本发明,任何熟悉本专业的技术人员,在不脱离本发明技术方案范围内,当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例,但凡是未脱离本发明技术方案的内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (1)
1.一种轻质、隔热、环保型复合墙体建筑材料制备方法,其特征在于:包括如下步骤:
(1)按照原料配比取浮石、泥炭土、水泥、生石灰、长石粉、粉煤灰、轻质陶瓷、硅酸镁在混料机中进行充分混合,粉碎制成均匀的混合料A;
(2)按照原料配比取纤维素、碳纤维颗粒、橡胶颗粒、植物颗粒、低密度聚乙烯树脂、有机硅改性环氧树脂、碳酸钙、氧化镁、碳酸镁钙、硼酸钙、纳米氧化硅在混料机中进行充分混合均匀,制得混合料B;
(3)将上述混合料A和混合料B进行充分混合,并放置24-48小时;
(4)在泡料池中加入所要制取建筑材料重量的40-60%的水,再通入蒸气加热13-15h,控制水温50-75℃,将上述步骤(3)的混合料加入,搅拌均匀得到混合液A;
(5)按照原料配比取EVA可再分散胶粉、聚-4-甲基-1-戊烯、聚苯乙烯磺酸、丁基橡胶、热稳定剂、防水剂、增韧剂、发泡剂、交联剂、硅烷基憎水剂、润湿剂混合,加剩下重量的水,在搅拌机中混合均匀,制成均匀的混合液B;
(6)将混合液A和B混合均匀,将蒸气通入加热,使液体温度达到85-90℃,加入添加剂,不得有悬浮杂质,达到清彻透明为止;
(7)将所得混合物再加压进行成型,加压压力为16MPa-24MPa,加压时间为5-8h,冷却后放置6-18h,得到复合墙体建筑材料。