CN105585763A - UHMWPE plastic alloy - Google Patents
UHMWPE plastic alloy Download PDFInfo
- Publication number
- CN105585763A CN105585763A CN201610178918.4A CN201610178918A CN105585763A CN 105585763 A CN105585763 A CN 105585763A CN 201610178918 A CN201610178918 A CN 201610178918A CN 105585763 A CN105585763 A CN 105585763A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic alloy
- uhmwpe
- uhmwpe plastic
- wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses UHMWPE plastic alloy. UHMWPE, HDPET, PE wax, PET, SBS, PS, PTW, PVA, SEP, lead stearate and a heat stabilizer are weighed according to the weight part matching, the UHMWPE plastic alloy is high in flame retardation and has the effect of self-extinguishing within 1-4 s after ignition, and the bending strength is 30-50 MPa; the UHMWPE plastic alloy is resistant to high temperature, and the Vika softening point is 90 DEG C-110 DEG C; the UHMWPE plastic alloy is high in strength, the notch impact strength is 10-30 kJ/m<2>, the tensile strength is 40-60 MPa, and the elongation at break is 105-125%.
Description
Technical field
The application belongs to plastic alloy material field, relates in particular to a kind of UHMWPE plastic alloy.
Background technology
UHMWPE (ultra-high molecular weight polyethylene) is that a kind of molecule has the comprehensive of linear structureThe thermoplastic engineering plastic of the excellent energy of energy, molecular weight is up to more than 1,500,000. Density is little, hasWell wearability, self lubricity, impact resistance, corrosion resistance etc.
The high molecular weight (molecular weight of HDPE only has 2～300,000 conventionally) of UHMWPE is givenThe serviceability that it is excellent, and belong to thermoplastic engineering plastic moderate, function admirable,It has almost concentrated the advantage of various plastics, and having common polythene and other engineering plastics can notWear-resisting, shock-resistant, the self-lubricating of analogy, corrosion-resistant, impact-absorbing energy, low temperature resistant, healthNontoxic, be difficult for adhering to, be difficult for water suction, the combination property such as density is less. In fact, at present alsoDo not have a kind of simple macromolecular material to have so numerous excellent properties concurrently.
Because UHMWPE has towards the architectural feature of stretch orientation indispensability, so have without a rivalUltra-Drawing intensity, therefore can make modulus of ultra high elasticity and intensity by gel spinningFiber, its hot strength is up to 3～3.5GPa, and tensile modulus of elasticity is up to 100～125GPa;Fiber specific strength is the highest in commercial all fibres so far, large 4 times than carbon fiber,Than steel wire large 10 times, than aramid fiber large 50%.
Textile machine is the field that UHMWPE applies the earliest, as far back as 1958, just has several the father-in-lawDepartment manufactures textile machinery part with UHMWPE, as replaced the most durable buffalo hide in toughness materialLeather block on the loom of making, bears 40～180 times/min Long-term Vibration and impacts, its life-spanCan reach 5～6 times of buffalo leather block. At present, the UHMWPE zero abroad applying on every loomPart on average has 30 left and right, as the device of throwing a spear, picking stick, gear, hookup, sweep line rod,The shock-resistant wearing parts such as buffer stopper, rod sleeve, oscillating back rest.
Summary of the invention
The technical problem solving:
The application, for above-mentioned technical problem, provides a kind of UHMWPE plastic alloy, solves existingThere are the technical problems such as plastic alloy cost is high, temperature resistance is poor, intensity is low.
Technical scheme:
A kind of UHMWPE plastic alloy, the raw materials by weight portion of described UHMWPE plastic alloyProportioning is as follows: UHMWPE100 part; HDPE2-8 part; PE wax 5-25 part; PET0.2-0.8Part; SBS5-25 part; PS30-50 part; PTW20-40 part; PVA10-30 part; SEP15-35Part; Lead stearate is 1.5-3.5 part; Heat stabilizer 5-25 part.
As a preferred technical solution of the present invention: the raw material of described UHMWPE plastic alloyProportioning is as follows by weight: UHMWPE100 part; HDPE3 part; 10 parts, PE wax; PET0.4Part; SBS10 part; PS35 part; PTW25 part; PVA15 part; SEP20 part; Lead stearateIt is 2 parts; 10 parts of heat stabilizers.
