CN105500842B - Low radiation coated glass - Google Patents
Low radiation coated glass Download PDFInfo
- Publication number
- CN105500842B CN105500842B CN201511018717.XA CN201511018717A CN105500842B CN 105500842 B CN105500842 B CN 105500842B CN 201511018717 A CN201511018717 A CN 201511018717A CN 105500842 B CN105500842 B CN 105500842B
- Authority
- CN
- China
- Prior art keywords
- glass
- film layer
- base
- film
- low radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of low radiation coated glass, including glass-base, and the outer surface of glass-base is sequentially provided with chromium film layer, sound insulation film, Al-Doped ZnO film layer, graphite coating from inside to outside；Film layers are equipped between glass-base and the chromium film layer and between Al-Doped ZnO film layer and graphite coating.The sound insulation film that the present invention is set both had improved the soundproof effect of glass, and excellent adhesion property is carried again；The graphite film plating layer of setting, adds the hardness of glass, while preventing from scratching, and with lubrication and cushioning effect, is conducive to extending the service life of glass.
Description
Technical field
The present invention relates to a kind of coated glass, and in particular to a kind of low radiation coated glass.
Background technology
Coated glass (Reflective glass) is also referred to as reflecting glass, is in one or more layers gold of glass surface coating
Category, alloy or metal compound film, to change the optical property of glass, meet certain particular requirement.Coated glass presses product
Different qualities, following a few classes can be divided into：Heat-reflecting glass, low emissivity glass (Low-E), electropane etc..Low emissivity glass
Glass be glass surface plate by the metal such as multilayer silver, copper or tin or its compound group into film system, product have to visible ray compared with
High transmissivity, there is very high reflectivity to infrared ray, with good heat-proof quality, is mainly used in building and automobile, ship
Deng the vehicles, because film strength is poor, double glazing is typically all made and uses.Low radiation coated glass of the prior art
Chinese utility model patent such as Publication No. CN103029379A discloses a kind of double-sided coating low emissivity glass, and it includes glass
Glass matrix, the both sides of the glass basis are respectively provided with Low emissivity thermal insulation layer, and the Low emissivity thermal insulation layer is Al-Doped ZnO film layer,
Using the high isolation infrared band thermal radiation capability of aluminum zinc oxide film layer, the heat-proof quality of glass is improved.But such scheme has
There is following deficiency：One, aluminum zinc oxide film layer hardness is low wears no resistance, and is easily scratched and weares and teares, and its corrosion resistance
It can need to be improved, so as to shorten glass service life；Second, double-sided coating layer, hardly possible is combined closely with glass body, film plating layer
Easily come off from glass body so that glass loses film plating layer performance, influence service life；Thirdly, its be not provided with sound insulation
Layer, glass sound insulation value is poor, and the scope of application of glass is subject to certain restrictions；Its other translucency is also to be reinforced.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of low spoke that wear-resistant, sound-insulating and heat-insulating effect is good, brightness is good
Penetrate coated glass.
In order to solve the above technical problems, the technical solution adopted by the present invention is as follows：
Low radiation coated glass, including glass-base, the outer surface of glass-base be sequentially provided with from inside to outside chromium film layer, every
Sound film, Al-Doped ZnO film layer, graphite coating；Between glass-base and the chromium film layer and Al-Doped ZnO film
Film layers are equipped between layer and graphite coating.
Such scheme is preferred, and in order to take into account soundproof effect and translucency and production cost, the sound insulation film is
Bright sound insulation film, its thickness is 0.30~1.55mm.
Such scheme is preferred, in order to further improve the wearability, corrosion resistance, oxidative resistance of each film layer, the stone
Black coating upper surface is additionally provided with tin oxide film layer.
Such scheme is preferred, and the thickness of the tin oxide film layer is 5~20nm.
Such scheme is preferred, in order to take into account hardness, shock-absorbing capacity and the translucency of glass, the thickness of graphite coating
For 5~10nm.
Such scheme is preferred, and in order to improve the intensity of glass, the glass-base is safety glass.
Compared with prior art, the sound insulation film that the present invention is set both had improved the soundproof effect of glass, and that improves again is viscous
Connect performance；The graphite film plating layer of setting, adds the hardness of glass, while preventing from scratching, and with lubrication and cushioning effect, has
Beneficial to the service life of extension glass；Chromium film layer, the brightness of raising are set；The film layers of setting, improve knot between film plating layer
Compactness is closed, prevents film plating layer from coming off, so as to ensure that glass properties, is conducive to extending the service life of glass；The oxygen of setting
Change wearability, inoxidizability and corrosion resistance that tin film layer further improves film layer.
Brief description of the drawings
Fig. 1 is a kind of structural representation of low radiation coated glass of the invention.
In figure marked as：1st, glass-base；2nd, chromium film layer；3rd, sound insulation film；4th, Al-Doped ZnO film layer；5th, graphite is plated
Layer；6th, tin oxide film layer.
Embodiment
The present invention is a kind of low radiation coated glass, as shown in figure 1, including glass-base 1, the outer surface of glass-base 1
Chromium film layer 2, sound insulation film 3, Al-Doped ZnO film layer 4, graphite coating 5 are sequentially provided with from inside to outside.
The glass-base 1 can be simple glass, ultra-clear glasses, safety glass etc., in the preferred embodiment, be
Increase its intensity, the glass-base 1 is safety glass.Film layers are provided between glass-base 1 and chromium film layer 2, to increase
Strong cementability between glass-base 1 and chromium film layer 2, it is to avoid fall off problem after long-time use.The Al-Doped ZnO
Film layers also are provided between film layer 4 and graphite coating 5, between same enhancing Al-Doped ZnO film layer 4 and graphite coating 5
Cementability, it is to avoid the generation for the problem that comes off.
The sound insulation film 3 is transparent sound proof film, had both improved the soundproof effect of glass, excellent adhesion property is carried again,
Its thickness is 0.30~1.55mm, most preferably 0.80mm.
The upper surface of graphite coating 5 is additionally provided with tin oxide film layer 6, to improve the wearability of film layer, inoxidizability and anti-
Corrosivity.The thickness of tin oxide film layer 6 is 5~20nm, most preferably 10nm.
The graphite coating 5 adds the hardness of glass, while preventing from scratching, and with lubrication and cushioning effect, it is thick
Spend for 5~10nm.
Certainly, simply the preferred embodiments of the disclosure is described in detail above, this hair is not limited with this
Bright practical range, the equivalence changes that all principles under this invention, construction and structure are made all should be covered by the guarantor of the present invention
In the range of shield.
Claims (3)
1. low radiation coated glass, it is characterised in that：Including glass-base (1), the outer surface of glass-base (1) from inside to outside according to
It is secondary to be provided with chromium film layer (2), sound insulation film (3), Al-Doped ZnO film layer (4), graphite coating (5)；The glass-base (1) and
Film layers are equipped between chromium film layer (2) and between Al-Doped ZnO film layer (4) and graphite coating (5)；The acoustic mastic
Piece (3) is transparent sound proof film, and its thickness is 0.30~1.55mm；Graphite coating (5) upper surface is additionally provided with tin oxide film
Layer (6)；The thickness of the tin oxide film layer (6) is 5~20nm.
2. low radiation coated glass according to claim 1, it is characterised in that：The thickness of graphite coating (5) be 5~
10nm。
3. low radiation coated glass according to claim 1, it is characterised in that：The glass-base (1) is safety glass.