CN104440008A - Side-milling cutter manufacturing method - Google Patents

Abstract

The invention discloses a side-milling cutter manufacturing method. The side-milling cutter manufacturing method comprises the following steps that (1) cylindrical grinding, heat treatment, acid pickling and groove rolling are conducted on coarse steel; (2) 1.3 weight parts of diethanol amine, 2.6 weight parts of polyethylene glycol and 0.9 weight part of oleamide are put in 9.8 weight parts of deionized water, stirring and mixing are fully conducted, 0.8 weight part of polyvinyl butyral resin and 1.2 weight parts of sorbitan monooleate are sequentially added into the mixture, uniform stirring is fully conducted, and a grinding and cutting working solution is obtained; (3) grinding and cutting are conducted on a milling cutter blank, wherein the grinding and cutting working solution is used in the grinding and cutting process; (4) heat treatment and surface treatment are conducted. The side-milling cutter manufacturing method has the advantages that a manufactured milling cutter has high surface quality, is sharp, and can be used for fine machining, and the milling cutter is high in dimensional accuracy, good in stability and high in product percent of pass.

Description

The preparation method of face and side cutter

Technical field

The present invention relates to the preparation method of face and side cutter.

Background technology

The preparation method of existing face and side cutter, its milling cutter prepared, dimensional accuracy, stability, surface quality all have much room for improvement, and affect product percent of pass.

Summary of the invention

The object of the present invention is to provide a kind of preparation method of face and side cutter, its milling cutter prepared has high surface quality, and milling cutter is sharp, can be used for fine finishining, and milling cutter dimensional accuracy is high, and good stability, product percent of pass is high.

For achieving the above object, technical scheme of the present invention designs a kind of preparation method of face and side cutter, comprises the steps:

1) coarse fodder steel is carried out peripheral milling, heat treatment, pickling, rolling groove;

2) in 9.8 mass parts deionized waters, 1.3 mass parts diethanol amine, 2.6 mass parts polyethylene glycol, 0.9 mass parts oleamide is dropped into, be uniformly mixed fully, add 0.8 mass parts polyvinyl butyral resin, 1.2 mass parts sorbitol monooleates more successively, stir, obtain grinding cutting working solution;

3) grinding cutting is carried out to milling cutter blank, in grinding cutting process, use above-mentioned grinding cutting working solution;

4) heat treatment, surface treatment.

Advantage of the present invention and beneficial effect are: the preparation method providing a kind of face and side cutter, and its milling cutter prepared has high surface quality, and milling cutter is sharp, can be used for fine finishining, and milling cutter dimensional accuracy is high, and good stability, product percent of pass is high.

Detailed description of the invention

Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.

The technical scheme that the present invention specifically implements is:

A preparation method for face and side cutter, comprises the steps:

1) coarse fodder steel is carried out peripheral milling, heat treatment, pickling, rolling groove;

2) in 9.8 mass parts deionized waters, 1.3 mass parts diethanol amine, 2.6 mass parts polyethylene glycol, 0.9 mass parts oleamide is dropped into, be uniformly mixed fully, add 0.8 mass parts polyvinyl butyral resin, 1.2 mass parts sorbitol monooleates more successively, stir, obtain grinding cutting working solution;

3) grinding cutting is carried out to milling cutter blank, in grinding cutting process, use above-mentioned grinding cutting working solution;

4) heat treatment, surface treatment.

The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (1)

1. the preparation method of face and side cutter, is characterized in that, comprises the steps:

1) coarse fodder steel is carried out peripheral milling, heat treatment, pickling, rolling groove;

2) in 9.8 mass parts deionized waters, 1.3 mass parts diethanol amine, 2.6 mass parts polyethylene glycol, 0.9 mass parts oleamide is dropped into, be uniformly mixed fully, add 0.8 mass parts polyvinyl butyral resin, 1.2 mass parts sorbitol monooleates more successively, stir, obtain grinding cutting working solution;

3) grinding cutting is carried out to milling cutter blank, in grinding cutting process, use above-mentioned grinding cutting working solution;

4) heat treatment, surface treatment.