As a preferred technical solution of the present invention: the raw material of described UHMWPE plastic alloyProportioning is as follows by weight: UHMWPE100 part; HDPE7 part; 20 parts, PE wax; PET0.6Part; SBS20 part; PS45 part; PTW35 part; PVA25 part; SEP30 part; Lead stearateIt is 3 parts; 20 parts of heat stabilizers.
As a preferred technical solution of the present invention: the raw material of described UHMWPE plastic alloyProportioning is as follows by weight: UHMWPE100 part; HDPE5 part; 15 parts, PE wax; PET0.5Part; SBS15 part; PS40 part; PTW30 part; PVA20 part; SEP25 part; Lead stearateIt is 2.5 parts; 15 parts of heat stabilizers.
As a preferred technical solution of the present invention: described heat stabilizer adopts three alkali formula sulfuric acidLead or dibasic lead phosphite.
Beneficial effect:
A kind of UHMWPE plastic alloy of the present invention adopts above technical scheme and prior artCompare, there is following technique effect: 1, product fire resistance excellence, in igniting 1-4s, certainly put out,Bending strength 30-50MPa; 2, product is high temperature resistant, Vicat softening point 90-110 DEG C; 3, produceProduct intensity is high, notched Izod impact strength 10-30kJ/m2, hot strength 40-60MPa; 4, fracturePercentage elongation 105-125%, with low cost, simple to operate, corrosion-resistant, can widespread production alsoConstantly replace current material.
Detailed description of the invention
Embodiment 1:
Take UHMWPE100 part according to parts by weight proportioning; HDPE2 part; 5 parts, PE wax;PET0.2 part; SBS5 part; PS30 part; PTW20 part; PVA10 part; SEP15 part; StearicLead plumbate is 1.5 parts; 5 parts of dibasic lead phosphites.
Raw material is dropped into mixer and mix, be warming up to 70 DEG C, mixing velocity is 50r/min, mixedClose 6h.
Mix rear input double screw extruder, 200 DEG C, 205 DEG C, 210 DEG C of barrel temperatures,215 DEG C, 220 DEG C, 220 DEG C of extruder temperatures, 210 DEG C, 215 DEG C, 220 DEG C of head temperatures,230 DEG C, 240 DEG C, screw speed 14r/min, rotating speed 25r/min feeds intake.
Product fire resistance excellence, puts out bending strength 30MPa certainly in igniting 4s; Product is resistance toHigh temperature, 90 DEG C of Vicat softening points; Product strength is high, notched Izod impact strength 10kJ/m2, stretchIntensity 40MPa; Elongation at break 105%.
Embodiment 2:
Take UHMWPE100 part according to parts by weight proportioning; HDPE8 part; 25 parts, PE wax;PET0.8 part; SBS25 part; PS50 part; PTW40 part; PVA30 part; SEP35 part; FirmlyResin acid lead is 3.5 parts; 25 parts of dibasic lead phosphites.
Raw material is dropped into mixer and mix, be warming up to 90 DEG C, mixing velocity is 90r/min, mixedClose 10h.
Mix rear input double screw extruder, 210 DEG C, 215 DEG C, 220 DEG C of barrel temperatures,225 DEG C, 230 DEG C, 230 DEG C of extruder temperatures, 220 DEG C, 225 DEG C, 230 DEG C of head temperatures,240 DEG C, 250 DEG C, screw speed 20r/min, rotating speed 45r/min feeds intake.
Product fire resistance excellence, puts out bending strength 50MPa certainly in igniting 1s; Product is resistance toHigh temperature, 90 DEG C of Vicat softening points; Product strength is high, notched Izod impact strength 30kJ/m2, stretchIntensity 40MPa; Elongation at break 125%.
Embodiment 3:
Take UHMWPE100 part according to parts by weight proportioning; HDPE3 part; 10 parts, PE wax;PET0.4 part; SBS10 part; PS35 part; PTW25 part; PVA15 part; SEP20 part; FirmlyResin acid lead is 2 parts; 10 parts of dibasic lead phosphites.
Raw material is dropped into mixer and mix, be warming up to 70 DEG C, mixing velocity is 50r/min, mixedClose 6h.
Mix rear input double screw extruder, 200 DEG C, 205 DEG C, 210 DEG C of barrel temperatures,215 DEG C, 220 DEG C, 220 DEG C of extruder temperatures, 210 DEG C, 215 DEG C, 220 DEG C of head temperatures,230 DEG C, 240 DEG C, screw speed 14r/min, rotating speed 25r/min feeds intake.
