CN104433001A - Production process of woven type mushroom heat hook and loop fastener - Google Patents
Production process of woven type mushroom heat hook and loop fastener Download PDFInfo
- Publication number
- CN104433001A CN104433001A CN201410649156.2A CN201410649156A CN104433001A CN 104433001 A CN104433001 A CN 104433001A CN 201410649156 A CN201410649156 A CN 201410649156A CN 104433001 A CN104433001 A CN 104433001A
- Authority
- CN
- China
- Prior art keywords
- magic tape
- production technology
- woven type
- monofilament
- mushroom head
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production process of a woven type mushroom heat hook and loop fastener. The production process comprises the steps of weaving, cutting, washing, sizing treatment, moisture regaining and thermal forming. A cut monofilament can be firmly erected on a base surface of a hook belt through the sizing treatment step, so that the situation that the head of the monofilament is beaten down in the forming process, and then the appearance and performance of the monofilament are affected is avoided.
Description
[technical field]
The present invention relates to magic tape technology, particularly relate to a kind of production technology keeping mushroom head magic tape to hook body erectility.
[background technology]
Magic tape is also VELCRO, is that one way of life commonly uses coupling, is applied in a lot of occasion such as clothing, umbrella, knapsack.Magic tape generally comprises hook face and hair side two parts, and both draw generation viscosity by mutual hook, only has and two sides is firmly torn and could be separated, can reuse.Mushroom head magic tape is the magic tape type that a class hooks that body is mushroom-shaped.Because its structure is not yielding relative to thread hook, so have stronger stretching resistance, fasten peel strength good.China's application 200810181025.0 discloses a kind of Novel Velcro tape and special equipment thereof, its special equipment makes the hot formation mushroom shaped of monofilament head by heating wire, in actual production process, it is first cut off aftershaping by looped pile to form that mushroom head hooks body, easily lodge because looped pile cuts off rear monofilament, so can not ensure that each hook body head can form mushroom head, both affect outward appearance like this, affect function again.
Therefore, be necessary that the production technology improving magic tape is to solve the problem.
[summary of the invention]
The object of the invention is to, a kind of production technology keeping mushroom head magic tape to hook body erectility is provided.
For achieving the above object, following technical scheme provided by the present invention: a kind of production technology of woven type mushroom head magic tape, its step comprises:
1. weave: filling, veil, weft yarn are coiled integral respectively and loads loom, weave the hook band with O type looped pile;
2. cut off: being disconnected by O type looped pile becomes two monofilament erect;
3. wash: clean hooking band in containing the hot water of degreasing agent, then whole boiling hot;
4. gluing: use polyurethane resin gluing to fix each monofilament root, dry;
5. get damp again: the hook band after gluing is placed in 8-24 hour under room temperature environment;
6. thermoforming: be mushroom-head shape by monofilament head melt molding.
Concrete, the usage ratio of described weaving step yarn is filling 28-35%, veil 57-50%, weft yarn 15%.
Concrete, the usage ratio of described weaving step yarn is filling 28-35%, veil 57-50%, weft yarn 15%.
Concrete, described filling adopts the one in 300D/36F Polyester Yarns or 140D ~ 200D/24F polyamide staple fibre spun yarn.
Concrete, described weft yarn adopts the one in 150D/36F Polyester Yarns or 140D ~ 200D/24F polyamide staple fibre spun yarn.
Concrete, described veil adopts the PP line of wire diameter 0.15 ~ 0.3mm.
Concrete, described water-washing step condition is water temperature 60-80 DEG C, and scavenging period is 20-30min.
Concrete, described degreasing agent consumption is 15%.
Concrete, described in described cut-out step, O type looped pile is blown by 250-280 DEG C of high temperature.
Concrete, described thermoforming step fusion temperature is 200-250 DEG C.
Compared to existing technology, the beneficial effect of production technology of the present invention is:
1, the monofilament after being cut off by gluing order can be stood on the basal plane of hook band securely, can not affect its outward appearance and performance when making monofilament head shaping like this because of lodging;
2, weave with the ratio of filling 28-35%, veil 57-50%, weft yarn 15% and hook band, basal plane is more solid, hooks body and to be easily kept upright on basal plane state;
3, the combination of yarn variety can make belt meet different use needs;
4, adopt degreasing agent washing hook band can ensure gluing effect, make polyurethane resin can with yarn strong bonded;
5, cutting off O type looped pile before gluing can make monofilament first be kept upright, and makes monofilament height in thermoforming higher.
[detailed description of the invention]
A production technology for woven type mushroom head magic tape, its step comprises:
1. weave: filling, veil, weft yarn are coiled integral respectively and loads loom, weave the hook band with O type looped pile;
2. cut off: being disconnected by O type looped pile becomes two monofilament erect;
3. wash: clean hooking band in containing the hot water of degreasing agent, then whole boiling hot;
4. gluing: use polyurethane resin gluing to fix each monofilament root, dry;
5. get damp again: the hook band after gluing is placed in 8-24 hour under room temperature environment;
6. thermoforming: be mushroom-head shape by monofilament head melt molding.
Be described in further detail below in conjunction with the production technology of concrete case study on implementation to woven type mushroom head magic tape of the present invention.
Case study on implementation 1
1. weave: 300D/36F terylene filling 28%, 0.3mmPP veil 57%, 150D/36F terylene weft yarn 15% are coiled integral respectively and load loom, weaves the hook band with O type looped pile;
2. cut off: being fused under 250 DEG C of conditions by each O type looped pile is two monofilament erect;
3. washing: in containing 15% degreasing agent, the hot water of 80 DEG C, clean 20min by hooking band, then wholely to scald;
4. gluing: use polyurethane resin gluing to fix each monofilament root, dry;
5. get damp again: place 8 hours under the hook band after gluing being placed in room temperature environment;
6. thermoforming: be mushroom-head shape by melt molding under monofilament head 200 DEG C of conditions.
