CN105565699A - Construction glue - Google Patents
Construction glue Download PDFInfo
- Publication number
- CN105565699A CN105565699A CN201510980983.4A CN201510980983A CN105565699A CN 105565699 A CN105565699 A CN 105565699A CN 201510980983 A CN201510980983 A CN 201510980983A CN 105565699 A CN105565699 A CN 105565699A
- Authority
- CN
- China
- Prior art keywords
- jin
- polyethylene
- construction
- gluewater
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Construction glue comprises the following raw materials by weight: 10-15 kg of polyethylene, 10-15 kg of polypropylene resin, 0.75-1.25 kg of polyacrylamide, 0.05-0.1 kg of tributyl phosphate and 90-110kg of water. A preparation method comprises the following steps: (1), the 10-15 kg of polyethylene are placed in a steam heating reaction vessel, 90-110kg of water at room temperature are added, steam is introduced for heating and stirring to dissolve the polyethylene, the process takes about 24 hours; (2), after the polyethylene is thoroughly dissolved, the solution is poured into another container, while stirring, 10-15 kg of the polypropylene resin, 0.75-1.25 kg of the polyacrylamide and 0.05-0.1 kg of the tributyl phosphate are added, stirred evenly, and cooled to room temperature; and (3), the construction glue is packed in barrels for sale. The construction glue is excellent in waterproof property, reliable in quality, good in stability, easy in production method, and strong in operability and is applicable to water proofing and other engineers in the construction field.
Description
Technical field
The present invention relates to building material field, furthermore, relate to a kind of gluewater in use for construction.
Background technology
Building field gluewater in use for construction usage quantity is very large, such as subway station, mine, tunnel, elevator raise, vault, kitchen, toilet, bathroom, swimming pool, the sanitary sewage pond etc. such as concrete works, brick wall, indoor and outdoor waterproofing work all will use gluewater in use for construction, and after these engineerings use for some time, along with the possibility of leaking, also need regularly to use gluewater in use for construction to repair or to increase waterproof strength.The gluewater in use for construction of prior art, although production technique is simple, low price, effect is often unsatisfactory, there is hidden danger, and especially some important engineering dare not use.
Above-mentioned existing gluewater in use for construction, obviously has defect and exists, and need to be improved.Improving of the above-mentioned defect of thoughts of the present invention is that spy concentrates on studies and coordinates repetition test, finally proposes a kind of reasonable in design and effectively improve the invention of above-mentioned defect.
For solving the defect technical barrier of the gluewater in use for construction of prior art, propose a kind of gluewater in use for construction.Through retrieval, there is no relevant report.
Summary of the invention
The object of the invention is to the defect overcoming prior art, provide and produce simple, practical, effective a kind of gluewater in use for construction, to improve existing building glue performance, make easy construction, fast, greatly improve construction reliability.
A kind of gluewater in use for construction of the present invention, it is made up of the raw material of following weight proportioning, and the weight quota of often kind of raw material is respectively: polyethylene 20 ~ 30 jin, poly-third resin 20 ~ 30 jin, poly-propionic acid amide 1.5 ~ 2.5 jin, tbp 0.1 ~ 0.2 jin, 180 ~ 220 jin, water.
The preparation method of said a kind of gluewater in use for construction, comprises the following steps:
(1), be first put in steam heating reactor by polyethylene 20 ~ 30 jin, add 180 ~ 220 jin of normal-temperature water, rush steam heating and stir, polyethylene is dissolved, this process about needs 24 hours;
(2), after polyethylene thoroughly dissolves, solution is poured in another container, stir, add poly-third resin 20 ~ 30 jin, poly-propionic acid amide 1.5 ~ 2.5 jin and tbp 0.1 ~ 0.2 jin simultaneously, stir, be cooled to normal temperature;
(3), barrelling is for sale.
A kind of gluewater in use for construction water-repellancy of the present invention is excellent, reliable in quality, good stability, and its production method is convenient, and operability is very strong.
The present invention is applicable to the waterproofing work of building field and builds the application such as recovery project.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment:
One, gluewater in use for construction of the present invention is produced:
Be made up of the raw material of following weight proportioning, the weight quota of often kind of raw material is respectively: polyethylene 25 jin, poly-third resin 25 jin, poly-propionic acid amide 2 jin, tbp 0.1 jin, 200 jin, water.
The preparation method of said a kind of gluewater in use for construction, comprises the following steps:
(1), be first put in steam heating reactor by polyethylene 25 jin, add 200 jin of normal-temperature water, rush steam heating and stir, polyethylene is dissolved, this process about needs 24 hours;
(2), after polyethylene thoroughly dissolves, solution is poured in another container, stir, add poly-third resin 25 jin, poly-propionic acid amide 2 jin and tbp 0.1 jin simultaneously, stir, be cooled to normal temperature; (3), barrelling is for sale.
Two, apply:
1, gluewater in use for construction of the present invention and cement weight share 1:2 ratio are stirred, the waterproof that needs of this concrete rubber cement material being smeared or being brushed in buildings leaks position, continues 2 ~ 3 times, treats that this is site curing stiff.
2, by glue of the present invention and cement by weight 1; 1 stirs, and repeatedly brushes 3 to 4 times at cement pavement breakage, and road surface can be made firm, wear-resisting, anti-skidding.
Have employed the inventive method, easy construction, fast reliably, the waterproof good stability of buildings, construction period is short, substantially can not affect the normal use of buildings.
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, anyly do not depart from technical solution of the present invention content, the any simple modification done above embodiment according to technical spirit of the present invention, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (2)
1. a gluewater in use for construction, it is made up of the raw material of following weight proportioning, and the weight quota of often kind of raw material is respectively: polyethylene 20 ~ 30 jin, poly-third resin 20 ~ 30 jin, poly-propionic acid amide 1.5 ~ 2.5 jin, tbp 0.1 ~ 0.2 jin, 180 ~ 220 jin, water.
2. a preparation method for gluewater in use for construction, comprises the following steps:
(1), be first put in steam heating reactor by polyethylene 20 ~ 30 jin, add 180 ~ 220 jin of normal-temperature water, rush steam heating and stir, polyethylene is dissolved, this process about needs 24 hours;
(2), after polyethylene thoroughly dissolves, solution is poured in another container, stir, add poly-third resin 20 ~ 30 jin, poly-propionic acid amide 1.5 ~ 2.5 jin and tbp 0.1 ~ 0.2 jin simultaneously, stir, be cooled to normal temperature;
(3), barrelling is for sale.