CN105666620A - Anticorrosive method of willow for top grade furniture - Google Patents
Anticorrosive method of willow for top grade furniture Download PDFInfo
- Publication number
- CN105666620A CN105666620A CN201610100064.8A CN201610100064A CN105666620A CN 105666620 A CN105666620 A CN 105666620A CN 201610100064 A CN201610100064 A CN 201610100064A CN 105666620 A CN105666620 A CN 105666620A
- Authority
- CN
- China
- Prior art keywords
- willow
- parts
- grade furniture
- sanitas
- corrosion method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosive method of willow for top grade furniture. The anticorrosive method of willow for top grade furniture successively comprises the following steps: after air-drying the willow, putting the willow in distilled water to be soaked for 1-2 days; then performing drying treatment on the willow and drying the willow till the moisture content of the willow is 12-15%; injecting a preservative into the willow under a vacuum high-pressure condition; then performing high-temperature qualitative treatment on the willow for 3-5 hours after the preservative is added; and finally, after air-drying the willow subjected to high-temperature qualitative treatment, processing the willow to willow plates for top grade furniture. The kill ratio on worm eggs such as caterpillars, aphids, red spider mites, trialeurodes vaporariorum, noctuids and ladybirds by the method is above 95%, and the method can be further used for preventing and treating various domestic viruses with the effective rate above 85%. Moreover, the method further has the functions of removing peculiar smells such as peculiar smell of formaldehyde, is anticorrosive and waterproof, is quite environmentally friendly, is suitable for anticorrosive, mildewproof and insect-preventing applications of a willow material in various environments, and is low in cost and high in practicality.
Description
Technical field:
The present invention relates to the anti-corrosion method of a kind of high-grade furniture willow.
Background technology:
Timber is a kind of organic materials, has obvious biological nature, easily by biological attack such as bacterium, worm, the raw boring in sea worms,
So the life-time service of timber particularly long-term outdoor use be very restricted. Corrupt biology can cause rotting of timber so that it is is damaged. Before use, according to different applied environments, select suitable sanitas, carry out appropriate process, then can effectively delay foxy. Timber is carried out rotproofing, extends the working life of timber, be one of important channel saving timber, the protection forest reserves. The wood preservative mainly CCA sanitas that current countries in the world use, such sanitas, owing to having toxicity containing the material such as arsenic, chromium, is unfavorable for environment protection, uses in some countries strict limitation.
In addition, timber is also one of important raw and processed materials of nation-building and people's daily living article, is widely used in the manufacture of building and ornament materials and furniture, owing to timber is organic materials, not corrosion-resistant, if for a long time in open air use, timber can rot and be damaged because of what its corrupt biology caused.
The timber that nowadays China use after rotproofing is little, and mostly uses traditional anti-corrosion method that the mankind and environmental hazard are big. Especially at high-grade this block of furniture technology of willow, it is badly in need of a kind of practicality of research, it is easy to the anti-corrosion method of the willow of operation.
Summary of the invention:
For overcoming above-mentioned deficiency, it is an object of the present invention to provide the anti-corrosion method of a kind of high-grade furniture willow, have efficient, the insect protected of wide spectrum, sterilization effect, anticorrosion, waterproof, effectively removes the peculiar smell such as formaldehyde.
The solution of the present invention is as follows: the anti-corrosion method of a kind of high-grade furniture willow, and step is as follows:
(1) put into distilled water after willow is air-dry and soak 1-2 days;
(2) then willow being dried process, oven dry to water ratio is 12-15%;
(3) in willow, following weight part sanitas is injected when vacuum high-pressure: propylene glycol 2-4 part, chitin 30-48, chlorine oxygen hexichol amidine hydrochloride 1-2.3 part, chlorxylone 10-25 part, alkyl dimethyl benzyl ammonium chloride 1-4 part, Potassium Bromide 1-3 part, passive nano negative ion powder 35-46 part, fatty alcohol Ethoxylate 108-116 part;
(4) again the willow after adding sanitas is carried out high temperature qualitative process 3-5 hour;
(5) willow after qualitative for high temperature process is carried out air-dry process post-treatment and becomes high-grade furniture willow plate.
Further, described weight part sanitas is: propylene glycol 3.5 parts, chitin 40 parts, chlorine oxygen hexichol amidine hydrochloride 2 parts, chlorxylone 20 parts, alkyl dimethyl benzyl ammonium chloride 3 parts, Potassium Bromide 2 parts, passive nano negative ion powder 40 parts, fatty alcohol Ethoxylate 110 parts.
Further, described sanitas also comprises the nitrate of 1:0.3-0.7 and the raw material of vitriol.
Further, the temperature of described drying treatment is 70-75 DEG C.
Further, the temperature of the qualitative process of described high temperature is 50-60 DEG C.
The rate of killing of the worm's ovums such as caterpillar, aphid, red spider, trialeurodes vaporariorum, noctuid, ladybug is reached more than 95% by the present invention; also can be used for preventing and treating domestic various viruses; efficiency is had to reach more than 85%; and there is the effect removing the peculiar smell such as formaldehyde; anticorrosion, waterproof, very environmental protection, the anticorrosive mildewproof insect protected application of the willow material being applicable under various environment; and it is with low cost, practical.
Embodiment:
Below in conjunction with embodiment, the present invention will be further described.