Product fire resistance excellence, puts out bending strength 30MPa certainly in igniting 1s; Product is resistance toHigh temperature, 110 DEG C of Vicat softening points; Product strength is high, notched Izod impact strength 30kJ/m2, drawStretch intensity 40MPa; Elongation at break 125%.
Embodiment 4:
Take UHMWPE100 part according to parts by weight proportioning; HDPE7 part; 20 parts, PE wax;PET0.6 part; SBS20 part; PS45 part; PTW35 part; PVA25 part; SEP30 part; FirmlyResin acid lead is 3 parts; 20 parts of tribasic lead sulfates.
Raw material is dropped into mixer and mix, be warming up to 90 DEG C, mixing velocity is 90r/min, mixedClose 10h.
Mix rear input double screw extruder, 210 DEG C, 215 DEG C, 220 DEG C of barrel temperatures,225 DEG C, 230 DEG C, 230 DEG C of extruder temperatures, 220 DEG C, 225 DEG C, 230 DEG C of head temperatures,240 DEG C, 250 DEG C, screw speed 20r/min, rotating speed 45r/min feeds intake.
Product fire resistance excellence, puts out bending strength 50MPa certainly in igniting 4s; Product is resistance toHigh temperature, 110 DEG C of Vicat softening points; Product strength is high, notched Izod impact strength 10kJ/m2, drawStretch intensity 40MPa; Elongation at break 125%.
Embodiment 5:
Take UHMWPE100 part according to parts by weight proportioning; HDPE5 part; 15 parts, PE wax;PET0.5 part; SBS15 part; PS40 part; PTW30 part; PVA20 part; SEP25 part; FirmlyResin acid lead is 2.5 parts; 15 parts of tribasic lead sulfates.
Raw material is dropped into mixer and mix, be warming up to 80 DEG C, mixing velocity is 70r/min, mixedClose 8h.
Mix rear input double screw extruder, 205 DEG C, 210 DEG C, 215 DEG C of barrel temperatures,220 DEG C, 225 DEG C, 225 DEG C of extruder temperatures, 215 DEG C, 220 DEG C, 225 DEG C of head temperatures,235 DEG C, 245 DEG C, screw speed 17r/min, rotating speed 35r/min feeds intake.
Product fire resistance excellence, puts out bending strength 50MPa certainly in igniting 1s; Product is resistance toHigh temperature, 110 DEG C of Vicat softening points; Product strength is high, notched Izod impact strength 30kJ/m2, drawStretch intensity 60MPa; Elongation at break 125%.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, instead of restriction, because ofThis any change in implication and the scope suitable with claims of the present invention, all shouldThink to be included in the scope of claims.
Claims (5)
1. a UHMWPE plastic alloy, is characterized in that described UHMWPE plastic alloyRaw materials by weight portion proportioning is as follows: UHMWPE100 part; HDPE2-8 part; PE wax 5-25Part; PET0.2-0.8 part; SBS5-25 part; PS30-50 part; PTW20-40 part; PVA10-30Part; SEP15-35 part; Lead stearate is 1.5-3.5 part; Heat stabilizer 5-25 part.
2. a kind of UHMWPE plastic alloy according to claim 1, is characterized in that instituteState UHMWPE plastic alloy raw materials by weight portion proportioning as follows: UHMWPE100 part; HDPE3Part; 10 parts, PE wax; PET0.4 part; SBS10 part; PS35 part; PTW25 part; PVA15Part; SEP20 part; Lead stearate is 2 parts; 10 parts of heat stabilizers.
3. a kind of UHMWPE plastic alloy according to claim 1, is characterized in that instituteThe raw materials by weight portion proportioning of stating UHMWPE plastic alloy is as follows: UHMWPE100 part; HDPE7Part; 20 parts, PE wax; PET0.6 part; SBS20 part; PS45 part; PTW35 part; PVA25Part; SEP30 part; Lead stearate is 3 parts; 20 parts of heat stabilizers.
4. a kind of UHMWPE plastic alloy according to claim 1, is characterized in that instituteThe raw materials by weight portion proportioning of stating UHMWPE plastic alloy is as follows: UHMWPE100 part; HDPE5Part; 15 parts, PE wax; PET0.5 part; SBS15 part; PS40 part; PTW30 part; PVA20Part; SEP25 part; Lead stearate is 2.5 parts; 15 parts of heat stabilizers.
5. a kind of UHMWPE plastic alloy according to claim 1, is characterized in that:Described heat stabilizer adopts tribasic lead sulfate or dibasic lead phosphite.