CN105349917A - Oil slinger for wire rod mill - Google Patents

Oil slinger for wire rod mill Download PDF

Info

Publication number
CN105349917A
CN105349917A CN201510983465.8A CN201510983465A CN105349917A CN 105349917 A CN105349917 A CN 105349917A CN 201510983465 A CN201510983465 A CN 201510983465A CN 105349917 A CN105349917 A CN 105349917A
Authority
CN
China
Prior art keywords
speed
alloy material
wire rod
room temperature
min again
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510983465.8A
Other languages
Chinese (zh)
Inventor
单坤林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Original Assignee
CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd filed Critical CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Priority to CN201510983465.8A priority Critical patent/CN105349917A/en
Publication of CN105349917A publication Critical patent/CN105349917A/en
Pending legal-status Critical Current

Abstract

The invention discloses an oil slinger for a wire rod mill. The oil slinger comprises a main metal body made of an alloy material subjected to heat treatment, wherein the alloy material comprises components as follows: 1%-2% of As, 0.5% of Si, 0.7% of Te, 0.7% of Ge, 0.4% of Pd, 0.6% of W and the balance of Fe and inevitable impurities; the alloy material is subjected to heat treatment through steps as follows: 1), the temperature is increased to 680 DEG C at a speed of 25 DEG C/min, and the heat is preserved for 2.5 h; 2), the temperature is decreased to the room temperature at a speed of 30 DEG C/min; 3), the temperature is increased to 780 DEG C at a speed of 15 DEG C/min, and the heat is preserved for 3 h; 4), the temperature is decreased to the room temperature at a speed of 25 DEG C/min. The main metal body of the oil slinger for the wire rod mill has good performance, and the service time is long.

Description

Wire rod mill oil thrower
Technical field
The present invention relates to wire rod mill oil thrower.
Background technology
The work under bad environment of wire rod mill oil thrower, to its metal master performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of wire rod mill oil thrower, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of wire rod mill oil thrower of design, and comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1～2%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, wire rod mill oil thrower, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, wire rod mill oil thrower, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Advantage of the present invention and beneficial effect are: provide a kind of wire rod mill oil thrower, its metal master is made by through heat treated alloy material, metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of wire rod mill oil thrower, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1～2%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 2
Wire rod mill oil thrower, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 3
Wire rod mill oil thrower, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (3)

1. wire rod mill oil thrower, is characterized in that, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1～2%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
2. wire rod mill oil thrower according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
3. wire rod mill oil thrower according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%，
Si:0.5%，
Te:0.7%，
Ge:0.7%，
Pd:0.4%，
W:0.6%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 680 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 780 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
CN201510983465.8A 2015-12-24 2015-12-24 Oil slinger for wire rod mill Pending CN105349917A (en)