Above method produces the mushroom head magic tape that obtains, and to hook body long and upright, and outward appearance is good, and polyurethane resin is reliable to the cohesive force of yarn, and belt is durable corrosion-resistant, is applicable to electric wire and the industrial processes occasion such as ties up.
Case study on implementation 2
1. weave: 140D/24F polyamide fibre filling 35%, 0.15mmPP veil 50%, 140D/24F polyamide fibre weft yarn 15% are coiled integral respectively and load loom, weaves the hook band with O type looped pile;
2. cut off: being fused under 260 DEG C of conditions by each O type looped pile is two monofilament erect;
3. washing: in containing 15% degreasing agent, the hot water of 70 DEG C, clean 25min by hooking band, then wholely to scald;
4. gluing: use polyurethane resin gluing to fix each monofilament root, dry;
5. get damp again: place 10 hours under the hook band after gluing being placed in room temperature environment;
6. thermoforming: be mushroom-head shape by melt molding under monofilament head 250 DEG C of conditions.
Above method produces the mushroom head magic tape that obtains, and to hook body long and upright, and outward appearance is good, and polyurethane resin is reliable to the cohesive force of yarn, and entirety is comparatively soft, and outward appearance is good, is applicable to perambulator.
Case study on implementation 3
1. weave: 300D/36F terylene filling 30%, 0.2mmPP veil 55%, 200D/24F polyamide fibre weft yarn 15% are coiled integral respectively and load loom, weaves the hook band with O type looped pile;
2. cut off: being fused under 270 DEG C of conditions by each O type looped pile is two monofilament erect;
3. washing: in containing 15% degreasing agent, the hot water of 60 DEG C, clean 30min by hooking band, then wholely to scald;
4. gluing: use polyurethane resin gluing to fix each monofilament root, dry;
5. get damp again: place 16 hours under the hook band after gluing being placed in room temperature environment;
6. thermoforming: be mushroom-head shape by melt molding under monofilament head 230 DEG C of conditions.
Above method produces the mushroom head magic tape that obtains, and to hook body long and upright, and outward appearance is good, and polyurethane resin is reliable to the cohesive force of yarn, and belt is soft, solid, is applicable to the daily necessities field such as suitcase, curtain.
Case study on implementation 4
1. weave: 200D/24F polyamide fibre filling 32%, 0.25mmPP veil 53%, 150D/36F terylene weft yarn 15% are coiled integral respectively and load loom, weaves the hook band with O type looped pile;
2. cut off: being fused under 280 DEG C of conditions by each O type looped pile is two monofilament erect;
3. washing: in containing 15% degreasing agent, the hot water of 80 DEG C, clean 20min by hooking band, then wholely to scald;
4. gluing: use polyurethane resin gluing to fix each monofilament root, dry;
5. get damp again: place 24 hours under the hook band after gluing being placed in room temperature environment;
6. thermoforming: be mushroom-head shape by melt molding under monofilament head 240 DEG C of conditions.
Above method produces the mushroom head magic tape that obtains, and to hook body long and upright, and outward appearance is good, and polyurethane resin is reliable to the cohesive force of yarn, and belt is soft, solid, is applicable to the daily necessities field such as suitcase, curtain.
Above-described is only some embodiments of the present invention.For the person of ordinary skill of the art, without departing from the concept of the premise of the invention, can also make some distortion and improvement, these all belong to protection scope of the present invention.
Claims (9)
1. a production technology for woven type mushroom head magic tape, its step comprises:
1. weave: filling, veil, weft yarn are coiled integral respectively and loads loom, weave the hook band with O type looped pile;
2. cut off: being disconnected by O type looped pile becomes two monofilament erect;
3. wash: clean hooking band in containing the hot water of degreasing agent, then whole boiling hot;
4. gluing: use polyurethane resin gluing to fix each monofilament root, dry;
5. get damp again: the hook band after gluing is placed in 8-24 hour under room temperature environment;
6. thermoforming: be mushroom-head shape by monofilament head melt molding.
2. the production technology of woven type mushroom head magic tape according to claim 1, is characterized in that: the usage ratio of described weaving step yarn is filling 28-35%, veil 57-50%, weft yarn 15%.
3. the production technology of woven type mushroom head magic tape according to claim 1 and 2, is characterized in that: described filling adopts the one in 300D/36F Polyester Yarns or 140D ~ 200D/24F polyamide staple fibre spun yarn.
4. the production technology of woven type mushroom head magic tape according to claim 1 and 2, is characterized in that: described weft yarn adopts the one in 150D/36F Polyester Yarns or 140D ~ 200D/24F polyamide staple fibre spun yarn.
5. the production technology of woven type mushroom head magic tape according to claim 1 and 2, is characterized in that: described veil adopts the PP line of wire diameter 0.15 ~ 0.3mm.
6. the production technology of woven type mushroom head magic tape according to claim 1, it is characterized in that: described water-washing step condition is water temperature 60-80 DEG C, scavenging period is 20-30min.
7. the production technology of woven type mushroom head magic tape according to claim 1, is characterized in that: described degreasing agent consumption is 15%.
8. the production technology of woven type mushroom head magic tape according to claim 1, is characterized in that: described in described cut-out step, O type looped pile is blown by 250-280 DEG C of high temperature.
9. the production technology of woven type mushroom head magic tape according to claim 1, is characterized in that: described thermoforming step fusion temperature is 200-250 DEG C.