Embodiment 1
An anti-corrosion method for high-grade furniture willow, step is as follows:
(1) put into distilled water after willow is air-dry and soak 1-2 days;
(2) then willow being dried process, oven dry to water ratio is 12%;
(3) in willow, following weight part sanitas is injected when vacuum high-pressure: propylene glycol 2 parts, chitin 30, chlorine oxygen hexichol amidine hydrochloride 1 part, chlorxylone 10 parts, alkyl dimethyl benzyl ammonium chloride 1 part, Potassium Bromide 1 part, passive nano negative ion powder 35 parts, fatty alcohol Ethoxylate 108 parts;
(4) again the willow after adding sanitas is carried out the qualitative process of high temperature 3 hours;
(5) willow after qualitative for high temperature process is carried out air-dry process post-treatment and becomes high-grade furniture willow plate.
Embodiment 2
An anti-corrosion method for high-grade furniture willow, step is as follows:
(1) put into distilled water after willow is air-dry and soak 1-2 days;
(2) then willow being dried process, oven dry to water ratio is 15%;
(3) in willow, following weight part sanitas is injected when vacuum high-pressure: propylene glycol 4 parts, chitin 48, chlorine oxygen hexichol amidine hydrochloride 2.3 parts, chlorxylone 25 parts, alkyl dimethyl benzyl ammonium chloride 4 parts, Potassium Bromide 3 parts, passive nano negative ion powder 46 parts, fatty alcohol Ethoxylate 116 parts;
(4) again the willow after adding sanitas is carried out the qualitative process of high temperature 5 hours;
(5) willow after qualitative for high temperature process is carried out air-dry process post-treatment and becomes high-grade furniture willow plate.
Embodiment 3
An anti-corrosion method for high-grade furniture willow, step is as follows:
(1) put into distilled water after willow is air-dry and soak 1-2 days;
(2) then willow being dried process, oven dry to water ratio is 14%;
(3) in willow, following weight part sanitas is injected when vacuum high-pressure: propylene glycol 3.5 parts, chitin 40 parts, chlorine oxygen hexichol amidine hydrochloride 2 parts, chlorxylone 20 parts, alkyl dimethyl benzyl ammonium chloride 3 parts, Potassium Bromide 2 parts, passive nano negative ion powder 40 parts, fatty alcohol Ethoxylate 110 parts;
(4) again the willow after adding sanitas is carried out the qualitative process of high temperature 4 hours;
(5) willow after qualitative for high temperature process is carried out air-dry process post-treatment and becomes high-grade furniture willow plate.
Embodiment 4
An anti-corrosion method for high-grade furniture willow, step is as follows:
(1) put into distilled water after willow is air-dry and soak 1-2 days;
(2) then willow being dried process, oven dry to water ratio is 14%;
(3) in willow, following weight part sanitas is injected when vacuum high-pressure: propylene glycol 3.5 parts, chitin 40 parts, chlorine oxygen hexichol amidine hydrochloride 2 parts, chlorxylone 20 parts, alkyl dimethyl benzyl ammonium chloride 3 parts, Potassium Bromide 2 parts, passive nano negative ion powder 40 parts, fatty alcohol Ethoxylate 110 parts; Described sanitas also comprises the raw material of 1 part of nitrate and 0.6 part of vitriol;
(4) again the willow after adding sanitas is carried out the qualitative process of high temperature 4 hours;
(5) willow after qualitative for high temperature process is carried out air-dry process post-treatment and becomes high-grade furniture willow plate.
Describe in detail and explanation although above the specific embodiment of the present invention being given; but what should indicate is; above-mentioned enforcement mode can be carried out various equivalence according to the conception of the present invention and change and amendment by us; its function produced do not exceed that specification sheets contains yet spiritual time, all should within protection scope of the present invention.
Claims (5)
1. the anti-corrosion method of a high-grade furniture willow, it is characterised in that, step is as follows:
(1) put into distilled water after willow is air-dry and soak 1-2 days;
(2) then willow being dried process, oven dry to water ratio is 12-15%;
(3) in willow, following weight part sanitas is injected when vacuum high-pressure: propylene glycol 2-4 part, chitin 30-48, chlorine oxygen hexichol amidine hydrochloride 1-2.3 part, chlorxylone 10-25 part, alkyl dimethyl benzyl ammonium chloride 1-4 part, Potassium Bromide 1-3 part, passive nano negative ion powder 35-46 part, fatty alcohol Ethoxylate 108-116 part;
(4) again the willow after adding sanitas is carried out high temperature qualitative process 3-5 hour;
(5) willow after qualitative for high temperature process is carried out air-dry process post-treatment and becomes high-grade furniture willow plate.
2. the anti-corrosion method of a kind of high-grade furniture willow according to claim 1, it is characterized in that, described weight part sanitas is: propylene glycol 3.5 parts, chitin 40 parts, chlorine oxygen hexichol amidine hydrochloride 2 parts, chlorxylone 20 parts, alkyl dimethyl benzyl ammonium chloride 3 parts, Potassium Bromide 2 parts, passive nano negative ion powder 40 parts, fatty alcohol Ethoxylate 110 parts.
3. the anti-corrosion method of a kind of high-grade furniture willow according to claim 1 and 2, it is characterised in that, described sanitas also comprises the nitrate of 1:0.3-0.7 and the raw material of vitriol.
4. the anti-corrosion method of a kind of high-grade furniture willow according to claim 1 and 2, it is characterised in that, the temperature of described drying treatment is 70-75 DEG C.
5. the anti-corrosion method of a kind of high-grade furniture willow according to claim 1 and 2, it is characterised in that, the temperature of the qualitative process of described high temperature is 50-60 DEG C.